Non-burned plum-shaped colored lime lightweight ceramic particle
A technology of lightweight ceramsite and light through-hole ceramsite, which is applied in ceramic products, soilless culture, application, etc., can solve the problem of high specific gravity and bulk density, can not ensure normal growth and development of plants, no adsorption and air purification, etc. problem, to achieve the effect of improving specific surface area and strength, and bright colors
Inactive Publication Date: 2017-12-29
蒋文兰
View PDF2 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] The colored ceramsite sold in the market is made by mixing cement, fine sand and dyes and then granulating. The specific gravity and bulk density are very large, and the water absorption rate is small. It cannot ensure the normal growth and development of plants, and there is no adsorption and The function of purifying the air
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0039] Below in conjunction with embodiment the present invention will be further described:
[0040] 1. The ingredients of unburned plum-shaped white lime light ceramsite are composed of the following components by weight percentage: quicklime powder 36%, white cement 16%, acidified attapulgite clay 12%, powdery attapulgite foaming agent 8%, light magnesium oxide 4%, hollow glass microspheres 3%, aluminum silicate fiber 2%, iron oxide red 0%, iron oxide green 0%, iron oxide yellow 0%, iron oxide blue 0%, iron oxide Orange 0%, Iron Oxide Brown 0%, Iron Oxide Black 0%, Titanium Dioxide 3% and Water 16%.
[0041] 2. The ingredients of unburned plum blossom-shaped red lime light ceramsite are composed of the following components by weight percentage: quicklime powder 36%, white cement 16%, acidified attapulgite clay 12%, powdery attapulgite foaming 8% of magnesium oxide, 4% of light magnesium oxide, 3% of hollow glass microspheres, 2% of aluminum silicate fiber, 3% of iron oxide...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |
| water absorption | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses a non-burned plum-shaped colored lime lightweight ceramic particle. The key points of the technical scheme are that the non-burned plum-shaped colored lime lightweight ceramic particle consists of the following ingredients: quicklime powder, white cement, acidified attapulgite clay, a powdered attapulgite foaming agent, a hollow glass microsphere, aluminum silicate fibers, an iron oxide pigment and titanium dioxide, the ingredients of the non-burned plum-shaped colored lime lightweight ceramic particle are packaged into the non-burned plum-shaped colored lime lightweight ceramic particle after being stirred, mixed, extruded, granulated, steam-cured and screened, and the non-burned plum-shaped colored lime lightweight ceramic particle has the characteristics of being bright in color, attractive in appearance, good in lightweight strength, large in specific surface area, low in stacking density, excellent in air permeability and high in porosity and water absorption rate. The non-burned plum-shaped colored lime lightweight ceramic particle can ensure good plant growth and development, high survival rate and longer service life and greatly reduce the frequency of water replenishment and is suitable for not only landscape engineering and home gardens, but also soilless culture substrate preparation.
Description
technical field [0001] The invention relates to ceramsite, in particular to an unburned plum-shaped colored lime lightweight ceramsite. Background technique [0002] The colored ceramsite sold in the market is made of cement, fine sand and dyes mixed and granulated. The specific gravity and bulk density are very large, and the water absorption rate is small. It cannot ensure the normal growth and development of plants, and there is no adsorption and The function of purifying the air. [0003] After several sampling tests: the average bulk density of colored ceramsite sold in the market is ≥1200kg / m³, and the average water absorption rate is ≤20%. Contents of the invention [0004] The purpose of the present invention is to overcome the disadvantages of the prior art and provide a non-burning plum-shaped colored lime lightweight ceramsite. [0005] The ingredients of unburned plum-shaped colored lime light ceramsite are composed of quicklime powder, white cement, acidifie...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/10C04B38/02C04B38/08C04B38/10A01G31/00C04B111/20C04B111/40C04B111/82
CPCC04B28/10C04B2111/00284C04B2111/00758C04B2111/20C04B2111/40C04B2111/82C04B7/02C04B14/102C04B14/22C04B14/4656C04B14/308C04B14/305C04B12/04C04B24/2623C04B24/383C04B22/10C04B22/141C04B20/008C04B24/16C04B24/26C04B22/16C04B24/166C04B38/02C04B38/085C04B38/10C04B40/024Y02P60/21
Inventor 金白云吴一青王鲁海黄允金王雨润袁欣许庆华蒋文兰
Owner 蒋文兰