A printing film and coating technology, applied in printing, printing devices, copying/marking methods, etc., can solve the problems of multi-style commodity production cycle and production cost increase, inconvenient printing of calligraphy and painting patterns, and affect product sales. The appearance image, the effect of improving market sales and low production cost

Inactive Publication Date: 2006-10-18
刘希凡
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Although the existing coating film printing process can print calligraphy and painting patterns on glass, ceramics, metal and stone material objects with complex and changeable surface shapes, but because the existing coating film materials can only use gravure, flexo , lithography and pad printing process printing, the cost of plate making is relatively high, and it is not convenient to print calligraphy and painting patterns on coated film materials with a width greater than 2 meters, which greatly increases the production cycle and production cost of small batches and multi-style products , affecting product sales in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The coated film printing film of the present invention adopts the following steps to make:

[0021] (1) According to parts by weight water: 75, PVA: 22.6, glycerol: 0.4; hydrophilic ultrafine silica with product code name KR-101: 1.25, water treatment organosilicon defoamer with product code name FA10 : 0.75 to prepare membrane solution, first put water into a stainless steel container with heating device, put PVA into water and stir at room temperature for 15 minutes at a speed of 85 rpm, then heat the solution to 90 After keeping it warm for 50 minutes at ℃ to make it completely dissolve, put the glycerin, the hydrophilic ultrafine silica with the product code KR-101 and the water treatment silicone defoamer with the product code FA10 under the temperature of the indoor environment. Add it into the solution, stir evenly and completely dissolve it to obtain a membrane solution;

[0022] (2) Utilize the biaxially stretched polypropylene BOPP plastic film that thickness...

Embodiment 2

[0029] The coated film printing film of the present invention adopts the following steps to make:

[0030] (1) According to parts by weight water: 77, PVA: 22, glycerol: 0.3, hydrophilic ultrafine silica with product code name KR-101: 1, water treatment organosilicon defoamer with product code name FA10 : 0.5 to prepare membrane solution, first put water into a stainless steel container with heating device, put PVA into water and stir at room temperature for 15 minutes at a speed of 70 rpm, then heat the solution to 90 After keeping it warm for 30 minutes at ℃ to make it completely dissolve, put the glycerin, the hydrophilic ultrafine silica with the product code KR-101 and the water treatment silicone defoamer with the product code FA10 under the temperature of the indoor environment. Add it into the solution, stir evenly and completely dissolve it to obtain a membrane solution;

[0031](2) Utilize the biaxially stretched polypropylene BOPP plastic film that thickness is 120...

Embodiment 3

[0038] The coated film printing film of the present invention adopts the following steps to make:

[0039] (1) According to parts by weight water: 70, PVA: 23.2, glycerol: 0.5; hydrophilic ultrafine silica with product code name KR-101: 1.5, water treatment organosilicon defoamer with product code name FA10 : 1 To prepare membrane solution, first put water into a stainless steel container with heating device, put PVA into water and stir at room temperature for 15 minutes at a speed of 100 rpm, then heat the solution to 90 After keeping it warm for 60 minutes at ℃ to completely dissolve it, put glycerol, hydrophilic ultrafine silica with the product code KR-101, and water treatment silicone defoamer with the product code FA10 at the temperature of the indoor environment. Add it into the solution, stir evenly and completely dissolve it to obtain a membrane solution;

[0040] (2) Utilize the biaxially stretched polypropylene BOPP plastic film that thickness is 110 microns, it is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A coated film printing film is made by the following steps: prepare a film body solution according to parts by weight of water: 75, PVA: 22.6, glycerol: 0.4, KR-101: 1.25, FA10: 0.75, and put PVA in Stir in water and heat to dissolve, then add glycerol, KR-101 and FA10 into the solution to dissolve to obtain a membrane solution; spread the BOPP film on the platform, and spray the membrane solution evenly on the BOPP film , and be dried. The printing process is as follows: use color inkjet printing equipment to print calligraphy and painting patterns on the film-coated printing film, spread the film-coated printing film printed with calligraphy and painting patterns on the water surface, and wait until the film-coated printing film becomes solid-liquid in the water After mixing, press the printed object down into the water. Its purpose is to provide a coating printing film with short production cycle, low production cost and no need for plate printing and its printing process.

Description

technical field [0001] The present invention generally relates to a printing process, in particular to a coating printing film for transfer printing on articles with irregular surfaces and its printing process. Background technique [0002] Although the existing coating film printing process can print calligraphy and painting patterns on glass, ceramics, metal and stone material objects with complex and changeable surface shapes, but because the existing coating film materials can only use gravure, flexo , lithography and pad printing process printing, the cost of plate making is relatively high, and it is not convenient to print calligraphy and painting patterns on coated film materials with a width greater than 2 meters, which greatly increases the production cycle and production cost of small batches and multi-style products , affecting the sales of the product in the market. Contents of the invention [0003] The purpose of the present invention is to overcome the def...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B41M5/00B41M1/26
Inventor 刘希凡
Owner 刘希凡