PROCESS FOR MANUFACTURED AN ANNEILLATED STEEL SHEET BY GALVANIZING

Description

[0001] The present invention relates to a method for the manufacture of a galvannealed steel sheet. The invention is particularly well suited for the manufacture of automotive vehicles.

[0002] Zinc based coatings are generally used because they allow for a protection against corrosion, thanks to barrier protection and cathodic protection. The barrier effect is obtained by the application of a metallic coating on steel surface. Thus, the metallic coating prevents the contact between steel and corrosive atmosphere. The barrier effect is independent from the nature of the coating and the substrate. On the contrary, sacrificial cathodic protection is based on the fact that zinc is a metal less noble that steel. Thus, if corrosion occurs, zinc is consumed preferentially as compared to steel. Cathodic protection is essential in areas where steel is directly exposed to corrosive atmosphere, like cut edges where surrounding zinc will be consumed before steel.

[0003] However, when heating steps are performed on such zinc coated steel sheets, for example hot press hardening or welding, cracks are observed in steel which spread from the steel / coating interface. Indeed, occasionally, there is a reduction of metal mechanical properties due to the presence of cracks in the coated steel sheet after the above operation. These cracks appear with the following conditions: high temperature; contact with a liquid metal having a low melting point (such as zinc) in addition to the presence of tensile stress; heterogeneous diffusion of molten metal with substrate grain and grain boundaries. The designation for such phenomenon is known as liquid metal embrittlement (LME), also called liquid metal assisted cracking (LMAC).

[0004] Sometimes, zinc coated steel sheets are alloyed at high temperature in order to obtain a galvannealed steel sheet. This steel sheet is more resistance to LME than a zinc coated steel sheet because an alloy comprising Fe and Zn is formed which has higher melting point and forms less liquid during spot welding as compared to pure Zinc.

[0005] However, although galvannealed steel sheets are more resistance to LME, when heating steps are performed, some cracks can appear because the resistance to LME is not sufficient enough.

[0006] JP 2004-124187 discloses a cold rolled steel sheet containing, by weight %, 0.05 to 0.25% C, ≤0.1% P, ≤0.1% S, and ≤0.02% N, and containing one or more kinds selected from the group consisting of 0.5 to 3.0% Mn, 0.01 to 2.0% Si, and 0.01 to 2.0% Al at ≤4.0% in total, provided with plating films containing, by weight %, 0.50 to 7.0% Fe, containing 5 to 90vol% Fe-Zn alloy phase developing at the boundary of the plating film and the base metal, the balance being a η phase.

[0007] KR 2012-0074144 discloses a high manganese and high aluminum alloying galvanized steel plate composed of C 0.1 to 1.5wt.%, Mn 5 to 35wt.%, Si 0.1 to 3wt.%, Al 0.01 to 6wt.%, Ni 0.01 to 1wt.%, Ti 0.01 to 0.2wt.%, B 0005 to 0.006wt.% and which coating is a Fe-Mn-Zn alloy layer containing more than 1 wt.% of Mn, the sum of Mn and Fe being less than 12 wt.% in the alloy layer.

[0008] Thus, the object of the invention is to provide a galvannealed steel sheet which does not have LME issues. It aims to make available, in particular, an easy to implement method in order to obtain an assembly which does not have LME issues after the forming and / or the welding.

[0009] This object is achieved by providing a method according to claim 1. The method can also comprise any characteristics of claims 2 to 14.

[0010] Other characteristics and advantages of the invention will become apparent from the following detailed description of the invention.

[0011] The designation "steel" or "steel sheet" means a steel sheet, a coil, a plate having a composition allowing the part to achieve a tensile strength up to 2500 MPa and more preferably up to 2000MPa. For example, the tensile strength is above or equal to 500 MPa, preferably above or equal to 980 MPa, advantageously above or equal to 1180 MPa and even above or equal 1470 MPa.

[0012] The invention relates to a method for the manufacture of a galvannealed steel sheet comprising the following steps: A. the provision of a pre-coated steel sheet coated with a first coating consisting of iron and from 25 to 90% by weight of nickel such steel sheet having the following chemical composition in weight percent: 0.10 < C < 0.40 % , 1.5 < Mn < 3.0 % , 0.7 < Si < 2.0 % , 0.05 < Al < 1,0 % 0.75 < Si + Al < 3.0 % and on a purely optional basis, one or more elements such as Nb ≤ 0.5 % , B ≤ 0.005 % , Cr ≤ 1.0 % , Mo ≤ 0.50 % , Ni ≤ 1.0 % , Ti ≤ 0.5 % , the remainder of the composition making up of iron and inevitable impurities resulting from the elaboration, B. the thermal treatment of such pre-coated steel sheet at a temperature between 600 to 1000°C, C. the hot-dip coating of the steel sheet obtained in step B) with a second coating based on zinc and D. an alloying treatment to form a galvannealed steel sheet.

[0013] Without willing to be bound by any theory, it seems that during the thermal treatment, on the one hand, Ni diffuses towards the steel sheet allowing a Fe-Ni alloy layer. On the other hand, some amount of Ni is still present at the interface between the steel and the coating interface which preventing liquid zinc penetration into steel during any heating steps being for example a welding. Moreover, the presence of iron in the first coating allows for the formation of the Fe-Zn alloy during step D).

[0014] The first coating comprising iron and nickel is deposited by any deposition method known by the man skilled in the art. It can be deposited by vacuum deposition or electro-plating method. Preferably, it is deposited by electro-plating method.

[0015] In step A), the first coating comprises from 25.0 to 90%, preferably from 35 to 75% and advantageously from 40 to 60% by weight of nickel.

[0016] In step A), the first coating consists of iron and nickel.

[0017] Preferably, in step A), the first coating has a thickness equal or above 0.5 µm. More preferably, the first coating has a thickness between 0.8 and 5.0µm and advantageously between 1.0 and 2.0µm.

[0018] Preferably, in step B), the thermal treatment is a continuous annealing. For example, the continuous annealing comprises a heating, a soaking and a cooling step. It can further comprise a pre-heating step.

[0019] Advantageously, the thermal treatment is performed in an atmosphere comprising from 1 to 30% of H 2 at a dew point between -10 and -60°C. For example, the atmosphere comprises from 1 to 10% of H 2 at a dew point between - 40°C and -60°C.

[0020] Advantageously, in step C), the second layer comprises above 70%, more preferably above 80% of zinc and advantageously above 85% of zinc. The second layer can be deposited by any deposition method known by the man skilled in the art. It can be done by hot-dip coating, by vacuum deposition or by electro-galvanizing.

[0021] For example, the coating based on zinc comprises between 0.01 and 0.18 wt.% Al, optionally 0.2-8.0% Mg, the remainder being Zn.

[0022] Preferably, the coating based on zinc is deposited by hot-dip galvanizing method. In this embodiment, the molten bath can also comprise unavoidable impurities and residuals elements from feeding ingots or from the passage of the steel sheet in the molten bath. For example, the optionally impurities are chosen from Sr, Sb, Pb, Ti, Ca, Mn, Sn, La, Ce, Cr, Zr or Bi, the content by weight of each additional element being inferior to 0.3% by weight. The residual elements from feeding ingots or from the passage of the steel sheet in the molten bath can be iron with a content up to 5.0%, preferably 3.0%, by weight.

[0023] In a preferred embodiment, the second layer consists of zinc. In this case, when the coating is deposited by hot-dip galvanizing, the percentage of Aluminum is comprised between 0.10 and 0.18 wt.% in the bath.

[0024] Preferably, in step D), the alloying treatment is performed by heating the coated steel sheet obtained in step C) at a temperature between 460 and 550 °C for 5 to 40 seconds. For example, step D is performed at 500°C for 20 seconds.

[0025] With the method according to the present invention, a galvannealed steel sheet is obtained with a first layer comprising iron and nickel directly topped by a second layer based on zinc, the first and second layers being alloyed through diffusion such that the second alloy layer comprising from 5 to 15wt.% of iron, from 0 to 15wt.% and preferably from 1 to 15wt.% of nickel, the balance being zinc.

[0026] Preferably, the steel sheet has a microstructure comprising from 1 to 50% of residual austenite, from 1 to 60% of martensite and optionally at least one element chosen from: bainite, ferrite, cementite and pearlite. In this case, the martensite can be tempered or untempered.

[0027] In a preferred embodiment, the steel sheet has a microstructure comprising from 5 to 25 % of residual austenite.

[0028] Preferably, the steel sheet has a microstructure comprising from 1 to 60% and more preferably between 10 to 60% of tempered martensite.

[0029] Advantageously, the steel sheet has a microstructure comprising from 10 to 40% of bainite, such bainite comprising from 10 to 20% of lower bainite, from 0 to 15% of upper bainite and from 0 to 5% of carbide free bainite.

[0030] Preferably, the steel sheet has a microstructure comprising from 1 to 25% of ferrite.

[0031] Preferably, the steel sheet has a microstructure comprising from 1 to 15% untempered martensite.

[0032] After the manufacture of a steel sheet, in order to produce some parts of a vehicle, it is known to assembly by welding two metal sheets. Thus, a spot welded joint is formed during the welding of at least two metal sheets, said spot being the link between the at least two metal sheets.

[0033] To produce a spot welded joint, the welding is performed with an effective intensity is between 3kA and 15kA and the force applied on the electrodes is between 150 and 850 daN with said electrode active face diameter being between 4 and 10mm.

[0034] Thus, a spot welded joint of at least two metal sheets, comprising the coated steel sheet produced according to the present invention, is obtained, such said joint containing less than 3 cracks having a size above 100µm and wherein the longest crack has a length below 400µm.

[0035] Preferably, the second metal sheet is a steel sheet or an aluminum sheet. More preferably, the second metal sheet is a steel sheet according to the present invention.

[0036] In another embodiment, the spot welded joint comprises a third metal sheet being a steel sheet or an aluminum sheet. For example, the third metal sheet is a steel sheet according to the present invention.

[0037] The steel sheet or the spot welded joint can be used for the manufacture of parts for automotive vehicle.

[0038] The invention will now be explained in trials carried out for information only. They are not limiting.Example

[0039] For all samples, steel sheets used have the following composition in weight percent: C=0.37 wt.%, Mn=1.9 wt.%, Si=1.9 wt.%, Cr=0.35 wt.%, Al=0.05 wt.% and Mo=0.1%.

[0040] Trial 1 to 4 were prepared by deposited a first coating comprising 55% and 75% of Ni, the balance being Fe. Then, a continuous annealing was performed in an atmosphere comprising 5% of H 2 and 95% of N 2 at a dew point of -45°C. The pre-coated steel sheet was heated at a temperature of 900°C. A zinc coating was deposited by hot-dip galvanizing, the zinc bath comprising 0.2% of Al. The bath temperature was of 460°C. Finally, an alloying treatment was performed at 500°C for 20 seconds in order to obtain a galvannealed steel sheet.

[0041] For comparison purpose, Trial 5 was prepared by depositing a zinc coating by electro-galvanizing after the continuous annealing of the above steel sheet.

[0042] The resistance to LME of Trials 1 to 5 was evaluated. To this end, for each Trial, two coated steel sheets were welded together by resistance spot welding. The type of the electrode was ISO Type B with a diameter of 16mm; the force of the electrode was of 5kN and the flow rate of water of was 1.5g / min. The welding cycle was cycle is reported in Table 1. Table 1. Welding ScheduleWeld timePulsesPulse (cy)Cool time (cy)Hold time (cy)Cycle212210

[0043] The number of cracks above 100µm was then evaluated using an optical as well as SEM (Scanning Electron Microscopy) as reported in Table 2. Table 2. LME crack details after spot welding (2 layer stack-up condition)Trials1 st< coatingThickness (µm)2 nd< coatingThickness (µm)Number of cracks (> 100µm) per spot weldMaximum crack length (µm)Trial 1*Fe - (55%)Ni1Zn (GA)700Trial 2*Fe - (55%)Ni2Zn (GA)70250Trial 3*Fe - (75%)Ni1Zn (GA)70250Trial 4*Fe - (75%)Ni2Zn (GA)700Trial 5--Zn (EG)73760

[0044] Trials 1-4 show an excellent resistance to LME compared to Trial 5. Indeed, the number of cracks of Trials 1-4 is very low, even nonexistent, compared to Trial 5

[0045] For each Trial, three coated steel sheets were also welded together by resistance spot welding under three layer stack-up configuration. The number of cracks above 100µm was then evaluated using an optical as well as SEM (Scanning Electron Microscopy) as reported in Table 3. Table 3. LME crack details after spot welding (3 layer stack-up condition)TrialsNumber of cracks (> 1001µm) per spot weldMaximum crack length (µm)Trial 1*1250Trial 2*2350Trial 3*1150Trial 4*1250Trial 57850

[0046] Trials 1-4 show an excellent resistance to LME as compared to Trial 5.

[0047] Finally, Trials 1 to 4 were bent at a 90° angle followed. An adhesive tape was then applied and removed to verify the coating adhesion with the substrate steel. The coating adhesion of those Trials was excellent.

Claims

1. Method for the manufacture of a galvannealed steel sheet comprising the following steps: A. the provision of a pre-coated steel sheet coated with a first coating consisting of iron and from 25 to 90% by weight of nickel, such steel sheet having the following chemical composition in weight percent: 0.10 < C < 0.40 % , 1.5 < Mn < 3.0 % , 0.7 < Si < 2.0 % , 0.05 < Al < 1.0 % 0.75 < Si + Al < 3.0 % and on a purely optional basis, one or more elements such as Nb ≤ 0.5 % , B ≤ 0.005 % , Cr ≤ 1.0 % , Mo ≤ 0.50 % , Ni ≤ 1 .0% , Ti ≤ 0 .5% , the remainder of the composition making up of iron and inevitable impurities resulting from the elaboration, B. the thermal treatment of such pre-coated steel sheet at a temperature between 600 to 1000°C, C. the hot-dip coating of the steel sheet obtained in step B) with a second coating based on zinc and D. an alloying treatment to form a galvannealed steel sheet.

2. Method according to claim 1, wherein in step A), the first coating comprises from 10% to 75% by weight of iron.

3. Method according to claim 2, wherein in step A), the first coating comprises from 25.0 to 65.0% by weight of iron.

4. Method according to anyone of claims 1 to 3, wherein in step A), the first coating comprises from 40 to 60% of weight of iron.

5. Method according to anyone of claims 1 to 4, wherein in step A), the first coating has a thickness equal or above 0.5 µm.

6. Method according to claim 5, wherein in step A), the first coating has a thickness between 0.8 and 5.0 µm.

7. Method according to claim 6, wherein in step A), the first coating has a thickness between 1.0 and 2.0µm.

8. Method according to anyone of claims 1 to 7, wherein in step C), the second layer comprises above 70% of zinc.

9. Method according to claim 8, wherein in step C), the second layer comprises above 80% of zinc.

10. Method according to claim 9, wherein in step C), the second layer comprises above 85 % of zinc.

11. Method according to claim 10, wherein in step C), the second layer consists of zinc.

12. Method according to anyone of claims 1 to 11, wherein in step B), the thermal treatment is a continuous annealing.

13. Method according to anyone of claims 1 to 12, wherein in step B), the thermal treatment is performed in an atmosphere comprising from 1 to 10% of H2 at a dew point between -30 and -60°C.

14. Method according to anyone of claims 1 to 13, wherein in step D), the alloying treatment is performed by heating the coated steel sheet obtained in step C) at a temperature between 460 and 550 °C.