Colored asphalt glue and preparation method thereof

A technology of colored asphalt and cement, which is applied in the field of colored asphalt glue, can solve the problems affecting the effect of repair, and achieve the effect of good bonding performance and not easy interface separation

Inactive Publication Date: 2018-07-10
SHANGHAI PUDONG LUQIAO ASPHALT MATERIAL CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the different aging degrees and material properties of the new and old colored asphalt glue, there are certain problems in the bonding and fusion of the two during repairing, and it is easy to form a separation layer on the contact surface, which affects the effect of repairing
For how to solve the interface bonding problem of new and old colored asphalt, there is no feasible solution at present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1a to 1d

[0021] Embodiments 1a to 1d: In this group of embodiments, the proportioning of the colored asphalt glue is: in parts by weight, including: colored binder 40, diesel oil 30, stearic acid 5, paraffin oil 10, water 13, pigment 2 .

[0022] In Example 1a, the color binder includes petroleum resin 48, styrene-butadiene-styrene block copolymer (SBS) 10, and aromatic oil 42.

[0023] In Example 1b, the color binder includes petroleum resin 50, styrene-butadiene-styrene block copolymer (SBS) 10, and aromatic oil 40.

[0024] In Example 1c, the color binder includes petroleum resin 52, styrene-butadiene-styrene block copolymer (SBS) 7, and aromatic oil 41.

[0025] In Example 1d, the color binder includes petroleum resin 48.5, styrene-butadiene-styrene block copolymer (SBS) 8.5, and aromatic oil 43.

[0026] After obtaining the above composition, take one group and put it in the aging box, and one group measures the physical and chemical properties of the composition. After the meas...

Embodiment 2a to 2d

[0027] Examples 2a to 2d, in this group of examples, the proportioning of the colored asphalt glue is, in parts by weight, including: 35 colored binders, 20 diesel oil, 5 stearic acid, 20 paraffin oil, 18 water, and 2 pigments .

[0028] In Example 2a, the binder included petroleum resin 48, styrene-butadiene-styrene block copolymer (SBS) 10, and aromatic oil 42.

[0029] In Example 2b, the binder includes petroleum resin 50, styrene-butadiene-styrene block copolymer (SBS) 10, and aromatic oil 40.

[0030] In Example 2c, the binder includes petroleum resin 52, styrene-butadiene-styrene block copolymer (SBS) 7, and aromatic oil 41.

[0031] In Example 2d, the binder included petroleum resin 48.5, styrene-butadiene-styrene block copolymer (SBS) 8.5, and aromatic oil 43.

Embodiment 3

[0032] Embodiment 3 a to 3d, in this group of embodiments, the proportioning of colored asphalt glue is, in parts by weight, including: cementing material 45; diesel oil 25; stearic acid 8; paraffin oil 25; water 12; pigment 3.

[0033] In Example 3a, the binder included petroleum resin 48, styrene-butadiene-styrene block copolymer (SBS) 10, and aromatic oil 42.

[0034] In Example 3b, the binder includes petroleum resin 50, styrene-butadiene-styrene block copolymer (SBS) 10, and aromatic oil 40.

[0035] In Example 3c, the binder included petroleum resin 52, styrene-butadiene-styrene block copolymer (SBS) 7, and aromatic oil 41.

[0036] In Example 3d, the binder included petroleum resin 48.5, styrene-butadiene-styrene block copolymer (SBS) 8.5, and aromatic oil 43.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a colored asphalt glue and a preparation method thereof, wherein the colored asphalt glue comprises, by weight, 30-50 parts of a cementing material, 20-30 parts of diesel oil,3-8 parts of stearic acid, 10-30 parts of paraffin oil, 5-20 parts of water, and 1-5 parts of pigment. According to the present invention, when the colored asphalt material contacts the material usedfor a certain time, the bonding property of the interface is better, and the interface separation is not easily generated.

Description

technical field [0001] The invention relates to a colored asphalt glue, and provides a preparation method of the colored asphalt glue. Background technique [0002] The existing asphalt glue is basically black. The main materials used to pave roads are cement and asphalt. These two materials have multiple functions such as bonding, waterproofing, anti-corrosion and insulation, so they are widely used. The disadvantage is that the color is single, the senses are tedious, and it is not conducive to the beautification of the urban landscape. With the rapid development of society, people pay more and more attention to the beauty of the city, and now there are more and more colored asphalt roads. Paving different colors of colored pavement on the city streets can better coordinate the road with the surrounding architectural art, reflecting the characteristics and styles of a country or a city. In scenic areas, sanatoriums and parks, roads and squares of various colors are pave...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J157/02C09J153/02C09J191/00C09J11/06C09J11/08C09J11/04
CPCC09J157/02C08K2003/2272C08L2205/035C09J11/04C09J11/06C09J11/08C08L53/02C08L91/00C08L91/06C08K5/09C08K3/22
Inventor 闫国杰张浩刚周曹伟蒯苗俊胡睿刘张龙李代飞
Owner SHANGHAI PUDONG LUQIAO ASPHALT MATERIAL CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com