Papermaking reinforcing agent and preparation method thereof
A papermaking strengthening agent and initiator technology, applied in the field of papermaking, can solve the problems of harsh preparation process, high usage, inconvenient actual use, etc., and achieve the effect of simple preparation method, good storage stability and mild reaction process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] The invention provides a preparation method of a papermaking reinforcing agent, comprising: S1) polymerizing a first cationic monomer, acrylamide and a second cationic monomer under the action of an initiator to obtain a base polymer; the first The cationic monomer and the second cationic monomer are both quaternary ammonium salt cationic monomers with different types; S2) after mixing the weakly basic catalyst with the base polymer in water, adjust the pH value to weakly basic, and then add glyoxal, stirring and reacting to obtain a papermaking strengthening agent.
[0026] Wherein, in the present invention, there is no special restriction on the source of the reaction raw materials, and it may be commercially available.
[0027] According to the present invention, the first cationic monomer and the second cationic monomer are both quaternary ammonium salt cationic monomers with different types, preferably each independently is a diallyl quaternary ammonium salt cation...
Example Embodiment
[0040] Example 1
[0041] 56.9g of distilled water and 18g of DAD were added to a 500ml round-bottomed flask equipped with a condenser tube, a stirrer, a nitrogen inlet and a feeding port, and 28.6g of acrylamide, 5g of BZ-80 and 0.4g of mass concentration were added dropwise after being passed through nitrogen for 30 minutes. A 10% aqueous solution of ammonium persulfate and sodium bisulfite was heated to 80°C and reacted for 5h. After cooling to room temperature, the base polymer 2 was obtained by precipitation with acetone and vacuum drying.
Example
[0042] Examples 2 to 4
[0043] The preparation method of base polymer 3~base polymer 5 is the same as that of embodiment 1, and the feeding formula is shown in Table 1.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap