A kind of modified polyamide desalination layer, reverse osmosis membrane and preparation method and application thereof
A technology of reverse osmosis membrane and polyamide, which is used in reverse osmosis, semi-permeable membrane separation, chemical instruments and methods, etc., to achieve the effects of easy industrial production, simple operation, and good oxidation resistance.
Active Publication Date: 2022-04-12
WANHUA CHEM GRP CO LTD
View PDF13 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0006] Although some technical schemes about improving anti-biofouling or / and oxidation resistance of reverse osmosis membranes have been formed in the prior art, these technical schemes still need to improve the anti-biofouling and oxidation resistance of reverse osmosis membranes while improving flux. further improvement
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1～9
[0072] The polysulfone support membrane was prepared by the method in Comparative Examples 1-3.
[0073] The aromatic polyamide desalination layer was prepared by the following steps:
[0074] (1) First prepare 500 g of aqueous solution containing m-phenylenediamine, then add (2-aminobenzyl) triphenylphosphine bromide and 5-amino-6-hydroxyl-flavone (additive) in the solution, stir at room temperature to make It dissolves completely, obtains the aqueous phase A solution containing (2-aminobenzyl) triphenylphosphine bromide and 5-amino-6-hydroxyl-flavone (wherein, embodiment 9 does not add (2-aminobenzyl ) triphenylphosphine bromide).
[0075] (2) Immerse the polysulfone porous support layer into the water phase A solution, remove the excess water phase on the surface, and then contact with 25 g of the trimesoyl chloride organic phase B solution to obtain a reverse osmosis membrane.
[0076]In Examples 1-9, the concentration and contact time of each substance in the aqueous ph...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| salt rejection rate | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a modified polyamide desalination layer, a reverse osmosis membrane and a preparation method and application thereof. The modified substance of the modified polyamide desalination layer includes monoaminohydroxyflavone. The invention uses monoamino hydroxyflavone to modify the polyamide desalting layer. The addition of the substance can not only endow the reverse osmosis membrane with good oxidation resistance, but also obtain the effect of improving the flux of the membrane. Adding (2-aminobenzyl) triphenylphosphine bromide in the preferred scheme can obtain a reverse osmosis membrane with anti-biological pollution, oxidation resistance and high flux, which can be further improved when applied to water treatment. Processing efficiency, reduce production cost.
Description
technical field [0001] The invention relates to the technical field of water treatment, in particular to a modified polyamide desalination layer, a reverse osmosis membrane and a preparation method and application thereof. Background technique [0002] Reverse osmosis membranes have been widely used in household water purifiers, industrial pure water manufacturing, wastewater treatment, and seawater desalination because of their high separation efficiency, low energy consumption, and less pollution. At present, the mainstream reverse osmosis membrane on the market is a cross-linked aromatic polyamide composite reverse osmosis membrane, which uses m-phenylenediamine and trimesoyl chloride to perform interfacial polycondensation reaction on the surface of polysulfone support membrane to form a polyamide desalination layer. After decades of technical improvements, the performance of reverse osmosis membranes has been significantly improved. [0003] However, in actual use, rev...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/68B01D69/02B01D69/10B01D67/00B01D61/02C02F1/44
CPCB01D71/68B01D69/02B01D69/10B01D67/0002B01D61/025C02F1/441B01D2325/28B01D2325/30Y02A20/131
Inventor 苏蕾孙家宽赵伟国
Owner WANHUA CHEM GRP CO LTD