A kind of electromagnetic ultrasonic brazing method for sic ceramics

A technology of electromagnetic ultrasonic and brazing method, applied in the field of SiC ceramic welding, can solve problems such as large residual stress of joints, cracking of base materials, and difficulty in low-temperature connection, and achieve the effects of low production cost, improved joint strength, and improved comprehensive mechanical properties.

Active Publication Date: 2021-09-07
NORTHEAST GASOLINEEUM UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide an electromagnetic ultrasonic brazing method for SiC ceramics, which is used to solve the existing SiC ceramic brazing joints, low temperature connection difficulties, joint residual stress Yamato base metal cracking and other problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of electromagnetic ultrasonic brazing method for sic ceramics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This electromagnetic ultrasonic brazing method for SiC ceramics includes the following steps:

[0026] Step 1, the width of the solder foil 2 is processed to be completely consistent with the width and size of the SiC ceramic 6; the solder foil 2 is a Sn-Zn-Ti-Al foil.

[0027] Step 2: Grinding the surfaces of the solder foil 2 and the SiC ceramic 6 with sandpaper, and cleaning with acetone for 10-30 min.

[0028] Step 3. Fill the solder foil 2 processed in step 2 between the two surfaces of the SiC ceramics 6 to be welded, so that the two SiC ceramics 6 are horizontally placed side by side, and another solder foil 2 is horizontally placed between the two surfaces. on the upper edge of each surface to be welded, and put them in the muffle furnace, set it directly above the heating device 1, raise the temperature to 100 °C at a rate of 10 °C / min and keep it for 8 minutes, and then set it in the vertical direction In the static magnetic field, the permanent magnet 3 and ...

Embodiment 2

[0030] This electromagnetic ultrasonic brazing method for SiC ceramics includes the following steps:

[0031] Step 1, the width of the solder foil 2 is processed to be completely consistent with the width and size of the SiC ceramic 6; the solder foil 2 is a Sn-Zn-Ti-Al foil.

[0032] Step 2: Grinding the surfaces of the solder foil 2 and the SiC ceramic 6 with sandpaper, and cleaning with acetone for 10-30 min.

[0033] Step 3. Fill the solder foil 2 processed in step 2 between the two surfaces of the SiC ceramics 6 to be welded, so that the two SiC ceramics 6 are horizontally placed side by side, and another solder foil 2 is horizontally placed between the two surfaces. on the upper edge of each surface to be welded, and put them in the muffle furnace, set it directly above the heating device 1, raise the temperature to 400 °C at a rate of 30 °C / min and keep it for 10 minutes, and then set it in the vertical direction In the static magnetic field, the permanent magnet 3 and...

Embodiment 3

[0035] This electromagnetic ultrasonic brazing method for SiC ceramics includes the following steps:

[0036] Step 1, the width of the solder foil 2 is processed to be completely consistent with the width and size of the SiC ceramic 6; the solder foil 2 is a Sn-Zn-Ti-Al foil.

[0037] Step 2: Grinding the surfaces of the solder foil 2 and the SiC ceramic 6 with sandpaper, and cleaning with acetone for 10-30 min.

[0038] Step 3. Fill the solder foil 2 processed in step 2 between the two surfaces of the SiC ceramics 6 to be welded, so that the two SiC ceramics 6 are horizontally placed side by side, and another solder foil 2 is horizontally placed between the two surfaces. on the upper edge of each surface to be welded, and put them in the muffle furnace, set it directly above the heating device 1, raise the temperature to 260 °C at a rate of 20 °C / min and keep it for 5 minutes, and then set it in the vertical direction In the static magnetic field, the permanent magnet 3 and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an electromagnetic ultrasonic brazing method for SiC ceramics, comprising: processing the width of the brazing material foil to be completely consistent with the width and size of the SiC ceramics; grinding and cleaning the surfaces of the brazing material foil and the SiC ceramics; Fill the processed solder foil between the two surfaces to be welded of SiC ceramics, place the two SiC ceramics horizontally side by side, place another piece of solder foil horizontally on the upper edges of the two surfaces to be welded, And put it in the muffle furnace, after heating up, then set it in the static magnetic field in the vertical direction, the permanent magnet and the coil are located directly above the solder foil placed horizontally, the static magnetic field is generated by the superconducting magnet, in the solder foil Current is applied to both ends, and pressure is applied to both ends of SiC ceramics at the same time, and the SiC ceramics are brazed after being cooled to room temperature with the furnace. The present invention adopts the electromagnetic ultrasonic method, without the ultrasonic tool head, and the ultrasonic application does not directly contact the SiC ceramics, so the SiC ceramics will not be cracked by ultrasonic vibration.

Description

Technical field: [0001] The invention relates to the field of SiC ceramic welding, in particular to an electromagnetic ultrasonic brazing method for SiC ceramics. Background technique: [0002] Due to its small thermal expansion coefficient, good wear resistance, and stable chemical properties, SiC ceramics have been widely used in aviation, aerospace, petroleum, and chemical industries. The sintering technology for preparing SiC ceramic materials has also become mature, but the yield of complex and large components for preparing SiC ceramics is still very low. Therefore, the industry often adopts the method of welding small-sized SiC ceramics to form large components. [0003] Brazing is a potential technology to realize the connection of small-sized SiC ceramics. One of the main problems in the brazing connection process of SiC ceramics is the problem of interfacial wetting and bonding. The physical and chemical properties of SiC ceramics and metal solders are very differ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B37/00
Inventor 马志鹏张茗瑄王晓冬李昊宣于心泷于海洋
Owner NORTHEAST GASOLINEEUM UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products