Warm-rolling composite rolling mill process lubricant and preparation method thereof

A compound rolling mill and lubricant technology, applied in lubricating compositions, petroleum industry, etc., can solve problems such as high friction force and poor lubrication effect, and achieve the effects of extending oil change period, reducing wear and reducing cost

Inactive Publication Date: 2020-04-03
OKUMTEC TECH WENZHOU CO LTD
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention proposes a warm-rolling compound rolling mill process lubricant and its preparation method to solve the shortcomings of poor lubrication effect and high friction in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A lubricant for warm rolling compound rolling mill, the formula is as follows in parts by weight: 100 parts of crude oil, 10 parts of additive, 3 parts of antioxidant, 4 parts of metal deactivator, 2 parts of anti-wear and anti-rust agent, and 1 part of catalyst.

[0026] The additives include pour point depressant, detergent and dispersant, extreme pressure agent and anticorrosion agent, and the content ratio of pour point depressant, detergent and dispersant, extreme pressure agent and anticorrosion agent is 1:1:1:2.

[0027] It has the characteristics of controlling friction, reducing wear, cooling and sealing, and at the same time reduces the cost of lubricating oil preparation and prolongs the oil change period of the equipment.

[0028] The present invention also provides a kind of preparation method of lubricating agent of warm-rolling composite rolling mill process, comprising the following steps:

[0029] S1. Preparation of base oil: crude oil is firstly distil...

Embodiment 2

[0041] A kind of lubricating agent for warm rolling compound rolling mill, the formula is as follows in parts by weight: 150 parts of crude oil, 15 parts of additive, 4 parts of antioxidant, 5 parts of metal deactivator, 3 parts of antiwear and antirust agent, and 2 parts of catalyst.

[0042] The additives include pour point depressant, detergent and dispersant, extreme pressure agent and anticorrosion agent, and the content ratio of pour point depressant, detergent and dispersant, extreme pressure agent and anticorrosion agent is 1:1:1:2.

[0043] It has the characteristics of controlling friction, reducing wear, cooling and sealing, and at the same time reduces the cost of lubricating oil preparation and prolongs the oil change period of the equipment.

[0044] The present invention also provides a kind of preparation method of lubricating agent of warm-rolling composite rolling mill process, comprising the following steps:

[0045] S1. Preparation of base oil: crude oil is...

Embodiment 3

[0057] A lubricant for warm-rolling compound rolling mills, the formula is as follows in parts by weight: 200 parts of crude oil, 30 parts of additives, 5 parts of antioxidant, 6 parts of metal deactivator, 5 parts of anti-wear and anti-rust agent, and 3 parts of catalyst.

[0058] The additives include pour point depressant, detergent and dispersant, extreme pressure agent and anticorrosion agent, and the content ratio of pour point depressant, detergent and dispersant, extreme pressure agent and anticorrosion agent is 1:1:1:2.

[0059] It has the characteristics of controlling friction, reducing wear, cooling and sealing, and at the same time reduces the cost of lubricating oil preparation and prolongs the oil change period of the equipment.

[0060] The present invention also provides a kind of preparation method of lubricating agent of warm-rolling composite rolling mill process, comprising the following steps:

[0061] S1. Preparation of base oil: crude oil is firstly dis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of lubricants and discloses a warm-rolling composite rolling mill process lubricant and a preparation method thereof. The warm-rolling composite rolling mill process lubricant comprises 100-200 parts of crude oil, 10-30 parts of an additive, 3-5 parts of an antioxidant, 4-6 parts of a metal deactivator, 2-5 parts of an anti-wear antirust agent and 1-3 parts of a catalyst, and the preparation process comprises preparation, blending and sub-packaging of base oil and storage. According to the invention, the characteristics of friction control, abrasionreduction, cooling and sealing isolation can be well achieved.

Description

technical field [0001] The invention relates to the technical field of lubricants, in particular to a process lubricant for warm-rolling composite rolling mills and a preparation method thereof. Background technique [0002] Lubricants are lubricating media used to reduce the friction resistance of friction pairs and slow down their wear. Lubricants can also cool, clean and prevent pollution for friction pairs. In order to improve the lubricating performance, suitable additives can be added to some lubricants. [0003] However, the existing lubricants on the market have the disadvantages of controlling friction, reducing wear, cooling and cooling, and poor sealing and isolation. Contents of the invention [0004] The invention proposes a warm-rolling composite rolling mill process lubricant and a preparation method thereof to solve the shortcomings of poor lubricating effect and high friction force in the prior art. [0005] The present invention proposes a kind of lubri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M169/04C10M177/00C10N30/06
CPCC10M169/042C10M177/00
Inventor 包仲南徐泷黄伟马德高陈昊玉晓波
Owner OKUMTEC TECH WENZHOU CO LTD