Jewelry and surface treatment method thereof

A surface treatment and jewelry technology, applied in clothing, jewelry, applications, etc., can solve the problems of increasing the complexity of jewelry surface treatment, enamel can not shine, etc., to achieve a good user experience

Pending Publication Date: 2021-10-26
广东顺德周大福珠宝制造有限公司
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing jewelry products, the enamel generally cannot shine in the dark
Furthermore, if enamel is fired at high temperature on the surface of existing jewelry items, the processing temperature is usually around 1000°C (Celsius), which increases the complexity of the surface treatment of jewelry items

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Jewelry and surface treatment method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be further described below in conjunction with the embodiments shown in the accompanying drawings.

[0021] like figure 1 Shown, the surface treatment method of the jewelry that the present invention proposes, comprises the following steps:

[0022] (1) Mixing the low-temperature enamel glaze with the luminescent material to obtain the first glaze. Among them, the luminescent material can emit light in the dark.

[0023] (2) Mix the first glaze with the curing agent to obtain the second glaze. Wherein, the role of the curing agent is to promote the solidification and hardening of the second glaze in subsequent steps. Without a curing agent, the second glaze will not be able to set and harden after it is applied to the jewelry surface.

[0024] (3) Coating the second glaze material on the surface of the jewelry. Among them, special tools are used to apply the second glaze on the surface of the jewelry to ensure that the surface of the jewe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses jewelry and a surface treatment method thereof. The surface treatment method of the jewelry comprises the following steps: mixing low-temperature enamel glaze with a luminescent material to obtain a first glaze; mixing the first glaze with a curing agent to obtain a second glaze; coating the second glaze on the surface of the jewelry; and carrying out heating and drying treatment or air drying treatment on the coated jewelry. The jewelry is obtained by adopting the surface treatment method. According to the invention, the surface of the jewelry can be simply and efficiently glazed, and the jewelry not only has the advantages of basic enamel, but also can emit light in the dark so that the jewelry can also show unique and mysterious charm in the dark.

Description

technical field [0001] The invention belongs to the technical field of jewelry processing, and in particular relates to a jewelry and a surface treatment method thereof. Background technique [0002] In the existing jewelry products, the enamel generally cannot emit light in the dark. Furthermore, if enamel is fired at high temperature on the surface of existing jewelry items, the processing temperature is usually around 1000° C. (Celsius), which increases the complexity of the surface treatment of jewelry items. Contents of the invention [0003] The object of the present invention is to provide a kind of jewelry and its surface treatment method, which can emit light in the dark, aiming at the shortcomings of the prior art. [0004] In order to solve the above technical problems, the present invention adopts the following technical solution: a jewelry surface treatment method, comprising the following steps: mixing low-temperature enamel glaze with luminescent material t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine