A kind of bionic pearl oyster material and preparation method thereof

A technology of biomass and imitation pearls, applied in the field of composite materials, can solve the problems of flammability, loss of beautiful color on the surface, insufficient mechanical properties, etc., achieve simple preparation process, expand application fields, and increase the effect of photocatalysis

Active Publication Date: 2021-08-10
ZHEJIANG FORESTRY UNIVERSITY
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Defects of fiberboard, such as insufficient mechanical properties and hygroscopic expansion, will lead to a decrease in the dimensional stability of the wood, easy to be corroded by bacteria, easy to be polluted by organic matter and cause the surface to lose its beautiful color, and serious surface deterioration will occur after being exposed to ultraviolet rays. It is flammable when there is a fire source, which greatly limits the scope and field of use of fiberboard.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bionic pearl oyster material and preparation method thereof
  • A kind of bionic pearl oyster material and preparation method thereof
  • A kind of bionic pearl oyster material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for preparing wooden pearl oyster material, comprising the following steps:

[0029] S1: After pulverizing the wood fiber, with nano-CaCO 3 Dissolved together in distilled water to form a suspension, the mass ratio of the wood fiber: nanometer substance: distilled water is 1:5×10 -4 : 20; then the suspension is sent into the colloid mill at 2500rpm, and the suspension is obtained after 10h of processing, and then the suspension is sent into the disc grinder at 2500rpm to process 10h, to obtain nano-material-wood fiber Composite material suspension, the particle size of the nano-substance-wood fiber composite material suspension is 50-500nm; S2: the nano-suspension obtained in S1 is mixed with 3.632g / L NaCl, 0.113g / L NaCl 2 SO 4 , 0.332g / LNaHCO 3 , 0.328g / L MgCl 2 ·6H 2 O, 0.284g / L CaCl 2After uniform mixing with a mixed salt solution composed of 0.177g / L KCl, keep the reaction at 40°C for 60h to obtain a mineralized nano-lignofiber suspension, and pre-coo...

Embodiment 2

[0031] A method for preparing wooden pearl oyster material, comprising the following steps:

[0032] S1: After pulverizing the wood fiber, with nano-CaCO 3 Dissolved in distilled water together to form a suspension, the mass ratio of the wood fiber: nanometer substance: distilled water is 1:20:20; then the suspension is sent to a colloid mill with a rotation speed of 3000rpm, and the suspension is obtained after 5 hours of treatment liquid, and then the above-mentioned suspension was sent to a disc grinder with a rotating speed of 3000rpm for 5h to obtain a nano-material-wood fiber composite suspension, and the particle size of the nano-material-wood fiber composite suspension was 50 -500nm; S2: Mix the nanosuspension obtained in S1 with 3.632g / L NaCl, 0.113g / L NaCl 2 SO 4 , 0.332g / L NaHCO 3 , 0.328g / L MgCl 2 ·6H 2 O, 0.284g / L CaCl 2 After uniform mixing with a mixed salt solution composed of 0.177g / L KCl, keep the reaction at 60°C for 36h to obtain a mineralized nano-li...

Embodiment 3

[0034] A method for preparing wooden pearl oyster material, comprising the following steps:

[0035] S1: After pulverizing the wood fiber, with nano-CaCO 3 Dissolved in distilled water together to form a suspension, the mass ratio of the wood fiber: nanometer substance: distilled water is 1:0.02:20; then the suspension is sent to a colloid mill with a rotation speed of 2880rpm, and the suspension is obtained after 6 hours of treatment liquid, and then the above-mentioned suspension was sent to a disc grinder with a rotation speed of 2880rpm for 6h to obtain a suspension of nano-material-wood fiber composite material, and the particle size of the suspension liquid of nano-material-wood fiber composite material was 50 -500nm; S2: Mix the nanosuspension obtained in S1 with 3.632g / L NaCl, 0.113g / L NaCl 2 SO 4 , 0.332g / LNaHCO 3 , 0.328g / L MgCl 2 ·6H 2 O, 0.284g / L CaCl 2 After uniform mixing with a mixed salt solution composed of 0.177g / L KCl, keep the reaction at 50°C for 48h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a biomass pearl oyster material, which is characterized in that it comprises the following steps: S1: Using a thermal grinding method to evenly attach nano-materials to biomass fibers to prepare nano-material-biomass fiber composite materials Suspension; S2: The suspension obtained in S1 is used to generate a layered imitation pearl oyster structure matrix suspension by freezing casting method; S3: The organic polymer material is impregnated into the matrix suspension obtained in S2, and then obtained by hot pressing Wooden pearl oyster material. The preparation method of the invention is more environmentally friendly, and the prepared shell-like biomimetic layered material has higher mechanical strength and specific strength, and the functional group endows the material with new performance, so the application is very wide.

Description

technical field [0001] The invention relates to the field of composite materials, in particular to a bionic pearl oyster material and a preparation method thereof. Background technique [0002] In the long-term evolutionary process of nature, biological materials with perfect organizational structure and unique excellent properties have been formed, such as the gums of mammals, bones and shells of molluscs, etc., especially the pearl oyster layer in shells has outstanding mechanical properties And it has attracted much attention, such as the shell of abalone is mainly composed of CaCO 3 And a small amount of biological macromolecules, its hardness is ordinary CaCO 3 Twice that of crystal, toughness is ordinary CaCO 3 More than 1000 times of the crystal. These structures are mainly formed by using pre-organized templates formed by the self-assembly of organic macromolecules (proteins, polysaccharides, lipids, etc.), and depositing inorganic molecules on them through molecu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L97/02C08L33/12C08L23/06C08L29/04C08K3/00C08K3/26C08K3/36C08K3/16C08K3/30C08K3/22
CPCC08K2003/162C08K2003/166C08K2003/2241C08K2003/2275C08K2003/265C08K2003/3045C08K2201/011C08L97/02C08L33/12C08K3/00C08K3/26C08K3/16C08K3/30C08L23/06C08K3/36C08L29/04C08K3/22
Inventor 孙庆丰陈逸鹏党宝康
Owner ZHEJIANG FORESTRY UNIVERSITY