COMPOSITION WITH (PER)FLUORPOLYETHERPOLYMERS

Description

Technical field

[0001] The present application claims priority filed on 12 January 2023 in Europe with Nr. 23151333.4.Technical field

[0002] The present invention relates to a composition comprising a (per)fluoropolyether polymer as base oil and a salt of a (per)fluoropolyether polymer as an additive, so that the composition has a volume resistivity suitable for use as lubricant.Background

[0003] (Per)fluoropolyether polymers (PFPEs) are a family of fluorinated synthetic fluids, which have been known for a long time and are used to formulate lubricants that function for long periods of time in extreme environments.

[0004] However, one problem with PFPE-based lubricants is that they are highly dielectric and have poor electrical conductivity. Furthermore, low polarity of the fluorinated PFPE lubricants leads to poor solubility and / or affinity with most additives. Therefore, tailoring the conductivity of PFPE lubricants has proven to be problematic because conductive additives, which are typically polar species, are immiscible with PFPE lubricants.

[0005] Accordingly, several methods have been tried in the art to tailor the conductivity of PFPE lubricants, for example as disclosed in US 2008 / 0144219 (in the name of HGST Netherlands BV).

[0006] Also, N Suhaila A Japar et al. (International Journal of Engineering & Technology, 7, 3.26, 2018, 23.29) in "Grease and its Application on Electrical Equipment: a Review" summarizes the findings in relation with the use of greases containing a PFPE as the base oil and solid particles (fumed silica or polytetrafluoroethylene - PTFE) as the thickener. WO 2017 / 012909 A1 relates to the use of (per)fluoropolyether polymers as anti-foam agents in compositions based on hydrogenated or fluorinated oils. WO 2017 / 012909 A1 discloses compositions of a neutral perfluoropolyether base oil and perfluoropolyether (PFPE) polymers containing carboxylic acid end-groups salified with organic or inorganic counter-ions. WO 2023 / 274821 A1 relates to copolymers comprising (per)fluoropolyether (PFPE) chains, in particular neutral block copolymers having increased viscosity. WO 2023 / 274821 A1 discloses block copolymers comprising first and second PFPE chains, each having two chain ends, wherein the PFPE chains are bonded to each other via a linking block. The copolymers are characterized by an increased complex viscosity while maintaining a low glass transition temperature. WO 2023 / 274823 A1 relates to copolymers comprising (per)fluoropolyether (PFPE) chains, in particular block copolymers having increased viscosity and suitable for use as lubricants. WO 2023 / 274823 A1 discloses block copolymers comprising first and second PFPE chains, each having two chain ends, wherein the PFPE chains are bonded to each other via at least one linking block. The copolymers are characterized by an increased complex viscosity while maintaining suitable thermal properties. US 2002 / 0127475 A1 relates to perfluoropolyether (PFPE) additives for electrochemical applications. In particular, US 2002 / 0127475 A1 discloses electrolytic compositions comprising a perfluoropolyether additive of defined structure, containing perfluoropolyether chains bearing sulphonate groups converted into corresponding salts with mono- or multivalent cations, such as alkali metal cations (e.g. Li +< ).Summary of the invention

[0007] The Applicant is aware that the presence of electrical components is continuously growing in many different industries and for a variety of applications. However, their exposure to harsh environments, including without limitation very high temperatures, moisture, and corrosion, can accelerate the failure of such electrical components. Also, such components can undergo electric arc discharge burnings, which cause burnings on the components and hence decrease their lifetime.

[0008] Hence, the Applicant faced the problem of providing a composition suitable to lubricate electrical components suitable for use in different applications and industries, such as in particular automotive and electronic industries.

[0009] Such composition needs to show good electric conductivity and hence reduced volume resistivity (also referred to as "electrical resistivity" or "electrical resistance"), good viscosity and high viscosity index ("as measured according to ASTM D227), as well as outstanding compatibility between the base oil and the additive(s).

[0010] The Applicant has surprisingly found a composition that meets the above mentioned requirements and can be hence used as such as lubricant for electrical and electronic components, including electrical connectors, switchgears and circuit breakers, as well as for mechanical components, in particular suitable for use in the automotive industry, including to lubricate parts used in electric vehicles, such as ball bearings.

[0011] Furthermore, the composition according to the present invention can be used to manufacture greases, which are suitable in the same applications.Disclosure of the invention

[0012] In the present application: the use of parentheses around symbols or numbers identifying the formulae, for example in expressions like "polymer (P)", etc., has the mere purpose of better distinguishing the symbol or number from the rest of the text and, hence, said parenthesis can also be omitted; the acronym "PFPE" stands for "(per)fluoropolyether" and, when used as substantive, is intended to mean either the singular or the plural form, depending on the contex-t; the prefix "(per)" in the term "(per)fluoropolyether" means that the polyether can be fully or partially fluorinated.

[0013] In a first aspect, the present invention relates to a composition [composition (COMP)] comprising: at least one block copolymer [PFPE copolymer] comprising a first and a second (per)fluoropolyether chain [PFPE chain] each having two chain ends, wherein the first chain end of said first and second PFPE chain comprises a perfluorinated alkyl group and the second chain end of said first and second PFPE chain are bonded to each other via: at least one first block [block (1)] complying with formula (I): wherein n is 0 or an integer from 1 to 3; R 1 to R 4 , each independently, is selected in the group comprising, preferably consisting of, fluorine atom, perfluorinated linear or branched alkyl group having from 1 to 6 carbon atoms, group of formula (II):         (II)     -(R 10 ) t [C(R 11 )(R 12 )-C(R 13 )(R 14 )(R 15 )] z wherein R 10 is an oxygen atom, or a bi- / tri- / tetravalent perfluorinated alkyl chain comprising from 1 to 24 carbon atoms optionally interrupted by and / or comprising at least one oxygen atom, t is zero or 1, z is an integer from 1 to 3; R 11 to R 15 , each independently, is selected in the group comprising, preferably consisting of, fluorine atom, perfluorinated linear or branched alkyl group having from 1 to 6 carbon atoms and group of formula (III):         -[(A^) a^ -(B^) v^ -(E^) L^]u^ -(C^)-T     (III) wherein a^ is zero or 1, v^ is zero or an integer from 1 to 3, L^ is zero or an integer from 1 to 250, u^ is zero or an integer from 1 to 50; A^ is a PFPE chain B^ is a group of formula:         -[C(R 1^ )(R 2^ )-C(R 3^ )(R 4^ )]- wherein R 1^ to R 4^ each independently has the meaning defined above for each of R 1 to R 4 , E^ is a group of formula -(CR 100^ R 101^ CR 102^ R 103^ )- wherein R 100^ and R 101^ are independently selected from hydrogen atom, halogen atom, more preferably fluorine or chlorine atom, and R 102^ and R 103^ are independently selected from hydrogen atom, halogen atom, more preferably fluorine or chlorine atom; linear or branched alkyl chain comprising from 1 to 6 carbon atoms, optionally containing at least one heteroatom selected from O, N and S; -OR 200 wherein R 200 is linear or branched perfluorinated chain comprising from 1 to 6 carbon atoms or a group of formula -CF 2 OR 201 in which R 201 is a perfluorinated alkyl chain comprising from 1 to 6 carbon atoms, optionally interrupted by one or more oxygen ether atoms; or one of R 100^ and R 101^ and one of R 102^ and R 103^ are a fluorine atom and the other of R 100^ and R 101^ and the other of R 102^ and R 103^ together form a perhalogenated cyclic ring having from 4 to 6 members, optionally comprising heteroatoms, such as oxygen atoms; C^ is a PFPE chain, and T is a perfluorinated alkyl group; at least one second block [block (2)] complying with formula (IV):         -[(CR 1*< R 2*< CR 3*< R 4*< ) n* -(E) L ]-     (IV) wherein n* is zero or an integer from 1 to 250, L is zero or an integer from 1 to 250 and the sum of n* and L is 0 or from 1 to 250; R 1*< and R 2*< are independently selected from hydrogen atom, halogen atom, more preferably fluorine or chlorine atom, and R 3*< and R 4*< are independently selected from hydrogen atom, halogen atom, more preferably fluorine or chlorine atom; linear or branched alkyl chain comprising from 1 to 6 carbon atoms, optionally containing at least one heteroatom selected from O, N and S; -OR 200 wherein R 200 is linear or branched perfluorinated chain comprising from 1 to 6 carbon atoms or a group of formula -CF 2 OR 201 in which R 201 is a perfluorinated alkyl chain comprising from 1 to 6 carbon atoms, optionally interrupted by one or more oxygen ether atoms; or one of R 1*< and R 2*< and one of R 3*< and R 4*< are a fluorine atom and the other of R 1*< and R 2*< and the other of R 3*< and R 4*< together form a perhalogenated cyclic ring having from 4 to 6 members, optionally comprising heteroatoms, such as oxygen atoms; E has the same meaning provided for E^ above; optionally, at least a third block [block (3)] comprising a PFPE chain; with the proviso that: in said PFPE copolymer: -- at least one of n, n* and L is different from 0; -- said block (1), said block (2) and when present said block (3) are statistically distributed; in said formula (I): -- at least one of R 1 to R 4 is a group of formula (II), -- one of R 11 or R 12 and one of R 13 to R 15 , is a group of formula (III); in said formula (III) and said formula (IV) -- the recurring units are statistically distributed, in said formula (III) -- when a^ is 1 at least one of v^ and L^ is different from 0; and up to 20.0 wt.% based on the total weight of composition (COMP) of at least one salt of a (per)fluoropolyether polymer [PFPE additive] comprising a (per)fluoropolyether backbone having two chain ends bonded to opposite sides of said backbone, wherein at least one chain end comprises at least one group selected from: (i) acid group selected from: -COO -< , wherein said acid group is salified with at least one inorganic metal salt or with an organic group selected from ammonium salt and phosphonium salt; (ii) ammonium group and at least one inorganic or organic counterion; wherein the sum of said PFPE copolymer and said PFPE additive add up to 100 wt.% of composition (COMP).

[0014] If required by the final application, composition (COMP) according to the present invention can contain at least one additional ingredient.

[0015] Such at least one additional ingredient can be selected in the group comprising: antirust, antioxidants, rheological modifiers, corrosion inhibitors, dyes, pigments.

[0016] Each of such at least one additional ingredient can be present in an amount from 0.1 to 15 wt.% based on the total weight of composition (COMP).

[0017] Advantageously, depending on the final application, composition (COMP) can be used as lubricant without the need of adding a solid additive. Hence, according to a preferred embodiment, composition (COMP) does not contain any solid additive, more in particular any additive in the form of solid particles.

[0018] Advantageously, said PFPE copolymer has a viscosity of at least 1,000 mm 2< / s, measured at 20°C according to standard methods, such as ASTM D445, or with a dynamical mechanical spectrometer Anton Paar MCR 502 rheometer equipped with parallel plates 25 mm, at 1 rad / s and at 25°C.

[0019] It will be understood by those skilled in the art that said first chain end of said first and second PFPE chain correspond to the two chain ends of the PFPE copolymer.

[0020] Preferably, said first chain end of said first and second PFPE chain comprise a perfluorinated linear alkyl group having from 1 to 3 carbon atoms.

[0021] Preferably, said perfluorinated alkyl groups are the same from each other.

[0022] Preferably, said first chain end of said first and second PFPE chain and said T in formula (III), equal or different from each other, are a perfluorinated alkyl group having from 1 to 3 carbon atoms.

[0023] For example, T and T', equal to or different from each other, are a fluorine atom or a group selected from -CF 3 , -CF 2 CF 3 , -CF 2 CF 2 CF 3 , -CF(CF 3 ) 2 . Other halogenated groups, such as for example -CF 2 Cl and -CF 2 CF 2 Cl, can still be present.

[0024] Preferably, in said first and second PFPE chain, A^ and C^ are equal or different from each other.

[0025] Preferably, in the PFPE copolymer, said first PFPE chain is bonded to said block (1) via a sigma bond or a group -(C)- selected from -CF 2 -, -CF 2 CF 2 - or - O-.

[0026] Preferably, in the PFPE copolymer, said block (2) is bonded to said second PFPE chain via a sigma bond or a group -(C)- selected from -CF 2 -, -CF 2 CF 2 - or -O-.

[0027] Preferably, when both said block (1) and said block (2) are present, they are linked via a sigma bond.

[0028] Preferably, in the PFPE copolymer, each of said PFPE chain is a partially or fully fluorinated chain [chain (R f )] comprising, preferably consisting of, repeating units R°, said repeating units being independently selected from the group consisting of: (i) -CFXO-, wherein X is F or CF 3 ; (ii) -CFXCFXO-, wherein X, equal or different at each occurrence, is F or CF 3 , with the proviso that at least one of X is -F; (iii) -CF 2 CF 2 CW 2 O-, wherein each of W, equal or different from each other, are F, Cl, H; (iv) -CF 2 CF 2 CF 2 CF 2 O-; (v) -(CF 2 ) w -CFZ-O- wherein w is an integer from 0 to 3 and Z is a group of general formula -O-R( f-a )-Y, wherein R( f-a ) is a fluoropolyoxyalkene chain comprising a number of repeating units from 0 to 10, said recurring units being chosen among the followings : -CFXO- , -CF 2 CFXO-, -CF 2 CF 2 CF 2 O-, - CF 2 CF 2 CF 2 CF 2 O-, with each of each of X being independently F or CF 3 and Y being a C 1 -C 3 perfluoroalkyl group.

[0029] Preferably, chain (R f ) complies with the following formulae (R f -I) and (R f -II):         (R f -I)     -[(CFX 1< O) g1 (CFX 2< CFX 3< O) g2 (CF 2 CF 2 CF 2 O) g3 (CF 2 CF 2 CF 2 CF 2 O) g4 ]- -wherein X 1< is independently selected from -F and -CF 3 , X 2< , X 3< , equal or different from each other and at each occurrence, are independently -F, -CF 3 , with the proviso that at least one of X is -F; g1, g2, g3, and g4, equal or different from each other, are independently ≥0, such that g1 +g2+g3+g4 is in the range from 2 to 300, preferably from 10 to 250, even more preferably from 15 to 200; should at least two of g1, g2, g3 and g4 be different from zero, the different recurring units are generally statistically distributed along the chain;         (R f -II)     -[(CFX 1< O) g1 (CFX 2< CFX 3< O) g2 (CF 2 CF 2 CF 2 O) g3 (CF 2 CF 2 CF 2 CF 2 O) g4 - (CF(CF 3 )O) g5 (CF 2 CF(CF 3 )O) g6 ]- wherein X 1< , X 2< , X 3< are as defined above; g1, g2, g3, g4, g5 and g6, equal or different from each other, are independently ≥0,such that g1 +g2+g3+g4+g5+g6 is in the range from 2 to 300, preferably from 10 to 250, with the proviso that at least one of g5 and g6 are different from 0.

[0030] In a preferred embodiment, chain (R f ) complies with formula (R f -I) above.

[0031] Preferably, in the PFPE copolymer, the sum of (n + n* + v^) is from 1 to 15, preferably from 1 to 11, more preferably from 1 to 9.

[0032] Preferably, in the PFPE copolymer, the sum of (L+L^) is from 1 to 500, preferably from 2 to 500, more preferably from 2 to 300,

[0033] According to a preferred embodiment, the PFPE copolymer comprises a first and a second PFPE chain, each having two chain ends, wherein the first chain end of said first and second PFPE chain comprises a perfluorinated alkyl group and the second chain end of said first and second PFPE chain are bonded to each other via: at least one block (2) complying with formula (IV):         -[(CR 1< *R 2< *CR 3< *R 4< *) n* -(E) L ]-     (IV) wherein n* is an integer from 1 to 250, L is an integer from 1 to 250, and the sum of n* and L is from 1 to 250; R 1*< and R 2*< are fluorine atom, and R 3*< and R 4*< are independently selected from halogen atom, more preferably fluorine or chlorine atom; linear or branched alkyl chain comprising from 1 to 6 carbon atoms, optionally containing at least one heteroatom selected from O, N and S; -OR 200 wherein R 200 is linear or branched perfluorinated chain comprising from 1 to 6 carbon atoms or a group of formula -CF 2 OR 201 in which R 201 is a perfluorinated alkyl chain comprising from 1 to 6 carbon atoms, optionally interrupted by one or more oxygen ether atoms; E is a group of formula -(CR 100^ R 101^ CR 102^ R 103^ )- wherein R 100^ and R 101^ are independently selected from halogen atom, preferably fluorine or chlorine atom, and R 102^ and R 103^ are independently selected from halogen atom, preferably fluorine or chlorine atom; -OR 200 wherein R 200 is linear or branched perfluorinated chain comprising from 1 to 6 carbon atoms or a group of formula -CF 2 OR 201 in which R 201 is a perfluorinated alkyl chain comprising from 1 to 6 carbon atoms, optionally interrupted by one or more oxygen ether atoms; and optionally, at least one block (3) comprising a PFPE chain.

[0034] The PFPE copolymer can be prepared via known processes, for example as disclosed in WO 2008 / 065163 (SOLVAY SOLEXIS S.P.A.) or via supercritical fluid fractionation.

[0035] The PFPE copolymer can be prepared via a process [process (P)], which comprises contacting: at least one (per)fluoropolyether polymer comprising peroxidic groups [PFPE peroxy]; with at least one perfluorinated compound of formula (X-p): wherein each of R 21 to R 23 and R 31 to R 33 is independently fluorine atom, perfluorinated alkyl group having from 1 to 3 carbon atoms, R 10 is an oxygen atom, or a perfluorinated alkyl chain comprising from 2 to 18 carbon atoms, optionally and preferably interrupted by and / or comprising at least one oxygen atom, t is zero or 1, preferably 1; each of z* and z** is independently 1 or 2; and / or at least one compound [compound (O)] selected in the group comprising, preferably consisting of: (i) hydrogenated or (per)halogenated olefin comprising from 2 to 8 carbon atoms, preferably ethylene (E), propylene (PP), tetrafluoroethylene (TFE), hexafluoropropylene (HFP), chlorotrifluoroethylene (CTFE), and 1,1- difluoroethylene (VDF); (ii) CF 2 =CFOR f , wherein R f is a C 1 -C 6 (per)fluoroalkyl group, preferably -CF 3 , -C 2 F 5 , -C 3 F 7 (also referred to as "PAVE" hereinafter); a group C 1 -C 12 [(per)fluoro]-oxyalkyl comprising catenary oxygen atoms, preferably perfluoro-2-propoxypropyl group (also referred to as "perfluoro-oxy-alkyl-vinyl ethers" hereinafter); a group -CF 2 OR f2 (also referred to as "perfluoro-methoxy-vinyl ethers" or "MOVE" hereinafter) wherein R f2 is selected from the group consisting of C 1 - C 6 perfluoro-alkyls; C 5 -C 6 cyclic perfluoro-alkyls, and C 2 -C 6 perfluoro-oxy- alkyls, comprising at least one catenary oxygen atom, preferably R f2 is - CF 2 CF 3 (MOVE1), -CF 2 CF 2 OCF 3 (MOVE2), or -CF 3 (MOVE3); (iii) perfluorodioxoles having formula : wherein each of R f3 , R f4 , R f5 , R f6 , equal to or different from each other, is independently selected from the group consisting of fluorine atom and C 1 -C 6 perfluoroalkyl groups, optionally comprising one or more than one oxygen atom, such as notably -CF 3 , -C 2 F 5 , -C 3 F 7 , -OCF 3 , -OCF 2 CF 2 OCF 3 , in the presence of UV radiation or under heating, provided that the amount of the compound of formula (X-p) is less than 5 wt.% of the amount of the PFPE peroxy.

[0036] The viscosity of the PFPE copolymer can be measured using different methods depending on the viscosity of the PFPE copolymer itself.

[0037] Preferably, said PFPE copolymer has a viscosity higher than 1,000 mm 2< / s at 20°C, more preferably higher than 2,000 mm 2< / s at 20°C and even more preferably higher than 3,000 mm 2< / s at 20°C.

[0038] Preferably, said PFPE copolymer has a viscosity lower than 5,000,000 mm 2< / s at 20°C, more preferably lower than 2,500,000 mm 2< / s at 20°C, and even more preferably lower than 2,000,000 mm 2< / s at 20°C.

[0039] Preferably, said PFPE copolymer has a viscosity of from 3,000 to 1,500,000 mm 2< / s at 20°C, more preferably of from 3,500 to 1,000,000 mm 2< / s at 20°C and even more preferably of from 4,000 to 950,000 mm 2< / s at 20°C .

[0040] The above viscosity of the PFPE copolymer according to the present invention was measured at 0°C according to standard methods, such as ASTM D445, or with a dynamical mechanical spectrometer Anton Paar MCR 502 rheometer equipped with parallel plates 25 mm, at 1 rad / s and at 25°C.

[0041] Preferably, said PFPE additive is in an amount of at least 0.1 wt.% based on the total weight of composition (COMP).

[0042] More preferably, said PFPE additive is in an amount from 0.1 to 20.0 wt.%, even more preferably from 0.5 to 15 wt.% and still more preferably from 1.0 to 12 wt.% based on the total weight of composition (COMP).

[0043] Preferably, in the PFPE additive (i), said acid group is a carboxylic group.

[0044] Such carboxylic group can be salified with any of the inorganic metal salt or the organic salt selected from ammonium salt and phosphonium salt.

[0045] Preferably, in the PFPE additive (i), said at least one inorganic metal salt is selected from alkaline metals. More preferably, said alkaline metals are selected in the group comprising sodium, potassium, cesium, lithium, magnesium and calcium.

[0046] Preferably, in the PFPE additive (i), said organic ammonium salt is selected from those of formula: N +< H(R 21 )(R 22 )(R 23 ) wherein each of R 21 , R 22 , R 23 is selected from: linear or branched C 1 -C 20 aliphatic chain, optionally containing at least one heteroatom, preferably -O-; or two of R 21 , R 22 , R 23 together form a 5- or 6- membered aliphatic or aromatic ring, said ring optionally containing at least one heteroatom and / or being optionally substituted by at least one linear or branched alkyl chain comprising from 1 to 10 carbon atoms and optionally containing at least one heteroatom, preferably selected from -O- and -N-, and the third of R 21 , R 22 , R 23 is as defined above.

[0047] More preferably, said organic ammonium salt is selected from triethanol ammonium, triethyl ammonium, pyridinium, trimethyl ammonium, tributyl ammonium, 1-methyl imidazolium, di(ethyl)cyclohexyl-ammonium, benz- imidazolium, 1-benzyl imidazolium.

[0048] Preferably, in the PFPE additive (ii), said ammonium group is selected from those of formula:         §-N +< (R 31 )(R 32 )(R 33 ) wherein § indicates the bond to the (per)fluoropolyether backbone, and each of R 31 , R 32 , R 33 is selected from: linear or branched C 1 -C 20 aliphatic chain, optionally containing at least one heteroatom, preferably -O-; or two of R 31 , R 32 , R 33 together form a 5- or 6- membered aliphatic or aromatic ring, said ring optionally containing at least one heteroatom and / or being optionally substituted by at least one linear or branched alkyl chain comprising from 1 to 10 carbon atoms and optionally containing at least one heteroatom, preferably selected from -O- and -N-, and the third of R 31 , R 32 , R 33 is as defined above

[0049] More preferably, said ammonium group is selected from di(methyl)benzylammonium, di(methyl)octyl-ammonium, tri(methyl) ammonium, tri(butyl)ammonium, tri(tert-butyl)ammonium, di(cyclohexane) methylammonium, tri(pentyl)ammonium, di(ethyl)cyclohexylammonium, di-(butyl)methylammonium, di(ethyl)butyl-ammonium, 1-butyl-imidazolium, 1-methylimidazolium, 1-benzyl-imidazolium, benzimidazolium, pyridinium, pyridazinium, pyrimidinium, pyrazinium, 1,2,4-triazolium.

[0050] Preferably, in the PFPE additive (ii), said at least one inorganic or organic counterion is selected in the group comprising: Br -< , I -< , Cl -< , BF 4 -< , NO 3 , OH -< , [(CF 3 SO 2 ) 2 N] -< , sulfonate and sulfate.

[0051] Said sulfonate is preferably selected in the group comprising: triflate, nonaflate, mesylate and tosylate.

[0052] Preferably, said PFPE additive comprises a (per)fluoropolyether backbone complying with the following formula (II*):         -(X*) a* -O-(R f^ )-(X**) b* -     (II*) wherein a* and b* equal or different from each other, are equal to or higher than 1; X* and X**, equal to or different from each other, are selected from -CF 2 -, - CF 2 CF 2 -, -CF(CF 3 )- and -CF 2 CH 2 -; R f^ is a fully or partially fluorinated chain comprising, preferably consisting of repeating units R°, said repeating units being independently selected from the group consisting of: (i) -CFXO-, wherein X is -F or -CF 3 ; (ii) -CFXCFXO-, wherein X, equal or different at each occurrence, is -F or - CF 3 , with the proviso that at least one of X is -F; (iii) -CF 2 CF 2 CF 2 O-; (iv) -CF 2 CF 2 CF 2 CF 2 O-; (v) -(CF 2 ) j -CFZ-O- wherein j is an integer from 0 to 3 and Z is a group of general formula -O-R( f-a )-T, wherein R( f-a ) is a fluoropolyoxyalkene chain comprising a number of repeating units from 0 to 10, said recurring units being chosen among the following : -CFXO- , -CF 2 CFXO-, -CF 2 CF 2 CF 2 O-, - CF 2 CF 2 CF 2 CF 2 O-, with each of X being independently -F or -CF 3 and T being a C 1 -C 3 perfluoroalkyl alkyl chain.

[0053] Preferably, chain (R f^ ) complies with the following formula:         (R f* -I)     -[(CFX 1< O) g1 (CFX 2< CFX 3< O) g2 (CF 2 CF 2 CF 2 O) g3 (CF 2 CF 2 CF 2 CF 2 O) g4 ]- -wherein X 1< is independently selected from -F and -CF 3 , X 2< , X 3< , equal or different from each other and at each occurrence, are independently -F, -CF 3 , with the proviso that at least one of X is -F; g1, g2 , g3, and g4, equal or different from each other, are independently integers ≥0,such that g1+g2+g3+g4 is in the range from 2 to 300, preferably from 2 to 100; should at least two of g1, g2, g3 and g4 be different from zero, the different recurring units are generally statistically distributed along the chain.

[0054] More preferably, chain (R f^ ) is selected from chains of formula:         (R f^ -IIA)     -[(CF 2 CF 2 O) a1 (CF 2 O) a2 ]- -wherein: a1 and a2 are independently integers ≥ 0 such that the number average molecular weight is between 400 and 100,000, preferably between 400 and 50,000; both a1 and a2 are preferably different from zero, with the ratio a1 / a2 being preferably comprised between 0.1 and 10;         (R f^ -IIB)     -[(CF 2 CF 2 O) b1 (CF 2 O) b2 (CF(CF 3 )O) b3 (CF 2 CF(CF 3 )O) b4 ]- -wherein: b1, b2, b3, b4, are independently integers ≥ 0 such that the number average molecular weight is between 400 and 100,000, preferably between 400 and 50,000; preferably each of b1, b2, b3, b4 are > 0;         (R f ^ -IIC)     -[(CF 2 CF 2 O) c1 (CF 2 O) c2 (CF 2 (CF 2 ) cw CF 2 O) c3 ]- -wherein: cw = 1 or 2; c1, c2, and c3 are independently integers ≥ 0 chosen so that the number average molecular weight is between 400 and 100,000, preferably between 400 and 50,000; preferably c1, c2 and c3 are all > 0, with the ratio c3 / (c1+c2) being generally lower than 0.2.

[0055] Still more preferably, chain (R f^ ) complies with one of formulae:         (R f ^ -IIA)     -[(CF 2 CF 2 O) a1 (CF 2 O) a2 ]- -wherein: a1, and a2 are integers > 0 such that the number average molecular weight is between 400 and 100,000, preferably between 400 and 50,000, with the ratio a1 / a2 being generally between 0.1 and 10, more preferably between 0.2 and 5; or         (R f ^ -IIB)     -[(CF 2 CF 2 O) b1 (CF 2 O) b2 (CF(CF 3 )O) b3 (CF 2 CF(CF 3 )O) b4 ]- -wherein: b1, b2, b3, b4, are independently integers ≥ 0 such that the number average molecular weight is between 400 and 100,000, preferably between 400 and 50,000; preferably each of b1, b2, b3, b4 are > 0.

[0056] According to an embodiment, said PFPE additive (i) comprises at one chain end or at both chain ends, a carboxyl group salified with at least one inorganic metal salt. Said at least one inorganic metal salt is as defined above.

[0057] Preferably, said PFPE additive comprises, at one chain end or at both chain ends, a carboxyl group salified with at least one organic ammonium salt. Said at least one organic ammonium salt is as defined above.

[0058] More preferably, said PFPE additive comprises at one chain end a salified carboxyl group as defined herein above and at the other chain end a neutral group.

[0059] Such neutral group is preferably fluorine atom or a perfluorinated alkyl chain comprising 1 to 6 carbon atoms.

[0060] According to this embodiment, the chain end comprising an acid group is preferably bonded to the (per)fluoropolyether backbone complying with formula (R f^ ) as defined above via a group of formula -CF 2 - or -CF(CF 3 )-.

[0061] The PFPE additive (i) can be prepared according to methods known in the art, such as following the procedure disclosed in US 5,000,864 (Ausimont S.p.A.).

[0062] According to another embodiment, said PFPE additive (ii) comprises at one chain end or both chain ends, an ammonium group and at least one inorganic or organic counterion.

[0063] Preferably, said ammonium group is as defined above.

[0064] Preferably, said at least one inorganic or organic counterion is as defined above.

[0065] According to this second embodiment, the chain end comprising an ammonium group is preferably bonded to the (per)fluoropolyether backbone complying with formula (R f ) as defined above via a group of formula -CF 2 - or - CF 2 CH 2 -.

[0066] Also, according to this second embodiment, the chain end comprising an ammonium group is preferably bonded to said sigma bond or group (B1) via an alkoxylated chain [chain (R a )].

[0067] Preferably, said chain (R a ) complies with one of the following formulae (R a - 1 ) to (R a - III ):         (R a - I ) -(OCH 2 CH 2 ) j1 -H         (R a - II ) -[OCH(CH 3 )CH 2 ]j 2 -H         (R a - III ) -[(OCH 2 CH 2 ) j3 -(OCH(CH 3 )CH 2 ) j4 ] j ( x )-H wherein j1 and j2, each independently, are an integer from 1 to 10, more preferably from 1 to 5; j3, j4 and j(x) are integers from 1 to 25, and the sum of j3 and j4 is from 2 to 50.

[0068] The PFPE additive (ii) can be prepared according to methods known in the art, such as following the method disclosed in WO 2022 / 078766 (Solvay Specialty Polymers Italy S.p.A.).

[0069] In a further object, the present invention relates to the use of said composition (COMP) as lubricant for electrical components suitable for use in different applications and industries, such as in particular automotive and electronic industries. Such components include, electrical and electronic components, such - without limitation - electrical connectors, switchgears and circuit breakers.

[0070] In still a further object, the present invention relates to the use of said composition (COMP) as lubricant for mechanical components, suitable for use in the automotive industry, in particular for electric vehicles (EV) . Such components include - without limitations - ball bearings.

[0071] In still a further object, the present invention relates to the use of composition (COMP) according to the present invention for the manufacture of a grease.

[0072] In another object, the present invention relates to a grease comprising composition (COMP) according to the present invention and at least one other ingredient.

[0073] Such grease can be advantageously used as lubricant for electrical, electronic or mechanical components. Examples of such components are provided above and include - without limitation - electrical connectors, switchgears and circuit breakers, as well as ball bearings.

[0074] Should the disclosure of any patents, patent applications, and publications conflict with the description of the present application to the extent that it may render a term unclear, the present description shall take precedence.

[0075] The present invention will be now described in more detail with reference to the following examples, whose purpose is merely illustrative and not intended to limit the scope of the disclosure.EXAMPLES Materials

[0076] COMP1: Cyphos IL-169 from Solvay Technology Solutions (hydrogenated liquid additive) was used as comparison.

[0077] COMP2: Silver micropowder purchased from Sigma Aldrich (solid particle size = 5-8 µm) was also used as a comparison.

[0078] ADD1: triflate salt of 1-butyl imidazolium monofunctional PFPE comprising a backbone of formula -(CF 2 CF 2 O) m (CF 2 O) n - and having a Mw = 2520 g / mol as measured by Nuclear Magnetic Resonance (NMR) Spectroscopy.

[0079] ADD2: triflate salt of 1-butyl imidazolium monofunctional PFPE comprising a backbone of formula -(CF 2 CF 2 O) m (CF 2 O) n - and having a Mw = 4760 g / mol as measured by NMR.

[0080] ADD3: triflate salt of 1-benzyl imidazolium monofunctional PFPE comprising a backbone of formula -(CF 2 CF 2 O) m (CF 2 O) n - and having a Mw = 2580 g / mol as measured by NMR.

[0081] ADD4: triethanolamine salt of a mixture of neutral, mono and bi-functional PFPE having the backbone of formula -[CF 2 CF(CF 3 )O] n -(CF 2 O) g -[CF(CF 3 )O] g - and comprising at its chain ends the groups of formula: -OCF 2 COO -< , - OCF(CF 3 )COO -< , -OCF 2 C(=O)CF 3 , -OCF 3 .

[0082] Fomblin(R) HV25 is commercially available from Solvay Specialty Polymers Italy S.p.A. having a viscosity = 25000 mm 2< / s measured at 25°C.

[0083] Compositions of comparison and according to the present invention were prepared by mixing the ingredients detailed in Table 1 hereinafter. Table 1Example No.Base oilAdditiveConcentration (wt. %)1 C(*)Fomblin( R< ) HVCOMP152C(*)Fomblin( R< ) HVCOMP253Fomblin( R< ) HVADD454Fomblin( R< ) HVADD125Fomblin( R< ) HVADD226Fomblin( R< ) HVADD257Fomblin( R< ) HVADD328C(*)Fomblin( R< ) HVnone9Fomblin( R< ) HVADD410.010Fomblin( R< ) HVADD40.5(*) comparison

[0084] The additive used in composition of Example 1C was not soluble in Fomblin( R< ) HV, and hence such composition was no further tested.

[0085] The other compositions were evaluated for their volume resistivity at two different temperatures, i.e. 25°C and 80 °C, following ASTM D257. A voltage of 500 V was applied and the measured value was registered after 60 sec. Table 2Example No.Volume resistivity @25°C (Ωcm)Volume resistivity @80°C (Ωcm)2C(*)6x10 15< n / p33x10 15< 3x10 15< 43x10 14< 9x10 14< 51x10 15< 2x10 14< 62x10 14< 1x10 14< 71x10 15< 5x10 14< 8C(*)2x10 15< 4x10 15< 93x10 15< 2x10 13< 102x10 15< 3x10 15< (*) comparison

[0086] The comparative composition of Example 2C comprising solid particles showed a higher volume resistivity compared to the compositions according to the present invention.

[0087] The comparative composition of Example 2C was also evaluated for its shelf life: separation between two phases was observed by visual inspection after four days.

[0088] The compositions according to the present invention showed a volume resistivity lower than comparative composition 2C at 25°C and also lower than comparative composition 8C at 80°C.

Claims

1. A composition [composition (COMP)] comprising: - at least one block copolymer [PFPE copolymer] comprising a first and a second (per)fluoropolyether chain [PFPE chain] each having two chain ends, wherein the first chain end of said first and second PFPE chain comprises a perfluorinated alkyl group and the second chain end of said first and second PFPE chain are bonded to each other via: - at least one first block [block (1)] complying with formula (I): wherein n is 0 or an integer from 1 to 3; R1 to R4, each independently, is selected in the group comprising, preferably consisting of, fluorine atom, perfluorinated linear or branched alkyl group having from 1 to 6 carbon atoms, group of formula (II):         (II)     -(R10)t[C(R11)(R12)-C(R13)(R14)(R15)]z wherein R10 is an oxygen atom, or a bi- / tri- / tetravalent perfluorinated alkyl chain comprising from 1 to 24 carbon atoms optionally interrupted by and / or comprising at least one oxygen atom, t is zero or 1, z is an integer from 1 to 3; R11 to R15, each independently, is selected in the group comprising, preferably consisting of, fluorine atom, perfluorinated linear or branched alkyl group having from 1 to 6 carbon atoms and group of formula (III):         -[(A^)a^-(B^)v^-(E^)L^]u^-(C^)-T     (III) wherein a^ is zero or 1, v^ is zero or an integer from 1 to 3, L^ is zero or an integer from 1 to 250, u^ is zero or an integer from 1 to 50; A^ is a PFPE chain B^ is a group of formula:         -[C(R1^)(R2^)-C(R3^)(R4^)]- wherein R1^ to R4^ each independently has the meaning defined above for each of R1 to R4, E^ is a group of formula -(CR100^R101^CR102^R103^)- wherein R100^ and R101^ are independently selected from hydrogen atom, halogen atom, more preferably fluorine or chlorine atom, and R102^ and R103^ are independently selected from hydrogen atom, halogen atom, more preferably fluorine or chlorine atom; linear or branched alkyl chain comprising from 1 to 6 carbon atoms, optionally containing at least one heteroatom selected from O, N and S; -OR200 wherein R200 is linear or branched perfluorinated chain comprising from 1 to 6 carbon atoms or a group of formula -CF2OR201 in which R201 is a perfluorinated alkyl chain comprising from 1 to 6 carbon atoms, optionally interrupted by one or more oxygen ether atoms; or one of R100^ and R101^ and one of R102^ and R103^ are a fluorine atom and the other of R100^ and R101^ and the other of R102^ and R103^ together form a perhalogenated cyclic ring having from 4 to 6 members, optionally comprising heteroatoms, such as oxygen atoms; C^ is a PFPE chain, and T is a perfluorinated alkyl group; - at least one second block [block (2)] complying with formula (IV):         -[(CR1*R2*CR3*R4*)n*-(E)L]-     (IV) wherein n* is zero or an integer from 1 to 250, L is zero or an integer from 1 to 250 and the sum of n* and L is 0 or from 1 to 250; R1* and R2* are independently selected from hydrogen atom, halogen atom, more preferably fluorine or chlorine atom, and R3* and R4* are independently selected from hydrogen atom, halogen atom, more preferably fluorine or chlorine atom; linear or branched alkyl chain comprising from 1 to 6 carbon atoms, optionally containing at least one heteroatom selected from O, N and S; -OR200 wherein R200 is linear or branched perfluorinated chain comprising from 1 to 6 carbon atoms or a group of formula -CF2OR201 in which R201 is a perfluorinated alkyl chain comprising from 1 to 6 carbon atoms, optionally interrupted by one or more oxygen ether atoms; or one of R1* and R2* and one of R3* and R4* are a fluorine atom and the other of R1* and R2* and the other of R3* and R4* together form a perhalogenated cyclic ring having from 4 to 6 members, optionally comprising heteroatoms, such as oxygen atoms; E has the same meaning provided for E^ above; - optionally, at least a third block [block (3)] comprising a PFPE chain; with the proviso that: in said PFPE copolymer: -- at least one of n, n* and L is different from 0; -- said block (1), said block (2) and when present said block (3) are statistically distributed; in said formula (I): -- at least one of R1 to R4 is a group of formula (II), -- one of R11 or R12 and one of R13 to R15, is a group of formula (III); in said formula (III) and said formula (IV) -- the recurring units are statistically distributed, in said formula (III) -- when a^ is 1 at least one of v^ and L^ is different from 0; and - up to 20.0 wt.% based on the total weight of composition (COMP) of at least one salt of a (per)fluoropolyether polymer [PFPE additive] comprising a (per)fluoropolyether backbone having two chain ends bonded to opposite sides of said backbone, wherein at least one chain end comprises at least one group selected from: (i) acid group selected from: -COO-, -OSO32-, -OPO32-, -SO3-, wherein said acid group is salified with at least one inorganic metal salt or with an organic salt selected from ammonium salt and phosphonium salt; (ii) ammonium group and at least one inorganic or organic counterion; wherein the sum of said PFPE copolymer and said PFPE additive add up to 100 wt.% of composition (COMP).

2. The composition (COMP) according to Claim 1, said composition (COMP) containing at least one additional ingredient, preferably selected in the group comprising: antirust, antioxidants, rheological modifiers, corrosion inhibitors, dyes, pigments.

3. The composition (COMP) according to Claims 1 or 2, said composition (COMP) being free from additive(s) in the form of solid particles.

4. The composition (COMP) according to any one of the preceding Claims, wherein said PFPE copolymer has a viscosity of at least 1,000 mm2 / s, measured at 20°C according to standard methods, such as ASTM D445, or with a dynamical mechanical spectrometer Anton Paar MCR 502 rheometer equipped with parallel plates 25 mm, at 1 rad / s and at 25°C.

5. The composition (COMP) according to any one of the preceding Claims, wherein said first chain end of said first and second PFPE chain comprise a perfluorinated linear alkyl group having from 1 to 3 carbon atoms.

6. The composition (COMP) according to any one of the preceding Claims, wherein: - said first PFPE chain is bonded to said block (1) via a sigma bond or a group -(C)- selected from -CF2-, -CF2CF2- or -O-; and / or - said block (2) is bonded to said second PFPE chain via a sigma bond or a group -(C)- selected from -CF2-, -CF2CF2- or -O-; and / or - when both said block (1) and said block (2) are present, they are linked via a sigma bond.

7. The composition (COMP) according to any one of the preceding Claims, wherein each of said PFPE chain is a partially or fully fluorinated chain [chain (Rf)] comprising, preferably consisting of, repeating units R°, said repeating units being independently selected from the group consisting of: (i) -CFXO-, wherein X is F or CF3; (ii) -CFXCFXO-, wherein X, equal or different at each occurrence, is F or CF3, with the proviso that at least one of X is -F; (iii) -CF2CF2CW2O-, wherein each of W, equal or different from each other, are F, Cl, H; (iv) -CF2CF2CF2CF2O-; (v) -(CF2)w-CFZ-O- wherein w is an integer from 0 to 3 and Z is a group of general formula -O-R(f-a)-Y, wherein R(f-a) is a fluoropolyoxyalkene chain comprising a number of repeating units from 0 to 10, said recurring units being chosen among the followings : -CFXO- , -CF2CFXO-, -CF2CF2CF2O-, - CF2CF2CF2CF2O-, with each of each of X being independently F or CF3 and Y being a C1-C3 perfluoroalkyl group.

8. The composition (COMP) according to any one of the preceding Claims, wherein said PFPE copolymer comprises a first and a second PFPE chain, each having two chain ends, wherein the first chain end of said first and second PFPE chain comprises a perfluorinated alkyl group and the second chain end of said first and second PFPE chain are bonded to each other via: - at least one block (2) complying with formula (IV):         -[(CR1*R2*CR3*R4*)n*-(E)L]-     (IV) wherein n* is an integer from 1 to 250, L is an integer from 1 to 250, and the sum of n* and L is from 1 to 250; R1* and R2* are fluorine atom, and R3* and R4* are independently selected from halogen atom, more preferably fluorine or chlorine atom; linear or branched alkyl chain comprising from 1 to 6 carbon atoms, optionally containing at least one heteroatom selected from O, N and S; -OR200 wherein R200 is linear or branched perfluorinated chain comprising from 1 to 6 carbon atoms or a group of formula -CF2OR201 in which R201 is a perfluorinated alkyl chain comprising from 1 to 6 carbon atoms, optionally interrupted by one or more oxygen ether atoms; E is a group of formula -(CR100^R101^CR102^R103^)- wherein R100^ and R101^ are independently selected from halogen atom, preferably fluorine or chlorine atom, and R102^ and R103^ are independently selected from halogen atom, preferably fluorine or chlorine atom; -OR200 wherein R200 is linear or branched perfluorinated chain comprising from 1 to 6 carbon atoms or a group of formula -CF2OR201 in which R201 is a perfluorinated alkyl chain comprising from 1 to 6 carbon atoms, optionally interrupted by one or more oxygen ether atoms; and - optionally, at least one block (3) comprising a PFPE chain.

9. The composition (COMP) according to any one of the preceding Claims, wherein said PFPE additive is in an amount of at least 0.1 wt.% and up to 20.0 wt.% based on the total weight of composition (COMP).

10. The composition (COMP) according to any one of the preceding Claims, wherein in the PFPE additive (i): - said acid group is a carboxylic group salified with an inorganic metal salt or the organic salt selected from ammonium salt and phosphonium salt; or - said organic ammonium salt is selected from those of formula:         N+H(R21)(R22)(R23) wherein each of R21, R22, R23 is selected from: linear or branched C1-C20 aliphatic chain, optionally containing at least one heteroatom; or two of R21, R22, R23 together form a 5- or 6- membered aliphatic or aromatic ring, said ring optionally containing at least one heteroatom and / or being optionally substituted by at least one linear or branched alkyl chain comprising from 1 to 10 carbon atoms and optionally containing at least one heteroatom, and the third of R21, R22, R23 is as defined above.

11. The composition (COMP) according to any one of the preceding Claims, wherein in the PFPE additive (ii): - said ammonium group is selected from those of formula:         §-N+(R31)(R32)(R33) wherein § indicates the bond to the (per)fluoropolyether backbone, and each of R31, R32, R33 is selected from: linear or branched C1-C20 aliphatic chain, optionally containing at least one heteroatom; or two of R31, R32, R33 together form a 5- or 6- membered aliphatic or aromatic ring, said ring optionally containing at least one heteroatom and / or being optionally substituted by at least one linear or branched alkyl chain comprising from 1 to 10 carbon atoms and optionally containing at least one heteroatom, and the third of R31, R32, R33 is as defined above; and - said at least one inorganic or organic counterion is selected in the group comprising: Br-, I-, Cl-, BF4- , NO3- , OH-, [(CF3SO2)2N]-, sulfonate and sulfate.

12. The composition (COMP) according to any one of Claims 9 to 11, wherein said PFPE additive (ii) comprises a (per)fluoropolyether backbone complying with the following formula (II*):         -(X*)a*-O-(Rf^)-(X**)b*-     (II*) wherein a* and b* equal or different from each other, are equal to or higher than 1; X* and X**, equal to or different from each other, are selected from -CF2-, - CF2CF2-, -CF(CF3)- and -CF2CH2-; Rf^ is a fully or partially fluorinated chain comprising, preferably consisting of repeating units R°, said repeating units being independently selected from the group consisting of: (i) -CFXO-, wherein X is -F or -CF3; (ii) -CFXCFXO-, wherein X, equal or different at each occurrence, is -F or -CF3, with the proviso that at least one of X is -F; (iii) -CF2CF2CF2O-; (iv) -CF2CF2CF2CF2O-; (v) -(CF2)j-CFZ-O- wherein j is an integer from 0 to 3 and Z is a group of general formula -O-R(f-a)-T, wherein R(f-a) is a fluoropolyoxyalkene chain comprising a number of repeating units from 0 to 10, said recurring units being chosen among the following : -CFXO- , -CF2CFXO-, -CF2CF2CF2O-, - CF2CF2CF2CF2O-, with each of X being independently -F or -CF3 and T being a C1-C3 perfluoroalkyl alkyl chain.

13. Use of composition (COMP) according to any one of Claims 1 to 12 as lubricant for: - electrical components, preferably selected in the group comprising: electrical connectors, switchgears and circuit breakers; and / or - mechanical components, preferably selected from ball bearings.

14. A grease comprising composition (COMP) as defined in any one of Claims 1 to 12.