A kind of early-strength and corrosion-resistant C80 lightweight high-strength concrete and its preparation method

A high-strength concrete and corrosion-resistant technology, applied in the field of special concrete, can solve the problems of sulfate corrosion resistance, acid corrosion resistance, poor acid resistance, etc., to broaden the scope of application, improve toughness and consistency, and ensure overall performance and stability. Effect

Active Publication Date: 2022-04-01
中建西部建设新疆有限公司 +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Lightweight concrete is mostly used in exposed structures such as exterior walls and roofs, while conventional exterior coatings have poor acid resistance, and the concrete prepared with conventional Portland cement has poor sulfate and acid corrosion resistance; therefore, How to further formulate lightweight high-strength concrete with good corrosion resistance is particularly important

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of early-strength corrosion-resistant C80 lightweight high-strength concrete, its preparation method comprises the following steps:

[0037] 1) Weigh each raw material according to the ratio, each raw material and its dosage include: aluminate cement 490kg / m 3 , micro silica fume 250kg / m 3 , mineral powder 280kg / m 3 , glass beads 250kg / m 3 , sand 450kg / m 3 , Composite reinforced material 0.6kg / m 3 (The mass ratio of benzoic acid modified basalt fiber to calcium carbonate whisker is 80:20), admixture 20kg / m 3 , water 190kg / m 3 ;

[0038] 2) Mix the weighed aluminate cement, silica fume, mineral powder and glass microspheres to obtain a premixed cementitious material, dry mix the premixed cementitious material and sand, and then add water and additives Stir evenly, and finally add composite reinforcing materials to form fluid concrete with good workability, carry out moulding, leave the mold at 20°C for 24 hours, and then standardize for 28 days to obtain th...

Embodiment 2

[0041] A kind of ultra-early-strength corrosion-resistant C80 lightweight high-strength concrete, its preparation method comprises the following steps:

[0042] 1) Weigh each raw material according to the ratio, each raw material and its dosage include: aluminate cement 550kg / m 3 , micro silica fume 200kg / m 3 , mineral powder 285kg / m 3 , glass beads 180kg / m 3 , sand 450kg / m 3 , Composite reinforced material 0.8kg / m 3 (The mass ratio of benzoic acid modified basalt fiber to calcium carbonate whisker is 75:25), admixture 22kg / m 3 , water 200kg / m 3 ;

[0043] 2) Mix the weighed aluminate cement, silica fume, mineral powder and glass microspheres to obtain a premixed cementitious material, dry mix the premixed cementitious material and sand, then add water and admixtures to stir Uniform, finally add composite reinforcing materials to form fluid concrete with good workability, carry out moulding, let it stand at 20°C for 24 hours, then demould, and then standard curing for 2...

Embodiment 3

[0046] A kind of ultra-early-strength corrosion-resistant C80 lightweight high-strength concrete, its preparation method comprises the following steps:

[0047] 1) Weigh each raw material according to the ratio, each raw material and its dosage include: aluminate cement 600kg / m 3 , micro silica fume 200kg / m 3 , mineral powder 300kg / m 3 , glass beads 180kg / m 3 , sand 400kg / m 3 , Composite reinforced material 0.8kg / m 3 (The mass ratio of benzoic acid modified basalt fiber to calcium carbonate whisker is 70:30), admixture 22kg / m 3 , water 210kg / m 3 ;

[0048] 2) Mix the weighed aluminate cement, silica fume, mineral powder and glass microspheres to obtain a premixed cementitious material, dry mix the premixed cementitious material and sand, then add water and admixtures to stir Uniform, finally add composite reinforcing materials to form fluid concrete with good workability, carry out moulding, let it stand at 20°C for 24 hours, then demould, and then standard curing for 2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an early-strength and corrosion-resistant C80 lightweight high-strength concrete. The components and their contents include: aluminate cement 450-600kg / m 3 , composite mineral admixture 550‑900kg / m 3 , sand 250‑450kg / m 3 , composite reinforcement material 0.6‑1kg / m 3 , admixture 20‑25kg / m 3 , water 180‑220kg / m 3 , wherein the composite mineral admixture is composed of silica fume, mineral powder and glass beads. The early-strength and corrosion-resistant C80 lightweight high-strength concrete described in the present invention can further exhibit good fluidity, corrosion resistance and durability on the basis of effectively taking into account light weight and high strength performance, and the preparation method involved is simple and easy to operate. Convenient and suitable for promotion and application.

Description

technical field [0001] The invention belongs to the technical field of special concrete, and in particular relates to an early-strength and corrosion-resistant C80 lightweight high-strength concrete and a preparation method thereof. Background technique [0002] Lightweight high-strength concrete is prepared by using artificial high-strength lightweight coarse aggregate (ie high-strength ceramsite) or natural lightweight high-strength aggregate instead of ordinary aggregate, and its dry apparent density is not more than 1950kg / m 3 , Lightweight concrete for structures with a strength grade above LC30. Compared with ordinary concrete, it has the advantages of light weight, good earthquake resistance, good fire resistance, good durability and heat insulation. At the same time, because a large amount of industrial solid waste such as fly ash and silica fume is used in the production of lightweight aggregate and the preparation of lightweight aggregate concrete, it has importan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B111/40C04B111/20
CPCC04B28/06C04B2201/20C04B2111/20C04B2111/40C04B2201/50C04B18/146C04B18/141C04B14/22C04B14/06C04B14/4643C04B14/383C04B22/002C04B2103/302
Inventor 艾洪祥李凯张平王军陈旭卢霄苏温馨
Owner 中建西部建设新疆有限公司