Method for producing an optical effect layer containing magnetic or magnetisable pigment particles and exhibiting one or more indicia - Patents.com

Abstract

The present invention relates to the field of protection of security documents, such as for example banknotes and identity documents against counterfeiting and illegal copying. In particular, the present invention provides a method for producing an optical effect layer (OEL) exhibiting one or more indicia (x30) on a substrate (x20), comprising the steps of exposing a coating layer (x10) comprising non-spherical magnetic or magnetizable pigment particles to a magnetic field of a magnetic field generating device in order to orient at least a portion of the non-spherical magnetic or magnetizable pigment particles, applying a top coating composition on the coating layer (x10) in the form of one or more indicia (x30), and at least partially curing the coating layer (x10) and the one or more indicia (x30) in a curing device (x50).

Description

Detailed Description of the Invention

[0001] [Field of the Invention]

[0001] The present invention relates to the field of magnetic field generating devices and methods for producing optical effect layers (OELs) containing magnetically oriented non-spherical magnetic or magnetizable pigment particles. In particular, the present invention provides a magnetic field generating device and method for magnetically orienting non-spherical magnetic or magnetizable pigment particles in a coating layer to produce an OEL, and the use of said OELs for decorative purposes as well as for anti-counterfeiting measures for security documents or articles.

[0002] [Background of the invention]

[0002] It is known in the art to use inks, compositions, coatings or layers comprising oriented magnetic or magnetisable pigment particles, in particular also optically variable magnetic or magnetisable pigment particles, for the production of security elements, for example in the field of security documents. Coatings or layers comprising oriented magnetic or magnetisable pigment particles are disclosed, for example, in U.S. Pat. Nos. 2,570,856; 3,676,273; 3,791,864; 5,630,877 and 5,364,689. Coatings or layers comprising oriented magnetic colour-shifting pigment particles, which provide particularly attractive optical effects and serve to protect security documents, are disclosed in WO 2002 / 090002 and WO 2005 / 002866.

[0003]

[0003] For example, security features for security documents can generally be classified into "covert" security features on the one hand, and "overt" security features on the other hand. The protection offered by covert security features relies on the principle that such features are difficult to detect, typically requiring specialized equipment and knowledge for detection, whereas "overt" security features rely on the concept of being easily detectable by unaided human senses, e.g. such features may be visible and / or detectable by touch, whilst remaining difficult to produce and / or replicate. However, the effectiveness of overt security features depends crucially on their easy recognition as security features.

[0004]

[0004] Magnetic or magnetizable pigment particles in printing inks or coatings allow the creation of magnetically inductive images, designs and / or patterns by the application of a correspondingly configured magnetic field, causing local orientation of the magnetic or magnetizable pigment particles in the uncured (i.e. wet) coating, followed by curing of the coating. The result is a fixed, stable magnetically inductive image, design or pattern. Materials and techniques for the orientation of magnetic or magnetisable pigment particles in coating compositions are disclosed, for example, in U.S. Pat. No. 2,418,479; U.S. Pat. No. 2,570,856; U.S. Pat. No. 3,791,864, DE 2006848, U.S. Pat. No. 3,676,273, U.S. Pat. No. 5,364,689, U.S. Pat. No. 6,103,361, EP 0406667; U.S. Pat. Appl. Pub. No. 2002 / 0160194; U.S. Pat. Appl. Pub. No. 2004 / 0009309; EP 0710508; WO 2002 / 09002; WO 2003 / 000801; WO 2005 / 002866; WO 2006 / 061301. Such a method makes it possible to create magnetic induction patterns that are highly resistant to counterfeiting. The security element in question can only be created by having access to both magnetic or magnetisable pigment particles or corresponding pigment inks and the specific technology used to print said inks and to orient said pigments in the printed inks.

[0005]

[0005] In order to protect security documents or articles containing magnetically inductive images from the premature detrimental effects of soil and / or moisture over time and use, it is customary to apply a protective varnish, which is applied as a continuous layer over an already prepared, dried / cured magnetically inductive image.

[0006]

[0006] WO 2011 / 012520 discloses a transfer foil comprising a coating layer having the form of a design, said design comprising oriented optically variable magnetic pigments representing an image, indicia or pattern. The transfer foil may further comprise a top-coating layer, said top-coating layer being applied before the application of the layer comprising the optically variable magnetic pigment. The process of making said transfer foil comprises the steps of a) applying a top-coating layer and hardening / curing said top-coating layer, and b) applying a layer comprising the optically variable magnetic pigment, magnetically orienting the particles and hardening / curing said layer. The disclosed method is not suitable for making magnetically inductive images required to show personalized variable indicia.

[0007]

[0007] EP 1641624, EP 1937415, and EP 2155498 disclose an apparatus and method for magnetically transferring indicia to an uncured (i.e. wet) coating composition containing magnetic or magnetizable pigment particles to form an optical effect layer (OEL). The disclosed method allows the creation of security documents and articles with customer-specific magnetic designs. However, the disclosed magnetic devices are prepared to meet customer-specific magnetic designs and cannot be altered if the design is required to change from one article to another, and therefore the method is not suitable for creating OELs required to show personalized variable indicia.

[0008]

[0008] EP 3170566, EP 3459758, EP 2542421 and WO 2020 / 148076 disclose different methods for the creation of variable indicia in optically variable magnetic inks. However, said methods require the use of special equipment such as photomasks, lasers or addressable LEDs.

[0009]

[0009] In order to provide variable information with magnetic properties on security documents or articles, inkjet inks containing magnetic particles have been developed to enable magnetic ink character recognition (MICR). However, said inkjet inks face various problems, especially related to the shelf-life stability of the ink, ink printability, non-uniform magnetic ink deposits, and clogging of the print head. EP 2223976 discloses a method for the preparation of documents containing MICR features, comprising the steps of applying by inkjet onto a substrate a pattern of a curable ink containing a gelling agent, cooling the ink to a temperature below the gelling temperature of the ink, applying a magnetic material to the ink, and finally curing the ink. Alternatively, toners containing magnetic particles have also been developed, as disclosed, for example, in US Pat. Nos. 10,503,091 and 10,359,730. However, specific dedicated equipment is required to print those toners.

[0010]

[0010] There is therefore a need for a method for universally producing customized optical effect layers exhibiting one or more indicia on an industrial scale, said optical effect layers exhibiting noticeable effects. Furthermore, said method should be reliable, simple to implement, and capable of operating at high production speeds.

[0011] [Summary of the Invention]

[0011] The present invention therefore aims to overcome the deficiencies of the prior art by providing a method for producing an optical effect layer (OEL), said OEL comprising a motif consisting of at least two areas of a single applied and cured layer containing non-spherical magnetic or magnetisable pigment particles and exhibiting one or more indicia (x30) on a substrate (x20), The method is: a) applying onto a surface of a substrate (x20) a radiation curable coating composition comprising non-spherical magnetic or magnetizable pigment particles and one or more photoreactive compounds that do not absorb in the range of about 350 nm to about 470 nm, the radiation curable coating composition being in a first liquid state to form a coating layer (x10); b) after step a), at least partially applying a top coating composition onto the coating layer (x10), said top coating composition being applied in the form of one or more indicia (x30), said top coating composition comprising one or more compounds absorbing in the range of about 350 nm to about 470 nm; c) partially simultaneously with or after step b), at least partially curing the one or more indicia (x30) and one or more areas of the coating layer (x10) below said one or more indicia (x30) with LED curing units (x50) emitting between 350 nm and 470 nm; d) after step c), exposing the coating layer (x10) to a magnetic field of a magnetic field generating device in order to orient at least a portion of the non-spherical magnetic or magnetizable pigment particles; e) partially simultaneously with or after step d), at least partially curing the coating layer (x10) with curing units (x60) emitting at least between 250 nm and 320 nm, The radiation curable coating composition and the topcoating composition are cationically curable compositions; The method, wherein the one or more photoreactive compounds that do not absorb in the range of about 350 nm to about 470 nm of the radiation curable coating composition of step a) and the one or more compounds that absorb in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are selected according to one of the following combinations: i) one or more compounds of the radiation curable coating composition of step a) is an iodonium salt and one or more compounds of the top curable coating composition of step b) is a thioxanthone compound; ii) one or more compounds of the radiation curable coating composition of step a) is an iodonium salt and one or more compounds of the top curable coating composition of step b) is an anthracene compound; iii) one or more compounds of the radiation curable coating composition of step a) are iodonium salts and one or more compounds of the top curable coating composition of step b) are coumarin compounds; iv) one or more compounds of the radiation curable coating composition of step a) are iodonium salts and one or more compounds of the top curable coating composition of step b) are naphthalene compounds, and the top curable coating composition of step b) further comprises one or more anthracene compounds; v) The one or more compounds of the radiation curable coating composition of step a) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being 4-(phenylthio)phenyldiphenyl-sulfonium; bis[4-(diphenylsulfonium)phenyl]sulfide; (4-methylphenyl)diphenyl-sulfonium; (3-methylphenyl)diphenyl-sulfonium; bis(4-methylphenyl)phenyl-sulfonium; [(4-(1,1-dimethylethyl)phenyl]diphenyl-sulfonium; bis[4-(1-methyl [(4-(2-methylpropyl)phenyl]diphenyl-sulfonium;(4-methoxyphenyl)diphenyl-sulfonium;1-naphthalenyldiphenyl-sulfonium;Tris(4-methylphenyl)-sulfonium;(4-bromophenyl)diphenyl-sulfonium;(4-iodophenyl)diphenyl-sulfonium;(4-fluorophenyl)diphenyl-sulfonium;(4-chlorophenyl)diphenyl-sulfonium;(4-phenoxyphenyl)diphenyl-sulfonium;(4'-methylphenyl)diphenyl-sulfonium 4-(1,1-diphenyl)sulfonium;Tris(4-propylphenyl)sulfonium;Bis(4-butylphenyl)phenylsulfonium;Tris[4(1-methylethyl)phenyl]sulfonium;S,S'-1,3-phenylenebis[S,S'-diphenyl]sulfonium;(4-dodecylphenyl)diphenylsulfonium;(4-benzoylphenyl)diphenylsulfonium;Bis([1,1'-biphenyl]-4-yl)(4-methylphenyl)sulfonium;Tris[4-[1,1-diphenyl methylethyl)phenyl]-sulfonium;triphenyl-sulfonium,5-(4-methylphenyl)-dibenzothiophenium;10-(4-methylphenyl)-9H-thioxanthenium;diphenyl[4-[[(4-phenylthiophenyl]thio]phenyl]-sulfonium;phenylbis[4-phenylthio)phenyl]-sulfonium;5-[4-(phenylthio)phenyl]-thianthrenium;5-[4-(phenylthio)phenyl]-dibenzothiophenium;10-[4-(diphenylthio)phenyl]-9H-thioxanthenium;5-phenyl-thianthrenium; 10-phenyl-9H-thioxanthenium; 5-(4-methylphenyl)-thianthrenium; 5-[1,1'-biphenyl]-4-yl-thianthrenium; or S,S'-(thiodi-4,1-phenylene)bis[S,S'-bis[4-(2-hydroxyethoxy)]phenyl]-sulfonium; 5-[4-(2-hydroxyethoxy)phenyl]thianthrenium, and the one or more compounds of the top curable coating composition of step b) are anthracene compounds; vi) the one or more compounds of the radiation curable coating composition of step a) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those of v), the one or more compounds of the top curable coating composition of step b) are thioxanthone compounds, and the top curable coating composition of step b) further comprises one or more compounds which are iodonium salts; vii) the one or more compounds of the radiation curable coating composition of step a) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those of v), and the one or more compounds of the top curable coating composition of step b) are naphthalene compounds, and the top curable coating composition of step b) further comprises one or more anthracene compounds; viii) the one or more compounds of the radiation curable coating composition of step a) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those of v), the one or more compounds of the top curable coating composition of step b) are coumarin compounds, and the top curable coating composition of step b) further comprises one or more compounds which are iodonium salts; ix) the one or more compounds of the radiation curable coating composition of step a) are selected from the group consisting of iodonium salts, sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those of v), and mixtures thereof, and the one or more compounds of the top curable coating composition of step b) are iodonium salts having a cationic moiety and an anionic moiety, the cationic moiety being [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium or [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium; x) the one or more compounds of the radiation curable coating composition of step a) are selected from the group consisting of iodonium salts, sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those of v), and mixtures thereof, and the one or more compounds of the top curable coating composition of step b) are oxonium salts having a cationic moiety and an anionic moiety, the cationic moiety being 2,4,6-triphenylpyrylium; 2,4,6-tris(4-methylphenyl)-pyrylium; 2,4,6-tris(4-methoxyphenyl)-pyrylium; 2,6-bis(4-fluorophenyl)-4-(4-methoxyphenyl)-pyrylium; 3-methyl-2,4,6-triphenyl-pyrylium; 2,4,6-tris([1,1'-biphenyl]-4-yl)-pyrylium; 4-[4-(dimethylamino)phenyl]-2,6-diphenyl-pyrylium, or 2,4-bis(4-methoxyphenyl)-6-phenyl-pyrylium; xi) the one or more compounds of the radiation curable coating composition of step a) are selected from the group consisting of iodonium salts, sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those of v), and mixtures thereof; and the one or more compounds of the top curable coating composition of step b) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium; 10-[1,1′-biphenyl]-4-yl-2-(1-methylethyl)-9-oxo-9H-thioxanthenium; or (9-oxo-9H-thioxanthen-2-yl)diphenyl-sulfonium. This is achieved by providing:

[0012] In one preferred embodiment, step a) of applying the radiation curable coating composition is carried out by a process selected from the group consisting of screen printing, gravure printing, pad printing, and flexographic printing.

[0013] In one preferred embodiment, step b) of applying the top-coating composition is carried out by a non-contact fluid micro-dispensing technique, preferably an ink-jet printing process.

[0014]

[0014] Also described herein are optical effect layers (OELs) and security documents produced by the methods described herein, as well as decorative elements and decorative objects comprising one or more optical OELs described herein.

[0015]

[0015] Also described is a method for producing a security document, or a decorative element or body, the method comprising: a) providing a security document, or a decorative element or body, and b) providing an optical effect layer, such as those described in the present specification, in particular those obtained by the method described in the present specification, which is included by the security document or the decorative element or body.

[0016]

[0016] The method described herein advantageously allows the creation of an optical effect layer (OEL) consisting of a single layer and comprising two or more areas of a radiation curable coating composition comprising non-spherical magnetic or magnetizable pigment particles, said two or more areas comprising non-spherical magnetic or magnetizable pigment particles oriented according to different orientation patterns at high resolution, said method not requiring the use of a photomask or a curing unit equipped with a laser or an addressable LED curing unit.

[0017]

[0017] The method advantageously described herein uses two compositions, which are applied to each other in a wet-on-wet state. In particular, the method according to the invention allows the production of optical effect layers (OELs) universally exhibiting one or more indicia and can be easily carried out on an industrial scale at high production rates. The two compositions used in the method described herein comprise, as a first composition, a radiation-curable coating composition comprising non-spherical magnetic or magnetisable pigment particles, which is applied onto a substrate (x20), and, as a second composition, a top-coating composition, which is applied at least partially onto the radiation-curable coating composition comprising the pigment particles and partially overlaps (i.e. overlaps in at least one area) said composition, when the radiation-curable coating composition is still in a wet unpolymerized state, and is applied in the form of one or more indicia.

[0018]

[0018] The present invention provides a reliable and easy to implement method of producing a highly visible optical effect layer (OEL) exhibiting one or more indicia as described herein. The disclosed method advantageously allows the production of security documents and articles with customer-specific magnetic designs that also exhibit one or more indicia in an easy to implement and highly reliable manner with generic online changes, without requiring customization of magnet assemblies used to orient non-spherical magnetic or magnetizable pigment particles for each variable or individualized indicia and for each and every customer-specific optical effect layer (OEL), and without requiring the use of curing units with photomasks or addressable LED curing units.

[0019]

[0019] The method described herein for producing an optical effect layer (OEL) exhibiting one or more indicia (x30) on a substrate (x20) described herein is described in more detail below with reference to the drawings and specific embodiments. FIG. 1 illustrates diagrammatically non-spherical, in particular platelet-shaped, pigment particles. 2A-2K illustrate a schematic method of producing an optical effect layer (OEL) on a substrate (220) according to the present invention, in particular: 2A1,2 diagrammatically illustrate a method of producing an optical effect layer (OEL) on a substrate (220) according to the present invention. The method comprises the steps of: b) at least partially applying a top-coating composition on a coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); c) after step b) at least partially curing the one or more indicia (230) and one or more areas of the coating layer (210) below said one or more indicia (230) with a LED curing unit (250); d) after step c) of the coating layer (210) d) of exposing the coating layer (210) to a magnetic field of a magnetic field generator (B1) in order to uniaxially orient (2A1) or biaxially orient (2A2) at least a portion of the non-spherical magnetic or magnetisable pigment particles in the not yet cured areas; and e) of at least partially curing the coating layer (210) in a curing unit (260) radiating at least between 250 nm and 320 nm, partially simultaneously with step d) (Figure 2A1) or after step d) (Figure 2A2). 2B illustrates diagrammatically a method for producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of: applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b), exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetizable pigment particles; partially simultaneously with said orienting step, removing the indicia (230) and the coating under the indicia (230) while maintaining the magnetic field generating device (B1) in the vicinity of the coating layer (210). The method includes the steps of: c) at least partially curing one or more areas of the layer (210) in an LED curing unit (250); d) after step c) exposing the coating layer (210) to a magnetic field of a second magnetic field generator (B2) in order to orient at least a portion of the magnetic or magnetizable pigment particles in the yet uncured areas of the coating layer (210); and e) partially simultaneously with step d) at least partially curing the coating layer (210) in an Hg curing unit (260) while maintaining the magnetic field generator (B2) in the vicinity of the coating layer (210). 2C illustrates diagrammatically a method for producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of exposing a coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles, and partly simultaneously with said step, a step b) of applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230) while maintaining the magnetic field generating device (B1) in the vicinity of the coating layer (210), and after step b), removing the one or more indicia (230) and the coating under said one or more indicia (230) while maintaining the magnetic field generating device (B1) in the vicinity of the coating layer (210). the step c) of at least partially curing one or more areas of the coating layer (210) with a LED curing unit (250); after step c), a step d) of exposing the coating layer (210) to a magnetic field of a second magnetic field generator (B2) in order to orient at least a portion of the magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and partially simultaneously with step d), a step e) of at least partially curing the coating layer (210) with a curing unit (260) emitting at least between 250 nm and 320 nm while maintaining the second magnetic field generator (B2) in the vicinity of the coating layer (210). Fig. 2D illustrates diagrammatically a method for producing an optical effect layer (OEL) on a substrate (220) according to the invention, comprising the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generator (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles, and partially simultaneously with said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230) while maintaining the magnetic field generator (B1) in the vicinity of the coating layer (210); after step b), at least partially curing the one or more indicia (230) and one or more areas of the coating layer (210) below said one or more indicia (230) with a LED curing unit (250) while maintaining the magnetic field generator (B1) in the vicinity of the coating layer (210); the step d) of exposing the coating layer (210) to a magnetic field of a second magnetic field generator (B2) after step c) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the not yet cured areas of the coating layer (210) in a biaxial direction; the step of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) after said step in order to orient at least a portion of the magnetic or magnetisable pigment particles in the not yet cured areas of the coating layer (210); and the step e) of at least partially curing the coating layer (210) in a curing unit (260) radiating at least between 250 nm and 320 nm while keeping the magnetic field generator (B3) in the vicinity of the coating layer (210) partially simultaneously with said step. 2E illustrates diagrammatically a method for producing an optical effect layer (OEL) on a substrate (220) according to the present invention, comprising the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to biaxially orient at least a portion of the non-spherical magnetic or magnetisable pigment particles, after said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b) curing the one or more indicia (230) and one or more areas of the coating layer (210) beneath said one or more indicia (230) with a LED curing unit (250). a step c) of at least partially curing; after step c), a step d) of exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and partially simultaneously with step d), a step e) of at least partially curing the coating layer (210) in a curing unit (260) radiating at least between 250 nm and 320 nm while maintaining the second magnetic field generating device (B2) in the vicinity of the coating layer (210). 2F, 2G diagrammatically illustrate a method of producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in a biaxial direction; after said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b) exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles; partially simultaneously with said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230), while maintaining the second magnetic field generating device (B2) in the vicinity of the coating layer (210). The method includes step c) of at least partially curing the indicia (230) and one or more areas of the coating layer (210) below the one or more indicia (230) with an LED curing unit (250); after step c), step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generating device (B3) in order to orient at least a portion of the non-spherical magnetic or magnetizable pigment particles in the not yet cured areas of the coating layer (210); and step e) of at least partially curing the coating layer (x10) with a curing unit (260) radiating at least between 250 nm and 320 nm, partially simultaneously with step d) (Figure 2F) or after step d) (Figure 2G). 2H, 2I diagrammatically illustrate a method of producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in biaxial direction; after said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b) exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles; after said step b) applying a top-coating composition on the coating layer (210) in the form of one or more indicia (x30) and one or more indicia (x40); the step c) of at least partially curing one or more areas of the coating layer (210) under the first curing device (230) with a LED curing unit (250); after step c), a step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and partly simultaneously with step d) (Figure 2H) or after step d) (Figure 2I), a step e) of at least partially curing the coating layer (x10) with a curing unit (260) emitting at least between 250 nm and 320 nm. 2J illustrates diagrammatically a method of producing an optical effect layer (OEL) on a substrate (220) according to the invention, comprising the steps of: exposing a coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in a biaxial direction; after said step, exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles; partially simultaneously with said step, a step b) of applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230) while maintaining the second magnetic field generating device (B2) in the vicinity of the coating layer (210); after step b), maintaining the second magnetic field generating device (B2) in the vicinity of the coating layer (210). the step of at least partially curing the one or more indicia (230) and one or more areas of the coating layer (210) beneath said one or more indicia (230) in an LED curing unit (250) while maintaining the one or more indicia (230) in the vicinity of the coating layer (210); the step of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) after step c) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and the step of at least partially curing the coating layer (x10) in a curing unit (260) radiating at least between 250 nm and 320 nm while maintaining the third magnetic field generator (B3) in the vicinity of the coating layer (210) partially simultaneously with step d). Fig. 2K illustrates diagrammatically a method for producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in a biaxial direction; after said step, exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles; after said step, a step b) of applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b), applying a top-coating composition (x30) under the one or more indicia (230) and under the one or more indicia (230). the step c) of at least partially curing one or more areas of the coating layer (210) in an LED curing unit (250); after step c), a step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and partially simultaneously with step d), a step e) of at least partially curing the coating layer (x10) in a curing unit (260) radiating at least between 250 nm and 320 nm while maintaining the third magnetic field generator (B3) in the vicinity of the coating layer (210). 3A and B illustrate generally a magnetic field generating device for biaxially (FIG. 3A) or uniaxially (FIG. 3B) orienting magnetic or magnetizable pigment particles in a coating layer (310) on a substrate (320). 4A-D show photographs of OELs prepared by methods according to the invention (E1-E36) and by comparative methods (C1-C26). [Brief description of the drawings]

[0020] [Figure 1] FIG. 1 illustrates diagrammatically non-spherical, in particular platelet-shaped, pigment particles. [Figure 2A-1]2A1,2 diagrammatically illustrate a method of producing an optical effect layer (OEL) on a substrate (220) according to the present invention. The method comprises the steps of: b) at least partially applying a top-coating composition on a coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); c) after step b) at least partially curing the one or more indicia (230) and one or more areas of the coating layer (210) below said one or more indicia (230) with a LED curing unit (250); d) after step c) of the coating layer (210) d) of exposing the coating layer (210) to a magnetic field of a magnetic field generator (B1) in order to uniaxially orient (2A1) or biaxially orient (2A2) at least a portion of the non-spherical magnetic or magnetisable pigment particles in the not yet cured areas; and e) of at least partially curing the coating layer (210) in a curing unit (260) radiating at least between 250 nm and 320 nm, partially simultaneously with step d) (Figure 2A1) or after step d) (Figure 2A2). [Figure 2A-2]2A1,2 diagrammatically illustrate a method of producing an optical effect layer (OEL) on a substrate (220) according to the present invention. The method comprises the steps of: b) at least partially applying a top-coating composition on a coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); c) after step b) at least partially curing the one or more indicia (230) and one or more areas of the coating layer (210) below said one or more indicia (230) with a LED curing unit (250); d) after step c) of the coating layer (210) d) of exposing the coating layer (210) to a magnetic field of a magnetic field generator (B1) in order to uniaxially orient (2A1) or biaxially orient (2A2) at least a portion of the non-spherical magnetic or magnetisable pigment particles in the not yet cured areas; and e) of at least partially curing the coating layer (210) in a curing unit (260) radiating at least between 250 nm and 320 nm, partially simultaneously with step d) (Figure 2A1) or after step d) (Figure 2A2). [Figure 2B]2B illustrates diagrammatically a method for producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of: applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b), exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetizable pigment particles; partially simultaneously with said orienting step, removing the indicia (230) and the coating under the indicia (230) while maintaining the magnetic field generating device (B1) in the vicinity of the coating layer (210). The method includes the steps of: c) at least partially curing one or more areas of the layer (210) in an LED curing unit (250); d) after step c) exposing the coating layer (210) to a magnetic field of a second magnetic field generator (B2) in order to orient at least a portion of the magnetic or magnetizable pigment particles in the yet uncured areas of the coating layer (210); and e) partially simultaneously with step d) at least partially curing the coating layer (210) in an Hg curing unit (260) while maintaining the magnetic field generator (B2) in the vicinity of the coating layer (210). [Figure 2C]2C illustrates diagrammatically a method for producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of exposing a coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles, and partly simultaneously with said step, a step b) of applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230) while maintaining the magnetic field generating device (B1) in the vicinity of the coating layer (210), and after step b), removing the one or more indicia (230) and the coating under said one or more indicia (230) while maintaining the magnetic field generating device (B1) in the vicinity of the coating layer (210). the step c) of at least partially curing one or more areas of the coating layer (210) with a LED curing unit (250); after step c), a step d) of exposing the coating layer (210) to a magnetic field of a second magnetic field generator (B2) in order to orient at least a portion of the magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and partially simultaneously with step d), a step e) of at least partially curing the coating layer (210) with a curing unit (260) emitting at least between 250 nm and 320 nm while maintaining the second magnetic field generator (B2) in the vicinity of the coating layer (210). [Figure 2D]Fig. 2D illustrates diagrammatically a method for producing an optical effect layer (OEL) on a substrate (220) according to the invention, comprising the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generator (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles, and partially simultaneously with said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230) while maintaining the magnetic field generator (B1) in the vicinity of the coating layer (210); after step b), at least partially curing the one or more indicia (230) and one or more areas of the coating layer (210) below said one or more indicia (230) with a LED curing unit (250) while maintaining the magnetic field generator (B1) in the vicinity of the coating layer (210); the step d) of exposing the coating layer (210) to a magnetic field of a second magnetic field generator (B2) after step c) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the not yet cured areas of the coating layer (210) in a biaxial direction; the step of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) after said step in order to orient at least a portion of the magnetic or magnetisable pigment particles in the not yet cured areas of the coating layer (210); and the step e) of at least partially curing the coating layer (210) in a curing unit (260) radiating at least between 250 nm and 320 nm while keeping the magnetic field generator (B3) in the vicinity of the coating layer (210) partially simultaneously with said step. [Figure 2E]2E illustrates diagrammatically a method for producing an optical effect layer (OEL) on a substrate (220) according to the present invention, comprising the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to biaxially orient at least a portion of the non-spherical magnetic or magnetisable pigment particles, after said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b) curing the one or more indicia (230) and one or more areas of the coating layer (210) beneath said one or more indicia (230) with a LED curing unit (250). a step c) of at least partially curing; after step c), a step d) of exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and partially simultaneously with step d), a step e) of at least partially curing the coating layer (210) in a curing unit (260) radiating at least between 250 nm and 320 nm while maintaining the second magnetic field generating device (B2) in the vicinity of the coating layer (210). [Figure 2F]2F, 2G diagrammatically illustrate a method of producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in a biaxial direction; after said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b) exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles; partially simultaneously with said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230), while maintaining the second magnetic field generating device (B2) in the vicinity of the coating layer (210). The method includes step c) of at least partially curing the indicia (230) and one or more areas of the coating layer (210) below the one or more indicia (230) with an LED curing unit (250); after step c), step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generating device (B3) in order to orient at least a portion of the non-spherical magnetic or magnetizable pigment particles in the not yet cured areas of the coating layer (210); and step e) of at least partially curing the coating layer (x10) with a curing unit (260) radiating at least between 250 nm and 320 nm, partially simultaneously with step d) (Figure 2F) or after step d) (Figure 2G). [Figure 2G]2F, 2G diagrammatically illustrate a method of producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in a biaxial direction; after said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b) exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles; partially simultaneously with said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230), while maintaining the second magnetic field generating device (B2) in the vicinity of the coating layer (210). The method includes step c) of at least partially curing the indicia (230) and one or more areas of the coating layer (210) below the one or more indicia (230) with an LED curing unit (250); after step c), step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generating device (B3) in order to orient at least a portion of the non-spherical magnetic or magnetizable pigment particles in the not yet cured areas of the coating layer (210); and step e) of at least partially curing the coating layer (x10) with a curing unit (260) radiating at least between 250 nm and 320 nm, partially simultaneously with step d) (Figure 2F) or after step d) (Figure 2G). [Figure 2H]2H, 2I diagrammatically illustrate a method of producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in biaxial direction; after said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b) exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles; after said step b) applying a top-coating composition on the coating layer (210) in the form of one or more indicia (x30) and one or more indicia (x40); the step c) of at least partially curing one or more areas of the coating layer (210) under the first curing device (230) with a LED curing unit (250); after step c), a step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and partly simultaneously with step d) (Figure 2H) or after step d) (Figure 2I), a step e) of at least partially curing the coating layer (x10) with a curing unit (260) emitting at least between 250 nm and 320 nm. [Figure 2I]2H, 2I diagrammatically illustrate a method of producing an optical effect layer (OEL) on a substrate (220) according to the invention. The method comprises the steps of: exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in biaxial direction; after said step b) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b) exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles; after said step b) applying a top-coating composition on the coating layer (210) in the form of one or more indicia (x30) and one or more indicia (x40); the step c) of at least partially curing one or more areas of the coating layer (210) under the first curing device (230) with a LED curing unit (250); after step c), a step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and partly simultaneously with step d) (Figure 2H) or after step d) (Figure 2I), a step e) of at least partially curing the coating layer (x10) with a curing unit (260) emitting at least between 250 nm and 320 nm. [Figure 2J]2J illustrates diagrammatically a method of producing an optical effect layer (OEL) on a substrate (220) according to the invention, comprising the steps of: exposing a coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in a biaxial direction; after said step, exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles; partially simultaneously with said step, a step b) of applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230) while maintaining the second magnetic field generating device (B2) in the vicinity of the coating layer (210); after step b), maintaining the second magnetic field generating device (B2) in the vicinity of the coating layer (210). the step of at least partially curing the one or more indicia (230) and one or more areas of the coating layer (210) beneath said one or more indicia (230) in an LED curing unit (250) while maintaining the one or more indicia (230) in the vicinity of the coating layer (210); the step of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) after step c) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and the step of at least partially curing the coating layer (x10) in a curing unit (260) radiating at least between 250 nm and 320 nm while maintaining the third magnetic field generator (B3) in the vicinity of the coating layer (210) partially simultaneously with step d). [Figure 2K]A method for producing an optical effect layer (OEL) on a substrate (220) according to the invention is illustrated diagrammatically, comprising the steps of: exposing a coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in a biaxial direction; after said step, exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles; after said step, a) applying a top-coating composition on the coating layer (210), said top-coating composition being applied in the form of one or more indicia (230); after step b), applying a top-coating composition (x30) under the one or more indicia (230) and under the one or more indicia (230). the step c) of at least partially curing one or more areas of the coating layer (210) in an LED curing unit (250); after step c), a step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) in order to orient at least a portion of the non-spherical magnetic or magnetisable pigment particles in the yet uncured areas of the coating layer (210); and partially simultaneously with step d), a step e) of at least partially curing the coating layer (x10) in a curing unit (260) radiating at least between 250 nm and 320 nm while maintaining the third magnetic field generator (B3) in the vicinity of the coating layer (210). [Figure 3A] 3A and B illustrate generally a magnetic field generating device for biaxially (FIG. 3A) or uniaxially (FIG. 3B) orienting magnetic or magnetizable pigment particles in a coating layer (310) on a substrate (320). [Figure 3B] 3A and B illustrate generally a magnetic field generating device for biaxially (FIG. 3A) or uniaxially (FIG. 3B) orienting magnetic or magnetizable pigment particles in a coating layer (310) on a substrate (320). [Figure 4A] 4A-D show photographs of OELs prepared by methods according to the invention (E1-E36) and by comparative methods (C1-C26). [Figure 4B]4A-D show photographs of OELs prepared by methods according to the invention (E1-E36) and by comparative methods (C1-C26). [Figure 4C] 4A-D show photographs of OELs prepared by methods according to the invention (E1-E36) and by comparative methods (C1-C26). [Figure 4D] 4A-D show photographs of OELs prepared by methods according to the invention (E1-E36) and by comparative methods (C1-C26).

[0021] [Detailed Description] (definition) The following definitions are discussed in the detailed description and are used to interpret the meaning of terms recited in the claims.

[0022]

[0021] As used herein, the term "at least one" is meant to define one or more than one, for example, 1, 2, or 3.

[0023]

[0022] The terms "about" and "substantially" used in this specification mean that the amount or value in question is a specified specific value or some other value in its vicinity. In general, the terms "about" and "substantially" indicating a value are intended to indicate a range within ±5% of the value. As an example, the expression "about 100" indicates a range of 100 ±5, i.e., a range of 95 to 105. In general, when the terms "about" and "substantially" are used, it can be expected that similar results or effects of the present invention can be obtained within a range of ±5% of the indicated value.

[0024]

[0023] The term "substantially parallel" refers to a deviation of 10° or less from a parallel alignment, and the term "substantially perpendicular" refers to a deviation of 10° or less from a perpendicular alignment.

[0025]

[0024] As used herein, the term "and / or" means that all or only one of the elements of the group may be present. For example, "A and / or B" is intended to mean "A only, or B only, or both A and B." In the case of "A only," the term also encompasses the possibility that B is not present, i.e., "A only and no B."

[0026]

[0025] The term "comprises" as used herein is meant to be non-exclusive and non-limiting. Thus, for example, a coating composition comprising compound A may comprise other compounds in addition to A. However, the term "comprises" also encompasses the more restrictive meanings of "consisting essentially of" and "consisting of" as specific embodiments thereof, so that, for example, "a fountain solution comprising A, B and optionally C" may also consist (substantially) of A and B, or may consist (substantially) of A, B and C.

[0027]

[0026] As used herein, the term "optical effect layer" (OEL) refers to a coating layer comprising oriented magnetic or magnetizable pigment particles, which are oriented by a magnetic field, and which are fixed / solidified (i.e., after curing) in their orientation and position to form a magnetically induced image.

[0028]

[0027] The term "coating composition" refers to any composition capable of forming an optical effect layer (OEL) on a solid substrate, preferably, but not limited to, applied by a printing method. The coating composition comprises the non-spherical magnetic or magnetizable pigment particles described herein, and a binder as described herein. The term "top coating composition" refers to a composition that does not comprise the non-spherical magnetic or magnetizable pigment particles described herein.

[0029]

[0028] As used herein, the term "wet" refers to an uncured coating layer, e.g., a coating layer in which non-spherical magnetic or magnetizable pigment particles are still able to change their position and orientation under the influence of external forces acting on them.

[0030]

[0029] The term "security document" refers to a document that is typically protected against counterfeiting or fraud by at least one security feature. Examples of security documents include, but are not limited to, documents of value and articles of value.

[0031]

[0030] The term "security feature" is used to describe an image, pattern, or graphic element that can be used for authentication purposes.

[0032]

[0031] Where this detailed description refers to "preferred" embodiments / features, combinations of these "preferred" embodiments / features shall also be deemed to be disclosed to the extent that such combinations of "preferred" embodiments / features make technical sense.

[0033]

[0032] The present invention provides a method for making an optical effect layer (OEL) exhibiting one or more indicia (x30) on a substrate (x20), said OEL further exhibiting one or more indicia (x30) based on magnetically oriented non-spherical magnetic or magnetizable pigment particles. A preferred example of said process is shown in Figures 2A-2K.

[0034]

[0033] The method described herein comprises the step a) of applying to the surface of a substrate (x20) as described herein a radiation curable coating composition comprising non-spherical magnetic or magnetizable pigment particles as described herein and one or more photoreactive compounds not absorbing in the range of about 350 nm to about 470 nm as described herein, said composition being in a first liquid state that allows its application as a layer and is not yet cured (i.e. wet), and the pigment particles are able to move and rotate within the layer. As the radiation curable coating composition described herein is to be provided on the surface of the substrate (x20), the radiation curable coating composition comprises at least a binder material and magnetic or magnetizable pigment particles, said composition being in a form that allows its processing in the desired printing or coating equipment. Preferably, said step a) is carried out by a printing process preferably selected from the group consisting of screen printing, gravure printing, flexography, intaglio printing (also referred to in the art as engraved copper printing, engraved steel die printing), pad printing and curtain coating, more preferably selected from the group consisting of intaglio printing, screen printing, gravure printing, pad printing and flexography, even more preferably selected from the group consisting of screen printing, gravure printing, pad printing and flexography. According to a preferred embodiment, step a) is carried out by a printing process selected from the group consisting of screen printing, gravure printing and flexography.

[0035]

[0034] The non-spherical magnetic or magnetizable pigment particles described in this specification are preferably prolate or oblate ellipsoidal, platelet-like or needle-like magnetic or magnetizable pigment particles, or a mixture of two or more thereof, more preferably platelet-like particles.

[0036]

[0035] The non-spherical magnetic or magnetizable pigment particles described herein are defined as having anisotropic reflectivity for incident electromagnetic radiation, for which the cured binder material is at least partially transparent, due to their non-spherical shape. The term "anisotropic reflectivity" as used herein indicates that the proportion of incident radiation from a first angle to a certain (viewing) direction (second angle) reflected by the particle is a function of the particle's orientation, i.e., a change in the particle's orientation with respect to the first angle can cause a different magnitude of reflection in the viewing direction. Preferably, the non-spherical magnetic or magnetizable pigment particles described herein have anisotropic reflectivity for incident electromagnetic radiation in part or in the complete wavelength range of about 200 to about 2500 nm, more preferably about 400 to about 700 nm, such that a change in the particle's orientation results in a change in the reflection by the particle in a certain direction. As known by those skilled in the art, the magnetic or magnetizable pigment particles described herein differ from conventional pigments in that said conventional pigment particles exhibit the same color and reflectance independent of particle orientation, whereas the magnetic or magnetizable pigment particles described herein exhibit reflectance or color, or both, that are dependent on particle orientation.

[0037]

[0036] The radiation curable coating composition described herein and the coating layer (x10) described herein contain the non-spherical, preferably platelet-shaped magnetic or magnetizable pigment particles described herein in an amount of preferably from about 5% to about 40% by weight, more preferably from 10% to about 30% by weight, the weight percentages being based on the total weight of the radiation curable coating composition or coating layer (x10).

[0038]

[0037] In the OELs described herein, the magnetic or magnetizable pigment particles described herein are dispersed in a radiation curable coating composition comprising a hardened binder material that fixes the orientation and position of the magnetic or magnetizable pigment particles. The binder material is at least in the hardened or solid state (also referred to herein as the second state) and is at least partially transparent to electromagnetic radiation in the range of wavelengths from 200 nm to 2500 nm, a range of wavelengths typically referred to as the "optical spectrum" and including the infrared, visible, and UV portions of the electromagnetic spectrum. Thus, the particles contained in the hardened or solid state binder material and their orientation dependent reflectance can be seen through the binder material at some wavelengths within this range. Preferably, the hardened binder material is at least partially transparent to electromagnetic radiation in the range of wavelengths from 200 nm to 800 nm, more preferably from 400 nm to 700 nm. In this specification, the term "transmittance" indicates that the transmission of electromagnetic radiation through a 20 μm layer of the cured binder material present in the OEL (not including the non-spherical magnetic or magnetisable pigment particles, but including all other optional components of the OEL, if such components are present) is at least 50%, more preferably at least 60%, even more preferably at least 70% at the relevant wavelength. This can be determined by well-established test methods, for example by measuring the transmittance of a test piece of the cured binder material (without the non-spherical magnetic or magnetisable pigment particles) according to DIN 5036-3 (1979-11). If the OEL serves as a covert security feature, then typically technical means are required to detect the (completed) optical effect produced by the OEL in the respective lighting conditions including the selected non-visible wavelengths, said detection requiring that the wavelength of the incident radiation is selected outside the visible range, for example in the near UV range.

[0039] Suitable examples of non-spherical, preferably platelet-shaped, magnetic or magnetizable pigment particles as described herein include, but are not limited to, pigment particles comprising a magnetic metal selected from the group consisting of cobalt (Co), iron (Fe), and nickel (Ni); a magnetic alloy of iron, manganese, cobalt, nickel, or a mixture of two or more thereof; a magnetic oxide of chromium, manganese, cobalt, iron, nickel, or a mixture of two or more thereof; or a mixture of two or more thereof. The term "magnetic" with respect to metals, alloys, and oxides covers ferromagnetic or ferrimagnetic metals, alloys, and oxides. The magnetic oxides of chromium, manganese, cobalt, iron, nickel, or a mixture of two or more thereof may be pure or mixed oxides. Examples of magnetic oxides include, but are not limited to, hematite (Fe2O3), magnetite (Fe3O4), chromium dioxide (CrO2), magnetic ferrite (MFe2O4), magnetic spinel (MR2O4), magnetic hexaferrite (MFe 12 O 19 ), magnetic orthoferrite (RFeO3), and magnetic garnet M3R2(AO4)3, where M represents a divalent metal, R represents a trivalent metal, and A represents a tetravalent metal.

[0040]

[0039] Examples of non-spherical, preferably platelet-shaped, magnetic or magnetizable pigment particles as described herein include, but are not limited to, pigment particles comprising a magnetic layer M consisting of one or more of a magnetic metal, such as cobalt (Co), iron (Fe), or nickel (Ni); and a magnetic alloy of iron, cobalt, or nickel, said magnetic or magnetizable pigment particles may be a multi-layer structure comprising one or more further layers. Preferably, the one or more further layers are a layer A independently of one or more selected from the group consisting of metal fluorides such as magnesium fluoride (MgF), silicon oxide (SiO), silicon dioxide (SiO), titanium oxide (TiO), and aluminum oxide (AlO), more preferably silicon dioxide (SiO); or a layer B independently of one or more selected from the group consisting of metals and metal alloys, preferably selected from the group consisting of reflective metals and reflective alloys, more preferably one or more selected from the group consisting of silver (Ag), aluminum (Al), chromium (Cr), and nickel (Ni), even more preferably aluminum (Al); or a combination of one or more layers A such as those mentioned above and one or more layers B such as those mentioned above. Representative examples of platelet-shaped magnetic or magnetizable pigment particles having such a multilayer structure include, but are not limited to, A / M multilayer structures, A / M / A multilayer structures, A / M / B multilayer structures, A / B / M / A multilayer structures, A / B / M / B multilayer structures, A / B / M / B / A / multilayer structures, B / M multilayer structures, B / M / B multilayer structures, B / A / M / A multilayer structures, B / A / M / B multilayer structures, B / A / M / B / A / multilayer structures, where layer A, magnetic layer M, and layer B are selected from those described above.

[0041]

[0040] The radiation curable coating composition described herein may comprise non-spherical, preferably platelet-shaped, optically variable magnetic or magnetisable pigment particles and / or non-spherical, preferably platelet-shaped, magnetic or magnetisable pigment particles not having optically variable properties. Preferably, at least a portion of the magnetic or magnetisable pigment particles described herein are constituted by non-spherical, preferably platelet-shaped, optically variable magnetic or magnetisable pigment particles. In addition to the overt security provided by the colour shifting properties of the optically variable magnetic or magnetisable pigment particles, which allow the easy detection, recognition and / or discrimination of articles or security documents bearing the inks, coating compositions or coating layers comprising the optically variable magnetic or magnetisable pigment particles described herein from their possible counterfeits using unaided human senses, the optical properties of the optically variable magnetic or magnetisable pigment particles may also be used as a machine-readable tool for the recognition of OELs. Thus, the optical properties of the optically variable magnetic or magnetisable pigment particles may simultaneously be used as a covert or semi-covert security feature in the authentication process in which the optical (e.g. spectral) properties of the pigment particles are analysed, thus improving counterfeit resistance.

[0042]

[0041] The use of non-spherical, preferably platelet-shaped, optically variable magnetic or magnetizable pigment particles in the coating layer to produce the OEL enhances the significance of the OEL as a security feature in security document applications, since such materials are reserved for the security document printing industry and are not generally commercially available.

[0043] As mentioned above, preferably at least a part of the non-spherical, preferably platelet-shaped, magnetic or magnetisable pigment particles is constituted by non-spherical, preferably platelet-shaped, optically variable magnetic or magnetisable pigment particles, which are preferably selected from the group consisting of magnetic thin film interference pigment particles, magnetic cholesteric liquid crystal pigment particles, interference coated pigment particles comprising a magnetic material and mixtures of two or more thereof.

[0044]

[0043] Magnetic thin film interference pigment particles are known to those skilled in the art and are disclosed, for example, in U.S. Pat. No. 4,838,648; WO 2002 / 073250; EP 0686675; WO 2003 / 000801; U.S. Pat. No. 6,838,166; WO 2007 / 131833; EP 2402401; WO 2019 / 103937; WO 2020 / 006286 and the documents cited therein. Preferably, the magnetic thin film interference pigment particles include pigment particles having a 5-layer Fabry-Perot multilayer structure, and / or pigment particles having a 6-layer Fabry-Perot multilayer structure, and / or pigment particles having a 7-layer Fabry-Perot multilayer structure, and / or pigment particles having a multilayer structure combining one or more multilayer Fabry-Perot structures.

[0045]

[0044] A preferred five-layer Fabry-Perot multilayer structure consists of a multilayer structure of absorber / dielectric / reflector / dielectric / absorber, where the reflector and / or absorber are also magnetic layers, preferably the reflector and / or absorber are magnetic layers comprising nickel, iron, and / or cobalt, and / or magnetic alloys comprising nickel, iron, and / or cobalt, and / or magnetic oxides comprising nickel (Ni), iron (Fe), and / or cobalt (Co).

[0046] A preferred six-layer Fabry-Perot multilayer structure consists of the following multilayer structure: absorber / dielectric / reflector / magnetic / dielectric / absorber.

[0047] A preferred seven-layer Fabry-Perot multilayer structure consists of an absorber / dielectric / reflector / magnetic / reflector / dielectric / absorber multilayer structure such as that disclosed in US Pat. No. 4,838,648.

[0048]

[0047] Preferred pigment particles having a multilayer structure combining one or more Fabry-Perot structures are described in WO 2019 / 103937, which consist of a combination of at least two Fabry-Perot structures, said two Fabry-Perot structures independently comprising a reflector layer, a dielectric layer and an absorber layer, the reflector and / or absorber layer each independently may comprise one or more magnetic materials and / or the magnetic layer is sandwiched between the two structures. WO 2020 / 006 / 286 and EP 3587500 disclose further preferred pigment particles having a multilayer structure.

[0049]

[0048] Preferably, the reflector layer described herein is selected from the group consisting of metals and metal alloys, preferably selected from the group consisting of reflective metals and reflective metal alloys, more preferably selected from the group consisting of aluminum (Al), silver (Ag), copper (Cu), gold (Au), platinum (Pt), tin (Sn), titanium (Ti), palladium (Pd), rhodium (Rh), niobium (Nb), chromium (Cr), nickel (Ni), and alloys thereof, even more preferably independently selected from one or more of the group consisting of aluminum (Al), chromium (Cr), nickel (Ni), and alloys thereof, even more preferably independently selected from aluminum (Al). Preferably, the dielectric layer is independently selected from the group consisting of metal fluorides such as magnesium fluoride (MgF2), aluminum fluoride (AlF3), cerium fluoride (CeF3), lanthanum fluoride (LaF3), sodium aluminum fluoride (e.g., Na3AlF6), neodymium fluoride (NdF3), samarium fluoride (SmF3), barium fluoride (BaF2), calcium fluoride (CaF2), lithium fluoride (LiF), and metal oxides such as silicon oxide (SiO), silicon dioxide (SiO2), titanium oxide (TiO2), aluminum oxide (Al2O3), more preferably one or more independently selected from the group consisting of magnesium fluoride (MgF2) and silicon dioxide (SiO2), and even more preferably magnesium fluoride (MgF2). Preferably, the absorber layer is independently selected from the group consisting of aluminum (Al), silver (Ag), copper (Cu), palladium (Pd), platinum (Pt), titanium (Ti), vanadium (V), iron (Fe), tin (Sn), tungsten (W), molybdenum (Mo), rhodium (Rh), niobium (Nb), chromium (Cr), nickel (Ni), metal oxides thereof, metal sulfides thereof, metal carbides thereof, and metal alloys thereof, more preferably selected from the group consisting of chromium (Cr), nickel (Ni), metal oxides thereof, and metal alloys thereof, even more preferably selected from the group consisting of chromium (Cr), nickel (Ni), and alloys thereof.Preferably, the magnetic layer comprises nickel (Ni), iron (Fe) and / or cobalt (Co); and / or a magnetic alloy comprising nickel (Ni), iron (Fe) and / or cobalt (Co); and / or a magnetic oxide comprising nickel (Ni), iron (Fe) and / or cobalt (Co). When magnetic thin film interference pigment particles comprising a seven-layer Fabry-Perot structure are preferred, it is particularly preferred that the magnetic thin film interference pigment particles comprise a seven-layer Fabry-Perot absorber / dielectric / reflector / magnetic / reflector / dielectric / absorber multilayer structure consisting of a Cr / MgF2 / Al / Ni / Al / MgF2 / Cr multilayer structure.

[0050]

[0049] The magnetic thin film interference pigment particles described herein are considered to be safe for human health and the environment, and may be, for example, multilayer pigment particles based on a 5-layer Fabry-Perot multilayer structure, a 6-layer Fabry-Perot multilayer structure, a 7-layer Fabry-Perot multilayer structure, and pigment particles having a multilayer structure combining one or more Fabry-Perot multilayer structures, said pigment particles comprising one or more magnetic layers comprising a magnetic alloy having a substantially nickel-free composition comprising about 40% to about 90% by weight iron, about 10% to about 50% by weight chromium, and about 0% to about 30% by weight aluminum. Representative examples of multilayer pigment particles considered to be safe for human health and the environment can be found in EP 2402401, the entire contents of which are incorporated herein by reference.

[0051] Suitable magnetic cholesteric liquid crystal pigment particles exhibiting optically variable properties include, but are not limited to, magnetic single-layer cholesteric liquid crystal pigment particles and magnetic multi-layer cholesteric liquid crystal pigment particles. Such pigment particles are disclosed, for example, in WO 2006 / 063926, U.S. Pat. No. 6,582,781, and U.S. Pat. No. 6,531,221. WO 2006 / 063926 discloses monolayers and pigment particles obtained therefrom, with high brightness and color shifting properties, and with further specific properties such as magnetization. The disclosed monolayers and pigment particles are obtained therefrom by grinding the monolayers, and include a three-dimensionally crosslinked cholesteric liquid crystal mixture and magnetic nanoparticles. U.S. Pat. No. 6,582,781 and U.S. Pat. No. 6,410,130 disclose a method for producing a cholesteric liquid crystal pigment having a sequence A. 1 / B / A 2 The present invention discloses platelet-shaped cholesteric multi-layer pigment particles comprising: 1 and A 2 A and B may be the same or different and each comprises at least one cholesteric layer, B being an intermediate layer that absorbs all or part of the light transmitted by layers A1 and A2 and confers magnetic properties to said intermediate layer. US Patent No. 6,531,221 discloses platelet-shaped cholesteric multilayer pigment particles comprising the sequence A / B and optionally C, where A and C are absorbing layers containing pigment particles that impart magnetic properties and B is a cholesteric layer.

[0052]

[0051] Suitable interference coated pigments containing one or more magnetic materials include, but are not limited to, a structure consisting of a substrate selected from the group consisting of a core coated with one or more layers, at least one or one or more layers of the core having magnetic properties. For example, suitable interference coated pigments include a core consisting of a magnetic material such as those described above, said core being coated with one or more layers consisting of one or more metal oxides, or they have a structure consisting of a core consisting of synthetic or natural mica, layered silicates (e.g., talc, kaolin, and sericite), glass (e.g., borosilicate), silicon dioxide (SiO2), aluminum oxide (Al2O3), titanium oxide (TiO2), graphite, and mixtures of two or more thereof. In addition, one or more additional layers, such as a colored layer, may be present.

[0053]

[0052] The non-spherical, preferably platelet-shaped, magnetic or magnetisable pigment particles described herein preferably have a size d50 (measured by direct optical particle size distribution) of from about 2 μm to about 50 μm.

[0054]

[0053] The non-spherical, preferably platelet-shaped, magnetic or magnetizable pigment particles described in this specification may be surface treated to protect them from possible deterioration of the coating compositions and coating layers and / or to promote their incorporation into said coating compositions and coating layers, typically using corrosion-inhibiting materials and / or wetting agents.

[0055]

[0054] As described herein, the method described herein includes steps c) and e) of at least partially curing the coating layer (x10) to a second state in order to fix the magnetic or magnetisable pigment particles in their adopted positions and orientations. In the first liquid state of the radiation curable coating composition, the magnetic or magnetisable pigment particles can move and rotate, and in the second state, the magnetic or magnetisable pigment particles are fixed and set by using a type of radiation curable coating composition. For example, the components of the radiation curable coating composition other than the non-spherical magnetic or magnetisable pigment particles may take the form of an ink or radiation curable coating composition, such as those used in security applications, e.g., in the printing of banknotes. The aforementioned first and second states are brought about by using a material that exhibits an increase in viscosity in response to exposure to electromagnetic radiation. That is, when the flowable binder material is cured or solidified, said binder material changes to a second state and the non-spherical magnetic or magnetisable pigment particles are fixed in their current positions and orientations and can no longer move and rotate within the binder material. By "at least partially curing the coating layer (x10)" as used herein is meant that the non-spherical, preferably platelet-shaped, magnetic or magnetizable pigment particles are fixed / solidified in their adopted position and orientation and can no longer move or rotate (also referred to in the art as "pinning" the particles).

[0056]

[0055] The radiation curable coating composition used to prepare the coating layer (x10) described herein comprises non-spherical, preferably platelet-shaped, magnetic or magnetizable pigment particles as described herein, and one or more compounds that do not absorb in the range of about 350 nm to about 470 nm as described herein. Radiation curing, especially UV-Vis curing, advantageously leads to a momentary increase in the viscosity of the coating composition after exposure to radiation, thus preventing further migration of the pigment particles and, consequently, loss of information after the magnetic orientation step.

[0057]

[0056] A radiation curable coating composition comprising the non-spherical, preferably platelet-shaped, magnetic or magnetizable pigment particles described herein and one or more photoreactive compounds that do not absorb in the range of about 350 nm to about 470 nm described herein is a cationically curable composition. In other words, the radiation curable coating composition, preferably a UV-Vis curable coating composition, comprises monomers and / or oligomers that are cationically curable compounds.

[0058]

[0057] The cationically curable composition comprises one or more cationic compounds that are cured by a cationic mechanism, typically involving activation by radiation of one or more compounds that react and / or crosslink monomers and / or oligomers, thereby curing the coating composition, liberating a cationic species, such as an acid, which then initiates curing. Preferably, the one or more cationic curable compounds are selected from the group consisting of vinyl ethers, propenyl ethers, epoxides, oxetanes, glycidyl ethers, and tetrahydrofuran, cyclic ethers, lactones, cyclic thioethers, vinyl thioethers, propenyl thioethers, hydroxyl-containing compounds, and mixtures thereof, preferably vinyl ethers, propenyl ethers, epoxides, oxetanes, and cyclic ethers, such as tetrahydrofuran, lactones, and mixtures thereof.

[0059]

[0058] Preferably, the radiation curable coating composition comprising the non-spherical, preferably platelet-shaped, magnetic or magnetizable pigment particles described herein comprises one or more alicyclic epoxides which may be difunctional or polyfunctional, and may optionally further comprise one or more components selected from the group consisting of vinyl ethers, oxetanes, polyhydroxy compounds, and mixtures thereof.

[0060]

[0059] Preferably, the one or more cycloaliphatic epoxides described independently herein contain at least one cyclohexane group and at least two epoxy groups. Preferred cycloaliphatic epoxides contain more than one (i.e., at least two) cyclohexane groups and have structural formula (I): [ka] In the formula, -X- represents a single bond or a divalent group containing one or more atoms.

[0061] According to one embodiment, X is a divalent hydrocarbon group which is a linear or branched alkylene group having 1 to 18 carbon atoms, including, but not limited to, methylene, methylmethylene, dimethylmethylene, ethylene, propylene, and trimethylene.

[0062] According to one embodiment, X is a divalent alicyclic hydrocarbon or cycloalkyne group, such as 1,2-cyclopentylene, 1,3-cyclopentylene, cyclopentylidene, 1,2-cyclohexylene, 1,3-cyclohexylene, 1,4-cyclohexylene, and cyclohexylidene.

[0063] According to one embodiment, X is a divalent radical containing one or more oxygen-containing linking groups, which are -CO-, -O-CO-O-, -COO-, and -O-. According to one embodiment, a preferred epoxy derivative contains more than one cyclohexene oxide group and has the structural formula (I), and X is a divalent radical containing one or more oxygen-containing linking groups, which are -CO-, -O-CO-O-, -COO-, -O-, and has the structural formula (II), (III), or (IV): [ka] corresponds to 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate, where R1 to R9 are independently hydrogen or a linear or branched alkyl radical containing 1 to 12 carbon atoms, preferably containing 1 to 3 carbon atoms (e.g., methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, s-butyl, t-butyl, hexyl, octyl, decyl, and dodecyl), and preferably the cycloaliphatic epoxides having structural formula (II) are 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate, 3,4-epoxy-6-methyl-cyclohexylmethyl-3,4-epoxy-6-methylcyclohexanecarboxylate, 3,4-epoxy-2-methyl-cyclohexylmethyl-3,4-epoxy-2-methyl-cyclohexanecarboxylate, and 3,4-epoxy-4-methyl-cyclohexylmethyl-3,4-epoxy-4-methylcyclohexanecarboxylate; [ka] corresponds to a cycloaliphatic diepoxide ester of a dicarboxylic acid, R1 to R9 are independently hydrogen or a linear or branched alkyl radical containing from 1 to 12 carbon atoms, preferably containing from 1 to 3 carbon atoms (e.g., methyl, ethyl, n-propyl, isopropyl, butyl, hexyl, octyl, and decyl), A is a valence bond or a linear or branched divalent hydrocarbon radical, generally containing from 1 to 12 carbon atoms, preferably containing from 3 to 8 carbon atoms, such as an alkylene radical (e.g., trimethylene, tetramethylene, hexamethylene, and 2-ethylhexyl). cycloaliphatic radicals (e.g., 1,4-cyclohexane, 1,3-cyclohexane, and 1,2-cyclohexane), preferably the cycloaliphatic diepoxide esters of dicarboxylic acids having structural formula (III) are bis(3,4-epoxycyclohexylmethyl)adipate, bis(3,4-epoxy-6-methylcyclohexylmethyl)adipate, bis(3,4-epoxycyclohexylmethyl)oxalate, bis(3,4-epoxycyclohexylmethyl)pimelate, and bis(3,4-epoxycyclohexylmethyl)sebacate; [ka] R1 to R9 are independently hydrogen or a linear or branched hydrocarbon group containing 1 to 3 carbon atoms, and a preferred example of an alicyclic diepoxide having structural formula (IV) is 2-(3,4-epoxycyclohexyl-5,5-spiro-3,4-epoxy)cyclohexane-meta-dioxane.

[0064] According to one embodiment, the one or more alicyclic epoxides described herein have structural formula (V) or (VI): [ka]

[0065]

[0064] The cycloaliphatic epoxide or epoxides described herein may be hydroxy- or (meth)acrylate-modified, for example as sold under the names Cyclomer A400 (CAS: 64630-63-3) and Cyclomer M100 (CAS: 82428-30-6) by Daicel, or TTA15 and TTA16 by TetraChem / Jiangsu.

[0066]

[0065] For embodiments in which the radiation curable coating composition includes one or more vinyl ethers as described herein, the one or more vinyl ethers are preferably present in an amount less than about 25% by weight, preferably from about 3% to about 20% by weight, the weight percentage being based on the total weight of the radiation curable coating composition. Vinyl ethers are known in the art to accelerate curing and reduce tackiness, thereby limiting the risk of blocking and offset when printed sheets are placed in a stack immediately after printing and curing. They also improve the physical and chemical resistance of the printed security components and improve the flexibility of the printed, cured ink layer, which can be advantageous when the security inks of the invention are printed on plastic or polymeric substrates. Vinyl ethers also help reduce the viscosity of the ink while strongly copolymerizing with the ink vehicle.

[0067]

[0066] Examples of preferred vinyl ethers include methyl vinyl ether, ethyl vinyl ether, n-propyl vinyl ether, n-butyl vinyl ether, iso-butyl vinyl ether, ethylhexyl vinyl ether, octadecyl vinyl ether, dodecyl vinyl ether, isopropyl vinyl ether, tert-butyl vinyl ether, tert-amyl vinyl ether, cyclohexyl vinyl ether, cyclohexanedimethanol monovinyl ether, cyclohexanedimethanol divinyl ether, 4-(vinyloxymethyl)cyclohexylmethylbenzoate, phenyl vinyl ether, methylphenyl vinyl ether, methoxyphenyl vinyl ether, 2-chloroethyl vinyl ether, 2-hydroxyethyl vinyl ether, 4-hydroxybutyl vinyl ether, 1,6-hexanediol monovinyl ether, ethylene glycol divinyl ether, ethylene glycol monovinyl ether, 1,4-butanediol divinyl ether, 1,6-hexanediol divinyl ether, ether, 4-(vinyloxy)butyl benzoate, bis[4-(vinyloxy)butyl]adipate, bis[4-(vinyloxy)butyl]succinate, bis[4-(vinyloxymethyl)cyclohexylmethyl]glutarate, 4-(vinyloxy)butyl stearate, trimethylolpropane trivinyl ether, propenyl ether of propylene carbonate, diethylene glycol monovinyl ether, diethylene glycol divinyl ether, ethylene glycol butyl vinyl ether, dipropylene glycol divinyl ether, triethylene glycol divinyl ether, triethylene glycol methyl vinyl ether, triethylene glycol monobutyl vinyl ether, tetraethylene glycol divinyl ether, poly(tetrahydrofuran) divinyl ether, polyethylene glycol-520 methyl vinyl ether, pluriol-E200 divinyl ether, tris[4-(vinyloxy)butyl]trimellitate, 1,4-bis(2-vinyloxyethoxy)benzene, 2,Examples of suitable vinyl ethers include 2-bis(4-vinyloxyethoxyphenyl)propane, bis[4-(vinyloxy)methyl]cyclohexyl]methyl]terephthalate, and bis[4-(vinyloxy)methyl]cyclohexyl]methyl]isophthalate. Suitable vinyl ethers are commercially available under the names EVE, IBVE, DDVE, ODVE, BDDVE, DVE-2, DVE-3, CHVE, CHDM-di, and HBVE from BASF. One or more of the vinyl ethers described herein may be hydroxy- or (meth)acrylate-modified (e.g., VEEAR®, 2-(2-vinyloxyethoxy)ethyl acrylate (CAS: 86273-46-3) from Nippon Shokubai).

[0068]

[0067] For embodiments in which the radiation curable coating composition comprises one or more oxetanes described herein, the one or more oxetanes are preferably present in an amount of about 20% by weight or less, preferably from about 3% by weight to about 15% by weight or less, said weight percentages being based on the total weight of the radiation curable coating composition.

[0069]

[0068] Oxetanes are known in the art to accelerate curing and reduce tackiness, thereby limiting the risk of blocking and offset when print sheets are placed in a stack immediately after print curing. They also help to reduce the viscosity of the ink while strongly copolymerizing with the composition. Preferred examples of oxetanes include trimethylene oxide, 3,3-dimethyloxetane, trimethylolpropaneoxetane, 3-ethyl-3-hydroxymethyloxetane, 3-ethyl-3-[(2-ethylhexyloxy)methyl]oxetane, 3,3-dicyclomethyloxetane, 3-ethyl-3-phenoxymethyloxetane, bis([1-ethyl(3-oxetanyl)]methyl)ether, 1,4-bis[3-ethyl-3-oxetanylmethoxy)methyl]benzene, 3,3-dimethyl-2(p-methoxy-phenyl)-oxetane, 3-ethyl-[(tri-ethoxysilylpropoxy)methyl]oxetane, 4,4-bis(3-ethyl-3-oxetanyl)methoxymethyl]biphenyl, and 3,3-dimethyl-2(p-methoxy-phenyl)oxetane. One or more of the oxetanes described herein may be hydroxy-modified or (meth)acrylate-modified (for example: Uvi-Cure S170 CAS from Lambson (CAS:37674-57-0)).

[0070]

[0069] For embodiments in which the radiation curable coating composition comprises one or more polyhydroxy compounds described herein, the one or more polyhydroxy compounds are preferably present in an amount of about 15 wt % or less, more preferably about 1 wt % to about 10 wt %, said weight percentages being based on the total weight of the radiation curable coating composition.

[0071]

[0070] Polyhydroxy compounds are known to improve adhesion to substrates known to exhibit poor adhesion, such as plastic or polymer substrates which are increasingly prevalent in the field of security documents, especially banknotes.

[0072]

[0071] The polyhydroxy compound(s) described herein preferably contain more than two hydroxyl groups and may be linear, branched, or hyperbranched (also referred to in the art as arborescent). Preferably, the polyhydroxy compound(s) described herein are multifunctional compounds, such as trifunctional, tetrafunctional, hexafunctional compounds, etc.

[0073]

[0072] The one or more polyhydroxy compounds described in this specification are preferably selected from the group consisting of polyhydroxy derivatives of aliphatic or aromatic polyethers, polyhydroxy derivatives of polyesters, polyhydroxy derivatives of polycarbonates, glycerol, trimethylolpropane, di-trimethylolpropane, pentaerythritol, dipentaerythritol, and mixtures thereof.

[0074]

[0073] One or more of the polyhydroxy compounds described herein may be at least partially alkoxylated. Thus, one or more of the polyhydroxy compounds described herein may have alkoxylated units, preferably ethoxylated and / or propoxylated units.

[0075] According to a preferred embodiment, the one or more polyhydroxy compounds described herein are selected from the group consisting of trifunctional compounds, preferably glycerol and trimethylolpropane, tetrafunctional compounds, preferably di-trimethylolpropane and pentaerythritol, hexafunctional compounds, preferably dipentaerythritol, and mixtures thereof, said compounds, preferably said trimethylolpropane, pentaerythritol, and dipentaerythritol, may be alkoxylated (ethoxylated and / or propoxylated).

[0076] For embodiments in which the radiation curable coating composition comprises one or more glycidyl ether compounds described herein, the one or more glycidyl ethers are preferably present in an amount of from about 1% to about 5% by weight, the weight percentage being based on the total weight of the radiation curable coating composition, or from 1% to 25% by weight, based on the total weight of the top coating composition.

[0077] The use of epoxides in UV-Vis radiation curable inks helps to accelerate cure and reduce tackiness, as well as reducing the viscosity of the ink while strongly copolymerizing with the ink vehicle. Preferred examples of epoxides other than the cycloaliphatic epoxides described herein include, but are not limited to, cyclohexanedimethanol diglycidyl ether, poly(ethylene glycol) diglycidyl ether, poly(propylene glycol) diglycidyl ether, butanediol diglycidyl ether, hexanediol diglycidyl ether, bisphenol-A diglycidyl ether, neopentyl glycol diglycidyl ether, trimethylolpropane triglycidyl ether, glycerol triglycidyl ether, pentaerythritol tetraglycidyl ether, butyl glycidyl ether, p-tert-butylphenyl glycidyl ether, hexadecyl glycidyl ether, 2-ethyl-hexyl glycidyl ether, octyl glycidyl ether, decyl glycidyl ether, dodecyl glycidyl ether, tetradecyl glycidyl ether, C12 / C14 alkyl glycidyl ether, C13 / C15 alkyl glycidyl ether, and mixtures thereof. Suitable epoxides other than cycloaliphatic epoxides are commercially available from EMS Griltech under the trademark Grilonit® (eg Grilonit® V51-63 or RV1806).

[0078]

[0077] The radiation curable coating compositions comprising the non-spherical, preferably platelet-shaped, magnetic or magnetisable pigment particles described herein may further comprise one or more colouring components selected from the group consisting of organic pigment particles, inorganic pigment particulates and organic dyes, and / or one or more additives. Examples of the latter include, but are not limited to, compounds and materials used to adjust the physical, rheological and chemical parameters of the coating composition, such as viscosity (e.g., solvents, thickeners and surfactants), consistency (e.g., anti-settling agents, fillers and plasticisers), foamability (e.g., defoamers), lubricity (waxes, oils), UV stability (light stabilizers), adhesion, antistatic properties, storage stability (polymerisation inhibitors). The additives described herein may be present in the coating composition in amounts and forms known in the art, including so-called nanomaterials, where at least one of the dimensions of the additive is in the range of 1-1000 nm.

[0079]

[0078] The radiation curable coating composition comprising the non-spherical, preferably platelet-shaped, magnetic or magnetisable pigment particles described herein may further comprise one or more marking substances or identification additives selected from the group consisting of magnetic materials (different from the magnetic or magnetisable pigment particles described herein), luminescent materials, electroluminescent materials, upconverting materials, electrically conductive materials, and infrared absorbing materials, and / or one or more machine-readable materials. As used herein, the term "machine-readable material" refers to a material exhibiting at least one unique property that is detectable by a device or machine and that can be included in said coating to provide a method for its detection and / or authentication to authenticate the coating or an article comprising said coating by use of a specific device.

[0080]

[0079] The radiation curable coating compositions described herein may be prepared by dispersing or mixing the magnetic or magnetizable pigment particles described herein and one or more additives, when present, in the presence of a binder material described herein to form a liquid composition. When present, the one or more photoinitiators may be added to the composition during the dispersing or mixing step of all the other ingredients or may be added at a later stage, i.e., after formation of the liquid coating composition.

[0081] The method described herein further comprises, after step a) as described herein, step b) of applying at least partially onto the coating layer (x10) as described herein, a top coating composition as described herein, which is applied in the form of one or more indicia (x30) as described herein and which partially overlaps (i.e. overlaps in at least one area) the coating layer (x10) as described herein, the radiation curable coating composition of the coating layer (x10) being in a wet unpolymerized state and the magnetic or magnetizable pigment particles being free to move and rotate.

[0082]

[0081] The term "indicia" as used herein means continuous and discontinuous layers of markings or signs or patterns of identification. Preferably, the one or more indicia (x30) described herein are selected from the group consisting of codes, symbols, alphanumeric symbols, motifs, geometric patterns (e.g., circles, triangles, and regular or irregular polygons), letters, words, numbers, logos, figures, portraits, and combinations thereof. Examples of codes include coded marks such as coded alphanumeric data, one-dimensional barcodes, two-dimensional barcodes, QR codes, data matrices, and IR-readable codes. The one or more indicia (x30) described herein may be solid indicia and / or raster indicia.

[0083]

[0082] The topcoating composition described herein is applied in the form of one or more indicia (x30) as described herein by an application process, preferably a non-contact fluid micro-dispensing process, preferably selected from the group consisting of spray coating, aerosol inkjet printing, electrohydrodynamic printing, slot-die coating, and inkjet printing, more preferably an inkjet printing process, said non-contact fluid micro-dispensing printing process being a variable information printing method allowing the unique creation of one or more indicia (x30) on or in an optical effect layer (OEL) as described herein. The application process is selected as a function of the design and resolution of the indicia or indicia to be created.

[0084] Inkjet printing may be advantageously used to create optical effect layers (OELs) exhibiting one or more of the indicia described herein, including variable halftones. Inkjet halftone printing is a reproduction technique that simulates continuous tone images containing an infinite number of colors or shades of gray by the application of variable inkjet coverage or basis weight.

[0085]

[0084] Spray coating is a technique in which a fine aerosol is formed by forcing a composition through a nozzle. A carrier gas and an electrostatic charge may be involved to function to direct the aerosol onto the surface to be printed. Spray printing makes it possible to print spots and lines. Compositions suitable for spray printing typically have a viscosity of about 10 mPa.s to about 1 Pa.s at 25°C (1000 s -1 ) The resolution of spray coating printing is in the millimeter range. Spray printing is described, for example, in F. C. Krebs, Solar Energy Materials & Solar Cells (2009), 93, 407.

[0086] Aerosol inkjet printing (AJP) is a new non-contact direct-write approach aimed at producing fine features on a wide range of substrates. AJP is compatible with a wide range of materials and freeform deposition, allowing high resolution (on the order of about 10 micrometers) along with relatively large separation distances (e.g., 1-5 mm) in addition to orientation independence. The technique involves aerosol generation using ultrasonic or pneumatic atomizers, with typical flow rates of about 1 mPa.s to about 1 Pa.s at 25°C (1000 s -1 Aerosols are generated from compositions having a viscosity of about 100 nm. Aerosol jet printing is described, for example, in NJ Wilkinson et al., The International Journal of Advanced Manufacturing Technology (2019) 105: 4599-4619.

[0087] Electrohydrodynamic inkjet printing is a high resolution inkjet printing technique. Electrohydrodynamic inkjet printing uses an externally applied electric field to manipulate droplet size, ejection times, and placement on a substrate to obtain higher resolution than conventional inkjet printing while maintaining high production speed. The resolution of electrohydrodynamic inkjet printing is about two orders of magnitude higher than conventional inkjet printing techniques, and therefore it can be used to orient nanoscale and microscale patterns. Electrohydrodynamic inkjet printing may be used in both DOD or continuous modes. Electrohydrodynamic inkjet printing compositions typically have a viscosity of about 1 mPa.s to about 1 Pa.s at 25°C (1000 s -1 ) The electrohydrodynamic inkjet printing technique is described, for example, in PV Raje and NC Murmu, International Journal of Emerging Technology and Advanced Engineering, (2014), 4(5), pp. 174-183.

[0088]

[0087] Slot die coating is a one-dimensional coating technique. Slot die coating allows for the coating of stripes of material well suited for creating multi-layer coatings in which stripes of different materials are layered on top of each other. Alignment of the pattern is provided by moving the coating head along a direction perpendicular to the direction of web movement. A slot die coating head includes a mask that defines a slot in the coating head through which the slot die coating ink is dispersed. An example of a slot die coating head is described in FCKrebs, Solar Energy Materials & Solar Cells (2009), 93, pp. 405-406. Compositions suitable for slot die coating typically have a viscosity of about 1 mPa.s to about 20 mPa.s at 25°C (1000 s -1 ) viscosity.

[0089] According to one embodiment, the top coating composition described herein is printed in the form of one or more indicia (x30) as described herein by an inkjet printing process, preferably a continuous inkjet (CI) printing process, or a drop-on-demand (DOD) inkjet printing process, more preferably a drop-on-demand (DOD) inkjet printing process. Drop-on-demand (DOD) printing is a non-contact printing process, where droplets are simply created when needed for printing, generally by an ejection mechanism, rather than by destabilizing the jet. Depending on the mechanism used in the print head to create the droplets, DOD printing can be performed by a variety of methods, including piezoelectric impulse, thermal jet, valve jet (approximately 1 mPa.s to approximately 1 Pa.s at 25°C (1000 s -1 ) viscous), and electrostatic processes.

[0090] According to one embodiment, the top-coating composition described herein is a radiation-curable coating composition comprising a cationically curable compound, such as a magnetic or magnetisable pigment particle as described herein, in particular one or more monomers and / or oligomers selected from the group consisting of vinyl ethers, propenyl ethers, cyclic ethers, such as epoxides, oxetanes and tetrahydrofuran, mixtures thereof, and one or more solvents. For embodiments in which the top-coating composition is applied by an inkjet printing process, said top-coating composition may further comprise conventional additives and ingredients such as wetting agents, defoamers, surfactants, (co)solvents, and mixtures thereof, used in the field of radiation-curable inkjet.

[0091]

[0090] The top coating compositions described herein may further comprise one or more labeling substances or taggants and / or one or more machine-readable materials, such as those described for the radiation-curable coating compositions comprising the non-spherical magnetic or magnetizable pigment particles described herein, provided that the size of the substances, taggants, or machine-readable materials is suitable for the application process described herein.

[0092]

[0091] The method for producing an optical effect layer (OEL) exhibiting one or more indicia (x30) thereof comprises at least partially curing the one or more indicia (x30) and one or more areas of the coating layer (x10) under said one or more indicia (x30) with a LED curing unit (x50), and at least partially curing the coating layer (x10) with a curing unit (x60) emitting at least between 250 nm and 320 nm, allowing selective curing of the one or more indicia (x30) and the coating layer (x10) at different stages of the method requiring specific combinations. Thus, the one or more photoreactive compounds that do not absorb in the range of about 350 nm to about 470 nm of the radiation curable coating composition of step a) and the one or more compounds that absorb in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are selected according to one of the combinations described in the following embodiments.

[0093] According to a first embodiment, the one or more photoreactive compounds of the radiation curable coating composition of step a) that do not absorb in the range of about 350 nm to about 470 nm are iodonium salts having a cationic moiety and an anionic moiety. Preferably, the one or more compounds of the radiation curable coating composition of step a) are iodonium salts, the anionic moiety being preferably SbF6 - (Hexafluoroantimonate, CAS Nr 17111-95-4); PF6 - (Hexafluorophosphate, CAS Nr 16919-18-9);AsF6 - (Hexafluoroarsenate, CAS Nr 16973-45-8); F4B - (Tetrafluoroborate, CAS Nr 14874-70-5);(C6F5)4B - (Tetrakis(pentafluorophenyl)borate, CAS Nr 47855-94-7);(CF3SO2)3C - (Tris(trifluoromethylsulfonyl)methide, CAS Nr 130447-45-9); (CF3)SO3- (Trifluoromethanesulfonate, CAS Nr 37181-39-8);(CH3C6H4)SO3 - (4-Methylbenzenesulfonate, CAS Nr 16722-51-3);(CF3)CO2 - (Trifluoroacetate, CAS Nr 14477-72-6);(C4F9)SO3 - (1,1,2,2,3,3,4,4,4-Nonafluoro-1-butanesulfonate, CAS Nr 45187-15-3);(C4F9)CO2 - (2,2,3,3,4,4,5,5,5-nonafluoro-1-pentanoate, CAS Nr 45167-47-3); preferably SbF6 - , PF6 - or (C6F5)4B -and the cationic moiety is preferably bis(4-dodecylphenyl)iodonium (CAS Nr 71786-69-1); bis[4-(1,1-dimethylethyl)phenyl]iodonium (CAS Nr 61267-44-5); (4-isopropylphenyl)(4-methylphenyl)iodonium (CAS Nr 178233-71-1); bis(4-methylphenyl)iodonium (CAS Nr 46449-56-3); (4-methylphenyl)[4-(2-methylpropyl)phenyl]iodonium (CAS Nr 344562-79-4); bis(2,4-dimethylphenyl)]iodonium (CAS Nr 78337-07-2); bis(3,4-dimethylphenyl)]iodonium (CAS Nr 66482-57-3); (4-methylphenyl)(2,4,6-trimethylphenyl)iodonium (CAS Nr 758629-51-5;Bis[(4-(2-methylpropyl)phenyl]iodonium (CAS Nr 157552-66-4);Bis(4-butylphenyl)iodonium (CAS Nr 76310-29-7);Bis(2,4,6-trimethylphenyl)iodonium (CAS Nr 94564-97-3);Bis(4-hexylylphenyl)iodonium (CAS Nr 249300-48-9);Bis(4-decylphenyl)iodonium (CAS Nr 137141-44-7);(4-decylphenyl)(4-undecylphenyl)iodonium (CAS Nr 167997-83-3);Bis(4-undecylphenyl)iodonium (CAS Nr 167997-61-7);Bis(4-tridecylphenyl)iodonium (CAS Nr 124053-08-3;Bis(4-tetradecylphenyl)iodonium (CAS Nr 167997-63-9);Bis(4-hexadecylphenyl)iodonium (CAS Nr 137141-41-4);Bis(4-heptadecylphenyl)iodonium (CAS Nr 144095-91-0);Bis(4-octadecylphenyl)iodonium (CAS Nr 202068-75-5);(4-decylphenyl)(4-dodecylphenyl)iodonium (CAS Nr 167997-67-3);(4-Decylphenyl)(4-Tridecylphenyl)iodonium (CAS Nr 167997-77-5);(4-Decylphenyl)(4-Tetradecylphenyl)iodonium (CAS Nr 167997-81-1);(4-Dodecylphenyl)(4-Undecylphenyl)iodonium (CAS Nr 167997-71-9);(4-Dodecylphenyl)(4-Tridecylphenyl)iodonium (CAS Nr 167997-69-5);(4-Dodecylphenyl)(4-Tetradecylphenyl)iodonium (CAS Nr 167997-65-1);(4-Tridecylphenyl)(4-Undecylphenyl)iodonium (CAS Nr 167997-73-1);(4-Tetradecylphenyl)(4-Undecylphenyl)iodonium (CAS Nr 167997-79-7;(4-tetradecylphenyl)(4-tridecylphenyl)iodonium (CAS Nr 167997-75-3);p-(octyloxyphenyl)phenyliodonium (CAS Nr 121239-74-5);[4-[(2-hydroxytetradecyl)oxy]phenyl]phenyliodonium (CAS Nr 139301-14-7);phenyl[3-(trifluoromethyl)phenyl]iodonium (CAS Nr 789443-26-1);bis(4-fluorophenyl)iodonium (CAS Nr 91290-88-9);(4-nitrophenyl)phenyliodonium (CAS Nr 46734-23-0);(4-nitrophenyl)(2,4,6-trimethylphenyl)iodonium (CAS Nr 1146127-10-7; more preferably bis(4-dodecylphenyl)iodonium (CAS Nr 71786-69-1); bis[4-(1,1-dimethylethyl)phenyl]iodonium (CAS Nr 61267-44-5); (4-isopropylphenyl)(4-methylphenyl)iodonium (CAS Nr 178233-71-1); bis(4-methylphenyl)iodonium (CAS Nr 46449-56-3);or (4-methylphenyl)[4-(2-methylpropyl)phenyl]iodonium (CAS Nr 344562-79-4). Preferably, the one or more compounds of the radiation curable coating composition of step a) are bis(4-dodecylphenyl)iodonium hexafluoroantimonate (CAS Nr 71786-70-4); bis[4-(1,1-dimethylethyl)phenyl]iodonium hexafluorophosphate (CAS Nr 61358-25-6); (4-isopropylphenyl)(4-methylphenyl)iodonium tetrakis(pentafluorophenyl)borate (CAS Nr 178233-72-2); bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0); (4-methylphenyl)[4-(2-methylpropyl)phenyl]iodonium hexafluorophosphate (CAS Nr 344562-80-7), and mixtures thereof, more preferably the iodonium salts are selected from the group consisting of bis(4-dodecylphenyl)iodonium hexafluoroantimonate (CAS Nr 71786-70-4); bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0); and mixtures thereof. Particularly suitable examples of iodonium salts for the first embodiment of the invention are commercially available under the names SpeedCure 937 (CAS Nr 71786-70-4), SpeedCure 938 (CAS Nr 61358-25-6), SpeedCure 939 (CAS Nr 178233-72-2) from Lambson, OMNICAT 250 (CAS Nr 344562-80-7) and OMNICAT 440 (CAS Nr 60565-88-0) from IGM Resins, and DEUTERON UV1240 (CAS Nr 71786-70-4) and DEUTERON UV1242 (CAS Nr 71786-70-4) from DEUTERON;

[0094] According to said first embodiment, the one or more compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are thioxanthone compounds, preferably 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 5495-84-1); 4-(1-methylethyl)-9H-thioxanthen-9-one (CAS Nr 83846-86-0); 2,4-diethyl-9H-thioxanthen-9-one (CAS Nr 82799-44-8); 2-chloro-9H-thioxanthen-9-one (CAS Nr 86-39-5); 1-chloro-4-propoxy-9H-thioxanthen-9-one (CAS Nr 142770-42-1;1,3-di[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxy]-2,2-bis[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxymethylpropane (CAS Nr 1003567-83-6);α-[2-[(9-oxo-9H-thioxanthenyl)oxy]acetyl]-ω-[[2-[(9-oxo-9H-thioxanthenyl)oxy]acetyl]oxy]-poly(oxy-1,4-butanediyl) (CAS Nr 813452-37-8;2-[2-[1-[2-[[2-(9-oxothioxanthen-2-yl)oxyacetyl]amino]-3-[1-[2-(2-prop-2-enoyloxyethoxy)ethoxy]ethoxy]-2-[1-[2-(2-prop-2-enoyloxyethoxy)ethoxy]ethoxymethyl]propoxy]ethoxy]ethoxy]ethylprop-2-enoate (CAS Nr 1427388-03-1);α-[2-[(9-oxo-9H-thioxanthenyl)oxy]acetyl]-ω-[[2-[(9-oxo-9H-thioxanthenyl)oxy]acetyl]oxy]-poly(oxy-1,4-butanediyl) (CAS Nr 813452-37-8); their oligomeric and polymeric compounds (CAS Nr 515139-51-2 and 2055335-46-9); and preferably 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 5495-84-1);4-(1-methylethyl)-9H-thioxanthen-9-one (CAS Nr 83846-86-0); 1-chloro-4-propoxy-9H-thioxanthen-9-one (CAS Nr 142770-42-1); 1,3-di[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxy]-2,2-bis[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxymethylpropane (CAS Nr 1003567-83-6); oligomeric and polymeric compounds thereof (CAS Nr 2055335-46-9); and mixtures thereof selected from the group consisting of: Particularly suitable examples of thioxanthone compounds for the first embodiment of the invention are SpeedCure 2-ITX (CAS Nr 5495-84-1), 2-chloro-thioxanthone (CAS Nr 86-39-5), SpeedCure CPTX (CAS Nr 142770-42-1), and SpeedCure 7010 / 7010L (CAS Nr 1003567-83-6) from Lambson; Omnirad ITX (CAS Nr 5495-84-1 and 83846-86-0), Omnirad DETX (CAS Nr 82799-44-8), Omnipol TX (CAS Nr 813452-37-8), Omnipol 3TX (CAS Nr 82799-4 ... 1427388-03-1) and Genopol® TX-1 (CAS Nr 515139-51-2), Genopol® TX-2 (CAS Nr 2055335-46-9) from Rahn;

[0095]

[0094] According to a second embodiment, the one or more photoreactive compounds that do not absorb in the range of about 350 nm to about 470 nm of the radiation curable coating composition in step a) are iodonium salts, as described above for the first embodiment.

[0096] According to said second embodiment, the one or more compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are anthracene compounds preferably selected from the group consisting of 9,10-diethoxy-anthracene (CAS Nr 68818-86-0); 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4) and mixtures thereof, preferably 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4). Particularly suitable examples of anthracene compounds for the second embodiment of the invention are commercially available under the names ANTHRACURE® UVS 1101 (CAS Nr 68818-86-0), ANTHRACURE® UVS 1331 (CAS Nr 76275-14-4) from Kawasaki Kasei Chemicals.

[0097]

[0096] According to a third embodiment, the one or more photoreactive compounds that do not absorb in the range of about 350 nm to about 470 nm of the radiation curable coating composition in step a) are iodonium salts, as described above for the first example.

[0098] According to the third embodiment, the one or more compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are coumarin compounds, preferably 3-(4-dodecylbenzoyl)-5,7-dimethoxy-2H-1-benzopyran-2-one (CAS Nr 2170153-43-0), 3-(4-C 10 -C 13 -benzoyl)-5,7-dimethoxy-2H-1-benzopyran-2-one (CAS Nr 2243703-91-3). A particularly suitable example of a coumarin compound for the third embodiment of the invention is commercially available under the name SACURE3644 (CAS Nr 2243703-91-3) from IGM Resins.

[0099]

[0098] According to a fourth embodiment, the one or more photoreactive compounds that do not absorb in the range of about 350 nm to about 470 nm of the radiation curable coating composition in step a) are iodonium salts, as described above for the first embodiment.

[0100]

[0099] According to said fourth embodiment, the one or more compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are naphthalene compounds, preferably 9,10-diethoxy-naphthalene (CAS Nr 27294-37-7), and the top curable coating composition of step b) further comprises one or more anthracene compounds preferably selected from the group consisting of 9,10-diethoxy-anthracene (CAS Nr 68818-86-0); 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4), and mixtures thereof, preferably 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4). A particularly suitable example of the naphthalene compound for the fourth embodiment of the invention is commercially available under the name ANTHRACURE® ET2201 (CAS Nr 27294-37-7) from Kawasaki Chemical Industries, Ltd. A particularly suitable example of the anthracene compound for the fourth embodiment of the invention is commercially available under the name ANTHRACURE® UVS1331 (CAS Nr 76275-14-4) from Kawasaki Chemical Industries, Ltd.

[0101] According to a fifth embodiment, the one or more photoreactive compounds of the radiation curable coating composition of step a) that do not absorb in the range of about 350 nm to about 470 nm are sulfonium salts having a cationic moiety and an anionic moiety. Preferably, the one or more compounds of the radiation curable coating composition of step a) are sulfonium salts, the anionic moiety being preferably SbF6 - (Hexafluoroantimonate, CAS Nr 17111-95-4); PF6 - (Hexafluorophosphate, CAS Nr 16919-18-9);AsF6 -(Hexafluoroarsenate, CAS Nr 16973-45-8); F4B - (Tetrafluoroborate, CAS Nr 14874-70-5);(C6F5)4B - (Tetrakis(pentafluorophenyl)borate, CAS Nr 47855-94-7);(CF3SO2)3C - (Tris(trifluoromethylsulfonyl)methide, CAS Nr 130447-45-9); (CF3)SO3 - (Trifluoromethanesulfonate, CAS Nr 37181-39-8);(CH3C6H4)SO3 - (4-Methylbenzenesulfonate, CAS Nr 16722-51-3);(CF3)CO2 - (Trifluoroacetate, CAS Nr 14477-72-6);(C4F9)SO3 - (1,1,2,2,3,3,4,4,4-Nonafluoro-1-butanesulfonate (CAS Nr 45187-15-3); (C4F9)CO2 - (2,2,3,3,4,4,5,5,5-nonafluoro-1-pentanoate, CAS Nr 45167-47-3); preferably SbF6 - or PF6 -and the cationic moiety is preferably 4-(phenylthio)phenyldiphenyl-sulfonium (CAS Nr 47480-44-4); bis[4-(diphenylsulfonium)phenyl]sulfide (CAS Nr 74227-34-2); (4-methylphenyl)diphenyl-sulfonium (CAS Nr 47045-31-8); (3-methylphenyl)diphenyl-sulfonium (CAS Nr 347841-49-0); bis(4-methylphenyl)phenyl-sulfonium (CAS Nr 70082-58-5); [(4-(1,1-dimethylethyl)phenyl]diphenyl-sulfonium (CAS Nr 66482-54-0); bis[4-(1-methylethyl)phenyl]phenyl-sulfonium (CAS Nr 70084-21-8); [(4-(2-methylpropyl)phenyl]diphenyl-sulfonium (CAS Nr 255056-41-8;(4-Methoxyphenyl)diphenyl-sulfonium (CAS Nr 70084-23-0);1-Naphthalenyldiphenyl-sulfonium (CAS Nr 116808-68-5);Tris(4-methylphenyl)-sulfonium (CAS Nr 47197-43-3);(4-Bromophenyl)diphenyl-sulfonium (CAS Nr 70244-60-9);(4-Iodophenyl)diphenyl-sulfonium (CAS Nr 255056-45-2);(4-Fluorophenyl)diphenyl-sulfonium (CAS Nr 70084-25-2);(4-Chlorophenyl)diphenyl-sulfonium (CAS Nr 47045-32-9);(4-Phenoxyphenyl)diphenyl-sulfonium (CAS Nr 82617-07-0;(4'-methyl[1,1'-biphenyl]-4-yl)diphenyl-sulfonium (CAS Nr 868610-38-2);tris(4-propylphenyl)-sulfonium (CAS Nr 935399-09-0);bis(4-butylphenyl)phenyl-sulfonium (CAS Nr 518991-23-6);tris[4(1-methylethyl)phenyl]-sulfonium (CAS Nr 592518-39-3);S,S'-1,3-phenylenebis[S,S'-diphenyl]-sulfonium (CAS Nr 641638-18-8);(4-dodecylphenyl)diphenyl-sulfonium (CAS Nr 108493-55-6);(4-benzoylphenyl)diphenyl-sulfonium (CAS Nr 127855-23-6);Bis([1,1'-biphenyl]-4-yl)(4-methylphenyl)-sulfonium (CAS Nr 91815-48-4);Tris[4-[1,1-dimethylethyl)phenyl]-sulfonium (CAS Nr 91815-56-4);Triphenyl-sulfonium (CAS Nr 18393-55-0);5-(4-methylphenyl)-dibenzothiophenium (CAS Nr 49867-39-2);5-[4-(2-hydroxyethoxy)phenyl]-thianthrenium (CAS Nr 492466-55-4);10-(4-methylphenyl)-9H-thioxanthenium (CAS Nr 66482-77-7;Diphenyl[4-[[(4-phenylthiophenyl]thio]phenyl]-sulfonium (CAS Nr 101200-54-8);Phenylbis[4-phenylthio)phenyl]-sulfonium (CAS Nr 101200-59-3);5-[4-(phenylthio)phenyl]-thianthrenium (CAS Nr 101200-56-0);5-[4-(phenylthio)phenyl]-dibenzothiophenium (CAS Nr 492466-67-8);10-[4-(diphenylthio)phenyl]-9H-thioxanthenium (CAS Nr 903907-41-5);5-phenyl-thioxanthenium (CAS Nr 47041-10-1);10-phenyl-9H-thioxanthenium (CAS Nr 53512-22-4);5-(4-methylphenyl)-thioxanthenium (CAS Nr 47124-94-7);5-[1,1'-biphenyl]-4-yl-thioxanthenium (CAS Nr 478774-67-3);or S,S'-(thiodi-4,1-phenylene)bis[S,S'-bis[4-(2-hydroxyethoxy)]phenyl]-sulfonium (CAS Nr 106220-69-3);More preferably it is 4-(phenylthio)phenyldiphenyl-sulfonium (CAS Nr 47480-44-4) or bis[4-(diphenylsulfonium)phenyl]sulfide (CAS Nr 74227-34-2). Preferably, the one or more photoreactive compounds of the radiation curable coating composition of step a) that do not absorb in the range of about 350 nm to about 470 nm are selected from the group consisting of 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0); bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9); 4-(phenylthio)phenyldiphenylsulfonium hexafluorophosphate (CAS Nr 75482-18-7); bis[4-(diphenylsulfonium)phenyl]sulfide bis(hexafluorophosphate (CAS Nr 74227-35-3); S,S'-(thiodi-4,1-phenylene)bis[S,S'-bis[4-(2-hydroxyethoxy)]phenyl]-sulfonium bis[hexafluorophosphate] (CAS Nr 106220-70-6);S,S'-(thiodi-4,1-phenylene)bis[S,S'-bis[4-(2-hydroxyethoxy)]phenyl]-sulfonium bis[hexafluoroantimonate] (CAS Nr 125054-47-9);5-[4-(2-hydroxyethoxy)phenyl]thianthrenium hexafluorophosphate (CAS Nr 492466-56-5);and mixtures thereof;more preferably 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0);bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9);and mixtures thereof. Particularly suitable examples of sulfonium salts for the fifth embodiment of the invention are those sold under the names SpeedCure 976 (CAS Nr 71449-78-0 and 89452-37-9) and SpeedCure 992 (CAS Nr 75482-18-7 and 74227-35-3) from Lambson, DoubleCure® 1172 (CAS Nr 617711-03-2) from DoubleBond, ESACURE 1187 (CAS Nr 492466-56-5) from IGM Resins, and Optomer SP150 (CAS Nr 106220-70-6), Optomer SP170 (CAS Nr 125054-47-9) from Adeka;

[0102]

[0101] According to the fifth embodiment, the one or more compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are anthracene compounds as described for the second embodiment.

[0103]

[0102] According to a sixth embodiment, the one or more photoreactive compounds that do not absorb in the range of about 350 nm to about 470 nm of the radiation curable coating composition in step a) are sulfonium salts, as described above for the fifth embodiment.

[0104] According to the sixth embodiment, the one or more compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are thioxanthone compounds as described above for the first embodiment, and the top curable coating composition of step b) further comprises one or more compounds which are iodonium salts as described above for the first embodiment.

[0105]

[0104] According to a seventh embodiment, the one or more photoreactive compounds that do not absorb in the range of about 350 nm to about 470 nm of the radiation curable coating composition in step a) are sulfonium and are as described above for the fifth embodiment.

[0106]

[0105] According to the seventh embodiment, the one or more compounds of the top curable coating composition of step b) are naphthalene compounds as described above for the fourth embodiment, and the top curable coating composition of step b) further comprises one or more anthracene compounds as described above for the fourth embodiment.

[0107]

[0106] According to an eighth embodiment, the one or more photoreactive compounds that do not absorb in the range of about 350 nm to about 470 nm of the radiation curable coating composition in step a) are sulfonium salts, as described above for the fifth embodiment.

[0108] According to the eighth embodiment, the one or more compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are coumarin compounds as described above for the third embodiment, and the top curable coating composition of step b) further comprises one or more compounds which are iodonium salts as described above for the first embodiment.

[0109] According to a ninth embodiment, the one or more photoreactive compounds not absorbing in the range of about 350 nm to about 470 nm of the radiation curable coating composition of step a) are selected from the group consisting of iodonium salts, sulfonium salts, and mixtures thereof, as described above for the fifth embodiment. Non-limiting examples of iodonium salts are those described herein and others that can be found in standard texts, such as "Photoinitiators for Free Radical Cationic and Anionic Polymerization", 2nd Edition, by JV Crivello & K. Dietliker, "Chemistry & Technology of UV & EB Formulation for Coatings, Inks & Paints", vol. 3, edited by G. Bradley, published in 1998 by John Wiley & Sons in collaboration with SITA Technology Limited; non-limiting examples of sulfonium salts are those described above for the fifth embodiment.

[0110] According to the ninth embodiment, the one or more compounds of the top curable coating composition of step b) that absorb in the range of about 350 nm to about 470 nm are iodonium salts having a cationic moiety and an anionic moiety. Preferably, the one or more compounds of the top curable coating composition of step b) that absorb in the range of about 350 nm to about 470 nm are iodonium salts, and the anionic moiety is preferably SbF6 - (Hexafluoroantimonate, CAS Nr 17111-95-4); PF6 - (Hexafluorophosphate, CAS Nr 16919-18-9);AsF6 - (Hexafluoroarsenate, CAS Nr 16973-45-8); F4B - (Tetrafluoroborate, CAS Nr 14874-70-5);(C6F5)4B -(Tetrakis(pentafluorophenyl)borate, CAS Nr 47855-94-7);(CF3SO2)3C - (Tris(trifluoromethylsulfonyl)methide, CAS Nr 130447-45-9); (CF3)SO3 - (Trifluoromethanesulfonate, CAS Nr 37181-39-8);(CH3C6H4)SO3 - (4-Methylbenzenesulfonate, CAS Nr 16722-51-3);(CF3)CO2 - (Trifluoroacetate, CAS Nr 14477-72-6);(C4F9)SO3 - (1,1,2,2,3,3,4,4,4-Nonafluoro-1-butanesulfonate, CAS Nr 45187-15-3);(C4F9)CO2 - (2,2,3,3,4,4,5,5,5-nonafluoro-1-pentanoate, CAS Nr 45167-47-3); preferably SbF6 - or PF6 - and the cationic moiety is [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium (CAS Nr 2091854-11-2). Preferably, the radiation curable coating composition of step b) comprises one or more iodonium salts selected from the group consisting of [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium hexafluorophosphate (CAS Nr 2091854-12-3); [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium hexafluoroantimonate (CAS Nr 2091854-13-4); and mixtures thereof. Particularly suitable examples of iodonium salts for the ninth embodiment of the invention are commercially available under the names Sylanto® 7MP (CAS Nr 2091854-12-3) and Sylanto® 7MS (CAS Nr 2091854-13-4) from Synthos Group SA.

[0111] According to a tenth embodiment, the one or more photoreactive compounds not absorbing in the range of about 350 nm to about 470 nm of the radiation curable coating composition of step a) are selected from the group consisting of iodonium salts, sulfonium salts, and mixtures thereof, as described above for the fifth embodiment. Non-limiting examples of iodonium salts are those described herein and others that can be found in standard texts, such as "Photoinitiators for Free Radical Cationic and Anionic Polymerization", 2nd Edition, by JV Crivello & K. Dietliker, "Chemistry & Technology of UV & EB Formulation for Coatings, Inks & Paints", vol. 3, edited by G. Bradley, published in 1998 by John Wiley & Sons in collaboration with SITA Technology Limited; non-limiting examples of sulfonium salts are those described above for the fifth embodiment.

[0112] According to the tenth embodiment, the one or more compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are oxonium salts having a cationic moiety and an anionic moiety, the anionic moiety being preferably SbF6 - (Hexafluoroantimonate, CAS Nr 17111-95-4); PF6 - (Hexafluorophosphate, CAS Nr 16919-18-9);AsF6 - (Hexafluoroarsenate, CAS Nr 16973-45-8); F4B - (Tetrafluoroborate, CAS Nr 14874-70-5);(C6F5)4B - (Tetrakis(pentafluorophenyl)borate, CAS Nr 47855-94-7);(CF3SO2)3C - (Tris(trifluoromethylsulfonyl)methide, CAS Nr 130447-45-9); (CF3)SO3- (Trifluoromethanesulfonate, CAS Nr 37181-39-8);(CH3C6H4)SO3 - (4-Methylbenzenesulfonate, CAS Nr 16722-51-3);(CF3)CO2 - (Trifluoroacetate, CAS Nr 14477-72-6);(C4F9)SO3 - (1,1,2,2,3,3,4,4,4-Nonafluoro-1-butanesulfonate, CAS Nr 45187-15-3);(C4F9)CO2 - (2,2,3,3,4,4,5,5,5-nonafluoro-1-pentanoate, CAS Nr 45167-47-3); preferably F4B - and the cationic moiety is preferably 2,4,6-triphenylpyrylium (CAS Nr 15959-35-0); 2,4,6-tris(4-methylphenyl)-pyrylium (CAS Nr 47551-87-1); 2,4,6-tris(4-methoxyphenyl)-pyrylium (CAS Nr 47659-08-5); 2,6-bis(4-fluorophenyl)-4-(4-methoxyphenyl)-pyrylium (CAS Nr 1621587-27-6); 3-methyl-2,4,6-triphenyl-pyrylium (CAS Nr 33225-59-1); 2,4,6-tris([1,1'-biphenyl]-4-yl)-pyrylium (CAS Nr 114987-61-0); 4-[4-(dimethylamino)phenyl]-2,6-diphenyl-pyrylium (CAS Nr 47551-72-4) or 2,4-bis(4-methoxyphenyl)-6-phenyl-pyrylium (CAS Nr 47589-11-7); more preferably 2,4,6-triphenylpyrylium (CAS Nr 15959-35-0). Preferably, at least one of the one or more compounds of the top curable coating composition of step b) is 2,4,6-triphenylpyrylium tetrafluoroborate (CAS Nr 448-61-3).

[0113] According to an eleventh embodiment, the one or more photoreactive compounds not absorbing in the range of about 350 nm to about 470 nm of the radiation curable coating composition in step a) are selected from the group consisting of iodonium salts, sulfonium salts, and mixtures thereof, as described above for the fifth embodiment. Non-limiting examples of iodonium salts are those described herein and others that can be found in standard texts, such as "Photoinitiators for Free Radical Cationic and Anionic Polymerization", 2nd Edition, by JV Crivello & K. Dietliker, "Chemistry & Technology of UV & EB Formulation for Coatings, Inks & Paints", vol. 3, edited by G. Bradley, published in 1998 by John Wiley & Sons in collaboration with SITA Technology Limited; non-limiting examples of sulfonium salts are those described above for the fifth embodiment.

[0114] According to the eleventh embodiment, the one or more compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are sulfonium salts having a cationic moiety and an anionic moiety. Preferably, the one or more compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are sulfonium salts, and the anionic moiety is SbF6 - (Hexafluoroantimonate, CAS Nr 17111-95-4); PF6 - (Hexafluorophosphate, CAS Nr 16919-18-9);AsF6 - (Hexafluoroarsenate, CAS Nr 16973-45-8); F4B - (Tetrafluoroborate, CAS Nr 14874-70-5);(C6F5)4B - (Tetrakis(pentafluorophenyl)borate, CAS Nr 47855-94-7);(CF3SO2)3C- (Tris(trifluoromethylsulfonyl)methide, CAS Nr 130447-45-9); (CF3)SO3 - (Trifluoromethanesulfonate, CAS Nr 37181-39-8);(CH3C6H4)SO3 - (4-Methylbenzenesulfonate, CAS Nr 16722-51-3);(CF3)CO2 - (Trifluoroacetate, CAS Nr 14477-72-6);(C4F9)SO3 - (1,1,2,2,3,3,4,4,4-Nonafluoro-1-butanesulfonate, CAS Nr 45187-15-3);(C4F9)CO2 - (2,2,3,3,4,4,5,5,5-nonafluoro-1-pentanoate (CAS Nr 45167-47-3); preferably SbF6 - or PF6 -and the cationic moiety is tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium (CAS Nr 953084-12-3); 10-[1,1'-biphenyl]-4-yl-2-(1-methylethyl)-9-oxo-9H-thioxanthenium (CAS Nr 591773-91-0); or (9-oxo-9H-thioxanthen-2-yl)diphenyl-sulfonium (CAS Nr 1140908-08-2); more preferably tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium (CAS Nr 953084-12-3) or 10-[1,1'-biphenyl]-4-yl-2-(1-methylethyl)-9-oxo-9H-thioxanthenium (CAS Nr 591773-91-0). Preferably, the one or more photoreactive compounds absorbing in the range of about 350 nm to about 470 nm of the top curable coating composition of step b) are sulfonium salts selected from the group consisting of tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium hexafluorophosphate (CAS Nr 953084-13-4); 10-[1,1'-biphenyl]-4-yl-2-(1-methylethyl)-9-oxo-9H-thioxanthenium hexafluorophosphate (CAS Nr 591773-92-1); and mixtures thereof. Particularly suitable examples of sulfonium salts for the eleventh embodiment of the invention are commercially available under the names OMNICAT 270 (CAS Nr 953084-13-4) and OMNICAT 550 (CAS Nr 591773-92-1) from IGM RESINS.

[0115]

[0114] For the first, second, third, fourth, fifth, seventh, ninth and tenth embodiments described in this specification, the top curable coating composition of step b) may further comprise one or more iodonium salts as described above for the first embodiment, and / or one or more sulfonium salts as described above for the fifth embodiment.

[0116] For an eleventh embodiment described herein, the top curable coating composition of step b) may further comprise one or more iodonium salts as described above for the first embodiment, and / or one or more thioxanthones as described above for the first embodiment, and / or one or more mixtures of iodonium salts and anthracenes as described above for the sixth embodiment, and / or one or more anthracenes as described above for the second embodiment, and / or one or more coumarins as described above for the third embodiment, and / or one or more mixtures of naphthalene and anthracene as described above for the fourth embodiment, and / or one or more sulfonium salts as described above for the fifth embodiment, and / or one or more iodonium salts having cationic and anionic moieties as described above for the ninth embodiment, and / or one or more oxonium salts as described above for the tenth embodiment.

[0117]

[0116] Preferred embodiments are those described above as first, second, third, fourth, fifth, sixth, seventh, and eleventh herein.

[0118] A preferred example of the first embodiment described herein is a combination, wherein at least one of the compounds of the radiation curable coating composition of step a) is an iodonium salt, which is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) or bis(4-dodecylphenyl)iodonium hexafluoroantimonate (CAS Nr 71786-70-4), and at least one of the compounds of the top curable coating composition of step b) is 1-chloro-4-propoxy-9H-thioxanthen-9-one (CAS Nr 142770-42-1), 2-isopropyl-9H-thioxanthen-9-one, 2-(1-methylethyl)-9H-thioxanthen-9-one (CAS Nr 5495-84-1), a mixture of 2-(1-methylethyl)-9H-thioxanthen-9-one (CAS Nr 5495-84-1) and 4-(1-methylethyl)-9H-thioxanthen-9-one (CAS Nr 83846-86-0), thioxanthone oligomer or polymer (CAS Nr 2055335-46-9) or 1,3-di[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxy]-2,2-bis[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxymethylpropane (CAS Nr 1003567-83-6); more preferably a combination, wherein at least one of the one or more compounds of the radiation curable coating composition of step a) is an iodonium salt that is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) and at least one of the one or more compounds of the top curable coating composition of step b) is a thioxanthone compound that is 1-chloro-4-propoxy-9H-thioxanthen-9-one (CAS Nr 142770-42-1);At least one of the compounds of the radiation-curable coating composition of step a) is an iodonium salt that is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) and at least one of the compounds of the top-curable coating composition of step b) is a thioxanthone oligomer or polymer (CAS Nr 2055335-46-9); at least one of the compounds of the radiation-curable coating composition of step a) is an iodonium salt that is bis(4-dodecylphenyl)iodonium hexafluoroantimonate (CAS Nr 71786-70-4) and at least one of the compounds of the top-curable coating composition of step b) is 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 5495-84-1) or 4-(1-methylethyl)-9H-thioxanthen-9-one (CAS Nr or at least one of the compounds of the radiation curable coating composition of step a) is an iodonium salt that is bis(4-dodecylphenyl)iodonium hexafluoroantimonate (CAS Nr 71786-70-4) and at least one of the compounds of the top curable coating composition of step b) is a thioxanthone that is 1,3-di[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxy]-2,2-bis[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxymethylpropane (CAS Nr 100356-7-83-6);

[0119]

[0118] A preferred example of the second embodiment described herein is the combination, where at least one of the compounds of the radiation curable coating composition of step a) is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) and at least one of the compounds of the top curable coating composition of step b) is 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4).

[0120] A preferred example of the third embodiment described herein is the combination, wherein at least one of the compounds of the radiation curable coating composition of step a) is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) and at least one of the compounds of the top curable coating composition of step b) is 3-(4-dodecylbenzoyl)-5,7-dimethoxy-2H-1-benzopyran-2-one (CAS Nr 2243703-91-3).

[0121] A preferred example of the fourth embodiment described herein is a combination, where at least one of the compounds of the radiation curable coating composition of step a) is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) and at least one of the compounds of the top curable coating composition of step b) is a naphthalene compound which is 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4) and at least another one is 9,10-diethoxy-naphthalene (CAS Nr 27294-37-7).

[0122]

[0121] A preferred example of the fifth embodiment described herein is the combination, wherein at least one of the compounds of the radiation curable coating composition of step a) is 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) and / or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) and at least one of the compounds of the top curable coating composition of step b) is 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4).

[0123] A preferred example of the sixth embodiment described herein is a combination, in which at least one of the compounds of the radiation curable coating composition of step a) is 4-(phenylthio)phenyl diphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) and / or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9), and at least one of the compounds of the top curable coating composition of step b) is 1-chloro-4-propoxy-9H-thioxanthen-9-one (CAS Nr 142770-42-1) and at least another is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0).

[0124] A preferred example of the seventh embodiment described herein is a combination, in which at least one of the compounds of the radiation curable coating composition of step a) is 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) and at least one of the compounds of the top curable coating composition of step b) is a naphthalene compound, which is 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4) and at least another one is 9,10-diethoxy-naphthalene (CAS Nr 27294-37-7).

[0125] A preferred example of the eighth embodiment described herein is a combination, in which at least one of the compounds of the radiation curable coating composition of step a) is 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) and at least one of the compounds of the top curable coating composition of step b) is 3-(4-C 10 -C 13 -benzoyl)-5,7-dimethoxy-2H-1-benzopyran-2-one (CAS Nr 2243703-91-3), and at least one other is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0).

[0126] A preferred example of the ninth embodiment described herein is a combination, wherein at least one of the compounds of the radiation curable coating composition of step a) is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0), or 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9), and at least one of the compounds of the top curable coating composition of step b) is [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium hexafluoroantimonate (CAS Nr 2091854-13-4).

[0127] A preferred example of the tenth embodiment described herein is a combination, wherein at least one of the compounds of the radiation curable coating composition of step a) is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0), or 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0), or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9), and at least one of the compounds of the top curable coating composition of step b) is 2,4,6-triphenylpyrylium tetrafluoroborate (CAS Nr 448-61-3).

[0128]

[0127] A preferred example of the eleventh embodiment described herein is a combination, in which at least one of the compounds of the radiation curable coating composition of step a) is bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0), or 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0), or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9), and at least one of the compounds of the top curable coating composition of step b) is tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium hexafluorophosphate (CAS Nr 953084-13-4).

[0129]

[0128] The method described herein includes a step c) of at least partially curing one or more indicia (x30) and one or more areas of the coating layer (x10) under said one or more indicia (x30) with a light-emitting diode (LED) curing unit (x50), partially simultaneously or after step b) described herein. On the other hand, in contrast to medium pressure mercury lamps with emission bands in the UV-A, UV-B and UV-C regions of the electromagnetic spectrum, UV-LED lamps emit radiation in the UV-A and / or visible (Vis) regions, for example in the range of about 350 nm to about 470 nm. Moreover, current UV-LED and Vis-LED lamps emit quasi-monochromatic radiation, i.e., they only emit at one wavelength, for example, 365 nm, 385 nm, 395 nm, 405 nm or 450 nm. Step c) of at least partially curing the one or more indicia (x30) is carried out by exposure to UV light at a LED curing unit (x50), preferably at one or more wavelengths between about 355 nm and about 415 nm, more preferably at 365 nm and / or 385 nm and / or 395 nm, emitted from a LED curing unit (x50). "Partially simultaneously" means that both steps are carried out partially simultaneously, i.e. the time of carrying out each step partially overlaps. In the context described herein, it must be understood that if the curing is carried out partially simultaneously with the application step b), the curing is effective after the formation of the one or more indicia (x30) before full or partial curing. Step c) should be carried out after step b) described herein, the time between the two steps being preferably less than 10 seconds, more preferably less than 5 seconds.

[0130]

[0129] The method described herein comprises, after step c) described herein, a step d) of exposing the coating layer (x10) to a magnetic field of a magnetic field generating device described herein in order to orient at least a portion of the non-spherical magnetic or magnetizable pigment particles. According to one embodiment, step d) is performed in order to orient at least a portion of the magnetic or magnetizable pigment particles described herein in a uniaxial direction. According to another embodiment, step d) is performed in order to orient at least a portion of the platelet-shaped magnetic or magnetizable pigment particles in a biaxial direction, preferably in order to orient at least a portion of the platelet-shaped magnetic or magnetizable pigment particles in a biaxial direction having both an X-axis and a Y-axis substantially parallel to the substrate surface. For the embodiment in which the method described herein comprises a step of exposing the coating layer (x10) to a magnetic field of a magnetic field generating device described herein in order to orient at least a portion of the magnetic or magnetizable pigment particles in a biaxial direction, the coating layer (x10) may be subsequently exposed to said magnetic field generating device more than once.

[0131]

[0130] For the embodiment of the method described herein, in which the step of exposing the coating layer (x10) to the magnetic field of a magnetic field generating device described herein is performed to orient at least a portion of the magnetic or magnetizable pigment particles in a biaxial direction, it is required that at least a portion of the non-spherical magnetic or magnetizable pigment particles described herein consist of platelet-shaped magnetic or magnetizable pigment particles having an X-axis and a Y-axis defining the main extension plane of the particle. In contrast to needle-shaped pigment particles, which can be considered as one-dimensional particles, platelet-shaped pigment particles have an X-axis and a Y-axis defining the main extension plane of the particle. In other words, platelet-shaped pigment particles may be considered as two-dimensional particles due to the large aspect ratio of their dimensions, as can be seen from Figure 1. As shown in Figure 1, platelet-shaped pigment particles can be considered as two-dimensional structures with dimensions X and Y substantially larger than dimension Z. Platelet-shaped pigment particles are also referred to in the art as ellipsoidal particles or flakes. Such pigment particles may be described with a major axis X, corresponding to the longest dimension across the pigment particle, and a second axis Y, perpendicular to X, that also lies within said pigment particle.

[0132]

[0131] During the magnetic orientation step described herein of the non-spherical magnetic or magnetizable pigment particles, the substrate (x20) supporting the coating layer (x10) may be placed on a non-magnetic support plate (x40) made of one or more non-magnetic materials.

[0133]

[0132] During the magnetization orientation step of the magnetic or magnetizable pigment particles described herein, the position of the magnetic field generating device is not limited and depends on the selection and design of the magnetization orientation pattern to be created. Depending on the selection and design of the magnetization orientation pattern to be created, the magnetic field generating device (B1, B2, B3) may be placed under the substrate (x20) or above the coating layer (x10).

[0134]

[0133] In contrast to uniaxial orientation, where the magnetic or magnetisable pigment particles are oriented such that only their major axis is restrained by the magnetic field, performing biaxial orientation means that the platelet-shaped magnetic or magnetisable pigment particles are oriented such that their two main axes are restrained. That is, each platelet-shaped magnetic or magnetisable pigment particle can be considered to have a major axis in the plane of the pigment particle and an orthogonal minor axis in the plane of the pigment particle. The major and minor axes of the platelet-shaped magnetic or magnetisable pigment particles are each oriented according to the magnetic field. Effectively, this results in platelet-shaped magnetic pigment particles being adjacent to each other substantially parallel to each other with gaps therebetween. In other words, biaxial orientation aligns the faces of the platelet-shaped magnetic or magnetisable pigment particles such that the faces of said pigment particles are oriented substantially parallel to the faces of the adjacent (in all directions) platelet-shaped magnetic or magnetisable pigment particles. The magnetic field generating devices and methods described herein allow for biaxial orientation of the platelet-shaped magnetic or magnetisable pigment particles described herein, such that they form sheet-like structures with their X and Y axes preferably substantially parallel to the substrate (x20) surface and are flattened in said two dimensions.

[0135]

[0134] Magnetic field generating devices suitable for uniaxially orienting the magnetic or magnetizable pigment particles described herein include, but are not limited to, dipole magnets, quadrupole magnets, and combinations thereof. The following devices are provided herein as illustrative examples:

[0136]

[0135] The optical effect known as the flip-flop effect (also referred to in the art as the switch effect) comprises a first printed portion and a second printed portion separated by a transition, where the pigment particles are aligned parallel to a first surface in the first portion and the pigment particles are aligned parallel to a second surface in the second portion. Methods and magnets for producing said effect are disclosed, for example, in US Patent Application Publication No. 2005 / 0106367 and EP Patent No. 1819525.

[0137]

[0136] An optical effect known as the rolling bar effect as disclosed in US Patent Application Publication No. 2005 / 0106367 may also be produced. The "rolling bar" effect is based on pigment particle orientation that mimics a curved surface across the coating. The observer sees a specular reflection zone that faces away from or towards the observer when the image is tilted. The pigment particles are aligned in a curved manner and follow a convex curve (also referred to in the art as negative curve orientation) or a concave curve (also referred to in the art as positive curve orientation). Methods and magnets that produce said effect are disclosed, for example, in EP 2263806, EP 1674282, EP 2263807, WO 2004 / 007095, WO 2012 / 104098, and WO 2014 / 198905.

[0138]

[0137] An optical effect known as the Venetian blind effect may also be produced. The Venetian blind effect involves pigment particles oriented to impart visibility to the underlying substrate surface along a particular direction of observation such that indicia or other features present on or in the substrate surface are apparent to the observer while they obstruct visibility along other directions of observation. Methods and magnets for producing said effect are disclosed, for example, in U.S. Pat. No. 8,025,952 and European Patent No. 1,819,525.

[0139]

[0138] An optical effect known as the moving rings effect may also be produced. The moving rings effect consists of optical illusion images of objects such as funnels, cones, bowls, circles, ellipses, and hemispheres that appear to move in any xy direction depending on the tilt angle of the optical effect layer. Methods and magnets for producing said effect are disclosed, for example, in EP 1710756, US 8,343,615, EP 2306222, EP 2325677, WO 2011 / 092502, US 2013 / 0084411, WO 2014108404, and WO 2014 / 108303.

[0140]

[0139] Optical effects may also be produced which produce the optical impression of a pattern of light and dark areas that move upon tilting of the optical effect layer. Methods and magnets for producing said effects are disclosed, for example, in WO 2013 / 167425.

[0141]

[0140] Optical effects may also be produced which produce the optical impression of loop shaped bodies with varying sizes upon tilting of the optical effect layer. Methods and magnets for producing these optical effects are disclosed, for example, in WO 2017 / 064052, WO 2017 / 080698 and WO 2017 / 148789.

[0142]

[0141] The optical impression of one or more loop-shaped bodies that change shape when tilting the optical effect layer may also be produced. Methods and magnets for producing said effect are disclosed, for example, in WO 2018 / 054819.

[0143]

[0142] An optical effect may also be produced that gives the optical impression of a moving and rotating lunar crescent when tilted. Methods and magnets for producing said effect are disclosed, for example, in WO 2019 / 215148.

[0144]

[0143] Optical effects may be produced that produce the optical impression of a loop-shaped body that changes size and shape when tilted. Methods and magnets for producing said effect are disclosed, for example, in co-pending PCT patent application WO 2020 / 052862.

[0145]

[0144] The optical effect producing the optical impression of an ortho-parallax effect may be produced, namely in this case in the form of bright reflective vertical bars which move longitudinally when the substrate is tilted about a horizontal / latitudinal axis, or horizontally / latitudinally when the substrate is tilted about a longitudinal axis. Methods and magnets for producing said effect are disclosed, for example, in co-pending PCT patent application International Application No. PCT / EP2020 / 052265.

[0146]

[0145] An optical effect may be produced which produces the optical impression of a loop-shaped body surrounded by one or more loop-shaped bodies, said one or more loop-shaped bodies having their shape and / or their brightness which change on tilt. Methods and magnets for producing said effect are disclosed, for example, in co-pending PCT patent application International Application No. PCT / EP2020 / 054042.

[0147]

[0146] Optical effects may be produced which result in the optical impression of multiple dark spots and multiple bright spots which move and / or appear and / or disappear diagonally when the substrate is tilted, as well as moving and / or appearing and / or disappearing diagonally when the substrate is tilted. Methods and magnets for producing said effects are disclosed, for example, in co-pending European patent applications EP19205715.6 and EP19205716.4.

[0148]

[0147] The magnetic field generating devices described herein may be at least partially embedded in a non-magnetic supporting matrix made of one or more non-magnetic materials.

[0149]

[0148] The non-magnetic materials of the non-magnetic support plate (x40) described herein and the non-magnetic support matrix described herein are preferably independently selected from the group consisting of non-magnetic metals and engineering plastics and polymers, including but not limited to aluminum, aluminum alloys, brass (an alloy of copper and zinc), titanium, titanium alloys, and austenitic steel (i.e., non-magnetic steel). Engineering plastics and polymers include, but are not limited to, polyaryletherketone (PAEK) and its derivatives, polyetheretherketone (PEEK), polyetherketoneketone (PEKK), polyetheretherketoneketone (PEEKK), and polyetherketoneetherketoneketone (PEKEKK); polyacetal, polyamide, polyester, polyether, copolyetherester, polyimide, polyetherimide, high density polyethylene (HDPE), ultra-high molecular weight polyethylene (UHMWPE), polybutylene terephthalate (PBT), polypropylene, acrylonitrile butadiene styrene (ABS) copolymers, fluorinated and perfluorinated polyethylene, polystyrene, polycarbonate, polyphenylene sulfide (PPS), and liquid crystal polymers. Preferred materials are PEEK (polyetheretherketone), POM (polyoxymethylene), PTFE (polytetrafluoroethylene), Nylon (polyamide), and PPS.

[0150]

[0149] The magnetic field generating device described herein may comprise a magnetic plate carrying one or more reliefs, impressions or incisions. WO 2005 / 002866 and WO 2008 / 046702 are examples of such impressed magnetic plates.

[0151]

[0150] The magnetic field generating device described in this specification may be a soft magnetic plate supporting one or more indicia in the form of recesses and / or protrusions, or a soft magnetic plate containing one or more spaces having the shape of one or more indicia, and the orientation step is carried out by forming an assembly of a substrate (x20) supporting a coating layer (x10) on a soft magnetic plate, and said assembly is moved by the inhomogeneous magnetic field of a static magnetic field generating device (x40) in order to orient at least a portion of the platelet-shaped magnetic or magnetizable pigment particles in two axial directions, as described in WO 2018 / 019594 and WO 2018 / 033512.

[0152]

[0151] The magnetic field generating device described in this specification may be a magnetic assembly (x30) including a soft magnetic plate including one or more spaces for accommodating one or more dipole magnets and including one or more recesses and / or one or more protrusions forming one or more continuous loop-shaped indicia and / or one or more discontinuous loop-shaped indicia, as described in WO 2020 / 025218, or a magnetic assembly including a soft magnetic plate including one or more spaces and one or more dipole magnets arranged in the one or more spaces, facing one or more spaces and / or one or more spaces arranged below the soft magnetic plate and one or more pairs of two dipole magnets arranged at a regular interval, as described in WO 2020 / 025482.

[0153]

[0152] There is no limitation on the magnetic field generating devices suitable for biaxially orienting the platelet-shaped magnetic or magnetizable pigment particles described herein.

[0154]

[0153] A particularly preferred apparatus for orienting pigment particles in two axes is disclosed in EP-A-2 157 141. Upon movement of a substrate supporting a coating layer comprising pigment particles, the apparatus disclosed in EP-A-2 157 141 provides a dynamic magnetic field which causes the pigment particles to change direction and rapidly oscillate until both of their main axes (X-axis and Y-axis) are substantially parallel to the substrate surface, i.e. the pigment particles rotate and flatten in said two dimensions into a stable sheet-like formation with their X- and Y-axes substantially parallel to the substrate surface.

[0155]

[0154] Other particularly preferred devices for orienting pigment particles in two axes include linear permanent magnet Halbach arrays, i.e. devices comprising a plurality of magnets with different magnetization directions and a cylinder arrangement. A detailed description of Halbach permanent magnets is given by ZQZhu and D.Howe (Halbach permanent magnet machines and applications: a review, IEE.Proc.Electric Power Appl, 2001, 148, pp. 299-308). The magnetic field provided by such a Halbach array has the property that it is concentrated on one side while it is weakened to almost zero on the other side. Linear Halbach arrays are disclosed, for example, in WO 2015 / 086257 and WO 2018 / 019594, and Halbach cylinder arrangements are disclosed in EP 3224055.

[0156]

[0155] Another particularly preferred device for orienting pigment particles in two directions is a rotating magnet, said magnet comprising a disk-shaped rotating magnet or magnetic field generator that is substantially magnetized along their diameter. Suitable rotating magnets or magnetic field generators are described in US Patent Application Publication No. 2007 / 0172261, said rotating magnets or magnetic field generators generating a radially symmetric time-varying magnetic field allowing for a dual orientation of the magnetic or magnetizable pigment particles of the uncured coating composition. These magnets or magnetic field generators are driven by a shaft (or spindle) connected to an external motor. Chinese Patent No. 102529326 discloses examples of devices comprising a rotating magnet that may be suitable for orienting magnetic or magnetizable pigment particles in two directions. In a preferred embodiment, the device suitable for orienting magnetic or magnetizable pigment particles in two directions is a shaftless disk-shaped rotating magnet or magnetic field generator restrained in a housing made of a non-magnetic, preferably non-conductive material, driven by one or more coils of magnet wire wound around the housing. Examples of such shaft-free, disk-shaped rotating magnets or magnetic field generators are disclosed in WO 2015 / 082344, WO 2016 / 026896, and WO 2018 / 141547.

[0157]

[0156] Another particularly preferred apparatus for biaxially orienting pigment particles is shown in Figure 3A and comprises: a) at least a first set (S1) and a second set (S2), each of the first and second sets (S1, S2) comprising a first bar dipole magnet having a magnetic axis oriented substantially parallel to the substrate during magnetization orientation, and two bar dipole magnets having magnetic axes oriented substantially perpendicular to the substrate; and b) a third pair of bar dipole magnets (P1) having magnetic axes oriented substantially parallel to the substrate, such as those disclosed in co-pending European Patent Application No. 20176506.2.

[0158]

[0157] The method described herein comprises, partially simultaneously with or after step d) described herein, a step e) of at least partially curing the coating layer (x10) in curing units (x60) emitting at least between 250 nm and 320 nm.

[0159]

[0158] The method described herein comprises a step e) of at least partially curing the coating layer (x10) in a curing unit (x60) radiating at least between 250 nm and 320 nm, partially simultaneously or after step d) described herein. By "partially simultaneously" it is meant that both steps are performed partially simultaneously, i.e. the times of performing each step partially overlap. In the context described herein, it must be understood that if the curing is performed partially simultaneously with the application step c), the curing takes effect after the orientation of the non-spherical magnetic or magnetisable pigment particles in the coating layer (x10) before full or partial curing.

[0160]

[0159] According to one embodiment, for example as shown in Figures 2A1 and 2A2, the method described herein comprises the following steps: a) applying onto the surface of a substrate (x20) a radiation-curable coating composition comprising non-spherical magnetic or magnetisable pigment particles as described herein; After step a), a step b) of applying a top coating composition in the form of one or more indicia (x30) onto the coating layer (x10) as described herein, partially simultaneously with or subsequent to step b), step c) of at least partially curing one or more indicia (x30) and one or more areas of the coating layer (x10) beneath said one or more indicia (x30) with an LED curing unit (x50) as described herein; after step c), step d) of exposing the coating layer (x10) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the magnetic or magnetizable pigment particles described herein in areas of the coating layer (x10) not under said one or more indicia (x30), said step d) may be carried out to orient at least a portion of the magnetic or magnetizable pigment particles described herein uniaxially (FIG. 2A1), biaxially (FIG. 2A2), biaxially and then uniaxially (two steps, not shown) or simultaneously biaxially and uniaxially (one step, not shown); Partially simultaneously with or after step d), step e) of at least partially curing the coating layers (x10) with curing units (x60) emitting at least between 250 nm and 320 nm as described herein.

[0161]

[0160] According to one embodiment, the method described herein further comprises a step of exposing the coating layer (x10) to a magnetic field of a magnetic field generating device in order to orient at least a portion of the magnetic or magnetizable pigment particles, said step may be carried out after step b) or partially simultaneously and before step c).

[0162] For example, according to one embodiment shown in FIG. 2B, the method described herein comprises the following steps: a) applying a radiation-curable coating composition comprising non-spherical magnetic or magnetisable pigment particles as described herein onto a surface of a substrate (x20); After step a), a step b) of applying a top coating composition in the form of one or more indicia (x30) onto the coating layer (x10) described herein, After step b), or partially simultaneously, exposing the coating layer (x10) to a magnetic field of a magnetic field generator (B1) in order to orient at least a portion of the magnetic or magnetisable pigment particles as described herein, said step may be carried out to orient at least a portion of the magnetic or magnetisable pigment particles as described herein uniaxially (FIG. 2B), biaxially (not shown), biaxially and then uniaxially (two steps, not shown) or simultaneously biaxially and uniaxially (one step, not shown), After step b) and the orientation step with said magnetic field generating device (B1), a step c) of at least partially curing the one or more indicia (x30) and one or more areas of the coating layer (x10) below said one or more indicia (x30) with a LED curing unit (x50) as described herein, After step c), a step d) of exposing the coating layer (x10) to a magnetic field of a second magnetic field generator (B2) in areas of the coating layer (x10) not under said one or more indicia (x30) in order to orient at least a portion of the magnetic or magnetizable pigment particles as described herein, said step d) may be performed to orient at least a portion of the magnetic or magnetizable pigment particles as described herein uniaxially (FIG. 2B), biaxially (not shown), biaxially and then uniaxially (two steps, not shown) or biaxially and uniaxially simultaneously (one step, not shown), and Partially simultaneously with or subsequent to step d), step e) of at least partially curing the coating layers (x10) with curing units (x60) emitting at least between 250 nm and 320 nm as described herein.

[0163]

[0162] According to another embodiment, the method described herein further comprises a step of exposing the coating layer (x10) to a magnetic field of a magnetic field generating device in order to orient at least a portion of the magnetic or magnetizable pigment particles, said step may be performed after step a) and before step b).

[0164] For example, according to one embodiment shown in Figures 2C / 2D / 2E / 2J / 2K, the method described herein comprises the following steps: a) applying a radiation-curable coating composition comprising non-spherical magnetic or magnetisable pigment particles as described herein onto a surface of a substrate (x20); after step a), exposing the coating layer (x10) to a magnetic field of a magnetic field generator (B1) in order to orient at least a portion of the magnetic or magnetisable pigment particles, said step may be carried out in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles described herein (Figures 2C and D), to biaxially orient (Figure 2E), to biaxially and then uniaxially orient (two steps, Figures 2J and 2K) or to simultaneously biaxially and uniaxially orient (one step, not shown), b) partially simultaneously with or after the orientation step in the magnetic field generating device (B1), applying a top coating composition in the form of one or more indicia (x30) onto the coating layer (x10) as described herein, After step b), a step c) of at least partially curing the one or more indicia (x30) and one or more areas of the coating layer (x10) below said one or more indicia (x30) with an LED curing unit (x50) as described herein, after step c), a step d) of exposing the coating layer (x10) to a magnetic field of a second magnetic field generator (B2, Fig. 2C / 2E), or a third magnetic field generator (B3, Fig. 2J / 2K), or a second and a third magnetic field generator (B2 then B3, Fig. 2D) in order to orient at least a portion of the magnetic or magnetizable pigment particles as described herein, said step d) may be performed in areas of the coating layer (x10) not under the indicia (x30) in order to uniaxially orient (Fig. 2C / 2E / 2J / 2K), to biaxially orient (not shown), to biaxially and then uniaxially orient (two steps, Fig. 2D), or to biaxially and uniaxially orient simultaneously (one step, not shown); and Partially simultaneously with or subsequent to step d), step e) of at least partially curing the coating layers (x10) with curing units (x60) emitting at least between 250 nm and 320 nm as described herein.

[0165]

[0164] For example, according to one embodiment shown in Figures 2F / 2G / 2H / 2I, the method described herein comprises the following steps: a) applying a radiation-curable coating composition comprising non-spherical magnetic or magnetisable pigment particles as described herein onto a substrate (x20); after step a), a step a) of exposing the coating layer (x10) to a magnetic field of a magnetic field generator (B1) in order to orient at least a portion of the magnetic or magnetisable pigment particles as described herein, said step may be carried out in order to uniaxially orient (not shown), to biaxially orient (FIGS. 2F / 2G / 2H / 2I), to biaxially and then uniaxially orient (two steps, not shown) or to simultaneously biaxially and uniaxially orient (one step, not shown) at least a portion of the magnetic or magnetisable pigment particles as described herein, b) partially simultaneously with or after the orientation step in the magnetic field generating device (B1), applying a top coating composition in the form of one or more indicia (x30) onto the coating layer (x10) as described herein, After step b), exposing the coating layer (x10) to a magnetic field of a second magnetic field generator (B2) in order to orient at least a portion of the magnetic or magnetisable pigment particles as described herein, said step may be carried out to orient at least a portion of the magnetic or magnetisable pigment particles as described herein uniaxially (Figs. 2F / 2G / 2H / 2I), to orient biaxially (not shown), to orient biaxially and then uniaxially (two steps, not shown) or to orient biaxially and uniaxially simultaneously (one step, not shown); c) at least partially curing the one or more indicia (x30) and one or more areas of the coating layer (x10) beneath said one or more indicia (x30) with an LED curing unit (x50) as described herein, partially simultaneously with or after the step of exposing the coating layer (x10) to the magnetic field of the second magnetic field generating device (B2); after step c), step d) of exposing the coating layer (x10) to a magnetic field of a third magnetic field generator (B3) in areas of the coating layer (x10) not under said one or more indicia (x30) in order to orient at least a portion of the magnetic or magnetizable pigment particles as described herein, said step d) may be carried out to orient at least a portion of the magnetic or magnetizable pigment particles as described herein uniaxially (FIGS. 2F / 2G / 2H / 2I), to orient biaxially (not shown), to orient biaxially and then uniaxially (two steps, not shown) or to orient biaxially and uniaxially simultaneously (one step, not shown); and Partially simultaneously with or subsequent to step d), step e) of at least partially curing the coating layers (x10) with curing units (x60) emitting at least between 250 nm and 320 nm as described herein.

[0166] The three following steps: a) of applying a radiation-curable coating composition comprising non-spherical magnetic or magnetisable pigment particles as described herein on a surface of a substrate (x20); after step a), b) of applying a top-coating composition in the form of one or more indicia (x30) on a coating layer (x10) as described herein, and partly simultaneously with or after step b), step c) of at least partially curing the one or more indicia (x30) and one or more areas of the coating layer (x10) below said one or more indicia (x30) with an LED curing unit (x50) as described herein may be carried out more than once, and the method comprising two or more steps a) to c) as described herein may further comprise, after the last step c), applying a radiation-curable coating composition in the form of one or more indicia (x30) on a surface of a substrate (x20). or in areas of the coating layer (x10) not under the plurality of indicia (x30), further comprising a step d) of exposing the coating layer (x10) to a magnetic field of a magnetic field generating device (B1) to orient at least a portion of the magnetic or magnetizable pigment particles described herein, said step d) may be carried out to uniaxially orient at least a portion of the magnetic or magnetizable pigment particles described herein, to orient biaxially, to orient biaxially and then uniaxially, or to orient biaxially and uniaxially simultaneously; and further comprising a step e) partially simultaneously with or after step d) of at least partially curing the coating layer (x10) in a curing unit (x60) radiating at least between 250 nm and 320 nm as described herein.

[0167] Alternatively, steps a) and b) may be interchanged, i.e. the method described herein comprises the following steps: applying a top coating composition onto a substrate surface in the form of one or more indicia as described herein; applying a radiation curable coating composition comprising the non-spherical magnetic or magnetizable pigment particles described herein onto the one or more indicia; exposing the coating layer to a magnetic field of a magnetic field generating device to orient at least a portion of the magnetic or magnetizable pigment particles described herein, said step may be performed to uniaxially orient, biaxially orient, biaxially and then uniaxially or simultaneously biaxially and uniaxially orient at least a portion of the magnetic or magnetizable pigment particles described herein; at least partially curing the one or more indicia and one or more areas of the coating layer (x10) on said one or more indicia (x30) with an LED curing unit (x50) as described herein, either simultaneously with or after the orienting step; thereafter, exposing the coating layer (x10) to a magnetic field of a magnetic field generating device in order to orient at least a portion of the magnetic or magnetizable pigment particles as described herein in areas of the coating layer (x10) that are not on said one or more indicia (x30), said step may be carried out to orient at least a portion of the magnetic or magnetizable pigment particles as described herein uniaxially, to orient biaxially, or to orient biaxially and then uniaxially, or to orient biaxially and uniaxially simultaneously; and Partially simultaneously with or after the orientation step, at least partially curing the coating layers (x10) with curing units (x60) emitting at least between 250 nm and 320 nm as described herein.

[0168]

[0167] Alternatively, the step of at least partially curing the coating layer (x10) with a curing unit (x60) emitting at least between 250 nm and 320 nm as described herein may be replaced with a step of at least partially curing the coating layer (x10) with a LED curing unit (x50) as described herein, provided that the second step of applying a top coating composition as described herein to the entire surface of the coating layer (x10) is performed after the step of at least partially curing the one or more indicia (x30) and one or more areas of the coating layer (x10) below said one or more indicia (x30) with a LED curing unit (x50). For example, the method as described herein comprises the following steps: applying a radiation curable coating composition comprising the non-spherical magnetic or magnetisable pigment particles described herein onto a substrate surface; after said step, exposing the coating layer (x10) to a magnetic field of a magnetic field generating device (B1) in order to orient at least a portion of the magnetic or magnetisable pigment particles as described herein, said step may be carried out to uniaxially orient, to biaxially orient, to biaxially and then uniaxially or simultaneously biaxially and uniaxially, preferably to biaxially orient, at least a portion of the magnetic or magnetisable pigment particles as described herein, Partially simultaneously with or after the orientation step with the magnetic field generating device (B1), applying a top coating composition as described herein in the form of one or more indicia (x30) onto the coating layer (x10) as described herein; after said step, exposing the coating layer (x10) to a magnetic field of a second magnetic field generating device (B2) in order to orient at least a portion of the magnetic or magnetisable pigment particles as described herein, said step may be carried out in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles as described herein in order to uniaxially orient biaxially and then uniaxially or simultaneously biaxially and uniaxially, preferably in order to uniaxially orient; partially simultaneously with or after exposing the coating layers (x10) to the magnetic field of the second magnetic field generator (B2), at least partially curing the top coating composition and the lower coating layers (x10) with an LED curing unit (x50) as described herein; After the above step, applying a top coating composition as described herein onto the entire surface of the coating layer (x10) as described herein; after said step, exposing the coating layer (x10) to a magnetic field of a third magnetic field generating device (B3) in order to orient at least a portion of the magnetic or magnetizable pigment particles as described herein, said step may be carried out in order to uniaxially or to biaxially or to simultaneously biaxially and uniaxially orient at least a portion of the magnetic or magnetizable pigment particles as described herein, preferably in order to uniaxially orient; and Simultaneously with or subsequent to the above step, at least partially curing the top coating composition and coating layers (x10) with LED curing units (x50) as described herein.

[0169]

[0168] The present invention provides a method as described herein for making a substrate (x20) comprising an optical effect layer (OEL) exhibiting one or more indicia (x30) on a substrate (x20) as described herein and the resulting one or more optical effect layers (OEL). The substrate (x20) as described herein is preferably selected from the group consisting of paper or other fibrous materials (including woven and nonwoven fibrous materials) such as cellulose, paper-containing materials, glass, metal, ceramic, plastics and polymers, metallized plastics or polymers, composite materials, and mixtures or combinations of two or more thereof. Typical paper, paper-like or other fibrous materials are composed of various fibers including, but not limited to, abaca, cotton, linen, wood pulp, and mixtures thereof. As is well known to those skilled in the art, cotton and cotton / linen mixtures are preferred for banknotes, while wood pulp is commonly used in non-banknote security documents. According to other embodiments, the substrate (x20) described herein is based on plastics and polymers, metallized plastics or polymers, composite materials, and mixtures or combinations of two or more thereof. Suitable examples of plastics and polymers include polyolefins such as polypropylene (PP), including polyethylene (PE) and biaxially oriented polypropylene (BOPP), polyamides, polyesters such as poly(ethylene terephthalate) (PET), poly(1,4-butylene terephthalate) (PBT), poly(ethylene 2,6-naphthoate) (PEN), and polyvinyl chloride (PVC). Spunbond olefin fibers, such as those sold under the trademark Tyvek®, may also be used as substrates. Representative examples of plated plastics or polymers include the above plastics or polymeric materials with metals disposed on the surface in a continuous or discontinuous manner. Representative examples of metals include, but are not limited to, aluminum (Al), chromium (Cr), copper (Cu), gold (Au), silver (Ag), alloys thereof, and combinations of two or more of the aforementioned metals. The metallization of the plastic or polymeric material may be carried out by an electrodeposition process, a high vacuum coating process, or a sputtering process.Representative examples of composite materials include, but are not limited to, multi-layered structures or laminates of paper and at least one plastic or polymeric material such as those mentioned above, as well as plastic and / or polymeric fibers incorporated into paper-like or fibrous materials such as those mentioned above. Of course, the substrate may contain further additives known to those skilled in the art, such as fillers, sizing agents, whitening agents, processing aids, reinforcing agents, or wet strength agents. When the OELs exhibiting one or more indicia (x30) made according to the present invention are used for decorative or cosmetic purposes, including, for example, nail lacquers, said OELs may be made on other types of substrates, including animal or human nails, artificial nails, or other parts.

[0170]

[0169] Also described herein is a method for producing a security document, or a decorative element or body, the method comprising: a) preparing a security document, or a decorative element or body, and b) preparing one or more optical effect layers as described herein, in particular those obtained by the methods described herein, for inclusion in the security document, or the decorative element or body.

[0171]

[0170] Once the OEL made according to the present invention is on a security document or article, the substrate may include printing, coating, or laser mark or laser perforation indicia, water gauge, anti-counterfeit thread, fiber, planchette, luminescent compound, window, foil, decal, and combination of two or more thereof, for the purpose of further improving the security level and resistance of said security document or article to counterfeiting and illegal duplication. For the same purpose of further improving the security level and resistance of security documents and articles to counterfeiting and illegal duplication, the substrate may include one or more marking substances or identification additives and / or machine readable substances (e.g. luminescent substances, UV / visible / IR absorbing substances, magnetic substances, and combinations thereof).

[0172]

[0171] If necessary, a primer layer may be applied to the substrate before step a). This may enhance the quality or promote adhesion of the OELs described herein. Examples of such primer layers may be found in WO 2010 / 058026.

[0173]

[0172] With the purpose of improving the durability against dirt or chemical resistance and cleanliness, and thus the circulation life, of the security document, article, or decorative element or object comprising the OEL obtained by the method described herein, or with the purpose of modifying their aesthetics (e.g. optical gloss), one or more protective layers may be applied on the OEL. If present, the one or more protective layers typically consist of a protective varnish. The protective varnish may be a radiation curable composition, a thermal drying composition, or any combination thereof. Preferably, the one or more protective layers are a radiation curable composition, more preferably a UV-Vis curable composition. The protective layer is typically applied after the formation of the OEL.

[0174]

[0173] The present invention further provides an optical effect layer (OEL) exhibiting one or more indicia (x30) as described herein and produced by the method as described herein. The shape of the optical effect layer (OEL) as described herein may be continuous or discontinuous. According to one embodiment, the shape of the coating layer (x10) represents one or more indicia, dots and / or lines, said indicia having the same shape as one or more indicia (x30) of the top coating composition as described herein or having a different shape.

[0175]

[0174] The OEL exhibiting one or more indicia (x30) described herein may be applied directly onto a substrate on which it will remain permanently (such as for banknote applications). Alternatively, the optical effect layer may also be applied onto a temporary substrate for fabrication purposes from which the OEL is subsequently removed. This may facilitate, for example, the fabrication of the optical effect layer (OEL), especially while the binder material is still in its fluid state. The temporary substrate may then be removed from the OEL after curing the coating composition for fabrication of the OEL.

[0176] Alternatively, in other embodiments, the adhesive layer may be present on one or more indicating indicia (x30) or on the side of the substrate comprising the OEL, said adhesive layer being on the substrate opposite to the side on which the OEL is provided or on the same side as the OEL and on the OEL. Thus, the adhesive layer may be applied to the OEL or to the substrate, said adhesive layer being applied after the curing step is finished. Such articles may be attached to various kinds of documents or other articles or goods without machinery and printing and other processes involving fairly high effects. Alternatively, the substrates described herein comprising the OELs described herein may be in the form of transfer foils, which can be applied to the document or article in a separate transfer step. For this purpose, the substrate is provided with a release coating on which the OEL is produced as described herein. One or more adhesive layers may be applied to the optical effect layer so produced.

[0177]

[0176] Also described herein are substrates comprising more than one, ie, two, three, four, etc., optical effect layers (OELs) obtained by the methods described herein.

[0178] Also described herein are articles, documents, in particular security documents, decorative elements, and decorative objects, comprising an optical effect layer (OEL) made according to the present invention. The articles, in particular security documents, decorative elements, or decorative objects, may comprise more than one (e.g., two, three, etc.) OEL made according to the present invention.

[0179]

[0178] As mentioned above, OELs made according to the present invention may be used for decorative purposes and to protect and authenticate security documents.

[0180]

[0179] Representative examples of decorative elements or objects include, but are not limited to, articles of luxury goods, cosmetic packaging, automobile parts, electronic / electrical appliances, furniture, and nails.

[0181]

[0180] Security documents include, but are not limited to, value documents and value products. Representative examples of value documents include, but are not limited to, banknotes, certificates, tickets, invoices, certificates, revenue stamps, and tax labels, agreements, etc., passports, identity cards, visas, driver's licenses, bank cards, credit cards, transaction cards, access documents or cards, admission tickets, public transport tickets, academic diplomas or entitlements, etc., preferably identity documents such as banknotes, identity documents, entitlement documents, driver's licenses, and credit cards. The term "value products" refers in particular to packaging materials for cosmetics, dietary supplements, medicines, alcohol, tobacco articles, beverages or food, electrical / electronic articles, textiles or jewelry, i.e., articles that are protected against counterfeiting and / or illegal duplication to ensure the contents of the package, such as for example, for genuine medicines. Examples of these packaging materials include, but are not limited to, labels, such as authentication brand labels, tamper-evident labels, and seals. It is pointed out that, without limiting the scope of the present invention, the disclosed substrates, value documents, and value products are given solely for illustrative purposes.

[0182]

[0181] Alternatively, the optical effect layers (OELs) described herein may be fabricated on a supplementary substrate, such as, for example, a security thread, security stripe, foil, decal, window, or label, and then transferred to the security document in a separate step.

[0183]

[0182] Those skilled in the art may foresee some modifications from the specific embodiments described above without departing from the spirit of the present invention. Such modifications are encompassed by the present invention.

[0184]

[0183] Additionally, all documents referenced throughout the specification are incorporated by reference in their entirety, as if fully set forth herein. EXAMPLES

[0185] The present invention will now be described in more detail with reference to the following non-limiting examples. The following examples provide more detail on the preparation of an optical effect layer (OEL) exhibiting one or more indicia in the form of a rectangle. Magnetic pigment particles (obtained from VIAVI Solutions, Santa Rosa, Calif., with a diameter of about 10.7 μm, d 50 and seven-layered green-patina platelet-shaped optically variable magnetic pigment particles having a flake shape of about 1 μm thickness; and about 19 μm diameter d obtained from VIAVI Solutions (Santa Rosa, Calif.). 50 A screen printing composition comprising 5 layers of silver magnetic pigment particles having a flake shape and a thickness of about 1 μm has been prepared and is described in Table 1 A. A top coating inkjet printing composition has been prepared and is described in Tables 1B-1 and 1B-2. [Table 1] JPEG2024517567000008.jpg104149 [Table 2] JPEG2024517567000010.jpg73149 JPEG2024517567000011.jpg49149 [Table 3] JPEG2024517567000013.jpg20149 [Table 4]

[0186] (Preparation of Composition)

[0185] Screen printing compositions were prepared independently by mixing the ingredients shown in Table 1A using a Dispermat CV-3 for 10 minutes at 2000 rpm.

[0187]

[0186] Inkjet topcoating printing compositions were prepared independently by mixing the ingredients shown in Tables 1B1 and 1B2 using Dispermat LC220-12 at room temperature and 1000 rpm for 10 minutes.

[0188]

[0187] Primer compositions were prepared by mixing the ingredients listed in Table 2 using a Dispermat CV-3 at 2000 rpm for 10 minutes.

[0189]

[0188] The viscosities of the compositions were measured independently at 25°C using a Brookfield viscometer (model "DV-I Prime", spindle S27 at 100 rpm for screen printing compositions and primer compositions and S00 at 50 rpm for top coating inkjet printing compositions) and are shown in Tables 1A / B and 2.

[0190] (Preparation of Optical Effect Layer (OEL))

[0189] Optical effect layers (OELs) were prepared by the inventive methods (E1-E36) and comparative methods (C1-C26). Tables 5A1-5A4 provide an overview of i) the composition combinations used during the methods, ii) a schematic diagram of the methods themselves, iii) the substrates to which the screen printing compositions were applied, and iv) the magnetic field generating device used during the magnetic orientation step. [Table 5] JPEG2024517567000016.jpg72149 [Table 6] [Table 7] [Table 8] The magnetic field generator was: MD1: Magnetic assembly as described above and shown in FIG. 3A (for biaxial alignment) MD2: Bar dipole magnet (for uniaxial alignment) as described below MD3: Magnetic assembly (for uniaxial alignment) as described below and shown in FIG. 3B The substrates (x20) S1 to S4 were as follows: The substrate S1 is a polymer substrate (Guardian® from CCL Secure, Substrate S2 is a hybrid substrate (LongLife® from Louisenthal, The substrate S3 is a reference paper (Louisenthal BNP paper, 100 g / m 2 ), Substrate S4 is a reference paper (Louisenthal BNP paper, 100 g / m2) coated by hand screen printing using a T90 screen with the primer composition disclosed in Table 2 (primer thickness: 20 μm). 2 ), 250nm~320nm (two lamps: IST Metz GmbH iron-doped mercury lamp 200W / cm 2 + Mercury lamp 200W / cm 2 The coating was cured by UV irradiation using a curing unit irradiating at least 200 s (2 passes, 100 m / min).

[0191] In FIG. 2A1, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), step b) of inkjet printing a top coating inkjet printing composition to form indicia (230); Step c) at least partially curing the indicia (230) and the area of ​​the coating layer (210) below the indicia (230) with an LED curing unit (250); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1) in order to uniaxially orient at least a portion of the magnetic or magnetizable pigment particles in the not yet hardened areas of the coating layer (210), Partially simultaneously with step d), step e) of curing the coating layer (210) in a Hg curing unit (260) while maintaining a magnetic field generating device (B1) in the vicinity of the coating layer (210) to form an optical effect layer.

[0192] In FIG. 2B, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), step b) of inkjet printing a top coating inkjet printing composition to form indicia (230); After step b), exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B1) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles, partially simultaneously with step b), a step c) of at least partially curing the indicia (230) and areas of the coating layer (210) below the indicia (230) with an LED curing unit (250) while maintaining a first magnetic field generating device (B1) in the vicinity of the coating layer (210); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a second magnetic field generator (B2) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles as described herein in the not yet cured areas of the coating layer (210), Partially simultaneously with step d), step e) of curing the coating layer (210) in a Hg curing unit (260) while maintaining a magnetic field generating device (B2) in the vicinity of the coating layer (210) to form an optical effect layer.

[0193] In FIG. 2C, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B1) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles, b) inkjet printing a top coating inkjet printing composition onto the coating layer (210) to form indicia (230) while maintaining the first magnetic field generating device (B1) in proximity to the coating layer (210) partially simultaneously with the step of exposing the coating layer (210) to the magnetic field of the first magnetic field generating device (B1); After step b), a step c) of at least partially curing the indicia (230) and the area of ​​the coating layer (210) below the indicia (230) with an LED curing unit (250) while maintaining the magnetic field generating device (B1) in the vicinity of the coating layer (210); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a second magnetic field generator (B2) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the not yet hardened areas of the coating layer (210), Partially simultaneously with step d), step e) of curing the coating layer (210) in a Hg curing unit (260) while maintaining a magnetic field generating device (B2) in the vicinity of the coating layer (210) to form an optical effect layer.

[0194] In FIG. 2D, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B1) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles, b) inkjet printing a top coating inkjet printing composition onto the coating layer (210) to form indicia (230) while maintaining the first magnetic field generating device (B1) in proximity to the coating layer (210) partially simultaneously with the step of exposing the coating layer (210) to the magnetic field of the first magnetic field generating device (B1); After step b), a step c) of at least partially curing the indicia (230) and the area of ​​the coating layer (210) below the indicia (230) with a LED curing unit (250) while maintaining the first magnetic field generating device (B1) in the vicinity of the coating layer (210); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a second magnetic field generator (B2) in order to biaxially orient at least a portion of the magnetic or magnetisable pigment particles in the not yet hardened areas of the coating layer (210), After step d), exposing the coating layer (210) to a magnetic field of a third magnetic field generating device (B3) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the not yet hardened areas of the coating layer (210), After exposing the coating layer (210) to the magnetic field of the third magnetic field generator (B3), the coating layer (210) is cured in the Hg curing unit (260) to form an optical effect layer (e). For example E17 made according to the method shown in FIG. 2D, the time between the orientation step in the third magnetic field generator (B3) and step e) was about 0.5 seconds.

[0195] In FIG. 2E, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B1) in order to biaxially orient at least a portion of the magnetic or magnetisable pigment particles, b) inkjet printing a top-coating inkjet printing composition onto the coating layer (210) to form indicia (230), after exposing the coating layer (210) to a magnetic field of a magnetic field generating device (B1); After step b), a step c) of at least partially curing the indicia (230) and the area of ​​the coating layer (210) below said indicia (230) with an LED curing unit (250); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a second magnetic field generator (B2) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the not yet hardened areas of the coating layer (210), Partially simultaneously with the step of exposing the coating layer (210) to the magnetic field of the second magnetic field generating device (B2), step e) of curing the coating layer (210) in a Hg curing unit (260) while maintaining the second magnetic field generating device (B2) in the vicinity of the coating layer (210) to form an optical effect layer.

[0196] In FIG. 2F, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B1) in order to biaxially orient at least a portion of the magnetic or magnetisable pigment particles, b) inkjet printing a top-coating inkjet printing composition onto the coating layer (210) to form indicia (230), after the step of exposing the coating layer (210) to the magnetic field of a first magnetic field generating device (B1); After step b), exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles, partially simultaneously with step b), a step c) of at least partially curing the indicia (230) and the area of ​​the coating layer (210) below the indicia (230) with an LED curing unit (250) while maintaining a second magnetic field generating device (B2) in the vicinity of the coating layer (210); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the not yet cured areas of the coating layer (210), Partially simultaneously with the step of exposing the coating layer (210) to the magnetic field of the third magnetic field generating device (B3), step e) of curing the coating layer (210) in a Hg curing unit (260) while maintaining the third magnetic field generating device (B3) in the vicinity of the coating layer (210) to form an optical effect layer.

[0197]

[0196] In FIG. 2G, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B1) in order to biaxially orient at least a portion of the magnetic or magnetisable pigment particles, b) inkjet printing a top-coating inkjet printing composition onto the coating layer (210) to form indicia (230), after exposing the coating layer (210) to the magnetic field of a first magnetic field generating device (B1); After step b), exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles, c) at least partially curing the indicia (230) and the area of ​​the coating layer (210) below the indicia (230) with an LED curing unit (250) while maintaining the second magnetic field generating device (B2) in proximity to the coating layer (210) partially simultaneously with the step of exposing the coating layer (210) to the magnetic field of the second magnetic field generating device (B2); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the not yet cured areas of the coating layer (210), After exposing the coating layer (210) to the magnetic field of the third magnetic field generator (B3), the coating layer (210) is cured in the Hg curing unit (260) to form an optical effect layer (e). For Example E19 made according to the method shown in FIG. 2G, the time between the orientation in the third magnetic field generator (B3) and step e) was about 0.5 seconds.

[0198] In FIG. 2H, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B1) in order to biaxially orient at least a portion of the magnetic or magnetisable pigment particles, b) inkjet printing a top-coating inkjet printing composition onto the coating layer (210) to form indicia (230), after the step of exposing the coating layer (210) to the magnetic field of a first magnetic field generating device (B1); After step b), exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles, After step b), a step c) of at least partially curing the indicia (230) and the area of ​​the coating layer (210) below said indicia (230) with an LED curing unit (250); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the still hardened areas of the coating layer 210, Partially simultaneously with the step of exposing the coating layer (210) to the magnetic field of the third magnetic field generator (B3), step e) of curing the coating layer (210) in a Hg curing unit (260) while maintaining the magnetic field generator (B3) in the vicinity of the coating layer (210) to form an optical effect layer.

[0199] In FIG. 2I, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B1) in order to biaxially orient at least a portion of the magnetic or magnetisable pigment particles, b) inkjet printing a top-coating inkjet printing composition onto the coating layer (210) to form indicia (230), after the step of exposing the coating layer (210) to the magnetic field of a first magnetic field generating device (B1); After step b), exposing the coating layer (210) to a magnetic field of a second magnetic field generating device (B2) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles, c) at least partially curing the indicia (230) and the area of ​​the coating layer (210) below the indicia (230) with a LED curing unit (250) after said step of exposing the coating layer (210) to the magnetic field of the second magnetic field generator (B2); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the not yet cured areas of the coating layer (210), After exposing the coating layer (210) to the magnetic field of the third magnetic field generator (B3), the coating layer (210) is cured in the Hg curing unit (260) to form an optical effect layer (e). For example E21 produced according to the method shown in FIG. 2I, the time between the orientation in the third magnetic field generator (B3) and step e) was about 0.5 seconds.

[0200] In FIG. 2J, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B1) in order to biaxially orient at least a portion of the magnetic or magnetisable pigment particles, After the step of exposing the coating layer (210) to the magnetic field of the first magnetic field generating device (B1), exposing the coating layer (210) to the magnetic field of a second magnetic field generating device (B2) in order to uniaxially orient at least a portion of the magnetic or magnetizable pigment particles; b) inkjet printing a top coating inkjet printing composition onto the coating layer (210) to form indicia (230) while maintaining the second magnetic field generating device (B2) in proximity to the coating layer (210) partially simultaneously with the step of exposing the coating layer (210) to the magnetic field of the second magnetic field generating device (B2); c) at least partially curing the indicia (230) and the area of ​​the coating layer (210) below the indicia (230) with an LED curing unit (250) while maintaining the second magnetic field generating device (B2) in proximity to the coating layer (210) partially simultaneously with the step of exposing the coating layer (210) to the magnetic field of the second magnetic field generating device (B2); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a third magnetic field generator (B3) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the not yet cured areas of the coating layer (210), Partially simultaneously with the step of exposing the coating layer (210) to the magnetic field of the third magnetic field generator (B3), step e) of curing the coating layer (210) in a Hg curing unit (260) while maintaining the magnetic field generator (B3) in the vicinity of the coating layer (210) to form an optical effect layer.

[0201]

[0200] In FIG. 2K, the method included the following steps: Step a) (not shown) of screen printing a screen printing composition onto a substrate (220) to form a coating layer (210); After step a), exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B1) in order to biaxially orient at least a portion of the magnetic or magnetisable pigment particles, After the step of exposing the coating layer (210) to the magnetic field of the first magnetic field generating device (B1), exposing the coating layer (210) to the magnetic field of a second magnetic field generating device (B2) in order to uniaxially orient at least a portion of the magnetic or magnetizable pigment particles; b) inkjet printing a top-coating inkjet printing composition onto the coating layer (210) to form indicia (230), after exposing the coating layer (210) to the magnetic field of a first magnetic field generating device (B2); After step b), a step c) of at least partially curing the indicia (230) and the area of ​​the coating layer (210) below said indicia (230) with an LED curing unit (250); After step c), a step d) of exposing the coating layer (210) to a magnetic field of a first magnetic field generating device (B3) in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the not yet cured areas of the coating layer (210), Partially simultaneously with the step of exposing the coating layer (210) to the magnetic field of the third magnetic field generator (B3), step e) of curing the coating layer (210) and the indicia (230) in a Hg curing unit (260) while maintaining the magnetic field generator (B3) in proximity to the coating layer (210) to form an optical effect layer.

[0202]

[0201] Comparative Examples C1-C26 were prepared according to the following method: Method 1 (C1-C20) includes: screen printing the screen printing composition onto a substrate to form a coating layer; inkjet printing a top coating inkjet printing composition to form indicia; Thereafter, exposing the coating layer to an LED curing unit; thereafter, exposing the coating layer to a magnetic field of a first magnetic field generating device in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the as yet uncured areas of the coating layer; Partially simultaneously with the step of exposing the coating layer to the magnetic field of the first magnetic field generating device, exposing the coating layer to an Hg curing unit while maintaining the first magnetic field generating device in proximity to the coating layer. Method 2 (C21) involves: screen printing the screen printing composition onto a substrate to form a coating layer; Thereafter, exposing the coating layer to a magnetic field of a first magnetic field generating device in order to biaxially orient at least a portion of the magnetic or magnetizable pigment particles; thereafter, inkjet printing a top coating inkjet printing composition to form the indicia; thereafter, exposing the coating layer to a magnetic field of a second magnetic field generating device in order to uniaxially orient at least a portion of the magnetic or magnetizable pigment particles; partially simultaneously exposing the coating layer to an LED curing unit while maintaining a second magnetic field generating device in proximity to the coating layer; thereafter, exposing the coating layer to a magnetic field of a third magnetic field generating device in order to uniaxially orient at least a portion of the magnetic or magnetisable pigment particles in the as yet uncured areas of the coating layer; Partially simultaneously, exposing the coating layer to a Hg curing unit while maintaining a third magnetic field generating device in proximity to the coating layer. Method 3 (C22 and C24) involves: screen printing the screen printing composition onto a substrate to form a coating layer; thereafter, inkjet printing a top coating inkjet printing composition to form the indicia; Thereafter, exposing the coating layer to an LED curing unit; exposing the coating layer to a magnetic field of a magnetic field generating device to uniaxially orient at least a portion of the magnetic or magnetizable pigment particles in the as yet uncured areas of the coating layer; Thereafter, exposing the coating layer to a Hg curing unit. Method 4 (C23 and C25) includes: screen printing the screen printing composition onto a substrate to form a coating layer; Thereafter, exposing the coating layer to a magnetic field of a first magnetic field generating device in order to biaxially orient at least a portion of the magnetic or magnetizable pigment particles; thereafter, inkjet printing a top coating inkjet printing composition to form the indicia; Thereafter, exposing the coating layer to an LED curing unit; Thereafter, exposing the coating layer to a magnetic field of a second magnetic field generating device in order to uniaxially orient at least a portion of the magnetic or magnetizable pigment particles in the as yet uncured areas of the coating layer (210); Partially simultaneously, exposing the coating layer to a Hg curing unit while maintaining a second magnetic field generating device in proximity to the coating layer. Method 5 (C26) includes: screen printing the screen printing composition onto a substrate to form a coating layer; Thereafter, exposing the coating layer to a magnetic field of a first magnetic field generating device in order to biaxially orient at least a portion of the magnetic or magnetizable pigment particles; thereafter, inkjet printing a top coating inkjet printing composition to form the indicia; thereafter, exposing the coating layer to a magnetic field of a second magnetic field generating device in order to uniaxially orient at least a portion of the magnetic or magnetizable pigment particles; partially simultaneously exposing the coating layer to a Hg curing unit while maintaining a second magnetic field generating device in proximity to the coating layer; thereafter, exposing the coating layer to a magnetic field of a third magnetic field generating device in order to uniaxially orient at least a portion of the magnetic or magnetizable pigment particles; Partially simultaneously, exposing the coating layer to an LED curing unit while maintaining a third magnetic field generating device in proximity to the coating layer (210).

[0203] (Screen Printing of Screen Printing Composition)

[0202] The screen printing compositions described in Table 1A were independently applied by hand screen printing using a T90 screen onto the substrates (x20) (70 mm x 70 mm) described in Table 5 to form coating layers (x10) having the following dimensions: 25 mm x 25 mm and a thickness of approximately 20 μm.

[0204] Inkjet Printing of Top Coating Inkjet Printing Composition The top coating inkjet printing compositions described in Tables 1B-1 and 1B2 were printed at approximately 5 g / m by DOD inkjet printing using a Kyocera KJ4A-TA printhead (600 dpi) to form indicia having a rectangular shape with the following dimensions: 20 mm x 12 mm. 2 were given separately.

[0205] Magnetic Orientation of Screen Printing Compositions

[0204] A step of exposing the coating layer (x10) to a magnetic field of a magnetic field generating device described below was carried out separately to orient at least a portion of the magnetic or magnetizable pigment particles contained in the coating layer consisting of the screen printing composition.

[0206] Magnetic field generating device MD1 for biaxial alignment (shown in FIG. 3A) The magnetic field generating device MD1 used for biaxially orienting at least a portion of the magnetic or magnetizable pigment particles comprises a) a first rod-shaped dipole magnet (371) and two second rod-shaped dipole magnets (372). a and 372 b ) and a first set (S1) including a first bar-shaped dipole magnet (371) and a second bar-shaped dipole magnet (372) a and 372 b ), and b) a second set (S2) including a third rod-shaped dipole magnet (373 a and 373 b ) pair (P1).

[0207]

[0206] The first rod-shaped dipole magnets (371) of the first and second sets (S1, S2) and the second rod-shaped dipole magnets (372) of the first and second sets (S1, S2) a and 372 b ) and a pair (P1) of third rod-shaped dipole magnets (373 a and 373 b ) had the same outer surface.

[0208]

[0207] The third rod-shaped dipole magnet (373 a) is connected to the second rod-shaped dipole magnet (372) of the first set (S1) to form a line. a ) and a second rod-shaped dipole magnet (372) of a second set (S2). a ) was aligned with the third rod-shaped dipole magnet (373 b ) is connected to the second rod-shaped dipole magnet (372) of the first set (S1) to form a line. b ) and a second rod-shaped dipole magnet (372) of a second set (S2). b ) was aligned.

[0209]

[0208] The first rod-shaped dipole magnets (371) of the first and second sets (S1, S2) had the following dimensions: a first thickness (L1) of 5 mm, a first length (L4) of 60 mm, and a first width (L5) of 40 mm. The second rod-shaped dipole magnets (372) of the first and second sets (S1, S2) a and 372 b ) had the following dimensions: a second thickness (L2) of 10 mm, a second length (L6) of 40 mm, and a second width (L7) of 10 mm. Each of the pair (P1) of third rod-shaped dipole magnets (373a and 373b) had the following dimensions: a third thickness (L3) of 10 mm, a third length (L8) of 20 mm, and a third width (L9) of 10 mm.

[0210]

[0209] The first rod-shaped dipole magnet (371) of the first set (S1) and the second rod-shaped dipole magnet (372) of the first set (S1) a and 372 b ) are aligned to form a row, and a first rod-shaped dipole magnet (371) of the second set (S2) and a second rod-shaped dipole magnet (372) of the second set (S2) are aligned to form a row. a and 372 b ) were aligned to form a row. For each set (S1, S2) and each row described herein, a first rod-shaped dipole magnet (371) and two second rod-shaped dipole magnets (372 a and 372 b ) were spaced apart by a second distance (d2) of 2 mm. For each line described herein, a third rod-shaped dipole magnet (373 a and 373b ) and two second rod-shaped dipole magnets (372 a ) were spaced apart by a third distance (d3) of 2 mm.

[0211]

[0210] The first rod-shaped dipole magnets (371) of the first and second sets (S1, S2) had their magnetic axes oriented substantially parallel to the substrate (320), the first rod-shaped dipole magnets (371) of the first set (S1) had a magnetic direction opposite to the magnetic direction of the first rod-shaped dipole magnets (371) of the second set (S2), and were spaced apart by a first distance (d1) of 24 mm (corresponding to the sum of the third length (L8) and the two third distances (d3).

[0212]

[0211] The two second rod-shaped dipole magnets (372) of the first and second sets (S1, S2) a and 372 b The second rod-shaped dipole magnet (372) of the first set (S1) had a magnetic axis oriented substantially perpendicular to the first plane and substantially perpendicular to the substrate (320). a The south pole of the second rod-shaped dipole magnet (372) faces the first plane and the substrate (320), b The N pole of the first rod-shaped dipole magnet (371) of the first set (S1) faces the substrate (320), and the N pole of the first rod-shaped dipole magnet (372) of the first set (S1) faces the substrate (320). b ) in the second set (S2). a The north pole of the second rod-shaped dipole magnet (372) of the second set (S2) faces the first plane and the substrate (320). b The south pole of the first rod-shaped dipole magnet (371) of the second set (S2) faces the substrate (320), and the north pole of the first rod-shaped dipole magnet (372) of the second set (S2) faces the substrate (320). a ) was heading towards

[0213]

[0212] The third rod-shaped dipole magnet (373 a ) is connected to the south pole of the second rod-shaped dipole magnet (372) of the first set (S1). a ) toward the second rod-shaped dipole magnet (372 a) has a south pole facing the substrate (320), and a third rod-shaped dipole magnet (373 b The north pole of the second rod-shaped dipole magnet (372) of the first set (S1) is b ) toward the second rod-shaped dipole magnet (372 b ) has a north pole facing the substrate (320).

[0214]

[0213] The first rod-shaped dipole magnet (371) of the first and second sets (S1, S2), the second rod-shaped dipole magnet (373) of the first and second sets (S1, S2) a and 373 b ), and a pair (P1) of third rod-shaped dipole magnets (372 a and 372 b ) was embedded in a non-magnetic supporting matrix (not shown) made of NdFeB N42 and made of polyoxymethylene (POM) having the following dimensions: 115 mm×115 mm×12 mm.

[0215] During magnetic orientation, the substrate (320) supporting the coating layer (310) was placed on a non-magnetic support plate made of POM as described above with the coating layer (310) facing the environment to form an assembly, said non-magnetic support plate (340) having the following dimensions: 180 mm x 130 mm x 2 mm and including a centrally aligned opening (48 mm x 48 mm) with the coating layer (310) facing the magnetic field generator (300). The assembly was moved back and forth three times near and above the magnetic field generator (300) at a distance of about 2 mm from the top surface of said device.

[0216] [Magnetic field generator MD2 for uniaxial orientation]

[0215] The magnetic field generating device MD2 used to uniaxially orient at least a portion of the magnetic or magnetizable pigment particles included a bar-shaped dipole magnet having a length of about 30 mm, a width of about 24 mm, and a thickness of about 6 mm, said bar-shaped dipole magnet being embedded in a matrix made of POM and having the following dimensions: 40 mm x 40 mm x 15 mm. The N-S magnetic axis of the bar-shaped dipole magnet was parallel to the substrate (320) surface and parallel to the width. The bar-shaped dipole magnet was made of NdFeB N42.

[0217]

[0216] During magnetic orientation, the substrate (320) supporting the coating layer (310) was placed on a non-magnetic support plate made of the above-mentioned POM with the coating layer (310) facing the environment to form an assembly. The assembly was placed near and on top of the magnetic field generator such that the substrate (320) was at a distance of about 6 mm from the top surface of the rod-shaped dipole magnet.

[0218] [Magnetic field generating device MD3 for single-axis alignment (shown in FIG. 3B)] In Fig. 6A of co-pending European Patent Application No. 19205715.6, a magnetic field generating device MD3 used for uniaxially orienting at least a portion of magnetic or magnetisable pigment particles is disclosed, comprising a first magnetic field generating device (330) embedded in a first square support matrix (332) and a second magnetic field generating device (340) comprising a second dipole magnet (341) embedded in a second square support matrix (342), the second magnetic field generating device (340) being disposed below the first magnetic field generating device (330), the first magnetic field generating device (330) being disposed between a substrate (320) supporting a coating layer (310) and the second magnetic field generating device (340). The first magnetic field generating device (330) and the second magnetic field generating device (340) are positioned centrally with respect to each other.

[0219]

[0218] The first magnetic field generating device (330) has nine parallel straight lines α i (α 1~9 ) and nine parallel straight lines β j (β 1~941 first dipole magnets (331) each having their centers positioned on the intersections of a grid including 1~41 ), and the line α i (α 1~9 ) are parallel to each other, and the straight line β j (β 1~9 ) are parallel to each other, and the straight line α i is the line β j The nine lines α i (α 1~9 ) were equally spaced, with adjacent lines separated by a distance of 2.5 mm. i (α 1 / 3 / 5 / 7 / 9 ) includes five first dipole magnets and four wires α i (α 2 / 4 / 6 / 8 ) has a total of 41 first dipole magnets (331 1~41 ) contained four first dipole magnets. Nine wires β j (β 1~9 ) were equally spaced, with the adjacent lines separated by a distance of 2.5 mm. As shown in FIG. 3B, the first dipole magnet (331 1~41 ) were aligned on grid intersections, some of which did not include a first dipole magnet.

[0220]

[0219] 41 first dipole magnets (331 1~41 The first dipole magnet (331) was cylindrical with the following dimensions: 2 mm (A4, diameter) x 2 mm (A5, length) and was made of NdFeB N45. 1~41 ) are all magnetized in the length (A5) direction, as shown by the S→N arrows in FIG. 3B, and are aligned along a straight line α i The first magnetic field generator (330) had a magnetic axis oriented parallel to (α1 to α9). The first magnetic field generator (330) had a vector sum H1 substantially parallel to the substrate (320) surface.

[0221]

[0220] The first square support matrix (332) of the first magnetic field generator (330) has the following dimensions: 50 mm x 50 mm x 3 mm, is made of polyoxymethylene (POM) and contains 41 first dipole magnets (331). 1~41 ) for holding the 41 first dipole magnets (331 1~41 ) so that the 41 first dipole magnets (331 1~41 The top surface of the first square support matrix (332) was flush with the top surface of the first square support matrix (332). The second dipole magnet (341) of the second magnetic field generator (340) was a square dipole magnet with the following dimensions: 30 mm (B4) x 30 mm (B5) x 2 mm (B3) and was made of NdFeB N52. The second dipole magnet (341) had a north-south magnetic axis substantially parallel to the substrate (320) surface. The second magnetic field generator (340) had a vector sum H2 (corresponding to the magnetic axis of the second dipole magnet (341)) substantially parallel to the substrate (320).

[0222]

[0221] The second square support matrix (342) of the second magnetic field generating device (340) had the following dimensions: 50 mm x 50 mm x 2 mm, was made of polyoxymethylene (POM) and included a recess / hole for holding the second dipole magnet (341), said recess / hole having the same shape and dimensions as the second dipole magnet (341) (i.e. 30 mm (B4) x 30 mm (B5) x 2 mm (B3)), such that the top and bottom surfaces of the second dipole magnet (341) were flush with the top and bottom surfaces of the second square support matrix (342).

[0223]

[0222] The top surface of the first square support matrix (332) of the first magnetic field generating device (330) (41 first dipole magnets (331 1~41The distance (h1) between the upper surface of the second dipole magnet (341) of the second magnetic field generator (340) and the surface of the substrate (320) facing the magnetic assembly (300) was 1.5 mm. The distance (h2) between the upper surface of the second dipole magnet (341) of the second magnetic field generator (340) and the lowermost surface of the square support matrix (332) of the first magnetic field generator (330) was 0 mm, i.e. the first (330) and second (340) magnetic field generators were in direct contact.

[0224] (hardening unit) The following units were used in the preparation of the optical effect layers: LED curing unit (x50): Phoseon (FireLine type, 125 x 20 mm, 395 nm, 8 W / cm) with an exposure time of approximately 0.5 seconds 2 ) UV-LED lamp Hg curing unit (x60): 2 lamps: iron-doped mercury lamp 200 W / cm2 from IST Metz GmbH + mercury lamp 200 W / cm 2 ; 2 passes at 100m / min

[0225] After the curing step, each sample was rubbed with tissue paper to check for curing of both the coating layer (x10) and the indicia (x30). As can be seen from the photographs shown in Figure 4, in the comparative examples where curing was incomplete or insufficient, at least a portion of one or both layers was removed.

[0226] (Photos of Examples and Comparative Examples (FIGS. 4A to 4D))

[0225] Photographs of the optical effect layers prepared as described above are provided in Figures 4A-D.

[0227] As shown by the photograph disclosed in FIG. 4A, a) one or more iodonium salts as disclosed in the first embodiment described herein, in particular one or more salts selected from the group consisting of bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0), bis(4-dodecylphenyl)iodonium hexafluoroantimonate (CAS Nr 71786-70-4) and mixtures thereof in a screen printing composition, and b) one or more thioxanthone compounds as disclosed in the first embodiment described herein, in particular 1-chloro-4-propoxy-9H-thioxanthen-9-one (CAS Nr 142770-42-1), 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 142770-42-2), 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 142770-42-3), 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 142770-42-4), 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 142770-42-5), 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 142770-42-6), 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 142770-42-7), 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 142770-42-8), 2-isopropyl-9H-thioxanthen-9-one (CAS Nr 142770-42-9 ... 5495-84-1;4-(1-methylethyl)-9H-thioxanthen-9-one (CAS Nr 83846-86-0), their oligomers and polymers (CAS Nr 2055335-46-9), 1,3-di[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxy]-2,2-bis[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxymethylpropane (CAS Nr The use of a combination of one or more compounds selected from the group consisting of 1003567-83-6, and mixtures thereof in the claimed process described herein made it possible to produce an optical effect layer that exhibits indicia as well as dynamic movement of the rolling bar when the substrate is tilted due to magnetization orientation in a magnetic field generating device (B1) of particles, bright highly reflective areas.

[0228]

[0227] As shown by the photograph disclosed in Figure 4A, the use of a) one or more iodonium salts disclosed in the second embodiment described herein and b) one or more anthracene compounds disclosed in the second embodiment, in particular 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4) in a combination in the claimed process described herein in a top coating inkjet printing composition made it possible to produce an optical effect layer that shows indicia as well as dynamic movement of the rolling bar when tilting the substrate due to magnetization orientation in a magnetic field generating device (B1) of particles, bright highly reflective areas.

[0229]

[0228] As shown by the photograph disclosed in Figure 4A, the use of a) one or more iodonium salts disclosed in the third embodiment described herein and b) one or more coumarin compounds disclosed in the third embodiment, in particular 3-(4-dodecylbenzoyl)-5,7-dimethoxy-2H-1-benzopyran-2-one (CAS Nr 2170153-43) in combination in the claimed process described herein in a top coating inkjet printing composition made it possible to produce an optical effect layer that shows indicia as well as dynamic movement of the rolling bar when tilting the substrate due to magnetization orientation in a magnetic field generating device (B1) of particles, bright highly reflective areas.

[0230]

[0229] As shown by the photograph disclosed in Figure 4A, the use of a) one or more iodonium salts disclosed in the fourth embodiment described herein and b) naphthalene and anthracene compounds disclosed in the fourth embodiment, in particular 9,10-diethoxy-naphthalene (CAS Nr 27294-37-7) and 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4) in a top coating inkjet printing composition in the claimed process described herein made it possible to produce an optical effect layer that shows indicia as well as particles, dynamic movement of the rolling bar when tilting the substrate due to magnetization orientation in a magnetic field generating device (B1) with bright highly reflective areas.

[0231]

[0230] As shown by the photographs disclosed in Figure 4A, OELs obtained by the combination of the claimed process and the first embodiment described herein are designated E1-E4, E8, and E9; OELs obtained by the combination of the claimed process and the second embodiment described herein are designated E5; OELs obtained by the combination of the claimed process and the third embodiment described herein are designated E6; and OELs obtained by the combination of the claimed process and the fourth embodiment described herein are designated E7.

[0232]

[0231] As shown by the photograph disclosed in Figure 4A, the use in the claimed process described herein of a) one or more sulfonium salts disclosed in the fifth embodiment described herein, in particular one or more salts selected from the group consisting of 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) and bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) in the screen printing composition, and b) one or more anthracene compounds disclosed in the fifth embodiment, in particular 9,10-dibutoxy-anthracene (CAS Nr 76275-14-4) in the top coating inkjet printing composition, made it possible to produce an optical effect layer that shows particles, bright highly reflective areas as well as indications of dynamic movement of the rolling bar when tilting the substrate due to magnetization orientation in the magnetic field generating device (B1).

[0233] As shown by the photograph disclosed in FIG. 4A, a) one or more sulfonium salts as disclosed in the sixth embodiment described herein, in particular 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) and bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) in a screen printing composition, b) one or more iodonium salts as disclosed in the sixth embodiment described herein, in particular bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) in a top coating inkjet printing composition, and c) one or more thioxanthone compounds as disclosed in the sixth embodiment, in particular 1-chloro-4-propoxy-9H-thioxanthen-9-one (CAS Nr The use of a combination of a magnetic field generating device (142770-42-1) in the claimed process described herein made it possible to create an optical effect layer that exhibits indicia as well as dynamic movement of the rolling bar when the substrate is tilted due to magnetization orientation in a magnetic field generating device of particles, bright highly reflective areas.

[0234]

[0233] As shown by the photograph disclosed in Figure 4A, the use in the claimed process described herein of a combination of a) one or more sulfonium salts disclosed in the seventh embodiment described herein, in particular 4-(phenylthio)phenyl diphenyl sulfonium hexafluoroantimonate (CAS Nr 71449-78-0) and bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) in the screen printing composition, b) naphthalene compounds disclosed in the seventh embodiment described herein, in particular 9,10-diethoxy-naphthalene in the top coating inkjet printing composition, and c) anthracene compounds, in particular 9,10-dibutoxy-anthracene in the top coating inkjet printing composition, made it possible to produce an optical effect layer that shows indicia as well as particles, dynamic movement of the rolling bar when tilting the substrate due to magnetization orientation in a magnetic field generating device in a bright highly reflective area.

[0235]

[0234] As shown in Figure 4A, the OEL obtained by the combination of the claimed process and the fifth embodiment described herein is designated E10; the OEL obtained by the combination of the claimed process and the sixth embodiment described herein is designated E11; and the OEL obtained by the combination of the claimed process and the seventh embodiment described herein is designated E12.

[0236] As shown by the photograph disclosed in FIG. 4D, a) one or more sulfonium salts as disclosed in the eighth embodiment described herein, in particular one or more salts selected from the group consisting of 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) and bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) in a screen printing composition, and b) one or more coumarin compounds as disclosed in the eighth embodiment described herein, in particular 3-(4-C10-C13-benzoyl)-5,7-dimethoxy-2H-1-benzopyran-2-one (CAS Nr The use of the claimed process described herein in combination with one or more iodonium salts disclosed in the eighth embodiment described herein, in particular bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) in a top-coating inkjet printing composition, made it possible to produce an optical effect layer that exhibits particles, bright highly reflective areas, dynamic movement of the rolling bar when tilting the substrate due to magnetization orientation in a magnetic field generator (B1), as well as indicia. As shown in FIG. 4D, the OEL obtained by the combination of the claimed process and the eighth embodiment described herein is designated E30.

[0237]

[0236] As shown by the photograph disclosed in Fig. 4D, a) one or more iodonium salts as disclosed in the ninth embodiment described herein, in particular bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0), or one or more sulfonium salts as disclosed in the ninth embodiment described herein, in particular 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) and bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) in a screen printing composition, b) one or more iodonium salts as disclosed in the ninth embodiment described herein, in particular [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium hexafluoroantimonate (CAS Nr 60565-88-0) in a top coating inkjet printing composition, The use of the combination of the claimed process described herein with the magnetic field generator (Nr 2091854-13-4) made it possible to produce an optical effect layer that showed indicia as well as dynamic movement of the rolling bar when tilting the substrate due to magnetization orientation in a magnetic field generator of particles, bright highly reflective areas. As shown by the photographs disclosed in Figure 4D, OELs obtained by the combination of the claimed process and the ninth embodiment described herein are shown as OELs obtained by the combination of the claimed process and the ninth embodiment described herein, and are shown as E31 and E32.

[0238] As shown by the photograph disclosed in FIG. 4D, a) one or more iodonium salts as disclosed in the tenth embodiment described herein, in particular bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0), or one or more sulfonium salts as disclosed in the tenth embodiment described herein, in particular 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) and bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) in a screen printing composition, and b) one or more pyrylium salts as disclosed in the tenth embodiment described herein, in particular 2,4,6-triphenylpyrylium tetrafluoroborate (CAS Nr The use of the combination of the 10th embodiment (European Patent Publication No. 448-61-3) in the claimed process described herein made it possible to produce an optical effect layer that exhibits particles, bright highly reflective areas as well as dynamic movement of the rolling bar when tilting the substrate due to magnetization orientation in a magnetic field generator. As shown by the photograph disclosed in Figure 4D, the OELs obtained by the combination of the claimed process and the tenth embodiment described herein are designated E33 and E34.

[0239] As shown by the photograph disclosed in FIG. 4D, a) one or more iodonium salts as disclosed in the eleventh embodiment described herein, in particular bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0), or one or more sulfonium salts as disclosed in the eleventh embodiment described herein, in particular 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) and bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) in the screen printing composition, b) one or more sulfonium salts as disclosed in the eleventh embodiment described herein, in particular tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium hexafluorophosphate (CAS Nr The use of the combination of the 11th embodiment of the claimed process described herein with the 953084-13-4 made it possible to produce an optical effect layer that exhibits particles, bright highly reflective areas, as well as the dynamic movement of the rolling bar when tilting the substrate due to magnetization orientation in a magnetic field generator. As shown by the photograph disclosed in Figure 4D, the OELs obtained by the combination process of the 11th embodiment of the claimed and described herein are designated E35 and E36.

[0240]

[0239] Contrary to the examples according to the invention, comparative examples (C1-C20) made by the same process as the claimed process, except that the compounds in the screen printing composition and the compounds in the top coating inkjet printing composition did not consist of the embodiments described herein, could not show any indicia of dynamic movement of the rolling bar when the substrate was tilted due to the magnetization orientation in the magnetic field generator (B1) of particles, bright highly reflective areas. Comparative examples C1-C8 and C20 showed dynamic movement of the rolling bar when the substrate was tilted due to the magnetization orientation in the magnetic field generator of particles, but could not show any indicia due to the absence of a specific compound or compounds absorbing in the range of about 350 nm to about 470 nm in the top curable coating composition, or due to the combination of compounds in the screen printing composition and the top coating inkjet printing composition that did not consist of the embodiments described herein. Comparative Examples C10, C12, C14, and C17 could not show the dynamic movement of the rolling bar when tilting the substrate because there is no specific magnetization orientation pattern of the particles (random orientation of the particles), and could not show the indicia because the entire surface of the coating layer (x10) and the indicia (x30) are cured in the LED curing unit in step c), which does not prevent any reorientation thereafter. Comparative Examples C11, C13, C15, C16, and C18 could not show the screen printing composition because the screen printing composition is cured insufficiently. C9 and C19 could not show the screen printing composition and the top coating inkjet printing composition because the screen printing composition and the top coating inkjet printing composition are cured insufficiently.

[0241]

[0240] Contrary to the examples according to the present invention, comparative example C21, which was produced by the same process as the claimed process except that the compounds in the screen printing composition and the compounds in the top coating inkjet printing composition did not consist of the embodiments described herein, was able to show dynamic movement of the rolling bar when tilted, but failed to show any indications because the compounds in the screen printing composition and the compounds in the top coating inkjet printing composition did not consist of the embodiments described herein.

[0242]

[0241] Contrary to the examples according to the present invention, comparative examples C22 and C23, which were prepared by the same process as the claimed process except that the top coating inkjet printing composition was free of the compounds described herein, were able to show dynamic movement of the rolling bar when tilted, but were unable to show any indications.

[0243]

[0242] Contrary to the examples according to the present invention, comparative examples C24 and C25, which were prepared by the same process as the claimed process except that the top coating inkjet printing composition was free of the compounds described herein, failed to show dynamic movement of the rolling bar when tilted and failed to show any sign.

[0244] As shown by the photograph disclosed in FIG. 4A, a) one or more iodonium salts as disclosed in the eleventh embodiment described herein, in particular bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) in the screen printing composition, and b) one or more sulfonium salts as disclosed in the eleventh embodiment described herein, in particular tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium hexafluorophosphate (CAS Nr 953084-13-4); 10-[1,1′-biphenyl]-4-yl-2-(1-methylethyl)-9-oxo-9H-thioxanthenium hexafluorophosphate (CAS Nr 102626-1) in the top coating inkjet printing composition. The use of a combination of one or more compounds selected from the group consisting of 5,591,773-92-1; and mixtures thereof in the claimed process described herein made it possible to produce an optical effect layer that exhibits dynamic movement of the rolling bar as well as indicia when the substrate is tilted due to magnetization orientation in a magnetic field generating device (B1) of particles, bright highly reflective areas (see E13 in FIG. 4A).

[0245] As shown by the photograph disclosed in FIG. 4A, a) one or more sulfonium salts disclosed in the eleventh embodiment described herein, in particular one or more salts selected from the group consisting of 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate (CAS Nr 71449-78-0) and bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate (CAS Nr 89452-37-9) in a screen printing composition, and b) one or more sulfonium salts disclosed in the eleventh embodiment described herein, in particular tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium hexafluorophosphate (CAS Nr 953084-13-4); 10-[1,1'-biphenyl]-4-yl-2-(1-methylethyl)-9-oxo-9H-thioxanthenium hexafluorophosphate (CAS Nr 591773-92-1); and mixtures thereof, the use of the combination of one or more compounds selected from the group consisting of particles, bright highly reflective areas of the magnetic field generator (B1) makes it possible to produce optical effect layers that show dynamic movement of the rolling bar as well as indicia when the substrate is tilted due to magnetization orientation (see E14 in FIG. 4A).

[0246]

[0245] As shown by the photograph disclosed in Figure 4A, the OELs obtained by the combination of the claimed process and the eleventh embodiment described herein are designated E13 and E14.

[0247] As shown by the photographs disclosed in FIG. 4B, a) one or more iodonium salts as disclosed in the first embodiment described herein, in particular bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) in a screen printing composition, and b) one or more thioxanthone compounds as disclosed in the first embodiment described herein, in particular 1-chloro-4-propoxy-9H-thioxanthen-9-one (CAS Nr 60565-88-0) in a top coating inkjet printing composition in different processes according to the present invention. Use of the combination with a 142770-42-1) showed the indicia as well as a rolling bar when the substrate was tilted (see E18 and E23 in FIG. 4B) or a rolling bar when the substrate was tilted (area outside the indicia) and dynamic movement of multiple dark spots and multiple light spots (within the area of ​​the indicia) that moved and / or appeared and / or disappeared (see E15-E17 and E19-E22 in FIG. 4B).

[0248]

[0247] As shown by the photograph disclosed in Figure 4B, the use of a) one or more iodonium salts as disclosed in the second embodiment described herein, in particular bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) in a screen printing composition, in combination with b) one or more anthracene compounds as disclosed in the second embodiment described herein, in particular ANTHRACURE® UVS 1331 (CAS Nr 76275-14-4) in a top coating inkjet printing composition in a different process according to the invention, made it possible to produce an optical effect layer that not only shows a rolling bar (in the area outside the indicia) when the substrate is tilted, and multiple dark spots and multiple light spots (in the area of ​​the indicia) that move and / or appear and / or disappear (see E24 in Figure 4B), but also shows the indicia.

[0249]

[0248] As shown by the photograph disclosed in Figure 4B, the use of a) one or more sulfonium salts as disclosed in the fifth embodiment described herein, in particular SpeedCure 976 (CAS Nr 71449-78-0 and 89452-37-9) in a screen printing composition, in combination with b) one or more anthracene compounds as disclosed in the fifth embodiment described herein, in particular ANTHRACURE® UVS 1331 (CAS Nr 76275-14-4) in a top coating inkjet printing composition in a different process according to the invention, made it possible to produce an optical effect layer that not only shows a rolling bar (in the area outside the indicia) when the substrate is tilted, and multiple dark spots and multiple light spots (in the area of ​​the indicia) that move and / or appear and / or disappear (see E25 in Figure 4B), but also shows the indicia.

[0250] Contrary to the examples according to the invention, comparative example C26, which is a combination of a) one or more iodonium salts as disclosed in the first embodiment described herein, in particular bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) in a screen printing composition, and b) one or more thioxanthone compounds as disclosed in the first embodiment described herein, in particular 1-chloro-4-propoxy-9H-thioxanthen-9-one (CAS Nr 142770-42-1) in a top coating inkjet printing composition, but produced by a process different from the required one, i.e. the coating layer and the indicia are cured by a Hg curing unit after the step of exposing the coating layer to the magnetic field of the second magnetic field generating device, was fixed by the curing of said layer in the Hg curing unit (i.e. no further reorientation of the particles in the third magnetic field generating device occurred) and could not show the indicia. C26 exhibited dynamic movement of dark spots and light spots that moved and / or appeared and / or disappeared upon tilting the substrate without showing any indication.

[0251]

[0250] As shown by the photograph disclosed in Figure 4C, the use of a) one or more iodonium salts as disclosed in the first embodiment described herein, in particular bis(4-methylphenyl)iodonium hexafluorophosphate (CAS Nr 60565-88-0) in a screen printing composition, in combination with b) one or more thioxanthone compounds as disclosed in the first embodiment described herein, in particular 1-chloro-4-propoxy-9H-thioxanthen-9-one (CAS Nr 142770-42-1) in a top-coating inkjet printing composition on different substrates (S1-S4), made it possible to produce optical effect layers that not only show a rolling bar (see E1 and E26 in Figure 4C) when the substrate is tilted, or a number of bright spots that move and / or appear and / or disappear when the substrate is tilted (E27-E29 in Figure 4C), but also show indicia.

Claims

1. A method of making an optical effect layer (OEL), said OEL comprising a motif consisting of at least two areas of a single applied and cured layer comprising non-spherical magnetic or magnetisable pigment particles and exhibiting one or more indicia (x30) on a substrate (x20), The method is: a) applying onto a surface of a substrate (x20) a radiation curable coating composition comprising non-spherical magnetic or magnetisable pigment particles and one or more photoreactive compounds that do not absorb in the range of 350 nm to 470 nm, said radiation curable coating composition being in a first liquid state to form a coating layer (x10); b) after step a), at least partially applying a top-coating composition onto the coating layer (x10), said top-coating composition being applied in the form of one or more indicia (x30), said top-coating composition comprising one or more compounds absorbing in the range of 350 nm to 470 nm; c) partially simultaneously with or after step b), at least partially curing one or more indicia (x30) and one or more areas of the coating layer (x10) below said one or more indicia (x30) with LED curing units (x50) emitting between 350 nm and 470 nm; d) after step c), exposing the coating layer (x10) to a magnetic field of a magnetic field generating device in order to orient at least a portion of the non-spherical magnetic or magnetizable pigment particles; e) partially simultaneously with or after step d), at least partially curing the coating layer (x10) with curing units (x60) emitting at least between 250 nm and 320 nm, The radiation curable coating composition and the topcoating composition are cationically curable compositions; A method in which the one or more photoreactive compounds that do not absorb in the range of 350 nm to 470 nm of the radiation curable coating composition of step a) and the one or more compounds that absorb in the range of 350 nm to 470 nm of the top curable coating composition of step b) are selected according to one of the following combinations: i) one or more compounds of the radiation curable coating composition of step a) is an iodonium salt and one or more compounds of the top curable coating composition of step b) is a thioxanthone compound; ii) one or more compounds of the radiation curable coating composition of step a) is an iodonium salt and one or more compounds of the top curable coating composition of step b) is an anthracene compound; iii) one or more compounds of the radiation curable coating composition of step a) is an iodonium salt and one or more compounds of the top curable coating composition of step b) is a coumarin compound; iv) the one or more compounds of the radiation curable coating composition of step a) are iodonium salts and the one or more compounds of the top curable coating composition of step b) are naphthalene compounds, and the top curable coating composition of step b) further comprises one or more anthracene compounds; v) The one or more compounds of the radiation curable coating composition of step a) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being selected from the group consisting of 4-(phenylthio)phenyldiphenyl-sulfonium; bis[4-(diphenylsulfonium)phenyl]sulfide; (4-methylphenyl)diphenyl-sulfonium; (3-methylphenyl)diphenyl-sulfonium; bis(4-methylphenyl)phenyl-sulfonium; [(4-(1,1-dimethylethyl)phenyl]diphenyl-sulfonium; bis[4-(1-methyl [(4-(2-methylpropyl)phenyl]diphenyl-sulfonium; (4-methoxyphenyl)diphenyl-sulfonium; 1-naphthalenyldiphenyl-sulfonium; tris(4-methylphenyl)-sulfonium; (4-bromophenyl)diphenyl-sulfonium; (4-iodophenyl)diphenyl-sulfonium; (4-fluorophenyl)diphenyl-sulfonium; (4-chlorophenyl)diphenyl-sulfonium; (4-phenoxyphenyl)diphenyl-sulfonium; (4'-methylphenyl)diphenyl-sulfonium; 4-methylphenyl)diphenyl-sulfonium; tris(4-propylphenyl)-sulfonium; bis(4-butylphenyl)phenyl-sulfonium; tris[4(1-methylethyl)phenyl]-sulfonium; S,S'-1,3-phenylenebis[S,S'-diphenyl]-sulfonium; (4-dodecylphenyl)diphenyl-sulfonium; (4-benzoylphenyl)diphenyl-sulfonium; bis([1,1'-biphenyl]-4-yl)(4-methylphenyl)-sulfonium; tris[4-[1,1-di methylethyl)phenyl]-sulfonium; triphenyl-sulfonium, 5-(4-methylphenyl)-dibenzothiophenium; 10-(4-methylphenyl)-9H-thioxanthenium; diphenyl[4-[[(4-phenylthiophenyl]thio]phenyl]-sulfonium; phenylbis[4-phenylthio)phenyl]-sulfonium; 5-[4-(phenylthio)phenyl]-thianthrenium; 5-[4-(phenylthio)phenyl]-dibenzothiophenium; 10-[4-(diphenylthio)phenyl]-9H-thioxanthenium;5-phenyl-thianthrenium; 10-phenyl-9H-thioxanthenium; 5-(4-methylphenyl)-thianthrenium; 5-[1,1'-biphenyl]-4-yl-thianthrenium; or S,S'-(thiodi-4,1-phenylene)bis[S,S'-bis[4-(2-hydroxyethoxy)]phenyl]-sulfonium; 5-[4-(2-hydroxyethoxy)phenyl]thianthrenium, and the one or more compounds of the top curable coating composition of step b) are anthracene compounds; vi) the one or more compounds of the radiation curable coating composition of step a) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those of v), the one or more compounds of the top curable coating composition of step b) are thioxanthone compounds, and the top curable coating composition of step b) further comprises one or more compounds which are iodonium salts; vii) the one or more compounds of the radiation curable coating composition of step a) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those of v), and the one or more compounds of the top curable coating composition of step b) are naphthalene compounds, the top curable coating composition of step b) further comprising one or more anthracene compounds; viii) the one or more compounds of the radiation curable coating composition of step a) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those of v), the one or more compounds of the top curable coating composition of step b) are coumarin compounds, and the top curable coating composition of step b) further comprises one or more compounds which are iodonium salts; ix) the one or more compounds of the radiation curable coating composition of step a) are selected from the group consisting of iodonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those of v), sulfonium salts, and mixtures thereof, and the one or more compounds of the top curable coating composition of step b) are iodonium salts having a cationic moiety and an anionic moiety, the cationic moiety being [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium or [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium; x) the one or more compounds of the radiation curable coating composition of step a) are iodonium salts having a cationic moiety and an anionic moiety, the cationic moiety being selected from the group consisting of sulfonium salts, any one of those in v), and mixtures thereof; and the one or more compounds of the top curable coating composition of step b) are oxonium salts having a cationic moiety and an anionic moiety, the cationic moiety being 2,4,6-triphenylpyrylium; 2,4,6-tris(4-methylphenyl)-pyrylium; 2,4,6-tris(4-methoxyphenyl)-pyrylium; 2,6-bis(4-fluorophenyl)-4-(4-methoxyphenyl)-pyrylium; 3-methyl-2,4,6-triphenyl-pyrylium; 2,4,6-tris([1,1'-biphenyl]-4-yl)-pyrylium; 4-[4-(dimethylamino)phenyl]-2,6-diphenyl-pyrylium, or 2,4-bis(4-methoxyphenyl)-6-phenyl-pyrylium; xi) the one or more compounds of the radiation curable coating composition of step a) are selected from the group consisting of iodonium salts, sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any one of those in v), and mixtures thereof; and the one or more compounds of the top curable coating composition of step b) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium; 10-[1,1'-biphenyl]-4-yl-2-(1-methylethyl)-9-oxo-9H-thioxanthenium; or (9-oxo-9H-thioxanthen-2-yl)diphenyl-sulfonium.

2. 2. The method of claim 1, wherein the one or more photoreactive compounds that do not absorb in the range of 350 nm to 470 nm of the radiation curable coating composition of step a) and the one or more compounds that absorb in the range of 350 nm to 470 nm of the top curable coating composition of step b) are selected according to one of the following combinations: i') The one or more compounds of the radiation curable coating composition of step a) are iodonium salts having a cationic moiety and an anionic moiety, the cationic moiety being selected from the group consisting of bis(4-dodecylphenyl)iodonium; bis[4-(1,1-dimethylethyl)phenyl]iodonium; (4-isopropylphenyl)(4-methylphenyl)iodonium; bis(4-methylphenyl)iodonium; (4-methylphenyl)[4-(2-methylpropyl)phenyl]iodonium; bis(2,4-dimethylphenyl)]iodonium; bis(3,4-diphenyl)iodonium; methylphenyl)]iodonium;(4-methylphenyl)(2,4,6-trimethylphenyl)iodonium;bis[(4-(2-methylpropyl)phenyl]iodonium;bis(4-butylphenyl)iodonium;bis(2,4,6-trimethylphenyl)iodonium;bis(4-hexylylphenyl)iodonium;bis(4-decylphenyl)iodonium;(4-decylphenyl)(4-undecylphenyl)iodonium;bis(4-undecylphenyl)iodonium;bis(4-tridecylphenyl)iodonium;bis( 4-tetradecylphenyl)iodonium; bis(4-hexadecylphenyl)iodonium; bis(4-heptadecylphenyl)iodonium; bis(4-octadecylphenyl)iodonium; (4-decylphenyl)(4-dodecylphenyl)iodonium; (4-decylphenyl)(4-tridecylphenyl)iodonium; (4-decylphenyl)(4-tetradecylphenyl)iodonium; (4-dodecylphenyl)(4-undecylphenyl)iodonium; (4-dodecylphenyl)(4-tridecylphenyl)iodonium; ( 4-dodecylphenyl)(4-tetradecylphenyl)iodonium; (4-tridecylphenyl)(4-undecylphenyl)iodonium; (4-tetradecylphenyl)(4-undecylphenyl)iodonium; (4-tetradecylphenyl)(4-tridecylphenyl)iodonium; p-(octyloxyphenyl)phenyliodonium; [4-[(2-hydroxytetradecyl)oxy]phenyl]phenyliodonium; phenyl[3-(trifluoromethyl)phenyl]iodonium; bis(4-fluorophenyl)iodonium;(4-nitrophenyl)phenyliodonium; (4-nitrophenyl)(2,4,6-trimethylphenyl)iodonium, and the one or more compounds of the top curable coating composition of step b) are 2-isopropyl-9H-thioxanthen-9-one; 4-(1-methylethyl)-9H-thioxanthen-9-one; 2,4-diethyl-9H-thioxanthen-9-one); 2-chloro-9H-thioxanthen-9-one; 1-chloro-4-propoxy-9H-thioxanthen-9-one; 1,3-di[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxy]-2,2-bis[[α- a thioxanthone compound selected from the group consisting of [1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxymethylpropane; α-[2-[(9-oxo-9H-thioxanthenyl)oxy]acetyl]-ω-[[2-[(9-oxo-9H-thioxanthenyl)oxy]acetyl]oxy]-poly(oxy-1,4-butanediyl; α-[2-[(9-oxo-9H-thioxanthenyl)oxy]acetyl]-ω-[[2-[(9-oxo-9H-thioxanthenyl)oxy]acetyl]oxy]-poly(oxy-1,4-butanediyl; oligomeric and polymeric compounds thereof and mixtures thereof; ii') the one or more compounds of the radiation curable coating composition of step a) is the iodonium salt of i') and the one or more compounds of the top curable coating composition of step b) is an anthracene compound selected from the group consisting of 9,10-diethoxy-anthracene; 9,10-dibutoxy-anthracene, and mixtures thereof; iii') the compound or compounds of the radiation curable coating composition of step a) are the iodonium salts of i') and the compound or compounds of the top curable coating composition of step b) are 3-(4-dodecylbenzoyl)-5,7-dimethoxy-2H-1-benzopyran-2-one, 3-(4-C １０ -C １３ -benzoyl)-5,7-dimethoxy-2H-1-benzopyran-2-one, and mixtures thereof; iv') the one or more compounds of the radiation curable coating composition of step a) is the iodonium salt of i') and the one or more compounds of the top curable coating composition of step b) is a naphthalene compound which is 9,10-diethoxy-naphthalene, the top curable coating composition of step b) further comprising one or more anthracene compounds selected from the group consisting of 9,10-diethoxy-anthracene; 9,10-dibutoxy-anthracene, and mixtures thereof; v') The one or more compounds of the radiation curable coating composition of step a) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being 4-(phenylthio)phenyldiphenyl-sulfonium; bis[4-(diphenylsulfonium)phenyl]sulfide; (4-methylphenyl)diphenyl-sulfonium; (3-methylphenyl)diphenyl-sulfonium; bis(4-methylphenyl)phenyl-sulfonium; [(4-(1,1-dimethylethyl)phenyl]diphenyl-sulfonium; bis[4-(1-methyl [(4-(2-methylpropyl)phenyl]diphenylsulfonium; (4-methoxyphenyl)diphenylsulfonium; 1-naphthalenyldiphenylsulfonium; tris(4-methylphenyl)sulfonium; (4-bromophenyl)diphenylsulfonium; (4-iodophenyl)diphenylsulfonium; (4-fluorophenyl)diphenylsulfonium; (4-chlorophenyl)diphenylsulfonium; (4-phenoxyphenyl)diphenylsulfonium; (4'- methyl[1',1-biphenyl]-4-yl)diphenyl-sulfonium; tris(4-propylphenyl)-sulfonium; bis(4-butylphenyl)phenyl-sulfonium; tris[4(1-methylethyl)phenyl]-sulfonium; S,S'-1,3-phenylenebis[S,S'-diphenyl]-sulfonium; (4-dodecylphenyl)diphenyl-sulfonium; (4-benzoylphenyl)diphenyl-sulfonium; bis([1,1'-biphenyl]-4-yl)(4-methylphenyl)-sulfonium; tris[4-[1,1-di methylethyl)phenyl]-sulfonium; triphenyl-sulfonium; 5-(4-methylphenyl)-dibenzothiophenium; 10-(4-methylphenyl)-9H-thioxanthenium; diphenyl[4-[[(4-phenylthiophenyl]thio]phenyl]-sulfonium; phenylbis[4-phenylthio)phenyl]-sulfonium; 5-[4-(phenylthio)phenyl]-thianthrenium; 5-[4-(phenylthio)phenyl]-dibenzothiophenium; 10-[4-(diphenylthio)phenyl]-9H-thioxanthenium;5-phenyl-thianthrenium; 10-phenyl-9H-thioxanthenium; 5-(4-methylphenyl)-thianthrenium; 5-[1,1'-biphenyl]-4-yl-thianthrenium; or S,S'-(thiodi-4,1-phenylene)bis[S,S'-bis[4-(2-hydroxyethoxy)phenyl]-sulfonium, and the one or more compounds of the top curable coating composition of step b) are an anthracene compound of ii'); vi') the one or more compounds of the radiation curable coating composition of step a) are the sulfonium salts of v'), the one or more compounds of the top curable coating composition of step b) are the thioxanthone compounds of i'), and the top curable coating composition of step b) further comprises one or more compounds which are the iodonium salts of i'); vii') the one or more compounds of the radiation curable coating composition of step a) is a sulfonium salt of v'); The one or more compounds of the top curable coating composition of step b) is a naphthalene compound which is 9,10-diethoxy-naphthalene, and the top curable coating composition of step b) further comprises one or more anthracene compounds selected from the group consisting of 9,10-diethoxy-anthracene, 9,10-dibutoxy-anthracene, and mixtures thereof; viii') the one or more compounds of the radiation curable coating composition of step a) are sulfonium salts of v'), the one or more compounds of the top curable coating composition of step b) are coumarin compounds of iii'), and the top curable coating composition of step b) further comprises one or more compounds which are iodonium salts of i'); ix') the one or more compounds of the radiation curable coating composition of step a) are selected from the group consisting of iodonium salts, sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any of those in v'), and mixtures thereof, and the one or more compounds of the top curable coating composition of step b) are iodonium salts having a cationic moiety and an anionic moiety, the cationic moiety being [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium or [(7-methoxy-4-methyl-2-oxo-2H-1-benzopyran-3-yl)phenyl]iodonium; x') the one or more compounds of the radiation curable coating composition of step a) are selected from the group consisting of iodonium salts, sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any of those in v', and mixtures thereof, and the one or more compounds of the top curable coating composition of step b) are oxonium salts having a cationic moiety and an anionic moiety, the cationic moiety being 2,4,6-triphenylpyrylium; 2,4,6-tris(4-methylphenyl)-pyrylium; 2,4,6-tris(4-methoxyphenyl)-pyrylium; 2,6-bis(4-fluorophenyl)-4-(4-methoxyphenyl)-pyrylium; 3-methyl-2,4,6-triphenyl-pyrylium; 2,4,6-tris([1,1'-biphenyl]-4-yl)-pyrylium; 4-[4-(dimethylamino)phenyl]-2,6-diphenyl-pyrylium (or 2,4-bis(4-methoxyphenyl)-6-phenyl-pyrylium; xi') the one or more compounds of the radiation curable coating composition of step a) are selected from the group consisting of iodonium salts, sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being any of those in v', and mixtures thereof; and the one or more compounds of the top curable coating composition of step b) are sulfonium salts having a cationic moiety and an anionic moiety, the cationic moiety being tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium; 10-[1,1'-biphenyl]-4-yl-2-(1-methylethyl)-9-oxo-9H-thioxanthenium; or (9-oxo-9H-thioxanthen-2-yl)diphenyl-sulfonium.

3. The method according to claim 1 or 2, wherein the one or more photoreactive compounds of the radiation curable coating composition in step a) that do not absorb in the range of 350 nm to 470 nm and the one or more compounds of step b) that absorb in the range of 350 nm to 470 nm are selected according to one of the following combinations: i'') at least one of the compounds of the radiation curable coating composition of step a) is an iodonium salt that is bis(4-methylphenyl)iodonium hexafluorophosphate or bis(4-dodecylphenyl)iodonium hexafluoroantimonate; and at least one of the compounds of the top curable coating composition of step b) is 1-chloro-4-propoxy-9H-thioxanthen-9-one, 2-isopropyl-9H-thioxanthen-9-one, 3-isopropyl-9H-thioxanthen-9-one, 4-isopropyl-9H-thioxanthen-9-one, 5-isopropyl-9H-thioxanthen-9-one, 6-isopropyl-9H-thioxanthen-9-one, 7-isopropyl-9H-thioxanthen-9-one, 8-isopropyl-9H-thioxanthen-9-one, 9-isopropyl-9H-thioxanthen-9-one, 10-isopropyl-9H-thioxanthen-9-one, 11-isopropyl-9H-thioxanthen-9-one, 12-isopropyl-9H-thioxanthen-9-one, 13-isopropyl-9H-thioxanthen-9-one, 14-isopropyl-9H-thioxanthen-9-one, 15-isopropyl-9H-thioxanthen-9-one, 16-isopropyl-9H-thioxanthen-9-one, 17-isopropyl-9H-thioxanthen-9-one, 18-isopropyl-9H-thioxanthen-9-one, 19-isopropyl-9H-thioxanthen-9-one, 20-isopropyl-9H-thioxanthen-9-one, 21-isopropyl-9H-thioxanthen-9-one, 22-isopropyl-9H-thioxanthen-9-one, 23-isopropyl-9H-thioxant thioxanthone compounds which are thioxanthone oligomers or polymers, or 1,3-di[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxy]-2,2-bis[[α-[1-chloro-9-oxo-9H-thioxanthen-4-yl)oxy]acetylpoly[oxy(1-methylethylene)]]oxymethylpropane; ii″) at least one of the one or more compounds of the radiation curable coating composition of step a) is an iodonium salt that is bis(4-methylphenyl)iodonium hexafluorophosphate and at least one of the one or more compounds of the top curable coating composition of step b) is an anthracene compound that is 9,10-dibutoxy-anthracene; iii'') at least one of the one or more compounds of the radiation curable coating composition of step a) is an iodonium salt that is bis(4-methylphenyl)iodonium hexafluorophosphate and at least one of the one or more compounds of the top curable coating composition of step b) is a coumarin compound that is 3-(4-dodecylbenzoyl)-5,7-dimethoxy-2H-1-benzopyran-2-one; iv″) at least one of the one or more compounds of the radiation curable coating composition of step a) is an iodonium salt which is bis(4-methylphenyl)iodonium hexafluorophosphate, at least one of the one or more compounds of the top curable coating composition of step b) is an anthracene compound which is 9,10-dibutoxy-anthracene, and at least one other is a naphthalene compound which is 9,10-diethoxy-naphthalene; v″) at least one of the one or more compounds of the radiation curable coating composition of step a) is a sulfonium salt which is 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate and at least one of the one or more compounds of the top curable coating composition of step b) is an anthracene compound which is 9,10-dibutoxy-anthracene; vi″) at least one of the one or more compounds of the radiation curable coating composition of step a) is a sulfonium salt which is 4-(phenylthio)phenyl diphenyl sulfonium hexafluoroantimonate or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate, at least one of the one or more compounds of the top curable coating composition of step b) is a thioxanthone compound which is 1-chloro-4-propoxy-9H-thioxanthen-9-one, and at least another is an iodonium salt which is bis(4-methylphenyl)iodonium hexafluorophosphate; vii″) at least one of the one or more compounds of the radiation curable coating composition of step a) is a sulfonium salt which is 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate, and at least one of the one or more compounds of the top curable coating composition of step b) is an anthracene compound which is 9,10-dibutoxy-anthracene and at least another is a naphthalene compound which is 9,10-diethoxy-naphthalene; xi'') at least one of the one or more compounds of the radiation curable coating composition of step a) is an iodonium salt which is bis(4-methylphenyl)iodonium hexafluorophosphate, or a sulfonium salt which is 4-(phenylthio)phenyldiphenylsulfonium hexafluoroantimonate or bis[4-(diphenylsulfonium)phenyl]sulfide bishexafluoroantimonate, and at least one of the one or more compounds of the top curable coating composition of step b) is a sulfonium salt having a cationic moiety and an anionic moiety, the cationic moiety being tris[4-(4-acetylphenylsulfanyl)phenyl]-sulfonium.

4. 4. The method according to claim 1, further comprising the step of exposing the coating layer (x10) to a magnetic field of a magnetic field generating device in order to orient at least a portion of the magnetic or magnetisable pigment particles, said step being carried out after or partially simultaneously with step b) and before step c).

5. 5. The method according to claim 1, further comprising the step of exposing the coating layer (x10) to a magnetic field of a magnetic field generating device in order to orient at least a portion of the magnetic or magnetisable pigment particles, said step being carried out after step a) and before step b).

6. The method according to any one of claims 1 to 5, wherein the step d) of exposing the coating layer (x10) and / or the step of exposing the coating layer (x10) to a magnetic field of a magnetic field generating device of claim 4 or 5 is performed in order to uniaxially orient at least a part of the non-spherical magnetic or magnetisable pigment particles.

7. The method according to any one of claims 1 to 5, wherein the step d) of exposing the coating layer (x10) and / or the step of exposing the coating layer (x10) to the magnetic field of a magnetic field generating device of claim 4 or 5 is carried out in order to orient at least a part of the non-spherical magnetic or magnetisable pigment particles in a biaxial direction, the non-spherical magnetic or magnetisable pigment particles being platelet-shaped magnetic or magnetisable pigment particles, with an X-axis and a Y-axis defining the main planes of extension of the particles.

8. 8. The method according to claim 7, wherein said step d) of exposing said coating layer (x10) is carried out in order to biaxially orient at least a portion of said platelet-shaped magnetic or magnetisable pigment particles with both their X-axis and Y-axis substantially parallel to the substrate surface.

9. The method according to any one of claims 1 to 5, wherein the step of exposing the coating layer (x10) to the magnetic field of a magnetic field generating device of step d) and / or of claim 4 or 5 comprises two steps: a first step of exposing the coating layer (x10) to the magnetic field of a magnetic field generating device in order to orient at least a portion of the platelet-shaped magnetic or magnetizable pigment particles in a biaxial direction, and a second step of exposing the coating layer (x10) to the magnetic field of a second magnetic field generating device in order to orient at least a portion of the platelet-shaped magnetic or magnetizable pigment particles in a uniaxial direction, said second step being carried out partially simultaneously, simultaneously or after the first step.

10. 10. The method according to any one of claims 1 to 9, wherein the step a) of applying the radiation curable coating composition is carried out by a process selected from the group consisting of screen printing, gravure printing, pad printing, and flexographic printing.

11. The method according to any one of claims 1 to 10, wherein the step b) of applying the top-coating composition is carried out by a non-contact fluid micro-dispensing technique.

12. Method according to any one of the preceding claims, wherein at least a part of said non-spherical magnetic or magnetisable pigment particles is constituted by non-spherical optically variable magnetic or magnetisable pigment particles.

13. 13. The method of claim 12, wherein said non-spherical optically variable magnetic or magnetisable pigment particles are selected from the group consisting of magnetic thin film interference pigments, magnetic cholesteric liquid crystal pigments, and mixtures thereof.

14. 14. The method according to any one of claims 1 to 13, wherein the one or more indicia are selected from the group consisting of codes, symbols, alphanumeric symbols, motifs, geometric patterns, letters, words, numbers, logos, figures, portraits, and combinations thereof.