Copolyamide industrial yarn and preparation method thereof
A technology of copolyamide and industrial yarn, which is applied in the direction of single-component polyamide rayon, rayon manufacturing, filament/thread forming, etc., which can solve the problem of low wear resistance and chemical resistance of polyester industrial yarn and increase production Cost, complex production process and other issues, to achieve low heat shrinkage performance, improve breaking strength, increase the effect of drafting ratio
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0072] Example 1
[0073] The copolyamide industrial yarn of this embodiment is obtained by polymerizing raw materials including monomers and additives. The monomers are composed of 1,5-pentanediamine, terephthalic acid and adipic acid. The mass content of diamine is 40%, the mass content of terephthalic acid is 25%, and the mass content of adipic acid is 35%; the additive is antioxidant 1010.
[0074] The preparation method of the copolyamide industrial yarn of this embodiment includes the following steps:
[0075] 1. Prepare the mixed solution
[0076] Under nitrogen conditions, mix 1.32kg of 1,5-pentanediamine, 0.817kg of terephthalic acid, 1.16kg of adipic acid, 3.3kg of water and antioxidant 1010 in the polymerizer, and use a small amount of pentanediamine to adjust The pH value is 8.0 to obtain a mixed solution; wherein, the total concentration of monomers in the mixed solution is 50 wt%, and the content of antioxidant 1010 is 50 ppm.
[0077] 2. Preparation of copolyamide melt ...
Example Embodiment
[0087] Example 2
[0088] The copolyamide industrial yarn of this embodiment is obtained by polymerizing raw materials including monomers and additives. The monomers are composed of 1,5-pentanediamine, terephthalic acid and adipic acid. The mass content of diamine is 40%, the mass content of terephthalic acid is 31%, and the mass content of adipic acid is 29%; the additive is copper acetate.
[0089] The preparation method of the copolyamide industrial yarn of this embodiment includes the following steps:
[0090] 1. Prepare the mixed solution
[0091] Under nitrogen conditions, mix 1.31kg of 1,5-pentanediamine, 1.02kg of terephthalic acid, 0.971kg of adipic acid, 3.3kg of water and copper acetate in a polymerizer, and use a small amount of pentanediamine to adjust the pH Is 8.0 to obtain a mixed solution; wherein the total concentration of monomers in the mixed solution is 50% by weight, and the content of copper acetate is 0.5%.
[0092] 2. Preparation of copolyamide melt
[0093] He...
Example Embodiment
[0102] Example 3
[0103] The copolyamide industrial yarn of this embodiment is obtained by polymerization of raw materials including monomers and additives. The monomers are composed of 1,5-pentanediamine, terephthalic acid and dodecanedicarboxylic acid. The mass content of 5-pentanediamine is 35%, the mass content of terephthalic acid is 37%, and the mass content of dodecanedioic acid is 28%; the additive is sodium hypophosphite.
[0104] The preparation method of the copolyamide industrial yarn of this embodiment includes the following steps:
[0105] 1. Prepare the mixed solution
[0106] Under nitrogen conditions, mix 1.4kg of 1,5-pentanediamine, 1.47kg of terephthalic acid, 1.09kg of dodecanedioic acid, 2.64kg of water and sodium hypophosphite in the polymerizer and use a small amount of The amine adjusts the pH to 7.8 to obtain a mixed solution; wherein the total concentration of monomers in the mixed solution is 60 wt%, and the content of sodium hypophosphite is 80 ppm.
[010...
PUM
Property | Measurement | Unit |
---|---|---|
Breaking strength | aaaaa | aaaaa |
Melting point | aaaaa | aaaaa |
Melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology