Aluminum laser welding plate cabinet material and production process

A laser welding and production process technology, applied in metal material coating process, polyester coating, coating and other directions, can solve the problems of choosing favorite color, poor compressive strength, single color, etc., to achieve low production cost, high performance Excellent and simple preparation process

Pending Publication Date: 2022-06-14
安徽维慕斯智能全铝家居有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the disadvantages of the prior art that the surface color of the aluminum profile is single, the color you like cannot be selected according to the needs, and the compressive strength is poor, and it is easy to be damaged when it is subjected to a large impact force. Laser welding board cabinet material and production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Aluminum laser welding board cabinet material, including the following raw materials by weight: 14 parts of aluminum profiles, 10 parts of polyester acrylic resin, 9 parts of diisocyanate, 7 parts of pigment, 11 parts of silicon carbide fiber, 5 parts of quartz sand, adhesive 14 parts of antifoaming agent, 3 parts of glass fiber, 3 parts of nano titanium dioxide, 13 parts of pentaerythritol, 4 parts of water, 14 parts of defoamer and 12 parts of phenolic resin.

[0027] This embodiment also proposes a production process for aluminum laser-welded panel cabinet materials, including the following steps:

[0028] S1: Preparation of raw materials: Weigh the raw materials in the following parts by weight: 14 parts of aluminum profiles, 10 parts of polyester acrylic resin, 9 parts of diisocyanate, 7 parts of pigments, 11 parts of silicon carbide fibers, 5 parts of quartz sand, and 14 parts of binder. parts, 3 parts of glass fiber, 3 parts of nano titanium dioxide, 13 parts of ...

Embodiment 2

[0036] Aluminum laser welding board cabinet material, including the following raw materials by weight: 15 parts of aluminum profiles, 11 parts of polyester acrylic resin, 10 parts of diisocyanate, 8 parts of pigment, 12 parts of silicon carbide fiber, 6 parts of quartz sand, adhesive 15 parts of antifoaming agent, 4 parts of glass fiber, 4 parts of nano titanium dioxide, 14 parts of pentaerythritol, 5 parts of water, 15 parts of defoamer and 13 parts of phenolic resin.

[0037] This embodiment also proposes a production process for aluminum laser-welded panel cabinet materials, including the following steps:

[0038] S1: Preparation of raw materials: Weigh the raw materials in sequence according to the following parts by weight: 15 parts of aluminum profiles, 11 parts of polyester acrylic resin, 10 parts of diisocyanate, 8 parts of pigments, 12 parts of silicon carbide fibers, 6 parts of quartz sand, and 15 parts of binder parts, 4 parts of glass fiber, 4 parts of nano titaniu...

Embodiment 3

[0046] The aluminum laser-welded panel cabinet material includes the following raw materials by weight: 16 parts of aluminum profiles, 12 parts of polyester acrylic resin, 11 parts of diisocyanate, 9 parts of pigment, 13 parts of silicon carbide fiber, 7 parts of quartz sand, adhesive 16 parts of antifoaming agent, 5 parts of glass fiber, 5 parts of nano titanium dioxide, 15 parts of pentaerythritol, 6 parts of water, 16 parts of defoamer and 14 parts of phenolic resin.

[0047] This embodiment also proposes a production process for aluminum laser-welded panel cabinet materials, including the following steps:

[0048] S1: Preparation of raw materials: Weigh the raw materials in the following parts by weight: 16 parts of aluminum profiles, 12 parts of polyester acrylic resin, 11 parts of diisocyanate, 9 parts of pigments, 13 parts of silicon carbide fibers, 7 parts of quartz sand, and 16 parts of binder. parts, 5 parts of glass fiber, 5 parts of nano titanium dioxide, 15 parts of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of furniture processing, and particularly relates to an aluminum laser welding plate cabinet material and a production process. The production process comprises the following steps: S1, raw material preparation: sequentially weighing the following raw materials in parts by weight: 14-18 parts of aluminum profile, 10-14 parts of polyester acrylic resin, 9-13 parts of diisocyanate, 7-11 parts of pigment, 11-15 parts of silicon carbide fiber, 5-9 parts of quartz sand, 14-18 parts of binder, 3-7 parts of glass fiber, 3-7 parts of nano titanium dioxide, 13-17 parts of pentaerythritol, 4-8 parts of clear water, 14-18 parts of defoaming agent and 12-16 parts of phenolic resin for later use; and S2, grinding and polishing treatment. The production process is simple to operate, low in production cost, beneficial to industrial popularization and application of enterprises at present, simple in preparation process and low in cost, and the prepared cabinet material is excellent in performance and has a very good market application prospect.

Description

technical field [0001] The invention relates to the technical field of furniture processing, in particular to the material and production process of an aluminum laser-welded panel cabinet body. Background technique [0002] An aluminum profile is a geometrically shaped object that is made of aluminum material and processed by rolling, extrusion and other processes. It is widely used in the field of construction. Aluminum furniture is widely used because of its high waterproof and fireproof performance, effective anti-moth-eaten, recyclable, safe, environmentally friendly and green. [0003] The aluminum profile traditionally used in furniture, after the surface of the aluminum profile is treated with anti-oxidation, it is not only resistant to dirt, but also has a smooth surface and is easy to clean. The compressive strength is poor, and it is easy to be damaged when subjected to a large impact force. Therefore, the material and production process of the aluminum laser-weld...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D161/06C09D167/06C09D7/61C09D7/63C23C26/00B23P15/00
CPCC09D161/06C09D7/61C09D7/63C09D7/70C23C26/00B23P15/00C08K2201/011C08K2003/2241C08L67/06C08K5/29C08K7/10C08K3/36C08K7/14C08K3/22C08K5/053
Inventor 程为华郭朝令宋桂平
Owner 安徽维慕斯智能全铝家居有限公司