A kind of stone back rib glue and preparation method thereof
A technology of back reinforcement and stone, applied in the directions of adhesives, adhesive additives, polymer adhesive additives, etc., can solve the problems of affecting the appearance, long cement curing time, affecting construction, etc., and achieve the integration of toughening and shrinkage resistance, comprehensive mechanics Excellent performance and the effect of improving comprehensive mechanical properties
Active Publication Date: 2022-03-22
江苏大力士云石护理材料有限公司
View PDF4 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The cement curing time is long, which affects the construction, and at least one week of water curing time is required, so that the stone is prone to pathological changes in a humid environment, such as water spots, white blooms, wet marks, etc., which will affect the appearance; moreover, the cement should not be corroded by acid. The substance and the calcium hydroxide in the cement will undergo a neutralization reaction, and the volume of the product will be loose and swell, and it will be easily hydrolyzed and pulverized when it meets water, causing the steel bar to fall off
However, marble glue has the problems of large shrinkage rate and brittle performance after curing, and marble glue is usually a viscous paste, which is not easy to level in stone grooves, which is not conducive to construction
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0036] This embodiment provides a kind of stone back reinforcement, including A component and B component, in parts by weight, the composition of A component is as follows: 100 parts of unsaturated polyester resin, 10 parts of anti-shrinkage toughening agent, active carbonic acid 50 parts of calcium, 50 parts of active barium sulfate, 15 parts of silicon powder, 2 parts of polydimethylsiloxane and 3 parts of polyester modified dimethylsiloxane; the composition of component B is as follows: Benzyl peroxide 30 parts of dibutyl peroxybenzoate, 10 parts of tert-butyl peroxybenzoate, 20 parts of dibutyl phthalate, 20 parts of calcium stearate and 10 parts of zinc stearate;
[0037] Wherein, the preparation method of the anti-shrinkage toughening agent is as follows: (1) Methyl vinyl silicone rubber raw rubber and natural rubber raw rubber are mixed in a double-roller open mill for 2-3 hours at a weight ratio of 1:1, Mix the raw rubber fully and evenly, and control the temperature o...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention provides a stone back rib glue and a preparation method thereof. The stone back rib glue includes A component and B component, the A component includes an unsaturated polyester resin, an anti-shrinkage toughening agent, and the B component Including a peroxide initiator; the anti-shrinkage and toughening agent includes a paste formed by mixing methyl vinyl silicone rubber and natural rubber raw rubber and dissolving in petroleum ether, and the anti-shrinking and toughening agent The mass percentage of the unsaturated polyester resin is 5-15%. The stone back rib glue provided by the embodiment of the present invention uses unsaturated polyester resin as the matrix, which can fully give the colloid excellent water and acid resistance, and is dissolved in petroleum ether after mixing with methyl vinyl silicone rubber raw rubber and natural rubber raw rubber. The paste formed in the paste can greatly improve the toughness of the stone back rib glue, and at the same time improve the anti-shrinkage performance, without adding an additional anti-shrinkage agent, to achieve the integration of toughening and shrinkage resistance, and obtain a stone back rib glue with excellent comprehensive mechanical properties.
Description
technical field [0001] The invention relates to the technical field of building materials, in particular to a stone backing glue and a preparation method thereof. Background technique [0002] In the field of building materials, stone back reinforcement means that after the stone is cut into slabs, in order to avoid damage or breakage during transportation, operation, etc., grooves are added to the back of the stone to add steel bars, so that the stone has better firmness. The stone back reinforcement glue is used to fix the steel bars. As a kind of reinforcement glue, it plays a vital role in ensuring the quality of the stone. [0003] At present, white cement or marble glue is mainly used for reinforcement of stone back reinforcement, but they all have some disadvantages. The cement curing time is long, which affects the construction, and at least one week of water curing time is required, so that the stone is prone to pathological changes in a humid environment, such as ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): C09J167/06C09J11/08
CPCC09J167/06C09J11/08C08L2205/035C08L83/04C08L7/00
Inventor 杜昆文杜昆武邱国峰王莉亚熊善高毛攀峰季亦同
Owner 江苏大力士云石护理材料有限公司