Method for producing monodisperse particles

Abstract

Disclosed are polymer particles. The polymer particles comprise a plurality of polymer stabilizing components. Each polymer stabilizing component comprises one or more hydrophilic polymer chains and a plurality of hydrophobic polymer chains. Each hydrophobic polymer chain is covalently bonded to one or more polymer stabilizing components. The polymer particles are monodisperse, having a coefficient of variation based on diameter of less than 20%. Also disclosed are methods for producing the polymer particles.

Description

[Technical field]

[0001] FIELD OF THEINVENTION The present invention relates to highly monodisperse polymer particles useful in biological assays and other applications, and to a method (or treatment or process) for preparing highly monodisperse submicron particles, particularly particles having diameters in the range of 100-370 nm. [Background technology]

[0002] (background) The listing or description of a published prior art document in this specification should not necessarily be taken as an acknowledgement that such document is part of the state of the art or is common general knowledge.

[0003] In recent years, immunological techniques (or procedures) have been increasingly adopted as clinical diagnostic methods due to their high specificity and sensitivity. Latex agglutination is a heterogeneous immunological assay method widely used in biology and medicine to detect small amounts of antibodies and antigens in liquid test samples. The agglutination reaction involves the in vitro aggregation of small carrier particles (usually polymeric in nature, known as latex particles). This agglutination is mediated by a specific reaction between antibodies and antigens, either of which are immobilized or adsorbed to the surface of the latex particles. Thus, the sensitivity and reproducibility of such assays are highly dependent on the consistency of the particle surface area. This in turn depends on the monodispersity and size repeatability of the latex particles, which must be consistent between manufacturing batches. For immunodiagnostic applications, the particle diameter is required to be about half the wavelength of visible light (approximately 100 nm to 370 nm) and the monodispersity (i.e., coefficient of variation) is preferably less than 5%.

[0004] Emulsion polymerization is defined as "a polymerization in which the monomer(s), initiator, dispersion medium, and possibly colloidal stabilizer constitute, first of all, a heterogeneous system, thereby resulting in colloidal sized particles, including the formed polymer" (Pure Appl. Chem., 2011, 83, 2229-2259). In this method, the components are mixed and homogenized. After obtaining a stable emulsion, the initiator is activated to start the polymerization. The stability of the emulsion is a key factor in achieving monodisperse polymer beads. To form a stable emulsion system, surfactants and emulsifiers are conventionally used to control the formation of micelles by the type of monomer and surfactant, which in turn controls the size and distribution of the resulting polystyrene beads. In United States (US) Patent Application Publication No. 20170218095A1, which describes the synthesis of polystyrene seeds by emulsion polymerization, sodium dodecyl sulfate (SDS) is used as a surfactant, ammonium persulfate (APS) is used as an initiator, and borax is used to increase the ionic strength. The stabilizer (4-tert-butylcatechol) is removed by extracting styrene with 10% by weight sodium hydroxide. Such stabilizers can inhibit the polymerization of styrene. Therefore, they affect the polymerization rate, the diameter, diameter and monodispersity of the polystyrene beads. The resulting monodisperse polystyrene particles have dimensions in the range of 50 to 200 nm.

[0005] A particular emulsion polymerization method discovered by John Ugelstad, also known as the seed activation method (US Pat. No. 4,530,956, International Publication No. WO 00 / 61647), has been used to prepare monodisperse seeds with dimensions (or sizes) between 50 nm and 200 nm. However, this method involves tedious procedures (one or more polymerization cycles) and complex recipes. Briefly, the process involves contacting the seeds with a mixture of reagents including an organic solvent to swell the seeds. Excess organic solvent is then removed and surfactants, monomers, initiators and crosslinkers are added to form particles of activated seeds in an aqueous vehicle. The monomers, initiators and crosslinkers diffuse into the activated seed particles to form an aqueous dispersion of swollen seed particles, whereby polymerization of the monomers and crosslinkers is initiated in the swollen seed particles.

[0006] Dispersion polymerization is defined as "a precipitation polymerization in which monomer(s), initiator(s) and colloidal stabilizer(s) are dissolved in a solvent, thereby first forming a homogeneous system that produces a polymer, resulting in the formation of polymer particles" (Pure Appl. Chem., 2011, 83, 2229-2259). To produce monodisperse polymer beads, it is important to first form a homogeneous system. In dispersion polymerization, oil-soluble initiators such as benzoyl peroxide (BPO) [Can. J. Chem. 1985, 63, 209-216], azobisisobutyronitrile (AIBN) / 2,2'-azodi(2-methylbutyronitrile) (AMBN) [J. Polym. Sci: Part A: 1986, 24, 2995-3007; J. Polym. Sci: Part A: 1996, 4, 1857-1871] and ammonium persulfate (APS) [Macromolecular Research, 2010, 8, 935-943] are commonly used. Water-soluble, oil-insoluble sodium persulfate (SPS) and potassium persulfate (KPS) have not been reported for use as initiators in homogeneous (or homogeneous) dispersion polymerization of styrene.

[0007] To obtain monodisperse polystyrene beads by dispersion polymerization, a binary solvent system was used in the past. For example, a mixture of ethanol (175 mL) and 2-methoxyethanol (250 mL) was used as a binary solvent system with BPO as the initiator. This allowed the production of monodisperse polystyrene beads (diameter 3 μm) with hydroxypropyl cellulose (HPC) (used as a steric stabilizer) [Can. J. Chem. 1985, 63, 209-216]. In principle, dispersion polymerization requires that all components (monomer, initiator and stabilizer) are completely dissolved in the initial solvent system to form a homogeneous solution. Therefore, styrene cannot be used alone as a solvent because it is insoluble in water. Instead, it is common to use a mixture of alcohol and water (e.g., 85% ethanol and 15% water) (Can. J. Chem. 1985, 63, 209-216; J. Polym. Sci: Part A: Polymer Chemistry, 1987, 25, 1395-1407). In another size control study (Macromolecular Research, 2010, 18, 935-943), monodisperse polystyrene beads were prepared using polyvinylpyrrolidone (PVP) as a steric stabilizer, ammonium persulfate (APS) as an initiator, and aqueous ethanol (ethanol / water, 25 / 3 by volume) as the solvent. This study also shows that the use of a purely aqueous medium (water as the only solvent) results in less control over particle size, shape, and size distribution. It is therefore concluded that monodisperse polystyrene beads cannot be produced by dispersion polymerization in water alone. It is also worth noting that the particles obtained were all found to be larger than 1 μm, and therefore it is not possible to produce particles smaller than this size using dispersion polymerization.

[0008] In surfactant-free emulsion polymerization (or surfactant-free emulsion polymerization), three components are included in the system: monomer, water, and initiator. The initiator is typically selected from 2,2'-azobis(2-methylpropionamidine) dihydrochloride (AIBA), potassium persulfate (KPS), and ammonium persulfate (APS). They are soluble in water. The process of polymerizing styrene involves mixing water and styrene monomer to form an emulsion system under certain reaction conditions, and then adding an initiator-water solution to start the reaction.

[0009] ·Langmuir 2004, 20, 4400-4405 reveals that the mechanism for the formation of polystyrene beads mainly involves the precipitation (or settling) and nucleation of polystyrene in water. The number of polystyrene beads formed from styrene micelles is very small and can be neglected. It also demonstrates that the particle dimensions (or size or diameter) are controlled by the reaction time and temperature, and that monodisperse polystyrene particles were not obtained using AIBA.

[0010] Another study (Colloid Polym. Sci. 1999, 277, 607-626) compared the use of AIBA with the use of KPS. It was found that the KPS recipe produced larger particle dimensions and a higher standard deviation than the AIBA recipe. However, both recipes produced particles smaller than 200 nm. Other recipes with different ionic strengths did not produce monodisperse polystyrene particles with particle dimensions larger than 200 nm.

[0011] In Eur. Polym. J., 1994, 30, 179-183, it was demonstrated that increasing the amount of APS results in larger particle dimensions (but at the expense of a wider distribution of particle dimensions). Furthermore, the smallest monodisperse polystyrene beads achievable with APS without added comonomer are believed to be 250 nm. Summary of the Invention [Problem to be solved by the invention]

[0012] The use of KPS in surfactant-free emulsion polymerization of styrene has been studied for over 20 years. Interestingly and surprisingly, the use of sodium persulfate (SPS), which is less expensive than KPS or APS, as an initiator in surfactant-free emulsion polymerization of styrene has not been reported so far. Although SPS, KPS and APS are all commonly used persulfate initiators, their effects on the monodispersity of polystyrene particles are unclear due to differences in their solubility, ionic strength, cation size, viscosity and decomposition temperature. Therefore, we developed a new technique for surfactant-free emulsion polymerization using SPS as an inexpensive initiator and Na + It is useful to prepare a colloidal solution of monodisperse polystyrene having

[0013] Surfactant-free emulsion polymerization of styrene is typically initiated with a saturated solution of styrene, a procedure that involves adding an aqueous initiator solution to a mixture of styrene and water. The use of a saturated solution of styrene explains the formation of anomalous regions in the beads. It is believed that such anomalous regions can be attributed to non-uniform monomer distribution within the polystyrene particles [Colloid Polym. Sci. 1999, 277, 607-626].

[0014] In summary, it is clear that existing polymerization methods do not provide highly monodisperse polystyrene particles suitable for immunodiagnostic applications. The dimensions of the particles formed are either too small (up to 200 nm) or too large (above 1 μm). Furthermore, the dimensions and / or monodispersity of the particles are influenced by the choice of surfactant (in the case of surfactant-mediated emulsion polymerization), the choice of initiator and initiator concentration (in the case of surfactant-free emulsion polymerization) and the polarity of the solvent (in the case of dispersion polymerization). Therefore, improved methods are needed to prepare monodisperse submicron particles suitable for clinical diagnostic methods. Monodisperse submicron particles have been noted to have many applications in micro- and nano-fluidics and nanotechnology in general. [Means for solving the problem]

[0015] Summary of the Invention This disclosure describes aspects and embodiments of the invention by reference to the following numbered paragraphs (or claims):

[0016] 1. A polymer particle comprising a plurality of polymeric stabilizing components and a plurality of hydrophobic polymer chains; each of the plurality of polymeric stabilizing components comprises one or more hydrophilic polymer chains; each of said plurality of hydrophobic polymer chains is covalently bonded to one or more of said polymeric stabilizing moieties; The polymer particles are monodisperse, with a coefficient of variation based on the diameter of the polymer particles being less than 20%.

[0017] 2. 2. The polymer particles of claim 1, wherein the coefficient of variation based on the diameter of the polymer particles is less than 15%, such as less than 10%, such as less than 5%.

[0018] 3. 3. The polymer particles according to claim 2, wherein the coefficient of variation based on the diameter of the polymer particles is 2% or less.

[0019] 4. 4. The polymer particles according to claim 3, wherein the coefficient of variation based on the diameter of the polymer particles is 1% or less.

[0020] 5. 5. The polymer particles according to any one of items 1 to 4, wherein the average diameter of the polymer particles is 50 to 1000 nm, for example, 100 to 600 nm, for example, 120 to 450 nm, for example, 150 to 400 nm, for example, 200 to 350 nm.

[0021] 6. 6. The polymer particle according to any one of claims 1 to 5, wherein the hydrophilic polymer chains of the polymer stabilizing component are selected from the group consisting of poly(vinylpyrrolidone), polyethyleneimine, polyacrylic acid, polyvinyl alcohol, water-soluble polysaccharides (e.g., hydroxypropylmethylcellulose, chitosan, and blends thereof), copolymers thereof, and blends thereof.

[0022] 7. 7. The polymer particle according to claim 6, wherein the hydrophilic polymer chain of the polymeric stabilizing component is poly(vinylpyrrolidone).

[0023] 8. 8. The polymer particle according to any one of items 1 to 7, wherein the hydrophobic polymer chain is formed from a monomer selected from one or more of styrene and its derivatives, acrylates, and alkyl acrylates.

[0024] 9. 9. The polymer particle of claim 8, wherein the hydrophobic polymer chains are formed from monomers selected from one or more of styrene, butyl acrylate, 2,2,2-trifluoroethyl methacrylate, methyl methacrylate, 4-methylstyrene, 3-methylstyrene, and 4-tert-butylstyrene.

[0025] 10. 10. The polymer particle according to claim 9, wherein the hydrophobic polymer chains are formed from styrene.

[0026] 11. 11. The polymer particle according to any one of items 1 to 10, wherein the weight:weight ratio of the plurality of polymer stabilizing components:the plurality of hydrophobic polymer chains is 1:1000 to 1:1, such as 1:500 to 1:2, for example 1:300 to 1:3, for example 1:150 to 1:5.

[0027] 12. 12. The polymer particle according to any one of claims 1 to 11, wherein the hydrophobic polymer chains are formed as copolymers and / or the hydrophobic polymer chains are crosslinked.

[0028] 13. (a) When the hydrophobic polymer chain is a copolymer, the copolymer is formed from a first set of monomers and a second set of monomers: the first set of monomers are hydrophobic and selected from one or more of styrene and its derivatives, acrylates, and alkyl acrylates; the second set of monomers is selected from one or more of monomers having a carboxylic acid group, monomers having a hydroxyl group, monomers having an amino group, and monomers having an epoxy group; and / or (b) When the hydrophobic polymer chains are crosslinked, the crosslinked polymer chains are formed by a crosslinking agent that reacts with the first set of monomers and / or the second set of monomers, if present, and optionally the crosslinking agent is a monomer having two or more unsaturated groups.

[0029] 14. (ai) the first set of monomers are selected from one or more of styrene, butyl acrylate, 2,2,2-trifluoroethyl methacrylate, methyl methacrylate, 4-methylstyrene, 3-methylstyrene, and 4-tert-butylstyrene; and / or (bi) the second set of monomers are selected from one or more of acrylic acid, methacrylic acid, 2-carboxyethyl acrylate, acrylamide, methacrylamide, allylamine, (hydroxyethyl)methacrylate, hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, glycidyl methacrylate, allyl glycidyl ether, 1,2-epoxy-5-hexene, 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or 14. The polymer particles of claim 13, wherein the crosslinking agent is one or more selected from divinylbenzene, ethylene glycol dimethylacrylate, bisphenol A dimethacrylate, butanediol dimethacrylate, tricyclodecane dimethanol diacrylate, pentaerythritol triacrylate, tripropylene glycol diacrylate, propoxylated neopentyl diacrylate, pentaerythritol triacrylate, ditrimethylolpropane tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol penta / hexaacrylate, tripropylene diacrylate, trimethylolpropane ethoxylate triacrylate, trimethylolpropane propoxylate triacrylate, di(trimethylolpropane)tetraacrylate, glycerol propoxylate triacrylate, pentaerythritol propoxylate triacrylate, poly(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, and tri(propylene glycol) diacrylate.

[0030] 15. (aii) the first set of monomers is styrene; and / or (bii) the second set of monomers are selected from one or more of N,N'-methylenebis(acrylamide), 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or (cii) the crosslinking agent is selected from one or more of divinylbenzene, ethylene glycol dimethyl acrylate, and bisphenol A dimethacrylate; 15. Polymer particles according to item 14.

[0031] 16. (aiii) the weight:weight ratio of the first set of monomers to the second set of monomers, if present, is from 40:1 to 1:1, for example from 20:1 to 2:1; and / or (biii) the weight:weight ratio of the first set of monomers:crosslinker, if present, is from 40:1 to 1:1, for example from 20:1 to 2:1; 16. The polymer particles according to any one of items 13 to 15.

[0032] 17. The polymer particles are of the formula: -SO4 - M + wherein the dash (-) represents the point of attachment to the polymer particle, and M + is Na + , K + or NH4 + 17. The polymer particles according to any one of claims 1 to 16, wherein the polymer particles are functionalized with a sulfate salt (or a sulfate salt or a sulfate salt) having the formula:

[0033] 18. A method for producing polymer particles, the method comprising the steps of: (A), (B) and (C) (A) reacting a water-soluble initiator compound with a hydrophilic polymeric stabilizer compound in water to form an aqueous macroinitiator complex; (B) adding one or more water-immiscible monomers to the aqueous solution of the macroinitiator complex to form a two-phase polymerization reaction mixture and reacting for a first period of time until particle nucleation occurs; and (C) continuing the reaction for a second period of time or quenching (or stopping) the reaction after the first period of time to obtain polymer particles. Including, The method wherein the polymer particles are monodisperse and the coefficient of variation based on the diameter of the polymer particles is less than 20%.

[0034] 19. 20. The method of claim 18, wherein the coefficient of variation based on the diameter of the polymer particles is less than 15%, such as less than 10%, such as less than 5%.

[0035] 20. 20. The method of claim 19, wherein the coefficient of variation based on the diameter of the polymer particles is 2% or less.

[0036] twenty one. 21. The method of claim 20, wherein the coefficient of variation based on the diameter of the polymer particles is 1% or less.

[0037] twenty two. 22. The method according to any one of items 18 to 21, wherein the average diameter of the polymer particles is from 50 to 1000 nm, for example from 100 to 600 nm, for example from 120 to 450 nm, for example from 150 to 400 nm, for example from 200 to 350 nm.

[0038] twenty three. 23. The method of any one of paragraphs 18 to 22, wherein the water soluble initiator comprises one or more of a peroxide initiator, a persulfate salt, and an azo initiator.

[0039] twenty four. 24. The method of claim 23, wherein the water soluble initiator is one or more selected from tert-amyl hydroperoxide, potassium persulfate, sodium persulfate, ammonium persulfate, 4,4'-azobis(4-cyanovaleric acid), 2,2'-azobis[2-methyl-N-(2-hydroxyethyl)propionamide, 2,2'-azobis[N-(2-carboxyethyl)-2-methylpropionamidine]hydrate, 2,2'-azobis(2-methylpropionamidine)dihydrochloride, 2,2''-azobis[2-(2-imidazolin-2-yl)propane] and 2,2'-azobis[2-(2-imidazolin-2-yl)propane]dihydrochloride.

[0040] twenty five. 25. The method of claim 24, wherein the water-soluble initiator is one or more selected from potassium persulfate, sodium persulfate, and ammonium persulfate.

[0041] 26. 26. The method of claim 25, wherein the water soluble initiator is sodium persulfate.

[0042] 27. 24. The method of claim 23, wherein the water-soluble initiator is a redox pair, optionally wherein the redox pair is selected from ascorbic acid and hydrogen peroxide or ammonium persulfate and sodium bisulfite.

[0043] 28. 28. The method of any one of claims 18 to 27, wherein the hydrophilic polymeric stabilizer compound is selected from the group consisting of poly(vinylpyrrolidone), polyethyleneimine, polyacrylic acid, polyvinyl alcohol, water soluble polysaccharides (e.g., hydroxypropylmethylcellulose, chitosan, and blends thereof), copolymers thereof, and blends thereof.

[0044] 29. 29. The method of claim 28, wherein the hydrophilic polymeric stabilizer compound is poly(vinylpyrrolidone).

[0045] 30. 29. The method of claim 28, wherein the hydrophilic polymeric stabilizer compound is a water-soluble polysaccharide (e.g., hydroxypropyl methylcellulose).

[0046] 31. 31. The method according to any one of claims 18 to 30, wherein the one or more water immiscible monomers are selected from one or more of styrene and its derivatives, acrylates, and alkyl acrylates.

[0047] 32. 32. The method of claim 31, wherein the one or more water immiscible monomers are selected from one or more of styrene, butyl acrylate, 2,2,2-trifluoroethyl methacrylate, methyl methacrylate, 4-methylstyrene, 3-methylstyrene, and 4-tert-butylstyrene.

[0048] 33. 33. The method of claim 32, wherein the one or more water immiscible monomers is styrene.

[0049] 34. 34. The method according to any one of items 18 to 33, wherein the weight:weight ratio of said hydrophilic polymeric stabiliser compound: said water immiscible monomer is from 1:1000 to 1:1, such as from 1:500 to 1:2, for example from 1:300 to 1:3, such as from 1:150 to 1:5.

[0050] 35. 35. The method of any one of claims 18 to 34, wherein in step (c), the reaction is continued for a second period of time.

[0051] 36. When the reaction is continued for a second period of time, a second set of monomers and / or crosslinkers are added to the reaction mixture; the second set of monomers is selected from one or more of monomers having a carboxylic acid group, monomers having a hydroxyl group, monomers having an amino group, and monomers having an epoxy group; The crosslinker is a monomer having two or more unsaturated groups; 36. The method according to claim 35.

[0052] 37. (ia) the second set of monomers are one or more selected from acrylic acid, methacrylic acid, 2-carboxyethyl acrylate, acrylamide, methacrylamide, allylamine, (hydroxyethyl)methacrylate, hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, glycidyl methacrylate, allyl glycidyl ether, 1,2-epoxy-5-hexene, 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or (ib) the crosslinker is selected from one or more of divinylbenzene, ethylene glycol dimethylacrylate, bisphenol A dimethacrylate, butanediol dimethacrylate, tricyclodecane dimethanol diacrylate, pentaerythritol triacrylate, tripropylene glycol diacrylate, propoxylated neopentyl diacrylate, pentaerythritol triacrylate, ditrimethylolpropane tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol penta / hexaacrylate, tripropylene diacrylate, trimethylolpropane ethoxylate triacrylate, trimethylolpropane propoxylate triacrylate, di(trimethylolpropane)tetraacrylate, glycerol propoxylate triacrylate, pentaerythritol propoxylate triacrylate, poly(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, and tri(propylene glycol) diacrylate; 37. The method according to paragraph 36.

[0053] 38. (iia) the second set of monomers are selected from one or more of N,N'-methylenebis(acrylamide), 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or (iib) the crosslinking agent is selected from one or more of divinylbenzene, ethylene glycol dimethyl acrylate, and bisphenol A dimethacrylate; 38. The method according to paragraph 37.

[0054] 39. (iiia) the weight:weight ratio of the first set of monomers to the second set of monomers, if present, is from 40:1 to 1:1, for example from 20:1 to 2:1; and / or (iiib) the weight:weight ratio of the first set of monomers:crosslinker, if present, is from 40:1 to 1:1, for example from 20:1 to 2:1; 39. The method according to any one of items 36 to 38.

[0055] 40. Item 40. The method according to any one of items 18 to 39, wherein the molar ratio of the water-soluble initiator compound:the hydrophilic polymeric stabilizer compound is from 10:1 to 10000:1, such as from 20:1 to 5000:1, for example from 30:1 to 1000:1, for example from 50:1 to 500:1.

[0056] 41. 41. The method according to any one of items 18 to 40, wherein the concentration of the hydrophilic polymeric stabilizer compound in the aqueous solution is 0.01% by weight to 20% by weight, for example 0.05% by weight to 10% by weight, for example 0.1% by weight to 5.0% by weight.

[0057] 42. 41. The method according to any one of items 18 to 40, wherein the method is substantially free of (or free of) surfactants and organic solvents.

[0058] (drawing) Certain embodiments of the present disclosure will now be described more fully with reference to the accompanying drawings. [Brief description of the drawings]

[0059] [Figure 1] Figure 1 shows the proposed mechanism of “monomer-deficient polymerisation initiation and nucleation using pre-formed macroradical via H-abstraction”. [Diagram 2] Figure 2 shows a schematic diagram of the macroradical formed from polyvinylpyrrolidone (PVP), polyacrylic acid (PAA) and chitosan after H-abstraction. [Diagram 3] FIG. 3 shows an SEM image of the polystyrene beads of Sample 1. [Figure 4] FIG. 4 shows an SEM image of the polystyrene beads of Sample 2. [Diagram 5] FIG. 5 shows an SEM image of the polystyrene beads of Sample 3. [Figure 6] FIG. 6 shows an SEM image of the polystyrene beads of Sample 4. [Figure 7] FIG. 7 shows an SEM image of the polystyrene beads of Sample 5. [Figure 8] FIG. 8 shows an SEM image of the polystyrene beads of Sample 1 after incubation with THF. [Figure 9] FIG. 9 shows an SEM image of the polystyrene beads of Sample 5 after incubation with THF. [Figure 10] FIG. 10 shows an SEM image of the polystyrene beads of Sample 6. [Figure 11] FIG. 11 shows SEM images of the polystyrene beads of Sample 7, showing (A) the polydispersity of the beads and (B) the anomalous regions of the beads. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0060] (explanation) The present invention solves one or more of the above identified problems.

[0061] Surprisingly, it has been found that it is possible to produce monodisperse polymer particles that can be used for a range of applications. Such monodisperse polymer particles have a surprising degree of monodispersity, which, as mentioned above, can be used in a wide range of applications making the particles highly desirable. For example, monodisperse polymer particles may be suitable for clinical diagnostic methods (e.g. immunodiagnostic applications). They may also be suitable for use in applications related to micro- and nanofluidics and nanotechnology in general.

[0062] Thus, according to a first aspect of the present invention there is provided a polymeric particle comprising a plurality of polymeric stabilising moieties and a plurality of hydrophobic polymer chains. The plurality of polymeric stabilizing components each comprises one or more hydrophilic polymer chains. Each of the hydrophobic polymer chains is covalently attached to one or more of the polymeric stabilizing moieties. The polymer particles are monodisperse and the coefficient of variation based on the diameter of the polymer particles is less than 20%.

[0063] In the embodiments of the present disclosure, the term "comprising" may be interpreted as requiring the mentioned (or described) features, but not limiting the presence of other features. Alternatively, the term "comprising" may relate to a situation (or case) where only the listed (or described) elements (or ingredients or components) / features (or configurations or features) are intentionally present (e.g., the term "comprising" may be replaced with the phrase "consist of" or "consist essentially of"). It is expressly expected that both the broader and narrower interpretations are applicable to all aspects and embodiments of the present invention. In other words, the term "comprising" and its synonyms may be replaced with the phrase "consisting of" or the phrase "consist essentially of" or their synonyms, and vice versa.

[0064] As used in this disclosure, the term "monodisperse" refers to particles having a low coefficient of variation (CV) for a particular parameter (e.g., particle diameter). For example, it refers to particles having a CV of less than 20%, such as less than 15%, such as less than 10%, such as less than 5%. More specifically, the particles may have a CV of 2% or less, such as 1% or less. The term "monodisperse" also encompasses the term "highly monodisperse". "Highly monodisperse" as used in this disclosure refers to a CV of less than 5%, such as less than 2%, such as less than 1%.

[0065] As used in this disclosure, the term "coefficient of variation" refers to its statistical meaning, namely:

[0066]

number

[0067] The terms "standard deviation" and "mean" refer to their ordinary statistical meaning.

[0068] As explained below in this disclosure, the diameter of the polymer particles may be measured by imaging (or image processing) techniques (eg, SEM images).

[0069] The polymer particles (or polymer particles) disclosed herein may have any suitable average diameter (or mean diameter). For example, the polymer particles may have an average diameter of 50-1000 nm, such as 100-600 nm, such as 120-450 nm, such as 150-400 nm, such as 200-350 nm. It is understood that each batch of polymer particles has a very small coefficient of variation between their diameter dimensions (or sizes), as required above.

[0070] The polymer particles each consist of a network formed from a plurality of polymer stabilizing components that form a backbone from which extend a plurality of hydrophobic polymer chains.

[0071] Any suitable hydrophilic polymer chain can be used as the polymer stabilizing component. The hydrophilic polymer chain can be activated at multiple sites by a free radical initiator. Examples of suitable hydrophilic polymer chains that can be used in the present disclosure include, but are not limited to, poly(vinylpyrrolidone), polyethyleneimine, polyacrylic acid, polyvinyl alcohol, water-soluble polysaccharides (e.g., hydroxypropylmethylcellulose, chitosan, and blends thereof), copolymers thereof, and blends thereof. In a specific example that can be mentioned in the present disclosure, the hydrophilic polymer chain of the polymer stabilizing component can be poly(vinylpyrrolidone).

[0072] When activated by a free radical initiator, each such hydrophilic polymer chain is believed to contain multiple radical sites. Each such radical site is then believed to be capable of promoting the formation of a hydrophobic polymer chain when a hydrophobic monomer is introduced into the reaction mixture. However, without wishing to be bound by theory, it is understood that these many radical sites on separate hydrophilic polymer chains may cross-react together. In this way, two (or more than two, e.g., multiple) hydrophilic polymer chains may be directly cross-linked together to form a network of hydrophilic polymer chains. Meanwhile, other radical sites are still retained that can react with a hydrophobic monomer to form a hydrophobic polymer chain. Additionally, the hydrophobic polymer chain may terminate the chain by reacting with a radical site on a hydrophilic polymer chain. Thereby, two hydrophilic polymer chains (or one chain and one network, or two networks) may be indirectly cross-linked together.

[0073] Any suitable hydrophobic monomer can be used to form the hydrophobic polymer chain referred to in this disclosure. The hydrophobic monomer is one that can undergo radical chain reaction. Examples of suitable hydrophobic monomers include styrene and its derivatives, acrylate(s), alkyl acrylate(s) and combinations thereof. Examples of styrene and its derivatives include, but are not limited to, styrene, 4-methylstyrene, 3-methylstyrene and 4-tert-butylstyrene. Examples of acrylate(s) include, but are not limited to, methyl acrylate, ethyl acrylate, propyl acrylate, and more specifically, butyl acrylate. Examples of alkyl acrylate(s) include, but are not limited to, 2,2,2-trifluoroethyl methacrylate and methyl methacrylate. In certain embodiments of the invention that may be referred to in this disclosure, the hydrophobic monomer may be styrene.

[0074] In the polymer particles disclosed herein, any suitable weight:weight ratio of polymer stabilizing component:multiple hydrophobic polymer chains may be used.The suitable weight:weight ratio example of polymer stabilizing component:multiple hydrophobic polymer chains that may be mentioned in the present disclosure may be 1:1000 to 1:1, for example 1:500 to 1:2, for example 1:300 to 1:3, for example 1:150 to 1:5.

[0075] As will be appreciated, the base polymer particle may be useful as is. However, it may be advantageous to incorporate additional properties into the polymer particle, which may open up additional potential applications for such monodisperse materials. This may be accomplished by forming the hydrophobic polymer chains as copolymers and / or by using crosslinking agents.

[0076] As will be understood, the above hydrophobic polymer chain may already include a copolymer formed by two or more hydrophobic monomeric materials. Thus, as used herein, the term "copolymer" may refer specifically to the incorporation of a monomer. The monomer is one that has (or carries) a pendant reactive functionality (or a pendant reactive functional group or pendant reactive functionality). These are then incorporated into the hydrophobic polymer chain. For example, when the hydrophobic polymer chain is a copolymer, the copolymer may be formed from the following first set of monomers and second set of monomers: The first set of monomers are hydrophobic monomers selected from one or more of styrene and its derivatives, acrylates, and alkyl acrylates. The second set of monomers is one or more selected from a monomer having a carboxylic acid group, a monomer having a hydroxyl group, a monomer having an amino group, and a monomer having an epoxy group.

[0077] The first set of monomers are the same materials as those mentioned above as monomers that can be used to form hydrophobic polymer chains. For example, the above definitions apply here and will not be repeated. The second set of monomers are materials that have (or bear) pendant reactive functionalities (e.g., free hydroxyl groups, free carboxylic acids, etc.) that are subsequently incorporated into the hydrophobic polymer chain. Examples of such materials include, but are not limited to, acrylic acid, methacrylic acid, 2-carboxyethyl acrylate, acrylamide, methacrylamide, allylamine, (hydroxyethyl)methacrylate, hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, glycidyl methacrylate, allyl glycidyl ether, 1,2-epoxy-5-hexene, 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, triallylamine, and combinations thereof.

[0078] As will be appreciated, since the hydrophobic polymer chain is intended to have (or retain) at least some hydrophobic character, the first set of monomers will be for the majority of the hydrophobic polymer chain, forming at least 50%. For example, the weight:weight ratio of the first set of monomers to the second set of monomers may be from 40:1 to 1:1, such as from 20:1 to 2:1.

[0079] It should be noted that the introduction of the second set of monomers into the hydrophobic polymer chain introduces functionality, such as carboxylic acid groups, which can be used for further reactions (e.g., in immunodiagnostic applications). For example, the reactive functional groups described above can be used to conjugate with antibodies that react with antigens in the immunodiagnostic test to which they are applied.

[0080] When the hydrophobic polymer chains are crosslinked together, a suitable crosslinking agent capable of reacting with the first set of monomers and / or the second set of monomers (if present) may be used. Examples of suitable crosslinking agents include monomeric materials having two or more unsaturated groups (i.e., those that can participate in radical chain extension of the hydrophobic polymer chains). Specific examples of crosslinking agents that may be mentioned in this disclosure include, but are not limited to, divinylbenzene, ethylene glycol dimethylacrylate, bisphenol A dimethacrylate, butanediol dimethacrylate, tricyclodecane dimethanol diacrylate, pentaerythritol triacrylate, tripropylene glycol diacrylate, propoxylated neopentyl diacrylate, pentaerythritol triacrylate, ditrimethylolpropane tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol penta / hexaacrylate, tripropylene diacrylate, trimethylolpropane ethoxylate triacrylate, trimethylolpropane propoxylate triacrylate, di(trimethylolpropane)tetraacrylate, glycerol propoxylate triacrylate, pentaerythritol propoxylate triacrylate, poly(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, and combinations thereof.

[0081] Any suitable amount of crosslinker may be incorporated into the hydrophobic polymer chain to result in a crosslinked structure. For example, the weight:weight ratio of the first set of monomers to the second set of monomers may be 40:1 to 1:1, such as 20:1 to 2:1. As used in this disclosure, the term "first set of monomers" is intended to refer to hydrophobic monomers that, in the absence of the crosslinker and / or the second set of monomers, form the entirety of the hydrophobic polymer chain. The second set of monomers are those that have (or retain) pendant reactive functionalities (or pendant reactive functional groups or pendant reactive functionalities). These are then incorporated into the hydrophobic polymer chain.

[0082] The crosslinking monomer can improve the solvent resistance of the polystyrene particles.

[0083] In an embodiment of the invention disclosed herein, the polymer particles have the formula: -SO4 - M + where the dash (-) represents the point of attachment to the polymer particle. + is Na + , K + or NH4 + may be represented as:

[0084] In certain embodiments of the invention that may be mentioned in the present disclosure, the hydrophobic polymer chains in the polymer particles may be formed from: Styrene alone; Styrene and one or more of N,N'-methylenebis(acrylamide), 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine and triallylamine (as copolymers); Styrene crosslinked with a crosslinker selected from one or more of divinylbenzene, ethylene glycol dimethyl acrylate, and bisphenol A dimethacrylate; or Styrene and one or more of N,N'-methylenebis(acrylamide), 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine and triallylamine (as copolymers), crosslinked with a crosslinker selected from one or more of divinylbenzene, ethylene glycol, dimethyl acrylate, bisphenol A dimethacrylate.

[0085] The present disclosure also discloses a method for producing (or generating) polymer particles, the method comprising the following (or processes or steps): (A) reacting a water-soluble initiator compound (or a water-soluble initiator compound) with a hydrophilic polymer stabilizer compound (or a hydrophilic polymer stabilizer compound) in water to form an aqueous macroinitiator complex (or a macroinitiator complex or a macroinitiator complex); (B) adding one or more water-immiscible monomers to the aqueous macroinitiator complex to form a biphasic polymerisation reaction mixture and reacting for a first period of time until particle nucleation occurs; and (C) continuing the reaction for a second period of time or quenching the reaction after the first period of time (or process or step) to obtain polymer particles. The polymer particles are monodisperse, that is, the coefficient of variation based on the diameter of the polymer particles is less than 20%.

[0086] As will be appreciated, the full details of the product have been described above and will not be repeated here for the sake of brevity.

[0087] As used in this disclosure, the term "macroinitiator complex" refers to either a single polymer strand or a crosslinked set of two or more polymer strands. A single polymer strand is a polymer strand of a hydrophilic polymeric stabilizer compound that contains multiple radicals along the polymer backbone. A polymer strand is a polymer strand of a hydrophilic polymeric stabilizer compound (each crosslink formed by a radical reaction between the polymer strands). A crosslinked set of two or more crosslinked polymer strands contains multiple radicals along the polymer backbone. The macroinitiator complexes described above are used to initiate the growth of hydrophobic polymer chains. Here, multiple hydrophobic polymer chains may be formed on the backbone of each macroinitiator complex. As will be appreciated, a macroinitiator complex is formed by a reaction between a hydrophilic polymeric stabilizer compound and a water-soluble initiator compound. This may result in the formation (or generation) of free radicals that abstract hydrogen atoms from the hydrophilic polymeric stabilizer compound, thereby forming (or generating) free radicals along the polymer backbone of the compound.

[0088] Any suitable water-soluble initiator may be used in the present disclosure. Examples of suitable water-soluble initiators include peroxide initiators (or peroxide initiators or peroxide initiators), persulfate salts (or persulfate salts or persulfate salts), azo initiators (or azo initiators), and combinations thereof. Specific examples of water-soluble initiators include, but are not limited to, tertiary amyl hydroperoxide, potassium persulfate, sodium persulfate, ammonium persulfate, 4,4'-azobis(4-cyanovaleric acid), 2,2'-azobis[2-methyl-N-(2-hydroxyethyl)propionamide, 2,2'-azobis[N-(2-carboxyethyl)-2-methylpropionamidine]hydrate, 2,2'-azobis(2-methylpropionamidine)dihydrochloride, 2,2''-azobis[2-(2-imidazolin-2-yl)propane], 2,2'-azobis[2-(2-imidazolin-2-yl)propane]dihydrochloride, and combinations thereof. In certain embodiments that may be mentioned in the present disclosure, the water-soluble initiator may be one or more selected from potassium persulfate, sodium persulfate, and ammonium persulfate. In further specific embodiments that may be mentioned in the present disclosure, the water soluble initiator may be sodium persulfate.

[0089] Additionally or alternatively, the water-soluble initiator may be a redox pair (or oxidation-reduction pair). Any suitable redox pair may be used in the present disclosure. For example, the redox pair may be selected from ascorbic acid and hydrogen peroxide, or ammonium persulfate and sodium bisulfite.

[0090] As will be appreciated, the above materials can automatically form (or generate) radicals when subjected to the correct conditions for this purpose. For example, when heated in aqueous solution, persulfate ions undergo thermal decomposition to produce two sulfate ion radicals (SO4 -Such radicals are capable of abstracting hydrogen atoms from the polymer molecule, thus forming (or generating) radicals in the polymer backbone.

[0091] Any suitable molar ratio (water-soluble initiator compound:hydrophilic polymeric stabilizer compound) can be used. For example, the molar ratio of water-soluble initiator compound:hydrophilic polymeric stabilizer compound can be 10:1 to 10000:1, such as 20:1 to 5000:1, such as 30:1 to 1000:1, such as 50:1 to 500:1. For the avoidance of doubt, where a number of numerical ranges relating to the same feature are listed in this disclosure, it is expressly contemplated that the end values ​​of each range are intended to be combined in any order to provide further contemplated ranges (and still be implicitly disclosed ranges). Thus, in relation to the numerical ranges relating to the above, the following ranges are disclosed: 10:1~20:1, 10:1~30:1, 10:1~50:1, 10:1~500:1, 10:1~1000:1, 10:1~10000:1 20:1~30:1, 20:1~50:1, 20:1~500:1, 20:1~1000:1, 20:1~10,000:1 30:1~50:1, 30:1~500:1, 30:1~1000:1, 30:1~10,000:1 50:1~500:1, 50:1~1000:1, 50:1~10000:1, 500:1 to 1000:1, 500:1 to 10,000:1, and 1000:1~10,000:1

[0092] The hydrophilic polymeric stabilizer compound corresponds to a plurality of polymeric stabilizer components. Each polymeric stabilizer component comprises one or more hydrophilic polymer chains. For example, the same polymeric materials as described above as hydrophilic polymer chains may be used in the present disclosure. In a specific embodiment that may be mentioned in the present disclosure, the hydrophilic polymeric stabilizer compound may be poly(vinylpyrrolidone) and / or a water-soluble polysaccharide (e.g., hydroxypropylmethylcellulose).

[0093] Any suitable concentration of the hydrophilic polymeric stabilizer compound may be used in the aqueous solution of step (A). For example, the concentration of the hydrophilic polymeric stabilizer compound in the aqueous solution of step (A) may be 0.01% to 20% by weight, such as 0.05% to 10% by weight, such as 0.1% to 5.0% by weight. The degree of crosslinking in the macroinitiator complex is highly dependent on the concentration of the hydrophilic polymeric stabilizer compound added to the aqueous solution. In turn, the degree of crosslinking in the macroinitiator complex affects the diameter of the formed polymer particles, the monodispersity of the beads, and the stability of the beads. It is believed (without wishing to be bound by theory) that the macroinitiator helps to avoid bead agglomeration and promotes the formation of highly monodisperse polystyrene beads.

[0094] The water-immiscible monomers may be monomers used to form the hydrophobic polymer chains mentioned above in the product of the polymer particles. For example, the water-immiscible monomer may be one or more selected from styrene and its derivatives, acrylate(s) and alkyl acrylate(s). Examples of styrene and its derivatives include, but are not limited to, styrene, 4-methylstyrene, 3-methylstyrene and 4-tert-butylstyrene. Examples of acrylate(s) include, but are not limited to, methyl acrylate, ethyl acrylate, propyl acrylate, and more specifically, butyl acrylate. Examples of alkyl acrylate(s) include, but are not limited to, 2,2,2-trifluoroethyl methacrylate and methyl methacrylate. In certain embodiments of the invention that may be mentioned in this disclosure, the water-immiscible monomer may be styrene.

[0095] In an embodiment of the invention, the weight:weight ratio of hydrophilic polymeric stabiliser compound:water immiscible monomer may be from 1:1000 to 1:1, such as from 1:500 to 1:2, such as from 1:300 to 1:3, such as from 1:150 to 1:5.

[0096] In the reaction mixture of step (B) (or step (B)), the concentration of the water-immiscible monomer may be 0.1-40.0% by weight, such as 1-30% by weight, for example 2-20% by weight. The colloidal solution formed (or produced) may have a dry mass of 0.1%-40% by weight, preferably 1%-30% by weight, more preferably 2%-20% by weight, based on the weight of the solution.

[0097] As mentioned above, the monomer material is water-immiscible. This is important for the success of the method described here. It is believed (without wishing to be bound by theory) that the water-immiscible monomer is constantly dissolved from the oil phase into the water phase to feed the polymerization process. This results in a lower concentration of the water-immiscible monomer in the water phase, which slows down the polymerization rate and lengthens the nucleation process. The resulting biphasic polymerisation reaction mixture is different from the reaction mixture formed (or produced) from a conventional homogeneous dispersion polymerisation, where the monomer concentration is higher in the organic solvent phase. The macroinitiator complex is hydrophilic and therefore also helps to retard the nucleation process by keeping the polymerisation product in the water phase. It is believed (without wishing to be bound by theory) that the slow and lengthy nucleation process results in the production of highly monodisperse polymer particles (or beads).

[0098] It should be noted that after step (B) (or step (B)) is completed, the remaining part of the process described below is not capable of nucleating new polymer particles. The period to obtain particle nucleation may be from 15 minutes to 45 minutes.

[0099] As mentioned above, step (C) of the method may result in quenching (or stopping) of the particles formed (to provide monodisperse polymer particles of minimum size) or the reaction may be allowed to continue. If the reaction is allowed to continue without introducing new material (e.g. potential copolymerization material), then the particle dimensions (or size) may simply grow to provide monodisperse polymer particles as described hereinabove. Alternatively, if additional functionality (or functional groups or functionality) is desired at this time, a second set of monomers and / or crosslinkers are added to the reaction mixture to form a product in which the hydrophobic polymer chains contain polymers with pendant reactive functionalities (or pendant reactive functional groups or pendant reactive functionality) and / or the hydrophobic polymer chains are crosslinked together.

[0100] In step (C) (or step (C)), when a second set of monomers is added to the reaction mixture, one or more of monomers having a carboxylic acid group, monomers having a hydroxyl group, monomers having an amino group, and monomers having an epoxy group may be selected. When a crosslinking agent is added to form crosslinks, the crosslinking agent may be a monomer having two or more unsaturated groups. For example, the second set of monomers and crosslinking agent are the same as those described in detail above for the product of polymer particles. Here, they will not be described again for the sake of brevity.

[0101] When a second set of monomers is added to the reaction mixture, the weight:weight ratio of the first set of monomers (i.e., water immiscible monomers):second set of monomers is 40:1 to 1:1, for example, 20:1 to 2:1. When a crosslinker is added to the reaction mixture, the weight:weight ratio of the first set of monomers (i.e., water immiscible monomers):crosslinker is 40:1 to 1:1, for example, 20:1 to 2:1.

