Chromatography Media For Removal Of Polyphenol Substances And Preparation Method Thereof

Abstract

The present disclosure relates to the technical field of organic polymer compounds, in particular to chromatography media for removal of polyphenol substances and a preparation method thereof. A method for preparing chromatography media for the removal of polyphenol substances includes: obtaining an aqueous phase by mixing a water-soluble inorganic salt, a dispersing agent and water; obtaining an oil phase by mixing N-vinyl pyrrolidone, a first crosslinking agent, a second crosslinking agent, a third crosslinking agent, an initiator and a pore-forming agent; and preparing the chromatography media for the removal of the polyphenol substances by adding the oil phase into the aqueous phase for suspension polymerization. The chromatography media of the present disclosure has an effective binding ability for the polyphenol substances in fermented beverages, and an adsorption rate of the polyphenol substances is in a range from 40% to 46%. After recovery, the chromatography media can be reused for adsorbing the polyphenol substances, a recycle loss rate is less than 1%, a recovery adsorption decrease rate is less than 2%, and cycling performance is good, thereby effectively reducing production costs and minimizing generation of solid waste. Moreover, the chromatography media prepared by the present disclosure has high mechanical properties. 20 24 27 06 43 03 D ec 2 02 4 A B S T R A C T 2 0 2 4 2 7 0 6 4 3 0 3 D e c 2 0 2 4 T h e p r e s e n t d i s c l o s u r e r e l a t e s t o t h e t e c h n i c a l f i e l d o f o r g a n i c p o l y m e r c o m p o u n d s , i n p a r t i c u l a r t o c h r o m a t o g r a p h y m e d i a f o r r e m o v a l o f p o l y p h e n o l s u b s t a n c e s a n d a p r e p a r a t i o n m e t h o d t h e r e o f . A m e t h o d f o r p r e p a r i n g c h r o m a t o g r a p h y m e d i a f o r t h e r e m o v a l o f p o l y p h e n o l s u b s t a n c e s i n c l u d e s : o b t a i n i n g a n a q u e o u s p h a s e b y m i x i n g a w a t e r - s o l u b l e i n o r g a n i c s a l t , a d i s p e r s i n g a g e n t a n d w a t e r ; o b t a i n i n g a n o i l p h a s e b y m i x i n g N - v i n y l p y r r o l i d o n e , a f i r s t c r o s s l i n k i n g a g e n t , a s e c o n d c r o s s l i n k i n g a g e n t , a t h i r d c r o s s l i n k i n g a g e n t , a n i n i t i a t o r a n d a p o r e - f o r m i n g a g e n t ; a n d p r e p a r i n g t h e c h r o m a t o g r a p h y m e d i a f o r t h e r e m o v a l o f t h e p o l y p h e n o l s u b s t a n c e s b y a d d i n g t h e o i l p h a s e i n t o t h e a q u e o u s p h a s e f o r s u s p e n s i o n p o l y m e r i z a t i o n . T h e c h r o m a t o g r a p h y m e d i a o f t h e p r e s e n t d i s c l o s u r e h a s a n e f f e c t i v e b i n d i n g a b i l i t y f o r t h e p o l y p h e n o l s u b s t a n c e s i n f e r m e n t e d b e v e r a g e s , a n d a n a d s o r p t i o n r a t e o f t h e p o l y p h e n o l s u b s t a n c e s i s i n a r a n g e f r o m 4 0 % t o 4 6 % . A f t e r r e c o v e r y , t h e c h r o m a t o g r a p h y m e d i a c a n b e r e u s e d f o r a d s o r b i n g t h e p o l y p h e n o l s u b s t a n c e s , a r e c y c l e l o s s r a t e i s l e s s t h a n 1 % , a r e c o v e r y a d s o r p t i o n d e c r e a s e r a t e i s l e s s t h a n 2 % , a n d c y c l i n g p e r f o r m a n c e i s g o o d , t h e r e b y e f f e c t i v e l y r e d u c i n g p r o d u c t i o n c o s t s a n d m i n i m i z i n g g e n e r a t i o n o f s o l i d w a s t e . M o r e o v e r , t h e c h r o m a t o g r a p h y m e d i a p r e p a r e d b y t h e p r e s e n t d i s c l o s u r e h a s h i g h m e c h a n i c a l p r o p e r t i e s . A B S T R A C T 2 0 2 4 2 7 0 6 4 3 0 3 D e c 2 0 2 4

Description

TECHNICAL FIELD The present disclosure relates to the technical field of organic polymer compounds, in particular to chromatography media for the removal of polyphenol substances and a preparation method thereof. BACKGROUND Due to precipitation and aggregation of polyphenol compounds in fermented beverages such as beer, precipitation substances that affect quality of the beverages may be produced during storage. At present, silica hydrogel (SHG) and / or cross-linked polyvinylpyrrolidone particles (PVPP) are mainly added into unstable fermented beverages to remove polyphenol substances. However, although the above method can achieve an effect of removing the polyphenol compounds, recovery is often difficult, mechanical properties are poor, and the fermented beverages cannot be treated at a high flow velocity. SUMMARY OF THE INVENTION Therefore, the technical problem to be solved by the present disclosure is to overcome defects of difficult recovery and poor mechanical properties of existing polyphenol substance removal media, so as to provide chromatography media for the removal of polyphenol substances and a preparation method thereof for solving the above problems. In order to achieve the above objective, the present disclosure provides the following technical solutions: A method for preparing chromatography media for removal of polyphenol substances includes: obtaining an aqueous phase by mixing a water-soluble inorganic salt, a dispersing agent and water; obtaining an oil phase by mixing N-vinyl pyrrolidone, a first crosslinking agent, a 2024270643   03 Dec 2024 second crosslinking agent, a third crosslinking agent, an initiator and a pore-forming agent; and preparing the chromatography media for the removal of the polyphenol substances by adding the oil phase into the aqueous phase for suspension polymerization; wherein the first crosslinking agent includes at least one of triallyl isocyanurate and N,N'-methylene bisacrylamide; the second crosslinking agent includes at least one of N,N'-divinyl imidazolidinone, N,N'-ethylenebisacrylamide, N,N'-divinylethyleneurea, and N,N'-divinylpropyleneurea; and the third crosslinking agent includes at least one of allyl methacrylate, ethylene glycol diacrylate, ethylene glycol dimethacrylate, and tetraethylene glycol diacrylate. Preferably, the water-soluble inorganic salt includes at least one of sodium sulfate, sodium chloride, calcium chloride and potassium chloride; and / or, the dispersing agent includes at least one of gelatin, polyvinyl alcohol, carboxymethyl cellulose, hydroxypropyl methyl cellulose, polyvinylpyrrolidone, and amylum. Preferably, the initiator includes at least one of benzoyl peroxide, azodiisobutyronitrile, and azobisisoheptonitrile; and / or, the pore-forming agent includes at least one of toluene, dichloromethane, dichloroethane, butyl acetate, and ethyl acetate. Preferably, a mass ratio of the water-soluble inorganic salt, the dispersing agent and water is (25-50):(0.1-3):100. Preferably, a mass ratio of N-vinyl pyrrolidone, the first crosslinking agent, the second crosslinking agent, the third crosslinking agent, the initiator, and the pore-forming agent is 100:(21-36):(11-26):(3-10):(0.7-1.8):(120-125). Preferably, a volume ratio of the aqueous phase to the oil phase is 1:(3-8). Preferably, the suspension polymerization is carried out at a temperature ranging from 50°C to 90°C for a time period ranging from 3 hours to 10 hours. Preferably, stirring treatment is performed after layering of liquid level in the suspension polymerization; and / or, the suspension polymerization is further followed by extraction with an 2024270643   03 Dec 2024 extractant, water washing, and sieving treatment. Preferably, a stirring speed of the stirring treatment is in a range from 100 rpm / min to 500 rpm / min; and / or, the extractant includes at least one of methanol, ethanol, acetone, and dimethoxymethane; and / or, a particle size of the sieving treatment is in a range from 100 pm to 3,000 pm. The present disclosure further provides chromatography media for the removal of polyphenol substances, and the chromatography media is prepared through the above method for preparing chromatography media for the removal of polyphenol substances. The technical solution of the present disclosure has the following advantages: 1. The method for preparing the chromatography media for the removal of the polyphenol substances includes: obtaining the aqueous phase by mixing the water-soluble inorganic salt, the dispersing agent and the water; obtaining the oil phase by mixing N-vinyl pyrrolidone, the first crosslinking agent, the second crosslinking agent, the third crosslinking agent, the initiator and the pore-forming agent; and preparing the chromatography media for the removal of the polyphenol substances by adding the oil phase into the aqueous phase for suspension polymerization, wherein the first crosslinking agent includes at least one of triallyl isocyanurate and N,N’-methylene bisacrylamide; the second crosslinking agent includes at least one of N,N’-divinyl imidazolidinone, N,N’-ethylenebisacrylamide, N, N'-divinylethyleneurea, and N, N'-divinylpropyleneurea; and the third crosslinking agent includes at least one of allyl methacrylate, ethylene glycol diacrylate, ethylene glycol dimethacrylate, and tetraethylene glycol diacrylate. In the prior art, cross-linked polyvinylpyrrolidone particles (PVPP) are usually produced using a single crosslinking agent, but the prepared microspheres have rough surfaces, and poor pore channel distribution and strength, resulting in low pressure-resistant flow velocity. However, the present disclosure uses a forward suspension polymerization method and three crosslinking agents with different activities to prepare the chromatography media for the removal of the polyphenol substances. The chromatography media has a smooth and uniform surface, uniform pore channel distribution, and better strength than that of the single crosslinking agent (the pressure-resistant flow velocity may reflect a shape and strength of the spheres, 2024270643   03 Dec 2024 and an adsorption rate and regeneration amount may reflect the pore channel distribution). The chromatography media has effective binding ability for polyphenol substances in fermented beverages, specifically, an adsorption rate of the polyphenol substances is in a range from 40% to 45%. And after recovery, the chromatography media can be reused for adsorbing the polyphenol substances, a recycle loss rate is less than 1%, a recovery adsorption decrease rate is less than 2%, and cycling performance is good, thereby effectively reducing production costs and minimizing generation of solid waste; and in addition, the chromatography media prepared by the present disclosure is high in mechanical properties. In an XK16 / 40 column, a linear flow rate of the chromatography media of the present disclosure may reach 1,000 cm / h, and a pressure resistance is greater than 1 Mpa. 2. In the method for preparing the chromatography media for the removal of the polyphenol substances in the present disclosure, crosslinking agents without benzene substances are used, and the usage amount is greatly reduced. The matrix of the microspheres is polyvinylpyrrolidone, which improves separation efficiency of the microspheres for the removal of the polyphenol substances and is more environmentally friendly. 3. In the method for preparing the chromatography media for the removal of the polyphenol substances in the present disclosure, a large amount of inorganic salt solution is added into the aqueous phase to reduce the solubility of N-vinyl pyrrolidone in the aqueous phase, and stable PVPP microspheres are prepared, which solves the preparation problem of N-vinyl pyrrolidone microspheres as the matrix and applies them to the removal of the polyphenol substances in fermented beverages, while also solving of their non-reusability. DETAILED DESCRIPTION The following embodiments are provided for a better understanding of the present disclosure, are not limited to the optimal implementation described, and do not limit the content and scope of protection of the present disclosure. Any product that is the same or similar to the present disclosure and is derived from the inspiration of the present disclosure by any one or by combining the features of the present disclosure with that of other prior art 2024270643   03 Dec 2024 falls within the scope of protection of the present disclosure. Specific experimental steps or conditions which are not specified in the embodiments may follow operations of conditions of conventional experimental steps described in the literature in the art. Reagents or instruments used without specifying the manufacturers are conventional reagent products that can be purchased form the market. Example 1 This embodiment provides a method for preparing chromatography media for removal of polyphenol substances, including the following steps: 1) 100 g of sodium chloride and 12 g of polyvinylpyrrolidone K90 were added into 1200 g of water, and a mixture was stirred and dissolved at 45°C to obtain an aqueous phase; 2) 196 g of N-vinyl pyrrolidone, 43.2 g of triallyl isocyanurate, 29.4 g of N,N’-divinyl imidazolidinone, 5.9 g of allyl methacrylate, 1.44 g of azodiisobutyronitrile, 120 g of butyl acetate, and 120 g of toluene were stirred and mixed to obtain an oil phase; and 3) the aqueous phase from step 1) and the oil phase from step 2) were weighed in a volume ratio of the aqueous phase to the oil phase of 1:5, the oil phase was added into the aqueous phase, after liquid stratification, stirring was started to form oil-in-water reverse suspension polymerization beads, a stirring speed was 200 rpm / min, then suspension polymerization was carried out at 80°C for 5 hours, after a reaction is complete, a reaction product was poured into ethanol for soaking, so as to remove residual monomers and other solvents, water was added to detect that the effluent ethanol has no white turbidity, and then the spherical chromatography media ranging from 100 pm to 300 pm was obtained after water washing and sieving. Example 2 This embodiment provides a method for preparing chromatography media for removal of polyphenol substances, including the following steps: 1) 150 g of sodium chloride and 14 g of polyvinylpyrrolidone K60 were added into 1,200 g of water, and a mixture was stirred and dissolved at 45°C to obtain an aqueous phase; 2) 200 g of N-vinyl pyrrolidone, 52 g of N,N’-methylene bisacrylamide, 22 g of 2024270643   03 Dec 2024 N,N’-ethylenebisacrylamide, 20 g of ethylene glycol diacrylate, 2.88 g of azobisisoheptonitrile, and 240 g of ethyl acetate were stirred and mixed to obtain an oil phase; and 3) the aqueous phase from step 1) and the oil phase from step 2) were weighed in a volume ratio of the aqueous phase to the oil phase of 1:8, the oil phase was added into the aqueous phase, after liquid stratification, stirring was started to form oil-in-water reverse suspension polymerization beads, a stirring speed was 250 rpm / min, then suspension polymerization was carried out at 80°C for 5 hours, after a reaction is complete, a reaction product was poured into ethanol for soaking, so as to remove residual monomers and other solvents, water was added to detect that the effluent ethanol has no white turbidity, and then the spherical chromatography media ranging from 110 gm to 320 gm was obtained after water washing and sieving. Example 3 This embodiment provides a method for preparing chromatography media for removal of polyphenol substances, including the following steps: 1) 150 g of calcium chloride, 12 g of polyvinyl alcohol and 12 g of gelatin were added into 1200 g of water, and a mixture was stirred and dissolved at 45°C to obtain an aqueous phase; 2) 220 g of N-vinyl pyrrolidone, 66 g of triallyl isocyanurate, 35.2 g of N, N'-divinylpropyleneurea, 8.8 g of tetraethylene glycol diacrylate, 3.8 g of benzoyl peroxide, 120 g of dichloromethane, and 150 g of toluene were stirred and mixed to obtain an oil phase; and 3) the aqueous phase from step 1) and the oil phase from step 2) were weighed in a volume ratio of the aqueous phase to the oil phase of 1:3, the oil phase was added into the aqueous phase, after liquid stratification , stirring was started to form oil-in-water reverse suspension polymerization beads, a stirring speed was 200 rpm / min, then suspension polymerization was carried out at 80°C for 5 hours, after a reaction is complete, a reaction product was poured into ethanol for soaking, so as to remove residual monomers and other solvents, water was added to detect that the effluent ethanol has no white turbidity, and then the spherical chromatography media ranging from 200 gm to 500 gm was obtained after 2024270643   03 Dec 2024 water washing and sieving. Example 4 This embodiment provides a method for preparing chromatography media for removal of polyphenol substances, including the following steps: 1) 300 g of sodium sulfate and 1.2 g of carboxymethyl cellulose were added into 1,200 g of water, and a mixture was stirred and dissolved at 45°C to obtain an aqueous phase; 2) 200 g of N-vinyl pyrrolidone, 42 g of triallyl isocyanurate, 52 g of N, N'-divinylethyleneurea, 6 g of ethylene glycol dimethacrylate, 1.4 g of azodiisobutyronitrile, and 250 g of dichloroethane were stirred and mixed to obtain an oil phase; and 3) the aqueous phase from step 1) and the oil phase from step 2) were weighed in a volume ratio of the aqueous phase to the oil phase of 1:5, the oil phase was added into the aqueous phase, after liquid stratification, stirring was started to form oil-in-water reverse suspension polymerization beads, a stirring speed was 100 rpm / min, then suspension polymerization was carried out at 50°C for 10 hours, after a reaction is complete, a reaction product was poured into acetone for soaking, so as to remove residual monomers and other solvents, water was added to detect that the effluent acetone has no white turbidity, and then the spherical chromatography media ranging from 100 pm to 300 pm was obtained after water washing and sieving. Example 5 This embodiment provides a method for preparing chromatography media for removal of polyphenol substances, including the following steps: 1) 600 g of potassium chloride and 36 g of hydroxypropyl methyl cellulose were added into 1,200 g of water, and a mixture was stirred and dissolved at 45°C to obtain an aqueous phase; 2) 200 g of N-vinyl pyrrolidone, 72 g of triallyl isocyanurate, 22 g of N,N’-divinyl imidazolidinone, 6 g of allyl methacrylate, 3.6 g of azodiisobutyronitrile, and 240 g of butyl acetate were stirred and mixed to obtain an oil phase; and 3) the aqueous phase from step 1) and the oil phase from step 2) were weighed in a volume ratio of the aqueous phase to the oil phase of 1:5, the oil phase was added into the aqueous phase, after liquid stratification, stirring was started to form oil-in-water reverse 2024270643   03 Dec 2024 suspension polymerization beads, a stirring speed was 500 rpm / min, then suspension polymerization was carried out at 90°C for 3 hours, after a reaction is complete, a reaction product was poured into dimethoxymethane for soaking, so as to remove residual monomers and other solvents, water was added to detect that the effluent dimethoxymethane has no white turbidity, and then the spherical chromatography media ranging from 100 pm to 300 pm was obtained after water washing and sieving. Comparative Example 1 The difference between this comparative example and Example 1 is that only 78.5 g of triallyl isocyanurate was added as a crosslinking agent, and other conditions are the same as Example 1. Comparative Example 2 The difference between this comparative example and Example 1 is that 43.2 g of triallyl isocyanurate and 35.3 g of N,N’-divinyl imidazolidinone were added as crosslinking agents, and other conditions are the same as Example 1. Comparative Example 3 The difference between this comparative example and Example 1 is that 43.2 g of triallyl isocyanurate and 35.3 g of allyl methacrylate were added as crosslinking agents, and other conditions are the same as Example 1. Comparative Example 4 The difference between this comparative example and Example 1 is that 43.2 g of N,N’-divinyl imidazolidinone and 35.3 g of allyl methacrylate were added as crosslinking agents, and other conditions are the same as Example 1. Test Example 1 A pressure-resistant flow velocity and an adsorption capacity of the chromatography media prepared in Examples 1-5 and Comparative Examples 1-4 were tested. The pressure-resistant flow velocity testing was carried out by using a GE AKTA chromatography system, an XK16 / 40 column, and 0.10 mol / L NaCl. AKTA programming was used for pressure flow velocity testing, and the testing results are shown in Table 1 below. The adsorption capacity testing was carried out by using a GE AKTA chromatography system; a 1 mL chromatography column; a detection wavelength: 280 nm; 2024270643   03 Dec 2024 a mobile phase: 0.1% phosphoric acid aqueous solution: acetonitrile=85:15; a flow rate: 1,000 mL / min; a column temperature: 25°C, a maximum ultraviolet absorption value was recorded, and the absorption capacity thereof was calculated. The testing results are shown in Table 2 below. Table 1 Example 1 Linear flow rate (cm / h) 360 480 600 720 840 960 1080 1200 PreC (Mpa) 0.413 0.653 0.734 0.853 0.913 1.031 1.132 1.213 DeltaC (Mpa) 0.397 0.531 0.621 0.765 0.813 0.919 1.043 1.134 Example 2 Linear flow rate (cm / h) 350 470 590 710 820 930 1040 1100 PreC (Mpa) 0.403 0.633 0.714 0.833 0.903 1.001 1.032 1.113 DeltaC (Mpa) 0.374 0.521 0.611 0.795 0.863 0.909 1.003 1.004 Example 3 Linear flow rate (cm / h) 450 510 620 760 840 970 1080 1180 PreC (Mpa) 0.502 0.687 0.754 0.813 0.893 0.991 1.132 1.213 DeltaC (Mpa) 0.434 0.621 0.699 0.805 0.883 0.919 1.033 1.104 Example 4 Linear flow rate (cm / h) 460 520 630 770 850 980 1090 1190 PreC (Mpa) 0.472 0.657 0.724 0.783 0.863 0.961 1.102 1.183 DeltaC (Mpa) 0.214 0.401 0.479 0.585 0.663 0.699 0.813 0.884 Example 5 Linear flow rate (cm / h) 370 490 610 730 850 970 1090 1210 PreC (Mpa) 0.383 0.623 0.704 0.823 0.883 1.001 1.102 1.183 DeltaC (Mpa) 0.277 0.311 0.401 0.545 0.593 0.699 0.823 0.914 Comparative Example 1 Linear flow rate (cm / h) 60 180 300 420 540 660 780 900 PreC (Mpa) 0.543 0.783 0.864 0.983 1.043 1.161 1.262 1.343 DeltaC (Mpa) 0.517 0.651 0.741 0.885 0.933 1.039 1.163 1.254 Comparative Example 2 Linear flow rate (cm / h) 40 160 280 400 520 640 760 880 PreC (Mpa) 0.743 0.983 1.064 1.183 1.243 1.361 1.462 1.543 DeltaC (Mpa) 0.717 0.851 0.941 1.085 1.133 1.239 1.363 1.454 Comparative Example 3 Linear flow rate (cm / h) 240 360 480 600 720 840 860 980 PreC (Mpa) 0.943 1.183 1.264 1.383 1.443 1.561 1.662 1.743 DeltaC (Mpa) 0.849 0.983 1.073 1.217 1.265 1.371 1.495 1.586 Comparative Example 4 Linear flow rate (cm / h) 40 160 280 400 520 640 660 780 PreC (Mpa) 0.966 1.206 1.287 1.406 1.466 1.584 1.685 1.766 DeltaC (Mpa) 0.859 0.993 1.083 1.227 1.275 1.381 1.505 1.596 Table 2 First cycle Second cycle Third cycle Fourth cycle Fifth cycle Example 1 Flowthrough amount / mg 64.4 66.4 66.5 66.7 66.7 Adsorption capacity / mg 53.3 52.1 51.9 51.9 52 Regeneration amount / mg 53.0 52 51.5 51.4 51.8 Adsorption rate 45.20% 44.00% 43.80% 43.80% 43.80% Example 2 Flowthrough amount / mg 61.4 61.8 61.2 61.3 61.2 2024270643   03 Dec 2024 Adsorption capacity / mg 49.1 47.6 46.6 46.4 46.5 Regeneration amount / mg 48.7 46.5 46.1 46.3 46.4 Adsorption rate 44.40% 43.50% 43.20% 43.10% 43.20% Example 3 Flowthrough amount / mg 63.60 63.90 63.10 63.00 63.20 Adsorption capacity / mg 51.10 50.30 46.90 46.70 46.80 Regeneration amount / mg 50.80 50.00 46.10 46.30 46.40 Adsorption rate 44.60% 44.00% 42.60% 42.60% 42.50% Example 4 Flowthrough amount / mg 61.4 62.4 62.5 62.7 62.7 Adsorption capacity / mg 52.3 52.1 51.9 51.9 52 Regeneration amount / mg 51.1 51.4 50.3 50.1 50.15 Adsorption rate 46.00% 45.50% 45.37% 45.29% 45.34% Example 5 Flowthrough amount / mg 64.4 66.4 66.5 66.7 66.7 Adsorption capacity / mg 51.3 51.1 50.9 50.9 51 Regeneration amount / mg 53.1 52.4 51.3 51.1 51.15 Adsorption rate 44.34% 43.49% 43.36% 43.28% 43.33% Comparative Example 1 Flowthrough amount / mg 61.1 62.1 62.1 62.3 62.3 Adsorption capacity / mg 32.3 32.1 31.9 31.9 32 Regeneration amount / mg 31.1 31.4 30.3 30.1 30.15 Adsorption rate 34.58% 34.08% 33.94% 33.86% 33.93% Comparative Example 2 Flowthrough amount / mg 81.1 82.1 82.1 82.2 82.2 Adsorption capacity / mg 12.3 12.1 11.9 11.9 12 Regeneration amount / mg 11.1 11.4 10.3 10.1 10.1 Adsorption rate 13.17% 12.85% 12.66% 12.65% 12.74% Comparative Example 3 Flowthrough amount / mg 71.1 72.1 72.1 72.2 72.2 Adsorption capacity / mg 14.3 14.1 13.9 13.9 14 Regeneration amount / mg 13.1 13.4 12.3 12.1 12.1 Adsorption rate 16.74% 16.36% 16.16% 16.14% 16.24% Comparative Example 4 Flowthrough amount / mg 61.1 62.1 62.1 62.2 62.2 2024270643   03 Dec 2024 Adsorption capacity / mg 54.3 54.1 53.9 53.9 54 Regeneration amount / mg 23.1 23.4 22.3 22.1 22.1 Adsorption rate 47.05% 46.56% 46.47% 46.43% 46.47% According to the above testing results, it can be seen that the adsorption rate of the chromatography media prepared by the present disclosure for the polyphenol substances is in a range from 40% to 46%, and after recovery, the chromatography media can be reused for adsorbing the polyphenol substances, a recycle loss rate is less than 1%, a recovery adsorption decrease rate is less than 2%, and cycling performance is good. In addition, the chromatography media prepared by the present disclosure is high in mechanical properties. In an XK16 / 40 column, a linear flow rate of the chromatography media of the present disclosure may reach 1,000 cm / h, and a pressure resistance is greater than 1 MPa. Obviously, the above embodiments are only examples for clear explanation, not for limitation of the implementations. For those ordinarily skilled in the art, other changes or variations in different forms can further be made on the basis of the above description. It is unnecessary and impossible to enumerate all the implementations here. The obvious changes or variations arising therefrom are still within the protection scope of the present disclosure.

Claims

1. A method for preparing chromatography media for removal of polyphenol substances, comprising:obtaining an aqueous phase by mixing a water-soluble inorganic salt, a dispersing agent and water;obtaining an oil phase by mixing N-vinyl pyrrolidone, a first crosslinking agent, a second crosslinking agent, a third crosslinking agent, an initiator and a pore-forming agent; andpreparing the chromatography media for the removal of the polyphenol substances by adding the oil phase into the aqueous phase for suspension polymerization; whereinthe first crosslinking agent comprises at least one of triallyl isocyanurate and N,N'-methylene bisacrylamide;the second crosslinking agent comprises at least one of N,N'-divinyl imidazolidinone, N,N'-ethylenebisacrylamide, N,N'-divinylethyleneurea, and N,N'-divinylpropyleneurea; andthe third crosslinking agent comprises at least one of allyl methacrylate, ethylene glycol diacrylate, ethylene glycol dimethacrylate, and tetraethylene glycol diacrylate.

2. The method according to claim 1, wherein the water-soluble inorganic salt comprises at least one of sodium sulfate, sodium chloride, calcium chloride and potassium chloride;and / or, the dispersing agent comprises at least one of gelatin, polyvinyl alcohol, carboxymethyl cellulose, hydroxypropyl methylcellulose, polyvinylpyrrolidone, and amylum.

3. The method according to claim 1 or 2, wherein the initiator comprises at least one of benzoyl peroxide, azodiisobutyronitrile, and azobisisoheptonitrile;and / or, the pore-forming agent comprises at least one of toluene, dichloromethane, dichloroethane, butyl acetate, and ethyl acetate.2024270643   03 Dec 20244. The method according to any one of claims 1 to 3, wherein a mass ratio of the water-soluble inorganic salt, the dispersing agent and water is (25-50):(0.1-3):100.

5. The method according to any one of claims 1 to 4, wherein a mass ratio of N-vinyl pyrrolidone, the first crosslinking agent, the second crosslinking agent, the third crosslinking agent, the initiator, and the pore-forming agent is 100:(21-36):(11-26):(3-10):(0.7-1.8):(120-125).

6. The method according to any one of claims 1 to 5, wherein a volume ratio of the aqueous phase to the oil phase is 1:(3-8).

7. The method according to any one of claims 1 to 6, wherein the suspension polymerization is carried out at a temperature ranging from 50°C to 90°C for a time period ranging from 3 hours to 10 hours.

8. The method according to any one of claims 1 to 7, wherein stirring treatment is performed after liquid stratification in the suspension polymerization;and / or, the suspension polymerization is further followed by extraction with an extractant, water washing, and sieving treatment.

9. The method according to claim 8, wherein a stirring speed of the stirring treatment is in a range from 100 rpm / min to 500 rpm / min;and / or, the extractant comprises at least one of methanol, ethanol, acetone, and dimethoxymethane;and / or, a particle size of the sieving treatment is in a range from 100 pm to 3,000 pm.2024270643   03 Dec 202410. Chromatography media for the removal of polyphenol substances, wherein the chromatography media is prepared through the method for preparing chromatography media for the removal of polyphenol substances according to any one of claims 1 to 9 above.