Iodophor permeation-resistant antibacterial artificial stone and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An artificial stone and iodophor technology, applied in the field of artificial stone, can solve the problems of difficult cleaning, thinning and denting of plates, shortened service life, etc.
Inactive Publication Date: 2021-02-05
广州戈兰迪新材料股份有限公司
View PDF6 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] Artificial stone (solid surface material) is mainly a plate formed by unsaturated resin or acrylic resin and aluminum powder (some manufacturers will use calcium powder), color paste, auxiliary materials, etc. under certain process conditions. Some thermal bending properties and surface visual effects have gradually entered the field of hospital decoration. Because of the special environment of the hospital, iodophor disinfectant is often used. Iodophor has strong permeability. Once the general home decoration solid surface is stuck, it is difficult to clean. For pure-color plates (without large particles), professional treatment such as re-grinding and polishing is required to restore them. Partial grinding and refurbishment will cause the plates to become thinner and sunken, and their service life will be shortened. The deeper it is, the harder it is to clean
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] A kind of embodiment of the antibacterial artificial stone of resistance to povidone-iodine penetration of the present invention, the preparation method of the antibacterial artificial stone of resistance to penetration of iodine described in the present embodiment comprises the following steps:
[0036] (4) Add aluminum powder to the resin slurry and stir evenly to obtain mixture B;
[0037] (5) Add a curing agent to the mixture B and stir evenly to obtain the slurry C;
[0038] (6) Pour the slurry C into the glass mold, and assist the scraping to make it level automatically;
[0039] (7) Push the mold with the slurry loaded into the vacuum box, and vacuumize for 5 minutes;
[0040] (8) Send the mold that has been evacuat...
Embodiment 2～3
[0047] Two kinds of embodiments of the antibacterial artificial stone of iodophor infiltration of the present invention, the preparation method of the antibacterial artificial stone of iodophor infiltration described in embodiment 2~3 is the same as embodiment 1, and embodiment 2~3 is resistant to iodophor The raw materials for preparing the infiltrated antibacterial artificial stone are shown in Table 1, and the raw materials for preparing the m-phenylene resin are shown in Table 2.
Embodiment 4
[0049] An embodiment of the antibacterial artificial stone resistant to povidone-iodine penetration of the present invention, the antibacterial artificial stone resistant to povidone-iodine penetration in this embodiment comprises the broken particles of the antibacterial artificial stone resistant to povidone-iodine penetration in Example 1. Its preparation method is as follows:
[0050] (1) the antibacterial artificial stone of resistance to povidone iodine infiltration prepared in embodiment 1 is broken, and artificial stone particles are prepared;
[0051] (2) Soak the artificial stone particles in KH570 for 24 hours and set aside;
[0052] (3) m-phenylene resin is mixed with promotor and defoamer, stirred evenly to obtain mixture A;
[0053] (4) Add antibacterial agent and dispersant in mixture A, stir evenly, obtain resin slurry;
[0054] (5) Add aluminum powder to the resin slurry and stir evenly to obtain mixture B;
[0055] (6) Add a thickener fumed silica to the m...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
technical field [0001] The invention relates to the technical field of artificial stone, in particular to an antibacterial artificial stone resistant to iodophor penetration and a preparation method thereof. Background technique [0002] Artificial stone (solid surface material) is mainly a plate formed by unsaturated resin or acrylic resin and aluminum powder (some manufacturers will use calciumpowder), color paste, auxiliary materials, etc. under certain process conditions. Some thermal bending properties and surface visual effects have gradually entered the field of hospital decoration. Because of the special environment of the hospital, iodophor disinfectant is often used. Iodophor has strong permeability. Once the general home decoration solid surface is stuck, it is difficult to clean. For pure-color plates (without large particles), professional treatment such as re-grinding and polishing is required to restore them. Partial grinding and refurbishment will cause the ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).