[0102] According to the disclosed method, the particle size and dispersibility of the polymer particles formed can be controlled by the molecular weight and concentration of the macroinitiator complex. The macroinitiator complex is hydrophilic. This allows larger particle dimensions to be achieved because it retards the nucleation process of the polymer particles. The polymer beads or particles formed are crosslinked, stable, and free of organic solvents and surfactants.

[0103] The advantages of the disclosed method include the following (1) to (7). (1) The provision of monodisperse polymer particles having a particle size (or size or particle diameter or particle size) range or average diameter of 100-370 nm can be achieved. With conventional surfactant-free (or surfactant-free) methods, it has not been possible to provide beads larger than 250 nm (especially with respect to polystyrene beads). (2) Control of both monodispersity (or degree of monodispersity) and size (or size or particle diameter or particle size) can be consistently achieved. Previous methods have found that achieving larger particle sizes compromises monodispersity. (3) The method is a one-pot process and corresponds to the particle size of the target immunodiagnostic assay. (4) Traditionally, the addition of comonomers or a second set of monomers adversely affects size and monodispersity. In this method, the comonomers can be added after nucleation and do not significantly affect the overall system. (5) In this method, the macroinitiator complex plays a dual role as a nucleation template and a cross-linker. (6) By using hydrophilic macroinitiator complexes, secondary nucleation is suppressed, resulting in highly monodisperse beads. (7) This method potentially allows the direct use of commercially available monomers, without the need for purification (e.g., treatment with NaOH) to remove the stabilizer (4-tert-butylcatechol).

[0104] Further aspects and embodiments of the present invention are provided in the following non-limiting examples. EXAMPLES

[0105] (Example) The present invention relates to highly monodisperse polymer particles or beads obtained by a novel "monomer-deficient polymerisation initiation and nucleation" strategy, which is distinct from conventional dispersion, emulsion and surfactant-free emulsion polymerization.

[0106] In one embodiment of the present invention, highly monodisperse polystyrene particles (or polystyrene beads) having particle dimensions (or sizes or diameters or particle sizes) between 100 and 370 nm are prepared in a one-pot synthesis involving water (alone) as the solvent, styrene monomer 40, and hydrophilic macroradical 100 (formed by mixing a water-soluble initiator 20 and a hydrophilic polymeric stabilizer 30), as shown in the schematic diagram of FIG.

[0107] In step 1, a homogeneous aqueous solution (B) is formed. The aqueous solution (B) contains a hydrophilic macroradical 100 (or a macroinitiator complex). The aqueous solution (B) is formed by adding a water-soluble initiator 20 (e.g., a persulfate initiator) and a hydrophilic polymer stabilizer 30 (e.g., a PVP stabilizer) to water, and then heating the solution (A). This activates the initiator and generates new free radicals in the hydrophilic polymer stabilizer 30 by abstracting hydrogen (or hydrogen abstraction or hydrogen abstraction).

[0108] In step 2, styrene monomer 40 is then added to (B) to form a two-phase system (C) comprising an oil phase and an aqueous phase, where the oil phase is substantially formed from styrene monomer 40.

[0109] Styrene monomers 40 slowly dissolve into the aqueous phase as droplets 80. Hydrophilic macroradicals 100 initiate polymerization of the styrene monomers 40, which causes polystyrene 50 to precipitate and form nuclei in the aqueous phase of the two-phase system (D) (step 3).

[0110] If desired, a comonomer can be added after the nucleation of the polystyrene 50 is complete (not shown in Figure 1).

[0111] (Process 1) Typically, in step 1, a hydrophilic polymer stabilizer and a water-soluble initiator are completely dissolved in water at room temperature to form a uniform (or homogeneous) mixture (A). The system is then heated to a temperature above the thermal decomposition temperature of the initiator. The thermal decomposition temperature is typically 40 to 100°C (e.g., 60 to 90°C). Free radicals are formed (or generated) by the thermal decomposition of the initiator. The water-soluble initiator can be selected from peroxide initiators (or peroxide initiators), persulfates (or persulfate salts or persulfate salts) and azo initiators. For example, a persulfate initiator is thermally decomposed to produce two types of radicals, sulfate ion radicals (SO4· - ) and hydroxyl radicals (·OH), which can abstract hydrogen atoms from polymer molecules to form hydrophilic macroradicals. In one embodiment of the present invention, sodium persulfate (SPS) is used as the initiator, which is cheaper than KPS, APS and AIBA. This is believed to be the first reported use of SPS in the surfactant-free polymerization of styrene.

[0112] Generally, free radical sites are formed by abstracting a hydrogen atom from the alpha (α) carbon of hydrophilic polymeric stabilizers. The mechanism of hydrogen (H) abstraction for selected hydrophilic polymeric stabilizers is shown in Figure 2. Hydrogen (H) abstraction occurs from the vinyl group of PVP to form a macroradical. In the vicinity of the unpaired electron, it may rearrange to a more stable state by chain scission via disproportionation. A similar process also causes hydrogen (H) abstraction from the vinyl group of PAA. The formation of radicals in chitosan is due to the attack of an anionic radical on the C-4 carbon, resulting in the radical migrating to the C-4 carbon (C), where a hydrogen is removed from the C-4 carbon (C).

[0113] (Process 2) Typically, the monomer used in step 2 should have limited solubility in water (or should be water immiscible) to form a two-phase system (C). For example, the solubility of styrene in water is 0.030 g styrene / 100 g solution at 25° C. (JACS 1950, 72, 5034-5037) and 0.058 g / 100 g solution at 65° C. (Ind. Eng. Chem. Anal. Ed. 1946,18, 295-296). As styrene slowly dissolves in the water phase, it is grafted onto the macroradical formed from step 1, triggering the continued dissolution of styrene and polymerization of styrene.

[0114] (Step 3) Typically, in step 3, the process of polymer precipitation and nucleation proceeds in the aqueous phase. For example, conjugation of PVP with branched styrene oligomers results in a decrease in solubility in water. As the polystyrene chains grow longer, the polymer begins to nucleate in the aqueous phase. The process of polystyrene precipitation and nucleation is similar to homogeneous dispersion polymerization, but differs in that it occurs in a two-phase system.

[0115] The monodispersity of the polymerization product appears to be due to the low solubility of styrene monomer in the water phase. Styrene is constantly dissolved from the oil phase into the water phase to feed the polymerization process and grow polystyrene beads. This leads to a low concentration of styrene in the water phase, especially in the early stages of polymerization. This slows down the polymerization rate and lengthens the nucleation process (about 30 minutes). In contrast, the nucleation process of homogeneous dispersion polymerization is much faster (about 10 minutes) due to the high styrene concentration. The hydrophilic macroradicals also help to slow down the nucleation process by allowing the polymerization product to remain in the water phase for a longer time. The precipitation of polystyrene then begins. It is believed (without wishing to be bound by theory) that the slow and lengthy nucleation process leads to the formation of highly monodisperse polystyrene beads.

[0116] After the nucleation begins, the polystyrene particles swell and become concentrated with styrene monomer, which can accelerate the rate of polymerization. This can cause the polystyrene beads to become more spherical, giving beads with a smooth surface. As a result, the particles grow larger and denser. The polymerization is terminated when all the styrene monomer is used and incorporated into the monodisperse polystyrene beads.

[0117] If desired, comonomers can be added to the polystyrene beads (or after nucleation is complete) to increase the rigidity of the particles (or beads) or to functionalize the surface (by adding comonomers with functional groups).

[0118] (material and method) Materials were purchased from the following sources:

[0119] Styrene (Tokyo Chemical Industry Co. Ltd. (TCI), stabilized with 4-tert-butylcatechol, >99.0% (GC)) Sodium persulfate (Na2S2O8, SPS; Alfa Aesar, crystalline, 98%) Polyvinylpyrrolidone (PVP; K30, MW= 45000-58000; K60, MW= 270,000-400,000; K90, MW= 1,000,000-1,500,000; TCI, total nitrogen 12.0%-12.8% (calculated on anhydrous material); water (max) 7.0%, K value 26.0-34.0) Sodium chloride (NaCl; Alfa Aesar, ACS, 99.0% (min)) Acrylic acid (TCI;>99.0%(GC)) Divinylbenzene (DVB; Sigma-Aldrich, 85%)

[0120] Deionized (DI) water was obtained from ELGA Ultrapure Water Treatment Systems (PURELAB Option). Hydrochloric acid, Sigma-Aldrich, 37% Sodium hydroxide, BioXtra, ≥98% (acidometric), pellets (anhydrous)

[0121] SEM imaging was performed using a JEOL JSM 6700F according to the procedure described in CrystEngComm, 2017,19, 552-561. References to "average" diameter refer to the average diameter obtained from the SEM. The mechanical stirrer was a Wiggens WB2000-M overhead stirrer.

[0122] The coefficient of variation (CV)% of polystyrene beads was calculated from the measurement of SEM images. A drop of the as-synthesized latex solution was placed on a flat surface (e.g., aluminum foil) and allowed to dry overnight at ambient temperature. The obtained samples were attached (or mounted) on SEM stubs using conductive double-sided carbon tape. The stubs with the samples attached were sputter-coated with a thin layer of platinum. The prepared samples were examined with a SEM (Model JEOL JSM 6700F). For all samples, the diameters of 100 randomly selected particles were measured from the 30,000x images, and the standard deviation was calculated accordingly.

[0123] A mechanical stirrer (200 rpm) was used in all polymerization processes. DI water was bubbled with nitrogen for 20 min to remove oxygen before use. SPS, PVP, NaCl, acrylic acid, DVB, and styrene were used as received without purification.

[0124] Example 1 In a 250 mL two-neck round-bottom glass reactor equipped with a mechanical stirrer, SPS (76 mg), PVP (K60, 1 g), NaCl (584 mg) and DI water (100 mL) were added. The side neck of the reactor was then sealed with a rubber septum and nitrogen was introduced through a needle to sweep the air from inside the reactor. The mixture was stirred for about 5 min to obtain a homogeneous solution at room temperature. It was then heated in an oil bath at 70 °C for about 10 min. The required amount of styrene (10 mL) was quickly injected into the reactor with a syringe. The styrene formed an oil layer on top of the aqueous solution. The resulting mixture slowly became cloudy and turned into a white suspension after 30 min. This indicated a slow polymerization rate and nucleation process. The polymerization mixture was stirred overnight at 70 °C for 20 h. A milky colloidal solution was obtained. The as-synthesized colloidal solution was designated as "Sample 1." The surface morphology of the sample was observed using a scanning electron microscope (JOEL JSM-6700).

[0125] The SEM image (Figure 3) shows that the diameter of the resulting polystyrene beads is 260 nm with a CV of 1%. No anomalous regions were observed in the polystyrene beads.

[0126] This experiment shows that preformed macroradicals lead to highly monodisperse polystyrene beads under high ionic strength reaction conditions (contributed by NaCl).

