Aluminosilicate glass and strengthened glass
A technology of aluminosilicate glass and oxide, which is applied in the field of aluminosilicate glass and strengthened glass, and can solve the problems of high raw material cost, limited application range, and difficult production
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1～20
[0048]The aluminosilicate glasses of Examples 1-20 were weighed according to the proportions in Table 1 and Table 2 and the corresponding raw materials (the values corresponding to each component in Table 1 and Table 2 are the mass percentages) were mixed to obtain the mixture , wherein the particle size of the carbon powder (C) is 50 mesh to 100 mesh. Put the mixture into a platinum crucible, put the platinum crucible into a silicon-molybdenum furnace, raise the temperature to 1550°C, and melt it for 3 hours, homogenize it and cast it into a mold, and anneal it at 600°C for 1 hour to obtain a block shaped glass. The bulk glass was cut, and both surfaces were ground and polished to obtain a sheet glass with a size of 50 mm×50 mm×5 mm.
[0049] Table 1
[0050] Example 1 2 3 4 5 6 7 8 9 10 SiO 2
68.00 74.00 70.50 69.30 72.00 68.60 68.20 69.50 69.90 69.00 P 2 o 5
6.00 2.00 4.00 2.00 2.00 3.00 5.00 3.50 2.50 5.20 ...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| transmittivity | aaaaa | aaaaa |
Abstract