A non-silicon defoamer

A non-silicon defoamer and defoamer technology, applied in non-silicon defoamer, non-silicon defoamer containing acrylate polymer, and fine chemical preparation field, can solve problems such as precipitation residue, environmental damage, etc. The effect of improving the defoaming ability, improving the dispersing ability, and improving the defoaming performance

Active Publication Date: 2020-04-07
JIANGSU SIXIN SCI-TECH APPL RES INST CO LTD
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The emergence of this type of defoamer can solve the problem of environmental damage and silicon precipitation residues, but there is still a lot of room for improvement in the defoaming and antifoaming performance of the defoamer prepared by the current technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A non-silicon defoamer
  • A non-silicon defoamer
  • A non-silicon defoamer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] (1) Mix 80g isooctyl acrylate with 100g hydroxyethyl acrylate, 80g unsaturated end-capped polyether B1 and 4.8g benzoyl peroxide, and stir to completely dissolve benzoyl peroxide to form mixture a1;

[0065] (2) 50 g of olefin C1 and 0.8 g of benzoyl peroxide are stirred and mixed to completely dissolve benzoyl peroxide to form mixture b1;

[0066] (3) Stir and mix the remaining 20 g of isooctyl acrylate and 0.8 g of benzoyl peroxide to completely dissolve the benzoyl peroxide to form a mixture c1;

[0067] (4) Add 0.8 g of benzoyl peroxide to 662 g of diluent PPG1000 while stirring, heat up to 80°C after the addition of benzoyl peroxide, and keep it warm for 10 minutes to completely dissolve the benzoyl peroxide to form a mixture d1 ;

[0068] (5) Under the cooling of circulating cooling water, keep the temperature of the mixture d1 at 80°C, add the mixture a1 dropwise to the mixture d1 while stirring, and drop it within 3 hours to form the mixture e1;

[0069] (6) A...

Embodiment 2

[0074] (1) Mix 320g of isooctyl acrylate with 200g of hydroxyethyl methacrylate, 10g of unsaturated capped polyether B2 and 2.4g of benzoyl peroxide, and stir to completely dissolve benzoyl peroxide to form a mixture a2 ;

[0075] (2) 40g olefin C2 and 0.4g benzoyl peroxide are stirred and mixed to completely dissolve benzoyl peroxide to form mixture b2;

[0076](3) The remaining 80 g of isooctyl acrylate and 0.4 g of benzoyl peroxide were stirred and mixed to completely dissolve the benzoyl peroxide to form a mixture c2;

[0077] (4) Add 0.4 g of benzoyl peroxide to 346 g of diluent PPG600 while stirring. After the addition of benzoyl peroxide is completed, the temperature is raised to 100 ° C, and the temperature is kept for 10 minutes to completely dissolve the benzoyl peroxide to form a mixture d2 ;

[0078] (5) Under the cooling of circulating cooling water, keep the temperature of the mixture d2 at 100°C, add the mixture a2 dropwise to the mixture d2 while stirring, an...

Embodiment 3

[0084] (1) Mix 240g of isooctyl methacrylate with 100g of hydroxyethyl acrylate, 50g of unsaturated capped polyether B3 and 3.6g of benzoyl peroxide, and stir to completely dissolve benzoyl peroxide to form a mixture a3 ;

[0085] (2) 80g olefin C3 and 0.6g benzoyl peroxide are stirred and mixed to completely dissolve benzoyl peroxide to form mixture b3;

[0086] (3) The remaining 60 g of isooctyl methacrylate and 0.6 g of benzoyl peroxide were stirred and mixed to completely dissolve the benzoyl peroxide to form a mixture c3;

[0087] (4) Add 0.6 g of benzoyl peroxide to 464 g of diluent PPG2000 while stirring, heat up to 60°C after the addition of benzoyl peroxide, and keep it warm for 20 minutes to completely dissolve the benzoyl peroxide to form a mixture d3 ;

[0088] (5) Under the cooling of circulating cooling water, keep the temperature of the mixture d3 at 60°C, add the mixture a3 dropwise to the mixture d3 while stirring, and drop it within 1 hour to form the mixtu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of fine chemical preparations, and discloses a non-silicon defoamer, comprising an acrylate polymer, an organic solvent carrier, hydrophobic particles, and a defoaming aid; the acrylate polymer is composed of the following raw material components Made of: Monomer‑1, Monomer‑2, unsaturated capped polyethers, olefins, diluents, initiators. The invention also discloses a preparation method of the non-silicon defoamer. The invention also discloses the application of the non-silicon defoamer in defoaming and foam suppression in systems rich in anionic surfactants. The antifoaming agent of the present invention uses acrylate polymer as the main active substance, and the antifoaming agent has excellent antifoaming performance. The defoaming performance of the acrylate polymer is improved by adding the monomer step by step, and the hydrophilicity of the acrylate polymer is improved by modifying the unsaturated end-capped polyether, which further improves its instant defoaming ability. The olefins with 6-22 carbon atoms are modified to improve the anti-foaming performance of the defoamer.

Description

technical field [0001] The invention belongs to the technical field of fine chemical preparations, relates to a fine chemical preparation, in particular to a non-silicon defoamer, more precisely, a non-silicon defoamer containing an acrylate polymer, and a non-silicon defoamer in rich Applications in systems containing anionic surfactants such as papermaking, water treatment, textiles and other industries. Background technique [0002] Defoamers are compositions used in industrial production to control foam in various processes. In industrial production, especially in papermaking, water treatment, textile and other industries, due to the rich water and a large amount of chemical additives added in the system, and accompanied by a large amount of mechanical energy, such as stirring, washing and thickening processes, etc., it is extremely difficult May cause foam formation. Liquid media (such as water), chemical additives (such as surfactants), air sources and mechanical ene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D19/04C08F283/06C08F220/18C08F220/28C08F210/14
CPCB01D19/0404B01D19/0409C08F283/065C08F220/20C08F220/1808C08F220/281B01D19/04C08F210/14C08F283/06C08L51/08
Inventor 张振刘杨曹添
Owner JIANGSU SIXIN SCI-TECH APPL RES INST CO LTD