Diatomite and mica powder compound modified inorganic functional coating and application thereof

A technology of inorganic functional coatings and mica powder, which is applied in the direction of alkali metal silicate coatings, cement coatings, antifouling/underwater coatings, etc., which can solve the problems of limited innovation, lack of environmental protection functionality, and inability to meet the needs of environmental protection and home decoration, etc. problems, achieve the effects of reducing the content of harmful substances, improving indoor air quality, and improving decorative effects

Inactive Publication Date: 2021-06-25
JILIN CHUNZHIYUAN DIATOM OOZE CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the existing inorganic coatings generally lack environmental protection functionality. In addition, innovations in other aspects are also very limited, which can no longer meet people's growing decoration needs for environmentally friendly homes.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diatomite and mica powder compound modified inorganic functional coating and application thereof
  • Diatomite and mica powder compound modified inorganic functional coating and application thereof
  • Diatomite and mica powder compound modified inorganic functional coating and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0105] A kind of inorganic functional paint compounded and modified by diatomite and mica powder of the present invention comprises the following components in parts by weight:

[0106]

[0107] The preparation method of the decorative coating of this embodiment is as follows: first, diatomite and mica powder are pre-stirred, and after stirring evenly, a composite material is formed, and then the composite material and the remaining components are put into a shaker and mixed evenly, to obtain .

Embodiment 2

[0109] A kind of inorganic functional paint compounded and modified by diatomite and mica powder of the present invention comprises the following components in parts by weight:

[0110]

[0111] The preparation method of the decorative coating of this embodiment is as follows: first, diatomite and mica powder are pre-stirred, and after stirring evenly, a composite material is formed, and then the composite material and the remaining components are put into a shaker and mixed evenly, to obtain .

Embodiment 3

[0113] A kind of inorganic functional paint compounded and modified by diatomite and mica powder of the present invention comprises the following components in parts by weight:

[0114]

[0115] The preparation method of the decorative coating of this embodiment is as follows: first, diatomite and mica powder are pre-stirred, and after stirring evenly, a composite material is formed, and then the composite material and the remaining components are put into a shaker and mixed evenly, to obtain .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an inorganic functional coating, which comprises 30 to 50 parts by weight of diatomite, 8 to 12 parts by weight of nanometer titanium dioxide, 3 to 5 parts by weight of tourmaline powder, 15 to 20 parts by weight of mica powder, 8 to 10 parts by weight of sepiolite, 12 to 15 parts by weight of titanium dioxide, 5 to 8 parts by weight of mordenite, 5 to 8 parts by weight of talcum powder, 10 to 15 parts by weight of white cement, 3 to 5 parts by weight of cellulose ether, 8 to 12 parts by weight of nanometer calcium powder and 5 to 8 parts by weight of potassium silicate. The provided inorganic functional coating compounded by the diatomite and the mica powder has multiple functions of purifying formaldehyde, breathing and humidifying, preventing mildew and bacteria and the like, and has high-gloss decorative property. According to the present invention, the traditional chemical auxiliary agent does not need to be added, the formula does not contain any organic compound, such that the chemical raw material is saved, the generation of the volatile organic compound polluting the environment is avoided, and the real zero VOC wall material coating material is obtained.

Description

technical field [0001] The invention belongs to the technical field of inorganic functional coatings, and relates to an inorganic functional coating and an application thereof, in particular to an inorganic functional coating modified by compounding diatomite and mica powder and an application thereof. Background technique [0002] Paint is coated on the surface of the object to be protected or decorated, and can form a continuous solid film firmly attached to the object to be coated, also known as paint film or coating, usually based on resin, or oil, or emulsion, adding Or do not add pigments, fillers, add corresponding additives, and use organic solvents or water to prepare viscous liquids. There are many types of coatings. According to the form of the product, they are mainly divided into: solvent-based coatings, water-based coatings, powder-based coatings, high-solid coatings, metallic coatings, pearlescent coatings, and inorganic coatings. [0003] In recent years, wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/08C09D1/04C09D5/14C09D7/61
CPCC09D1/04C09D1/08C09D5/14C09D7/61
Inventor 赵若羽马振永王星
Owner JILIN CHUNZHIYUAN DIATOM OOZE CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com