一种仿大理石复刻釉及其制备方法和在制备仿大理石瓷砖中的应用
By preparing a modified kaolin-aluminum borate whisker composite, a stable modified kaolin is formed. Combined with chitosan and sodium dodecylbenzenesulfonate, the aluminum borate whiskers are uniformly dispersed, which solves the problem of poor wear resistance of imitation marble ceramic tiles and improves the wear resistance and hardness of the glaze.
CN120987567BActive Publication Date: 2026-07-17GUANGDONG GUANXING CERAMIC ENTERPRISE CO LTD
Patent Information
- Authority / Receiving Office
- CN · China
- Patent Type
- Patents(China)
- Current Assignee / Owner
- GUANGDONG GUANXING CERAMIC ENTERPRISE CO LTD
- Filing Date
- 2025-08-14
- Publication Date
- 2026-07-17
AI Technical Summary
Technical Problem
Existing marble-look ceramic tiles have poor wear resistance and are prone to scratches during daily use, affecting their appearance and lifespan.
Method used
A modified kaolin-aluminum borate whisker complex is used. Hydroxy zinc, manganese and magnesium ions are loaded and polymerized through hydrolysis polymerization to form a stable modified kaolin. Combined with chitosan and sodium dodecylbenzenesulfonate, the aluminum borate whiskers are uniformly dispersed to form a continuous reinforcing network, thereby improving the wear resistance of the glaze.
Benefits of technology
It significantly improves the wear resistance and hardness of the marble-look ceramic tile glaze, reduces scratches, and extends service life.
✦ Generated by Eureka AI based on patent content.
Smart Images
Figure SMS_1 
Figure SMS_2
Abstract
本发明涉及一种仿大理石复刻釉及其制备方法和在制备仿大理石瓷砖中的应用，所述复刻釉包括质量比为(0.2‑0.6)：(0.5‑0.8)：1的干粒、釉浆和悬浮剂；所述釉浆包括质量比为100：40‑50的干粉釉料和水，所述干粉釉料包括钠长石15‑20份、钾长石15‑20份、改性高岭土‑硼酸铝晶须复配物20‑25份、白云石5‑8份、硼酸钙5‑10份、碳酸锶5‑10份和碳酸钡5‑10份。本发明的仿大理石复刻釉通过多组分协同作用，实现了釉面耐磨性的显著提升，最终获得仿大理石效果的高性能瓷砖。