Stabilizer combination to prevent degradation of synthetic polymers

Abstract

The present invention relates to a composition comprising component (i) a synthetic polymer; and component (ii) a ternary stabilizer combination comprising a sterically hindered phenolic compound, such as a benzofuranone, a bisphenol stabilizer, and an aliphatic phosphorous acid (III) compound. A process for preparing said composition, the use of the stabilizer combination as component (ii) for stabilizing a synthetic polymer component (i) against degradation, and the use of the stabilizer combination (ii) for stabilizing a synthetic polymer (i) are also described. Further specific additive mixtures comprising these components and, for example, amine-based and / or phenolic and / or chromanol-based antioxidants as further components are also described.

Description

[Technical field]

[0001] The present invention relates to a composition comprising as component (i) a polyether polyol or polyurethane (PU) and as component (ii) a stabilizer combination based on (ii.1) a benzofuranone derivative, such as a 3-phenylbenzofuran-2-one derivative, (ii.2) a sterically hindered phenol, such as a bisphenol stabilizer, and (ii.3) an aliphatic phosphorous acid (III) compound, such as a phosphite or phosphonate. The composition is suitable for preventing oxidative, thermal or light-induced degradation of synthetic polymers. The present invention also relates to a process for preparing said composition, to the use of the particular stabilizer combination (ii) for stabilizing component (i). [Background technology]

[0002] Polyurethane foams are commonly used as materials in applications such as home furnishings, automotive interiors, or architecture. These are applications where a long-lasting operating time of the material used is desirable. This may be contrasted with packaging applications in the case of one-off packaging to protect the packaged goods from mechanical impacts. Like many organic materials, polyurethanes themselves, and especially polyurethane foams, are susceptible to degradation caused by exposure to energy or chemically reactive species. On the one hand, there is already an initial exothermic reaction of the starting polyols and di- or polyisocyanates that form the polyurethane foam itself, and on the other hand, there is prolonged exposure to heat and / or light during its operating time. The initial exothermic reaction of the starting materials for polyurethane foam is carried out under conditions in which the blowing agent produces blowing gas. If water is used as the blowing agent, the reaction with the isocyanates to release carbon dioxide is further exothermic. Polyether polyols are often used as polyol starting materials for polyurethane foams when a polyurethane foam with a soft foam consistency is desired. Polyether polyols are organic materials that are themselves already susceptible to degradation caused by exposure to energy or chemically reactive species. If polyether polyol is used as a starting material for polyurethane foam in an already damaged state, this will not be beneficial to the resistance of the formed polyurethane foam to future exposure to energy or chemically reactive species.

[0003] Anti-scorch performance of polyether polyols and additives used in PU foams is necessary to ensure the stability of the polyols during storage and transportation. In addition, and even more importantly, anti-scorch systems are used to prevent degradation of the PU foams during the exothermic foam manufacturing process, which causes discoloration and loss of mechanical properties. This degradation is well known in the industry and is referred to as "scorch". In extreme cases, uncontrolled exothermic reactions during the foaming process can even cause fires. For this reason, protection against scorch and degradation during the foaming process is of utmost importance.

[0004] Over the years, additional undesirable properties, considered secondary properties, such as discoloration upon exposure to gas fading, as well as light-induced discoloration, have also gained importance.

[0005] As the automotive industry sets increasingly strict standards (e.g., VDA 278 10 / 2011, which describes the measurement procedures for volatile organic compounds (VOCs) and semi-volatile organic compounds (SVOCs or FOGs) in car trim materials, and related standards that ensure the performance of the equipment and allow semi-quantification), attention to emissions from PU foams used in automobiles becomes more important to control and reduce emissions from volatile and semi-volatile organic compounds in interior applications. In Asia, countries such as China, Japan, and Korea have raised the emission standards for automotive interiors, especially by monitoring the emission of aldehydes and aromatic compounds (see, for example, China's automotive standard GB 27630).

[0006] Liquid anti-scorch additives are generally preferred in the industry because they are easy to incorporate into the liquid raw materials used to make polyurethane foam. Summary of the Invention [Problem to be solved by the invention]

[0007] The liquid sterically hindered phenols, aromatic amines, and phosphites typically used in industry often contribute to emissions. Furthermore, a negative effect on the color change during storage of PU foams is observed when aromatic amines are used. [Means for solving the problem]

[0008] The object of the present invention is to describe novel scorch inhibitor compositions, preferably liquid, based on benzofuranones, sterically hindered phenols, and aliphatic phosphorous (III) compounds, which provide scorch protection, low emissions in compliance with stringent automotive emission standards, and reduced aldehyde emissions from polyols and PU foams. Another advantageous feature is the low discoloration of PU foams on storage when using the novel stabilizer compositions according to the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0009] The present invention relates to a composition comprising as component (i) a synthetic polymer selected from polyurethane foams or polyether polyols and as component (ii) a ternary stabilizer combination comprising as component (ii.1) at least a substituted benzofuranone derivative, preferably a 3-phenylbenzofuran-2-one derivative, as component (ii.2) at least one sterically hindered phenol, preferably a bisphenol based stabilizer, as component (ii.3) and at least an aliphatic phosphite (III) compound, preferably an aliphatic phosphite (di)ester compound, as component (ii.4).

[0010] The individual components described above and compositions comprising them are described to protect synthetic polymers from undergoing oxidative, thermal or light-induced degradation.

[0011] For example, the preparation and use of benzofuranone derivatives as stabilizers for polymers has been reported in several publications.

[0012] EP 1291384 discloses the application of benzofuranones substituted with acetoxy-substituted phenyls as depicted below as stabilizers for polyurethane foams based on polyether polyols. The discoloration of the stabilized foams was found to be superior to that of comparative benzofuranones substituted with phenyls substituted with only two C1 alkyl groups as depicted below: [ka]

[0013] More specifically, examples based on the combination of octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid with the solid aromatic phosphorous acid derivative tris(2,4-di-tert-butylphenyl)phosphite, as well as the combination of sterically hindered phenols / aromatic amines / benzofuranones with the liquid aromatic isodecyldiphenyl phosphite (DPDP) have also been reported. DPDP is known in the polyurethane industry, but its use is considered undesirable due to the emission of free phenol and unfavourable regulatory classification.

[0014] WO 2006 / 065829 describes a novel class of compounds and compositions and methods of synthesis related to lactone antioxidant 3-benzofuranones that prevent yellowing of polymers such as polyurethane foams. It discloses the application of alkoxy-substituted phenyl-substituted benzofuranones, the main components of which are depicted below, as stabilizers for polyurethane foams based on polyether polyols. This was found to be superior or comparable to a comparative benzofuranone substituted with a phenyl group substituted with two C1 alkyl groups, as depicted below. Furthermore, both benzofuranones were applied as stabilizers for polyether polyols, and similar performance was described for both. [ka]

[0015] Reported examples include one polymeric lactone in combination with a sterically hindered phenol, an aromatic amine, and a UV absorber, however, the combination with a phosphite ester is not specifically mentioned.

[0016] WO 2015 / 121445 discloses benzofuranone phosphite derivatives as stabilizers for organic materials susceptible to oxidative, thermal or light-induced degradation. The benzofuranone phosphite described is mainly applied to the stabilization of polyethylene or polypropylene. In particular, two specific mono-benzofuranone phosphite derivatives are employed, as depicted below: [ka]

[0017] The examples show benzofuranone phosphite derivatives in combination with octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid and the aromatic phosphite derivative, tris(2,4-di-tert-butylphenyl) phosphite.

[0018] WO 2017 / 025431 discloses benzofuranone phosphate derivatives as stabilizers for organic materials susceptible to oxidative, thermal or light-induced degradation. The examples show the stabilization of polyethylene and polypropylene with a specific benzofuranone phosphate derivative. The specific benzofuranone phosphate is also shown to be more resistant to exposure to moisture than the corresponding specific benzofuranone phosphite. Other benzofuranone phosphates are also disclosed and are depicted below. [ka]

[0019] EP 2500341 describes antioxidant compounds synthesized or derived from benzofuranone and benzoic acid compounds, which exhibit heat resistance and can be used as additives in polymers to enhance melt flow and color stability.

[0020] However, there are no examples showing their use in polyols or polyurethanes.

[0021] WO 2020 / 002130 describes phosphorus-containing 3-phenylbenzofuran-2-one derivatives as stabilizers in polyols and polyurethanes. Some examples of stabilizer combinations containing benzofuranones are included. As possible further additives, phosphites and phosphonites are mentioned, while aromatic phosphites are particularly preferred, some of which are used in solid form in the examples.

[0022] EP 0871066 describes a colour photographic silver halide material containing a benzofuranone derivative in one layer to enhance storage stability.

[0023] The so-called sterically hindered phenols have been known in the industry for a long time. These are, for example, phenols with exactly one phenolic hydroxyl group attached to an aromatic ring, particularly preferably those with substituents, preferably alkyl groups, around it in the ortho position, most preferably in the ortho and para positions relative to the phenolic hydroxyl group, in particular alkyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate, respectively, substituted alkyl derivatives of such compounds. Their effect is based on steric hindrance, which is the result of steric effects. Steric hindrance is the slowing down of chemical reactions due to steric bulk, and usually appears in intermolecular reactions, while considerations of steric effects often focus on intramolecular interactions. These are usually understood by those skilled in the art as compounds that block radicals. Steric hindrance is often utilized to control selectivity, such as slowing down undesired side reactions. For example, sterically hindered phenols are used industrially as antioxidants in hydrocarbon-based products ranging from petrochemicals to plastics.

[0024] WO 17125291 describes stabilizer combinations based on high molecular weight bisphenol stabilizers such as liquid sterically hindered phenols.

[0025] One preferred sterically hindered phenol is the compound as depicted below. [ka]

[0026] The stabilizer combinations given in WO 17125291 further contain phosphites of aromatic origin, but the stabilizer combinations according to the invention are not described.

[0027] Organic compounds of trivalent phosphorous acid, such as phosphites or phosphonates, are often used as hydroperoxide decomposers through oxidation to their phosphoric acid derivatives. Phosphites have long been known in the industry as antioxidants, and some patents describe their use as secondary stabilizers, but in most cases they are aromatic in origin and solid. For example, the use of phosphites in combination with sterically hindered phenols is described.

[0028] WO 2019 / 057539 describes the use of liquid dioctyl phosphonates of aliphatic origin, reporting their use in polyisocyanate compositions.

[0029] However, its use in polyols or polyurethane foams has not been reported.

[0030] Despite the range of stabilizer concepts already available, further technological concepts are still needed for improved stabilization of polyurethane foams or polyether polyols against the harmful effects of heat, light, and / or oxidation. Preferably, the technological concepts allow for simplified handling during application. Furthermore, in view of the increasing need for sustainable solutions with a good profile under environmental, health, and safety standards, scorch prevention systems that lead to reduced emissions are desirable.

[0031] It is an object of the present invention to provide improved stabilization against the deleterious effects of heat, light, and / or oxidation.

[0032] In particular, good resistance to oxidation by oxygen is desired, and in particular good resistance to scorching, a deterioration observed in materials in the form of foams.

[0033] This object is achieved according to the present invention by Component (i) a synthetic polymer selected from a polyurethane foam or a polyether polyol; Component (ii) at least A substituted benzofuranone compound as component (ii.1), a sterically hindered phenol as component (ii.2), and Aliphatic phosphorous(III) compounds as component (ii.3) and a ternary stabilizer combination comprising This is accomplished by a composition comprising:

[0034] Preferably, the composition according to the invention comprises: a synthetic polymer selected from polyurethane foam or polyether polyol as component (i); Component (ii) at least 3-phenylbenzofuran-2-one derivatives as substituted benzofuranone compounds as component (ii.1), a bisphenol-based stabilizer as component (ii.2) as a sterically hindered phenol, and Aliphatic phosphites or phosphonates as phosphorous(III) compounds as component (ii.3) and a ternary stabilizer combination comprising The present invention relates to a method for producing a semiconductor device comprising the steps of:

[0035] Individual components of the composition of the present invention Synthetic polymer according to the present invention (i) Both polyurethanes and polyether polyols are susceptible to oxidative, thermal or light induced degradation. The compounds of formula I are incorporated into polyurethane foams or polyether polyols for stabilization of the polyurethane foams or polyether polyols.

[0036] Polyurethanes are obtained from the reaction of polyisocyanate and polyol reactants in a reaction mixture. In the production of polyurethane foams, gas evolution occurs during the reaction. Gas evolution during the reaction can be caused by adding water or carboxylic acids to the reaction mixture prior to the reaction to generate chemical gases, or by adding a blowing agent to the reaction mixture prior to the reaction.

[0037] When water is added, the water molecules react with the isocyanate groups, carbon dioxide is eliminated, and the primary amines formed react with further isocyanate groups to form urea groups. R a -N=C=O+H2O+R b -N=C=O->R a -NH-C(=O)-NH-R b +CO2

[0038] When a carboxylic acid is added, it reacts with the isocyanate group, eliminating carbon dioxide and forming an amide group. R a -N=C=O+HO(O=)CR c ->R a -NH-C(=O)-R c +CO2

[0039] As used herein, a blowing agent means an organic compound having a boiling point at 101.32 kPa between -15°C and the maximum temperature occurring during the reaction of the reaction mixture, preferably between -15°C and 110°C, more preferably between -10°C and 80°C, and very preferably between -5°C and 70°C. Furthermore, the blowing agent does not react under reaction conditions to form chemical bonds with the polyisocyanate reactant or the polyol reactant in the reaction mixture. Examples of blowing agents are alkanes having 4 to 10 carbon atoms, preferably 5 to 8 carbon atoms, cycloalkanes having 5 to 10 carbon atoms, acetone, methyl formate, carbon dioxide (added in liquid form), or partially or fully halogenated alkanes having 1 to 5 carbon atoms, preferably 1 to 3 carbon atoms.

[0040] Alkanes having 4 to 10 carbon atoms are, for example, butane, pentane, hexane, or heptane. Cycloalkanes having 5 to 10 carbon atoms are, for example, cyclopentane or cyclohexane. Partially or completely halogenated alkanes are, for example, methylene chloride, 1,1,1-trichloroethane, CFC-11, CFC-113, CFC-114, CFC-123, CFC-123a, CFC-124, CFC-133, CFC-134, CFC-134a, CFC-141b, CFC-142, CFC-151. From the partially or completely halogenated alkanes having 1 to 5 carbon atoms, those partially halogenated ones, i.e. those having at least one hydrogen atom, such as, for example, methylene chloride, CFC-123, CFC-141b, CFC-124, or 1,1,1-trichloroethane, are preferred.

[0041] When water is used for gas generation, it is preferred to add water to the reaction mixture prior to the reaction in an amount of 0.5 to 12 parts by weight based on 100 parts by weight of polyol reactant. More preferably, 1 to 8 parts of water are added. Most preferably, 2 to 7 parts of water are added, such as, for example, 3 to 7 parts or 4 to 7 parts of water. In particular, 16 to 32 kg / m 3 For polyurethane foams with densities between 3 and 8 parts of water are added.3 Exceeds 48kg / m 3 For polyurethane foams having a density less than 2 to 5 parts water are added.

[0042] When a blowing agent is used for gas generation, the blowing agent is preferably added to the reaction mixture in an amount of 2 to 50 parts by weight based on 100 parts by weight of polyol reactant. More preferably, 3 to 45 parts of blowing agent are added. Highly preferably, 4 to 30 parts of blowing agent are added, such as, for example, 5 to 25 parts of blowing agent.

[0043] The use of water or carboxylic acid, or the use of blowing agent, provides the desired reduction in polyurethane density. When water or carboxylic acid, especially water, is used, the reaction heat increases. When water is used, the amount of urea bond in polyurethane foam increases, hardening the foam. In contrast, when blowing agent is used, the temperature inside the reaction mixture is moderated, softening the foam. Nevertheless, the use of water is attractive, but increases the requirement for stabilization of polyurethane foam that occurs during reaction.

[0044] Polyurethane foams are, for example, normal polyurethane foams or self-skinning polyurethane foams (structural foams). A normal polyurethane foam has the same chemical composition and the same density over the cross section of a structure made from normal polyurethane foam. Of course, this is not the case if a small scale is chosen where the number of voids in the cells and the number of cell walls become too small. A self-skinning polyurethane foam (structural foam) possesses the same chemical composition, but the density over the cross section of a structure made from self-skinning foam increases from the porous core of the structure towards the peripheral zone of the structure. The peripheral zone is almost dense. A normal polyurethane foam is, for example, obtained by reaction of a reaction mixture in an infinite reaction vessel, i.e. the reaction vessel is open in at least one direction in the sense that if the volume of the reaction vessel is significantly increased, the emerging foam does not expand significantly further. A self-skinning polyurethane foam is, for example, obtained by reaction of a reaction mixture in a finite reaction vessel, i.e. the emerging foam fills the entire volume of the finite reaction vessel, and if the volume of the finite reaction vessel is increased, the emerging foam expands significantly further. Additionally, temperature gradients exist during the reaction due to, for example, the cold surfaces and uncooled core of the finite reaction vessel.The use of blowing agents in self-skinning polyurethane foams results in the formation of a substantially non-cellular skin on the surface of the outer perimeter zone of the structure.

[0045] It is preferred to add water or a carboxylic acid to the reaction mixture prior to the reaction, and more preferred to add water to the reaction mixture prior to the reaction. For conventional polyurethane foams, it is highly preferred to add water or a carboxylic acid to the reaction mixture prior to the reaction. For conventional polyurethane foams, it is most preferred to add water to the reaction mixture prior to the reaction.

[0046] The polyurethane foam has a lower density than polyurethanes obtained from the same reaction mixture but without the inclusion of water or carboxylic acid or blowing agent. The polyurethane foam preferably has a density of 5 to 500 kg / m at 20°C and 101.3 kPa. 3, more preferably 10 to 300 kg / m 3 , very preferably 15 to 100 kg / m 3 , and most preferably 16 to 48 kg / m 3 If the polyurethane foam is a self-skinning foam (structural foam), the density is determined as the average density of the entire foam structure. In many cases, the density of self-skinning polyurethane foam is 10 times higher than that of regular polyurethane foam.

[0047] Preferably, the polyurethane foam has a compressibility of 5 to 500 kg / m at 20° C. and 101.3 kPa. 3 It is a composition having a density between

[0048] The polyurethane foam is preferably thermoset.

[0049] The polyurethane foam is preferably a semi-rigid cellular material or a flexible (or soft) cellular plastic. More preferably, the polyurethane foam is a flexible (or soft) cellular plastic. The deformation resistance of the polyurethane foam is measured, for example, according to the standard DIN 53421, and a compressive stress of 15 kPa or less at 10% compression indicates a flexible cellular plastic. The polyurethane foam is very preferably a flexible (or soft) cellular plastic with a compressive stress of 15 kPa or less at 10% compression according to DIN 53421.

[0050] Polyurethane foam is preferably a thermosetting, flexible cellular plastic.

[0051] The surfactant is preferably added to the reaction mixture prior to the reaction. The surfactant supports the production of stable bubbles from the reaction mixture during the reaction, i.e., bubbles that do not collapse until the reaction has progressed sufficiently to the curing stage to maintain a foamable structure, or that do not contain a large amount of large pores. The surfactant may be, for example, a siloxane derivative, such as a siloxane / poly(alkylene oxide), or a fatty acid salt. Preferably, the surfactant is a siloxane derivative. Since excess surfactant tends to cause the reaction mixture to collapse before gelling, the surfactant is preferably added in an amount of 0.05 to 5 parts by weight, more preferably 0.15 to 4 parts by weight, very preferably 0.3 to 3 parts by weight, and most preferably 0.8 to 2 parts by weight, based on 100 parts by weight of polyol reactant.

[0052] A catalyst for the reaction of the polyisocyanate reactant with the polyol reactant is preferably added to the reaction mixture. The catalyst is, for example, an amine catalyst or an organometallic catalyst. The amine catalyst is, for example, triethylenediamine or a derivative based thereon, such as N-methylmorpholine, N-ethylmorpholine, diethylethanolamine, N-coconumorpholine, 1-methyl-4-dimethylaminoethylpiperazine, 3-methoxy-N-dimethylpropylamine, N,N-diethyl-3-diethyl-aminopropylamine, dimethylbenzylamine, bis-(2-dimethylaminoethyl)ether or dimethylbenzylamine. Preference is given to triethylenediamine or a derivative based thereon. The organometallic catalyst is, for example, an organic salt of tin, bismuth, iron, mercury, zinc or lead. Preference is given to organotin compounds. Examples of organotin compounds are dimethyltin dilaurate, dibutyltin dilaurate or stannous octoate. Preference is given to stannous octoate. Preferably, the amount of amine catalyst is from 0.01 to 5 parts by weight, more preferably from 0.03 to 2 parts by weight, based on 100 parts by weight of polyol reactant. Preferably, the amount of organometallic catalyst is from 0.001 to 3 parts by weight, based on 100 parts by weight of polyol reactant. Preferably, an amine catalyst and an organometallic catalyst are added to the reaction mixture.

[0053] The polyisocyanate reactant is an aromatic or aliphatic polyisocyanate. Aromatic polyisocyanates are, for example, 2,4- and / or 2,6-toluene diisocyanate (TDI), 2,4'-diphenylmethane diisocyanate, 1,3- and 1,4-phenylene diisocyanate, 4,4'-diphenylmethane diisocyanate (MDI), 2,4'-diphenylmethane diisocyanate (often contained in 4,4'-diphenylmethane diisocyanate as a minor isomer), 1,5-naphthylene diisocyanate, triphenylmethane-4,4',4'' triisocyanate or polyphenylpolymethylene polyisocyanates, such as polyisocyanates prepared by aniline-formaldehyde condensation followed by phosgenation ("crude MDI"). Mixtures of aromatic polyisocyanates are also included. Aliphatic polyisocyanates are, for example, ethylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 1,12-dodecane diisocyanate, cyclobutene-1,3-diisocyanate, cyclohexane-1,3- and 1,4-diisocyanate, 1,5-diisocyanato-3,3,5-trimethylcyclohexane, 2,4- and / or 2,6-hexahydrotoluene diisocyanate, perhydro-2,4'- and / or 4,4'-diphenylmethane diisocyanate (H 12MDI) or isophorone diisocyanate. Mixtures of aliphatic polyisocyanates are also included. In addition, derivatives and polymers of the aforementioned aromatic or aliphatic polyisocyanates are included, for example those containing urethane, carbodiimide, allophanate, isocyanurate, acylated urea, biuret or ester groups ("modified polyisocyanates"). Examples of aromatic polyisocyanurates are the so-called "liquid MDI" products, which contain carbodiimide groups. It is also possible to use isocyanate group-containing distillation residues of aromatic or aliphatic polyisocyanates, obtained in the course of the industrial preparation of isocyanates, as such or dissolved in one or more of the abovementioned polyisocyanates. Preferred polyisocyanate reactants are the aromatic polyisocyanates TDI, MDI or derivatives of MDI, and the aliphatic polyisocyanates, isophorone diisocyanate, H 12 MDI, hexamethylene diisocyanate or cyclohexane diisocyanate. Highly preferred are aromatic polyisocyanates. Most preferred are polyisocyanates that are TDI, MDI or derivatives of MDI. Particularly preferred are polyisocyanates that are TDI, especially mixtures of 2,4-toluene diisocyanate and 2,6-toluene diisocyanate.

[0054] The polyisocyanate reactant is preferably used in an amount that gives an isocyanate index of 90-130, more preferably 95-115, most preferably 100-113, and especially preferably 105-112. In this specification, isocyanate index is used to mean 100 times the ratio of isocyanate groups used to the theoretical equivalents required to react with the active hydrogen equivalents in the reaction mixture, for example in the polyol reactant, in water, carboxylic acid, crosslinker, chain extender if present, and in other components having functional groups that are active hydrogen-containing groups and therefore reactive towards isocyanate groups. An index of 100 indicates a 1:1 stoichiometric ratio, and an index of 107 indicates, for example, a 7% excess of isocyanate equivalents. Isocyanate equivalent is the total number of isocyanate groups. Active hydrogen equivalent means the total number of active hydrogens. An active hydrogen-containing group that is a hydroxyl group or a secondary amine group contributes one active hydrogen equivalent. Active hydrogen-containing groups that are primary amine groups also contribute one active hydrogen equivalent because after reaction with an isocyanate group, the original second hydrogen is no longer an active hydrogen. Active hydrogen-containing groups that are carboxylic acids contribute one active hydrogen equivalent per carboxylic acid functional group.

[0055] The polyol reactant is a polyether polyol or a polyester polyol.

[0056] Polyether polyols are, for example, polymers obtained by polymerization of alkylene oxides or cyclic ethers having at least four ring atoms, which contain at least two active hydrogen-containing groups per molecule, and the at least two active hydrogen-containing groups per molecule are hydroxyl groups. The active hydrogen-containing groups are, for example, primary hydroxyl groups, secondary hydroxyl groups, primary amines or secondary amines. The intended function of the active hydrogen-containing groups is to react with isocyanates to form covalent bonds. Preferably, the polyether polyols contain 2 to 8, very preferably 2 to 6, most preferably 2 to 4, and particularly preferably 2 to 3 active hydrogen-containing groups per molecule. Polyether polyols having 3 active hydrogen-containing groups per molecule are also called trifunctional polyether polyols. The alkylene oxides are, for example, ethylene oxide, propylene oxide, 1,2-butylene oxide, 2,3-butylene oxide or styrene oxide. The cyclic ethers are, for example, oxetane or tetrahydrofuran.

[0057] Polyether polyols are prepared, for example, by polymerizing alkylene oxides alone or in mixtures or in succession with an initiator component containing at least two reactive hydrogen atoms. The initiator component containing at least two reactive hydrogen atoms is, for example, water, a polyhydric alcohol, ammonia; a primary amine or a secondary amine containing a second reactive hydrogen atom. The polyhydric alcohol is, for example, ethylene glycol, propane-1,2-diol, propane-1,3-diol, glycerin, trimethylolpropane, 4,4'-dihydroxydiphenylpropane or alpha-methyl glucoside. The primary amine is, for example, ethanol-amine, ethylenediamine, diethylenetriamine or aniline. The secondary amine containing a second reactive hydrogen atom is, for example, diethanolamine, triethanolamine or N-(2-hydroxyethyl)piperazine. The initiator component containing at least two reactive hydrogen atoms is preferably water or a polyhydric alcohol. The initiator component containing at least two reactive hydrogen atoms preferably contains 2 to 6, more preferably 2 to 4, and most preferably 2 to 3 reactive hydrogen atoms. The average number of reactive hydrogen atoms in the initiator component used to prepare the polyether polyol defines the "nominal functionality" of the polyether polyol, i.e., the average number of active hydrogen-containing groups of the polyether polyol. The nominal functionality of the polyether polyol is preferably 2 to 6, more preferably 2 to 4, most preferably 2 to 3.5, and particularly preferably 2 to 3.3.

[0058] The polyether polyol has a molecular weight of, for example, 400 to 10,000 daltons, preferably 800 to 10,000 daltons. The molecular weight is more preferably the number average molecular weight (M n The equivalent weight of a polyether polyol is defined herein as its molecular weight divided by the average number of active hydrogen-containing groups per molecule, and preferably the number average molecular weight (M n ) is used. In particular, the number average molecular weight (M nThe equivalent weight of the polyether polyol determined by the above formula (1) is preferably 400 to 5,000, more preferably 800 to 2,500, very preferably 900 to 1,300, and particularly preferably 1,000 to 1,200.

[0059] Preferred are polyether polyols that contain predominantly (up to 90% by weight, based on total hydroxyl groups present in the polyether polyol) active hydrogen-containing groups that are secondary hydroxyl groups.

[0060] Polyester polyols are produced, for example, by polycondensation of diacids and diols, where the diols are applied in excess. Partial replacement of the diols with polyols having two or more hydroxyl groups results in branched polyester polyols. Diacids are, for example, adipic acid, glutaric acid, succinic acid, maleic acid or phthalic acid. Diols are, for example, ethylene glycol, diethylene glycol, 1,4-butanediol, 1,5-pentanediol, neopentyl glycol or 1,6-hexanediol. Polyols having more than two hydroxyl groups are, for example, glycerin, trimethylolpropane or pentaerythritol.

[0061] Crosslinkers are, for example, further components of the reaction mixture. Crosslinkers may improve the elasticity of polyurethane foams. Crosslinkers as defined herein have three to eight, preferably three to four, active hydrogen-containing groups per molecule. Thus, crosslinkers react with the polyisocyanate reactant and, if present, are considered as reactants for the calculation of the polyisocyanate index. Crosslinkers do not contain ester bonds and are particularly important for the calculation of the number average molecular weight (M n ) is less than 200. When a crosslinker is present, the polyether polyols are particularly nThe equivalent of the polyether polyol determined by the above method is preferably 400 to 5000. The crosslinking agent is, for example, an alkylene triol or an alkanolamine. The alkylene triol is, for example, glycerin or trimethylolpropane. The alkanolamine is, for example, diethanolamine, triisopropanolamine, triethanolamine, diisopropanolamine, an adduct of 4 to 8 moles of ethylene oxide and ethylenediamine, or an adduct of 4 to 8 moles of propylene oxide and ethylenediamine. The crosslinking agent is preferably an alkanolamine, more preferably diethanolamine.

[0062] Chain extenders are, for example, further components of the reaction mixture. Chain extenders as defined herein have two active hydrogen-containing groups, i.e., hydroxyl groups, per molecule. Thus, the chain extender reacts with the polyisocyanate reactant and, if present, is considered as a reactant for the calculation of the polyisocyanate index. Chain extenders do not contain ester bonds and, in particular, have a number average molecular weight (M n ) is 31 to 300, preferably 31 to 150. When a chain extender is present, the polyether polyol is preferably, in particular, n The equivalent weight determined by the above method is 400 to 5000. The chain extender is, for example, an alkylene glycol or a glycol ether. The alkylene glycol is, for example, ethylene glycol, 1,3-propylene glycol, 1,4-butylene glycol, or 1,6-hexamethylene glycol. The glycol ether is, for example, diethylene glycol, triethylene glycol, dipropylene glycol, tripropylene glycol, or 1,4-cyclohexanedimethanol.

[0063] If used, the combined amount of crosslinker and chain extender in the reaction mixture is less than 50 parts by weight based on 100 parts by weight of polyol reactant. The combined amount is preferably less than 20 parts by weight, and more preferably less than 5 parts by weight.

[0064] The reaction mixture prior to reaction comprises a polyisocyanate reactant and a polyol reactant, and 60 to 100 parts by weight of the polyol reactant, based on 100 parts by weight of the polyol reactant, is preferably a polyether polyol, more preferably 80 to 100 parts by weight, very preferably 95 to 100 parts by weight, and most preferably 98 to 100 parts by weight of the polyol reactant is a polyether polyol, and especially preferably the polyol reactant is a polyether polyol.

[0065] The polyurethane foam is obtained from the reaction of the reaction mixture. The above selectivity may be expressed in another way, i.e., the polyurethane foam is preferably obtained from the reaction of a polyisocyanate reactant with a polyol in the reaction mixture, the polyol reactant being 60 to 100 parts by weight, based on 100 parts by weight of the polyol reactant being a polyether polyol.

[0066] Preferred are compositions in which the polyurethane foam results from the reaction of a polyisocyanate reactant and a polyol reactant in a reaction mixture.

[0067] Preferred are compositions in which polyurethane foams result from the reaction of a polyisocyanate reactant and a polyol reactant in a reaction mixture, where the reaction mixture comprises the polyisocyanate reactant, the polyol reactant, and optionally water, a carboxylic acid or blowing agent, and optionally a surfactant, and optionally a catalyst, and optionally a crosslinker, and optionally a chain extender.

[0068] Preferred is a composition in which the polyurethane foam is obtained from the reaction of a polyisocyanate reactant with a polyol reactant in a reaction mixture, the polyol reactant being 60 to 100 parts by weight based on 100 parts by weight of the polyol reactant being a polyether polyol.

[0069] Preferred are compositions in which the polyurethane foam results from the reaction of a polyisocyanate reactant with a polyol reactant in a reaction mixture, the reaction mixture containing water, a carboxylic acid, or a blowing agent prior to the reaction.

[0070] Preferred is a composition in which component (i) is a polyurethane foam.

[0071] Preferred are compositions in which component (i) is a polyether polyol.

[0072] The content of stabilizer combination (ii) in the composition is defined for polyurethane foam, as component (i), based on the polyol reactant in the reaction mixture which subsequently reacts with the polyisocyanate reactant to form the polyurethane foam.

[0073] The content of the stabilizer combination (ii) in the composition is defined for the polyether polyol as component (i) based on the polyether polyol.

[0074] In either case, the amount of stabilizer combination (ii) is preferably from 0.01 to 10 parts by weight, based on 100 parts by weight of polyol reactant in the case of polyurethane foams, and based on 100 parts by weight of polyether polyol in the case of polyether polyols. More preferably, the amount is from 0.02 to 5 parts by weight, very preferably from 0.025 to 2.5 parts by weight, and most preferably from 0.03 to 2 parts by weight.

[0075] The aim of the present invention is to obtain a stabilizer combination and an improved stabilizing composition for such synthetic polymers compared to those known in the prior art.

[0076] Surprisingly, it is preferably liquid, preferably ● Component (ii.1): at least one 3-phenylbenzofuran-2-one derivative; Component (ii.2): at least one bisphenol-based stabilizer, and Component (ii.3): at least one aliphatic phosphite or phosphonate It has been found that the stabilizer combination (ii) as defined above, based on the three components:

[0077] Combinations of stabilizers (ii) according to the invention: (ii.1) Benzofuranone derivatives The benzofuranone derivative according to the present invention preferably has the formula (I): [ka] is a substituted 3-phenyl-benzofuran-2-one derivative, as defined below as During the ceremony, R 1-i is hydrogen, O-alkyl, O-acyl or OP(OR a )(OR b ) and; R 2-i and R 3-i are each independently an optionally substituted alkyl, cycloalkyl, alkenyl, phenyl, OR 4 , COOR 5 or COR 6 and During the ceremony, R 4 , R 5 and R 6 are, independently of each other, optionally further substituted hydrogen, alkyl, cycloalkyl, alkenyl, phenyl; n and m are each an integer selected from 0, 1, 2, 3, or 4; or Two residues R 2-i or R 3-i may each represent a fused carbocyclic or heterocyclic ring, or the compound of formula I may 1-i , R 2-i or R 3-I or R 1-i OP(OR a )(OR b ) and R a and R bmay each optionally be an alkyl substituted aryl linked to each other via a CH2 or CHCH3 group, where the phosphate atom is optionally OP(=O)(OR a )(OR b ) may be further oxidized to

[0078] Preferably R 1-i is O-acyl or OP(OR a )(OR b ) in which R a and R b each optionally has a C1-C8 alkyl substituted phenyl linked to each other via a CH2 or CHCH3 group, wherein the phosphorus atom is optionally OP(=O)(OR a )(OR b ) may be further oxidized to

[0079] Preferably, R 2-i and R 3-i are each independently selected from straight or branched C1-C8 alkyl-.

[0080] Preferably R 2-i and R 3-i are independently selected from methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, and tert-butyl, wherein the alkyl radicals may be further substituted with one or more C1-C4 alkyl radicals.

[0081] Preferably, R 2-i and R 3-i are both the same and are methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, and tert-butyl, where the alkyl radical may be further substituted with one or more C1-C4 alkyl radicals.

[0082] Preferably, n and m are, independently of each other, integers selected from 1 or 2.

[0083] Preferably, in the benzofuranone compound of formula (I), R 1-i OP(OR a )(OR b ) and R a and R b are both phenyl rings substituted with two C(CH3)3 groups, which are linked together via a CHCH3 group, and R 2-i is methyl, R 3-i is C(CH3)3, and m and n are each 2. Optionally, the phosphorus atom is OP(=O)(OR a )(OR b ) may be further oxidized to

[0084] Preferably, in the benzofuranone compound of formula (I), R 1-i is hydrogen or O-acyl, R 2-i is R 3-i and m is identical to n.

[0085] Preferably, in the benzofuranone compound of formula (I), R 1-i is acetoxy and R 2-i and R 3-i are both C(CH3)2CH2C(CH3)3 and m and n are both 1.

[0086] Preferably, in the benzofuranone compound of formula (I), R 1-i is a 2-oxoethyl-6-hydroxyhexanoic acid derivative with three repeating 6-hydroxyhexanoic acid units, R 2-i is hydrogen, and R 3-i is C(CH3)2 and m is 2.

[0087] Preferably, in the benzofuranone compound of formula (I), R 1-i is a p-salicylic acid ester substituted with two C(CH3)3 groups, and R 2-i are both C(CH3)3 and m and n are both 1.

[0088] The benzofuranone compounds of formula I have at least one asymmetric* R holds the carbon atom at the 3-position of the benzofuran-2-one structural unit. 1-i OP(OR a )(OR b ), there is a further asymmetric carbon atom present, (OR a )(OR b ) the linking group is CHCH3.

[0089] (ii.2) Sterically hindered phenolic compounds The sterically hindered phenolic compound according to the present invention is a phenolic stabilizer, preferably represented by the formula (II), [ka] It is a bisphenol-based stabilizer compound made by During the ceremony, R 1-ii are each independently methyl or tert-butyl; n is 1, 2, 3, 4, 5, 6, 7, 8, 9, 10 or 11.

[0090] Preferably, n is 1, 2, 3, 4, 5 or 6 in formula (II) of the bisphenol based stabilizer.

[0091] Particularly preferred are bisphenol-based stabilizers of formula II, where n=1, 2, 3 or 4, in particular n=2, 3 or 4, especially n=2 or 3.

[0092] (ii.3) Aliphatic phosphite(III) compounds The aliphatic phosphorous acid (III) compounds according to the present invention may be present as phosphite compounds or in the form of phosphonates. The phosphites are represented by the formula P(OR c )(OR d )(OR e ) type compounds, wherein R c , R d , R e are the same or different aliphatic radicals, and the phosphonate is R f -PO(OR c )(ORd ) type compounds, wherein R f , R c , and R d are the same or different aliphatic radicals. c ;R d , and R e are each independently an alkyl-substituted C1-C 20 While R may be alky f is hydrogen or alkyl substituted C1-C 20 It may also be alky.

[0093] The phosphite or phosphonate compounds according to the present invention are of aliphatic origin, meaning that they are esters of an aliphatic alcohol having at least one primary hydroxyl group (i.e. HO-CH2-...).

[0094] Preferably, the aliphatic phosphorous acid (III) compound according to the invention is a phosphonic acid diester compound Rf-PO(OR c )(OR d ) in which Rf is hydrogen.

[0095] More preferably, the aliphatic phosphorous acid (III) compound according to the present invention is a phosphonic acid diester compound, Rf-PO(OR c )(OR d ) in which R f is hydrogen, and R c ; and R d Both have the same alkyl substituted C1-C 20 His name is alky.

[0096] Particularly preferred aliphatic phosphorous(III) compounds for use in accordance with the present invention are HP(=O)(OCH 17 )(OC8H 17 ).

[0097] Selection Particular embodiments and selections of the stabilizer combinations according to the invention are outlined in the following paragraphs.

[0098] Component (ii.1), 3-phenylbenzofuran-2-one derivative: The stabilizer component (I.1-1) is depicted below and is available according to Example S-8 of WO 2015 / 121445 A1. [ka]

[0099] The stabilizer component (I.1-2) is depicted below and is available according to Example P-2 of WO 2017 / 025431 A1. [ka]

[0100] The stabilizer component (I.1-3) is depicted below and is available under its compound number I-30 according to EP 0871066 A1. [ka]

[0101] The stabilizer component (I.1-4) is the reaction product of 5,7-di-tert-butyl-3-[4-(2-hydroxyethoxy)phenyl]-3H-benzofuran-2-one and ε-caprolactone, depicted below and available according to Example 3 of WO 2006 / 065829 A1. [ka]

[0102] The stabilizer component (I.1-5) is 4-tert-butyl-2-(5-tert-butyl-2-oxo-2,3-dihydro-1-benzofuran-3-yl)phenyl 3,5-di-tert-butyl-4-hydroxybenzoate, depicted below and commercially available as Revonox 501™. [ka]

[0103] Component (ii.2), bisphenol stabilizer: The stabilizer component (II.2-1) is a transesterification product of 3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid methyl ester and polyethylene glycol 200s, depicted below and available according to Example 1a of WO 2010 / 003813 A1. [ka]

[0104] The stabilizer component (II.2-2) is depicted below and is commercially available as Irganox 245™. [ka]

[0105] Component (ii.3), an aliphatic phosphite(III) compound: Preferred aliphatic phosphite or phosphonate compounds for use for the purposes of the present invention are, for example, bis(2-ethylhexyl) hydrogen phosphite, dimethyl hydrogen phosphite, dioleyl hydrogen phosphite, dibutyl hydrogen phosphite, di-n-octyl hydrogen phosphite, dilauryl hydrogen phosphite, trialkyl (C12-C15) phosphites [CAS number 68610-62-8], tri-C12-C14 phosphorous acid [CAS number 93686-48-7], tris(tridecyl) phosphite, triisodecyl phosphite, triisotridecyl phosphite, tris(dipropylene glycol) phosphite, trioctyl phosphite, tridecyl phosphite, trilauryl phosphite, trilauryl trithiophosphite, trioctadecyl phosphite, triisooctyl phosphite, diisodecyl pentaerythritol diphosphate, heptakis(dipropylene glycol) triphosphite, and (dipropylene glycol) phosphite.

[0106] The aliphatic phosphorous acid (III) compounds preferably used for the present invention are liquid dialkyl hydrogen phosphites and trialkyl phosphites.

[0107] More preferred are liquid dialkyl hydrogen phosphites.

[0108] Examples of such dialkyl hydrogen phosphites are dioleyl hydrogen phosphite and dioctyl hydrogen phosphite.

[0109] Particularly preferred is dioctyl hydrogen phosphite.

[0110] The composition according to the invention may preferably comprise further components as additives.

[0111] These further additives may, for example, be selected from the following list: 1. Antioxidants 1.1. Alkylated monophenols, such as 2,6-di-tert-butyl-4-methylphenol, 2-tert-butyl-4,6-dimethylphenol, 2,6-di-tert-butyl-4-ethylphenol, 2,6-di-tert-butyl-4-n-butylphenol, 2,6-di-tert-butyl-4-isobutylphenol, 2,6-dicyclopentyl-4-methylphenol, 2-(α-methylcyclohexyl)-4,6-dimethylphenol, 2,6-dioctadecyl-4-methylphenol, 2,4,6-tricyclo Hexylphenol, 2,6-di-tert-butyl-4-methoxymethyl-phenol, nonylphenols in which the side chain is linear or branched, such as 2,6-dinonyl-4-methylphenol, 2,4-dimethyl-6-(1'-methylundec-1'-yl)phenol, 2,4-dimethyl-6-(1'-methylheptadec-1'-yl)phenol, 2,4-dimethyl-6-(1'-methyltridec-1'-yl)phenol, 2,4-dimethyl-6-(1'-methyl-1'-tetradecyl-methyl)phenol, and mixtures thereof.

[0112] 1.2. Alkylthiomethylphenols, for example 2,4-dioctylthiomethyl-6-tert-butylphenol, 2,4-dioctylthiomethyl-6-methylphenol, 2,4-dioctylthiomethyl-6-ethylphenol, 2,6-didodecyl-thiomethyl-4-nonyl-phenol.

[0113] 1.3. Hydroquinone and alkylated hydroquinones, such as 2,6-di-tert-butyl-4-methoxyphenol, 2,5-di-tert-butylhydroquinone, 2,5-di-tert-amylhydroquinone, 2,6-diphenyl-4-octadecyl-oxyphenol, 2,6-di-tert-butylhydroquinone, 2,5-di-tert-butyl-4-hydroxyanisole, 3,5-di-tert-butyl-4-hydroxyanisole, 3,5-di-tert-butyl-4-hydroxyphenyl stearate, bis(3,5-di-tert-butyl-4-hydroxyphenyl)adipate.

[0114] 1.4. Tocopherols, for example α-tocopherol, β-tocopherol, γ-tocopherol, δ-tocopherol, and mixtures thereof (vitamin E), vitamin E acetate.

[0115] Particularly preferred are the following: [ka] The addition of 2,5,7,8-tetramethyl-2-[4,8,12-trimethyltridecyl]-chroman-6-ol as depicted in Figure 1, which is a commercially available form of vitamin E (e.g., Irganox E 201™).

[0116] 1.5. Hydroxylated thiodiphenyl ethers, such as 2,2'-thiobis(6-tert-butyl-4-methylphenol), 2,2'-thiobis(4-octylphenol), 4,4'-thiobis(6-tert-butyl-3-methylphenol), 4,4'-thiobis(6-tert-butyl-2-methylphenol), 4,4'-thiobis(3,6-di-sec-amylphenol), 4,4'-bis(2,6-dimethyl-4-hydroxyphenyl) disulfide.

[0117] 1.6. Alkylidene bisphenols, such as 2,2'-methylenebis(6-tert-butyl-4-methylphenol), 2,2'-methylenebis(6-tert-butyl-4-ethylphenol), 2,2'-methylenebis[4-methyl-6-(α-methylcyclohexyl)phenol], 2,2'-methylenebis(4-methyl-6-cyclohexylphenol), 2,2'-methylenebis(6-nonyl-4-methylphenol), 2,2'-methylenebis(4,6-di-tert-butylphenol), 2,2'-ethylidene bis (4,6-di-tert-butylphenol), 2,2'-ethylidenebis(6-tert-butyl-4-isobutylphenol), 2,2'-methylenebis[6-(α-methylbenzyl)-4-nonylphenol], 2,2'-methylenebis[6-(α,α-dimethylbenzyl)-4-nonylphenol], 4,4'-methylenebis(2,6-di-tert-butylphenol), 4,4'-methylenebis-(6-tert-butyl-2-methylphenol), 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl) )butane, 2,6-bis(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol, 1,1,3-tris(5-tert-butyl-4-hydroxy-2-methylphenyl)butane, 1,1-bis(5-tert-butyl-4-hydroxy-2-methylphenyl)-3-n-dodecylmercaptobutane, ethylene glycol bis[3,3-bis(3'-tert-butyl-4'-hydroxyphenyl)butyrate], bis(3-tert-butyl-4-hydroxy-5-methylphenyl)dicyclopentadiene terephthalate, bis[2-(3'-tert-butyl-2'-hydroxy-5'-methylbenzyl)-6-tert-butyl-4-methylphenyl]terephthalate, 1,1-bis-(3,5-dimethyl-2-hydroxyphenyl)butane, 2,2-bis(3,5-di-tert-butyl-4-hydroxyphenyl)propane, 2,2-bis-(5-tert-butyl-4-hydroxy-2-methylphenyl)-4-n-dodecylmercaptobutane, 1,1,5,5-tetra(5-tert-butyl-4-hydroxy-2-methylphenyl)pentane.

[0118] 1.7. O-, N-, and S-benzyl compounds, such as 3,5,3',5'-tetra-tert-butyl-4,4'-dihydroxydibenzyl ether, octadecyl-4-hydroxy-3,5-dimethylbenzyl mercaptoacetic acid, tridecyl-4-hydroxy-3,5-di-tert-butylbenzyl mercaptoacetic acid, tris(3,5-di-tert-butyl-4-hydroxy-benzyl)amine, bis(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)dithioterephthalic acid, bis(3,5-di-tert-butyl-4-hydroxybenzyl)sulfide, isooctyl-3,5-di-tert-butyl-4-hydroxybenzyl mercaptoacetic acid.

[0119] 1.8. Hydroxybenzylated malonic acids, such as dioctadecyl-2,2-bis(3,5-di-tert-butyl-2-hydroxybenzyl)malonic acid, dioctadecyl-2-(3-tert-butyl-4-hydroxy-5-methylbenzyl)malonic acid, didodecylmercaptoethyl-2,2-bis(3,5-di-tert-butyl-4-hydroxybenzyl)malonic acid, bis[4-(1,1,3,3-tetramethylbutyl)phenyl]-2,2-bis(3,5-di-tert-butyl-4-hydroxybenzyl)malonic acid.

[0120] 1.9. Aromatic hydroxybenzyl compounds, such as 1,3,5-tris(3,5-di-tert-butyl-4-hydroxy-benzyl)-2,4,6-trimethylbenzene, 1,4-bis(3,5-di-tert-butyl-4-hydroxybenzyl)-2,3,5,6-tetra-methylbenzene, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)phenol.

[0121] 1.10. Triazine compounds, such as 2,4-bis(octylmercapto)-6-(3,5-di-tert-butyl-4-hydroxy-anilino)-1,3,5-triazine, 2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxy-anilino)-1,3,5-triazine, 2-octylmercapto-4,6-bis(3,5-di-tert-butyl-4-hydroxy-phenoxy)-1,3,5-triazine, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxyphenoxy)-1,2,3-triazine, 1,3 ,5-Tris(3,5-di-tert-butyl-4-hydroxy-benzyl)isocyanurate, 1,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)isocyanurate, 2,4,6-tris(3,5-di-tert-butyl-4-hydroxyphenylethyl)-1,3,5-triazine, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hexahydro-1,3,5-triazine, 1,3,5-tris(3,5-dicyclohexyl-4-hydroxybenzyl)isocyanurate.

[0122] 1.11. Benzylphosphonic acids, for example, dimethyl-2,5-di-tert-butyl-4-hydroxybenzylphosphonic acid, diethyl-3,5-di-tert-butyl-4-hydroxybenzylphosphonic acid, dioctadecyl-3,5-di-tert-butyl-4-hydroxybenzylphosphonic acid, dioctadecyl-5-tert-butyl-4-hydroxy-3-methylbenzylphosphonic acid, calcium salts of 3,5-di-tert-butyl-4-hydroxybenzylphosphonic acid, (3,5-ditertbutyl-4-hydroxyphenyl)methylphosphonic acid.

[0123] 1.12. Acylaminophenols, for example, 4-hydroxylauranilide, 4-hydroxystearanilide, N-(3,5-di-tert-butyl-4-hydroxyphenyl)octyl carbamate.

[0124] 1.13. β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid with, for example, methanol, ethanol, n-octanol, i-octanol, mixtures of linear and branched C7-C9 alkanols, octadecanol, linear and branched C 13 ~C 15 Mixtures of alkanols, esters with mono- or polyhydric alcohols such as 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, tetraethylene glycol, pentaerythritol; tris-(hydroxyethyl)isocyanurate, N,N'-bis-(hydroxy-ethyl)oxamide, 3-thiaundecanol, 3-thiapenta-decanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane.

[0125] Preferred are esters of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid, in particular with octadecanol, such as those of formula (V): [ka] An adduct of octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid as depicted in, which is commercially available (e.g., Irganox 1076™).

[0126] 1.14. Esters of β-(5-tert-butyl-4-hydroxy-3-methylphenyl)propionic acid with monohydric or polyhydric alcohols, such as, for example, methanol, ethanol, n-octanol, i-octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol; tris(hydroxyethylene) (ethyl) isocyanurate, N,N'-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane; 3,9-bis[2-{3-(3-tert-butyl-4-hydroxy-5-methylphenyl)propionyloxy}-1,1-dimethylethyl]-2,4,8,10-tetraoxaspiro[5.5]undecane.

[0127] 1.15. Esters of β-(3,5-dicyclohexyl-4-hydroxyphenyl)propionic acid with mono- or polyhydric alcohols, such as, for example, methanol, ethanol, octanol, octadecanol, 1,6-hexane-diol, 1,9-nonane-diol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol; tris(hydroxyethyl)isocyanurate, N,N'-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxy-methyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane.

[0128] 1.16. Esters of 3,5-di-tert-butyl-4-hydroxyphenylacetic acid with mono- or polyhydric alcohols, such as, for example, methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol; tris(hydroxyethyl)isocyanurate, N,N'-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane.

[0129] 1.17. Amides of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid, such as N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)hexamethylenediamide, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)trimethylenediamide, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenyl-propionyl)hydrazide, N,N'-bis[2-(3-[3,5-di-tert-butyl-4-hydroxyphenyl]-propionyloxy)ethyl]oxamide (Naugard XL-1®, supplied by SI Group).

[0130] 1.18. Ascorbic Acid (Vitamin C)

[0131] 1.19. Amine antioxidants, such as N,N'-diisopropyl-p-phenylenediamine, N,N'-di-sec-butyl-p-phenylenediamine, N,N'-bis(1,4-dimethylpentyl)-p-phenylenediamine, N,N'-bis(1-ethyl-3-methylpentyl)-p-phenylenediamine, N,N'-bis(1-methylheptyl)-p-phenylene-diamine, N,N'-dicyclohexyl-p-phenylenediamine, N,N'-diphenyl-p-phenylenediamine, Diamine, N,N'-bis(2-naphthyl)-p-phenylenediamine, N-isopropyl-N'-phenyl-p-phenylenediamine, N-(1,3-dimethylbutyl)-N'-phenyl-p-phenylenediamine, N-(1-methylheptyl)-N'-phenyl-p-phenylenediamine, N-cyclohexyl-N'-phenyl-p-phenylenediamine, 4-(p-toluenesulfamoyl)diphenylamine, N,N'-dimethyl-N,N'-di-sec-butyl-p- Phenylenediamine, diphenylamine, N-allyldiphenylamine, 4-isopropoxydiphenylamine, N-phenyl-1-naphthylamine, N-(4-tert-octylphenyl)-1-naphthylamine, N-phenyl-2-naphthylamine, octylated diphenylamines such as p,p'-di-tert-octyldiphenylamine, 4-n-butylaminophenol, 4-butyrylaminophenol, 4-nonanoylaminophenol, 4-dodecanoylaminophenol, aminophenol, 4-octadecanoylaminophenol, bis(4-methoxyphenyl)amine, 2,6-di-tert-butyl-4-dimethylaminomethylphenol, 2,4'-diaminodiphenylmethane, 4,4'-diaminodiphenylmethane, N,N,N',N'-tetramethyl-4,4'-diaminodiphenylmethane, 1,2-bis[(2-methylphenyl)amino]ethane, 1,2-bis(phenylamino)propane, (o-tolyl)biguanide, bis[4-(1',3'-Dimethylbutyl)phenylamine, tert-octylated N-phenyl-1-naphthylamine, diaminodiphenylmethane, mixtures of mono- and di-alkylated tert-butyl / tert-octyldiphenylamines, mixtures of mono- and di-alkylated nonyldiphenylamines, mixtures of mono- and di-alkylated dodecyldiphenylamines, mixtures of mono- and di-alkylated isopropyl / isohexyldiphenylamines, mixtures of mono- and di-alkylated tert-butyl-diphenylamines amine mixture, 2,3-dihydro-3,3-dimethyl-4H-1,4-benzothiazine, phenothiazine, mixture of mono- and dialkylated tert-butyl / tert-octyl phenothiazines or mixture of mono- and dialkylated tert-octyl phenothiazines, N-allyl phenothiazine, N,N,N',N'-tetraphenyl-1,4-diamino-but-2-ene, N-[(1,1,3,3-tetramethylbutyl)phenyl]-1-napthalenamine] (commercially available as Irganox L06™).

[0132] 2.UV absorbers and light stabilizers 2.1. 2-(2'-hydroxyphenyl)benzotriazoles, such as 2-(2'-hydroxy-5'-methylphenyl)benzotriazole, 2-(3',5'-di-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(5'-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(2'-hydroxy-5'-(1,1,3,3-tetramethylbutyl)phenyl)benzotriazole, 2-(3',5'-di-tert-butyl-2'-hydroxyphenyl)-5-chlorobenzotriazole, 2- (3'-tert-butyl-2'-hydroxy-5'-methylphenyl)-5-chlorobenzotriazole, 2-(3'-sec-butyl-5'-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(2'-hydroxy-4'-octyloxyphenyl)benzotriazole, 2-(3',5'-di-tert-amyl-2'-hydroxyphenyl)benzotriazole, 2-(3',5'-bis(α,α-dimethylbenzyl)-2'-hydroxyphenyl)benzotriazole, 2-(3'-tert-butyl-2'-hydroxyphenyl)benzotriazole, 2-(3'-tert-butyl-5'-[2-(2-ethylhexyloxy)-carbonylethyl]-2'-hydroxyphenyl)-5-chlorobenzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-methoxycarbonylethyl)phenyl)-5-chlorobenzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-methoxycarbonylethyl)phenyl)-5-chlorobenzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-methoxycarbonylethyl)phenyl)benzotriazole, 2-(3 '-tert-butyl-2'-hydroxy-5'-(2-octyloxycarbonylethyl)phenyl)benzotriazole, 2-(3'-tert-butyl-5'-[2-(2-ethylhexyloxy)carbonylethyl]-2'-hydroxyphenyl)benzotriazole, 2-(3'-dodecyl-2'-hydroxy-5'-methylphenyl)benzotriazole, 2-(3'-tert-butyl-2'-hydroxy-5'-(2-isooctyloxycarbonylethyl)phenylbenzotriazole, 2,2'-methylenebis[4-(1,1,3,3-Tetramethylbutyl)-6-benzotriazol-2-ylphenol];Transesterification product of 2-[3'-tert-butyl-5'-(2-methoxycarbonylethyl)-2'-hydroxyphenyl]-2H-benzotriazole with polyethylene glycol 300;, [ka] (wherein R' = 3'-tert-butyl-4'-hydroxy-5'-2H-benzotriazol-2-ylphenyl; 2-[2'-hydroxy-3'-(α,α-dimethyl-benzyl)-5'-(1,1,3,3-tetra-methylbutyl)phenyl]benzotriazole; 2-[2'-hydroxy-3'-(1,1,3,3-tetramethyl-butyl)-5'-(α,α-dimethylbenzyl)phenyl]benzotriazole).

[0133] 2.2.2-Hydroxybenzophenones, such as the 4-hydroxy, 4-methoxy, 4-octyloxy, 4-decyl-oxy, 4-dodecyloxy, 4-benzyloxy, 4,2',4'-trihydroxy, and 2'-hydroxy-4,4'-dimethoxy derivatives.

[0134] 2.3. Esters of substituted and unsubstituted benzoic acids, such as, for example, 4-tert-butyl-phenyl salicylate, phenyl salicylate, octylphenyl salicylate, dibenzoylresorcinol, bis(4-tert-butylbenzoyl)resorcinol, benzoylresorcinol, 2,4-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzoate, hexadecyl 3,5-di-tert-butyl-4-hydroxybenzoate, octadecyl 3,5-di-tert-butyl-4-hydroxybenzoate, 2-methyl-4,6-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxybenzoate.

[0135] 2.4. Acrylates, such as ethyl α-cyano-β,β-diphenylacrylate, isooctyl α-cyano-β,β-diphenylacrylate, methyl α-carbomethoxycinnamate, methyl α-cyano-β-methyl-p-methoxycinnamate, butyl α-cyano-β-methyl-p-methoxycinnamate, methyl α-carbomethoxy-p-methoxycinnamate, N-(β-carbomethoxy-β-cyanovinyl)-2-methylindoline, and neopentyl tetra(α-cyano-β,β-diphenylacrylic acid).

[0136] 2.5. Nickel compounds, for example nickel complexes of 2,2'-thiobis[4-(1,1,3,3-tetramethylbutyl)phenol], such as the 1:1 or 1:2 complexes, with or without additional ligands, such as n-butylamine, triethanolamine, or N-cyclohexyldiethanolamine; nickel dibutyldithiocarbamate; nickel salts of monoalkyl esters, such as the methyl or ethyl ester of 4-hydroxy-3,5-di-tert-butylbenzyl-phosphonic acid; nickel complexes of ketoximes, such as 2-hydroxy-4-methylphenyl-undecyl-ketoxime; nickel complexes of 1-phenyl-4-lauroyl-5-hydroxypyrazole, with or without additional ligands.

