Flame-retardant polyether type polyurethane elastomer with high tear strength

A polyurethane elastomer and polyether polyurethane technology, applied in the field of polymer elastomer materials, can solve the problems of simple start-up process, difficulty in achieving production efficiency and quality, and achieve the effect of soft hand feeling, low hardness and increased stability

Inactive Publication Date: 2019-07-09
中广核高新核材科技(苏州)有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when many customers tried polyurethane elastomers to make wires and cables, they found that the start-up process was far less simple than PVC and low-smoke halogen-free polyolefins. Many cable manufacturers using polyurethane elastomers used special equipment and special molds, otherwise it would be very difficult Difficult to achieve both production efficiency and quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant polyether type polyurethane elastomer with high tear strength

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1~3

[0027] Embodiments 1 to 3: A flame-retardant polyether polyurethane elastomer with high tear resistance, consisting of the following components by weight, as shown in Table 1:

[0028] Table 1

[0029] Example 1 Example 2 Example 3 Polyether polyurethane elastomer / part 55 52 50 Ethylene-butyl acrylate copolymer / part 14 15 12 Ethylene-methyl methacrylate copolymer / part 9 8 10 Maleic anhydride / part 2 3 2.5 Double 25 / set 0.5 0.8 1 Aluminum diethylphosphinate / part 4.6 5.1 5 Piperazine Phosphate / part 19.4 21 20 Compton 445 / part 0.2 0.25 0.18 US Dover S-9228 / copy 0.3 0.25 0.35 Rhine polymerized carbodiimide / part 1.5 1.4 1.6 Antioxidant / part 0.5 0.4 0.7

Embodiment 1

[0030] In the polyether polyurethane elastomer of Example 1, the polyether polyol is polyethylene glycol, and the antioxidant is a compound of an amine antioxidant and a high molecular weight phosphite antioxidant, and the compounding weight ratio is 2:3, the amine antioxidant is 4,4'-bis(phenylisopropyl)diphenylamine, and the high molecular weight phosphite antioxidant is bis(2,4-dicumylphenyl)pentaerythritol disulfide Phosphate.

Embodiment 2

[0031] In the polyether polyurethane elastomer of Example 2, the polyether polyol is polytetrahydrofuran ether glycol, and the antioxidant is a compound of an amine antioxidant and a high molecular weight phosphite antioxidant, and the compounding weight ratio is is 2:4,

[0032] The amine antioxidant is 4,4'-di(phenylisopropyl)diphenylamine, and the high molecular weight phosphite antioxidant is bis(2,4-dicumylphenyl)pentaerythritol diphosphite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant polyether type polyurethane elastomer with high tear strength. The flame-retardant polyether type polyurethane elastomer consists of the following componentsin parts by weight: 48-58 parts of polyether type polyurethane elastomer, 12-15 parts of ethylene-butyl acrylate copolymer, 8-10 parts of ethylene-methyl methacrylate copolymer, 1.5-4.5 parts of maleic anhydride, 0.4-1.2 parts of 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane, 4.5-5.1 parts of aluminum diethylphosphinate, 19-22 parts of piperazine phosphate, 0.1-0.3 part of Compton 445, America DoverS-9228, Lanxess polymeric carbodiimide, and an antioxidant, wherein polyether polyol in the polyether type polyurethane elastomer is one of polyethylene glycol or polytetrahydrofuran ether glycol. The flame-retardant polyether type polyurethane elastomer with high tear strength has the characteristics of bending resistance, distortion resistance, fatigue resistance, soft hand feeling and the like, and the characteristics are just the characteristics required by wind energy cables and mobile cables of electric vehicle charging piles, and the hardness can reach 75 to 80 A, the tear strength isgreater than or equal to 45 N / mm.

Description

technical field [0001] The invention relates to the technical field of polymer elastomer materials, in particular to a flame-retardant polyether polyurethane elastomer with high tear resistance. Background technique [0002] TPU is a polymer material formed by co-polymerizing diisocyanate molecules such as diphenylmethane diisocyanate (MDI) or toluene diisocyanate (TDI) with macromolecular polyols and low molecular polyols (chain extenders). Its molecular structure is a rigid block obtained by reacting diphenylmethane diisocyanate (MDI) or toluene diisocyanate (TDI) with a chain extender and diisocyanates such as diphenylmethane diisocyanate (MDI) or toluene diisocyanate (TDI) Molecules and macromolecular polyols react to form flexible segments alternately. TPU has excellent characteristics of high tension, high tensile strength, toughness and aging resistance, and has been widely used in medical and health care, electronic appliances, industry and sports, etc. Wear resist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08L23/08C08K5/14C08K5/5313C08K5/18C08K5/527H01B3/30
CPCC08L75/08H01B3/302C08L2201/02C08L2201/08C08L2203/202C08L2205/025C08L2205/03C08L23/0869C08K5/14C08K5/5313C08K5/18C08K5/527
Inventor 唐伟
Owner 中广核高新核材科技(苏州)有限公司