A kind of marbled silica gel and preparation method thereof

A technology of marble and texture, applied in the field of marble texture silica gel and its preparation, can solve the problems of complex coloring and single color, and achieve the effect of simple operation, clear and natural texture, and easy realization

Active Publication Date: 2021-02-05
FOSHAN DRAGON TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of the shortcomings of the above-mentioned prior art, the purpose of the present invention is to provide a marbled silica gel and its preparation method, aiming to solve the problem of single color and complex coloring of silica gel products in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of marbled silica gel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] A preferred method of marble-textured silica gel, including a texture rubber material and a ground color rubber material, the ratio of the texture rubber material to the ground color rubber material is 5.5:100;

[0070] Wherein, the texture rubber material includes by weight:

[0071] Silicone rubber raw material 1000 parts;

[0072] Silicone masterbatch #1924 5.15 parts;

[0073] Silicone masterbatch #1801 0.75 parts;

[0074] Silicone masterbatch #1807 2.14 parts;

[0075] Described base color rubber material is calculated by weight:

[0076] Silicone rubber raw material 1000 parts;

[0077] Silicone masterbatch #1924 6 parts.

[0078] The preparation steps of the marble texture silica gel include: refining the texture rubber material and the background color rubber material, taking the corresponding silicone rubber raw material and placing it on the open mill, adjusting the roller distance to 18mm and kneading for 3 minutes, and mixing the above-mentioned color ...

Embodiment 2

[0083] A kind of silica gel with marble texture, including texture rubber material and base color rubber material, the proportion of texture rubber material and base color rubber material is 10:100;

[0084] Wherein, the texture rubber material includes by weight:

[0085] Silicone rubber raw material 800 parts;

[0086] Silicone masterbatch #1924 2.0 parts;

[0087] Silicone masterbatch #1807 1.0 parts;

[0088] Described base color rubber material is calculated by weight:

[0089] Silicone rubber raw material 800 parts;

[0090] Silicone masterbatch #1807 3.0 parts.

[0091] The preparation steps are the same as those in Example 1, only when mixing the texture rubber and the base color rubber, the material is taken according to the ratio of the texture rubber and the base color rubber to 10:100.

[0092] Through this invention, it is possible to obtain marble-like silica gel products with white lines and black background.

Embodiment 3

[0094] A marble texture silica gel, comprising a texture rubber material and a ground color rubber material, the ratio of the texture rubber material to the ground color rubber material is 2.5:100;

[0095] Wherein, the texture rubber material includes by weight:

[0096] Silicone rubber raw material 1200 parts;

[0097] Silicone color masterbatch #1924 6.0 parts;

[0098] Silicone masterbatch #1102 3.5 parts;

[0099] Silicone masterbatch #1104 1.5 parts;

[0100] Described base color rubber material is calculated by weight:

[0101] Silicone rubber raw material 1200 parts;

[0102] Silicone masterbatch #1924 9 parts.

[0103] The preparation steps are the same as those in Example 1, only when mixing the texture rubber and the base color rubber, the material is taken according to the ratio of the texture rubber and the base color rubber as 2.5:100.

[0104] Through this invention, it is possible to obtain marble-like silica gel products with red lines and white backgrou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a silica gel with a marble pattern, which comprises a pattern rubber material and a background color rubber material. The mass ratio of the texture rubber material to the background color rubber material is 2.5 to 10.0:100, and the texture rubber material includes in parts by weight : 800-1200 parts of silicone rubber raw materials, 7-11 parts of silica gel color masterbatch A, the base color rubber material includes by weight: 800-1200 parts of silica gel raw materials, 5-9 parts of silica gel color masterbatch B; The method of adding color masterbatch in the production process is used to refine the texture rubber and the background color rubber respectively, so as to form a natural and clear marble texture. The method of the invention is simple and easy, solves the problems of single color and complex coloring of the silica gel, and makes the silica gel products more widely used.

Description

technical field [0001] The invention relates to the field of silica gel, in particular to a marbled silica gel and a preparation method thereof. Background technique [0002] Silica gel has the characteristics of high and low temperature resistance, weather resistance, insulation, non-toxic environmental protection and physiological inertness, and has been widely used in the fields of electronics, aviation, aerospace, automobiles, machinery, medical and health care, etc. At present, most of the silica gel products on the market are white, transparent or monochromatic products. With the improvement of living standards, people's demand for silicone rubber products is increasing. On the other hand, the requirements for the color and pattern of silicone rubber products are becoming more and more diverse. . In order to meet people's needs, the way of coloring is often used to make silica gel have various colors. The currently used coloring methods include adding color paste in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L83/04
CPCC08L83/04
Inventor 熊道武魏新安
Owner FOSHAN DRAGON TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com