[0137] 2.6. Sterically hindered amines, such as bis(2,2,6,6-tetramethyl-4-piperidyl)sebacic acid, bis(2,2,6,6-tetramethyl-4-piperidyl)succinic acid, bis(1,2,2,6,6-pentamethyl-4-piperidyl)sebacic acid, n-butyl-3,5-di-tert-butyl-4-hydroxybenzylmalonate bis(1,2,2,6,6-pentamethyl-4-piperidyl), condensation product of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine with succinic acid, N,N'-bis(2,2,6,6-tetramethyl-4-piperidyl)sebacic acid, bis(1,2,2,6,6-pentamethyl-4-piperidyl)sebacic acid, Linear or cyclic condensation products of tetramethyl-4-piperidyl)hexamethylenediamine with 4-tert-octylamino-2,6-dichloro-1,3,5-triazine, tris(2,2,6,6-tetramethyl-4-piperidyl)nitrilotriacetic acid, tetrakis(2,2,6,6-tetramethyl-4-piperidyl)-1,2,3,4-butanetetracarboxylic acid, 1,1'-(1,2-ethanediyl)-bis(3,3,5,5-tetramethylpiperazinone), 4-benzoyl-2,2,6,6-tetramethylpiperidine, 4-stearyloxy-2,2,6,6-tetramethylpiperidine, tetramethylpiperidine, bis(1,2,2,6,6-pentamethylpiperidyl)-2-n-butyl-2-(2-hydroxy-3,5-di-tert-butylbenzyl)malonic acid, 3-n-octyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]-decane-2,4-dione, bis(1-octyloxy-2,2,6,6-tetramethylpiperid-4-yl)sebacic acid, bis(1-octyloxy-2,2,6,6-tetramethyl-piperid-4-yl)succinic acid, bis[2,2,6,6-tetramethyl-1-(undecyloxy) piperidin-4-yl] carbonate, linear or cyclic condensation products of N,N'-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine with 4-morpholino-2,6-dichloro-1,3,5-triazine, condensation products of 2-chloro-4,6-bis(4-n-butylamino-2,2,6,6-tetramethylpiperidyl)-1,3,5-triazine with 1,2-bis(3-amino-propyl-amino)ethane, condensation products of 2-chloro-4,6-di-(4-n-butylamino-1,2,2,6,6-pentamethylpiperidyl)-1,3,5-triazine with 1,Condensation product with 2-bis(3-aminopropylamino)ethane 8-acetyl-3-dodecyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]-decane-2,4-dione, 3-dodecyl-1-(2,2,6,6-tetramethyl-4-piperidyl)pyrrolidine-2,5-dione, 3-dodecyl-1-(1,2,2,6,6-pentamethyl-4-piperidyl)pyrrolidine-2,5-dione, mixture of 4-hexadecyloxy- and 4-stearyloxy-2,2,6,6-tetramethylpiperidine, N,N'-bis(2,2,6,6-tetramethylpiperidine), Condensation products of methyl-4-piperidyl)hexamethylenediamine and 4-cyclohexylamino-2,6-dichloro-1,3,5-triazine, 1,2-bis(3-aminopropylamino)ethane and 2,4,6-trichloro-1,3,5-triazine and 4-butylamino-2,2,6,6-tetramethylpiperidine (CAS registration number [136504-96-6]); 1,6-hexanediamine and 2,4,6-trichloro-1,3,5-triazine, and N,N-dibutylamine and 4-butylamino-2,2,6,6-tetramethylpiperidine (CAS) condensation product (CAS registration number [19226864-7]); N6,N6'-hexane-1,6-diylbis[N2,N4-dibutyl-N2,N4,N6-tris(2,2,6,6-tetramethylpiperidin-4-yl)-1,3,5-triazine-2,4,6-triamine] reaction product with butanal and hydrogen peroxide; N-(2,2,6,6-tetramethyl-4-piperidyl)-n-dodecylsuccinimide, N-(1,2,2,6,6-pentamethyl-4-piperidyl)-n-dodecylsuccinimide, 2-undecyl-7,7,9,9-tetramethyl tetramethyl-1-oxa-3,8-diaza-4-oxo-spiro[4,5]decane, 7,7,9,9-tetramethyl-2-cycloundecyl-1-oxa-3,8-diaza-4-oxospiro[4,5]decane and epichlorohydrin, 1,1-bis(1,2,2,6,6-pentamethyl-4-piperidyl-oxycarbonyl)-2-(4-methoxyphenyl)ethene, N,N'-bis-formyl-N,N'-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine, 4-methoxymethylenemalonic acid and 1,2,2,Diesters with 6,6-pentamethyl-4-hydroxy-piperidine, poly[methylpropyl-3-oxy-4-(2,2,6,6-tetramethyl-4-piperidyl)]-siloxane, reaction products of maleic anhydride-α-olefin copolymers with 2,2,6,6-tetramethyl-4-aminopiperidine or 1,2,2,6,6-pentamethyl-4-aminopiperidine, N,N'-bis-(2,2,6,6-tetramethyl-1-propoxy-piperidin-4-yl)hexane-1,6-diamine and 2-chloro-4,6-bis-(di-n-butyl) a mixture of oligomeric compounds which are the formal condensation products of 2,4-dichloro-6-{n-butyl-(2,2,6,6-tetramethyl-1-propoxy-piperidin-4-yl)amino}-[1,3,5]triazine end-capped with N,N'-bis-(2,2,6,6-tetramethyl-piperidin-4-yl)hexane-1,6-diamine and 2-chloro-4,6-bis-(di-n-butylamino)-[1,3,5]triazine end-capped with N,N'-bis-(2,2,6,6-tetramethyl-piperidin-4-yl)hexane-1,6-diamine; A mixture of oligomeric compounds which are formal condensation products with 2,6,6-tetramethyl-piperidin-4-yl)amino}-[1,3,5]triazine, (N2,N4-dibutyl-N2,N4-bis(1,2,2,6,6-pentamethyl-4-piperidinyl)-6-(1-pyrrolidinyl)-[1,3,5]-triazine-2,4-diamine, 2,4-bis[N-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)-N-butylamino]-6-(2-hydroxyethyl)amino-1,3,5-triazine, 1-( 2-Hydroxy-2-methylpropoxy)-4-octadecanoyloxy-2,2,6,6-tetramethylpiperidine, 5-(2-ethylhexanoyl)oxymethyl-3,3,5-trimethyl-2-morpholinone, Sanduvor (Clariant; CAS Registry Number [106917-31-1]), 5-(2-ethylhexanoyl)oxymethyl-3,3,5-trimethyl-2-morpholinone, 2,4-bis-[(1-cyclohexyloxy-2,2,6,6-piperidin-4-ylbutylamino]-6-chloro-s-triazine and N,N'-bis-(3-amino-propyl)ethylenediamine), 1,3,5-tris(N-cyclohexyl-N-(2,2,6,6-tetramethylpiperazin-3-one-4-yl)amino)-s-triazine, 1,3,5-tris(N-cyclohexyl-N-(1,2,2,6,6-pentamethylpiperazin-3-one-4-yl)amino)-s-triazine.

[0138] 2.7. Oxamides, such as 4,4'-dioctyloxyoxanilide, 2,2'-diethoxyoxanilide, 2,2'-dioctyloxy-5,5'-di-tert-butoxanilide, 2,2'-didodecyloxy-5,5'-di-tert-butoxanilide, 2-ethoxy-2'-ethyloxanilide, N,N'-bis(3-dimethylaminopropyl)oxamide, 2-ethoxy-5-tert-butyl-2'-ethoxanilide and its mixture with 2-ethoxy-2'-ethyl-5,4'-di-tert-butoxanilide, mixtures of o- and p-methoxy disubstituted oxanilides, and mixtures of o- and p-ethoxy disubstituted oxanilides.

[0139] 2.8. 2-(2-hydroxyphenyl)-1,3,5-triazines, such as 2,4,6-tris(2-hydroxy-4-octyloxyphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2,4-dihydroxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2,4-bis(2-hydroxy-4-propyloxyphenyl)-6-(2,4-dimethylphenyl)-1,3,5-triazine , 2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(4-methylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-dodecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-tridecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-butyloxypropoxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine, 2 -[2-hydroxy-4-(2-hydroxy-3-octyloxypropyloxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine, 2-[4-(dodecyloxy / tridecyloxy-2-hydroxypropoxy)-2-hydroxyphenyl]-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-[2-hydroxy-4-(2-hydroxy-3-dodecyloxypropoxy)phenyl]-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine, 2-(2-hydroxy-4-hexyl 2-(2-hydroxy-4-methoxyphenyl)-4,6-diphenyl-1,3,5-triazine, 2,4,6-tris[2-hydroxy-4-(3-butoxy-2-hydroxypropoxy)phenyl]-1,3,5-triazine, 2-(2-hydroxyphenyl)-4-(4-methoxyphenyl)-6-phenyl-1,3,5-triazine, 2-{2-hydroxy-4-[3-(2-ethylhexyl-1-oxy)-2-hydroxypropyloxy]phenyl}-4,6-bis(2,4-Dimethylphenyl)-1,3,5-triazine.

[0140] 3. Metal deactivators, such as N,N'-diphenyloxamide, N-salicylal-N'-salicyloylhydrazine, N,N'-bis(salicyloyl)hydrazine, N,N'-bis(3,5-di-tert-butyl-4-hydroxyphenyl-propionyl)hydrazine, 3-salicyloylamino-1,2,4-triazole, bis(benzylidene)oxalyl dihydrazide, oxanilide, isophthaloyl dihydrazide, sebacoyl bisphenylhydrazide, N,N'-diacetyladipoyl dihydrazide, N,N'-bis-(salicyloyl)oxalyl dihydrazide, N,N'-bis(salicyloyl)thiopropionyl dihydrazide.

[0141] 4. Phosphites and phosphonates are necessary additives for the stabilizer combination according to the invention. For example, trisalkyl(C12-C15)phosphites, triisodecyl phosphite, triisotridecyl phosphite, dioleyl hydrogen phosphite, triisooctyl phosphite, heptakis(dipropylene glycol)triphosphite, trilauryltrithiophosphite, tris(dipropylene glycol)phosphite, dimethyl hydrogen phosphite, dibutyl hydrogen phosphite, dilauryl hydrogen phosphite, triC12-C14 phosphite, bis(2-ethylhexyl) hydrogen phosphite have already been mentioned, and particularly preferred are liquid phosphites such as di-n-octyl hydrogen phosphite or diisooctyl hydrogen phosphite.

[0142] However, further phosphites and phosphonates which are different from the defined component (ii.3) but which may additionally be used in the compositions according to the invention are preferably liquid, such as, for example, triphenyl phosphite, tris(nonylphenyl) phosphite, phenyl diisodecyl phosphite, diphenyl isodecyl phosphite, [triphenyl phosphite, polymer of 1,4-cyclohexanedimethanol and polypropylene glycol, C10-16 alkyl ester (CAS Registry Number 1821217-71-3)].

[0143] Further optional phosphorous or phosphonic acid additives which are also mentioned herein are, for example, alkyl (C12-C15) bisphenol A phosphites, alkyl (C10) bisphenol A phosphites, poly(dipropylene glycol) phenyl phosphites, tris(tridecyl) phosphites, diphenyl phosphites, dodecyl nonyl phenol blend phosphites, phenyl neopentylene glycol phosphites, poly 4,4' isopropylidenediphenol-C10 alcohol phosphites, poly 4,4' isopropylidenediphenol-C12-15 alcohol phosphites, diphenyl alkyl phosphites, phenyl dialkyl phosphites, C 12 ~C 18 Alkylbis[4-(1-methyl-1-phenylethyl)phenyl]phosphite, C 12 ~C 18Alkenyl bis[4-(1-methyl-1-phenylethyl)phenyl]phosphite, bis[4-(1-methyl-1-phenyl-ethyl)phenyl][(E)octadec-9-enyl] phosphite, decyl bis[4-(1-methyl-1-phenylethyl)phenyl] phosphite, didecyl phosphite[4-(1-methyl-1-phenyl-ethyl)phenyl], phosphite[4-(1-methyl-1-phenyl-ethyl)phenyl]bis[(E)octadec-9-enyl] ], trilauryl phosphite, trioctadecyl phosphite, distearyl pentaerythritol diphosphite, tris(2,4-di-tert-butylphenyl) phosphite, bis(2,4-di-tert-butylphenyl) pentaerythritol diphosphite, bis(2,4-dicumylphenyl) pentaerythritol diphosphite, bis(2,6-di-tert-butyl-4-methylphenyl) pentaerythritol diphosphite, diisodecyloxy cypentaerythritol diphosphite, bis(2,4-di-tert-butyl-6-methylphenyl)pentaerythritol diphosphite, bis(2,4,6-tris(tert-butylphenyl)pentaerythritol diphosphite, ditridecyl phosphite [2-tert-butyl-4-[1-[5-tert-butyl-4-di(tridecoxy)phosphanyloxy-2-methylphenyl]butyl]-5-methylphenyl]; see, e.g., U.S. Pat. No. 74,333,742. mixtures of at least two different tris(mono-C1-C8 alkyl)phenyl phosphites, such as those referred to in U.S. Pat. No. 68410 B2 as the products of Examples 1 and 2; mixtures of phosphites comprising at least two different tris(amylphenyl) phosphites, such as those referred to in U.S. Pat. No. 8,008,383 B2 as mixtures 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, and 26;mixtures of four different phosphites comprising at least tris[4-(1,1-dimethylpropyl)phenyl]phosphite, [2,4-bis(1,1-dimethylpropyl)phenyl]bis[4-(1,1-dimethylpropyl)phenyl]phosphite, bis[2,4-bis(1,1-dimethylpropyl)phenyl][4-(1,1-dimethylpropyl)phenyl]phosphite, and tris[2,4-bis(1,1-dimethylpropyl)phenyl]phosphite; mixtures of at least two different tris(butylphenyl)phosphites, such as those referred to in U.S. Pat. No. 8,008,383 B2 as mixtures 34, 35, 36, 37, 38, 39, and 40; mixtures of phosphites comprising bis(2,4-di-tert-butyl-6-methylphenyl)methyl phosphite, bis(2,4-di-tert-butyl-6-methylphenyl)ethyl phosphite, 6-fluoro-2,4,8,10-tetra-tert-butyl-2-methylphenyl ... t-Butyl-12-methyldibenzo[d,g]-1,3,2-dioxaphosphocin, 1,3,7,9-tetra-tert-butyl-11-octoxy-5H-benzo[d][1,3,2]benzodioxaphosphocin, 2,2',2''-nitrilo[triethyltris(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2,2'-diyl)phosphite], phosphorous acid, triphenyl ester, α-hydro-ω-hydroxypoly[ Polymers of oxy(methyl-1,2-ethanediyl)], C10-16 alkyl esters (CAS Registry Number [1227937-46-3]), 2-ethylhexyl(3,3',5,5'-tetra-tert-butyl-1,1'-biphenyl-2,2'-diyl)phosphite, and mixtures of 2,4-bis(1,1-dimethylpropyl)phenyl and 4-(1,1-dimethylpropyl)phenyl triesters (CAS Registry Number [939402-02-5]).

[0144] 5. Hydroxylamines and amine N-oxides, such as N,N-dibenzylhydroxylamine, N,N-di-ethylhydroxylamine, N,N-dioctylhydroxylamine, N,N-dilaurylhydroxylamine, N,N-ditetradecylhydroxylamine, N,N-dihexadecylhydroxylamine, N,N-dioctadecylhydroxylamine, N-hexadecyl-N-octadecylhydroxylamine, N-heptadecyl-N-octadecylhydroxylamine, N,N-dialkylhydroxylamines derived from hydrogenated tallow amine, N,N-bis-(hydrogenated rapeseed oil alkyl)-N-methylamine N-oxide, or trialkylamine N-oxides.

[0145] 6. Nitrones, such as N-benzyl-α-phenyl nitrone, N-ethyl-α-methyl nitrone, N-octyl-α-heptyl nitrone, N-lauryl-α-undecyl nitrone, N-tetradecyl-α-tridecyl nitrone, N-hexadecyl-α-pentadecyl nitrone, N-octadecyl-α-heptadecyl nitrone, N-hexadecyl-α-heptadecyl nitrone, N-octadecyl-α-pentadecyl nitrone, N-heptadecyl-α-heptadecyl nitrone, N-octadecyl-α-hexadecyl nitrone, nitrones derived from N,N-dialkylhydroxylamines derived from hydrogenated tallow amine.

[0146] 7. Thiosynergists, such as dilauryl thiodipropionate, dimistryl thiodipropionate, distearyl thiodipropionate, and pentaerythritol tetrakis-[3-(n-lauryl)propionate].

[0147] 8. Peroxide scavengers, such as esters of α-thiodipropionic acid; such as the lauryl, stearyl, myristyl or tridecyl ester, mercaptobenzimidazole; or zinc salts of 2-mercaptobenzimidazole, zinc dibutyldithiocarbamate, dioctadecyl disulfide, pentaerythritol tetrakis(β-dodecylmercapto)propionate.

[0148] 9. Acid scavengers, such as melamine, polyvinylpyrrolidone, dicyandiamide, triallyl cyanurate, urea derivatives, hydrazine derivatives, alkali metal salts and alkaline earth metal salts of higher fatty acids, such as calcium stearate, zinc stearate, magnesium behenate, magnesium stearate, sodium ricinoleate and potassium palmitate, antimony pyrocatecholate, and zinc pyrocatecholate.

[0149] 10. Further benzofuranones and indolinones other than those defined above, such as, for example, U.S. Pat. No. 4,325,863 A; U.S. Pat. No. 4,338,244 A; U.S. Pat. No. 5,175,312 A; U.S. Pat. No. 5,216,052 A; U.S. Pat. No. 5,252,643 A; DE 4316611 A; DE 4316622 A; DE 4316876 A; EP 0589839 A or EP 0591 102A, or 5,7-di-tert-butyl-3-(4-hydroxyphenyl)-3H-benzofuran-2-one, 5,7-di-tert-butyl-3-[4-(2-hydroxyethoxy)phenyl]-3H-benzofuran-2-one, 5,7-di-tert-butyl-3-[4-[2-[2-[2-[2-(2-hydroxyethoxy)ethoxy]ethoxy]-ethoxy]-phenyl]-3H-benzofuran-2-one, 3-[4-(2-acetoxy-ethoxy)phenyl ]-5,7-di-tert-butylbenzofuran-2-one, 5,7-di-tert-butyl-3-[4-(2-stearoyloxy-ethoxy)phenyl]benzofuran-2-one, 3,3'-bis[5,7-di-tert-butyl-3-(4-[2-hydroxyethoxy]phenyl)benzofuran-2-one], 5,7-di-tert-butyl-3-(4-ethoxyphenyl)benzofuran-2-one, 3-(4-acetoxy-3,5-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one on, 3-(3,5-dimethyl-4-pivaloyloxyphenyl)-5,7-di-tert-butylbenzofuran-2-one, 3-(3,4-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one, 3-(2,3-dimethylphenyl)-5,7-di-tert-butylbenzofuran-2-one, 3-(2-acetoxy-4-(1,1,3,3-tetramethylbutyl)phenyl)-5-(1,1,3,3-tetramethylbutyl)benzofuran-2-one, [6-[6-[6-[2-[4-(5,7-di-tert-butyl-2-oxo-3H-benzofuran-3-yl)phenoxy]ethoxy]-6-oxohexoxy]-6-oxohexoxy]-6-oxohexyl]6-hydroxyhexanoate, [4-tert-butyl-2-(5-tert-butyl-2-oxo-3H-benzofuran-3-yl)phenyl]benzoic acid, [4-tert-butyl-2-(5-tert-butyl-2-oxo-3H-benzo-furan-3-yl)phenyl]3,5-di-tert-butyl-4-hydroxybenzoic acid, and [4-tert-butyl-2-(5-tert-butyl-2-oxo-3H-benzofuran-3-yl)phenyl]3-(3,5-di-tert-butyl-4-hydroxy-phenyl)propanoic acid.

[0150] 11.Flame retardants 11.1. Phosphorus-containing flame retardants include, for example, the following reactive phosphorous-containing flame retardants: tetraphenylresorcinol diphosphite (Fyrolflex RDP, RTM, Akzo Nobel), tetrakis(hydroxy-methyl)phosphonium sulfide, triphenyl phosphate, diethyl-N,N-bis(2-hydroxyethyl)aminomethyl phosphonate, hydroxyalkyl esters of phosphoric acid, alkyl phosphate oligomers, ammonium polyphosphate (APP), resorcinol diphosphate oligomers (RDP), phosphazene flame retardants or ethylenediamine diphosphate (EDAP).

[0151] 11.2. Nitrogen-containing flame retardants, for example melamine-based flame retardants, isocyanurates, polyisocyanurates; tris(2-hydroxyethyl)isocyanuric acid, tris(hydroxymethyl)isocyanuric acid, tris(3-hydroxy-n-propyl)isocyanuric acid; esters of isocyanuric acid, such as triglycidyl isocyanurate; melamine cyanurate, melamine borate, melamine phosphate, melamine pyrophosphate, melamine polyphosphate, melamine ammonium polyphosphate, ammonium melamine pyrophosphate, dimelamine phosphate, dimelamine pyrophosphate, benzoguanamine, allantoin, glycoluril, urea cyanurate; condensation products and / or higher condensation compounds of melamine from the melem, melam, melon series; or reaction products of melamine with phosphoric acid or mixtures thereof.

[0152] 11.3. Organic halogen flame retardants, e.g., polybrominated diphenyl oxide, decabromodiphenyl oxide (DBDPO), tris[3-bromo-2,2-bis(bromomethyl)propyl]phosphate (PB 370, (RTM, FMC Corp.)), tris(2,3-dibromopropyl)phosphate), chloroalkyl phosphate esters, e.g., tris(chloropropyl)phosphate, tris(2,3-dichloropropyl)phosphate, tris(1,3-dichloro-2-propyl)phosphate (Fyrol FR 2 (RTM ICL)), chloroalkyl phosphate oligomers, chlorendic acid, tetrachlorophthalic acid, tetrabromophthalic acid, poly-β-chloroethyl triphosphonic acid mixtures; tetrabromobisphenol A-bis(2,3-dibromopropyl ether) (PE68), brominated epoxy resins, brominated aryl esters, ethylene-bis(tetrabromophthalimide) (Saytex BT-93 (RTM, Albemarle)), bis(hexachlorocyclopentadieno)cyclooctane (Declorane Plus (RTM, Oxychem)), chlorinated paraffins, octabromodiphenyl ethers, hexachlorocyclopentadiene derivatives, 1,2-bis(tribromophenoxy)ethane (FF680), tetrabromobisphenol A (Saytex RB100 (RTM, Albemarle)), ethylene bis-(dibromonorbornanedicarboximide) (Saytex BN-451 (RTM, Albemarle)), bis(hexachlorocycloentadeno)cyclooctane, PTFE, tris(2,3-dibromopropyl)isocyanurate or ethylene-bis-tetrabromophthalimide.

[0153] Some of the above halogenated flame retardants are routinely combined with inorganic oxide synergists. Some of the above halogenated flame retardants may be used in combination with triaryl phosphates (propylated, butylated triphenyl phosphate, etc.) and / or oligomeric aryl phosphates (resorcinol bis(diphenyl phosphate), bisphenol A bis(diphenyl phosphate), neopentyl glycol bis(diphenyl phosphate)), etc.

[0154] 11.4. Inorganic flame retardants, such as aluminum trihydroxide (ATH), boehmite (AlOOH), magnesium dihydroxide (MDH), zinc borate, CaCO3, organically modified layered silicates, organically modified layered double hydroxides, and mixtures thereof. With regard to synergistic effects in combination with halogenated flame retardants, the most common inorganic oxide synergists are zinc oxide, antimony oxides such as Sb2O3 or Sb2O5, or boron compounds.

[0155] From these further additives listed above, several compounds are also preferably present in the composition according to the invention.

[0156] Preferably, the composition according to the invention comprises: (iii) from the group of the chromanol antioxidants, such as α-tocopherol, β-tocopherol, γ-tocopherol, δ-tocopherol and mixtures thereof (vitamin E), vitamin E acetate; and / or Amines are phenyl and C6-C 10 Substituted only with aryl, phenyl or C6-C 10 from the group of aromatic amine antioxidants, such as phenylarylamines, in which the aryl is alkylated, and / or Esters of 3,5-di-tert-butyl-4-hydroxyphenylacetic acid with monohydric or polyhydric alcohols, such as methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol; from the group of tris(hydroxyethyl)isocyanurate, N,N'-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane. It may comprise at least one further additive as selected.

[0157] Particularly preferred compositions according to the invention comprise, as further additive (iii), a compound of formula III, [ka] wherein R 1-iii and R 2-iii are each independently H or methyl.

[0158] Alternatively or in addition, commercially available industrial additive mixtures may be added, particularly preferably (A) 5057 , diphenylamine; (B) 5057 , 4-tert-butyldiphenylamine; (C) 5057 i) 4-tert-octyldiphenylamine, ii) 4,4'-di-tert-butyldiphenylamine, iii) Compounds of the 2,4,4'-tris-tert-butyldiphenylamine group; (D) 5057 i) 4-tert-butyl-4'-tert-octyldiphenylamine, ii) o,o', m,m', or p,p'-di-tert-octyldiphenylamine; iii) Compounds of the 2,4-di-tert-butyl-4'-tert-octyldiphenylamine group; (E) 5057 i) 4,4'-di-tert-octyldiphenylamine, ii) Compounds of the 2,4-di-tert-octyl-4'-tert-butyldiphenylamine group Irganox 5057 (trademark) obtained by the reaction of diphenylamine with diisobutylene, comprising 5% by weight or less of component (A). 5057 , 8 to 15% by weight of component (B) 5057 , 24 to 32% by weight of component (C) 5057 , 23 to 34% by weight of component (D) 5057 , 21 to 34% by weight of component (E) 5057This is commercially available.

[0159] Furthermore, in addition to the bisphenol-based stabilizer, further phenolic antioxidants may optionally be present in the composition according to the invention.

[0160] Particularly preferred are, for example, esters of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid with octadecanol.

[0161] Formula (V), [ka] Such octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid, depicted in Figure 1, is commercially available as Irganox 1076 (trademark).

[0162] The addition of octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid may also reduce the content of bisphenol stabilizer present. In such cases, it may be necessary to add the concentration of phenolic antioxidant to the concentration of component (ii.2) the sterically hindered phenol, preferably the bisphenol stabilizer, to achieve the desired ratio of components (ii.1):(ii.2):(ii.3).

