METHOD FOR THE PRODUCTION OF POLYESTER POLYOL

Description

TECHNICAL FIELD

[0001] The present application relates to a method for preparing polyester polyol, which belongs to the field of polymer synthesis.BACKGROUND

[0002] Polyester polyols are prepared by polycondensation of dibasic organic carboxylic acids, carboxylic anhydrides and polyhydric alcohols, and their relative molecular masses are generally less than 4500. Dibasic acids include phthalic acid or phthalic anhydride or its esters, adipic acid, halogenated phthalic acid and so on, and polyhydric alcohols include ethylene glycol, propylene glycol, diethylene glycol, trimethylolpropane, pentaerythritol and so on. The polyester polyols are generally classified based on carboxylic acids, and usually comprise following species: adipic acid polyester polyols, alkyd polyester polyols, caprolactone polyester polyols and acrylic polyester polyols. The methods for preparing polyester polyols include vacuum dehydration method and high temperature nitrogen dehydration method. Vacuum dehydration method refers to that, under vacuum conditions, using acetate as a catalyst, dibasic acid and dihydric alcohol undergo polycondensation reaction to synthesize a certain molecular mass of polyester polyol. High temperature nitrogen dehydration method refers to synthesizing polyester polyol at high temperature under the protection of nitrogen.

[0003] Traditional polyester polyols are produced from organic acids, anhydrides or organic acid esters as raw materials, which have poor heat resistance and the initial decomposition temperature is generally lower than 300°C (see CN106660252A; Synthesis and properties of acrylpimaric acid polyester polyol[J]. Chemistry and Industry of Forest Products,1999, (02):63-67.), and are difficult to apply in fields requiring high heat resistance. CN 101 735 436 discloses the preparation method of copolymer ether ester comprising ester exchange or esterification reaction, and fasculation reaction. The product has excellent comprehensive performance, and the thermal decomposition temperature is 360-450°C.SUMMARY

[0004] According to one aspect of the present application, a method for preparing polyester polyol is provided, and the polyester polyol prepared by the method has higher heat resistance.

[0005] The polyester polyol polymer of the present application is a new type of polyester polyol polymer obtained by transesterification of inorganic oxyacid ester and polyhydric alcohols as raw materials as indicated in the annexed claims. In contrast, the traditional polyester polyol is prepared by dehydration esterification reaction of organic acid and polyhydric alcohols as raw materials.

[0006] The method for preparing polyester polyol is characterized in that it comprises performing transesterification of raw materials containing inorganic oxyacid ester and polyhydric alcohol to obtain the polyester polyol.

[0007] Optionally, the inorganic oxyacid ester is at least one of compounds having a chemical formula shown in Formula I and Formula II:         M(OR 1< ) n 1<      Formula I         O=P (OR 2< ) n 2<      Formula II wherein, M is a metal element or a non-metal element that does not include P, R 1< and R 2< are independently selected from at least one of C 1 to C 8 alkyl groups, n 1< =2~8, n 2< =2~8.

[0008] Optionally, n 1< =2, 3, 4, 5, 6, 7, or 8.

[0009] Optionally, n 2< =3.

[0010] Optionally, M comprises at least one of B, Si, Ge, P, Al, Ti, Fe, Sn, V, Ga, Zr, Cr, Sb and W.

[0011] Optionally, M is B, Si, Ge, P, Al, Ti, Fe, Sn, V, Ga, Zr, Cr, Sb or W.

[0012] Optionally, M is B, Si, Ge, P, Al, Ti, Fe, Sn, V, Ga, Zr, Cr, Sb or W.

[0013] Optionally, in the Formula I, R 1< and R 2< are independently selected from at least one of C 1 to C 4 alkyl groups.

[0014] Optionally, the inorganic oxyacid ester comprises at least one of trimethyl borate, triethyl borate, tripropyl borate, tributyl borate, tri-n-hexyl borate, triisooctyl borate, trioctyl borate, tetramethoxysilane, tetraethyl orthosilicate, tetrapropyl silicate, tetrabutyl silicate, ethyl orthogermanate, triethyl phosphate, tripropyl phosphate, tributyl phosphate, tri-n-pentyl phosphate, trihexyl phosphate, aluminium ethoxide, aluminum isopropoxide, aluminum n-butoxide, aluminum tert-butoxide, tetraethyl titanate, tetraisopropyl titanate, tetrabutyl titanate, tetrahexyl titanate, tetraisooctyl titanate, tetrabutyl ferrite, tetrabutyl stannate, butyl orthovanadate, gallium ethoxide, tetra-n-propyl zirconate, tetrabutyl zirconate, tert-butyl chromate, ethyl antimonite, butyl antimonate, tungsten ethoxide and tungsten isopropoxide.

[0015] The molar ratio of the inorganic oxyacid ester to the polyhydric alcohol satisfies: inorganic oxyacid ester: polyhydric alcohol = (0.8~1.2) n 3< / x; wherein x is the number of moles of alkoxyl groups contained in each mole of inorganic oxyacid ester, and n 3< is the number of moles of hydroxyl groups contained in each mole of polyhydric alcohol.

[0016] Optionally, the upper limit of the molar ratio of the inorganic oxyacid ester to the polyol is 0.85n 3< / x, 0.9n 3< / x, 0.95n 3< / x, 1n 3< / x, 1.05n 3< / x, 1.1n 3< / x, 1.15n 3< / x or 1.2n 3< / x, and the lower limit thereof is 0.8n 3< / x, 0.85n 3< / x, 0.9n 3< / x, 0.95n 3< / x, 1n 3< / x, 1.05n 3< / x, 1.1n 3< / x or 1.15n 3< / x; wherein, x is the number of moles of alkoxy groups contained in each mole of the inorganic oxyacid ester, and n 3< is the number of moles of hydroxyl groups contained in each mole of the polyhydric alcohol.

[0017] Optionally, the number of hydroxyl groups in the polyhydric alcohol is not less than two.

[0018] Optionally, the polyhydric alcohol comprises at least one of ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,4-butylene glycol, 1,6-hexanediol, polyethylene glycol 200, polyethylene glycol 400, polyethylene glycol 600, polyethylene glycol 800, 1,4-cyclohexanediol, 1,4-cyclohexane dimethanol, terephthalyl alcohol, glycerin, trimethylolpropane, pentaerythritol, xylitol and sorbitol.

[0019] Optionally, the formula of the polyhydric alcohol is R 2< -(OH) x , wherein x≥2.

[0020] Optionally, the molar ratio of the inorganic oxyacid ester to the polyhydric alcohol satisfies: (0.8~1.2) n / x; wherein, x is the number of moles of alkoxy groups contained in each mole of the inorganic oxyacid ester, and n is the number of moles of hydroxyl groups contained in each mole of the polyhydric alcohol.

[0021] Optionally, the transesterification is carried out in the presence of a transesterification catalyst.

[0022] Optionally, the amount of the transesterification catalyst is in a range from 0.1wt% to 5wt% of the inorganic oxyacid ester.

[0023] Optionally, the upper limit of amount of the transesterification catalyst is 0.2wt%, 0.5wt%, 0.8wt%, 1.0wt%, 1.5wt%, 2.0wt%, 2.5wt%, 3.0wt%, 3.5wt%, 4.0wt%, 4.5wt% or 5.0wt% of the inorganic oxyacid ester, and the lower limit thereof is 0.1wt%, 0.2wt%, 0.5wt%, 0.8wt%, 1.0wt%, 1.5wt%, 2.0wt%, 2.5wt%, 3.0wt%, 3.5wt%, 4.0wt% or 4.5wt% of the inorganic oxyacid ester.

[0024] Optionally, the transesterification catalyst is at least one of acidic catalyst and basic catalyst.

[0025] Optionally, the acidic catalyst includes at least one of alcohol-soluble acid, solid acid, aluminum alkoxide, aluminum phenoxide, tetrabutyl stannate, titanium alkoxide, zirconium alkoxide, ethyl antimonite and butyl antimonite; and the basic catalyst includes at least one of alcohol-soluble base and solid base.

[0026] Optionally, the alcohol-soluble acid is an acid that is easily soluble in alcohol.

[0027] Optionally, the alcohol-soluble base is a base that is easily soluble in alcohol.

[0028] Optionally, the alcohol-soluble acid includes sulfuric acid, sulfonic acid and the like.

[0029] Optionally, the alcohol-soluble base includes NaOH, KOH, NaOCH 3 , organic base and the like.

[0030] Optionally, the transesterification catalyst is: a basic catalyst including bases that are easily soluble in alcohol (such as NaOH, KOH, NaOCH 3 , organic bases and so on) and various solid base catalysts; and an acidic catalyst including acids that are easily soluble in alcohol (such as sulfuric acid, sulfonic acid and so on) and various solid acidic catalysts, aluminum alkoxide, aluminum phenoxide, tetrabutyl stannate, titanium alkoxide, zirconium alkoxide, ethyl antimonite, butyl antimonite and so on. And the amount of the transesterification catalyst is in a range from 0.1wt% to 5wt% of the inorganic oxyacid ester.

[0031] Optionally, the conditions for the transesterification are: a reaction temperature ranges from 80 to °C, and a reaction time ranges from 2 to10 hours in an inactive atmosphere.

[0032] Optionally, the inactive atmosphere includes at least one of nitrogen and inert gas atmosphere.

[0033] Optionally, the inactive atmosphere is nitrogen atmosphere.

[0034] Optionally, the transesterification is carried out under stirring condition.

[0035] Optionally, the upper limit of the reaction temperature is 85°C, 90°C, 100°C, 110°C, 120°C, 130°C, 140°C, 150°C, 160°C, 170°C, 175°C or 180°C, and the lower limit thereof is 80°C, 85°C, 90°C, 100°C, 110°C, 120°C, 130°C, 140°C, 150°C, 160°C, 170°C or 175°C.

[0036] Optionally, the upper limit of the reaction time is 3 hours, 4 hours, 5 hours, 6 hours, 7 hours, 8 hours, 9 hours or 10 hours, and the lower limit thereof is 2 hours, 3 hours, 4 hours, 5 hours, 6 hours, 7 hours, 8 hours or 9 hours.

[0037] Optionally, the conversion rate of the transesterification ranges from 60% to 80%.

[0038] Optionally, the conditions for the transesterification further comprise performing vacuum distillation thereafter.

[0039] Optionally, the conditions of the vacuum distillation comprise: a vacuum degree ranges from 0.01 to 5kPa, a vacuum distillation temperature ranges from 170 to 230°C, and a vacuum distillation time ranges from 0.5 to 5 hours.

[0040] Optionally, in the vacuum distillation process, the upper limit of the vacuum degree is 0.02kPa, 0.05kPa, 0.1kPa, 0.5kPa, 1kPa, 2kPa, 3kPa, 4kPa, 4.5kPa or 5kPa, and the lower limit thereof is 0.01kPa, 0.02kPa, 0.05 kPa, 0.1kPa, 0.5kPa, 1kPa, 2kPa, 3kPa, 4kPa or 4.5kPa.

[0041] Optionally, in the vacuum distillation process, the upper limit of the vacuum distillation temperature is 175°C, 180°C, 190°C, 200°C, 210°C, 220°C,225°C or 230°C, and the lower limit thereof is 170°C, 175°C, 180°C, 190°C, 200°C, 210°C, 220°C or 225°C.

[0042] Optionally, in the vacuum distillation process, the upper limit of the vacuum distillation time is 0.8 hours, 1 hours, 2 hours, 3 hours, 4 hours, 4.5 hours or 5 hours, and the lower limit thereof is 0.5 hours, 0.8 hours, 1 hours, 2 hours, 3 hours, 4 hours or 4.5 hours.

[0043] Optionally, the conversion rate of the transesterification is greater than 90%.

[0044] The method comprises: a) mixing inorganic oxyacid ester, polyhydric alcohol and transesterification catalyst, and then performing the transesterification under stirring conditions and in an inactive protection atmosphere, wherein the reaction temperature ranges from 80 to 180°C, and the reaction time ranges from 2 to 10 hours; b) after the reaction in step a), performing vacuum distillation during which the vacuum degree ranges from 0.01 to 5kPa, the reaction temperature ranges from 170 to 230 °C, and the reaction time ranges from 0.5 to 5 hours.

[0045] As a specific embodiment, the method comprises: 1) mixing inorganic oxyacid ester, polyhydric alcohol and transesterification catalyst uniformly in a three-necked flask, and performing the transesterification under stirring conditions during which a distillation device is connected to the three-necked flask and nitrogen is passed in the three-necked flask for protection, wherein the reaction temperature ranges from 80 to 180 °C, the reaction time ranges from 2 to 10 hours, and the conversion rate of the transesterification ranges from 60% to 80%; 2) after step 1), connecting the distillation device to the water pump or oil pump for vacuum distillation to make the transesterification more complete, wherein the vacuum degree is controlled to range from 0.01 to 5kPa, the reaction temperature ranges from 170 to 230°C, the reaction time ranges from 0.5 to 5 hours, and the conversion rate of the transesterification is greater than 90%.

[0046] Optionally, the initial decomposition temperature of the polyester polyol is higher than 300°C.

[0047] Optionally, the initial decomposition temperature of the polyester polyol reaches 500°C.

[0048] In the present application, "C 1 ~C 8 " and the like all refer to the number of carbon atoms contained in the alkyl group.

[0049] In the present application, "alkyl" is a group formed by the loss of any hydrogen atom on the molecule of an alkane compound.

[0050] In the present application, the "initial decomposition temperature" refers to the temperature at which the polyester polyol has an obvious weight loss peak through thermogravimetric analysis.

[0051] The beneficial effects that the present application can achieve comprise: 1) The present application uses inorganic oxyacid esters and polyhydric alcohol as raw materials to perform transesterification to obtain a new type of polyester polyol polymer; 2) The polyester polyol polymer prepared in the present application has good heat resistance, the initial decomposition temperature thereof can reach 500 °C, and it can be used in fields that require high heat resistance. BRIEF DESCRIPTION OF DRAWINGS

[0052] Figure 1 is a thermal analysis diagram of the product synthesized in Example 1 of the present application. Figure 2 is a thermal analysis diagram of the product synthesized in Example 2 of the present application. DETAILED DESCRIPTION

[0053] The present application will be described in detail below with reference to the examples, but the present application is not limited to these examples.

[0054] Unless otherwise specified, the raw materials in the examples of the present application are all commercially available.

[0055] The analysis methods in the examples of the present application are as follows.

[0056] Thermogravimetric analysis is conducted by TA Q-600 thermogravimetric analyzer produced by TA Instruments. The nitrogen flow rate is 100ml / min, and the temperature is increased to 700°C at a temperature rise rate of 10°C / min.

[0057] The conversion rate of the transesterification in the examples of the present application is calculated as follows: according to the number of moles n of the by-product alcohols distilled out during the reaction, the number of groups participating in the transesterification is determined to be n, and the total number of moles of esters in the reaction raw materials is m, and then the conversion rate of the transesterification is n / xm. x depends on the number of alkoxy groups connected to the central atom in the esters.

[0058] According to an embodiment of the present application, the polyester polyol polymer and the method for preparing the same are characterized in that the method includes the following steps: a) mixing inorganic oxyacid ester, polyhydric alcohol and transesterification catalyst uniformly in a three-necked flask, and performing the transesterification under stirring conditions during which a distillation device is connected to the three-necked flask and nitrogen is passed in the three-necked flask for protection, wherein the reaction temperature ranges from 80 to 180 °C, the reaction time ranges from 2 to 10 hours, and the conversion rate of the transesterification ranges from 60% to 80%; b) after step a), connecting the distillation device to the water pump or oil pump for vacuum distillation to make the transesterification more complete, wherein the vacuum degree is controlled to range from 0.01 to 5kPa, the reaction temperature ranges from 170 to 230°C, the reaction time ranges from 0.5 to 5 hours, and the conversion rate of the transesterification is greater than 90%.

[0059] Optionally , the formula of the inorganic oxyacid ester in step a) is M(OR) n , wherein M is B, Si, Ge, P, Al, Ti, Fe, Sn, V, Ga, Zr, Cr, Sb, W; R is any one of "C 1 to C 8 " alkyl groups; and the inorganic oxyacid ester comprises at least one of trimethyl borate, triethyl borate, tripropyl borate, tributyl borate, tri-n-hexyl borate, triisooctyl borate, trioctyl borate, tetramethoxysilane, tetraethyl orthosilicate, tetrapropyl silicate, tetrabutyl silicate, ethyl orthogermanate, triethyl phosphate, tripropyl phosphate, tributyl phosphate, tri-n-pentyl phosphate, trihexyl phosphate, aluminium ethoxide, aluminum isopropoxide, aluminum n-butoxide, aluminum tert-butoxide, tetraethyl titanate, tetraisopropyl titanate, tetrabutyl titanate, tetrahexyl titanate, tetraisooctyl titanate, tetrabutyl ferrite, tetrabutyl stannate, butyl orthovanadate, gallium ethoxide, tetra-n-propyl zirconate, tetrabutyl zirconate, tert-butyl chromate, ethyl antimonite, butyl antimonate, tungsten ethoxide and tungsten isopropoxide.

[0060] Optionally, the formula of the polyhydric alcohol in step a) is R-(OH) x , wherein x ≥ 2; the polyhydric alcohol comprises at least one of ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,4-butylene glycol, 1,6-hexanediol, polyethylene glycol 200, polyethylene glycol 400, polyethylene glycol 600, polyethylene glycol 800, 1,4-cyclohexanediol, 1,4-cyclohexane dimethanol, terephthalyl alcohol, glycerin, trimethylolpropane, pentaerythritol, xylitol and sorbitol.

[0061] Optionally, in the step a), the molar ratio of the inorganic oxyacid ester to the polyhydric alcohol satisfies: M(OR) n / R-(OH) x = (0.8~1.2)x / n.

[0062] Optionally, the transesterification catalyst used in the step a) is: a basic catalyst including bases that are easily soluble in alcohol (such as NaOH, KOH, NaOCH 3 , organic bases and so on) and various solid base catalysts; and an acidic catalyst including acids that are easily soluble in alcohol (such as sulfuric acid, sulfonic acid and so on) and various solid acidic catalysts, aluminum alkoxide, aluminum phenoxide, tetrabutyl stannate, titanium alkoxide, zirconium alkoxide, ethyl antimonite, butyl antimonite and so on; and the amount of the transesterification catalyst is in a range from 0.1wt% to 5wt% of the inorganic oxyacid ester.

[0063] Optionally, the step a) is carried out under nitrogen protection, the reaction temperature thereof ranges from 80 to180 °C, and the reaction time thereof ranges from 2 to 10 hours.

[0064] Optionally, the conversion rate of the transesterification in step a) ranges from 60% to 80%.

[0065] Optionally, the step b) is carried out under vacuum distillation conditions, and the vacuum degree thereof ranges from 0.01 to 5kPa.

[0066] Optionally, in step b), the reaction temperature ranges from 170 to 230°C, and the reaction time ranges from 0.5 to 5 hours.

[0067] Optionally, the conversion rate of the transesterification in step b) is greater than 90%.Example 1

[0068] 10g 1,3-propanediol, 6.84g tetraethyl orthosilicate and 5g tetramethoxysilane are added to a three-necked flask which is connected to a distillation device. 0.12g concentrated sulfuric acid as catalyst is added dropwise in the three-necked flask under stirring condition. The temperature is heated up to 100°C under nitrogen protection, and the reaction time is 6 hours. During this process, a large amount of methanol and ethanol are distilled out, and the conversion rate of the transesterification reaction is 75%. Then a vacuum device is connected to distillation device and the transesterification continues under vacuum distillation conditions, wherein the vacuum degree of the reaction system was controlled to be 1kPa and the temperature was raised to 170°C.After reacting for 1 hour, the transesterification is stopped. After the temperature is naturally cooled to be room temperature, the resulting sample is taken, and the conversion rate of the transesterification is 93%.Example 2

[0069] 5g ethylene glycol and 8.7g aluminum ethoxide are added to a three-necked flask which is connected to a distillation device, wherein the aluminum ethoxide is used not only as an inorganic oxyacid salt raw material, but also as a transesterification catalyst. The temperature is heated up to 175°C under nitrogen protection and stirring condition, and the reaction time is 5 hours. During this process, a large amount of ethanol is distilled out, and the conversion rate of the transesterification reaction is 73%. Then a vacuum device is connected to distillation device and the transesterification continues under vacuum distillation conditions, wherein the vacuum degree of the reaction system was controlled to be 0.1kPa and the temperature was raised to 210°C.After reacting for 1 hour, the transesterification is stopped. After the temperature is naturally cooled to be room temperature, the resulting sample is taken, and the conversion rate of the transesterification is 92%.Example 3

[0070] 10g terephthalyl alcohol and 9.07g tripropyl borate are added to a three-necked flask which is connected to a distillation device. 0.05g tetrabutyl titanate as catalyst is added dropwise in the three-necked flask under stirring condition. The temperature is heated up to 180°C under nitrogen protection, and the reaction time is 6 hours. During this process, a large amount of propanol is distilled out, and the conversion rate of the transesterification reaction is 75%. Then a vacuum device is connected to distillation device and the transesterification continues under vacuum distillation conditions, wherein the vacuum degree of the reaction system was controlled to be 1kPa and the temperature was raised to 230°C. After reacting for 1 hour, the transesterification is stopped. After the temperature is naturally cooled to be room temperature, the resulting sample is taken, and the conversion rate of the transesterification is 93%.Examples 4 to 13

[0071] The specific raw materials, amounts thereof and reaction conditions different from Example 1 are shown in Table 1 below, and the other procedures are the same as those in Example 1. Table 1 Raw materials, amounts thereof and reaction conditions of Examples 4 to 13Example NumberTransesterificationVacuum distillationInorganic oxyacid esterPolyhydric alcoholCatalystReaction temperatureReaction timeVacuum degreeReaction temperatureReaction time4Tetrahexyl titanate, 0.1molDiethylene glycol, 0.2molNaOH, 0.03g80°C10 hours5kPa180°C2 hours5Triethyl phosphate, 0.2molPolyethylene glycol 200, 0.3molNa 2 CO 3 , 0.1g100°C5 hours2kPa200°C0.5 hours6Tetrabutyl stannate, 0.15molTrimethylolpropane, 0.2molSulfonic acid, 0.06g150°C2 hours0.01kPa175°C5 hours7Tungsten ethoxide, 0.2molXylitol, 0.1molTetrabutyl stannate, 0.02gThe one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 18Tetrabutyl ferrite, 0.1mol1,4-butanediol, 0.2molEthyl antimonite, 0.04gThe one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 19Butyl orthovanadate, 0.1molGlycerol, 0.2molButyl antimonite, 0.02gThe one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 110Gallium ethoxide, 0.4molPentaerythritol, 0.3molThe one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 111Tetra-n-propyl zirconate, 0.2molCyclohexanediol, 0.4molThe one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 112Tert-Butyl chromate, 0.1molThe one in Example 1, 0.1molThe one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 113Ethyl antimonite, 0.4molThe one in Example 1, 0.3molThe one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 1The one in Example 1 Example 5 Thermogravimetric Analysis

[0072] The polyester polyol prepared in Example 1 to Example 13 are subjected to thermogravimetric analysis respectively, results of which are typically shown in Figures 1 and 2. Figure 1 shows the thermal analysis curve of the polyester polyol prepared in Example 1. It can be seen from the figure that the initial decomposition temperature of the polyester polyol prepared in Example 1 is 500°C.

[0073] Figure 2 shows the thermal analysis curve of the polyester polyol prepared in Example 2. It can be seen from the figure that the initial decomposition temperature of the polyester polyol prepared in Example 2 is 500°C.

[0074] The results of the polyester polyol prepared in other examples are similar to the above, and the initial decomposition temperature of the polyester polyol is higher than 300°C.

[0075] The above examples are only illustrative, and do not limit the present application in any form. Any change or modification, made by the skilled in the art based on the technical content disclosed above, without departing from the spirit of the present application, is equivalent example and falls within the scope of the present application.

Claims

1. A method for preparing polyester polyol comprising following steps: a) mixing inorganic oxyacid ester, polyhydric alcohol as raw materials and transesterification catalyst, and then performing the transesterification under stirring conditions and in an inactive protection atmosphere, wherein the reaction temperature ranges from 80 to 180°C, and the reaction time ranges from 2 to 10 hours; b) after the reaction in step a), performing vacuum distillation during which the vacuum degree ranges from 0.01 to 5kPa, the reaction temperature ranges from 170 to 230 °C, and the reaction time ranges from 0.5 to 5 hours; wherein a molar ratio of inorganic oxyacid ester, polyhydric alcohol and transesterification catalyst satisfies: inorganic oxyacid ester: polyhydric alcohol = (0.8~1.2)n3 / x, wherein x is the number of moles of alkoxyl groups contained in each mole of inorganic oxyacid ester, and n3 is the number of moles of hydroxyl groups contained in each mole of polyhydric alcohol.

2. The method according to claim 1, wherein the inorganic oxyacid ester is at least one of compounds having a chemical formula shown in Formula I and Formula II,         M(OR1)n1     Formula I         O=P (OR2)n2     Formula II wherein, M is a metal element or a non-metal element that does not include P, R1 and R2 are independently selected from at least one of C1 to C8 alkyl groups, n1 =2~8, n2 =2~ 8.

3. The method according to claim 2, wherein M is B, Si, Ge, Al, Ti, Fe, Sn, V, Ga, Zr, Cr, Sb or W.

4. The method according to claim 1 or 2, wherein inorganic oxyacid ester comprises at least one of trimethyl borate, triethyl borate, tripropyl borate, tributyl borate, tri-n-hexyl borate, triisooctyl borate, trioctyl borate, tetramethoxysilane, tetraethyl orthosilicate, tetrapropyl silicate, tetrabutyl silicate, ethyl orthogermanate, triethyl phosphate, tripropyl phosphate, tributyl phosphate, tri-n-pentyl phosphate, trihexyl phosphate, aluminium ethoxide, aluminum isopropoxide, aluminum n-butoxide, aluminum tert-butoxide, tetraethyl titanate, tetraisopropyl titanate, tetrabutyl titanate, tetrahexyl titanate, tetraisooctyl titanate, tetrabutyl ferrite, tetrabutyl stannate, butyl orthovanadate, gallium ethoxide, tetra-n-propyl zirconate, tetrabutyl zirconate, tert-butyl chromate, ethyl antimonite, butyl antimonate, tungsten ethoxide and tungsten isopropoxide.

5. The method according to claim 1, wherein the number of hydroxyl groups in the polyhydric alcohol is not less than two.

6. The method according to claim 1 or 5, wherein the polyhydric alcohol comprises at least one of ethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,4-butylene glycol, 1,6-hexanediol, polyethylene glycol 200, polyethylene glycol 400, polyethylene glycol 600, polyethylene glycol 800, 1,4-cyclohexanediol, 1,4-cyclohexane dimethanol, terephthalyl alcohol, glycerin, trimethylolpropane, pentaerythritol, xylitol and sorbitol.

7. The method according to claim 1, wherein an amount of the transesterification catalyst is in a range from 0.1wt% to 5wt% of the inorganic oxyacid ester.

8. The method according to claim 7, wherein the transesterification catalyst is at least one of acidic catalyst and basic catalyst.

9. The method according to claim 8, wherein the acidic catalyst comprises at least one of alcohol-soluble acid, solid acid, aluminum alkoxide, aluminum phenoxide, tetrabutyl stannate, titanium alkoxide, zirconium alkoxide, ethyl antimonite and butyl antimonite; and the basic catalyst comprises at least one of alcohol-soluble base and solid base.

10. The method according to claim 1, wherein an initial decomposition temperature of the polyester polyol is higher than 300°C measured as indicated in the description.

11. The method according to claim 10, wherein the initial decomposition temperature of the polyester polyol reaches 500°C measured as indicated in the description.