Environmental-friendly composite material for 3D printing clothing and preparation method of environmental-friendly composite material

A technology of 3D printing and composite materials, which is applied in the field of environmental protection composite materials for 3D printing clothing and its preparation, can solve the problems of poor moisture absorption rate and moisture dissipation rate, and achieve the effects of low cost, safe use and easy industrial production.

Inactive Publication Date: 2017-12-12
NANNING MENGHUAN 3D ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The invention provides an environmentally friendly composite material for 3D printing clothing and a preparation method thereof to solve the problems of poor moisture absorption rate and moisture dissipation rate in existing composite materials for 3D printing clothing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] An environmentally friendly composite material for 3D printing clothing, in parts by weight, comprising the following raw materials: 198 parts of PCL, 90 parts of PLA, 2.3 parts of azobisisobutyrate (ethylene glycol acrylate), 1.6 parts of magnesium oxide, ACR 3 parts of conditioner, 3 parts of aerosol generating agent, 10 parts of trimethylolpropane tris(3-aziridinyl propionate), 5 parts of acrylic compatibilizer, 2,6-tertiary butyl-4 - 4 parts of methylphenol, 6 parts of propyltrimethoxysilane, 10 parts of bis(2-ethylhexyl) phthalate, 12 parts of chlorosulfonated polyethylene, 6 parts of polyaluminum chloride, quaternary ester 16 parts of ammonium salt softener, 3.2 parts of styrene, 2.5 parts of rare earth stabilizer, 5 parts of boric acid, 5 parts of flame retardant;

[0052] The flame retardant includes the following raw materials in parts by weight: 25 parts of ethylene glycol butyl ether acetate, 9 parts of ammonium dihydrogen phosphate, 13 parts of antimony trio...

Embodiment 2

[0067] An environmentally friendly composite material for 3D printing clothing, in parts by weight, comprising the following raw materials: 168 parts of PCL, 72 parts of PLA, 1.6 parts of azobisisobutyrate (ethylene glycol acrylate), 1 part of magnesium oxide, ACR 2 parts of conditioner, 2 parts of aerosol generating agent, 7 parts of trimethylolpropane tris(3-aziridinyl propionate), 4 parts of acrylic compatibilizer, 2,6-tertiary butyl-4 - 3 parts of methylphenol, 4 parts of propyltrimethoxysilane, 8 parts of bis(2-ethylhexyl) phthalate, 9 parts of chlorosulfonated polyethylene, 4 parts of polyaluminum chloride, ester group quaternary 10 parts of ammonium salt softener, 2 parts of styrene, 2 parts of rare earth stabilizer, 3 parts of boric acid, 3 parts of flame retardant;

[0068] The flame retardant includes the following raw materials in parts by weight: 20 parts of ethylene glycol butyl ether acetate, 6 parts of ammonium dihydrogen phosphate, 10 parts of antimony trioxide...

Embodiment 3

[0083] An environmentally friendly composite material for 3D printing clothing, in parts by weight, comprising the following raw materials: 235 parts of PCL, 95 parts of PLA, 3 parts of azobisisobutyrate (ethylene glycol acrylate), 2 parts of magnesium oxide, ACR 4 parts of regulator, 5 parts of aerosol generating agent, 10 parts of trimethylolpropane tris(3-aziridinyl propionate), 6 parts of acrylic compatibilizer, 2,6-tertiary butyl-4 - 5 parts of methylphenol, 7 parts of propyltrimethoxysilane, 12 parts of bis(2-ethylhexyl) phthalate, 15 parts of chlorosulfonated polyethylene, 8 parts of polyaluminum chloride, ester group quaternary 20 parts of ammonium salt softener, 4 parts of styrene, 3 parts of rare earth stabilizer, 6 parts of boric acid, 6 parts of flame retardant;

[0084] The flame retardant includes the following raw materials in parts by weight: 28 parts of ethylene glycol butyl ether acetate, 12 parts of ammonium dihydrogen phosphate, 16 parts of antimony trioxid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environmental-friendly composite material for 3D printing clothing and a preparation method of the environmental-friendly composite material. The composite material comprises the following raw materials: PCL, PLA, azo (acrylic ethanediol) diisobutyrate, magnesium oxide, an ACR regulator, an aerosol generating agent, trimethylolpropane tri(3-aziridinyl propionate), an acrylic compatibilizer, 2,6-tert-butyl-4-methylphenol, propyltrimethoxysilane, bis(2-ethylhexyl) phthalate, chlorosulfonated polyethylene, aluminum polychloride, an ester quaternary ammonium salt softening agents, styrene, a rare earth stabilizer, boric acid and a flame retardant. The composite material is prepared by grinding, mixing, granulating, drawing, rolling and the like. The environmental-friendly composite material for 3D printing clothing prepared by the invention is low in cost, environmental-friendly and safe to use, and industrialized production is easily realized.

Description

【Technical field】 [0001] The invention belongs to the technical field of material preparation for 3D printing, and in particular relates to an environmentally friendly composite material for 3D printing clothing and a preparation method thereof. 【Background technique】 [0002] With the continuous progress of society, people have higher and higher requirements for wearing comfort. The comfort of clothing can be divided into physical comfort and psychological comfort. Physiological comfort includes moisture absorption, breathability, warmth retention, softness, stretchability, weight and chemical properties, etc. Most of them are determined by the properties of materials used to make clothing; psychological comfort includes color, luster, Style, wrinkle resistance, crispness, pilling resistance, suitability to the environment, etc. Many of the appearance properties are also determined by the properties of the clothing materials. In recent years, people have higher and higher ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04C08K13/02C08K5/3412C08K5/13C08K3/22C08K3/32B33Y70/00B29B9/06B29C47/92B29C48/92
CPCC08L67/04B29B9/06B29C48/92B29C2948/92704B33Y70/00C08L2205/025C08L2205/035C08K13/02C08K5/3412C08K5/13C08K3/2279C08K3/32
Inventor 覃杨华
Owner NANNING MENGHUAN 3D ENVIRONMENTAL PROTECTION TECH CO LTD