Heat-shrinkable film and manufacturing process for it

Description

Technical Field

[0001] Embodiments relate to a heat shrinkable film, which has a low heat shrinkage in the direction perpendicular to the main shrinkage direction, the heat shrinkage being not high even at a high temperature of 70°C or higher, and which is printable thereon, and a process for preparing the same.Background Art

[0002] A heat shrinkable film refers to a film that tends to shrink to a shape before stretching thereof at a certain temperature or higher once it has been oriented by stretching thereof. A heat shrinkable film is used for shrinkable labels for various types of containers, bundle packaging, or cap seals.

[0003] Polyvinyl chloride (PVC) films and oriented polystyrene (OPS) films have been used as heat shrinkable films for a long period of time. However, the use of PVC heat shrinkable films has been regulated due to a problem of environmental pollution since they generate poisonous dioxins when incinerated. OPS heat shrinkable films have a disadvantage in that it is not suitable for shrinkable labels for glass, metal cans, or the like since they have an insufficient heat resistance.

[0004] Hence, polyester-based heat shrinkable films having a high shrinkage and a high heat resistance have been developed to address the disadvantages of the PVC and OPS heat shrinkable films.

[0005] EP 2631261 describes a heat-shrinkable polyester film having a heat shrinkage initiation temperature of 60 °C or lower, a glass transition temperature (Tg) of 77 °C or lower and a heat shrinkage rate of 2% or more at 60 °C.

[0006] EP 2365025 describes a heat-shrinkable polyester film having a heat shrinkage change per degree Celsius (% / °C) along the main shrinkage direction of 1.5 to 3.0 in the range of 60 °C to 70 °C, 2.5 to 3.5 in the range of 70°C to 80 °C, 1.0 to 2.0 in the range of 80°C to 90 °C and 0.1 to 1.0 in the range of 90°C to 100 °C.

[0007] EP 1418042 describes heat-shrinkable polyester films having a content of 1,4-cyclohexane dimethanol of 10 to 50 % by mole based on the polyhydric alcohol component and wherein the heat shrinkage factors of a 10 cm square sample of the films in (A) hot water of 75 °C, (B) hot water of 85 °C and (C) hot water of 95 °C are 30 to 40 %, 50 to 60 % and 65 to 77 %, respectively.

[0008] EP 0349960 describes a heat-shrinkable polyester film having a shrinkage of not less than 40% after 5-minute treatment in a 100 °C air oven in one of the machine and transverse directions, and a shrinkage of not more than 15% after 5-minute treatment in a 100 °C air oven and a maximum shrinkage stress of not more than 50 g / mm 2< at 40 to 100 °C in the other direction.

[0009] Such a polyester-based heat shrinkable film can be used for metallic food containers. Since a food container has a direct impact on the human body, the container is subjected to a sterilization process at a high temperature for a predetermined time once the film has been applied to the container. In such event, however, a film applied to the surface of a food container by taking advantage of the mechanism that the film shrinks in the main shrinkage direction may also shrink in the direction perpendicular to the main shrinkage direction. This causes deformation, giving birth to a problem that the film fails to conform to the surface shape of the food container.

[0010] Accordingly, there has been a demand for a polyester-based heat shrinkable film, which has a heat shrinkage in the direction perpendicular to the main shrinkage direction that is not high even at a high temperature.Detailed Description of Invention Technical Problem

[0011] In order to meet the above demand, the embodiments aim to provide a heat shrinkable film, which has a low heat shrinkage in the direction perpendicular to the main shrinkage direction, the heat shrinkage being not high even at a high temperature of 70°C or higher, and which is printable thereon, and a process for preparing the same.Solution to Problem

[0012] According to an embodiment, there is provided a heat shrinkable film, which comprises a polyester resin, wherein the polyester resin consists in a dicarboxylic acid component and a diol component, wherein the dicarboxylic acid component is terephthalic acid (TPA) and wherein the diol component consists of ethylene glycol (EG), diethylene glycol (DEG) and neopentyl glycol (NPG), wherein the content of ethylene glycol is 50 to 80 wt% by mole based on the total number of moles of the diol component, the content of diethylene glycol is 5 to 15% by mole based on the total number of moles of the diol component, the content of neopentyl glycol is 22 to 30% by mole based on the total number of moles of the diol component, and the heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction satisfy the following Relationships 1 and 2: − 15 % ≤ Δ T 70 − 65 ≤ 0 % 0 % ≤ Δ T 100 − 95 ≤ 5 % wherein △T X-Y is a value obtained by subtracting the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at Y°C from the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at X°C.

[0013] According to another embodiment, there is provided a process for preparing a heat shrinkable film as hereinbefore defined, which comprises preparing a polyester resin composition; extruding the composition to obtain an unstretched sheet; preheating the unstretched sheet at a preheating temperature (T1) of 100 to 110°C; stretching the preheated unstretched sheet in one direction to obtain a stretched sheet; thermally treating the stretched sheet at a thermal treatment temperature (T2) of 70 to 98°C; and cooling the thermally treated and stretched sheet to prepare the heat shrinkable film.Effects of Invention

[0014] The heat shrinkable film according to the embodiment has an excellent shrinkage in the main shrinkage direction and a low heat shrinkage in the direction perpendicular to the main shrinkage direction, wherein this heat shrinkage is not high even at a high temperature of 70°C or higher. Thus, even if the film applied to the surface of a food container is subjected to a sterilization process, it is not deformed. Therefore, the film can be advantageously used for food containers.

[0015] In addition, the heat shrinkable film according to the embodiment is printable thereon. Thus, it is possible to remove the inconvenience of printing on the surface of the container in a conventional way, resulting in an advantage that the container can be readily recycled.

[0016] Further, the process for preparing a heat shrinkable film according to the embodiment can provide a heat shrinkable film, which has a heat shrinkage in the direction perpendicular to the main shrinkage direction that is not high even at a high temperature and which is printable thereon. Since the film can serve as an economical and environmentally friendly film, it can be used in various ways.Best Mode for Carrying out the Invention

[0017] Hereinafter, the present invention will be described in detail with reference to embodiments.

[0018] Throughout the description of the embodiments, the term "comprise" means that other elements may be included unless otherwise indicated.<Heat Shrinkable Film>

[0019] An embodiment provides a heat shrinkable film, which has a low heat shrinkage in the direction perpendicular to the main shrinkage direction, the heat shrinkage being not high even at a high temperature, and which is printable thereon.

[0020] The heat shrinkable film according to the embodiment comprises a polyester resin.

[0021] The polyester resin consists in a dicarboxylic acid component and a diol component.

[0022] The dicarboxylic acid component is terephthalic acid.

[0023] The diol component consists of ethylene glycol (EG), diethylene glycol (DEG), and neopentyl glycol (NPG).

[0024] The content of ethylene glycol in the diol component is 50 to 80% by mole based on the total number of moles of the diol component. Specifically, the content of ethylene glycol may be 50 to 77% by mole, 60 to 75% by mole, 65 to 75% by mole, 65 to 71% by mole, or 69 to 71% by mole, based on the total number of moles of the diol component. But it is not limited thereto.

[0025] The content of diethylene glycol in the diol component is 5 to 15% by mole based on the total number of moles of the diol component. Specifically, the content of diethylene glycol may be 5 to 10% by mole, or 3 to 7% by mole, based on the total number of moles of the diol component. But it is not limited thereto.

[0026] Specifically, the content of neopentyl glycol in the diol component is 22 to 30 % by mole based on the total number of moles of the diol component. Specifically, the content of neopentyl glycol in the diol component may be 24 to 30% by mole, 22 to 26% by mole, or 24 to 26% by mole, based on the total number of moles of the diol component. But it is not limited thereto.

[0027] If the content of neopentyl glycol satisfies the above range, a heat shrinkable film having a heat shrinkage in the direction perpendicular to the main shrinkage direction that is not high even at a high temperature can be prepared. In particular, if the content of neopentyl glycol exceeds the above range, the film may excessively expand in the direction perpendicular to the main shrinkage direction, so that wrinkles or deformation may occur when the film is applied to a container. Specifically, if the content of neopentyl glycol exceeds the above range, the amorphous region is unnecessarily larger, whereby the expansion coefficient would be increased due to low shrinkage characteristics in the direction perpendicular to the main shrinkage direction although the shrinkage characteristics in the main shrinkage direction could be improved.

[0028] The dicarboxylic acid component and the diol component may be subjected to a transesterification reaction and then polymerization to thereby form a copolymerized polyester resin.

[0029] The heat shrinkable film according to an embodiment has heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction, which satisfy the following Relationships 1 and 2: − 15 % ≤ ΔT 70 − 65 ≤ 0 % 0 % ≤ ΔT 100 − 95 ≤ 5 % wherein △T X-Y is a value obtained by subtracting the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at Y°C from the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at X°C.

[0030] That is, △T 70-65 refers to a value obtained by subtracting the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at 65°C from the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at 70°C.

[0031] In addition, △T 100-95 refers to a value obtained by subtracting the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at 95°C from the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at 100°C.

[0032] The heat shrinkage is calculated by the equation of (a - b) / a × 100 in the unit of percent once the length (a) of a sample before being immersed in the hot water tank and the length (b) of the sample after being immersed in the hot water tank for 10 seconds have been measured.

[0033] That is, if b is smaller than a, it means that the sample shrinks when immersed in the hot water tank, and the heat shrinkage would have a positive value. On the other hand, if b is larger than a, it means that the sample expands when immersed in the hot water tank, and the heat shrinkage would have a negative value. If a heat shrinkage is negative, the (heat) expansion has the same absolute value with the opposite sign. For example, when a heat shrinkage is -10%, the (heat) expansion is 10%.

[0034] In an embodiment, the maximum expansion in the direction perpendicular to the main shrinking direction of the heat shrinkable film may be 3 to 15%. Specifically, the maximum expansion in the direction perpendicular to the main shrinkage direction of the heat shrinkable film may be 3 to 12%, 5 to 12%, 5 to 11%, 5 to 10%, 5 to 8%, or 7 to 8%, but it is not limited thereto.

[0035] If the maximum expansion in the direction perpendicular to the main shrinkage direction of the heat shrinkable film is within the above range, even if the film applied to the surface of a food container is subjected to a sterilization process for a predetermined period of time at a high temperature, the film can be adhered to the surface of the container in a desired shape without significant deformation. Further, as a slight shrinkage occurs in the main shrinkage direction during the sterilization process at a high temperature, an insufficient shrinkage, if any, in the previous shrinkage step could be compensated.

[0036] The maximum expansion is calculated from the minimum value of the heat shrinkage measured in the direction perpendicular to the main shrinkage direction after the film has been immersed in a water bath for 10 seconds at a specific temperature (for example, at a 5°C interval between 50 and 100°C).

[0037] According to an embodiment, when the heat shrinkage in the direction perpendicular to the main shrinkage direction of the heat shrinkable film is measured at an interval of 5°C between 50°C and 100°C, the minimum value of the heat shrinkage may be present between 70°C and 90°C. In other words, the heat shrinkable film may have a maximum expansion that is present between 70°C and 90°C.

[0038] Specifically, the heat shrinkable film may have a maximum expansion between 75°C and 90°C. More specifically, the heat shrinkable film may have a maximum expansion between 75°C and 85°C.

[0039] With respect to the heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction, the heat shrinkable film according to another embodiment may satisfy that T 75 is -12 to 0%, that T 80 is -15 to 0%, that T 85 is -10 to 0%, and optionally that T 90 is -10 to 5%.

[0040] In the above, T Z refers to a heat shrinkage in the direction perpendicular to the main shrinkage direction after the heat shrinkable film has been immersed in a water bath for 10 seconds at Z°C.

[0041] Specifically, T 75 may be -12 to -3%, -12 to -5%, -10 to -5%, -9 to -5%, -10 to -6%, or -8 to -6%.

[0042] In addition, T 80 may be -12 to -0.5%, -12 to -2%, -12 to -2.5% -12 to -3%, -10 to - 2.5%, -8 to -2.5%, -7 to -2.5%, or -7 to -3%.

[0043] In addition, T 85 may be -9 to -0.2%, -7 to -0.2%, -5 to -0.5%, -5 to -0.7%, -4.5 to - 0.7%, or -4.3 to -0.7%.

[0044] In addition, T 90 may be -10 to 2%, -7 to 2%, -7 to 1%, -3 to 1.5%, -2 to 1%, or -2 to 0.5%.

[0045] With respect to the heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction, the heat shrinkable film according to another embodiment may satisfy that all of T 75 , T 80 , and T 85 are less than 0%.

[0046] If the heat shrinkable film satisfies that T 75 , T 80 , and T 85 are within the above range with respect to the heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction, the shrinkage characteristics of the film are optimized for the shape of a bottle when it is used as a general heat shrinkable film. Further, the shrinkage in the direction perpendicular to the main shrinkage direction is less likely to occur in the sterilization process under the high-temperature and high-pressure conditions.

[0047] According to an embodiment, the heat of crystallization (ΔHc) of the heat shrinkable film as measured by differential scanning calorimetry (DSC) may be 0 to 30 J / g. Specifically, the heat of crystallization (ΔHc) of the heat shrinkable film as measured by differential scanning calorimetry (DSC) may be 0 to 27 J / g, 0 to 20 J / g, 0 to 15 J / g, 0 to 10 J / g, 0 to 5 J / g, 0 to 2 J / g, or 0 to 1 J / g, but it is not limited thereto.

[0048] The heat of crystallization (ΔHc) refers to the amount of heat generated during crystallization as measured by differential scanning calorimetry (DSC). Specifically, the larger the heat of crystallization, the higher the crystallinity of the film. If the heat of crystallization is within the above range, it indicates that the film has a structure close to being amorphous. For example, if the heat of crystallization (ΔHc) is 0 J / g, it means that the film is composed of an amorphous structure having no crystallinity.

[0049] The heat shrinkable film according to another embodiment may have heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction that satisfy the following Relationships 1a and 2a: − 10 % ≤ ΔT 70 − 65 ≤ 0 % 0 % ≤ ΔT 100 − 95 ≤ 2 %

[0050] Specifically, the heat shrinkable film may have heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction that satisfy the following Relationships 1b and 2b: − 8 % ≤ ΔT 70 − 65 ≤ − 1 % 0.2 % ≤ ΔT 100 − 95 ≤ 1 %

[0051] More specifically, the heat shrinkable film may have heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction that satisfy the following Relationships 1c and 2c: − 6 % ≤ ΔT 70 − 65 ≤ − 1.2 % 0.2 % ≤ ΔT 100 − 95 ≤ 0.7 %

[0052] If the heat shrinkage characteristics of the heat shrinkable film in the direction perpendicular to the main shrinkage direction satisfy the above-mentioned conditions, the film may shrink in conformation to the shape and size of a container. Thus, it can properly adhere to the surface shape of the container.

[0053] Various characteristics such as the constituent components of the heat shrinkable film and the physical properties of the heat shrinkable film may be combined.<Process for Preparing a Heat Shrinkable Film>

[0054] The process for preparing a heat shrinkable film according to an embodiment comprises preparing a polyester resin composition; extruding the composition to obtain an unstretched sheet; preheating the unstretched sheet at a preheating temperature (T1) of 100 to 110°C; stretching the preheated unstretched sheet in one direction to obtain a stretched sheet; thermally treating the stretched sheet at a thermal treatment temperature (T2) of 70 to 98°C; and cooling the thermally treated and stretched sheet to prepare the heat shrinkable film.

[0055] The process for preparing a heat shrinkable film, which has a heat shrinkage in the direction perpendicular to the main shrinkage direction that is not high even at a high temperature and which is printable thereon, is described in detail, as follows.

[0056] First, a polyester resin composition is prepared.

[0057] The polyester resin contained in the polyester resin composition consists in a dicarboxylic acid component and a diol component. The dicarboxylic acid component and the diol component may be mixed and subjected to a transesterification reaction.

[0058] In such event, at least one catalyst selected from manganese acetate, calcium, and zinc may be used as a catalyst for the transesterification reaction. The amount of the catalyst used is preferably 0.02 to 0.2 part by weight based on 100 parts by weight of the dicarboxylic acid compound.

[0059] Upon completion of the transesterification reaction, at least one additive selected from silica, potassium, and magnesium; a stabilizer such as trimethyl phosphate; a polymerization catalyst selected from antimony trioxide and tetrabutylene titanate; and the like may be selectively added to carry out the reaction, to thereby prepare a copolymerized polyester resin composition.

[0060] For details on the polyester resin, the dicarboxylic acid component, and the diol component, the reader is referred to those described in the above section of<Heat Shrinkable Film>.

[0061] Next, the composition is extruded to obtain an unstretched sheet.

[0062] The composition may be extruded through a T-die at an extrusion temperature of 260 to 300°C or 270 to 290°C and then cooled.

[0063] The unstretched sheet obtained by extruding and cooling the composition may be fed to, and passed through, a roll at a speed of 50 m / min to 100 m / min or 50 m / min to 80 m / min.

[0064] In such event, the desired thickness of the film can be adjusted by controlling the feed speed of the unstretched sheet. For example, the thickness of the film may be adjusted to 35 to 75 µm or 40 to 50 µm at this step.

[0065] Then, the unstretched sheet is preheated at a preheating temperature (T1) of 100 to 110°C.

[0066] Specifically, the preheating temperature (T1) may be 103 to 107°C or 104 to 106°C.

[0067] In addition, the preheating time at the preheating temperature (T1) may be 0.01 to 1 minute. Specifically, the preheating time may be 0.05 to 0.5 minutes or 0.08 to 0.2 minutes, but it is not limited thereto.

[0068] Next, the preheated unstretched sheet is stretched in one direction to obtain a stretched sheet.

[0069] The stretching may be carried out at a temperature lower than the preheating temperature (T1) by 20°C or more. Specifically, the stretching temperature may be 60 to 90°C, 70 to 90°C, or 80 to 90°C, but it is not limited thereto.

[0070] The stretching may be carried out at a stretching ratio of 3 to 5 times in one direction at the stretching temperature. Specifically, the stretching may be carried out at a stretching ratio of 3 to 4.5 times, 3.5 to 4.5 times, or 4 to 4.5 times in one direction, but it is not limited thereto.

[0071] Then, the stretched sheet is thermally treated at a thermal treatment temperature (T2) of 70 to 98°C.

[0072] Specifically, the thermal treatment temperature (T2) may be 70 to 95°C, 70 to 90°C, 70 to 85°C, or 70 to 80°C, but it is not limited thereto.

[0073] According to an embodiment, the preheating temperature (T1) - the thermal treatment temperature (T2) is preferably 10 to 40°C. For example, T1 - T2 may be 13 to 35°C, 11 to 34°C, 15 to 34°C, or 20 to 34°C.

[0074] If T1 - T2 satisfies the above range, the shrinkage in the main shrinkage direction and the heat shrinkage in the direction perpendicular to the main shrinkage direction can be controlled.

[0075] In addition, the thermal treatment time at the thermal treatment temperature (T2) may be 0.01 to 1 minute. Specifically, the thermal treatment time may be 0.05 to 0.5 minute or 0.08 to 0.2 minute, but it is not limited thereto.

[0076] Even if a film is produced using the same dicarboxylic acid and diol components in the same amounts, the physical properties of the film thus produced may be significantly different depending on the specific process steps.

[0077] A heat shrinkable film that has a heat shrinkage in the direction perpendicular to the main shrinkage direction at a desired level and is printable thereon can be prepared through the process steps according to the embodiment.

[0078] Next, the thermally treated and stretched sheet is cooled to prepare the heat shrinkable film.

[0079] The heat shrinkable film may be continuously produced through the above-described process.

[0080] Then, the process may further comprise the step of winding the cooled heat shrinkable film into a roll shape.

[0081] In addition, the process may further comprise the step of printing on the heat shrinkable film. At this time, the printing step may be performed before or after the step of winding the heat shrinkable film.

[0082] Since the heat shrinkable film has amorphous character, it is possible to directly print on the film itself.

[0083] In a conventional process, a heat shrinkable film is normally applied to the surface of a container once the surface of the container has been printed. This inconveniently involves the removal of the film and the printing in order to recycle the container.

[0084] In contrast, the heat shrinkable film prepared according to the embodiment is printable thereon. Thus, it has an advantage that the container can be readily recycled.

[0085] For details on the heat shrinkable film prepared according to the process for preparing a heat shrinkable film, the reader is referred to those described in the above section of <Heat Shrinkable Film>.

[0086] For example, the heat shrinkable film prepared by the process for preparing a heat shrinkable film comprises a polyester resin and has heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction that satisfy the above Relationships 1 and 2.

[0087] In addition, various characteristics such as the constituent components of the heat shrinkable film and the physical properties of the heat shrinkable film may be combined.Embodiments for Carrying Out the Invention [Example]

[0088] Hereinafter, the present invention will be described in more detail with reference to the following examples. However, these examples are set forth to illustrate the present invention, and the scope of the present invention is not limited thereto.Examples 1 to 7 and Comparative Examples 1 and 2

[0089] The dicarboxylic acid component and the alcohol component in the kinds and contents shown in Table 1 below were charged to an autoclave equipped with a stirrer and a distillation tower. In addition, 0.007 parts by weight of manganese acetate as a transesterification catalyst was added per 100 parts by weight of the dicarboxylic acid component, followed by heating the mixture to 220°C and the removal of methanol produced as a byproduct to carry out the reaction.

[0090] Upon completion of the transesterification reaction, 0.07 part by weight of silica having an average particle diameter of 0.28 µm was added per 100 parts by weight of the dicarboxylic acid component, and 0.4 part by weight of trimethyl phosphate as a stabilizer was added. After 5 minutes, 0.035 part by weight of antimony trioxide and 0.005 part by weight of tetrabutylene titanate were added as a polymerization catalyst, followed by stirring for 10 minutes.

[0091] Subsequently, the reaction mixture was transferred to a second reactor equipped with a vacuum apparatus. The pressure was gradually reduced while the temperature was raised to 285°C, and the polymerization was carried out for about 210 minutes to thereby prepare a copolymerized polyester resin.

[0092] A composition containing the polyester resin thus obtained was extruded through a T-die at 270°C and then cooled to thereby obtain an unstretched sheet. The unstretched sheet was fed to, and passed through, a roll at a speed of 55 m / min to thereby adjust the thickness of the sheet. Then, the unstretched sheet was preheated at a preheating temperature (T1) of 100 to 110°C for 0.1 minute while it was transferred at a speed of 55 m / min.

[0093] Next, the unstretched sheet was stretched at a stretching ratio of 4 to 4.5 times in one direction at a stretching temperature lower than T1 by 20°C or more to thereby prepare a stretched sheet.

[0094] Then, the stretched sheet was subjected to thermal treatment at a thermal treatment temperature (T2) at which T1 - T2 satisfied the conditions shown in Table 2 below for 0.1 minute to thereby prepare a stretched sheet having a thickness of 40 µm.[Evaluation Example]Evaluation Example 1: Measurement of heat shrinkage amounts

[0095] Each film thus produced was cut into a length of 300 mm (a, length of the sample before being immersed in a hot water bath) and a width of 15 mm. The cut sample was immersed in a water bath heated to a specific temperature for 10 seconds, and the length of the sample was then measured. The heat shrinkage was calculated by the equation of (a - b) / a × 100. The results are shown in Table 2 below.Evaluation Example 2: Heat of crystallization (ΔHc) measured by DSC

[0096] A sample of each film thus produced was mounted on an equipment capable of measuring Tg, Tm, and Tc. The endotherm and exotherm of the sample were measured while the temperature was raised at a rate of 1°C / min to obtain a heat flow graph with respect to the temperature. The heat of crystallization (ΔHc) was measured from this graph. The results are shown in Table 2 below. [Table 1]Dicarboxylic acidAlcoholTPADEGEGNPGCHDMIPAEx. 110057124--Ex. 210057124--Ex. 310056926--Ex. 410056530--Ex. 510056530--Ex. 6*100565-30-Ex. 7*1001068-22-Ex. 8*10016314-22Ex. 910057124--C. Ex. 110057817--C. Ex. 210057817--*not in accordance with the invention [Table 2] T1 - T2 (°C)Heat flow on DSC (J / g)Heat shrinkage in the direction perpendicular to the main shrinkage direction (%)Max. expansion (%)ΔT 70-65 ΔT 100-95 75°C80°C85°C90°CEx. 1270-7-3-10.37-4.70.4Ex. 2200-6-7-4.3-27-1.40.7Ex. 3340-8-4-0.71.38-5.30.3Ex. 4230-11.7-7.7-1.3-0.711.7-4.41Ex. 5130-9.7-12-9-612-2.31Ex. 6*280-5-3-125-10Ex. 7*2100-1-5-3501Ex. 8*3527-3-2-1-0.33-1.40.8Ex. 9110-1.7-4-5-6.36.3-1.71C. Ex. 13546.8-2-1.70.72.320.40C. Ex. 22546.8-1-2-0.71.720-0.3 *not in accordance with the invention T1: preheating temperature T2: thermal treatment temperature

[0097] Heat shrinkage in the direction perpendicular to the main shrinkage direction: heat shrinkage in the direction perpendicular to the main shrinkage direction after the sample was immersed in a water bath for 10 seconds at a specific temperature

[0098] As confirmed from Tables 1 and 2, the specific dicarboxylic acid and diol components were employed in the specific amounts, and the preheating temperature and the thermal treatment temperature were adjusted to produce films in Examples 1 to 9. As a result, the heat of crystallization on DSC was 30 J / g or less, and the maximum expansion in the direction perpendicular to the main shrinkage direction was 3 to 15%, unlike Comparative Examples 1 and 2. Since the films had a heat expansion in the direction perpendicular to the main shrinkage direction that is not high at a high temperature, they are suitable as a shrinkable label for containers. The films are also economical since they are printable thereon.

Claims

1. A heat shrinkable film, which comprises a polyester resin, wherein the polyester resin consists in a dicarboxylic acid component and a diol component, wherein the dicarboxylic acid component is terephthalic acid (TPA) and wherein the diol component consists of ethylene glycol (EG), diethylene glycol (DEG) and neopentyl glycol (NPG), wherein the content of ethylene glycol is 50 to 80 wt% by mole based on the total number of moles of the diol component, the content of diethylene glycol is 5 to 15% by mole based on the total number of moles of the diol component, the content of neopentyl glycol is 22 to 30% by mole based on the total number of moles of the diol component, and the heat shrinkage characteristics in the direction perpendicular to the main shrinkage direction satisfy the following Relationships 1 and 2: − 15 % ≤ ΔT 70 − 65 ≤ 0 % 0 % ≤ ΔT 100 − 95 ≤ 5 % wherein △TX-Y is a value obtained by subtracting the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at Y°C from the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at X°C.

2. The heat shrinkable film of claim 1, whose maximum expansion in the direction perpendicular to the main shrinking direction is 3 to 15%.

3. The heat shrinkable film of claim 2, wherein the maximum expansion of the heat shrinkable film is present between 70°C and 90°C when the heat shrinkage of the heat shrinkable film in the direction perpendicular to the main shrinkage direction is measured at an interval of 5°C between 50°C and 100°C.

4. The heat shrinkable film of any one of the preceding claims, whose heat of crystallization (ΔHc) as measured by differential scanning calorimetry (DSC) is 0 to 30 J / g.

5. The heat shrinkable film of any one of the preceding claims, which satisfies that T75 is -12 to 0%, that T80 is -15 to 0%, and that T85 is -10 to 0%, wherein TZ refers to a heat shrinkage in the direction perpendicular to the main shrinkage direction after the heat shrinkable film is immersed in a water bath for 10 seconds at Z°C.

6. A process for preparing the heat shrinkable film of any one of claims 1-5, which comprises: preparing a polyester resin composition; extruding the composition to obtain an unstretched sheet; preheating the unstretched sheet at a preheating temperature (T1) of 100 to 110°C; stretching the preheated unstretched sheet in one direction to obtain a stretched sheet; thermally treating the stretched sheet at a thermal treatment temperature (T2) of 70 to 98°C; and cooling the thermally treated and stretched sheet to prepare the heat shrinkable film.

7. The process for preparing a heat shrinkable film of claim 6, wherein the extrusion is carried out at 260 to 300°C.

8. The process for preparing a heat shrinkable film of claim 6 or claim 7, wherein T1 - T2 is 10 to 40°C.

9. The process for preparing a heat shrinkable film of any one of claims 6-8, wherein the preheating is carried out for 0.01 to 1 minute.

10. The process for preparing a heat shrinkable film of any one of claims 6-9, wherein the stretching is carried out at a stretching ratio of 3 to 5 times in one direction.

11. The process for preparing a heat shrinkable film of any one of claims 6-10, further comprising printing on the heat shrinkable film.