Method for producing thermoformed plastics parts from polyethylene terephthalate
Patent Information
- Authority / Receiving Office
- AU · AU
- Patent Type
- Applications
- Current Assignee / Owner
- THERMAPET TECH PTE LTD
- Filing Date
- 2023-03-08
- Publication Date
- 2026-07-30
AI Technical Summary
Current thermoforming processes for producing polyethylene terephthalate (PET) plastic parts require nucleating agents, making recycling difficult and limiting the production of transparent parts with sufficient heat resistance for microwave use.
A method involving stretching amorphous nucleating agent-free PET semi-finished products to a temperature of 90-180°C with a stretching degree of 1.2-5.0, followed by shaping and quenching, which induces strain-crystallization and enhances transparency and heat resistance without the need for nucleating agents.
The method produces transparent, heat-resistant PET parts suitable for microwave use with minimal energy expenditure and allows for recyclability, maintaining economical cycle times and reducing shrinkage and energy-intensive thermal treatments.
Smart Images
Figure 00000001_0000 
Figure 00000017_0000
Abstract
Description
[0001] Process for the production of thermoformed plastic parts from
[0002] Polyethylene terephthalate
[0003] Technical area
[0004] The invention relates to a process for producing thermoformed and completely pure recyclable plastic parts made of nucleating agent-free amorphous polyethylene terephthalate.
[0005] State of the art
[0006] To manufacture plastic parts such as plastic cups or plastic containers, manufacturing processes known as thermoforming are generally used. In the case of polyethylene terephthalate (PET), for example, a film or sheet-shaped plastic semi-finished product is first preheated to up to 90 °C, then fed via a conveyor system to a thermoforming device, where it is usually formed in two steps. In a first step, the PET semi-finished product is gradually heated to over 200 °C to create the conditions for heat-induced crystallization and thus ultimately achieve high temperature resistance of the containers. The semi-finished product is then formed in a thermoforming tool, after which in a second step the semi-finished product is quickly cooled in a cooled thermoforming tool.These measures enable PET to be crystallized to improve its mechanical properties, including temperature resistance of at least 120°C. However, to make such processes economical, nucleating agents, e.g. in the form of nucleating inorganic filler particles and / or polymer-based nucleating agents, must be added to the PET during the extrusion process of the corresponding semi-finished products in order to minimize the heat-induced crystallization time, which would otherwise be over 15 seconds, depending on the target product. However, the use of such additives makes recycling more difficult because pure recycling is not possible. A further disadvantage is that, due to crystallization, only opaque, but not transparent, plastic parts can be produced from PET.
[0007] In addition, thermoforming processes are known that also enable the production of transparent plastic parts using amorphous PET. However, the disadvantage is that plastic parts produced in this way are unsuitable for use in microwaves due to their low heat resistance up to a maximum of 60-70 °C and their undesirable tendency to shrink at temperatures above 62 °C.
[0008] Furthermore, there are processes for producing so-called biaxially oriented PET films. In this process, a PET film is first preheated to up to 90 °C and then biaxially stretched, i.e. in both the machine direction and the transverse direction, using a suitable stretching device. In this process, auxiliary materials are usually added to the PET to facilitate the heating of the stretching gap, which is usually carried out using an infrared heater. Stretching induces crystallization of the PET to specifically influence the property profile of the film. During a thermal post-treatment, the PET film is subsequently heated to up to 200 °C or higher. This relieves crystallization-related residual stresses in the film, which can reduce the tendency to shrink.However, due to the necessary thermal post-treatment and the associated high temperatures, a correspondingly high energy expenditure is required.
[0009] Description of the invention
[0010] There is therefore a need to create a process of the type described above which, despite economical cycle times and with relatively low energy consumption, enables the production of thermoformed, pure-grade recyclable plastic parts which, with sufficient, visually appealing transparency, are also suitable for use in microwaves or for applications requiring a temperature resistance of 120 - 145 °C.
[0011] The invention achieves the stated object in that, in a feeding step, a semi-finished product, in particular a film-shaped or plate-shaped semi-finished product with a predetermined semi-finished product width, is first fed in a machine direction running parallel to the longitudinal direction of the semi-finished product to a processing section of a thermoforming device comprising a thermoforming tool and is then heated there in at least one heating step to a stretching temperature of 90 - 180°C and is actively stretched in at least one stretching step depending on the set stretching temperature at a degree of stretching of 1.2 - 5.0 in the machine direction, after which, in a forming step, the semi-finished product stretched in the processing section is shaped with the aid of the cooled thermoforming tool and is quenched to a temperature of at least 30 °C below the glass transition temperature of the polyethylene terephthalate used.For this purpose, the hot-forming tool preferably has a tool temperature of 15-20 °C. A degree of stretching of 1.2-5.0 means that the semi-finished product is stretched during the processing section to 1.2-5 times its original reference length. Alternatively, the degree of stretching can also be specified as a percentage; for a reference length defined as 100%, the degree of stretching is accordingly 120-500%.
[0012] Ways to implement the invention
[0013] The invention is based on the finding that, in the case of amorphous, nucleating agent-free PET, the combination of at least one stretching step in the machine direction at a degree of stretching of 1.2-5.0, preferably 3.0-5.0, more preferably 3.5-4.5, particularly preferably 4.4, and at least one heating step to a stretching temperature of 90-180°C, preferably 90-160°C, more preferably 90-145°C, more preferably 120-145°C, more preferably 120-140°C, more preferably 125-135°C, and particularly preferably 130°C enables advantageous crystallization conditions with regard to a low tendency to shrink and sufficient transparency of the produced plastic part. The stretching temperature refers in particular to the core temperature of the semi-finished product.
[0014] It has surprisingly been found that the stretch-induced crystallization triggered by the at least one stretching step in the machine direction, in combination with the at least one heating step, results in a particularly fine-grained lamellar crystal structure, which can be fixed to a temperature of at least 30 °C below the glass transition temperature of the PET used by the cooling or quenching in the forming step immediately following the at least one stretching step. Depending on the thickness or strength of the semi-finished product orof the finished plastic parts, it can generally also be provided that after the at least one stretching step, a short but intensive heating of the stretched semi-finished product takes place in a post-heating step at a temperature of 120 - 200 °C, preferably 130 - 200 °C, more preferably 140 - 200 °C, particularly preferably 160 - 180 °C, in order to further improve the crystallization conditions for a temperature resistance of the plastic part of 120 - 145 °C. The higher the temperature selected in this regard, the shorter the residence time in the post-heating step. In particular, it can also be provided that the at least one stretching step is immediately followed by the post-heating step, which is immediately followed by the forming step.The post-heating step not only further improves the temperature resistance of the finished plastic part, but also enables better formability of the semi-finished product in the forming step.
[0015] In principle, additional active stretching of the semi-finished product in the processing section can also take place in a transverse direction running transversely to the machine direction or along the semi-finished product width. However, active stretching preferably takes place exclusively in the machine direction, while the semi-finished product is fixed in terms of the semi-finished product width in the processing section. Because the semi-finished product remains fixed in terms of its semi-finished product width, a normally occurring shrinkage of the semi-finished product, i.e. a reduction in the semi-finished product width due to longitudinal stretching in the machine direction, is prevented during active stretching in the machine direction. Thus, in addition to the active stretching in the machine direction, slight passive stretching in the transverse direction is forced, which together with the active stretching in the machine direction promotes the formation of the fine-grained lamellar crystal structures.Preferably, it can be provided that in at least one stretching step, the semi-finished product is secured in the processing section at the semi-finished product edges opposite one another in the transverse direction. Active stretching, in the sense of the invention, means that stretching forces, in particular tensile forces, are introduced into the semi-finished product by the active movement of at least one holding element of a stretching device that can be fastened to the semi-finished product such that the semi-finished product is stretched parallel to the direction of movement of the holding element. In contrast, passive stretching in the transverse direction occurs as an inevitable side effect of active stretching in the machine direction when the semi-finished product is secured with respect to its semi-finished product width.
[0016] In principle, the semi-finished product can initially be overstretched in the machine direction during the processing step. After the molecular orientation phase, the semi-finished product is then slightly shrunk again in a shrinking step before the final forming step. This can further increase the advantageous crystallization effects because this measure aligns the crystalline chains of the PET material in even more ordered structures, which are therefore even more advantageous for the material properties of the product. The overstretching should preferably be carried out in such a way that the subsequent shrinkage of the semi-finished product in the machine direction before the forming step in the shrinking step is at most 20%, preferably 1 to 20%, more preferably 5 to 15%, even more preferably 7 to 13%, particularly preferably 10 to 12%.Preferably, the at least one stretching step is immediately followed by the shrinking step, which is immediately followed by the forming step.
[0017] The shrinkage to be selected depends in particular on the stretching ratio(s) and the stretching rate(s) used to stretch the sheet-shaped semi-finished product in the at least one stretching step and / or the thickness or strength of the sheet-shaped semi-finished product after the at least one stretching step. If the thickness of the sheet-shaped semi-finished product after hiding is, for example, 1.2 mm, shrinkage of preferably 10% occurs in the shrinking step. If the thickness of the sheet-shaped semi-finished product after hiding is, for example, 1.5 mm, shrinkage of preferably 12% occurs in the shrinking step.
[0018] The shrinking step can generally be carried out at a temperature of 120–200°C, or within the preferred temperature ranges specified above for the post-heating step. In particular, the shrinking step can be carried out at a temperature of 120–160°C, and even more preferably at a temperature of 130–140°C.
[0019] As described above, the active stretching of the semi-finished product in the machine direction can generally be carried out using a separate stretching device which introduces the relevant stretching forces, for example, via the end face of the semi-finished product, i.e. via the semi-finished product front defined by the semi-finished product edges opposite each other in the transverse direction. Particularly favorable process conditions arise, however, if the semi-finished product edges are fixed and positively guided in the processing section on fastening clips, and stretching forces for active stretching in the machine direction are introduced into the semi-finished product via the fastening clips. As a result of these measures, both the fixing of the semi-finished product with regard to its semi-finished product width and the introduction of the stretching forces for active stretching in the machine direction take place exclusively via fastening clips which are assigned to the semi-finished product edges opposite each other in the transverse direction.For example, the fastening clamps can be guided and moved via a known chain-based transport system. The transport system can be designed such that the fastening clamps are positioned against the semi-finished product edges at the beginning of the processing section and hold them in place. After stretching, the fastening clamps release the semi-finished product edges at the end of the processing section and are removed via the transport system. It goes without saying that, as an alternative to the fastening clamps, other suitable detachable holding elements can also be used. These can be positioned against the semi-finished product edges using a transport system and can hold and release them again.
[0020] The plastic parts produced by the process according to the invention can exhibit a shrinkage of no more than 0.5% at a service temperature of 120°C. Consequently, the measures according to the invention eliminate the need for energy-intensive thermal post-treatment after the stretching step to reduce any residual stresses caused by crystallization. Depending on the process conditions, plastic parts produced according to the invention can exhibit a haze value according to ASTM D 1003 of no more than 1%. Overall, the process according to the invention enables the production of plastic parts that are both sufficiently temperature-resistant for microwave use, in particular heat-resistant, and also have a visually appealing appearance due to their sufficient transparency.It has also been shown that the stretch-induced crystallization rate according to the invention proceeds at a sufficient speed despite the lack of nucleating agents in the PET, so that the cycle times customary for known thermoforming processes can essentially be maintained. Due to the fact that no nucleating agents or auxiliary materials are added to the PET used to improve heating efficiency, the plastic parts obtained by the process according to the invention can be recycled essentially in a single type. The process according to the invention can be tailored as required to the original semi-finished product thickness, which for the production of microwave-compatible plastic containers is, for example, 2.5-3.5 mm, with regard to the stretching temperature, degree of stretching, stretching rate, cooling rate, residence time in the thermoforming tool, etc., as well as, if necessary,The temperature and residence time during the post-heating step and the temperature, residence time, and shrinkage during the shrinking step can be adjusted accordingly. Likewise, the number and temporal sequence or order of the respective heating and stretching steps can be adjusted as required. For example, the at least one heating step can take place simultaneously with the at least one stretching step. However, particularly favorable conditions generally arise when the at least one heating step precedes the at least one stretching step, i.e., the heating step takes place first, followed by the stretching step.
[0021] In order to reduce the cycle time, the feeding step and at least one stretching step can in principle also take place simultaneously.
[0022] For favorable crystallization conditions, depending on the original semi-finished product thickness, the active stretching of the semi-finished product in the machine direction can be carried out in at least one stretching step at a stretching rate of 50–400% per second, preferably 90–350% per second, and more preferably 200–350% per second. In principle, an increase in the stretching temperature should also result in an increase in the stretching rate, and vice versa.
[0023] The stretching rate should generally be set as fast as the material allows, depending on the material thickness, etc. The faster the molecular orientation of the PET material occurs as a result of stretching, the higher the subsequent heat energy requirement to induce a shrinkage process in the finished, molded product. Accordingly, higher stretching rates can increase the temperature resistance of the final product. To carry out a method according to the invention, known plastic thermoforming devices can be used, which, for example, include not only a thermoforming tool but also a corresponding feed or transport system for the semi-finished product and, if appropriate, a punching device for punching out the molded plastic parts.
[0024] The drawing shows the subject matter of the invention, for example, in a schematic plan view of a semi-finished product stretched in a processing section of a hot-forming device.
[0025] A process according to the invention is used, for example, to produce thermoformed containers made of nucleating agent-free, amorphous PET. Such containers have a haze value according to ASTM D 1003 of no more than 1% and a shrinkage at a service temperature of 120°C of no more than 0.5%. Accordingly, the containers exhibit visually appealing transparency and are also suitable for use in microwaves. Because no nucleating agents or additives are added to the PET used to improve heating efficiency, the cups obtained by the process according to the invention can be recycled essentially in a single-material manner at the end of their service life.
[0026] The drawing shows a schematic representation of a semi-finished product 1 in the form of a PET film. The semi-finished product 1 can in principle be supplied as a continuous roll or continuous film strip. The dashed reference lines 2 on the semi-finished product 1, which run in a transverse direction TD with respect to the width of the semi-finished product, are intended to illustrate that the semi-finished product 1 is stretched in a processing section 3 of a thermoforming device (not shown in detail) in a machine direction MD running parallel to the longitudinal direction of the semi-finished product. The processing gate 3 is indicated by two dashed-dotted lines, which also run in the transverse direction TD. In the present exemplary embodiment, the semi-finished product 1 is stretched in the machine direction MD with respect to a reference length 4 defined between two reference lines 2 in the processing section 3 at a degree of stretching of 4.4 or 440%, as can be seen from the greater distance between the reference lines 2 in the processing section 3.
[0027] The semi-finished product 1 is held in processing section 3 by schematically indicated fastening clips 5 at the edges of the semi-finished product, so that the semi-finished product 1 is fixed in terms of its semi-finished product width. Stretching forces for active stretching in the machine direction MD are introduced into the semi-finished product 1 via the fastening clips 5, which can be moved in the machine direction MD in processing section 3, for example, using a chain drive. Exclusively active stretching in the machine direction MD would normally cause the PET film to shrink, i.e., a reduction in the width of the semi-finished product 1, as indicated by the dash-dotted line waisting of the semi-finished product 1 in processing section 3. However, by keeping the semi-finished product 1 fixed in terms of its semi-finished product width, such shrinkage is prevented. Consequently, in addition to the active stretching in the machine direction MD, slight passive stretching in the transverse direction TD is enforced.The fastening clamps are placed against the semi-finished product edges at the beginning of processing section 3 so that they are held by the fastening clamps 5. After stretching, the fastening clamps 5 release the semi-finished product edges again at the end of processing section 3. In principle, the number of fastening clamps 5 or releasable holding elements used can be freely selected depending on the desired process conditions and product properties. For example, depending on the application, it can also be advantageous for the process conditions if as many fastening clamps 5 or releasable holding elements as possible are provided in processing section 3, so that the set total degree of stretching is therefore resulting from several smaller partial stretchings in the machine direction MD.
[0028] Simultaneously with or prior to the stretching step, a heating step takes place, during which the semi-finished product 1 is heated to a stretching temperature of approximately 130 °C. Immediately after the stretching step, the semi-finished product 1 is formed in a forming step using a cooled thermoforming tool (not shown in detail) and quenched to a temperature at least 30 °C below the glass transition temperature of the PET used. For this purpose, the water-cooled thermoforming tool is heated to a tool temperature of 15 °C.
[0029] Alternatively, it can also be provided that the stretching step is immediately followed by a post-heating step, wherein the stretched semi-finished product 1 is briefly and intensively heated at a temperature of 120 - 200 °C. The post-heating step then follows immediately after the post-heating step. According to a further alternative, the stretching step can be followed by a shrinking step, wherein the semi-finished product 1 experiences a shrinkage of at most 20% in the machine direction MD. This can take place at a temperature of 120 - 200 °C. The forming step then follows immediately after the shrinking step. After the forming step, the formed semi-finished product 1 is transported further in the machine direction MD and fed to a punching device, where the finished plastic containers are punched out of the semi-finished product 1.
Claims
Patent claims 1. A method for producing hot-formed and completely recyclable plastic parts made of germ-forming-free, amorphous polyethylene terephthalate, characterized in that, in a feeding step, a semi-finished product (1), in particular film- or sheet-shaped, with a predetermined semi-finished product width, is first fed in a machine direction (MD) parallel to the longitudinal direction of the semi-finished product to a processing section (3) of a hot-forming device comprising a hot-forming tool and is subsequently heated there in at least one heating step to a drawing temperature of 90–180°C and actively drawn in at least one drawing step in the machine direction (MD) at a degree of drawing of 1.2–5.0, depending on the set drawing temperature, wherein the at least one heating step takes place simultaneously with or preceding the at least one drawing step.and in a forming step the semi-finished product (1) stretched in the processing section (3) is formed using the cooled hot forming tool and thereby quenched to a temperature of at least 30 °C below the glass transition temperature of the polyethylene terephthalate used.
2. Method according to claim 1, characterized in that the forming step immediately follows the at least one stretching step.
3. Method according to claim 1, characterized in that a shrinking step takes place between the at least one stretching step and the forming step, wherein the semi-finished product (1 ) undergoes a shrinkage of at most 20% in the machine direction (MD).
4. Method according to claim 3, characterized in that the shrinkage step takes place at a temperature of 120 - 200 °C.
5. Method according to one of claims 1 to 4, characterized in that the semi-finished product (1 ) is actively stretched exclusively in the machine direction (MD) in the processing section (3), while the semi-finished product (1 ) is fixed with respect to the semi-finished product width in the processing section (3).
6. Method according to claim 5, characterized in that in the stretching step the semi-finished product (1 ) is fixed in the processing section (3) at the semi-finished product edges opposite each other in a transverse direction (TD) running perpendicular to the machine direction (MD).
7. Method according to claim 5 or 6, characterized in that the semi-finished product edges in the processing section (3) are fixed and positively guided on releasable retaining elements, in particular fastening clamps (5), and that stretching forces for active stretching in the machine direction (MD) are introduced into the semi-finished product (1) via the retaining elements.
8. Method according to one of claims 1 to 7, characterized in that in the stretching step the active stretching of the semi-finished product (1 ) in the machine direction (MD) takes place at a stretching rate of 50 - 400 % per second, preferably of 90 - 350 % per second, more preferably of 200 - 350 % per second.
9. Plastic part, in particular a plastic container or plastic vessel, obtainable by a method according to any one of claims 1 to 5, wherein the shrinkage of the plastic part at a service temperature of 120 °C is at most 0.5%.
10. Plastic part according to claim 9, characterized in that the haze value according to ASTM D 1003 is at most 1%.