Baffle plate material for absorption tower of desulfurization and denitrification device

A desulfurization, denitrification, and absorption tower technology, applied in the field of baffles, can solve the problems of not meeting actual production requirements, complex raw material ratio, general corrosion resistance, etc., and achieve easy processing, long service life, and improved corrosion resistance. Effect

Inactive Publication Date: 2019-06-18
江苏赛尔亚环保科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing baffle materials for absorption towers used in desulfurization and denitrification devices have general material properties, common problems such as complex raw material ratios, insufficient overall strength, general corrosion resistance, and high processing costs, which do not meet actual production requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The present invention will be further described below in conjunction with embodiment.

[0012] The baffle material for the absorption tower of a desulfurization and denitrification device according to the present invention, in parts by weight, comprises:

[0013] (1) 73 parts of alloy steel;

[0014] (2) 29 parts of manganese;

[0015] (3) 18 parts of rock particles;

[0016] (4) 14 parts of 1-2 mesh rhodium fiber filaments;

[0017] (5) 2 parts of zirconium silicate.

[0018] The present invention makes the finished material excellent in performance through accurate raw material proportioning, and the proportioning is simple, adopts 1-2 purpose rhodium fiber filaments, effectively improves the use strength of the product, adopts rock particles and zirconium silicate, can greatly improve the durability of the product Corrosive, this product has a long service life, reliable operation, easy processing, and meets the actual production requirements.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a baffle plate material for an absorption tower of a desulfurization and denitrification device. The baffle plate material comprises the following components of, in parts by weight, 60-79 parts of alloy steel, 24-37 parts of manganese, 13-21 parts of rock particles, 5-18 parts of 1-2-mesh rhodium fiber yarns and 1-3 parts of zirconium silicate. The baffle plate material has the advantages of being excellent in performance, high in strength and resistant to corrosion.

Description

technical field [0001] The invention relates to a baffle, in particular to a baffle material. Background technique [0002] The existing baffle materials for absorption towers used in desulfurization and denitrification devices have general material properties, common problems such as complex ratio of raw materials, insufficient overall strength, general corrosion resistance, and high processing costs, which do not meet actual production requirements. Contents of the invention [0003] Purpose of the invention: the purpose of the invention is to overcome the deficiencies in the prior art and provide a baffle material with excellent performance, high strength and corrosion resistance for the absorption tower of the desulfurization and denitrification device. [0004] Technical solution: In order to solve the above technical problems, a baffle material for an absorption tower for a desulfurization and denitrification device according to the present invention comprises, in pa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C49/08C22C49/14
Inventor 曹国中
Owner 江苏赛尔亚环保科技有限公司