Iridescent-free structural color material and preparation method thereof
A structural color and inorganic material technology, applied in instruments, optical components, optics, etc., can solve problems such as limiting the application of photonic structural color, achieve a wide range of applications, solve the problem of angle dependence, and a wide range of inorganic materials.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] Example 1
[0028] Take steel beads having a diameter of 1 mm, which is tightly arranged on a glass plate, and the steel bead is fixed to the glass plate as a template with ultraviolet cured glue. The polydimethylsiloxane (PDMS) monomer and the curing agent are mixed uniform in mass than 25: 1, and the vacuum conditions are 30 min, and the prepolymer is spread on the glass plate, placed in an oven at 80 ° C. Curing 10 min, closely bonded to the steel ball template, 100 min under 100 ° C for 30min, remove the PDMS from the template, peeled from the glass plate to obtain a PDMS with a bowl array structure. Elastomer.
[0029] It is called 40.0 g of water, 1.0 g of hexadalkyltrimel bromide (CTAb) and 2.5 g of methyl methacrylate (MMA) and acrylamide (AM) mixed monomer (mass ratio 10: 1) In the reaction flask, stirring was stirred under nitrogen protection for 30 min. The water bath was heated to 75 ° C to add 45.0 mg of potassium sulfate (KPS) to the reaction bottle to react 1...
Example Embodiment
[0034] Example 2-4
[0035] The method is the same as in Example 1, but the diameter of a steel bead is prepared by a steel bead having a diameter of 3.0 mm, and a PDMS elastomer with a bowl structure is prepared.
Example Embodiment
[0036] Example 5-6
[0037] The method is in Example 1, but the silicon sheet and the quartz sheet are respectively carried out as a matrix as a matrix as a matrix.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap