一种耐腐蚀热浸镀锌带钢及其制备工艺
By using flux and passivation solutions with specific components, the problem of poor adhesion between the zinc coating and the substrate in hot-dip galvanized steel strip was solved, thereby improving the corrosion resistance of hot-dip galvanized steel strip and extending its service life.
CN117966064BActive Publication Date: 2026-07-17TANGSHAN SHENGXIN COLD ROLLED SHEET CO LTD
Patent Information
- Authority / Receiving Office
- CN · China
- Patent Type
- Patents(China)
- Current Assignee / Owner
- TANGSHAN SHENGXIN COLD ROLLED SHEET CO LTD
- Filing Date
- 2024-01-18
- Publication Date
- 2026-07-17
Smart Images
Figure SMS_1
Abstract
本发明涉及钢铁材料防腐蚀技术领域，提出了一种耐腐蚀热浸镀锌带钢及其制备工艺，热浸镀锌带钢的制备工艺，包括以下步骤：带钢依次经碱洗、酸洗、水洗、助镀、烘干、热浸镀和冷却后，得到热浸镀锌带钢；助镀时，助镀液由以下重量百分比的组分组成：氯化锌6%~8%、氯化亚锡4%~6%、单盐酸肼2%~4%、月桂醇硫酸钠0.1%~1%、聚乙烯吡咯烷酮0.1%~0.3%，其余为水。通过上述技术方案，解决了现有技术中的热浸镀锌带钢耐腐蚀性能较差的问题。