Unlock instant, AI-driven research and patent intelligence for your innovation.

Blue glass product

A glass product and blue technology, applied in the field of blue glass products, can solve the problems of large production limitations, unstable material quality and color, poor product quality, etc., to achieve high economic and social benefits, and good market development. Space, the effect of reducing product cost

Inactive Publication Date: 2019-03-22
李明
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although sprayed glass products are colorful from the outside, they lose the transparency of the glass, which hinders people's visual senses and lacks a refreshing feeling. The original ecological colored glass products are not only crystal clear from the outside to the inside It is thorough, and gives people a fresh and simple feeling, which makes people feel particularly comfortable, especially the sky blue glass products, which are delicate and tender in texture, and give people a sense of depth like a vast blue sky. Glass products with high market demand potential
In addition, the previous production adopts the crucible furnace production process, which belongs to intermittent production. Not only the output is low, but also restricted by the production process, the material quality and color are extremely unstable, the product quality is poor, and the production limitations are large. Therefore, no matter the output or quality far from meeting the needs of the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blue glass product
  • Blue glass product
  • Blue glass product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A kind of blue glass product, the glass product that is made by glass raw material and colorant raw material, the composition and weight part of glass raw material are as follows:

[0046]

[0047] The composition and parts by weight of colorant raw materials are as follows:

[0048] Copper oxide with 99% CuO content 0.4-1.0%

[0049] Composite colorant 0.0-1%

[0050] The composite coloring agent is one or both of cobalt oxide and chromium oxide.

[0051] The manufacturing process of blue glass products includes the following steps:

[0052] S1. After mixing the glass raw material and the colorant raw material evenly, melt them;

[0053] S2. Add the mixed material into the pool kiln, control the hot spot temperature of the melting furnace to be 1520-1580°C, and the atmosphere in the material blanket area in the melting furnace is a reducing atmosphere (the material blanket area refers to the glass batch that has not yet been released after entering the melting fu...

Embodiment 2

[0056] A kind of blue glass product, the glass product that is made by glass raw material and colorant raw material, the composition and weight part of glass raw material are as follows:

[0057]

[0058] The composition and parts by weight of colorant raw materials are as follows:

[0059] Copper oxide with 99% CuO content 0.4-1.0%

[0060] Composite colorant 0.0-1%

[0061] The composite coloring agent is one or both of cobalt oxide and chromium oxide.

[0062] The manufacturing process of blue glass products includes the following steps:

[0063] S1. After mixing the glass raw material and the colorant raw material evenly, melt them;

[0064] S2. Put the mixed material into the electric melting furnace and melt it completely, then flow into the homogenization tank for homogenization, and finally pour it;

[0065] The operating parameters of the electric furnace are as follows:

[0066]

[0067] The parameters of the homogenization pool are as follows:

[0068] ...

Embodiment 3

[0070] The composition and parts by weight of glass raw materials are as follows:

[0071]

[0072] The composition and parts by weight of coloring agent raw material are as follows:

[0073]Copper oxide with 99% CuO content 0.4-1.0%

[0074] Composite colorant 0.0-1%

[0075] The composite coloring agent is one or both of cobalt oxide and chromium oxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a blue glass product. The blue glass product is characterized by being prepared from glass raw materials and colorant raw materials, wherein the glass raw materials comprise components by weight as follows: 71%-76% of quartz sand containing 99% of SiO2, 1%-4% of aluminium hydroxide containing 65% of Al2O3, 13%-16% of soda ash containing 57% of Na2O and 5%-10% of calcite containing 56% of CaO; the colorant raw materials comprise components by weight as follows: 0.4%-1.0% of copper oxide containing 99% of CuO and 0.0-1% of a compound colorant. The blue glass product is smooth on surface, fine and tender in luster and deep in color, the volatilization quantity of the colorant is small, product quality is guaranteed, and the production cost is reduced greatly.

Description

technical field [0001] The invention relates to the technical field of glass products, in particular to a blue glass product. Background technique [0002] In recent years, with the continuous improvement of people's living standards, quality of life, and pursuit of life, the requirements for the use of glass products are also getting higher and higher. People's demand for glass products is not limited to its use function, but more importantly, it is to pursue a taste of life and enjoy the beauty of colorful glass products in daily consumption. Therefore, in order to continuously meet people's increasing living needs, there has been a spraying treatment of various colors of environmentally friendly water-based paints on the appearance of glass products, that is, sprayed glass products. [0003] Although sprayed glass products are colorful from the outside, they lose the transparency of the glass, which hinders people's visual senses and lacks a refreshing feeling. The origi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine