Preparation method of blended fabric suitable for exercise mat
A technology of blended fabrics and gymnastics, applied in the field of textile fabrics, can solve the problems that affect the technical level of athletes, do not consider antibacterial, easily breed a large number of bacteria, etc., and achieve the effects of low cost, improved antibacterial effect, and beautiful appearance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] A method for preparing a blended fabric suitable for gymnastics mats includes the following steps:
[0027] A. Using Polygonum multiflorum vine as raw material, using alkaline boiling degumming process to prepare Polygonum multiflorum monofilament;
[0028] B. Put the monofilament of Polygonum multiflorum rattan into lime water to soak for 2.5 hours, and then dry it until the moisture content is 28%;
[0029] C. Freeze the single fiber of Polygonum multiflorum rattan at a low temperature of minus 28°C for 7 hours;
[0030] D. Take out the monofilament of Polygonum multiflorum rattan and put it into a vacuum puffing box, reduce the air pressure from 12MPa to normal pressure within 7s, put it in water, add biological antibacterial agent, carry out microwave dispersion, and dry until the moisture content is 8 %;
[0031] E. Use cotton fiber as the outer layer and Polygonum multiflorum rattan single fiber as the core to make core-spun yarn;
[0032] F. The core-spun yarn and polyeste...
Embodiment 2
[0040] A method for preparing a blended fabric suitable for gymnastics mats includes the following steps:
[0041] A. Using Polygonum multiflorum vine as raw material, using alkaline boiling degumming process to prepare Polygonum multiflorum monofilament;
[0042] B. Put the monofilament of Polygonum multiflorum rattan into lime water and soak for 2h, and then dry it to 30% water content;
[0043] C. Freeze the single fiber of Polygonum multiflorum rattan at minus 22℃ for 8h;
[0044] D. Take out the monofilament of Polygonum multiflorum rattan and put it in a vacuum puffing box, reduce the air pressure from 15MPa to normal pressure within 5s, put it in water, add biological antibacterial agent, carry out microwave dispersion, and dry it to a moisture content of 9 %;
[0045] E. Use cotton fiber as the outer layer and Polygonum multiflorum rattan single fiber as the core to make core-spun yarn;
[0046] F. The core-spun yarn and polyester fiber are blended, dyed, printed, and post-proce...
Embodiment 3
[0054] A method for preparing a blended fabric suitable for gymnastics mats includes the following steps:
[0055] A. Using Polygonum multiflorum vine as raw material, using alkaline boiling degumming process to prepare Polygonum multiflorum monofilament;
[0056] B. Put the monofilament of Polygonum multiflorum rattan into lime water to soak for 3 hours, and then dry it until the water content is 20%;
[0057] C. Freeze the single fiber of Polygonum multiflorum rattan at a low temperature below minus 20°C for 8 hours;
[0058] D. Take out the monofilament of Polygonum multiflorum rattan and put it into a vacuum puffing box, reduce the air pressure from 15MPa to normal pressure within 5s, put it in water, add biological antibacterial agent, carry out microwave dispersion, and dry it to a moisture content of 6 %;
[0059] E. Use cotton fiber as the outer layer and Polygonum multiflorum rattan single fiber as the core to make core-spun yarn;
[0060] F. The core-spun yarn and polyester fi...
PUM
Property | Measurement | Unit |
---|---|---|
Length | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com