[0127] Example 2 In a 250 mL two-neck round-bottom glass reactor equipped with a mechanical stirrer, SPS (86 mg), PVP (K30, 200 mg) and DI water (100 mL) were added. The side neck of the reactor was then sealed with a rubber septum and nitrogen was introduced through a needle to sweep the air from inside the reactor. The mixture was stirred for about 60 min to obtain a homogeneous solution at room temperature. It was then heated in an oil bath at 70 °C for about 20 min. The required amount of styrene (30 mL) was quickly injected into the reactor with a syringe. The styrene formed an oil layer on top of the aqueous solution. The resulting mixture slowly became cloudy and turned into a white suspension after 30 min. This indicated a slow polymerization rate and nucleation process. The polymerization mixture was stirred overnight at 70 °C for 20 h. A milky colloidal solution was obtained. The as-synthesized colloidal solution was designated as "Sample 2." The surface morphology of the sample was observed using a scanning electron microscope (JOEL JSM-6700).

[0128] The SEM image (Figure 4) shows that the diameter of the resulting polystyrene beads is 310 nm with a CV of 1%. No anomalous regions were observed in the polystyrene beads.

[0129] This experiment shows that preformed macroradicals lead to highly monodisperse polystyrene beads under low ionic strength reaction conditions (in the absence of NaCl).

[0130] Example 3 In a 250 mL two-neck round-bottom glass reactor equipped with a mechanical stirrer, SPS (57 mg), PVP (K90, 1 g) and DI water (100 mL) were added. The side neck of the reactor was then sealed with a rubber septum and nitrogen was introduced through a needle to sweep the air from inside the reactor. The mixture was stirred for about 5 min to obtain a homogeneous solution at room temperature. It was then heated in an oil bath at 70 °C for about 3 min. The required amount of styrene (10 mL) was quickly injected into the reactor with a syringe. The styrene formed an oil layer on top of the aqueous solution. The resulting mixture slowly became cloudy and turned into a white suspension after 30 min. This indicated a slow polymerization rate and nucleation process. The polymerization mixture was stirred overnight at 70 °C for 20 h. A milky colloidal solution was obtained. The as-synthesized colloidal solution was designated as "Sample 3." The surface morphology of the sample was observed using a scanning electron microscope (JOEL JSM-6700).

[0131] The SEM image (Figure 5) shows that the diameter of the resulting polystyrene beads is 120 nm with a CV of 2%. No anomalous regions were observed in the polystyrene beads.

[0132] This experiment shows that preformed macroradicals can produce highly monodisperse polystyrene beads with diameters as small as 120 nm using low initiator concentrations.

[0133] Example 4 In a 250 mL two-neck round-bottom glass reactor equipped with a mechanical stirrer, SPS (46 mg), PVP (K60, 100 mg) and DI water (100 mL) were added. The side neck of the reactor was then sealed with a rubber septum and nitrogen was introduced through a needle to sweep the air from inside the reactor. The mixture was stirred for about 5 min to obtain a homogeneous solution at room temperature. It was then heated in an oil bath at 70 °C for about 3 min. The required amount of styrene (30 mL) was quickly injected into the reactor with a syringe. The styrene formed an oil layer on top of the aqueous solution. The resulting mixture slowly became cloudy and turned into a white suspension after 30 min. This indicated a slow polymerization rate and nucleation process. The polymerization mixture was stirred at 70 °C for 10 h. Acrylic acid (5 wt.% relative to styrene) was then added and polymerization was continued for another 20 h at 70 °C. A milky white colloidal solution was obtained. The as-synthesized colloidal solution was designated as "Sample 4". The surface morphology of the sample was observed using a scanning electron microscope (JOEL JSM-6700).

[0134] (SEM) The SEM image (Figure 6) shows that the diameter of the resulting polystyrene beads is 267 nm with a CV of 1%. No anomalous regions were observed in the polystyrene beads.

[0135] (Acid titration) The carboxyl groups on the surface of polystyrene particles were measured using a previously reported acid titration method (Journal of Colloid and Interlace Science, 1974, 49, 3,425-432). An accurately weighed sample of latex (containing approximately 1 g of polymer solids) was diluted to a volume of 25 ml with deionized water (in a 50 mL container). The pH value of the diluted latex sample was adjusted to 11.0 ± 0.2 by adding diluted NaOH solution. Meanwhile, the pH value was monitored using a pH meter (Hanna Instruments, HI2211). A conductance probe (Hanna Instruments, EC portable meter) was then placed in the diluted latex dispersion. The sample was titrated with a standard 0.421 N aqueous hydrochloric acid (HCl) solution. Each 0.050 mL increment was accompanied by mechanical stirring with a 1 minute interval between two increments. The conductivity of the latex dispersion was monitored using an EC portable meter. The temperature was maintained at approximately 25° C. throughout the titration process.

[0136] The titration end point is determined according to the literature (Journal of Colloid and Interlace Science, 1974, 49, 3, 425-432). The acid concentration is expressed as milliequivalent charge per gram of polymer solids (MEQ / g). The "surface-bound" acid concentration is calculated from the following formula:

[0137]

number

[0138] During the ceremony, Vsb is the volume of HCl titrant (in cc) required to neutralize the "surface bound" acid. N is the normality of the HCl titrant. W is the sample weight of the latex. S is the fraction (or fraction or percentage) of polymer solids in the latex.

[0139] This experiment shows that the density of surface-bound acid is 0.22 mmol / g. This experiment shows that monodisperse beads rich in carboxyl groups can be achieved using this method. Comonomers (e.g., acrylic acid) can be added after the nucleation of polystyrene is complete, thereby achieving surface functionalization with carboxylic acid groups.

[0140] Example 5 In a 250 mL two-neck round-bottom glass reactor equipped with a mechanical stirrer, SPS (476 mg), PVP (K60, 50 mg) and DI water (100 mL) were added. The side neck of the reactor was then sealed with a rubber septum and nitrogen was introduced through a needle to sweep the air from inside the reactor. The mixture was stirred for about 5 min to obtain a homogeneous solution at room temperature. It was then heated in an oil bath at 70 °C for about 3 min. The required amount of styrene (20 mL) was quickly injected into the reactor with a syringe. The styrene formed an oily layer on top of the aqueous solution. The resulting mixture slowly became cloudy and turned into a white suspension after 30 min. This indicated a slow polymerization rate and nucleation process. The polymerization mixture was stirred overnight at 70 °C for 20 h. The reaction was then diluted with DI water (50 mL). Subsequently, DVB (3.6 g) was added. The polymerization was continued for another 20 h at 70° C. A milky white colloidal solution was obtained. The as-synthesized colloidal solution was designated as “Sample 5”. The surface morphology of the sample was observed using a scanning electron microscope (JOEL JSM-6700).

[0141] The SEM image (Figure 7) shows that the diameter of the resulting polystyrene beads is 250 nm with a CV of 1%. No anomalous regions were observed in the polystyrene beads.

[0142] This experiment shows that using preformed macroradicals, a crosslinker (e.g., DVB) can be added after polystyrene nucleation is complete, producing monodisperse beads with enhanced solvent resistance.

[0143] (Example 6: Solvent resistance test) The as-synthesized latex solutions, Sample 1 and Sample 5, were subjected to solvent resistance test. Both samples were mixed with equal amount of THF and incubated for 1 h. After incubation, SEM images were taken of Sample 1 (Figure 8) and Sample 5 (Figure 9). Without the use of crosslinker, the beads were quickly destroyed by THF. However, with 20% DVB (w / w, DVB / styrene), the solvent resistance of polystyrene particles was improved.

[0144] Comparative Example 1 SPS (46 mg) and DI water (100 mL) were added to a 250 mL two-neck round-bottom glass reactor equipped with a mechanical stirrer. The side neck of the reactor was then sealed with a rubber septum and nitrogen was introduced through a needle to sweep the air from inside the reactor. The mixture was stirred for about 10 min to obtain a homogeneous solution at room temperature. The required amount of styrene (20 mL) was quickly injected into the reactor with a syringe. The resulting mixture was heated in an oil bath at 70 °C. The styrene formed an oily layer on top of the aqueous solution. The resulting mixture slowly became cloudy and turned into a white suspension after 10 min. This indicated a faster polymerization rate and nucleation process when compared to the experiments containing hydrophilic polymer stabilizers (e.g., PVP). The polymerization mixture was stirred overnight at 70 °C for 20 h. A milky colloidal solution was obtained. The as-synthesized colloidal solution was designated as "Sample 6." The surface morphology of the sample was observed using a scanning electron microscope (JOEL JSM-6700).

[0145] The SEM image (Figure 10) shows that the resulting polystyrene beads are polydisperse (or polydisperse).

[0146] This comparative example shows that without the use of preformed macroradicals, even a monomer-starved polymerization procedure was unable to produce monodisperse polystyrene beads.

[0147] Comparative Example 2 DI water (100 mL) was added to a 250 mL two-neck round-bottom glass reactor equipped with a mechanical stirrer. The side neck of the reactor was then sealed with a rubber septum and nitrogen was introduced through a needle to sweep the air in the reactor. The required amount of styrene (20 mL) was injected into the reactor with a syringe. This was followed by constant stirring for 10 min to form a saturated aqueous system of styrene. The system was heated in an oil bath at 70 °C for about 3 min. The polymerization was then initiated by injecting SPS (46 mg) dissolved in 10 mL of DI water into the system. The polymerization mixture was stirred overnight at 70 °C for 20 h. A milky white colloidal solution was formed. The as-synthesized colloidal solution was designated as “Sample 7”. The surface morphology of the sample was observed using a scanning electron microscope (JOEL JSM-6700).

[0148] The SEM image (FIG. 11A) shows that the resulting polystyrene beads were polydisperse (or polydisperse). The SEM image (FIG. 11B) shows that the polystyrene beads contained anomalous regions on their surface.

