METHOD FOR MANUFACTURING A HEAT-TREATED STEEL SHEET

Description

[0001] The present invention relates to a method for manufacturing a thermally treated steel sheet having a chemical steel composition and a microstructure m target comprising from 0 to 100% of at least one phase chosen among: ferrite, martensite, bainite, pearlite, cementite and austenite, in a heat treatment line. The invention is particularly well suited for the manufacture of automotive vehicles.

[0002] It is known to use coated or bare steel sheets for the manufacture of automotive vehicles. A multitude of steel grades are used to manufacture a vehicle. The choice of steel grade depends on the final application of the steel part. For example, IF (Interstitial-Free) steels can be produced for an exposed part, TRIP (Transformation-Induced Plasticity) steels can be produced for seat and floor cross members or A-pillars and DP (Dual Phase) steels can be produced for rear rails or roof cross member.

[0003] During the production of theses steels, crucial treatments are performed on the steel in order to obtain the desired part having excepted mechanical properties for one specific application. Such treatments can be, for example, a continuous annealing before deposition of a metallic coating or a quenching and partitioning treatment. Usually, the treatment to perform is selected in a list of known treatments, this treatment being chosen depending on the steel grade.

[0004] The patent application WO2010 / 049600 relates to a method of using an installation for heat treating a continuously moving steel strip, comprising the steps of: selecting a cooling rate of the steel strip depending on, among others metallurgical characteristics at the entry and metallurgical characteristics required at the exit of the installation; enter the geometric characteristics of the band; calculate power transfer profile along the steel route in the light with the line speed; determine desired values for the adjustment parameters of the cooling section and adjust the power transfer of the cooling devices of the cooling section according to said monitoring values.

[0005] However, this method is only based on the selection and the application of well-known cooling cycles. It means that for one steel grade, for example TRIP steels, there is a huge risk that the same cooling cycle is applied even if each TRIP steel has its own characteristics comprising chemical composition, microstructure, properties, surface texture, etc. Thus, the method does not take into account the real characteristics of the steel. It allows for the non-personalized heat treatment of a multitude of steel grades.

[0006] Consequently, the heat treatment is not adapted to one specific steel and therefore at the end of the treatment, the desired properties are not obtained. Moreover, after the treatment, the steel can have a big dispersion of the mechanical properties. Finally, even if a wide range of steel grades can be manufactured, the quality of the treated steel is poor.

[0007] The patent application JPH1036923 describes a method of annealing in a furnace wherein, when processing is performed under special conditions different from preset predetermined manufacturing conditions, the manufacturing conditions are updated and transmitted. The update information and the identification information corresponding to the update information are set in advance.

[0008] The patent application WO 2010 / 049600 describes a furnace for the thermal processing of a continuously-running rolled steel strip, said furnace comprising a preheating section, a temperature-maintaining section and a cooling section comprising, a first quenching device that does not oxidise the strip and has an adjustable transfer power and a second quenching device that oxidises the strip and has an adjustable transfer power. The furnace comprises a control and actuation means for adjusting the transfer power of each of the first and second quenching devices based on a desired cooling rate and on the size characteristics of the strip.

[0009] Thus, the object of the invention is to solve the above drawbacks by providing a method for manufacturing a thermally treated steel sheet having a specific chemical steel composition and a specific microstructure m target to reach in a heat treatment line. In particular, the object is to perform a treatment adapted to each steel sheet, such treatment being calculated very precisely in the lowest calculation time possible in order to provide a steel sheet having the excepted properties, such properties having the minimum of properties dispersion possible.

[0010] This object is achieved by providing a method according to claim 1. The method can also comprise any characteristics of claims 2 to 16.

[0011] Other characteristics and advantages of the invention will become apparent from the following detailed description of the invention.

[0012] To illustrate the invention, various embodiments and trials of non-limiting examples will be described, particularly with reference to the following Figures: Figure 1 illustrates an example of the method according to the present invention. Figure 2 illustrates an example wherein a continuous annealing of a steel sheet comprising a heating step, a soaking step, a cooling step and an overaging step is performed. Figure 3 illustrates a preferred embodiment according to the invention. Figure 4 illustrates an example according to the invention wherein a continuous annealing is performed on a steel sheet before the deposition of a coating by hot-dip. Figure 5 illustrates an example wherein a quenching & partitioning treatment is performed on a steel sheet.

