A kind of preparation method of transparent conductive film glass
A technology of transparent conductive film and glass, which is applied in the direction of coating, etc., can solve the problems of poor electrical conductivity and low light transmittance of transparent conductive film glass, and achieve the effects of improving electrical conductivity, reducing grain boundary scattering, and improving compactness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0025]Dissolve 10g of zinc acetate dihydrate in a beaker containing 180mL of isopropanol, place the beaker in a water bath, heat up to 70°C, add 30mL of diethanolamine to the beaker, and keep it warm with a magnetic stirrer at a speed of 300r / min Stir for 30 minutes, continue to add 15g of aluminum nitrate nonahydrate to the beaker, keep stirring until the solid is completely dissolved, and obtain a transparent homogeneous sol; put the ordinary glass slide into a beaker filled with deionized water, and then place the beaker in ultrasonic cleaning In a vacuum cleaner, clean it with a power of 150W for 15 minutes, put the cleaned ordinary glass slide in a sodium hydroxide solution with a mass fraction of 40% and soak for 2 hours, take out the ordinary glass slide and wash it with deionized water for 3 times, and then put it in Soak in 20% hydrochloric acid for 1 hour, take out the ordinary glass slide and wash it with absolute ethanol until the washing liquid is neutral to obtain...
example 2
[0027] Dissolve 11g of zinc acetate dihydrate in a beaker containing 190mL of isopropanol, place the beaker in a water bath, heat up to 75°C, add 35mL of diethanolamine to the beaker, and keep it warm with a magnetic stirrer at a speed of 320r / min Stir for 32 minutes, continue to add 17g of aluminum nitrate nonahydrate to the beaker, keep stirring until the solid is completely dissolved, and obtain a transparent homogeneous sol; put the ordinary glass slide into a beaker filled with deionized water, and then place the beaker in ultrasonic cleaning Clean the ordinary glass slide with a power of 165W for 17min, put the cleaned ordinary glass slide into the sodium hydroxide solution with a mass fraction of 40% and soak for 2.5h, take out the ordinary glass slide and wash it with deionized water for 4 times, and then put immerse in hydrochloric acid with a mass fraction of 20% for 1.5h, take out the ordinary glass slide and wash it with absolute ethanol until the washing liquid is ...
example 3
[0029] Dissolve 12g of zinc acetate dihydrate in a beaker containing 200mL of isopropanol, place the beaker in a water bath, heat up to 80°C, add 40mL of diethanolamine to the beaker, and keep it warm with a magnetic stirrer at a speed of 350r / min Stir for 35 minutes, continue to add 18g of aluminum nitrate nonahydrate to the beaker, keep stirring until the solid is completely dissolved, and obtain a transparent homogeneous sol; put the ordinary glass slide into a beaker filled with deionized water, and then place the beaker in ultrasonic cleaning In a vacuum cleaner, wash with 180W power for 20min, put the cleaned ordinary glass slide into 40% sodium hydroxide solution and soak for 3h, take out the ordinary glass slide and wash it with deionized water for 5 times, and then put it into Soak in 20% hydrochloric acid for 2 hours, take out the ordinary glass slide and wash it with absolute ethanol until the washing solution is neutral to obtain a glass substrate; Tetraacetic acid...