[0149] This comparative example shows that monodisperse polystyrene beads could not be produced without the use of preformed macroradicals. Since the polymerization was started in a saturated state of styrene, anomalous regions were observed in the beads (Figure 11B). This could be due to the non-uniform distribution of monomers within the polystyrene particles. The disclosure of this specification may include the following aspects. (Aspect 1) A polymer particle comprising a plurality of polymeric stabilizing components and a plurality of hydrophobic polymer chains; each of the plurality of polymeric stabilizing components comprises one or more hydrophilic polymer chains; each of said plurality of hydrophobic polymer chains is covalently bonded to one or more of said polymeric stabilizing moieties; The polymer particles are monodisperse, with a coefficient of variation based on the diameter of the polymer particles being less than 20%. (Aspect 2) 2. The polymer particles according to embodiment 1, wherein the coefficient of variation based on the diameter of the polymer particles is less than 15%, such as less than 10%, such as less than 5%. (Aspect 3) 3. The polymer particles of embodiment 2, wherein the coefficient of variation based on the diameter of the polymer particles is 2% or less. (Aspect 4) 4. The polymer particles of embodiment 3, wherein the coefficient of variation based on the diameter of the polymer particles is 1% or less. (Aspect 5) The polymer particles according to any one of aspects 1 to 4, wherein the average diameter of the polymer particles is from 50 to 1000 nm, for example, from 100 to 600 nm, for example, from 120 to 450 nm, for example, from 150 to 400 nm, for example, from 200 to 350 nm. (Aspect 6) 6. The polymer particle of any one of the preceding claims, wherein the hydrophilic polymer chains of the polymeric stabilizing component are selected from the group consisting of poly(vinylpyrrolidone), polyethyleneimine, polyacrylic acid, polyvinyl alcohol, water soluble polysaccharides (e.g., hydroxypropylmethylcellulose, chitosan, and blends thereof), copolymers thereof, and blends thereof. (Aspect 7) 7. The polymer particle according to embodiment 6, wherein the hydrophilic polymer chain of the polymeric stabilizing component is poly(vinylpyrrolidone). (Aspect 8) 8. The polymer particle according to any one of the preceding embodiments, wherein the hydrophobic polymer chains are formed from monomers selected from one or more of styrene and its derivatives, acrylates, and alkyl acrylates. (Aspect 9) 9. The polymer particle of embodiment 8, wherein the hydrophobic polymer chains are formed from monomers selected from one or more of styrene, butyl acrylate, 2,2,2-trifluoroethyl methacrylate, methyl methacrylate, 4-methylstyrene, 3-methylstyrene, and 4-tert-butylstyrene. (Aspect 10) 10. The polymer particle of embodiment 9, wherein the hydrophobic polymer chains are formed from styrene. (Aspect 11) 11. The polymer particle according to any one of the preceding aspects, wherein the weight:weight ratio of the plurality of polymer stabilizing components:the plurality of hydrophobic polymer chains is from 1:1000 to 1:1, such as from 1:500 to 1:2, such as from 1:300 to 1:3, for example from 1:150 to 1:5. (Aspect 12) 12. The polymer particle of any one of the preceding embodiments, wherein the hydrophobic polymer chains are formed as copolymers and / or the hydrophobic polymer chains are crosslinked. (Aspect 13) (a) When the hydrophobic polymer chain is a copolymer, the copolymer is formed from a first set of monomers and a second set of monomers: the first set of monomers are hydrophobic and selected from one or more of styrene and its derivatives, acrylates, and alkyl acrylates; the second set of monomers is selected from one or more of monomers having a carboxylic acid group, monomers having a hydroxyl group, monomers having an amino group, and monomers having an epoxy group; and / or (b) When the hydrophobic polymer chains are crosslinked, the crosslinked polymer chains are formed by a crosslinking agent that reacts with the first set of monomers and / or the second set of monomers (if present), and optionally the crosslinking agent is a monomer having two or more unsaturated groups. (Aspect 14) (ai) the first set of monomers are selected from one or more of styrene, butyl acrylate, 2,2,2-trifluoroethyl methacrylate, methyl methacrylate, 4-methylstyrene, 3-methylstyrene, and 4-tert-butylstyrene; and / or (bi) the second set of monomers are selected from one or more of acrylic acid, methacrylic acid, 2-carboxyethyl acrylate, acrylamide, methacrylamide, allylamine, (hydroxyethyl)methacrylate, hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, glycidyl methacrylate, allyl glycidyl ether, 1,2-epoxy-5-hexene, 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or (ci) The polymer particles of embodiment 13, wherein the crosslinker is one or more selected from divinylbenzene, ethylene glycol dimethylacrylate, bisphenol A dimethacrylate, butanediol dimethacrylate, tricyclodecane dimethanol diacrylate, pentaerythritol triacrylate, tripropylene glycol diacrylate, propoxylated neopentyl diacrylate, pentaerythritol triacrylate, ditrimethylolpropane tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol penta / hexaacrylate, tripropylene diacrylate, trimethylolpropane ethoxylate triacrylate, trimethylolpropane propoxylate triacrylate, di(trimethylolpropane)tetraacrylate, glycerol propoxylate triacrylate, pentaerythritol propoxylate triacrylate, poly(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, and tri(propylene glycol) diacrylate. (Aspect 15) (aii) the first set of monomers is styrene; and / or (bii) the second set of monomers are selected from one or more of N,N'-methylenebis(acrylamide), 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or (cii) the crosslinking agent is selected from one or more of divinylbenzene, ethylene glycol dimethyl acrylate, and bisphenol A dimethacrylate; 15. The polymer particle according to embodiment 14. (Aspect 16) (aiii) the weight:weight ratio of the first set of monomers to the second set of monomers, if present, is from 40:1 to 1:1, for example from 20:1 to 2:1; and / or (biii) the weight:weight ratio of the first set of monomers:crosslinker, if present, is from 40:1 to 1:1, for example from 20:1 to 2:1; 16. The polymer particle according to any one of embodiments 13 to 15. (Aspect 17) The polymer particles are represented by the formula: -SO 4 - M + wherein the dash (-) represents the point of attachment to the polymer particle, and M + is Na + 、K + or NH 4 + 17. The polymer particle of any one of the preceding embodiments, wherein the polymer particle is functionalized with a sulfate salt having a formula: (Aspect 18) A method for producing polymer particles, the method comprising the steps of: (A), (B) and (C) (A) reacting a water-soluble initiator compound with a hydrophilic polymeric stabilizer compound in water to form an aqueous macroinitiator complex; (B) adding one or more water-immiscible monomers to the aqueous solution of the macroinitiator complex to form a two-phase polymerization reaction mixture and reacting for a first period of time until particle nucleation occurs; and (C) continuing the reaction for a second period of time or quenching the reaction after the first period of time to obtain polymer particles. Including, The method wherein the polymer particles are monodisperse and the coefficient of variation based on the diameter of the polymer particles is less than 20%. (Aspect 19) 20. The method of embodiment 18, wherein the coefficient of variation based on diameter of the polymer particles is less than 15%, such as less than 10%, such as less than 5%. (Aspect 20) 20. The method of embodiment 19, wherein the coefficient of variation based on diameter of the polymer particles is 2% or less. (Aspect 21) 21. The method of embodiment 20, wherein the coefficient of variation based on diameter of the polymer particles is 1% or less. (Aspect 22) The method according to any one of aspects 18 to 21, wherein the polymer particles have an average diameter of 50 to 1000 nm, for example 100 to 600 nm, for example 120 to 450 nm, for example 150 to 400 nm, for example 200 to 350 nm. (Aspect 23) 23. The method of any one of embodiments 18-22, wherein the water soluble initiator comprises one or more of a peroxide initiator, a persulfate salt, and an azo initiator. (Aspect 24) 24. The method of claim 23, wherein the water soluble initiator is one or more selected from tert-amyl hydroperoxide, potassium persulfate, sodium persulfate, ammonium persulfate, 4,4'-azobis(4-cyanovaleric acid), 2,2'-azobis[2-methyl-N-(2-hydroxyethyl)propionamide, 2,2'-azobis[N-(2-carboxyethyl)-2-methylpropionamidine]hydrate, 2,2'-azobis(2-methylpropionamidine)dihydrochloride, 2,2''-azobis[2-(2-imidazolin-2-yl)propane], and 2,2'-azobis[2-(2-imidazolin-2-yl)propane]dihydrochloride. (Aspect 25) 25. The method of embodiment 24, wherein the water soluble initiator is selected from one or more of potassium persulfate, sodium persulfate, and ammonium persulfate. (Aspect 26) 26. The method of claim 25, wherein the water soluble initiator is sodium persulfate. (Aspect 27) 24. The method of claim 23, wherein the water soluble initiator is a redox pair, optionally wherein the redox pair is selected from ascorbic acid and hydrogen peroxide or ammonium persulfate and sodium bisulfite. (Aspect 28) 28. The method of any one of aspects 18 to 27, wherein the hydrophilic polymeric stabilizer compound is selected from the group consisting of poly(vinylpyrrolidone), polyethyleneimine, polyacrylic acid, polyvinyl alcohol, water soluble polysaccharides (e.g., hydroxypropylmethylcellulose, chitosan, and blends thereof), copolymers thereof, and blends thereof. (Aspect 29) 29. The method of embodiment 28, wherein the hydrophilic polymeric stabilizer compound is poly(vinylpyrrolidone). (Aspect 30) The method of embodiment 28, wherein the hydrophilic polymeric stabilizer compound is a water soluble polysaccharide (e.g., hydroxypropyl methylcellulose). (Aspect 31) The method of any one of aspects 18 to 30, wherein the one or more water-immiscible monomers are one or more selected from styrene and its derivatives, acrylates, and alkyl acrylates. (Aspect 32) 32. The method of embodiment 31, wherein the one or more water-immiscible monomers are selected from one or more of styrene, butyl acrylate, 2,2,2-trifluoroethyl methacrylate, methyl methacrylate, 4-methylstyrene, 3-methylstyrene, and 4-tert-butylstyrene. (Aspect 33) 33. The method of embodiment 32, wherein the one or more water immiscible monomers is styrene. (Aspect 34) 34. The method according to any one of aspects 18 to 33, wherein the weight:weight ratio of said hydrophilic polymeric stabiliser compound:said water immiscible monomer is from 1:1000 to 1:1, such as from 1:500 to 1:2, for example from 1:300 to 1:3, such as from 1:150 to 1:5. (Aspect 35) A method according to any one of aspects 18 to 34, wherein in step (c), the reaction is continued for a second period of time. (Aspect 36) When the reaction is continued for a second period of time, a second set of monomers and / or crosslinkers are added to the reaction mixture; the second set of monomers is selected from one or more of monomers having a carboxylic acid group, monomers having a hydroxyl group, monomers having an amino group, and monomers having an epoxy group; The crosslinker is a monomer having two or more unsaturated groups; The method according to embodiment 35. (Aspect 37) (ia) the second set of monomers are one or more selected from acrylic acid, methacrylic acid, 2-carboxyethyl acrylate, acrylamide, methacrylamide, allylamine, (hydroxyethyl)methacrylate, hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, glycidyl methacrylate, allyl glycidyl ether, 1,2-epoxy-5-hexene, 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or (ib) the crosslinker is selected from one or more of divinylbenzene, ethylene glycol dimethylacrylate, bisphenol A dimethacrylate, butanediol dimethacrylate, tricyclodecane dimethanol diacrylate, pentaerythritol triacrylate, tripropylene glycol diacrylate, propoxylated neopentyl diacrylate, pentaerythritol triacrylate, ditrimethylolpropane tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol penta / hexaacrylate, tripropylene diacrylate, trimethylolpropane ethoxylate triacrylate, trimethylolpropane propoxylate triacrylate, di(trimethylolpropane)tetraacrylate, glycerol propoxylate triacrylate, pentaerythritol propoxylate triacrylate, poly(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, and tri(propylene glycol) diacrylate; The method according to embodiment 36. (Aspect 38) (iia) the second set of monomers are selected from one or more of N,N'-methylenebis(acrylamide), 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or (iib) the crosslinking agent is selected from one or more of divinylbenzene, ethylene glycol dimethyl acrylate, and bisphenol A dimethacrylate; The method according to embodiment 37. (Aspect 39) (iiia) the weight:weight ratio of the first set of monomers to the second set of monomers, if present, is from 40:1 to 1:1, for example from 20:1 to 2:1; and / or (iiib) the weight:weight ratio of the first set of monomers:crosslinker, if present, is from 40:1 to 1:1, for example from 20:1 to 2:1; The method according to any one of embodiments 36 to 38. (Aspect 40) The method according to any one of aspects 18 to 39, wherein the molar ratio of the water-soluble initiator compound:the hydrophilic polymeric stabilizer compound is from 10:1 to 10000:1, such as from 20:1 to 5000:1, for example from 30:1 to 1000:1, for example from 50:1 to 500:1. (Aspect 41) The method according to any one of aspects 18 to 40, wherein the concentration of the hydrophilic polymeric stabilizer compound in the aqueous solution is from 0.01% to 20% by weight, such as from 0.05% to 10% by weight, for example from 0.1% to 5.0% by weight. (Aspect 42) Aspect 41. The method of any one of aspects 18 to 40, wherein the method is substantially free of surfactants and organic solvents.

