Low magnetic trace rate round steel, crankshaft forging and manufacturing method thereof

A manufacturing method and technology of round steel, applied in the crankshaft and other directions, can solve the problems of difficult control of non-quenched and tempered crankshaft magnetic marks, crankshaft scrapping, and reduced crankshaft fatigue life, etc., to achieve band structure reduction, tensile strength enhancement, The effect of improving the qualified rate of products

Active Publication Date: 2021-07-20
BAOSTEEL SPECIAL STEEL SHAOGUAN CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The round steel is forged into a crankshaft blank, and the crankshaft is obtained after finishing the crankshaft blank. Magnetic particle inspection is carried out on the surface of the crankshaft. If there are magnetic defects on the surface of the crankshaft, the fatigue life of the crankshaft will be significantly reduced, and the crankshaft will be scrapped.
[0003] In the prior art, it is very difficult to control the magnetic traces of the non-quenched and tempered crankshaft, and it is difficult to stably control the magnetic trace rate within 2%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low magnetic trace rate round steel, crankshaft forging and manufacturing method thereof
  • Low magnetic trace rate round steel, crankshaft forging and manufacturing method thereof
  • Low magnetic trace rate round steel, crankshaft forging and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

experiment example

[0069] The composition of round steel with low magnetic trace rate is shown in Table 1.

[0070] The composition (weight / %) of the round steel of table 1 low magnetic trace rate

[0071] C Si mn P S Mo V Cr Al N Ceq Example 1 0.46 0.26 1.08 0.015 0.004 0.01 0.07 0.18 0.011 0.0124 0.87 Example 2 0.49 0.25 1.14 0.012 0.005 0.01 0.08 0.17 0.009 0.0118 0.92 Example 3 0.48 0.29 1.07 0.010 0.003 0.01 0.08 0.17 0.010 0.0133 0.90 Comparative example 1 0.51 0.26 1.18 0.016 0.003 0.01 0.07 0.18 0.012 0.0136 0.94 Comparative example 2 0.47 0.23 1.11 0.013 0.004 0.01 0.09 0.19 0.009 0.0127 0.91 Comparative example 3 0.46 0.28 1.09 0.009 0.002 0.01 0.08 0.20 0.013 0.0115 0.89

[0072]The main production process parameters of low magnetic trace rate round steel and crankshaft forgings are shown in Table 2,

[0073] Table 2 The main production process parameters of rou...

Embodiment 1

[0083] It can be seen from Example 1 that the composition of round steel satisfies C: 0.46-0.50%, Si: 0.20-0.30%, Mn: 1.05-1.15%, P≤0.020%, S≤0.035%, Cr≤0.25%, Mo≤ 0.05%, Al≤0.030%, V: 0.06-0.10%, N: 0.010-0.018%, Ceq: 0.87-0.92%; and the manufacturing method of the round steel satisfies the above conditions. The properties of the obtained round steel meet: tensile strength ≥ 850MPa, elongation A ≥ 17%, band structure ≤ 1.5, C segregation at the center of 4%, C segregation at the cross-section R / 2 of the round steel The value is 4.8%. Using it to prepare crankshaft forgings, the performance of the obtained crankshaft forgings meets: tensile strength ≥ 870MPa, elongation after forging ≥ 11%, metallographic structure includes ferrite and pearlite, does not contain bainite, and Brinell hardness is 240 -260HBW, magnetic trace rate is 1.1%.

[0084] As can be seen from Comparative Example 1, if the C content in the round steel is greater than 0.50%, the Mn content is greater than...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The application provides a round steel with a low magnetic trace rate, a crankshaft forging and a manufacturing method thereof, which belong to the technical field of crankshafts. Round steel includes: C: 0.46‑0.50%, Si: 0.20‑0.30%, Mn: 1.05‑1.15%, P≤0.020%, S≤0.035%, Cr≤0.25%, Mo≤0.05%, Al≤0.030%, V: 0.06‑0.10%, N: 0.010‑0.018%. Among them, carbon equivalent Ceq=C+Si / 6+Mn / 5+Cr / 4+1.5V, Ceq: 0.87‑0.92%, tensile strength of round steel ≥ 850MPa, elongation A ≥ 12%; band structure ≤2.0 level; the C segregation values ​​at R / 2 and the center of the cross-section of the round steel are all ≤10%. The round steel is used to prepare crankshaft forgings, which can reduce the magnetic trace rate of crankshaft forgings.

Description

technical field [0001] The present application relates to the technical field of crankshafts, in particular to a round steel with a low magnetic trace rate, a crankshaft forging and a manufacturing method thereof. Background technique [0002] Round steel is forged into a crankshaft blank, and the crankshaft is obtained after finishing the crankshaft blank. Magnetic particle inspection is performed on the surface of the crankshaft. If there are magnetic defects on the surface of the crankshaft, the fatigue life of the crankshaft will be significantly reduced, and the crankshaft will be scrapped. [0003] In the prior art, it is difficult to control the magnetic marks of the non-tempered crankshaft, and it is difficult to stably control the magnetic mark rate within 2%. Contents of the invention [0004] The purpose of this application is to provide a round steel with a low magnetic trace rate, a crankshaft forging and its manufacturing method, which can effectively reduce ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/12C22C38/06C22C38/24C22C38/22B22D11/115B22D11/12F16C3/06
CPCB22D11/115B22D11/1206C21D2211/005C21D2211/009C22C38/02C22C38/04C22C38/06C22C38/12C22C38/22C22C38/24F16C3/06
Inventor 刘年富黄铸铭周成宏钟芳华
Owner BAOSTEEL SPECIAL STEEL SHAOGUAN CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com