Process for preparing silicon dioxide of carrying nano silver
A technology of silica and silica gel, applied in the direction of silica, silica, etc., can solve the problems of wide distribution range, coarse nano-silver loaded silica particles, complex process, etc., achieve complete adsorption, low cost, The effect of simple process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0017] Example 1
[0018] 25.6 grams of silver nitrate solids are added to 75.26 liters of deionized water and dissolved at room temperature to prepare a silver nitrate solution; In the silver solution, stir evenly, then add 1600 milliliters of 1% (wt %) ascorbic acid aqueous solution under stirring, after reacting to the solution at room temperature all change to nano-silver, add 2600 milliliters of 30% (wt %) silica sol solution or 10% ( wt%) 7200 milliliters of nano-silica dispersion liquid, stir until the nano-silver is fully adsorbed on the silica particles, then centrifuge and concentrate to obtain a yellow-brown nano-silver-loaded silica suspension, filter, dry, and pulverize to obtain the nano-silver-loaded silica suspension. Silica powder of nano silver.
Example Embodiment
[0019] Example 2
[0020] 25.6 grams of silver nitrate solids are added to 73.6 liters of deionized water and dissolved at room temperature to prepare a silver nitrate solution; 2176 milliliters of 10% (wt %) anionic surfactant sodium lauryl sulfate aqueous solution are added in the silver nitrate solution, Stir evenly, be warming up to 90 DEG C, constant temperature 2 hours, then add 1600 milliliters of 1% (wt %) ascorbic acid aqueous solution under stirring, after reacting to solution and all change to nano-silver, add 30% (wt %) silica sol solution 2600 milliliters, Stir until the nano-silver is fully adsorbed on the silica particles, then cool down to 40°C, use an ultrafiltration membrane with a molecular weight cut-off of 10,000 to perform ultrafiltration, and wash the concentrated solution with 24 liters of deionized water three times, and continue ultrafiltration until the volume of the filtrate is 8 liters Afterwards, the dark yellow-brown silver-loaded nano-silver sil...
Example Embodiment
[0021] Example 3
[0022] 25.6 grams of silver nitrate solids are added to 73.6 liters of deionized water and dissolved at room temperature to prepare a silver nitrate solution; 2176 milliliters of 10% (wt %) anionic surfactant sodium dodecylsulfonate aqueous solution are added in the silver nitrate solution , stir evenly, be warming up to 90 DEG C, constant temperature 2 hours, then add 1300 milliliters of 1% (wt%) citric acid aqueous solution under stirring, after reacting to the solution and all change to nano-silver, add 10% (wt%) nano-silicon dioxide 7200 milliliters of the dispersion liquid, stirred until the nano-silver is fully adsorbed on the silica particles, then cooled and left to settle, concentrated to obtain a yellow-brown nano-silver-loaded silica suspension, filtered, dried, and pulverized to obtain nano-silver-loaded silica Silica powder body.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap