Liquid hydrogenated nitrile-butadiene rubber, preparation method therefor and use thereof

AU2021346019B2Pending Publication Date: 2026-09-17ZANNAN SCITECH CO LTD
View PDF 2 Cites 0 Cited by

Patent Information

Application Number
AU2021346019
Authority / Receiving Office
AU · AU
Patent Type
Applications
Current Assignee / Owner
Priority Date
2020-09-16
Filing Date
2021-09-16
Publication Date
2026-09-17
Estimated Expiration
2041-09-16
Patent Text Reader

Abstract

Disclosed are a liquid hydrogenated nitrile-butadiene rubber, a preparation method therefor and the use thereof. In the liquid hydrogenated nitrile-butadiene rubber, the content of acrylonitrile is 15-50%; the hydrogenation saturation is 75-99.5%; the weight-average molecular weight (Mw) is 3,000-60,000; the molecular weight polydispersity index (PDI) is 2.0-8.0; and the glass transition temperature (Tg) is lower than -28°C. The liquid hydrogenated nitrile-butadiene rubber is low in molecular weight and wide in molecular weight distribution, simultaneously has an excellent fluidity during processing and excellent mechanical properties after curing, and has a unique application value in the field of special rubbers; and the preparation method therefor is simple and feasible in terms of the process.
Need to check novelty before this filing date? Find Prior Art

