A nanoscale intercalated hydrotalcite catalyst and its preparation method and application

A catalyst and a technology for hydrotalcite, which are applied in the field of nano-scale intercalated hydrotalcite catalyst and its preparation, can solve the problems of low conversion rate and high cost of raw materials, and achieve the effects of easy operation, simple preparation method and stable performance.

Active Publication Date: 2021-10-29
BEIJING INSTITUTE OF PETROCHEMICAL TECHNOLOGY
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] In order to solve the technical problems that the synthesis gas conversion catalyst in the prior art cannot catalytically convert synthesis gas into aldehyde organic compounds, and the existing catalyst used solely for the preparation of acetaldehyde has high raw material cost and low conversion rate, etc., the present invention provides A nano-scale intercalated hydrotalcite catalyst and its preparation method and application, the nano-scale intercalated hydrotalcite catalyst has high selectivity to acetaldehyde, can catalytically convert synthesis gas into acetaldehyde, and has a high conversion rate and a simple preparation method , easy to operate, can greatly reduce the cost of raw materials for the preparation of acetaldehyde, and has a good industrial application prospect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A nanoscale intercalated hydrotalcite catalyst and its preparation method and application
  • A nanoscale intercalated hydrotalcite catalyst and its preparation method and application
  • A nanoscale intercalated hydrotalcite catalyst and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] A kind of nanoscale intercalation hydrotalcite catalyst, its preparation method can comprise the following steps:

[0036] Step A, mix the soluble salt with catalytic activity, the soluble salt of trivalent metal and alkaline substance, make the pH value of mixed solution be 7~13 (this pH value is preferably 8~11), and with reaction temperature 60-160° C. (the reaction temperature is preferably 80-140° C.), and react for 6-48 hours to prepare a catalyst precursor with a pH value of 7-13 (the pH value is preferably 8-11). Wherein, the soluble salt with catalytic activity and the soluble salt of the trivalent metal can be in any ratio, and the amount of the alkaline substance is enough so that the pH of the mixed solution is 7-13.

[0037] Step B, adding macromolecular organic matter to the catalyst precursor for intercalation reaction (the intercalation reaction can adopt the intercalation reaction in the prior art, that is, when the main reactant is a layered structure,...

Embodiment approach

[0041](1) The soluble salt with catalytic activity is a soluble salt of at least one of Co, Fe, Ru, Rh, Ni; for example: the soluble salt with catalytic activity can be Co(NO 3 ) 2 ·6H 2 O, Fe(NO 3 ) 2 9H 2 O, Ni(NO 3 ) 2 ·6H 2 O or RuCl 3 ·3H 2 O.

[0042] (2) the soluble salt of described trivalent metal can be the soluble salt of at least one in aluminum ion or chromium ion; For example: the soluble salt of described trivalent metal can be Al(NO 3 ) 3 9H 2 O.

[0043] (3) The alkaline substance can use NH 3 ·H 2 O, NaOH, Na 2 CO 3 , urea, and at least one of hexamethylenetetramine.

[0044] (4) The macromolecular organic matter is at least one of sodium lactate, short-chain alcohol, formamide and derivatives thereof.

[0045] (5) The reducing gas is at least one of hydrogen and carbon monoxide.

[0046] (7) The peeling can use one or a combination of vibration, ultrasound, and centrifugation.

[0047] Specifically, the preparation method of the nanoscale...

Embodiment 1

[0054] A kind of nanoscale intercalation hydrotalcite catalyst, its preparation method can comprise the following steps:

[0055] Step a1, 3.638g of Co(NO 3 ) 2 ·6H 2 O, 2.345g of Al(NO 3 ) 3 9H 2 The urea of ​​O, 2.289g all adds to 50mL and removes CO 2 in deionized water, fully stirred evenly, and then placed in a 100mL hydrothermal kettle, and reacted for 48h at a reaction temperature of 80°C, thereby preparing a catalyst precursor with a pH value of 8-11.

[0056] Step b1, adding 20 mL of sodium lactate to the catalyst precursor for intercalation reaction, the reaction temperature is 70° C., and the reaction time is 24 h, so as to prepare a catalyst precursor for intercalation organic matter.

[0057] Step c1. Add 20 mL of deionized water to the catalyst precursor of the intercalated organic matter, place it in a high-speed centrifuge, and centrifuge it at a speed of 6000 r / min for 30 min to remove solids, thereby preparing a stripping solution.

[0058] Step d1, us...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano-scale intercalation hydrotalcite catalyst and its preparation method and application. The soluble salt with catalytic activity and the soluble salt of a trivalent metal are mixed with an alkaline substance so that the pH value of the mixed solution is 7-13. , and react at a reaction temperature of 60-160°C for 6-48 hours to obtain a catalyst precursor with a pH value of 7-13; add macromolecular organics to the catalyst precursor for intercalation, thereby obtaining an intercalation The catalyst precursor of the organic matter; the catalyst precursor of the intercalated organic matter is stripped to obtain a stripping liquid; the stripping liquid is reduced by a reducing gas to obtain a nanoscale intercalated hydrotalcite catalyst. The invention has high selectivity to acetaldehyde, can catalytically convert synthesis gas into acetaldehyde, and has high conversion rate, simple preparation method and easy operation, can greatly reduce raw material cost for preparing acetaldehyde, and has good industrial application prospect.

Description

technical field [0001] The invention relates to the technical field of synthesis gas conversion and utilization, in particular to a nano-scale intercalated hydrotalcite catalyst and its preparation method and application. Background technique [0002] Acetaldehyde is a low-boiling organic compound soluble in water and organic solvents. It can be condensed with formaldehyde to generate pentaerythritol, and can be condensed and hydrolyzed with cyanide ions and ammonia to synthesize alanine, which can be used to produce acetic acid, ethanol, and ethyl acetate. It can be used to synthesize pesticide DDT, can be used to prepare sleeping pills with chloral as the main component, and can also be used to prepare food additive potassium sorbate. There are following several methods for preparing acetaldehyde in the prior art: [0003] (1) Chinese patent application CN201210349547.3 discloses a catalyst for the direct dehydrogenation of ethanol to prepare acetaldehyde; the catalyst is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/75B01J31/28B01J37/10B01J37/18C07C45/50C07C47/06B82Y30/00B82Y40/00