Decorative material and preparation method thereof

A decorative material and decorative paper technology, applied in the field of decorative materials, can solve problems such as incapability of coating and modeling, inability to bend, high hardness, etc., and achieve the effects of bright colors, improved flexibility, and fast curing speed

Inactive Publication Date: 2020-11-20
GUANGDONG TIANAN NEW MATERIAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the decorative paper is impregnated with melamine resin glue, it can be used on the surface of wood-based panels after drying and cutting. It is wrapped and molded

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Decorative material and preparation method thereof
  • Decorative material and preparation method thereof
  • Decorative material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] The selection of embodiment 1 electron beam curing process parameter

[0062] a decorative material such as figure 1 As shown, it includes a decorative paper 1 and a coating that penetrates into the interior of the decorative paper and is cured, and the coating is polyurethane acrylate oligomer and alkoxylated phenol acrylate.

[0063] The preparation method of the decoration material of the present embodiment comprises the following steps:

[0064] (1) preparation viscosity is the primer of 15cps, and described primer is polyurethane acrylate oligomer and alkoxylated phenol acrylate, and the content of alkoxylated phenol acrylate in primer is 10wt%;

[0065] (2) Apply primer to 40g / m 2 The coating amount is applied to the lower surface of the decorative paper. The primer completely penetrates into the interior of the decorative paper and is cured by electron beams. After passing the inspection, the decorative material is obtained. The selected electronic curing proce...

Embodiment 2

[0069] Embodiment 2 surface paint viscosity selection

[0070] a decorative material such as figure 2 As shown, it includes decorative paper 1 and a coating that penetrates into the interior of the decorative paper and solidifies, and the coating is polyurethane acrylate oligomer and alkoxylated phenol acrylate; the upper surface of the decorative paper 1 is provided with a top coat 2, so The top coat 2 contains an acrylic resin.

[0071] The preparation method of the decoration material of the present embodiment comprises the following steps:

[0072] (1) preparation viscosity is the primer of 15cps, and described primer is polyurethane acrylate oligomer and alkoxylated phenol acrylate, and the content of alkoxylated phenol acrylate in primer is 10wt%;

[0073] (2) Apply primer to 40g / m 2 The coating amount is applied to the lower surface or upper surface of the decorative paper, and the primer is completely penetrated into the interior of the decorative paper and then cu...

Embodiment 3

[0082] Embodiment 3 surface coating amount of coating is selected

[0083] a decorative material such as figure 2 As shown, it includes a decorative paper 1 and a coating that penetrates into the interior of the decorative paper and solidifies, and the coating is acrylic novolak epoxy ester and trimethylolpropane triacrylate; the upper surface of the decorative paper 1 is provided with a top coat 2 , the top coat 2 contains acrylic resin.

[0084] The preparation method of the decoration material of the present embodiment comprises the following steps:

[0085] (1) preparation viscosity is the primer of 15cps, and described primer is acrylic novolac epoxy ester and trimethylolpropane triacrylate, and the content of trimethylolpropane triacrylate in primer is 10wt%;

[0086] (2) Apply primer to 40g / m 2 The coating amount is applied to the lower surface of the decorative paper, and the primer is completely infiltrated into the interior of the decorative paper and cured by el...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Coating amountaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a decorative material and a preparation method thereof. The decorative material comprises a plastic film, decorative paper and coating which penetrates into the decorative paper and cured, wherein the coating comprises at least one of acrylic epoxy ester, acrylic phenolic epoxy ester, polyurethane acrylate oligomer, polyester acrylate and active monomer, the plastic film isattached to the upper surface of the decorative paper, and the material of the plastic film comprises polypropylene. According to the decorative material disclosed by the invention, the occurrence ofa paper layering phenomenon is reduced in the using process, the decorative material does not need to be stored at a low temperature, has good flexibility, has no obvious cracking phenomenon after being bent, and can be subjected to flat pasting, cladding and modeling pasting treatment.

Description

technical field [0001] The invention relates to the technical field of decorative materials, in particular to a decorative material and a preparation method thereof. Background technique [0002] Wood-based panel is a kind of board made of wood or other non-wood plants as the main raw material after certain mechanical processing. Compared with solid wood panels, artificial panels have the advantages of large format, stable size, good structure and convenient construction. In order to improve the decorative effect of the artificial board, a decorative layer can be set on the surface of the artificial board, and the required pattern can be printed on the decorative layer, so that the board surface has various wood grains or patterns, bright and smooth and other decorative effects, and also has high Excellent heat resistance, cold resistance, wear resistance, moisture resistance and other properties. [0003] Both PVC film and decorative paper can be used as decorative materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C5/04D21H17/37D21H17/52D21H17/57D21H19/20D21H19/24D21H27/38B32B7/12B32B27/10B32B27/32B32B33/00
CPCB32B7/12B32B27/10B32B27/32B32B33/00B32B2255/10B32B2255/26B32B2307/558B32B2451/00B44C5/0469D21H17/37D21H17/52D21H17/57D21H19/20D21H19/24D21H27/38
Inventor 吴启超宋岱瀛周春发张华荣陈润娇徐芳谭嘉昇周子潇
Owner GUANGDONG TIANAN NEW MATERIAL