Claims

1. A polymer particle comprising a plurality of polymeric stabilizing components and a plurality of hydrophobic polymer chains; each of the plurality of polymeric stabilizing components comprises one or more hydrophilic polymer chains; each of said plurality of hydrophobic polymer chains is covalently bonded to one or more of said polymeric stabilizing moieties; The polymer particles are monodisperse and have a coefficient of variation based on the diameter of the polymer particles of 1% or less.

2. 2. The polymer particles of claim 1, wherein the average diameter of the polymer particles is from 50 to 1000 nm.

3. 3. The polymer particle according to claim 1 or 2, wherein the hydrophilic polymer chains of the polymer stabilizing component are selected from the group consisting of poly(vinylpyrrolidone), polyethyleneimine, polyacrylic acid, polyvinyl alcohol, water-soluble polysaccharides selected from hydroxypropylmethylcellulose, chitosan and blends thereof, copolymers thereof and blends thereof.

4. 4. The polymer particle of claim 3, wherein the hydrophilic polymer chain of the polymeric stabilizing component is poly(vinylpyrrolidone).

5. 5. The polymer particle according to claim 1, wherein the hydrophobic polymer chains are formed from monomers selected from one or more of styrene and its derivatives, acrylates and alkyl acrylates.

6. 6. The polymer particle of claim 5, wherein the hydrophobic polymer chains are formed from monomers selected from one or more of styrene, butyl acrylate, 2,2,2-trifluoroethyl methacrylate, methyl methacrylate, 4-methylstyrene, 3-methylstyrene, and 4-tert-butylstyrene.

7. The polymer particle of claim 6 , wherein the hydrophobic polymer chains are formed from styrene.

8. 8. The polymer particle of claim 1, wherein the weight:weight ratio of said plurality of polymeric stabilizing components to said plurality of hydrophobic polymer chains is from 1:1000 to 1:

1.

9. The polymer particle according to any one of claims 1 to 8, wherein the hydrophobic polymer chains are formed as copolymers and / or the hydrophobic polymer chains are crosslinked.

10. (a) When the hydrophobic polymer chain is a copolymer, the copolymer is formed from a first set of monomers and a second set of monomers: the first set of monomers are hydrophobic and selected from one or more of styrene and its derivatives, acrylates, and alkyl acrylates; the second set of monomers are selected from one or more of monomers having a carboxylic acid group, monomers having a hydroxyl group, monomers having an amino group, and monomers having an epoxy group; and / or (b) when the hydrophobic polymer chains are crosslinked, the crosslinked polymer chains are formed by a crosslinking agent, which reacts with the first set of monomers and / or the second set of monomers, if present.

11. (ai) the first set of monomers are selected from one or more of styrene, butyl acrylate, 2,2,2-trifluoroethyl methacrylate, methyl methacrylate, 4-methylstyrene, 3-methylstyrene, and 4-tert-butylstyrene; and / or (bi) the second set of monomers are selected from one or more of acrylic acid, methacrylic acid, 2-carboxyethyl acrylate, acrylamide, methacrylamide, allylamine, (hydroxyethyl)methacrylate, hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, glycidyl methacrylate, allyl glycidyl ether, 1,2-epoxy-5-hexene, 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or 11. The polymer particle of claim 10, wherein the crosslinking agent is one or more selected from divinylbenzene, ethylene glycol dimethylacrylate, bisphenol A dimethacrylate, butanediol dimethacrylate, tricyclodecane dimethanol diacrylate, pentaerythritol triacrylate, tripropylene glycol diacrylate, propoxylated neopentyl diacrylate, pentaerythritol triacrylate, ditrimethylolpropane tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol penta / hexaacrylate, tripropylene diacrylate, trimethylolpropane ethoxylate triacrylate, trimethylolpropane propoxylate triacrylate, di(trimethylolpropane)tetraacrylate, glycerol propoxylate triacrylate, pentaerythritol propoxylate triacrylate, poly(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, and tri(propylene glycol) diacrylate.

12. (aii) the first set of monomers is styrene; and / or (bii) the second set of monomers are selected from one or more of N,N'-methylenebis(acrylamide), 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or (cii) the crosslinking agent is selected from one or more of divinylbenzene, ethylene glycol dimethyl acrylate, and bisphenol A dimethacrylate; 12. The polymer particle of claim 11.

13. (aiii) the weight:weight ratio of the first set of monomers to the second set of monomers, if present, is from 40:1 to 1:1; and / or (biii) the weight:weight ratio of the first set of monomers:crosslinker, if present, is from 40:1 to 1:1; The polymer particles according to any one of claims 10 to 12.

14. The polymer particles are represented by the formula: ４ － M ＋ [wherein the dash (-) represents the point of attachment to the polymer particle, M ＋ is Na ＋ , K ＋ or NH ４ ＋ The polymer particles according to any one of claims 1 to 13, which are functionalized with a sulfate having the formula:

15. A method for producing polymer particles, the method comprising the steps of: (A), (B) and (C) (A) reacting a water-soluble initiator compound with a hydrophilic polymeric stabilizer compound in water to form an aqueous macroinitiator complex; (B) adding one or more water-immiscible monomers to the aqueous solution of the macroinitiator complex to form a two-phase polymerization reaction mixture and reacting for a first period of time until particle nucleation occurs; and (C) continuing the reaction for a second period of time or quenching the reaction after the first period of time to obtain polymer particles. Including, The process wherein the polymer particles are monodisperse and the coefficient of variation based on the diameter of the polymer particles is less than 20%.

16. 16. The method of claim 15, wherein the coefficient of variation based on the diameter of the polymer particles is less than 15%.

17. 17. The method of claim 16, wherein the coefficient of variation based on the diameter of the polymer particles is 2% or less.

18. 18. The method of claim 17, wherein the coefficient of variation based on the diameter of the polymer particles is 1% or less.

19. The method according to any one of claims 15 to 18, wherein the average diameter of the polymer particles is from 50 to 1000 nm.

20. The method of any one of claims 15 to 19, wherein the water-soluble initiator comprises one or more of a peroxide initiator, a persulfate salt, and an azo initiator.

21. 21. The method of claim 20, wherein the water soluble initiator is selected from one or more of tert-amyl hydroperoxide, potassium persulfate, sodium persulfate, ammonium persulfate, 4,4'-azobis(4-cyanovaleric acid), 2,2'-azobis[2-methyl-N-(2-hydroxyethyl)propionamide, 2,2'-azobis[N-(2-carboxyethyl)-2-methylpropionamidine]hydrate, 2,2'-azobis(2-methylpropionamidine)dihydrochloride, 2,2''-azobis[2-(2-imidazolin-2-yl)propane] and 2,2'-azobis[2-(2-imidazolin-2-yl)propane]dihydrochloride.

22. 22. The method of claim 21, wherein the water soluble initiator is selected from one or more of potassium persulfate, sodium persulfate, and ammonium persulfate.

23. 23. The method of claim 22, wherein the water soluble initiator is sodium persulfate.

24. The method according to any one of claims 15 to 19, wherein the water-soluble initiator is a redox pair.

25. 25. The method of any one of claims 15 to 24, wherein the hydrophilic polymeric stabiliser compound is selected from the group consisting of poly(vinylpyrrolidone), polyethyleneimine, polyacrylic acid, polyvinyl alcohol, water soluble polysaccharides selected from hydroxypropylmethylcellulose, chitosan and blends thereof, copolymers thereof and blends thereof.

26. 26. The method of claim 25, wherein the hydrophilic polymeric stabilizer compound is poly(vinylpyrrolidone).

27. 26. The method of claim 25, wherein the hydrophilic polymeric stabilizer compound is a water soluble polysaccharide.

28. The method of any one of claims 15 to 27, wherein the one or more water-immiscible monomers are one or more selected from styrene and its derivatives, acrylates, and alkyl acrylates.

29. 29. The method of claim 28, wherein the one or more water immiscible monomers are selected from one or more of styrene, butyl acrylate, 2,2,2-trifluoroethyl methacrylate, methyl methacrylate, 4-methylstyrene, 3-methylstyrene, and 4-tert-butylstyrene.

30. 30. The method of claim 29, wherein the one or more water immiscible monomers is styrene.

31. The method of any one of claims 15 to 30, wherein the weight:weight ratio of said hydrophilic polymeric stabiliser compound to said water immiscible monomer is from 1:1000 to 1:

1.

32. 32. The method of any one of claims 15 to 31, wherein in step (c), the reaction is allowed to continue for a second period of time.

33. When the reaction is continued for a second period of time, a second set of monomers and / or crosslinkers are added to the reaction mixture; the second set of monomers is selected from one or more of monomers having a carboxylic acid group, monomers having a hydroxyl group, monomers having an amino group, and monomers having an epoxy group; The crosslinker is a monomer having two or more unsaturated groups; 33. The method of claim 32.

34. (ia) the second set of monomers are one or more selected from acrylic acid, methacrylic acid, 2-carboxyethyl acrylate, acrylamide, methacrylamide, allylamine, (hydroxyethyl)methacrylate, hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, glycidyl methacrylate, allyl glycidyl ether, 1,2-epoxy-5-hexene, 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or (ib) the crosslinker is one or more selected from divinylbenzene, ethylene glycol dimethylacrylate, bisphenol A dimethacrylate, butanediol dimethacrylate, tricyclodecane dimethanol diacrylate, pentaerythritol triacrylate, tripropylene glycol diacrylate, propoxylated neopentyl diacrylate, pentaerythritol triacrylate, ditrimethylolpropane tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol penta / hexaacrylate, tripropylene diacrylate, trimethylolpropane ethoxylate triacrylate, trimethylolpropane propoxylate triacrylate, di(trimethylolpropane)tetraacrylate, glycerol propoxylate triacrylate, pentaerythritol propoxylate triacrylate, poly(ethylene glycol) diacrylate, poly(propylene glycol) diacrylate, and tri(propylene glycol) diacrylate; 34. The method of claim 33.

35. (iia) the second set of monomers are selected from one or more of N,N'-methylenebis(acrylamide), 1,4-diamino-6-diallylamino-1,3,5-triazine, diallylamine, and triallylamine; and / or (iib) the crosslinking agent is one or more selected from divinylbenzene, ethylene glycol dimethyl acrylate, and bisphenol A dimethacrylate; 35. The method of claim 34.

36. (iiia) the weight:weight ratio of the first set of monomers to the second set of monomers, if present, is from 40:1 to 1:1; and / or (iiib) the weight:weight ratio of the first set of monomers to crosslinker, if present, is from 40:1 to 1:1; 36. The method according to any one of claims 33 to 35.

37. The method of any one of claims 15 to 36, wherein the molar ratio of said water-soluble initiator compound to said hydrophilic polymeric stabilizer compound is from 10:1 to 10000:

1.

38. The method of any one of claims 15 to 37, wherein the concentration of the hydrophilic polymeric stabiliser compound in the aqueous solution is from 0.01% to 20% by weight.

39. The method of any one of claims 15 to 37, wherein the method is substantially free of surfactants and organic solvents.