No-opening inner glaze of Ru porcelain wine bottle and preparation method thereof

A wine bottle and Ru porcelain technology, which is applied in the non-opening inner glaze of Ru porcelain wine bottle and its preparation field, can solve problems such as tire wall cracking and wine seepage, optimize the green body, improve anti-seepage performance, and realize anti-seepage seepage effect

Inactive Publication Date: 2020-01-10
汝州市宣和坊汝瓷有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In the case of long-term storage of Ru porcelain wine bottle, the liquid will penetrate into the carcass through the opening of the inner glaze wall, causing the carcass to expand due to moisture absorption. crack, eventually leading to seepage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A piece-free inner glaze for Ru porcelain wine bottle, the wine bottle includes a carcass and glaze attached to the inner surface of the carcass, the carcass is composed of the following components in parts by mass: Taomugou soil 25-35 parts, 45-55 parts of raising field soil, 15-25 parts of black cat soil, and the glaze is composed of the following components by mass: 18-25 parts of mica, 12-20 parts of agate stone, 2-6 parts of plant ash 25-35 parts of Ru spar, 1.5-3 parts of calcined sheep bone, 10-15 parts of medical stone, and 10-16 parts of calcite.

[0025] Preferably, the Taomugou soil includes the following components in parts by mass: 55-60 parts of silicon dioxide, 25-35 parts of aluminum oxide, 0.8-3 parts of iron trioxide, 0.15-0.3 parts of calcium oxide, and 0.08-3 parts of magnesium oxide. 0.25 parts, potassium oxide 0.5~1.5 parts, sodium oxide 0.05~0.15 parts.

[0026] Preferably, the field soil includes the following components in parts by mass: 58-66 ...

Embodiment 2

[0038] A Ru porcelain wine bottle with no cracked inner glaze. The wine bottle includes a carcass and glaze attached to the inner surface of the carcass. The carcass is composed of the following components in parts by mass: 30 parts of Taomugou soil, 50 parts of field soil, 20 parts of black cat soil, the glaze is composed of the following components in parts by mass: 22 parts of mica, 18 parts of agate stone, 4 parts of plant ash, 30 parts of Ru spar, calcined sheep bone 2 parts, medical stone 13 parts, calcite 11 parts.

[0039] Preferably, the Taomugou soil includes the following components in parts by mass: 55-60 parts of silicon dioxide, 25-35 parts of aluminum oxide, 0.8-3 parts of iron trioxide, 0.15-0.3 parts of calcium oxide, and 0.08-3 parts of magnesium oxide. 0.25 parts, potassium oxide 0.5~1.5 parts, sodium oxide 0.05~0.15 parts.

[0040] Preferably, the field soil includes the following components in parts by mass: 58-66 parts of silicon dioxide, 20-25 parts of ...

Embodiment 3

[0052] A kind of Ru porcelain wine bottle without open piece inner glaze, the wine bottle includes a carcass and a glaze attached to the inner surface of the carcass, the carcass is composed of the following components in parts by mass: 25 parts of Taomugou soil, 55 parts of field soil, 20 parts of black cat soil, the glaze is composed of the following components in parts by mass: 20 parts of mica, 20 parts of agate stone, 5 parts of plant ash, 30 parts of Ru spar, calcined sheep bone 2 parts, medical stone 10 parts, calcite 13 parts.

[0053] Preferably, the Taomugou soil includes the following components in parts by mass: 55-60 parts of silicon dioxide, 25-35 parts of aluminum oxide, 0.8-3 parts of iron trioxide, 0.15-0.3 parts of calcium oxide, and 0.08-3 parts of magnesium oxide. 0.25 parts, potassium oxide 0.5~1.5 parts, sodium oxide 0.05~0.15 parts.

[0054] Preferably, the field soil includes the following components in parts by mass: 58-66 parts of silicon dioxide, 20...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a no-opening inner glaze of Ru porcelain wine bottle and a preparation method thereof. The wine bottle comprises a blank and a glaze coated on the surface of the blank, the blank is composed of the following components in parts by mass: Mugou soil, Yangtian soil, Heimao soil, the glaze is composed of the following components in parts by mass: Mica, agate stone, plant ash, Ruspar, calcined sheep bone, medical stone, calcite. The Ru porcelain no-opening glaze wine bottle is prepared by the following preparation steps: preparation of a plain tire, preparation of a glaze, glazing and firing. The invention provides the prepared Ru porcelain no-opening glaze wine bottle and the preparation method thereof, wherein the expansion coefficient of the wine bottle blank and theglaze on the surface of the blank body are consistent, so that the inner surface of the wine bottle achieves the effects of no opening, no crack and leakage prevention.

Description

technical field [0001] The invention relates to the technical field of processing and preparation of Ru porcelain, in particular to a piece-free inner glaze of Ru porcelain wine bottle and a preparation method thereof. Background technique [0002] Ru porcelain is one of the five famous porcelains in China. It was named after it was produced in Ruzhou. It was first fired in the middle of the Tang Dynasty and became famous in the Northern Song Dynasty. Because of its simple and elegant shape, its glaze is like "after the rain, the sky is clear and the clouds are broken", "a thousand peaks are green and green", its soil is fine and moist, its body is like a Dong body, its glaze is thick and its sound is like an engine, bright but not dazzling, It has the characteristics of "pear skin, crab claws, and sesame flowers", and is praised by the world as "like jade, not jade, but better than jade", and was once designated as imperial porcelain. Ru porcelain is exquisite in craftsman...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B33/04C04B33/13C04B33/34C04B41/86
CPCC03C8/00C04B33/04C04B33/13C04B33/34C04B41/5022C04B41/86C04B2235/6562C04B2235/6567C04B2235/661
Inventor 杨云超仝利军
Owner 汝州市宣和坊汝瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com