[0013] The following terms will be defined: CC: chemical composition in weight percent, m target : targeted value of the microstructure, m standard : the microstructure of the selected product, P target : targeted value of a mechanical property, m i : initial microstructure of the steel sheet, X: phase fraction in weight percent, T: temperature in degree Celsius (°C), t: time (s), s: seconds, UTS: ultimate tensile strength (MPa), YS: yield stress (MPa), metallic coating based on zinc means a metallic coating comprising above 50% of zinc, metallic coating based on aluminum means a metallic coating comprising above 50% of aluminum and thermal path, TP standard , TP target , TP x and TP xint comprise a time, a temperature of the thermal treatment and at least one rate chosen from: a cooling, an isotherm or a heating rate. The isotherm rate has a constant temperature.

[0014] The designation "steel" or "steel sheet" means a steel sheet, a coil, a plate having a composition allowing the part to achieve a tensile strength up to 2500 MPa and more preferably up to 2000MPa. For example, the tensile strength is above or equal to 500 MPa, preferably above or equal to 1000 MPa, advantageously above or equal to 1500 MPa. A wide range of chemical composition is included since the method according to the invention can be applied to any kind of steel.

[0015] The invention relates to a method for manufacturing a thermally treated steel sheet having a chemical steel composition and a microstructure m target comprising from 0 to 100% of at least one phase chosen among: ferrite, martensite, bainite, pearlite, cementite and austenite, in a heat treatment line comprising: A. a preparation step comprising: 1) a selection sub step wherein the chemical composition and m target are compared to a list of predefined products, which microstructure includes predefined phases and predefined proportion of phases, in order to select a product having a microstructure m standard closest to m target and a predefined thermal path TP standard to obtain m standard , 2) a calculation sub step wherein at least two thermal path TP x , each TP x corresponding to a microstructure m x obtained at the end of TP x , are calculated based on the selected product of step A.1) and TP standard and m i to reach m target , the thermal enthalpy H released or consumed between m i and m target being calculated such that: H x = X ferrite * H ferrite + X martensite * H martensite + X bainite * H bainite + _ X pearlite * H pearlite + H cementite * X cementite + H austenite ∗ X austenite _ X being a phase fraction, all thermal cycle TP x being calculated such that: T t + Δt = T t + φ Convection + φ radiance ρ ⋅ Ep ⋅ C pe Δt ± H x C pe with Cpe: the specific heat of the phase (J·kg -1< ·K -1< ), ρ: the density of the steel (g.m -3< ), Ep: thickness of the steel (m), ϕ: the heat flux (convective + radiative in W), H x (J.Kg -1< ), T: temperature (°C) and t: time (s), 3) a selection sub step wherein one thermal path TP target to reach m target is selected, TP target being chosen from TP x and being selected such that m x is the closest to m target , B. a thermal treatment step wherein TP target is performed on the steel sheet.

[0016] Without willing to be bound by any theory, it seems that when the method according to the present invention is applied, it is possible to obtain a personalized heat treatment for each steel sheet to treat in a short calculation time. Indeed, the method according to the present invention allows for a precise and specific heat treatment which takes into account m target , more precisely the proportion of all the phases along the treatment and m i (including the microstructure dispersion along the steel sheet). Indeed, the method according to the present invention takes into account for the calculation the thermodynamically stable phases, i.e. ferrite, austenite, cementite and pearlite, and the thermodynamic metastable phases, i.e. bainite and martensite. Thus, a steel sheet having the expected properties with the minimum of properties dispersion possible is obtained.

[0017] Preferably, the microstructure m target to reach comprises: 100% of austenite, from 5 to 95% of martensite, from 4 to 65% of bainite, the balance being ferrite, from 8 to 30% of residual austenite, from 0.6 to 1.5% of carbon in solid solution, the balance being ferrite, martensite, bainite, pearlite and / or cementite, from 1% to 30% of ferrite and from 1% to 30% of bainite, from 5 and 25% of austenite, the balance being martensite , from 5 to 20% of residual austenite, the balance being martensite, ferrite and residual austenite, residual austenite and intermetallic phases, from 80 to 100% of martensite and from 0 to 20% of residual austenite 100% martensite, from 5 to 100% of pearlite and from 0 to 95% of ferrite and at least 75% of equiaxed ferrite, from 5 to 20% of martensite and bainite in amount less than or equal to 10%.

[0018] Advantageously, during the selection sub step A.1), the chemical composition and m target are compared to a list of predefined products. The predefined products can be any kind of steel grade. For example, they include Dual Phase DP, Transformation Induced Plasticity (TRIP), Quenched & Partitioned steel (Q&P), Twins Induced Plasticity (TWIP), Carbide Free Bainite (CFB), Press Hardening Steel (PHS), TRIPLEX, DUPLEX and Dual Phase High Ductility (DP HD).

[0019] The chemical composition depends on each steel sheet. For example, the chemical composition of a DP steel can comprise: 0.05 < C < 0.3%, 0.5 ≤ Mn < 3.0%, S ≤ 0.008%, P ≤ 0.080%, N ≤ 0.1%, Si ≤ 1.0%, the remainder of the composition making up of iron and inevitable impurities resulting from the development.

[0020] Each predefined product comprises a microstructure including predefined phases and predefined proportion of phases. Preferably, the predefined phases in step A.1) are defined by at least one element chosen from: the size, the shape and the chemical composition. Thus, m standard includes a predefined phase in addition to predefined proportions of phase. Advantageously, mi, m x , m target include phases defined by at least one element chosen from: the size, the shape and the chemical composition. According to the invention, the predefined product having a microstructure m standard closest to m target is selected as well as thermal path TP standard to reach m standard . m standard comprises the same phases as m target . Preferably, m standard also comprises the same phases proportions as m target .

[0021] Figure 1 illustrates an example according to the invention wherein the steel sheet to treat has the following CC in weight: 0.2% of C, 1.7% of Mn, 1.2% of Si and of 0.04% Al. m target comprises 15% of residual austenite, 40% of bainite and 45% of ferrite, from 1.2% of carbon in solid solution in the austenite phase. According to the invention, CC and m target are selected and compared to a list of predefined products chosen from among products 1 to 4. CC and m target correspond to product 3 or 4, such product being a TRIP steel.

[0022] Product 3 has the following CC 3 in weight: 0.25% of C, 2.2% of Mn, 1.5% of Si and 0.04% of Al. m 3 comprises 12% of residual austenite, 68% of ferrite and 20% of bainite, from 1.3% of carbon in solid solution in the austenite phase.

[0023] Product 4 has the following CC 4 in weight: 0.19% of C, 1.8% of Mn, 1.2% of Si and 0.04% of Al. m 4 comprises 12% of residual austenite, 45% of bainite and 43 % of ferrite, from 1.1% of carbon in solid solution in the austenite phase.

[0024] Product 4 has a microstructure closest to m target since it has the same phases as m target in the same proportions.

[0025] As shown in Figure 1, two predefined products can have the same chemical composition CC and different microstructures. Indeed, Product 1 and Product 1' are both DP600 steels (Dual Phase having an UTS of 600MPa). One difference is that Product 1 has a microstructure m i and Product 1' has a different microstructure m 1' . The other difference is that Product 1 has a YS of 360MPa and Product 1' has a YS of 420MPa. Thus, it is possible to obtain steel sheets having different compromise UTS / YS for one steel grade.

[0026] During the calculation sub step A.2), at least two thermal paths TP x are calculated based on the selected product of step A.1) and m i to reach m target . The calculation of TP x takes into account the thermal behavior and metallurgical behavior of the steel sheet when compared to the conventional methods wherein only the thermal behavior is considered. In the example of Figure 1, product 4 is selected because m 4 is the closest to m target and TP 4 is selected, m 4 and TP 4 corresponding respectively to m standard and TP standard .

[0027] Figure 2 illustrates a continuous annealing of a steel sheet comprising a heating step, a soaking step, a cooling step and an overaging step. A multitude of TP x is calculated to reach m target as shown only for the heating step in Figure 2. In this example, TP x are calculated along the all continuous annealing (not shown).

[0028] Preferably, at least 10 TP x are calculated, more preferably at least 50, advantageously at least 100 and more preferably at least 1000. For example, the number of calculated TP x is between 2 and 10000, preferably between 100 and 10000, more preferably between 1000 and 10000.

[0029] In step A.3), one thermal path TP target to reach m target is selected. TP target is chosen from TP x such that m x is the closest to m target . Thus, in Figure 1, TP target is chosen from a multitude of TP x . Preferably, the differences between proportions of phase present in m target and m x is ±3 %.

[0030] In step A.2), the thermal enthalpy H released or consumed between m i and m target is calculated such that: H x = X ferrite * H ferrite + X martensite * H martensite + X bainite * H bainite + X pearlite * H pearlite + H cementite + _ ∗ X cementite + H austenite + _ ∗ X austenite X being a phase fraction.

[0031] Without willing to be bound by any theory, H represents the energy released or consumed along the all thermal path when a phase transformation is performed. It is believed that some phase transformations are exothermic and some of them are endothermic. For example, the transformation of ferrite into austenite during a heating path is endothermic whereas the transformation of austenite into pearlite during a cooling path is exothermic.

[0032] In step A.2), the all thermal cycle TP x is calculated such that: T t + Δt = T t + φ Convection + φ radiance ρ ⋅ Ep ⋅ C pe Δt ± H x C pe with C pe : the specific heat of the phase (J·kg -1< ·K -1< ), ρ: the density of the steel (g.m -3< ), Ep: the thickness of the steel (m), ϕ: the heat flux (convective and radiative in W), H∗ (J.kg -1< ), T: temperature (°C) and t: time (s).

[0033] Preferably, in step A.2), at least one intermediate steel microstructure m xint corresponding to an intermediate thermal path TP xint and the thermal enthalpy H xint are calculated. In this case, the calculation of TP x is obtained by the calculation of a multitude of TP xint . Thus, preferably, TP x is the sum of all TP xint and H x is the sum of all H xint . In this preferred embodiment, TP xint is calculated periodically. For example, it is calculated every 0.5 seconds, preferably 0.1 seconds or less.

[0034] Figure 3 illustrates a preferred embodiment wherein in step A.2), m int1 and m int2 corresponding respectively to TP xint1 and TP xint2 as well as H xint1 and H xint2 are calculated. H x during the all thermal path is determined to calculate TP x .

[0035] In a preferred embodiment, before step A.1), at least one targeted mechanical property P target chosen among yield strength YS, Ultimate Tensile Strength UTS, elongation, hole expansion, formability is selected. In this embodiment, preferably, m target is calculated based on P target .

[0036] Without willing to be bound by any theory, it is believed that the characteristics of the steel sheet are defined by the process parameters applied during the steel production. Thus, advantageously, in step A.2), the process parameters undergone by the steel sheet before entering the heat treatment line are taken into account to calculate TP x . For example, the process parameters comprise at least one element chosen from among: a final rolling temperature, a run out table cooling path, a coiling temperature, a coil cooling rate and cold rolling reduction rate.

[0037] In another embodiment, the process parameters of the treatment line that the steel sheet will undergo in the heat treatment line are taken into account to calculate TP x . For example, the process parameters comprise at least one element chosen from among: the line speed, a specific thermal steel sheet temperature to reach, heating power of the heating sections, a heating temperature and a soaking temperature, cooling power of the cooling sections, a cooling temperature, an overaging temperature.

[0038] Preferably, the thermal path, TP x , TP xint , TP standard or TP target comprise at least one treatment chosen from: a heating, an isotherm or a cooling treatment. For example, the thermal path can be a recrystallization annealing, a press hardening path, a recovery path, an intercritical or full austenitic annealing, a tempering or partitioning path, an isothermal path or a quenching path.

[0039] Preferably, a recrystallization annealing is performed. The recrystallization annealing comprises optionally a pre-heating step, a heating step, a soaking step, a cooling step and optionally an equalizing step. In this case, it is performed in a continuous annealing furnace comprising optionally a pre-heating section, a heating section, a soaking section, a cooling section and optionally an equalizing section. Without willing to be bound by any theory, it is believed that the recrystallization annealing is the thermal path the more difficult to handle since it comprises many steps to take into account comprising cooling and heating steps.

[0040] Preferably, every time a new steel sheet enters into the heat treatment line, a new calculation step A.2) is automatically performed based on the selection step A.1) performed beforehand. Indeed, the method according to the present invention adapts the thermal path TP target to each steel sheet even if the same steel grade enters in the heat treatment line since the real characteristics of each steel often differs. The new steel sheet can be detected and the new characteristics of the steel sheet are measured and are pre-selected beforehand. For example, a detector detects the welding between two coils.

[0041] In this preferred embodiment, an adaptation of the thermal path is performed as the steel sheet entries into the heat treatment line on the first meters of the sheet in order to avoid strong process variation.

[0042] Figure 4 illustrates an example according to the invention wherein a continuous annealing is performed on a steel sheet before the deposition of a coating by hot-dip. With the method according to the present invention, after a selection of a predefined product having a microstructure close to m target (not shown), a TP x is calculated based on m i , the selected product and m target . In this example, intermediate thermal paths from TP xint1 to TP xint6 , corresponding respectively to m xint1 to m xint6 , and H xint1 to H xint6 are calculated. H x is determined in order to obtain TP x . In this Figure, TP target has been selected from a multitude of TP x .

[0043] According to the present invention, m target can be the excepted microstructure at any time of a thermal treatment. In other words, m target can be the expected microstructure at the end of a thermal treatment as shown in Figure 4 or at a precise moment of a thermal treatment as shown in Figure 5. Indeed, for example, for the Q&P steel sheet, an important point of a quenching & partitioning treatment is the T q , corresponding to T' 4 in Figure 5, which is the temperature of quenching. Thus, the microstructure to consider can be m' target . In this case, after the application of TP' target on the steel sheet, it is possible to apply a predefined treatment.

[0044] With the method according to the present invention, it is possible to obtain a coil made of a steel sheet including said predefined product types include DP, TRIP, Q&P, TWIP, CFB, PHS, TRIPLEX, DUPLEX, DP HD is obtained, such coil having a standard variation of mechanical properties below or equal to 25MPa, preferably below or equal to 15MPa, more preferably below or equal to 9 MPa, between any two points along the coil. Indeed, without willing to be bound by any theory, it is believed that the method including the calculation step B.1) takes into account the microstructure dispersion of the steel sheet along the coil. Thus, TP target applied on the steel sheet in step B) allows for a homogenization of the microstructure and also of the mechanical properties.

[0045] Preferably, the mechanical properties are chosen from YS, UTS and elongation. The low value of standard variation is due to the precision of TP target .

[0046] Preferably, the coil is covered by a metallic coating based on zinc or based on aluminum.

[0047] Preferably, in an industrial production, the standard variation of mechanical properties between 2 coils made of a steel sheet including said predefined product types include DP, TRIP, Q&P, TWIP, CFB, PHS, TRIPLEX, DUPLEX, DP HD measured successively produced on the same line is below or equal to 25MPa, preferably below or equal to 15MPa, more preferably below or equal to 9 MPa.

[0048] A thermally treatment line for the implementation of a method according to the present invention is used to perform TP target . For example, the thermally treatment line is a continuous annealing furnace, a press hardening furnace, a batch annealing or a quenching line.

[0049] Finally, the present invention can be implemented using a computer program product comprising at least a metallurgical module, an optimization module and a thermal module that cooperate together to determine TP target , such modules comprising software instructions that when implemented by a computer implement the method according to the present invention.

[0050] The metallurgical module predicts the microstructure (m x , m target including metastable phases: bainite and martensite and stables phases: ferrite, austenite, cementite and pearlite) and more precisely the proportion of phases all along the treatment and predicts the kinetic of phases transformation.

[0051] The thermal module predicts the steel sheet temperature depending on the installation used for the thermal treatment, the installation being for example a continuous annealing furnace, the geometric characteristics of the band, the process parameters including the power of cooling, heating or isotherm power, the thermal enthalpy H released or consumed along the all thermal path when a phase transformation is performed.

[0052] The optimization module determines the best thermal path to reach m target , i.e. TP target following the method according to the present invention using the metallurgical and thermal modules.

[0053] The invention will now be explained in trials carried out for information only. They are not limiting.Examples

[0054] In this example, DP780GI having the following chemical composition was chosen: C (%)Mn (%)Si (%)Cr (%)Mo (%)P (%)Cu (%)Ti (%)N (%)0.1451.80.20.20.00250.0150.020.0250.06

[0055] The cold-rolling had a reduction rate of 50% to obtain a thickness of 1mm. m target to reach comprised 13% of martensite, 45% of ferrite and 42% of bainite, corresponding to the following P target : YS of 500MPa and a UTS of 780MPa. A cooling temperature T cooling of 460°C had also to be reached in order to perform a hot-dip coating with a zinc bath. This temperature must be reached with an accuracy of + / - 2°C to guarantee good coatability in the Zn bath.

[0056] Firstly, the steel sheet was compared to a list of predefined products in order to obtain a selected product having a microstructure m standard closest to m target . The selected product was a DP780GI having the following chemical composition: C (%)Mn (%)Si (%)0.1501.9000.2

[0057] The microstructure of DP780GI, i.e. m standard , comprises 10% martensite, 50% ferrite and 40% bainite. The corresponding thermal path TP standard comprises: - a pre-heating step wherein the steel sheet is heated from ambient temperature to 680°C during 35 seconds, - a heating step wherein the steel sheet is heated from 680°C to 780°C during 38 seconds, - soaking step wherein the steel sheet is heated at a soaking temperature T soaking of 780°C during 22 seconds, - a cooling step wherein the steel sheet is cooled with 11 jets cooling spraying HN x as follows: JetsJet 1Jet 2Jet 3Jet 4Jet 5Jet 6Jet 7Jet 8Jet 9Jet 10Jet 11Cooling rate (°C / s)131012710144126251618Time (s)1.761.761.761.761.571.681.681.521.521.521.52T(°C)748730709697681658590550513489462Cooling power(%)00000058100100100100 - a hot-dip coating in a zinc bath à 460°C, - the cooling of the steel sheet until the top roll during 24.6s at 300°C and - the cooling of the steel sheet at ambient temperature.

[0058] Then, a multitude of thermal paths TP x were calculated based on the selected product DP780 and TP standard and m i of DP780 to reach m target .

[0059] After the calculation of TP x , one thermal path TP target to reach m target was selected, TP target being chosen from TP x and being selected such that m x is the closest to m target . TP target comprises: - a pre-heating step wherein the steel sheet is heated from ambient temperature to 680°C during 35 seconds, - a heating step wherein the steel sheet is heated from 680°C to 780°C during 38s, - soaking step wherein the steel sheet is heated at a soaking temperature T soaking of 780°C during 22 seconds, - a cooling step wherein the steel sheet is cooled with 11 jets cooling spraying HN x as follows: JetsJet 1Jet 2Jet 3Jet 4Jet 5Jet 6Jet 7Jet 8Jet 9Jet 10Jet 11Cooling rate (°C / s)181112738274819376Time (s)1.761.761.761.761.571.681.681.521.521.521.52T(°C)748729709697637592511483479468458Cooling power(%)00004020100100202020 - a hot-dip coating in a zinc bath à 460°C, - the cooling of the steel sheet until the top roll during 24.6s at 300°C and - the cooling of the steel sheet until ambient temperature. Table 1 shows the properties obtained with TP standard and TP target on the steel sheet: TP standard TP target Expected propertiesT cooling obtained462°C458.09°C460°CMicrostructure obtained at the end of the thermal pathX martensite : 12.83%X martensite : 12.86%X martensite : 13%X ferrite : 53.85%X ferrite : 47.33%X ferrite : 45%X bainite : 33.31%X bainite : 39.82%X bainite : 42%Microstructure deviation with respect to m target X martensite : 0.17%X martensite : 0.14%-X ferrite : 8.85%X ferrite : 2.33%X bainite : 8.69%X bainite : 2.18%YS (MPa)434494500YS deviation with respect to P target (MPa)666-UTS (MPa)786792780UTS deviation with respect to P target (MPa)148-

[0060] Table 1 shows that with the method according to the present invention, it is possible to obtain a steel sheet having the desired expected properties since the thermal path TP target is adapted to each steel sheet. On the contrary, by applying a conventional thermal path, TP standard , the expected properties are not obtained.

Claims

1. A method for manufacturing a thermally treated steel sheet having a chemical steel composition and a microstructure mtarget comprising from 0 to 100% of at least one phase chosen among: ferrite, martensite, bainite, pearlite, cementite and austenite, in a heat treatment line comprising: A. a preparation step comprising: 1) a selection sub step wherein the chemical composition and mtarget are compared to a list of predefined products, which microstructure includes predefined phases and predefined proportion of phases, in order to select a product having a microstructure mstandard closest to mtarget and a predefined thermal path TPstandard to obtain mstandard, 2) a calculation sub step wherein at least two thermal path TPx, each TPx corresponding to a microstructure mx obtained at the end of TPx, are calculated based on the selected product of step A.1) and TPstandard and the initial microstructure mi of the steel sheet to reach mtarget, the thermal enthalpy H released or consumed between mi and mtarget being calculated such that: H x = X ferrite * H ferrite + X martensite * H martensite + X bainite * H bainite + X pearlite * H pearlite + H cementite * X cementite + H austenite ∗ X austenite X being a phase fraction, all thermal cycle TPx being calculated such that T t + Δt = T t + φ Convection + φ radiance ρ ⋅ Ep ⋅ C pe Δt ± H x C pe with Cpe: the specific heat of the phase (J·kg-1·K-1), ρ: the density of the steel (g.m-3), Ep: thickness of the steel (m), ϕ: the heat flux (convective + radiative in W), Hx (J.Kg-1), T: temperature (°C) and t: time (s), 3) an selection sub step wherein one thermal path TPtarget to reach mtarget is selected, TPtarget being chosen from TPx and being selected such that mx is the closest to mtarget, B. a thermal treatment step wherein TPtarget is performed on the steel sheet.

2. Method according to claim 1, wherein the predefined phases in step A.1) are defined by at least one element chosen from: the size, the shape, a chemical and the composition.

3. Method according to anyone of claim 1 or 2, wherein the microstructure mtarget comprises: - 100% of austenite, - from 5 to 95% of martensite, from 4 to 65% of bainite, the balance being ferrite, - from 8 to 30% of residual austenite, from 0.6 to 1.5% of carbon in solid solution, the balance being ferrite, martensite, bainite, pearlite and / or cementite, - from 1% to 30% of ferrite and from 1% to 30% of bainite, from 5 and 25% of austenite, the balance being martensite , - from 5 to 20% of residual austenite, the balance being martensite, - ferrite and residual austenite, - residual austenite and intermetallic phases, - from 80 to 100% of martensite and from 0 to 20% of residual austenite - 100% martensite, - from 5 to 100% of pearlite and from 0 to 95% of ferrite and - at least 75% of equiaxed ferrite, from 5 to 20% of martensite and bainite in amount less than or equal to 10%.

4. Method according to anyone of claims 1 to 3, wherein said predefined product types include Dual Phase, Transformation Induced Plasticity, Quenched & Partitioned steel, Twins Induced Plasticity, Carbide Free Bainite, Press Hardening Steel, TRIPLEX, DUPLEX and Dual Phase High Ductility.

5. Method according to anyone of claims 1 to 4, the differences between proportions of phase present in mtarget and mx is ±3%.

6. Method according to anyone of claims 1 to 5, wherein in step A.2), at least one intermediate steel microstructure mxint corresponding to an intermediate thermal path TPxint and the thermal enthalpy Hxint are calculated.

7. Method according to claim 6, wherein in step in step A.2), TPx is the sum of all TPxint and Hx is the sum of all Hxint.

8. Method according to anyone of claims 1 to 7, wherein before step A.1), at least one targeted mechanical property Ptarget chosen among yield strength YS, Ultimate Tensile Strength UTS, elongation hole expansion, formability is selected.

9. Method according to claim 8, wherein mtarget is calculated based on Ptarget.

10. Method according to anyone of the preceding claims wherein in step A.2), the process parameters undergone by the steel sheet before entering the heat treatment line are taken into account to calculate TPx.

11. Method according to claim 10, wherein the process parameters comprise at least one element chosen from among: a cold rolling reduction rate, a coiling temperature, a run out table cooling path, a cooling temperature and a coil cooling rate.

12. Method according to anyone of claims 1 to 11, wherein the process parameters of the treatment line that the steel sheet will undergo in the heat treatment line are taken into account to calculate TPx.

13. Method according to claim 12, wherein the process parameters comprise at least one element chosen from among: a specific thermal steel sheet temperature to reach, the line speed, cooling power of the cooling sections, heating power of the heating sections, an overaging temperature, a cooling temperature, a heating temperature and a soaking temperature.

14. A method according to anyone of the preceding claims, wherein thermal path, TPx, TPxint, TPstandard or TPtarget, comprise at least one treatment chosen from: a heating, an isotherm or a cooling treatment.

15. A method according to anyone of claims 1 to 14, wherein every time a new steel sheet enters into the heat treatment line, a new calculation step A.2) is automatically performed based on the selection step A.1) performed beforehand.

16. A method according to claim 15, wherein an adaptation of the thermal path is performed as the steel sheet entries into the heat treatment line on the first meters of the sheet.