一种含Sialon结合长寿命鱼雷罐冲击区砖及制备方法
By adding a catalyst to the bricks in the impact zone of the torpedo canister to induce the formation of a robust layer of Sialon material, the problem of easy damage to the impact zone of the torpedo canister was solved, achieving long service life and high wear resistance of the torpedo canister lining.
Patent Information
- Authority / Receiving Office
- CN · China
- Patent Type
- Patents(China)
- Current Assignee / Owner
- QINHUANGDAO SHOUGANG KROSAKI REFRACTORIES CO LTD
- Filing Date
- 2023-12-25
- Publication Date
- 2026-07-17
AI Technical Summary
The existing impact zone bricks of torpedo canisters are easily damaged under high temperature and high pressure, resulting in uneven service life and seriously affecting the overall service life of the torpedo canister lining. Current technology has reached a bottleneck in improving the grade of raw materials and cannot further improve wear resistance.
By adding a catalyst to the bricks in the impact zone of the torpedo tank, Sialon material is spontaneously generated under high temperature and pressure, forming a stronger overall superhard layer. The high temperature and pressure conditions inside the torpedo tank allow Sialon to react with the aggregate to form a robust layer, improving its resistance to erosion and corrosion.
It effectively solved the wear resistance problem in the impact zone of the torpedo canister, extended the overall service life of the torpedo canister lining, and improved the comprehensive performance of the refractory material.