High-performance environmental-friendly plastic as well as preparation method and application thereof

An environmentally friendly plastic and high-performance technology, applied in the field of plastics, can solve the problems of poor mechanical properties and poor heat resistance, and achieve the effects of high mechanical properties, good high temperature resistance, and high degradation rate

Inactive Publication Date: 2018-04-06
ZHENGZHOU YUANRAN BIOLOGY TECH CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing plastics still have the disadvantages of poor heat resistance and poor mechanical properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance environmental-friendly plastic as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A high-performance environmentally friendly plastic, comprising the following raw materials in parts by weight: 80 parts of polyvinyl chloride, 25 parts of carvacrol, 20 parts of tannic acid, 10 parts of L-theanine, 10 parts of ethyl maltol, and 10 parts of fish scale powder 7 parts of calcium L-aspartate.

[0021] A preparation method of high-performance environmentally friendly plastics, the preparation steps are: (1) mixing carvacrol and tannin, adding 40 parts of 50% ethanol solution, stirring and mixing evenly to obtain mixture A; stirring speed is 300r / min; (2) Mix ethyl maltol, calcium L-aspartate and L-theanine, add 50 parts of deionized water, stir and mix evenly to obtain mixture B; stirring speed is 100r / min; (3) Mix mixture A and mixture B uniformly at 80°C to obtain mixture C; stirring speed is 500r / min; (4) mix polyvinyl chloride and fish scale powder, add mixture C, mix and stir at 165°C for 20min; stirring speed It is 100r / min; (5) Extrude the product ...

Embodiment 2

[0023] A high-performance environmentally friendly plastic, comprising the following raw materials in parts by weight: 130 parts of polyvinyl chloride, 34 parts of carvacrol, 30 parts of tannic acid, 18 parts of L-theanine, 15 parts of ethyl maltol, and 30 parts of fish scale powder parts, L-calcium aspartate 15 parts.

[0024] A preparation method of high-performance environmentally friendly plastics, the preparation steps are: (1) mixing carvacrol and tannin, adding 60 parts of 75% ethanol solution, stirring and mixing evenly to obtain mixture A; the stirring speed is 500r / min; (2) Mix ethyl maltol, calcium L-aspartate and L-theanine, add 75 parts of deionized water, stir and mix evenly to obtain mixture B; stirring speed is 200r / min; (3) Mix mixture A and mixture B uniformly at 105°C to obtain mixture C; stirring speed is 700r / min; (4) mix polyvinyl chloride and fish scale powder, add mixture C, and mix and stir at 185°C for 35min; stirring speed It is 300r / min; (5) Extru...

Embodiment 3

[0026] A high-performance environmentally friendly plastic, comprising the following raw materials in parts by weight: 120 parts of polyvinyl chloride, 28 parts of carvacrol, 25 parts of tannic acid, 16 parts of L-theanine, 13 parts of ethyl maltol, and 20 parts of fish scale powder parts, 11 parts of calcium L-aspartate.

[0027] A preparation method of high-performance environmentally friendly plastics, the preparation steps are: (1) mixing carvacrol and tannin, adding 50 parts of 65% ethanol solution, stirring and mixing evenly to obtain mixture A; the stirring speed is 400r / min; (2) Mix ethyl maltol, calcium L-aspartate and L-theanine, add 65 parts of deionized water, stir and mix evenly to obtain mixture B; stirring speed is 180r / min; (3) Mix mixture A and mixture B uniformly at 95°C to obtain mixture C; stirring speed is 600r / min; (4) mix polyvinyl chloride and fish scale powder, add mixture C, and mix and stir at 175°C for 30min; stirring speed It is 200r / min; (5) Ext...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance environmental-friendly plastic as well as a preparation method and application thereof. The high-performance environmental-friendly plastic comprises the following raw materials in parts by weight: 80-130 parts of polyvinyl chloride, 25-34 parts of carvacrol, 20-30 parts of tannic acid, 10-18 parts of L-theanine, 10-15 parts of ethyl maltol, 10-30 parts of fish scale powder and 7-15 parts of L-calcium aspartate. The high-performance environmental-friendly plastic disclosed by the invention has the advantages of excellent high-temperature resistance and high mechanical property and can be widely applied to the fields of electronics and electrical equipment, buildings, automobiles, office equipment and machinery; and moreover, the preparation process is simple and favorable for market popularization.

Description

technical field [0001] The invention relates to a plastic, in particular to a high-performance environment-friendly plastic and its preparation method and application. Background technique [0002] As a material with a wide range of uses, plastic has greatly facilitated people's lives, but its non-decomposable characteristics have also caused serious environmental problems. Therefore, the research and production of degradable plastic products have attracted great attention internationally. People have begun to conduct a lot of research and development on the use of starch and vegetable protein to produce degradable plastics. However, the existing plastics still have the disadvantages of poor heat resistance and poor mechanical properties. Therefore, the present invention provides a high-performance environmentally friendly plastic and its preparation method and application. Contents of the invention [0003] The object of the present invention is to provide a high-perfo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K5/13C08K5/20C08K3/32C08K5/17
Inventor 张力
Owner ZHENGZHOU YUANRAN BIOLOGY TECH CO LTD