Preparation method of inorganic silicon modified mineral coating

A technology of inorganic silicon and mineral fillers, applied in chemical instruments and methods, coatings, mixers, etc., can solve the problems of poor resistance and poor chemical resistance, improve weather resistance and chemical resistance, shorten processing time, and integrate sex enhancing effect

Active Publication Date: 2021-08-03
HUBEI BASTER TECHNOOGY CO LTD
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Silicate mineral coatings are provided in the prior art, which satisfies people's needs well, but it still has some deficiencies, such as the problems of post-resistance and poor chemical resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of inorganic silicon modified mineral coating
  • Preparation method of inorganic silicon modified mineral coating
  • Preparation method of inorganic silicon modified mineral coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] like figure 1 Shown, a kind of preparation method of inorganic silicon modified mineral paint, comprises steps:

[0045] Step A: Add 30 parts by weight of water-based inorganic resin and 60 parts by weight of mineral filler into the reaction kettle, stir for 15 minutes, and set the speed at 500 r / min;

[0046] Step B: Add 1 part by weight of defoamer, 1 part by weight of dispersant, and 0.5 part by weight of leveling agent into the reactor, and stir for 15 minutes to obtain a finished product.

[0047] The step A specifically includes: TI: premixing 30 parts by weight of water-based inorganic resin and 60 parts by weight of mineral filler; T2: mixing and adding to the reactor, stirring for 15 minutes, and setting the speed at 500 r / min.

Embodiment 2

[0049] like figure 1 Shown, a kind of preparation method of inorganic silicon modified mineral paint, comprises steps:

[0050] Step A: Add 40 parts by weight of water-based inorganic resin and 70 parts by weight of mineral filler into the reaction kettle, stir for 30 minutes, and set the speed to 600r / min;

[0051] Step B: Add 2 parts by weight of defoamer, 3 parts by weight of dispersant, and 1 part by weight of leveling agent into the reactor, and stir for 30 minutes to obtain a finished product.

[0052] The step A specifically includes: TI: premixing 40 parts by weight of water-based inorganic resin and 70 parts by weight of mineral filler; T2: mixing and adding to the reaction kettle, stirring for 30 minutes, and setting the speed at 600 r / min.

Embodiment 3

[0054] like figure 1 Shown, a kind of preparation method of inorganic silicon modified mineral paint, comprises steps:

[0055] Step A: Add 35 parts by weight of water-based inorganic resin and 65 parts by weight of mineral filler into the reaction kettle, stir for 20 minutes, and set the speed at 550r / min;

[0056] Step B: Add 1.5 parts by weight of defoamer, 2 parts by weight of dispersant, and 0.8 parts by weight of leveling agent into the reactor, and stir for 25 minutes to obtain a finished product.

[0057] The step A specifically includes: TI: premixing 35 parts by weight of water-based inorganic resin and 65 parts by weight of mineral filler; T2: mixing and adding to the reactor, stirring for 20 minutes, and setting the speed at 550 r / min.

[0058] In the above embodiments, the water-based inorganic resin is composed of methyltrimethoxysilane, and the mineral filler includes one or more of feldspar powder, talc powder and silicon dioxide.

[0059] The pre-mixing proc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an inorganic silicon modified mineral coating, which comprises the following steps: step A, adding 30-40 parts by weight of water-based inorganic resin and 60-70 parts by weight of mineral filler into a reaction kettle, conducting stirring for 15-30 minutes, and setting the rotating speed to be 500-600r / min; and step B, adding 1-2 parts by weight of a defoaming agent, 1-3 parts by weight of a dispersing agent and 0.5-1 part by weight of a flatting agent into the reaction kettle, and conducting stirring for 15-30 minutes to obtain a finished product. Compared with the prior art, the invention provides the preparation method of the inorganic silicon modified mineral coating.

Description

technical field [0001] The invention relates to a preparation method of paint, in particular to a preparation method of inorganic silicon modified mineral paint. Background technique [0002] With the advancement of science and technology and the improvement of people's living standards, people have higher and higher requirements for indoor environment and air quality. Scientists have detected more than 500 kinds of organic substances from indoor air, among which the common indoor pollutants that everyone is generally concerned about mainly include benzene, formaldehyde, xylene and total volatile organic compounds. Since most modern people spend 80-90% of their time indoors every day, indoor air pollutants are more harmful to the human body. As people pay more and more attention to the environment and health, the emission standards for volatile organic compounds are becoming more and more stringent, and the research and development of bio-environmental protection wall coati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D183/04C09D7/61B01F5/20B01F5/22B01F15/02B01J19/00B01J19/18B01F25/74