Ru porcelain lavender grey glaze and preparation method thereof

A technology of celadon glaze and porcelain powder, applied in the field of ceramics, can solve the problems of agate glaze, natural kiln turning pink and blue, etc., to achieve the effect of soft luster and pure and delicate glaze layer

Inactive Publication Date: 2018-07-27
马聚魁
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of Ru porcelain powder green glaze, in order to solve the age-dated glaze color of the powder green glaze in the prior art, and solve the problem that agate enters the glaze, and the natural kiln becomes pink blue; the purpose of the present invention is also It is to provide a kind of preparation method of Ru porcelain powder green glaze

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A Ru porcelain powder green glaze, comprising the following components in parts by weight: 15 parts of agate stone, 6 parts of purple gold soil, 38 parts of feldspar powder, 9 parts of quartz powder, 1.5 parts of bone ash, 11 parts of wood ash, 15 parts of calcite, red 3 parts of iron ore, 6 parts of spotted fossils, 11 parts of local overglaze (local glazed soil in Baofeng, Henan), and 13 parts of self-made medicine.

[0026] The preparation method of Ru porcelain powder green glaze comprises the following steps:

[0027] 1) Refining, washing and crushing agate, calcite, hematite and porphyrin respectively into granules or powder;

[0028] 2) Mix the purple gold soil, feldspar powder, quartz powder, bone ash, wood ash, local overglaze, self-made medicine and the stones treated in step 1) according to the proportion, and then add water for ball milling. The amount of water added is 0.85 times, the ball milling time is 20 hours, and the glaze slurry is obtained;

[002...

Embodiment 2

[0035] A Ru porcelain powder green glaze, comprising the following components in parts by weight: 21 parts of agate stone, 9 parts of purple gold, 48 parts of feldspar powder, 13 parts of quartz powder, 3 parts of bone ash, 16 parts of wood ash, 18 parts of calcite, red 8 parts of iron ore, 9 parts of spotted fossils, 16 parts of local glazed soil (local glazed soil in Baofeng, Henan), and 18 parts of self-made medicine.

[0036] The preparation method of Ru porcelain powder green glaze comprises the following steps:

[0037] 1) Refining, washing and crushing agate, calcite, hematite and porphyrin respectively into granules or powder;

[0038] 2) Mix purple gold soil, feldspar powder, quartz powder, bone ash, wood ash, local glazed soil, self-made medicine and the stones treated in step 1) according to the proportion, and then add water for ball milling. The amount of water added is 0.90 of the glaze. times, the ball milling time is 60 hours, and the glaze slurry is obtained;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses Ru porcelain lavender grey glaze and a preparation method thereof. The Ru porcelain lavender grey glaze comprises, by weight, 15-21 parts of agate, 6-9 parts of violet golden clay, 38-48 parts of feldspar powder, 9-13 parts of quartz powder, 1.5-3 parts of bone ash, 11-16 parts of wood ash, 15-18 parts of calcite, 3-8 parts of hematite, 6-9 parts of exposed iron ore, 11-16parts of local glaze clay and 13-18 parts of self-made glaze chemical. The Ru porcelain lavender grey glaze and the preparation method thereof have the advantages that the through-ages division glazecolor of the Ru porcelain lavender grey glaze is achieved, the agate is added into the glaze and naturally turned into a lavender grey color in a kiln, the lavender grey glaze is simple and elegant, fine and smooth, capable of changing along with light and smooth and unique like milk and ice, the lavender grey color of the glaze is elegant and watery, the glaze layer is pure and fine and smooth, has an elegant and plain and neat blue jade color and is attractive and implicit in quality and soft in luster, and cracked glaze is densely distributed on the surface of the glaze and has the unique features of fish scale cracked glaze, cicada's wing cracked glaze, crab claw cracked glaze, ice cracking cracked glaze and sesame flower cracked glaze.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a Ru porcelain green glaze and a preparation method thereof. Background technique [0002] Ru porcelain was listed as the first of the five famous porcelains (Ru, Guan, Jun, Ge, Ding) in the Song Dynasty of our country, and was designated as royal porcelain at that time. The clay of Ru porcelain is fine, the fetal bone is hard, the glaze color is moist, and the shape is simple and generous. The characteristics of "sesame flower" are called "like jade but not jade but better than jade" by the world. Ru porcelain began in the late Northern Song Dynasty and got its name because the kiln site was in Ruzhou (now Ruzhou and Baofeng, Henan). Due to historical reasons, Ru Kiln flourished for only 20 years. Due to the short firing time, there are less than 100 pieces of treasures handed down to this day, which are very precious. [0003] The traditional ceramic glaze is a kind of sili...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/14C04B33/34C04B41/86
CPCC03C8/14C04B33/34C04B41/5022C04B41/86
Inventor 马聚魁马得原马铭
Owner 马聚魁