PSA sheet for conductive member, conductive member laminate, and image display device
A conductive member, adhesive sheet technology, applied in synthetic resin layered products, film/sheet adhesives, non-polymer adhesive additives, etc. and other problems, to achieve the effect of good curing characteristics, foam resistance and reliability curing characteristics
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1-1
[0170] To 1 kg of (meth)acrylic (co)polymer (A-1), 3 g of 1,2,3-triazole (manufactured by Otsuka Chemical Co., Ltd.) 15 g of a mixture of 4-methylbenzophenone and 2,4,6-trimethylbenzophenone (manufactured by Lamberti, trade name "Esacure TZT") were uniformly mixed to obtain a resin composition for an adhesive layer. things.
[0171] Two sheets of polyethylene terephthalate films (manufactured by Mitsubishi Plastics, Inc., trade name "Diafoil MRV", thickness 100 µm and Mitsubishi Plastics, Inc., trade name "Diafoil MRQ", thickness 75 μm) sandwiched the resin composition for an adhesive layer, and shaped into a sheet shape so that the thickness of the adhesive sheet became 150 μm, thereby producing an adhesive sheet laminate. The following various evaluations were performed on the pressure-sensitive adhesive sheet laminate. The results are shown in Table 1.
Embodiment 1-2
[0173] Add 3 g of 1,2,3-triazole as a metal corrosion inhibitor and propoxylated pentaerythritol as a crosslinking agent to 1 kg of (meth)acrylic (co)polymer (A-2) Triacrylate (Shin Nakamura Industry Co., Ltd., trade name "ATM-4PL") 20 g, a mixture of 4-methylbenzophenone and 2,4,6-trimethylbenzophenone as a photopolymerization initiator (The Lamberti company make, brand name "Esacure TZT") 15g was uniformly mixed, and the resin composition for adhesive layers was obtained.
[0174] Next, the aforementioned resin composition for an adhesive layer was made to have a thickness of 150 μm on a peeled polyethylene terephthalate film (manufactured by Mitsubishi Plastics, Inc., trade name “Diafoil MRV”, thickness 100 μm). After being formed into a sheet by the above-mentioned method, a peeled polyethylene terephthalate film (manufactured by Mitsubishi Plastics, Inc., trade name "Diafoil MRQ", thickness 75 μm) was covered to prepare an adhesive sheet laminate. The following various e...
Embodiment 1-3
[0176] Except having used 5 g of 1,2,3-triazole which is a metal corrosion inhibitor, it carried out similarly to Example 1-2, and produced the adhesive sheet laminated body. The following various evaluations were performed on the pressure-sensitive adhesive sheet laminate. The results are shown in Table 1.
PUM
| Property | Measurement | Unit |
|---|---|---|
| melting point | aaaaa | aaaaa |
| melting point | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |