Preparation method of cerate used for wood furniture

A technology for wax paste and furniture, applied in chemical instruments and methods, wax coatings, paints containing biocides, etc., can solve the problems of shortening the service life of wood furniture, moisture-proof and anti-scratch effects, etc. Good wound effect, good moisture resistance, easy to attach effect

Inactive Publication Date: 2018-01-26
佛山市三水区白坭镇巨财红木厂
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in the wood furniture wax prepared by the existing preparation method, when applied to wood furniture, its moisture-proof and anti-scratch effects are not particularly ideal, which greatly shortens the service life of wood furniture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of cerate used for wood furniture
  • Preparation method of cerate used for wood furniture
  • Preparation method of cerate used for wood furniture

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Wax paste for wood furniture, its raw material components by mass parts include:

[0023]

[0024] Its preparation method is:

[0025] Palm wax, PA66, yellow beeswax, asbestos powder, sodium benzoate and silicone oil are weighed;

[0026] Add palm wax, PA66 and yellow beeswax to the twin-screw extruder, the screw speed is 300r / min, control the temperature of each zone to be between 110°C, mix, mix and extrude, and granulate to obtain material a;

[0027] Add the material a, asbestos powder and sodium benzoate into the silicone oil, the stirring speed is 100r / min, and the stirring time is 15min to obtain a wax paste.

Embodiment 2

[0029] Wax paste for wood furniture, its raw material components by mass parts include:

[0030]

[0031] Its preparation method is:

[0032] Palm wax, PA46, yellow beeswax, mica powder, sodium benzoate and silicone oil are weighed;

[0033] Add palm wax, PA46 and yellow beeswax to the twin-screw extruder, the screw speed is 270r / min, control the temperature of each zone to 114°C, mix, mix and extrude, and granulate to obtain material a;

[0034] Add the material a, mica powder and sodium benzoate into the silicone oil, the stirring speed is 95r / min, and the stirring time is 18min to obtain a wax paste.

Embodiment 3

[0036] Wax paste for wood furniture, its raw material components by mass parts include:

[0037]

[0038] Its preparation method is:

[0039] Palm wax, PA610, yellow beeswax, quartz powder, sodium benzoate and silicone oil are weighed;

[0040] Add palm wax, PA610 and yellow beeswax to the twin-screw extruder, the screw speed is 200r / min, control the temperature of each zone to be between 120°C, mix, mix and extrude, and granulate to obtain material a;

[0041] The material a, quartz powder and sodium benzoate were added to the silicone oil, the stirring speed was 60r / min, and the stirring time was 25min to obtain a wax paste.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of cerate used for wood furniture. The preparation method comprises the following steps: adding palm wax, polyamide resin and yellow beeswax into a twin-screw extruder, wherein the rotating speed of screws is 200-300r / min, controlling the temperature of each zone to be 110-120 DEG C, mixing, carrying out mixed extrusion, and granulating to obtain a material a; and adding a filling agent and sodium benzoate into silicone oil, and stirring for 15-25 minutes at the speed of 60-100 r / min, thus obtaining the cerate. Compared with aerial fog wax and solid-state wax, the prepared cerate can be adhered more easily, is easy to process and moistureproof and has good scratch-proof effect when applied to the wood furniture; meanwhile, when the cerate is prepared by adopting the preparation method, the sodium benzoate ingredient is also added, bacteria and mould which are adhered to the surface of furniture can be rapidly killed by waxing solid wood furniture, and the protective effect on the solid wood furniture is realized, so that the service life of the solid wood furniture can be prolonged; besides, the preparation method is simple and low in cost.

Description

technical field [0001] The invention relates to the technical field of furniture wax technology, in particular to a preparation method of wax paste for wood furniture. Background technique [0002] Waxing of wood furniture can block the moisture of solid wood furniture and the circulation of the outside world, so that it can effectively avoid the structural deformation of solid wood furniture, and it can also help the wood fibers of solid wood furniture to be moisturized, so that solid wood furniture looks so shiny forever . [0003] However, when the wood furniture wax prepared by the existing preparation method is applied to wood furniture, its moisture-proof and anti-scratch effects are not particularly ideal, which greatly shortens the service life of the wood furniture. Contents of the invention [0004] In view of this, the invention provides a preparation method of wax paste for wood furniture. [0005] The preparation method of wax paste for wood furniture, the m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More