Description

LIQUID HYDROGENATED NITRILE-BUTADIENE RUBBER, PREPARATION METHOD THEREFOR AND USE THEREOF TECHNOLOGY FIELD OF THE INVENTION The present invention relates to a novel class of the liquid hydrogenated butadiene nitrile rubber (LHNBR), its preparation method and applications. BACKGROUND TECHNOLOGY OF THE INVENTION Hydrogenated nitrile butadiene rubber (HNBR) plays an important role in aerospace, petroleum, automotive and energy applications with its excellent properties. One of the special HNBR grades is LHNBR, which can be combined with reinforcing fillers, vulcanisation accelerators and other rubber additives to produce a vulcanized rubber with good elasticity, better flow and easier processing. In addition, it has important applications in the special adhesives, sealants and shaped complex elastic products, especially as a possible matrix material as special composite materials such as electromagnetic shielding coatings, oil resistant coatings, battery corrosion resistant coatings sealing accessories, damping and noise reduction coatings. According to the literature, there were two technical routes for the preparation of liquid hydrogenated nitrile butadiene rubber (LHNBR): one was prepared by catalyzed hydrogenation of liquid nitrile butadiene rubber (LNBR) in solution, and another method was to prepare by dissolving the solid NBR, then carried out the degradation and followed by the catalyzed hydrogenation. Patent CN104231118A disclosed a hydrogenated LNBR capped with hydroxyl group (LNBR-OH) and its preparation method, in which the LNBR-OH was hydrogenated by a liquid non-homogeneous reaction using a catalytic hydrogenation system consisting of hydrazine hydrate-boric acid-hydrogen peroxide to obtain a hydrogenated LNBR-OH rubber 2021346019   25 Aug 2026 without gel byproduct and with a hydrogenation degree of more than 90%. CN102481562A disclosed a method for the preparation of the LHNBR by dissolving NBR in a chlorobenzene solvent, and a certain amount of 1-hexene is added, stirred for 2hours at 22°C, followed by adding the coupound catalyst "1,3-bis-(2,4,6-trimethylphenyl)-2-imidazolylmethylene)-(tricyclohexylphosphine)-(phenylmethylene)ruthenium dichloride" (the second generation of Grubbs catalyst), and stirred for 2hours at 22°C to completed the degradation of NBR; after degradation of NBR, the hydrogenation catalyst "tris-(triphenylphosphine)-rhodium chloride" (Wilkinson's catalyst) was then added and the hydrogenation reaction was stirred at 138°C for 4hours.. The result was a LHNBR with a molecular weight (Mw) between 10,000 and 50,000 and a molecular weight polydispersity index (PDI) was less than 2.0. Since some hydrogenation catalysts such as Wilkinson's catalysts only hydrogenate the carbon-carbon double bond in NBR during the hydrogenation reaction, the result was not possible to change the molecular weight polydispersity index (PDI) of the corresponding LHNBR in the hydrogenation reaction. Obviously, the existing techniques for the preparation of LHNBR were still not good enough to prepare different kinds of LHNBR products, and it was still needed to develop more LHNBR products with better properties and diversity of applications. For example, in the method disclosed in CN102481562A, the entire preparation process undergoes two process steps: the degradation and hydrogenation in two steps and two different kinds of metal catalysts used in each step, resulting in a relatively narrow molecular weight polydispersity (PDI < 2.0), and it may be difficult to balance the fluidity during processing and the mechanical properties after curing (e.g. elasticity and strength, etc.), however if the molecular weight is high, although the mechanical properties were good after curing, but the fluidity is poor, which means that it was not only difficult to dry during the preparation process, but also very undesirable when used to prepare adhesives, sealants and cast shaped complex elastic products. 2021346019   25 Aug 2026 A reference herein to a patent document or any other matter identified as prior art, is not to be taken as an admission that the document or other matter was known or that the information it contains was part of the common general knowledge as at the priority date of any of the claims. Unless the context requires otherwise, where the terms “comprise”, “comprises”, “comprised” or “comprising” are used in this specification (including the claims) they are to be interpreted as specifying the presence of the stated features, integers, steps or components, but not precluding the presence of one or more other features, integers, steps or components, or group thereof. SUMMARY OF THE INVENTION The present invention is designed to address the strength and flowability balancing of LHNBR during the processing and mechanical properties after LHBNR curing, thereby to provide different kinds of new LHNBR products and its preparation method and application. The LHNBR of the present invention has not only low molecular weight but also wide molecular weight polydispersity, as well as excellent fluidity during processing and excellent mechanical properties after curing; and the preparation method of the present invention was also quite simple and feasible process. In various aspects, the invention provides: The First Aspect: A liquid hydrogenated nitrile rubber (LHNBR), wherein: the acrylonitrile (ACN) content is from 15% to 50%; the hydrogenation degree is from 75% to 99.5%; the weight average molecular weight (Mw) is from 3,000 to 60,000; 2021346019   25 Aug 2026 the molecular weight polydispersity index (PDI) is 2.0 to 8.0; the glass transition temperature (Tg) is below -28°C. In the present invention, the acrylonitrile (ACN) content of the LHNBR is preferably from 17% to 45%, e.g., 25%, 33% or 43%. In the present invention, the LHNBR has a hydrogenation degree of preferably 80% to 99%, more preferably from 90% to 99%, e.g., 91%, 92%, 95% or 96%. In the present invention, the LHNBR has a weight average molecular weight (Mw) preferably in the range of 5,000 to 50,000, more preferably in the range of 8,000 to 20,000 or 24,000 to 46,000. In the present invention, the molecular weight polydispersity index (PDI) of LHNBR is preferably in the range of 2.0 to 6.0. In the present invention, the LHNBR had a glass transition temperature (Tg) preferably below -35°C, better below -40°C. In the present invention, the LHNBR has an extrapolated glass transition onset temperature (Tig) lower than -30°C, preferably lower than -35°C, and more preferably lower than -45°C. In the present invention, the LHNBR has an extrapolated end of the glass transition temperature (Teg) lower than -25°C, preferably lower than 30°C, and better lower than -35°C. In the present invention, the LHNBR preferably a kind of LHNBR as shown in the following formula IIIa or IIIb, HoC-CH^H-CHoH^C^-CH-W-HoC-CHo-CHo-CHo-V- / P \        | / n \                            / q CN Illa 2021346019   25 Aug 2026 H2C-CH=CH-CH2-WcH2-CH4-7^-H2C-CH2-CH2-CH24-r / p \       | / n \                           / q CN IHb wherein, p = 1~150; p’= 1~150; q = 30~590; q’= 30~590; n = 20~500; n’ = 20~500. In the present invention, preferably in the LHNBR: the acrylonitrile (ACN) content of 17 to 45 per cent; the hydrogenation degree is from 80% to 99%; the weight average molecular weight (Mw) is from 5,000 to 50,000; the molecular weight polydispersity index (PDI) is from 2.0 to 6.0; the glass transition temperature (Tg) is below -28°C. In the present invention, preferably in the LHNBR: the acrylonitrile (ACN) content is 33%; the hydrogenation degree is 99%; the weight average molecular weight (Mw) is from 8,000 to 20,000; the molecular weight polydispersity index (PDI) is from 2.5 to 3.5; the glass transition temperature (Tg) is below -35°C. In the present invention, preferably in the LHNBR: the acrylonitrile (ACN) content is 25% to 43%; the hydrogenation degree is 91% to 99%; the weight average molecular weight (Mw) is from24,000~46,000; the molecular weight polydispersity index (PDI) is from 2.1 to 5.6; the glass transition temperature (Tg) below -29°C. In a preferable embodiment of the present invention, wherein the LHNBR is: the acrylonitrile(ACN) content of 33%; 2021346019   25 Aug 2026 the hydrogenation degree is 92%; the weight average molecular weight (Mw) is from 37,000 to 38,000; the molecular weight polydispersity index (PDI) is 2.1; the glass transition temperature (Tg) is -31.2°C. In a preferable embodiment of the present invention, wherein the LHNBR is: the acrylonitrile(ACN) content is 33%; the hydrogenation degree is 96%; the weight average molecular weight (Mw) is from 44,000 to 45,000; the molecular weight polydispersity index (PDI) is 2.2; the glass transition temperature (Tg) is -2.5°C. In a preferable embodiment of the present invention, wherein the LHNBR is: the acrylonitrile(ACN) content is 33%; the hydrogenation degree is 99%; the weight average molecular weight (Mw) is from 45,000 to 46,000; the molecular weight polydispersity index (PDI) is 2.2; the glass transition temperature (Tg) is -29.8°C. In a preferable embodiment of the present invention, wherein the LHNBR is: the acrylonitrile(ACN) content is 33%; the hydrogenation degree is 99%; the weight average molecular weight (Mw) is from 24,000 to 25,000; the molecular weight polydispersity index (PDI) is 2.4; the glass transition temperature (Tg) is -30.9°C. In a preferable embodiment of the present invention, wherein the LHNBR is: the acrylonitrile(ACN) content is 33%; the hydrogenation degree is 99%; 2021346019   25 Aug 2026 the weight average molecular weight (Mw) is from 8,000 to 10,000; the molecular weight polydispersity index (PDI) is 2.7; the glass transition temperature (Tg) is -42.8°C. In a preferable embodiment of the present invention, wherein the LHNBR is: the acrylonitrile(ACN) content is 33%; the hydrogenation degree is 99%; the weight average molecular weight (Mw) is from 16,000 to 17,000; the molecular weight polydispersity index (PDI) is 3.3; the glass transition temperature (Tg) is -38.8°C. In a preferable embodiment of the present invention, wherein the LHNBR is: the acrylonitrile(ACN) content is 43%; the hydrogenation degree is 91%; the weight average molecular weight (Mw) is from 33,000 to 34,000; the molecular weight polydispersity index (PDI) is 4.3; the glass transition temperature (Tg) is -30.2°C. In a preferable embodiment of the present invention, wherein the LHNBR is: the acrylonitrile content is 25%; the hydrogenation degree is 95%; the weight average molecular weight (Mw) is from 33,000 to 34,000; the molecular weight polydispersity index (PDI) is 5.6; the glass transition temperature (Tg) is -32.9°C. The liquid hydrogenated nitrile rubber (LHNBR) according to any embodiment of the first aspect may be produced by the method of the second aspect, to be described hereafter. The Second Aspect: A method of preparing LHNBR comprising the steps of: under the protection of an inert 2021346019   25 Aug 2026 gas, in an organic solvent, added the NBR to a degradation reaction and a hydrogenation reaction, or added the NBR to a hydrogenation reaction, and in the presence of a catalyst to obtain the liquid hydrogenated nitrile rubber (LHNBR); wherein the catalyst comprises one or more of Zhan Catalysts as shown in the following general formula I: In the present invention, the general formula I was documented in CN200910175790.6, US12684410 and WO2011079439A1, referred to CN200910175790.6, US12684410 and WO2011079439A1 for definitions of the individual substituents in general formula I. In general formula I, L is an electron-donating complex ligand; for example, L may be IMes—N. .N-Mes .                                         1                        ; L1 and L2 are independently halogen; n = 0 or 1; when n=1, Y1 is independently nitrogen, oxygen, sulfur, CH2, substituted or unsubstituted C1-C20 alkyl, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C6-C20 aryloxy, substituted or unsubstituted C1-C2 heterocyclic aryl, carbonyl, a carbonyl group linked to a substituted or unsubstituted C1-C20 alkyl, a carbonyl group linked to a substituted or unsubstituted C1-C20 alkoxy carbonyl, imino, substituted or unsubstituted C1-C20alkylimino or amino as shown in RcRdN- group; wherein Rc and Rd are independently hydrogen, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C1-C2 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkylcarbonyl, substituted or unsubstituted C6-C20 aryl formyl or substituted or unsubstituted C1-C2 2021346019   25 Aug 2026 heterocyclic formyl group; or Rc, Rd and the N atom are linked each other to form a ring; X is nitrogen, oxygen, sulphur, CH, CH2 or carbonyl group; Y is nitrogen, oxygen, CH, methylene, substituted or unsubstituted C1-C20 alkoxy, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C2-C20 heterocyclic aryl, a carbonyl group linked to a substituted or unsubstituted C1-C20 alkyl, a carbonyl group linked to a substituted or unsubstituted C1-C20 alkoxy, an imino group, a substituted or unsubstituted C1-C20 alkyl imino group or a group as shown in RcRdN-group; wherein Rc and Rd are independently hydrogen, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkylcarbonyl, substituted or unsubstituted C6-C20 arylcarbonyl or substituted or unsubstituted C2-C20 heterocycliccarbonyl;; or Rc, Rd and N atom are linked to form a ring; the parent to which the group indicated by X is linked is Y and the parent to which the group indicated by Y is linked is X; " " between single or double bonds; R1 is hydrogen, substituted or unsubstituted C1-C20 alkyl, substituted or unsubstituted C1-C20 alkoxy, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C6-C20 aryloxy or substituted or unsubstituted C2-C20 heterocyclic; R2 is hydrogen, substituted or unsubstituted C1-C20 alkyl, substituted or unsubstituted C1-C20 alkoxy, substituted or unsubstituted C1-C20 alkylthio, substituted or unsubstituted C1-C20 alkylsiloxy, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C6-C20 aryl, C6-C20 aryloxy, aldehyde, a carbonyl group linked to a substituted or unsubstituted C1-C20 alkyl, a carbonyl group linked to a substituted or unsubstituted C6-C20 aryl, a carbonyl group linked to a substituted or unsubstituted C2-C20 heterocyclic or a group as shown in RcRdN- group; wherein Rc and Rd are independently hydrogen, a formyl group, a substituted or unsubstituted C1-C20 alkyl formyl group, a substituted or unsubstituted C6-C20 aryl formyl group or a substituted or unsubstituted C2-C20 heterocyclic formyl group; or wherein Rc, Rd 2021346019   25 Aug 2026 and the N atom are linked each other to form a ring; E is hydrogen, halogen, nitro, nitrile, sulfinyl, sulfone, aldehyde, C1-C20 alkyl, C1-C20 alkoxy, C1-C20 alkylthio, C1-C20 alkyl silyl, C1-C20 alkyl siloxy, C2-C20 heterocyclic, C6-C20 aryl, C6-C20 aryloxy, carbonyl linked to C1-C20 alkyl, carbonyl linked to C6-C20 aryl C6-C20 heterocyclic, carbonyl linked to C2-C20 heterocyclic, carbonyl linked to C1-C20 alkoxy, carbonyl linked to C6-C20 aryloxy, carbonyl linked to C6-C20 heterocyclic oxy, aminoacyl, carbonyl linked to C1-C20 alkylamino, carbonyl linked to C6-C20 arylamino, carbonyl linked to C2-C20 heterocyclic amino, ureido, substituted or unsubstituted C1-C20 alkyl ureido, substituted or unsubstituted C6-C20 aryl ureido, substituted or unsubstituted C2-C20 heterocyclic ureido, sulfonyl group linked to a C1-C20 alkyl amino group, sulfonyl group linked to a C6-C20 aryl amino group, sulfonyl group linked to a C2-C20 heterocyclic amino group, or a group as shown in RcRdN- group; wherein Rc and Rd are independently hydrogen, substituted or unsubstituted C6-C2 aryl, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkyl formyl, substituted or unsubstituted C6-C2 aryl formyl, substituted or unsubstituted C2-C20 heterocyclic formyl, substituted or unsubstituted C1-C20 alkyl sulfonyl, substituted or unsubstituted C6-C2 aryl sulfonyl, or substituted or unsubstituted C2-C20heterocyclic sulfonyl; or Rc, Rd and the N atom are linked each other to form a ring. E1 is hydrogen, halogen, nitro, nitrile, C1-C20 alkyl, C1-C20 alkoxy, C1-C20 alkylthio, C1-C20 alkasilyl, C1-C20 alkasiloxy, C2-C20 heterocyclic, substituted or unsubstituted amino, aminoacyl, carbonyl linked to C1-C20 alkylamino, C6-C20 aryl, C6-C20 aryloxy, sulfinyl, sulfone group, aldehyde group, carbonyl group linked to a C1-C20 alkyl group, carbonyl group linked to a substituted or unsubstituted C6-C20 aryl group, carbonyl group linked to a substituted or unsubstituted C2-C20 heterocyclic group, carbonyl group linked to a C1-C20 alkoxy group, carbonyl group linked to a C6-C20 aryloxy group, carbonyl group linked to a C2-C20 2021346019   25 Aug 2026 heterocyclic oxy group, urea group, substituted or unsubstituted C1-C20 alkyl urea group , substituted or unsubstituted C6-C20 aryl ureido groups or substituted or unsubstituted C2-C20 heterocyclic ureido groups: E2 is hydrogen, halogen, C1-C20 alkyl, C1-C20 alkoxy, C1-C20 alkylthio, C1-C20 alkyl silyl, C1-C20 alkyl siloxy, aminoacyl, carbonyl linked to C1-C20 alkylamino, carbonyl linked to C6-C20 arylamino, carbonyl linked to C2-C20 heterocyclic amino, C6-C20 aryl, C6-C20 aryl oxy, C2-C20 heterocyclic aryl, aldehyde, a carbonyl group linked to a C1-C20 alkyl group, a carbonyl group linked to a C6-C20 aryl group, a carbonyl group linked to a C2-C20 heterocyclic group, a carbonyl group linked to a C1-C20 alkoxy group, a carbonyl group linked to a C6-C20 aryloxy group, a carbonyl group linked to a C2-C20 heterocyclic oxy group or a group as shown in RcRdN- group; wherein Rc and Rd are independently hydrogen, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkyl formyl, substituted or unsubstituted C6-C20 aryl formyl, substituted or unsubstituted C2-C20 heterocyclic formyl, substituted or unsubstituted C1-C20 alkyl sulfonyl, substituted or unsubstituted C6-C20 aryl sulfonyl, or substituted or unsubstituted C2-C20 heterocyclic sulfonyl; or Rc, Rd and the N atom are linked each other to form a ring. E3 is hydrogen, halogen, C1-C20 alkyl, C1-C20 alkoxy, C1-C20 alkylthio, C1-C20 alkyl siloxy, C6-C20 aryloxy, C6-C20 aryl, C2-C20 heterocyclic aryl, a carbonyl group linked to a C1-C20 alkoxy, a carbonyl group linked to a substituted or unsubstituted C6-C20 aryloxy, a carbonyl group linked to a substituted or unsubstituted C6-C20 heterocyclic aryloxy or a group as shown in RcRdN- group; wherein Rc and Rd are independently hydrogen, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkyl formyl, substituted or unsubstituted C6-C20 aryl formyl, substituted or unsubstituted C2-C20 heterocyclic formyl, 2021346019   25 Aug 2026 substituted or unsubstituted C1-C20 alkyl sulfonyl, substituted or unsubstituted C6-C20 aryl sulfonyl, or substituted or unsubstituted C2-C20 heterocyclic sulfonyl; or Rc, Rd and the N atom are linked each other to form a ring. E4, E5, E6 and E7 are independently hydrogen, halogen, nitro, nitrile, sulfinyl, sulfonyl, aldehyde, substituted or unsubstituted C1-C20 alkyl, substituted or unsubstituted C1-C20 alkoxy, C1-C20 alkylthio, C1-C20 alkasilyl, C1-C20 alkasiloxy, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted amino, amino acyl, carbonyl groups linked to substituted or unsubstituted C1-C20 alkylamino groups, carbonyl groups linked to substituted or unsubstituted C6-C20 arylamino groups, carbonyl groups linked to substituted or unsubstituted C2-C20 heterocyclic amino groups, carbonyl groups linked to substituted or unsubstituted C1-C20 alkyl groups, carbonyl groups linked to substituted or unsubstituted C6-C20 aryl groups, carbonyl groups linked to substituted or unsubstituted C2-C20 heterocyclic group, carbonyl group linked to substituted or unsubstituted C1-C20 alkoxy, carbonyl group linked to substituted or unsubstituted C6-C20 aryloxy, carbonyl group linked to substituted or unsubstituted C6-C20 heterocyclic oxy, ureido, substituted or unsubstituted C1-C20 alkyl ureido, substituted or unsubstituted C6-C20 aryl ureido, substituted or unsubstituted C2-C20 heterocyclic based ureido, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C6-C20 aryloxy, or a group as shown in RcRdN- group; wherein Rc and Rd are independently hydrogen, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkyl formyl, substituted or unsubstituted C6-C20 aryl formyl, substituted or unsubstituted C2-C20 heterocyclic formyl, substituted or unsubstituted C1-C20 alkyl sulfonyl, substituted or unsubstituted C6-C20 aryl sulfonyl, or substituted or unsubstituted C2-C20 heterocyclic sulfonyl; or Rc, Rd and the N atom are linked each other to form a ring. In various embodiments disclosed herein is: a method for the preparation of a liquid 2021346019   25 Aug 2026 hydrogenated nitrile butadiene rubber comprising the steps of: adding nitrile butadiene rubber (NBR) to a degradation reaction and a hydrogenation reaction in the presence of Zhan catalyst under the protection of an inert gas in an organic solvent, or adding NBR to a hydrogenation reaction in the presence of Zhan catalyst under the protection of an inert gas in an organic solvent, to obtain liquid hydrogenated nitrile butadiene rubber; wherein the Zhan catalyst is one or more of the Zhan catalysts shown in general formula I: in the general formula I: L is an electron-donating complex ligand; L1 and L2 are independently halogen; n = 0 or 1; when n=1, Y1 is independently nitrogen, oxygen, sulphur, CH2, substituted or unsubstituted C1-C20 alkyl, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C6-C20 aryloxy, substituted or unsubstituted C2-C20 heterocyclic aryl, carbonyl, carbonyl linked to a substituted or unsubstituted C1-C20 alkyl, carbonyl linked to a substituted or unsubstituted C1-C20 alkoxy, imino, substituted or unsubstituted C1-C20 alkyl imino or amino as shown in RcRdN- group; wherein, Rc and Rd are independently hydrogen, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkyl formyl, substituted or unsubstituted C6-C20 aryl formyl or substituted or unsubstituted C2-C20 heterocyclic formyl; or Rc, Rd and the N atom are linked each other to form a ring; X is CH2; Y is nitrogen, an imino group, a substituted or unsubstituted C1-C20 alkyl imino group; the parent to which the group indicated by X linked is Y, and the parent to which the group indicated by Y linked is X; "X Y" between the X and Y is single bond; R1 is hydrogen, substituted or unsubstituted C1-C20 2021346019   25 Aug 2026 alkyl, substituted or unsubstituted C1-C20 alkoxy, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C6-C20 aryloxy or substituted or unsubstituted C2-C20 heterocyclic group; R2 is hydrogen, substituted or unsubstituted C1-C20 alkyl, substituted or unsubstituted C1-C20 alkoxy, substituted or unsubstituted C1-C20 alkylthio, substituted or unsubstituted C1-C20 alkylsiloxy, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C6-C20 aryl, C6-C20 aryloxy, aldehyde, carbonyl group linked to a substituted or unsubstituted C1-C20 alkyl, carbonyl group linked to a substituted or unsubstituted C6-C20 aryl, carbonyl group linked to a substituted or unsubstituted C2-C20 heterocyclic or a group as shown in RcRdN-group; wherein Rc and Rd are independently hydrogen, formyl, substituted or unsubstituted C1-C20 alkyl formyl group, substituted or unsubstituted C6-C20 aryl formyl group, substituted or unsubstituted C2-C2 heterocyclic formyl group; or wherein Rc, Rd and the N atom are linked each other to form a ring; E is hydrogen, halogen, nitro, nitrile, sulfinyl, sulfone, aldehyde, C1-C20 alkyl, C1-C20 alkoxy, C1-C20 alkylthio, C1-C20 alkyl silyl, C1-C20 alkyl siloxy, C2-C20 heterocyclic, C6-C20 aryl, C6-C20 aryloxy, carbonyl linked to C1-C20 alkyl, carbonyl linked to C6-C20 aryl C6-C20 heterocyclic, carbonyl linked to C2-C20 heterocyclic, carbonyl linked to C1-C20 alkoxy, carbonyl linked to C6-C20 aryloxy, carbonyl linked to C6-C20 heterocyclicoxy, aminoacyl, carbonyl linked to C1-C20 alkylamino, carbonyl linked to C6-C20 arylamino, carbonyl linked to C2-C20 heterocyclic amino, ureido, substituted or unsubstituted C1-C20 alkyl ureido, substituted or unsubstituted C6-C20 aryl ureido, substituted or unsubstituted C2-C20 heterocyclic ureido, sulfonyl group linked to a C1-C20 alkyl amino group, sulfonyl group linked to a C6-C20 aryl amino group, sulfonyl group linked to a C2-C20 heterocyclic amino group, or a group as shown in RcRdN- group; wherein Rc and Rd are independently hydrogen, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkyl formyl, substituted or unsubstituted C6-C20 aryl formyl, substituted or unsubstituted C2-C20 heterocyclic formyl, 2021346019   25 Aug 2026 substituted or unsubstituted C1-C20 alkyl sulfonyl, substituted or unsubstituted C6-C20 aryl sulfonyl, or substituted or unsubstituted C2-C20 heterocyclic sulfonyl group; or Rc, Rd and the N atom are linked each other to form a ring; E1 is hydrogen, halogen, nitro, nitrile, C1-C20 alkyl, C1-C20 alkoxy, C1-C20 alkylthio, C1-C20 alkasilyl, C1-C20 alkasiloxy, C2-C20 heterocyclic, substituted or unsubstituted amino, aminoacyl, carbonyl linked to C1-C20 alkylamino, C6-C20 aryl, C6-C20 aryloxy, sulfinyl, sulfone group, aldehyde group, carbonyl group linked to a C1-C20 alkyl group, carbonyl group linked to a substituted or unsubstituted C6-C20 aryl group, carbonyl group linked to a substituted or unsubstituted C2-C20 heterocyclic group, carbonyl group linked to a C1-C20 alkoxy group, carbonyl group linked to a C6-C20 aryloxy group, carbonyl group linked to a C2-C20 heterocyclicoxy group, urea group, substituted or unsubstituted C1-C20 alkyl urea group , substituted or unsubstituted C6-C20 aryl ureido group, substituted or unsubstituted C2-C20 heterocyclic ureido group; E2 is hydrogen, halogen, C1-C20 alkyl, C1-C20 alkoxy, C1-C20 alkylthio, C1-C20 alkyl silyl, C1-C20 alkyl siloxy, aminoacyl, carbonyl linked to C1-C20 alkylamino, carbonyl linked to C6-C20 arylamino, carbonyl linked to C2-C20 heterocyclic amino, C6-C20 aryl, C6-C20 aryl oxy, C2-C20 heterocyclic aryl, aldehyde, a carbonyl group linked to a C1-C20alkyl group, a carbonyl group linked to a C6-C20 aryl group, a carbonyl group linked to a C2-C20 heterocyclic group, a carbonyl group linked to a C1-C20 alkoxy group, a carbonyl group linked to a C6-C20 aryloxy group, a carbonyl group linked to a C2-C20 heterocyclic oxy group or a group as shown in RcRdN- group; wherein Rc and Rd are independently hydrogen, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkyl formyl, substituted or unsubstituted C6-C20 aryl formyl, substituted or unsubstituted C2-C20 heterocyclic formyl, substituted or unsubstituted C1-C20 alkyl sulfonyl, substituted or unsubstituted C6-C20 aryl sulfonyl, or substituted or unsubstituted C2-C20 heterocyclic sulfonyl group; or Rc, Rd and the N atom are linked each other to form a ring; E3 is hydrogen, halogen, 2021346019   25 Aug 2026 C1-C20 alkyl, C1-C20 alkoxy, C1-C20 alkylthio, C1-C20 alkyl siloxy, C6-C20 aryloxy, C6-C20 aryl, C2-C20 heterocyclic aryl, a carbonyl group linked to a C1-C20 alkoxy, a carbonyl group linked to a substituted or unsubstituted C6-C20 aryloxy, a carbonyl group linked to a substituted or unsubstituted C6-C20 heterocyclic aryloxy or a group as shown in RcRdN- group; wherein, Rc and Rd are independently hydrogen, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkyl formyl, substituted or unsubstituted C6-C20 aryl formyl, substituted or unsubstituted C2-C20 heterocyclic formyl, substituted or unsubstituted C1-C20 alkyl sulfonyl, substituted or unsubstituted C6-C20 aryl sulfonyl, or substituted or unsubstituted C2-C20 heterocyclic sulfonyl group; or Rc, Rd and the N atom are linked each other to form a ring; E4, E5, E6 and E7 are independently hydrogen, halogen, nitro, nitrile, sulfinyl, sulfonyl, aldehyde, substituted or unsubstituted C1-C20 alkyl, substituted or unsubstituted C1-C20 alkoxy, C1-C20 alkylthio, C1-C20 alkasilyl, C1-C20 alkasiloxy, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted amino, amino acyl, carbonyl groups linked to substituted or unsubstituted C1-C20 alkylamino groups, carbonyl groups linked to substituted or unsubstituted C6-C20 arylamino groups, carbonyl groups linked to substituted or unsubstituted C2-C20 heterocyclic amino groups, carbonyl groups linked to substituted or unsubstituted C1-C20 alkyl groups, carbonyl groups linked to substituted or unsubstituted C6-C20 aryl groups, carbonyl groups linked to substituted or unsubstituted C2-C20 heterocyclic group, carbonyl group linked to substituted or unsubstituted C1-C20 alkoxy, carbonyl group linked to substituted or unsubstituted C6-C20 aryloxy, carbonyl group linked to substituted or unsubstituted C6-C20 heterocyclic oxy, ureido, substituted or unsubstituted C1-C20 alkyl ureido, substituted or unsubstituted C6-C20 aryl ureido, substituted or unsubstituted C2-C20 heterocyclic based ureido, substituted or unsubstituted C6-C20 aryl, substituted or unsubstituted C6-C20 aryloxy, or a group as shown in RcRdN- group; wherein, Rc and Rd are independently hydrogen, substituted or 2021346019   25 Aug 2026 unsubstituted C6-C20 aryl, substituted or unsubstituted C2-C20 heterocyclic, substituted or unsubstituted C1-C20 alkyl, formyl, substituted or unsubstituted C1-C20 alkyl formyl, substituted or unsubstituted C6-C20 aryl formyl, substituted or unsubstituted C2-C20 heterocyclic formyl, substituted or unsubstituted C1-C20 alkyl sulfonyl, substituted or unsubstituted C6-C20 aryl sulfonyl, substituted or unsubstituted C2-C20 heterocyclic sulfonyl group; or Rc, Rd and the N atom are linked each other to form a ring. In the present invention, the general formula I preferably comprises one or more of the following compounds: Mes-N^N-Mes 1 .> Cl / = Ru‘ 1 )^C'-N.__ H 4a Mes—N~N-Mes |    ci / = Ru' F_ / =<n / = F \C J / CJ / N^-x ^--- /   h^\ O^ 4d Mes-N~N-Mes 1 »Cl ^ / = Ru" ^N'OC^N । H %J\ O^ 4g pCy3               Mes—N  N-Mes 1    Cl                                    1 „,Cl Ru                        Ru K JVC--N'__ K >C'-N-__ H^\ O''                            Cl 4b                       4c pCy3                Mes-N  N-Mes | ,vCl                                             | ,vCl Ru‘           ^ / =Ru F'^'^^-Cl / N^F'~~^f:=>^C^N'- HXX o^ 4e                            4f Mes-N  N-Mes           Mes-N  N-Mes 1 .»Cl                                       l..>'Cl Ru          ^ / =Ru F^rtCiN^   F^CFiN>X H               H^S^ O'' 4h                          4j s’ Mes—N. ,N-Mes              Mes—N. ,N-Mes             Mes—N, ,N-Mes 2021346019   25 Aug 2026 4ae                          4af                      4ag 2021346019   25 Aug 2026 Mes-Nx N-Mes 4be F 4bh 4bf 4bj wherein the general formula I is preferably formula 4aa, 4ab, 4f or 4v, more preferably formula 4aa or 4v. In various embodiments, disclosed herein is a method for the preparation of a liquid hydrogenated nitrile butadiene rubber comprising the steps of: adding nitrile butadiene rubber (NBR) to a degradation reaction and a hydrogenation reaction in the presence of Zhan catalyst under the protection of an inert gas in an organic solvent, or adding NBR to a hydrogenation reaction in the presence of Zhan catalyst under the protection of an inert gas in an organic solvent, to obtain liquid hydrogenated nitrile butadiene rubber; wherein the Zhan catalyst is one or more of 4v and 4aa: 2021346019   25 Aug 2026 In the present invention, the NBR means a rubber obtained by copolymerisation of butadiene and acrylonitrile. In the present invention, the NBR may have an acrylonitrile content of 15% to 50%, preferably 17% to 45%, e.g. 25%, 33% or 43%. In the present invention, preferred, the NBR has a weight average molecular weight of from 3,000 to 60,000, at which point the NBR may be a LNBR, suitable for direct hydrogenation reaction of the NBR. In the present invention, preferred, the NBR has a Mooney viscosity of 30 to 60, in which case the NBR suitable for a degradation reaction and followed by the hydrogenation reaction. In the present invention, the NBR may have a molecular weight polydispersity index (PDI) is from 2.0 to 8.0. In the present invention, preferably, the NBR has a structure as shown in formula II, IIa or IIb as follows: h2c—ch=ch-ch24-4-ch2-chA- / J \ I / k CN II -4h2c—ch=ch-ch24—hch2-ch4- \                          / m \ z I / n CN Ila 2021346019   25 Aug 2026 4-H2C—CH=CH-CH2-W-CH2-CH-V, \                        / m'\ z I / n CN lib , wherein, the NBR of formula II refers to a solid NBR, wherein j = 100-6,000, for example, it can be 200-6,000, or 300-6,000, or 400-6,000, or 500-6,000, or 600-6,000, or 800-6,000, or 1,200-6,000, or 2,000-6, 000; k = 50-5,000, which can be, e.g., 300-5,000, or 500-5,000, or 800-5,000, or 1,000-5,000, or 2,000-5,000; The NBR of formula IIa represents liquid NBR prepared by an industrial process and is commercially available, which can be further hydrogenated to produce LHNBR, in fomula IIa, m = 30-600, e.g., it can be 30-500, or 30-400, or 30-300, or 30-200, or 30-100, or 50-80; n = 20-500, for example, it can be 20-450, or 20-400, or 30-300, or 40-200, or 50-100, or 60-80. The NBR of formula IIb represents LNBR obtained by degradation of the solid NBR of formula II, which can also be further hydrogenated to produce LHNBR, in fomula IIb, m' = 30-600, which can be, e.g., 30-500, or 30-400, or 30-300, or 30-200, or 30-100, or 50-80; n' = 20-500, which can be, e.g., 20-450, or 20- 400, or may be 30-300, or 40-200, or 50-100, or 60-80. According to one embodiment of the invention, j>m'; k>n'. In the present invention, the NBR IIa and NBR IIb may be LNBR, and NBR II may be the solid NBR. In the present invention, the amount of Zhan catalyst may be selected according to the conventional methods, preferably from 0.005% to 0.1%, more preferably from 0.01% to 0.05%, where the percentage of Zhan catalyst was used relative to the NBR. In the present invention, the temperature of degradation reactionpreferably from 60 to 100°C, more preferably 80°C. The time of degradation reaction may be selected according to 2021346019   25 Aug 2026 the conventional methods, preferably from 0.5 to 10h, more preferably from 1.0 to 6.0 hours, more preferably from 2.0 to 3.0hours. In the present invention, the amount of hydrogen in the hydrogenation reaction may be a conventional amount for such reactions, preferably the pressure of the hydrogenation reaction system reaches 2 to 15 MPa, better 6 to 10 MPa, e.g., 8 MPa. In the present invention, the temperature of the hydrogenation reaction may be a conventional temperature for such reactions, preferably from 80 to 200°C, more preferably from 100 to 180°C, further more preferably from 130 to 160°C, e.g., 150°C. The time of the hydrogenation reaction may be selected according to the conventional methods and is from 2 to 6 hours. In the present invention, the organic solvent may be some solvents commonly used for such reactions, e.g. one or more of the trichloromethane, dichloroethane, acetone and / or chlorobenzene; preferably one or more of chlorobenzene, dichloroethane and trichloromethane; better chlorobenzene or dichloroethane; preferably chlorobenzene. The amount of the organic solvents can be selected according to the conventional methods in the field, preferably from 100 to 300 g of NBR / 1L of organic solvent, e.g., 120 g, 160 g, 200 g or 240 g of NBR / 1L of organic solvent. In the present invention, the inert gas may be an inert gas commonly used for such reactions, e.g., argon (Ar) or nitrogen. In the present invention, the hydrogenation reaction is preferably followed by a post-treatment. The post-treatment may be carried out by conventional methods, generally by removing the organic solvent under negative pressure. The temperature of the post-treatment is from 100 to 150°C, preferably from 130 to 140°C. In a preferable embodiment of the present invention, the reaction process for the preparation of the LHNBR is as shown in route-1, wherein under the protection of an inert gas, 2021346019   25 Aug 2026 in an organic solvent, hydrogen is passed, and Zhan catalyst is added simultaneously with or after the passage of hydrogen to subject NBR IIa to a hydrogenation reaction to obtainLHNBR IIIa; wherein m, n, p and q are defined as previously described. -(• H2C—CH=CH-CH2^j-^CH2-CH-^ CN IIa Hydrogenation Reaction H2 v Formula I Catalyst H2C-CH=CH-CH2^(cH2-CH-)^-(-H2C-CH2-CH2-CH2^j-CN IIIa Route-1 In another preferable embodiment of the present invention, the reaction process for the preparation of the LHNBR is as shown in route-2, wherein under the protection of an inert gas, in an organic solvent, Zhan catalyst is added to subject NBR II to a degradation reaction to obtain NBR IIb; then hydrogen is passed to subject NBR IIb to a hydrogenation reaction to obtain LHNBR IIIb; wherein j, k, m', n', p' and q' are defined as previously described. 4 H2C- CH=CH-CH2 II M CH2"CHh CN Degradation Formula I Reaction    v Catalyst 4 H2C-CH=CH-CH2^(CH2-CH^, CN IIb Hydrogenation Reaction H2 Formula I Catalyst H2C- CH=ch- CH2)y( CH2- Ch}^ H2C- CH2“ CH2- CH2)-^ CN IIIb 2021346019   25 Aug 2026 Route-2 The Third Aspect: A LHNBR, which is prepared according to the preparation method of the LHNBR. The Fourth Aspect: A method for the degradation of NBR comprising the steps of NBR by a degradation reaction in an organic solvent under the protection of an inert gas and in the presence of Zhan catalyst as shown in the general formula I. Wherein, The type and amount of Zhan catalyst are as previously described. The NBR is as previously described. The temperature and time of the degradation reaction are as previously described. The type and amount of organic solvents are as previously described. The inert gases are as previously described. In a preferable embodiment of the present invention, the reaction process for the degradation method of the NBR was as shown in route-3, wherein the degradation reaction of NBR II to NBR IIb was carried out by adding Zhan catalyst in an organic solvent under inert gas protection; wherein j, k, m' and n' were defined as previously described. 2021346019   25 Aug 2026 H2C-CH=CH-CH2)- II ch2-ch-)- 2   ।     / k CN Degradation Formula I Reaction v Catalyst h2c—ch=ch-ch2)—t(-ch2-ch4-, 2                   2 / m               n' CN II b Route-3 In various embodiments, disclosed herein is a method for the degradation reaction of nitrile butadiene rubber (NBR) comprising the steps of: adding the NBR to a degradation reaction in an organic solvent under the protection of an inert gas in the presence of Zhan catalyst 4v or 4aa to obtain a NBR degradation product; ; Wherein, the amount of Zhan catalyst is as previously described; the NBR is as previously described; the temperature and time of degradation reaction are as previously described; the organic solvent and the amount thereof are as previously described; the inert gas is as previously described; and the reaction process for the degradation method of NBR is shown in Route-3, wherein j=100-6000; k=50-5000; m’=30-600; n’=20-500; 2021346019   25 Aug 2026 Route-3. The Fifth Aspect: A rubber compound comprising the LHNBR, a filler and a vulcanizing agent. In the present invention, the filler may be conventional, and preferably carbon black and / or silica. The carbon black is preferably carbon black N220, carbon black N-330, carbon black N550 or carbon black N774. The silica is preferred, such as precipitated silica, fumed silica or alkaline silica. The precipitated silica is precipitated water & silica. The fumed silica refers to fumed silica. The basic silica is preferably basic silica AS-70, the basic silica AS-70 being a mixture of sodium aluminium silicate and silica, wherein the mass fraction of silica is 0.8%. In the present invention, the vulcanizing agent may be conventional, preferably 1,4-bis(tert-butylperoxyisopropyl)benzene (trade name F-40). In the present invention, the rubber compound may further comprise other rubber compounding agents customary in addition to the vulcanizing agent, such as one or more of co-sulfurizing agents, stearic acid, magnesium oxide, accelerators and antioxidants, wherein, the co-sulfurizing agent is preferably N,N’-m-phenylenebismaleimide (trade name PDM). The accelerator is preferably 2-mercaptobenzimidazole zinc salt (MBZ). 2021346019   25 Aug 2026 The antioxidant is preferably 4,4'-bis(dimethylbenzyl)diphenylamine (antioxidant 445). In a preferable embodiment of the present invention, the rubber compound comprises, in parts by weight, 100 parts of LHNBR, 50 parts of carbon black N-330, 10 parts of silica AS-70, 14 parts of 1,4-bis(tert-butylperoxyisopropyl)benzene (F-40),   0.5 parts of N,N’-m-phenylenebismaleimide (PDM), 0.5 parts of stearic acid, 6 parts of magnesium oxide, 0.5 parts of 2- Zinc salt of mercaptobenzimidazole (MBZ), and 1.0 part of 4,4'-bis(dimethylbenzyl)diphenylamine (antioxidant 445). In the present invention, the adhesive material can be prepared by means of methods customary, generally comprising the mixing of the components. The mixing may be carried out in a compacting machine using methods conventional. The mixing is preferably in stepwise. The Sixth Aspect: A vulcanized rubber, which is produced by vulcanizing the rubber materials. In the present invention, the vulcanisation may be carried out by conventional methods conventional. The vulcanisation preferably comprises: using an electric plate vulcaniser to vulcanize a section of the rubber at 180°C x 8 minutes; the product from the section of vulcanisation is then vulcanized in a second section at 150°C x 4 hours and then cooled to room temperature to obtain a vulcanized rubber. In the present invention, the vulcanized rubber may have a Shore hardness of 60 or more, preferably 80 or more. The elongation at break of the vulcanized rubber may be more than 160, preferably more than 190. 100% elongation strength of the vulcanized rubber may be 3 to 4 MPa. The Seventh Aspect: An application of the LHNBR, the adhesive or the vulcanized adhesive in industrial 2021346019   25 Aug 2026 products. Wherein, the industrial article preferably comprises a sealant, a binder, a coating, a potting material or an elastomeric article. The coating preferably an electromagnetic shielding coating, an oil resistant coating, a battery corrosion resistant coating or a damping and noise reduction coating. Preferred, the binder is a solid propellant binder or an ablative material binder. The elastomeric products are in particular shaped and complex elastomeric products. DEFINITION OF TERMS: The acrylonitrile content (ACN%) refers to the weight percentage content of the acrylonitrile fragment in NBR or HNBR. Hydrogenation degree: the degree of hydrogenation of the olefin double bond in a polymer, expressed by the iodine method. The molecular weight polydispersity index (PDI): the ratio of the weight average molecular weight to the number average molecular weight in a polymer is known as the polydispersity index, i.e. the molecular weight polydispersity index (PDI). Mooney viscosity: all the Mooney viscosities described in this invention are Mooney viscosities [ML (1+4) 100°C], which is a measure of the average molecular weight and plasticity of rubbers. Glass transition temperature (Tg): that refers to the temperature at which the high elastic state is transformed into the glass state or the glass table is loaded into the high elastic state. The glass transition is an inherent property of amorphous polymer materials and is a macroscopic manifestation of the transformation of polymer motion, it directly affects the use of material performance and process performance, the glass transition temperature (Tg) is located between the extrapolated glass transition start temperature (Tig) and extrapolated glass transition end temperature (Teg). 2021346019   25 Aug 2026 On the basis of common knowledge, each of the above preferable conditions can be combined in any way to obtain a preferable example of the invention. All of the reagents and raw materials used in the present invention are commercially available. The positive and progressive effects of the present invention are as follows: 1. The invention used "Zhan catalyst" to produce a low molecular weight (Mw 3,000~60,000) LHNBR with a broader molecular weight polydispersity (PDI=2.0~8.0) through a unique catalytic degradation reaction and followed by the hydrogenation reaction technique. It has excellent flowability during processing and excellent physical properties after vulcanisation, and has unique applications in the field of special rubbers. 2. The method provided by the preparation technology in the present invention simplifies the preparation process method of the prior art, used Zhan catalysts with the same metal (Ru) system, enabled degradation and hydrogenation to be completed in one process, effectively and easily prepared LHNBR for various applications, broadened the application field of LHNBR, and had obvious technical advantages. DETAILED DESCRIPTION OF THE INVENTION The invention is further illustrated below by some embodiments, but the invention is not thereby limited to the following described embodiments. Experimental methods for which no specific conditions are indicated in the following embodiments follow the conventional methods and conditions, or are selected according to the trade description. Zhan catalysts used in the following embodiment were the compounds 4aa and / or 4v of general formula I, as documented in our granted patent CN200910175790.6, with the following structures: 2021346019   25 Aug 2026 The raw material NBR and LHNBR product raw rubber, and the relevant characteristic parameters of the rubber material involved in the following embodiments, are expressed by testing according to the following methods: (1) Acrylonitrile content: Tested in accordance with the method specified in the standard SH / T 1157.2-2015 "Determination of bound acrylonitrile content in raw rubber acrylonitrile-butadiene rubber (NBR) Part 2: Kjeldahl method for nitrogen determination", with NMR hydrogen spectrometry analysis evaluation as an auxiliary verification method. (2) Hydrogenation degree: tested according to the method specified in the standard SH / T 1763 "Determination of residual unsaturation in hydrogenated nitrile butadiene rubber (HNBR) of nitrile rubber (NBR) by the iodine titration method". (3) Glass transition temperature (Tg): tested by DSC8500 differential scanning calorimeter in accordance with the method specified in the standard GB / T 29611-2013 "Determination of glass transition temperature of raw rubber by differential scanning calorimetry (DSC)". (4) Molecular weight and molecular weight polydispersity index (PDI): tested by ECS000113 type room temperature gel permeation chromatograph (Z-1601) in accordance with the method specified in the standard GB / T21863-2008 "Gel Gel permeation chromatography (GPC) with tetrahydrofuran as eluent". Example 1 Under nitrogen displacement conditions, 100 g of NBR [ACN 33%, ML(1+4) 35, 100°C] 2021346019   25 Aug 2026 was added into 500 mL of anhydrous chlorobenzene to a 1L stainless steel reactor, completely dissolved at 60°C under nitrogen seal conditions, then added "Zhan catalyst" (4v) at a dosage of 0.03% of NBR, the degradation reaction of NBR was carried out at 80°C for 1.5 hours to obtain a LNBR degradate; hydrogen was then introduced until the pressure reached 8 MPa and the temperature was increased to 150°C. The reaction was carried out for 4 hours to obtain a LHNBR solution. The solution of the hydrogenation reaction product was removed from the chlorobenzene solvent at 130°C under negative pressure to obtain a LHNBR raw rubber with a product yield of >98%. The characteristic parameters of the resulting raw LHNBR were: molecular weight (Mw) of 37,950, molecular weight polydispersity index of 2.1, ACN of 33%, Hydrogenation degree of 92% (iodine value: 24), and glass transition temperature (Tg) of -31.2°C (Tig: -31.7°C; Teg: -26.9°C). Example 2 Under nitrogen displacement conditions, 100g of NBR [ACN 33%, ML(1+4) 35 at 100°C] was added into 500mL of anhydrous chlorobenzene to a 1L stainless steel reactor, after completed dissolution at 60°C under nitrogen sealing, then added "Zhan catalyst" (4v) at a dosage of 0.04% of the NBR, degradation of the NBR at 80°C for 1 hour to obtain LNBR, hydrogen was then introduced until the pressure reached 8 MPa and the temperature was increased to 150°C. The reaction was carried out for 5 hours to obtain a LHNBR solution. The solution of the hydrogenation reaction product was removed from the chlorobenzene solvent at 130°C under negative pressure to obtain a raw LHNBR with a product yield of >98%. The characteristic parameters of the resulting raw LHNBR were: molecular weight (Mw) of 44960, molecular weight polydispersity index: 2.2, ACN: 33%, Hydrogenation degree: 96% (iodine value: 14), and glass transition temperature (Tg): -32.5°C (Tig: -36.1°C; Teg: -28.8°C). 2021346019   25 Aug 2026 Sample 3 Under nitrogen displacement conditions, 100 g of NBR [ACN of 33%, ML(1+4) 35 at 100°C] was added 500 mL of anhydrous chlorobenzene to a 1L stainless steel reactor, dissolved completely at 60°C under nitrogen seal, then added Zhan catalyst (4v) at a dosage of 0.05% of NBR; the degradation reaction of the NBR was carried out at 80°C and the reaction was carried out for 1 hour to obtain LNBR; hydrogen was then introduced until the pressure reached 8 MPa and the temperature was increased to 150°C. The reaction was carried out for 6 hours to obtain a highly hydrogenated LHNBR solution. The solution of the hydrogenation reaction product is removed from the chlorobenzene solvent at 130°C under negative pressure to obtain a raw LHNBR with a product yield of >98%. The properties of the resulting raw LHNBR were: molecular weight (Mw) of 45140, molecular weight polydispersity index: 2.2, combined ACN: 33%, hydrogenation degree: 99% (iodine value: 8), and glass transition temperature (Tg): -29.8°C (Tig: -33.5°C; Teg: -26.2°C). Sample 4 Under nitrogen displacement conditions, 100 g of NBR [ACN 33%, ML(1+4) 35 at 100°C] was added 500 mL of anhydrous chlorobenzene to a 1 L stainless steel reactor, after completed dissolution at 60°C under nitrogen sealing conditions, then added Zhan catalyst (4v) at a dosage 0.06% of the NBR. The NBR was subjected to a degradation reaction at 80°C for 2 hours to obtain LNBR; hydrogen is then introduced to a pressure of 8 MPa and the reaction was carried out at 150°C for 6 hours to obtain a highly hydrogenated LHNBR solution. The solution of the hydrogenation product was removed from the chlorobenzene solvent at 130°C under negative pressure, resulting in a raw LHNBR with a yield of >98%. The characteristic parameters of the resulting raw LHNBR were: molecular weight (Mw) 2021346019   25 Aug 2026 of 243.5 million, molecular weight polydispersity index: 2.4, ACN: 33%, hydrogenation: 99% (iodine value: 8), and glass transition temperature (Tg): -30.9°C (Tig: -31.5°C; Teg: -27.2°C). Sample 5 Under nitrogen displacement conditions, 100 g of nitrile rubber [33% acrylonitrile by weight, Moonny viscosity ML(1+4) 35 at 100°C] was added 500 mL of anhydrous chlorobenzene to a 1L stainless steel reactor, completely dissolved at 60°C under nitrogen seal conditions, then added Zhan catalyst (4v) at a dosage of 0.06% of the NBR, NBR was subjected to a degradation reaction at 80°C for 2.5 hours to obtain LNBR; hydrogen was then introduced until the pressure reached 8 MPa and the temperature was increased to 150°C. The reaction was carried out for 6 hours to obtain a highly hydrogenated LHNBR solution. The solution of the hydrogenation reaction product was removed from the chlorobenzene solvent at 130°C under negative pressure to obtain a raw LHNBR with a product yield of >98%. The characteristic parameters of the resulting raw LHNBR were: molecular weight (Mw): 8210, molecular weight polydispersity index: 2.7, ACN: 33%, hydrogenation: 99% (iodine value: 8) and glass transition temperature (Tg): -42.8°C (Tig: -49.8°C; Teg: -36.2°C). Sample 6 Under nitrogen displacement, 100 g of liquid nitrile rubber [33% acrylonitrile by weight, molecular weight (Mw) 15780, molecular weight polydispersity index 3.2] and 500 mL of anhydrous chlorobenzene were added to a 1 L stainless steel reactor, under nitrogen seal, added Zhan catalyst (4aa) at 60°C at a dosage 0.03% of NBR, hydrogen was then introduced until the pressure reached 8 MPa and then the temperature was increased to 150°C. The reaction was carried out for 4 hours to obtain a highly hydrogenated LHNBR solution. The solution of the hydrogenation reaction product was removed from the chlorobenzene solvent at 130°C under 2021346019   25 Aug 2026 negative pressure to obtain a raw LHNBR with a product yield of >98%. The characteristic parameters of the resulting LHNBR raw rubber were: molecular weight (Mw) of 16250, molecular weight polydispersity index: 3.3, ACN: 33%, hydrogenation: 99% (iodine value: 7) and glass transition temperature (Tg): -38.8°C (Tig: -44.5°C; Teg: -33.9°C). Sample 7 Under nitrogen displacement conditions, 100 g of LNBR [ACN 43%, molecular weight (Mw) 32660, molecular weight polydispersity index 4.3] and 500 mL of anhydrous chlorobenzene were added to a 1 L stainless steel reactor, under nitrogen sealing conditions, added Zhan catalyst (4aa) at 60°C at a dosage of 0.02% of NBR, then hydrogen was introduced until the pressure reached 8 MPa and the temperature was increased to 150°C. The reaction was carried out for 3 hours to obtain a highly hydrogenated LHNBR solution. The solution of the hydrogenation reaction product was removed from the chlorobenzene solvent at 130°C under negative pressure to obtain a raw LHNBR with a product yield of >98%. The characteristic parameters of the resulting raw LHNBR were: molecular weight (Mw) of 33420, molecular weight polydispersity index: 4.3, ACN: 43%, hydrogenation: 91% (iodine value: 25) and glass transition temperature (Tg): -30.2°C (Tig: -34.7°C; Teg: -26.9°C). Sample 8 Under nitrogen displacement conditions, 100 g of LNBR [25% acrylonitrile by weight, molecular weight (Mw) 32770, molecular weight polydispersity index 5.5] and 500 mL of anhydrous chlorobenzene were added to a 1 L stainless steel reactor, under nitrogen sealing conditions, add Zhan catalyst (4aa) at 60°C at a dosage of 0.03% of theNBR, then hydrogen was introduced until the pressure reached 8 MPa and then the temperature was increased to 150°C. The reaction was carried out for 4 hours to obtain a highly hydrogenated LHNBR 2021346019   25 Aug 2026 solution. The solution of the hydrogenation reaction product was removed from the chlorobenzene solvent at 130°C under negative pressure to obtain a raw LHNBR with a product yield of >98%. The characteristics of the resulting raw LHNBR are: molecular weight (Mw) of 33,950, molecular weight polydispersity index: 5.6, ACN: 25%, hydrogenation degree: 95% (iodine value: 13) and glass transition temperature (Tg): -32.9°C (Tig: -36.6°C; Teg: -29.4°C). Sample 9 1. Preparation of vulcanized rubber In parts by weight, the rubber material comprised: 100 parts of LHNBR (raw rubber obtained from Example 3), 14 parts of F-40, 0.5 parts of PDM, 0.5 parts of stearic acid, 6 parts of magnesium oxide, 50 parts of carbon black N-330, 10 parts of silica AS-70, 0.5 parts of MBZ and 1.0 parts of antioxidant 445. Preparation of rubber and vulcanized rubber according to the following process steps: (1) Mixing: first, the components of the the rubber material were put into the kneader machine and mixed at 30-60°C for 8-10min and then forced to discharge the rubber; then, a section of the rubber material obtained from mixing is thinly passed or ground 3-5 times on an open refiner or a three-roller mill, discharged and parked for 12 hours to obtain the required rubber material. (2) Vulcanisation: using an electric plate vulcaniser, a section of the above rubber was vulcanized at 180°C x 8 minutes; then a section of the vulcanized specimen is vulcanized at 150°C x 4 hours and then cooled to room temperature to obtain a vulcanized rubber. 2. Vulcanized rubber performance test Test Shore A hardness according to GB / T 531.1-2008 with GSD-719K type rubber hardness tester; test standard according to GB / T 528-2009, GB / T 529-2008 and GB / T 2021346019   25 Aug 2026 532-2008 respectively, in AI-7000-LU type. The tensile and fracture properties were tested on an electronic tensile tester. The performance test results are shown in Table 1. Table 1 Vulcanized rubber properties Shore hardness 82 Breaking strength, MPa 7.6 Elongation at break, % 199 100% set tensile strength, MPa 3.1 Sample 10 The raw LHNBR obtained from Example 4 was used, and other preparation steps and conditions were the same as in Example 9 to produce the vulcanized rubber, the performance test results of which are shown in Table 2. Table 2 Vulcanized rubber properties Shore hardness 67 Breaking strength, MPa 4.8 Elongation at break, % 163 100% set tensile strength, MPa 3.5

Claims

1. A method for the preparation of a liquid hydrogenated nitrile butadiene rubber comprising the steps of: adding nitrile butadiene rubber (NBR) to a degradation reaction and a hydrogenation reaction in the presence of Zhan catalyst under the protection of an inert gas in an organic solvent, or adding NBR to a hydrogenation reaction in the presence of Zhan catalyst under the protection of an inert gas in an organic solvent, to obtain liquid hydrogenated nitrile butadiene rubber; wherein the Zhan catalyst is one or more of 4v and 4aa:

2. The method for the preparation of liquid hydrogenated nitrile butadiene rubber according to Claim 1,wherein the NBR has an acrylonitrile content of 15% to 50%;the NBR has a weight average molecular weight of 3,000-60,000;the NBR has a meniscus viscosity of 30-60;the NBR has a molecular weight polydispersity index of 2.0-8.0;the NBR has a structure as shown in formula II, IIa or IIb as follows:-^h2c-ch=ch-ch2M-ch2-ch-V'J \           | / kCN2021346019   25 Aug 20264-h2c—ch=ch-ch2-W-ch2-ch-V\                          / m \ z I / nCNIla,-4h2c—ch=ch-ch24-4-ch2-ch-V,\                         / m \ z । / nCNlib,wherein,j=100-6000; k=50-5000;m=30-600; n=20-500;m’=30-600; n’=20-500;the amount of Zhan catalyst is 0.005%-0.1%, the percentage being the Zhan catalyst as a percentage by weight of the nitrile rubber;the degradation reaction at a temperature of 60-100°C, the degradation reaction at a time of 0.5-10hours;the amount of hydrogen in the hydrogenation reaction is such that the pressure of the reaction system reaches 2 to 15 MPa;the temperature of the hydrogenation reaction is 80 to 200°C; the time of the hydrogenation reaction is 2 to 6 hours;the organic solvent is one or more of trichloromethane, dichloroethane, acetone and chlorobenzene; the organic solvent is in an amount of 100 to 300 g of NBR / 1L of organic solvent;the inert gas is argon or nitrogen; andwhen the hydrogenation reaction is completed, a post-treatment is conducted; the post-treatment comprises removing the organic solvent under negative pressure; the post-treatment is at a temperature of 100 to 150°C.2021346019   25 Aug 20263. The method for the preparation of liquid hydrogenated nitrile butadiene rubber according to claim 1 or 2, wherein the reaction flow of the method of preparation of liquid hydrogenated nitrile butadiene rubber is as shown in route-1, in an organic solvent under the protection of an inert gas, with the passage of hydrogen, and the addition of the Zhan catalyst at the same time as or after the passage of hydrogen to the NBR IIa solution for the hydrogenation reaction to obtain liquid hydrogenated nitrile butadiene rubber IIIa.; wherein m=30-600; n=20-500; p = 1-150; q = 30-590;^h2c—ch=ch-ch2}^ch2-ch-)^CNIlaHydrogenation ,,              . , .Reaction H21 ZHAN catalyst ^H2C-CH=CH-CH2^CH2-CH-J-^H2C-CH2-CH2-CH2}— '                              CNIllaRoute-1or the reaction flow of the preparation method of liquid hydrogenated nitrile butadiene rubber was as shown in route-2, wherein the degradation reaction of NBR II was carried out to obtain NBR IIb by adding Zhan catalyst in an organic solvent under the protection of an inert gas; then hydrogen was passed to carry out the hydrogenation reaction of NBR IIb to obtain liquid hydrogenated nitrile butadiene rubber IIIb; wherein j=100-6000; k=50-5000; m’=30-600; n’ = 20-500; p’= 1-150; q’= 30-590;2021346019   25 Aug 2026Route-2.

4. A liquid hydrogenated nitrile butadiene rubber prepared by the method according to any one of claims 1-3.

5. The liquid hydrogenated nitrile butadiene rubber according to claim 4, wherein:the acrylonitrile content is from 15%-50%, wherein the acrylonitrile content is tested in accordance with the method specified in the standard SH / T 1157.2-2015 "Determination of bound acrylonitrile content in raw rubber acrylonitrile-butadiene rubber (NBR) Part 2: Kjeldahl method for nitrogen determination", with NMR hydrogen spectrometry analysis evaluation as an auxiliary verification method;the hydrogenation degree is from 75% to 99.5%, wherein the hydrogenation degree is the degree of hydrogenation of the olefin double bond in a polymer, expressed by the iodine method;the weight average molecular weight (Mw) is from 3,000 to 60,000;the molecular weight polydispersity index (PDI) is from 2.0 to 8.0;the glass transition temperature is below -28°C, wherein the glass transition temperature (Tg) is2021346019   25 Aug 2026tested by DSC8500 differential scanning calorimeter in accordance with the method specified in the standard GB / T 29611-2013 "Determination of glass transition temperature of raw rubber by differential scanning calorimetry (DSC)".

6. The liquid hydrogenated nitrile butadiene rubber according to claim 5, wherein,the liquid hydrogenated nitrile butadiene rubber has an acrylonitrile content of 17-45%;the liquid hydrogenated nitrile butadiene rubber has a hydrogenation degree of 80%-99%;the liquid hydrogenated nitrile butadiene rubber has the weight average molecular weight of 5,000-50,000;the liquid hydrogenated nitrile butadiene rubber has a molecular weight polydispersity index of 2.0-6.0;the liquid hydrogenated nitrile butadiene rubber having a glass transition temperature of lower than -35°C;the liquid hydrogenated nitrile butadiene rubber having an extrapolated glass transition onset temperature of lower than -30°C;the liquid hydrogenated nitrile butadiene rubber having an extrapolated glass transition end temperature of lower than -25°C;the liquid hydrogenated nitrile butadiene rubber is a liquid hydrogenated nitrile butadiene rubber shown in formula IIIa or IIIb;-^H2C-CH=CH-CH2-^CH2-CH-^-H2C-CH2-CH2-CH2^-CNIlla-^-H2C-CH=CH-CH2^r^CH2—CH-^-H2C-CH2-CH2-CH2^rCNIllb2021346019   25 Aug 2026wherein p = 1-150; p’= 1-150; q = 30-590; q’= 30-590; n = 20-500; n’ = 20-500.

7. A method for the degradation reaction of nitrile butadiene rubber (NBR) comprising thesteps of: adding the NBR to a degradation reaction in an organic solvent under the protection ofan inert gas in the presence of Zhan catalyst 4v or 4aa to obtain a NBR degradation product;the amount of Zhan catalyst is as described in Claim 2;the NBR is as described in Claim 2;the temperature and time of degradation reaction is as described in Claim 2;the organic solvent and the amount thereof is as described in Claim 2;the inert gas is as described in Claim 2; andthe reaction process for the degradation method of NBR is shown in Route-3, whereinj=100-6000; k=50-5000; m’=30-600; n’=20-500;Route-3.2021346019   25 Aug 20268. A rubber compound comprising the liquid hydrogenated nitrile butadiene rubber according to any one of claims 4 to 6, filler and vulcanizing agent;the filler is carbon black or silica; the carbon black is carbon black N220, carbon black N-330, carbon black N550 or carbon black N774; the silica is precipitated silica, fumed silica or alkaline silica; the alkaline silica is alkaline silica AS-70;the vulcanizing agent is 1,4-bis(tert-butylperoxyisopropyl)benzene;the rubber compound further comprising other rubber compounding agents than the vulcanizing agent, the other rubber compounding agents include one or more of a co-sulfurizing agent, stearic acid, magnesium oxide, accelerator and antioxidant; wherein the co-sulfurizing agent is N,N’-m-phenylenebismaleimide; the accelerator is zinc salt of 2-mercaptobenzimidazole; the antioxidant is 4,4'-bis(dimethylbenzyl)diphenylamine.

9. A vulcanized rubber, produced by vulcanizing the rubber compound of Claim 8.

10. The use of the liquid hydrogenated nitrile butadiene rubber according to any one of claims 4 to 6, the rubber compound according to Claim 8 or the vulcanized rubber according to Claim 9 in industrial products.

Citation Information

Patent Citations

  • Catalyst compositions and their use for hydrogenation of nitrile rubber

    EP2768866A1

  • Methods of modifying polymers with highly active and selective metathesis catalysts

    US20120252982A1