浆态床加氢催化剂、其制备方法及应用
By using a slurry-bed hydrogenation catalyst with uniformly sized iron-based metallurgical powder as a carrier, the problems of large catalyst loading and low efficiency in existing technologies have been solved, achieving the effect of low-cost and high-efficiency conversion of catalytic slurry into clean fuel oil.
Patent Information
- Authority / Receiving Office
- CN · China
- Patent Type
- Patents(China)
- Current Assignee / Owner
- NINGBO INST OF MATERIALS TECH & ENG CHINESE ACAD OF SCI
- Filing Date
- 2022-08-24
- Publication Date
- 2026-07-17
AI Technical Summary
Existing slurry-bed hydrogenation catalysts require a large loading of active metals, resulting in high costs and low catalytic efficiency, making it difficult to efficiently utilize inferior heavy oils such as catalytic slurry.
Using iron-based metallurgical powder with a particle size of 200-250 mesh and a particle size dispersion of less than 10% as a carrier, a slurry bed hydrogenation catalyst was prepared by impregnating an active metal solution, adding ammonia water to form a metal crystal precipitate, and then calcining it. This catalyst is used to catalyze the slurry bed hydrogenation reaction of oil slurry.
With a relatively small active metal loading, uniform distribution of catalytic efficiency and high catalytic effect are achieved, reducing catalyst cost, improving the conversion rate and economy of inferior heavy oil, and producing clean fuel oil products.