[0163] As discussed above, the present invention provides Component (ii.1), a 3-phenylbenzofuran-2-one derivative; Component (ii.2), a bisphenol-based stabilizer, and Component (ii.3), aliphatic phosphites It is demonstrated that the ternary stabilizer combination (ii) based on the three components above exhibits improved stabilization effect.

[0164] According to the invention, however, further additives may optionally be present as well.

[0165] Thus, preferred stabilizer compositions according to the present invention comprise the stabilizer combination in the following weight percentages: (ii.1) 5 to 50% by weight of a 3-phenyl-benzofuran-2-one derivative as defined herein above, (ii.2) 5 to 90 wt. % of a bisphenol stabilizer of formula II as defined herein above, and (ii.3) 5 to 50 wt. % of an aliphatic phosphite as defined herein above; and optionally (iii.1) 0 to 30 wt. % of a first further additive, and optionally (iii.2) 0-30 wt.-% of a second further additive.

[0166] Particularly preferred stabilizer compositions comprise the stabilizer combination in the following weight percentages: (ii.1) 5 to 20% by weight of a 3-phenyl-benzofuran-2-one derivative as defined herein above, (ii.2) 60 to 80% by weight of a bisphenol stabilizer of formula II as defined herein above, and (ii.3) 5 to 20 wt. % of an aliphatic phosphite as defined herein above; and optionally (iii.1) 0 to 15 wt. % of a first further additive, and optionally (iii.2) 0-15 wt.-% of a second further additive.

[0167] As a first further additive, for example, 2,5,7,8-tetramethyl-2-[4,8,12-trimethyltridecyl]chroman-6-ol (also known as Vitamin E and commercially available, for example, as Irganox E 201™) may be present.

[0168] As a second further additive there may be present, for example, a technical mixture of aromatic amines obtained by reaction of diphenylamine with diisobutylene (also commercially available as Irganox 5057™).

[0169] A third further additive may be present, for example octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid (commercially available as Irganox 1076™).

[0170] The references to a "first," "second," and "third" additive do not imply a priority or order of addition of each additive.

[0171] For example, an additional additive referred to as a "third" additive, octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid, may be added to an inventive ternary stabilizer combination in the absence of another additional additive.

[0172] In consideration of the above preferred combinations, the weight ratio of the component (ii.1), the component (ii.2) and the component (ii.3) is preferably 1:2:1 to 1:20:1.

[0173] A further embodiment of the present invention is represented by a weight ratio of components (ii.1) and (ii.2) of 1:3 to 3:1.

[0174] More preferably, the weight ratio of the components (ii.1), (ii.2) and (ii.3) is from 1:4:1 to 1:10:1.

[0175] A further embodiment of the present invention is represented by the weight ratio of components (ii.1) and (ii.2) being preferably from 1:2 to 2:1.

[0176] As mentioned above, if further additives are present in the composition according to the invention, the weight ratio between component (ii), meaning the total weight of [(ii.1)+(ii.2)+(ii.3)], and further component (iii), meaning the total weight of the further additives [(ii.1)+(iii.2)...], is (50-100) to (0-20).

[0177] Preferably, the ratio of the total weight of the further additives (iii) to the total weight of the stabilizer combination (ii) is (60-95):(2-15).

[0178] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol stabilizer, and an aliphatic phosphite, as defined above; (iii) a first further additive, preferably 2,5,7,8-tetramethyl-2-[4,8,12-trimethyltridecyl]chroman-6-ol (also known as vitamin E and commercially available, for example, as Irganox E 201™); The composition comprises:

[0179] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol stabilizer, and an aliphatic phosphite, as defined above; (iii) a first further additive, which is preferably a technical mixture of aromatic amines obtained by reaction of diphenylamine with diisobutylene (also commercially available as Irganox 5057™); The composition comprises:

[0180] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol stabilizer, and an aliphatic phosphite, as defined above; (iii) a first further additive, preferably octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid (commercially available as Irganox 1076™); The composition comprises:

[0181] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol stabilizer, and an aliphatic phosphite, as defined above; (iii.1) a first further additive, preferably 2,5,7,8-tetramethyl-2-[4,8,12-trimethyltridecyl]chroman-6-ol (also known as vitamin E and commercially available, for example, as Irganox E 201™); (iii.2) A second further additive, which is preferably a technical mixture of aromatic amines obtained by reaction of diphenylamine with diisobutylene (also commercially available as Irganox 5057™). The composition comprises:

[0182] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol stabilizer, and an aliphatic phosphite, as defined above; (iii.1) a first further additive, preferably 2,5,7,8-tetramethyl-2-[4,8,12-trimethyltridecyl]chroman-6-ol (also known as vitamin E and commercially available, for example, as Irganox E 201™); (iii.2) a second further additive, preferably octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid (commercially available as Irganox 1076™); The composition comprises:

[0183] The preferred (i) a polyurethane foam or a polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol stabilizer, and an aliphatic phosphite, as defined above; (iii.1) a first further additive which is preferably a technical mixture of aromatic amines obtained by reaction of diphenylamine with diisobutylene (also commercially available as Irganox 5057™); (iii.2) a second further additive, preferably octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid (commercially available as Irganox 1076™); The composition comprises:

[0184] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol-based stabilizer of formula (II.2-1) as defined herein above, and di-n-octyl hydrogen phosphite as the aliphatic phosphite; (iii) a first further additive, preferably 2,5,7,8-tetramethyl-2-[4,8,12-trimethyltridecyl]chroman-6-ol (also known as vitamin E and commercially available, for example, as Irganox E 201™); The composition comprises:

[0185] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol-based stabilizer of formula (II.2-1) as defined herein above, and di-n-octyl hydrogen phosphite as the aliphatic phosphite; (iii) a first further additive, which is preferably a technical mixture of aromatic amines obtained by reaction of diphenylamine with diisobutylene (also commercially available as Irganox 5057™); The composition comprises:

[0186] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol-based stabilizer of formula (II.2-1) as defined herein above, and di-n-octyl hydrogen phosphite as the aliphatic phosphite; (iii) a first further additive, preferably octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid (commercially available as Irganox 1076™); The composition comprises:

[0187] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol-based stabilizer of formula (II.2-1) as defined herein above, and di-n-octyl hydrogen phosphite as the aliphatic phosphite; (iii.1) a first further additive, preferably 2,5,7,8-tetramethyl-2-[4,8,12-trimethyltridecyl]chroman-6-ol (also known as vitamin E and commercially available, for example, as Irganox E 201™); (iii.2) A second further additive, which is preferably a technical mixture of aromatic amines obtained by reaction of diphenylamine with diisobutylene (also commercially available as Irganox 5057™). The composition comprises:

[0188] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol-based stabilizer of formula (II.2-1) as defined herein above, and di-n-octyl hydrogen phosphite as the aliphatic phosphite; (iii.1) a first further additive, preferably 2,5,7,8-tetramethyl-2-[4,8,12-trimethyltridecyl]chroman-6-ol (also known as vitamin E and commercially available, for example, as Irganox E 201™); (iii.2) a second further additive, preferably octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid (commercially available as Irganox 1076™); The composition comprises:

[0189] The preferred (i) polyurethane foam or polyether polyol; (ii) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol-based stabilizer of formula (II.2-1) as defined herein above, and di-n-octyl hydrogen phosphite as the aliphatic phosphite; (iii.1) a first further additive, preferably octadecyl-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid (commercially available as Irganox 1076™); (iii.2) A second further additive, which is preferably a technical mixture of aromatic amines obtained by reaction of diphenylamine with diisobutylene (also commercially available as Irganox 5057™). The composition comprises:

[0190] The preferred (a) polyurethane foam or polyether polyol; (b) a ternary stabilizer combination of a 3-phenyl-benzofuran-2-one derivative, a bisphenol stabilizer, and an aliphatic phosphite, as defined above; (c) optionally a first further additive; (d) optionally, a second additional additive different from the first additional additive; wherein the polyurethane foam is obtained from the reaction of a polyisocyanate reactant and a polyol reactant in a reaction mixture, wherein the reaction mixture prior to reaction comprises the polyisocyanate reactant, the polyol reactant, water, a surfactant, and a catalyst.

[0191] In the case of polyurethane foam as component (i), the composition can be part of a molded article or can be an integrally molded article, preferably the composition is an integrally molded article, more preferably the composition is a slabstock foam in the case of polyurethane foam, most preferably a flexible slabstock foam.

[0192] Preferred is a composition in which the composition is in the form of a molded article and component (i) is a polyurethane foam.

[0193] Preferred is a composition, wherein the composition is part of a molded article or is the entire molded article, and component (i) is a polyurethane foam.

[0194] Preferred is a composition in the form of a foam, which comprises (i) a polyurethane foam and (ii) a stabilizer combination according to the present invention.

[0195] Preferred is a slabstock foam composition comprising (i) a polyurethane foam and (ii) a stabilizer combination according to the present invention.

[0196] Examples of articles are: 1) Floating devices for marine applications. 2) Automotive applications, especially bumpers, dashboards, rear and front linings, under hood moulding parts, hat shelves, trunk linings, interior linings, airbag covers, instrument panels, exterior linings, upholstery, interior and exterior trim, door panels, seat backings, exterior panels, cladding, pillar covers, chassis parts, convertible tops, front end modules, pressed / stamped parts, side impact protection, sound deadening / insulation and sunroofs. 3) Aircraft equipment, railway equipment. 4) Architectural and design devices, acoustic quieting systems, shelters. 5) Coatings for steel or other materials such as textiles, e.g. cable coatings. 6) Electrical appliances, especially washing machines, tumblers, ovens (microwaves), dishwashers and mixers. 7) Rotor blades, ventilators and windmill blades, swimming pool covers, pool liners, pond liners, closets, wardrobes, bulkheads, slat walls, folding walls, roofs, shutters (e.g. roller shutters), sealings. 8) Packaging and packaging, isolated bottles. 9) General furniture, foam products (cushions, mattresses, shock absorbing materials), foam, sponges, dishwashing cloths, mats. 10) Shoes, soles, insoles, spats, adhesives, structural adhesives, sofas.

[0197] The above describes a selection of compositions comprising a polyurethane foam or a polyether polyol as component (i) and a stabilizer combination according to the invention as component (ii). These selections also apply to further embodiments of the present invention.

[0198] A further embodiment of the present invention relates to a process for preparing a composition comprising the step of incorporating a stabilizer combination according to the invention as component (II) into a polyurethane foam or a polyether polyol as component (I) to obtain the composition.

[0199] Polyurethane foams can be obtained, for example, by mixing a polyisocyanate reactant with a polyol reactant to obtain a reaction mixture which is then reacted. It is also possible to employ a two-stage technique in which all or most of the polyol reactant is reacted with a polyisocyanate reactant in a first stage to form an isocyanate-terminated prepolymer which is then reacted with the remaining components in a second stage to form the foam. However, it is preferred to employ a one-shot technique in which all of the components are contacted and reacted in one stage.

[0200] Preferably, the method for producing the composition comprises: (a) premixing components (ii.1), (ii.2) and (iii.3) with the stabilizer combination (ii) as defined herein above; (b)(bF-1) adding a stabilizer combination (ii) to a starting mixture comprising a polyol reactant and no polyisocyanate reactant to obtain a pre-reaction mixture; (bF-2) adding a polyisocyanate reactant to the pre-reaction mixture to obtain a reaction mixture; (bF-3) reacting the reaction mixture to obtain a composition comprising a polyurethane foam; or (bP-1) incorporating the stabilizer combination I as component (ii) into a polyurethane foam, comprising adding the stabilizer combination (ii) to a polyether polyol to obtain a composition comprising the polyether polyol; The present invention relates to a method for producing a semiconductor device comprising the steps of:

[0201] If added, the first further additive is preferably added before the polyisocyanate reactant is added, more preferably to the starting mixture or pre-reaction mixture.

[0202] If added, the second further additive is preferably added before the polyisocyanate reactant is added, more preferably to the starting mixture or pre-reaction mixture.

[0203] If added, water or carboxylic acid is preferably added before the polyisocyanate reactant is added, more preferably to the starting mixture or pre-reaction mixture. If added, the blowing agent is preferably added before the polyisocyanate reactant is added, or some or all of the blowing agent is added together with the polyisocyanate reactant.

[0204] If added, the surfactant is preferably added before the polyisocyanate reactants are added, more preferably to the starting mixture or pre-reaction mixture.

[0205] If added, the catalyst is preferably added before the polyisocyanate reactants are added, more preferably to the starting mixture or pre-reaction mixture.

[0206] If added, the crosslinker is preferably added before the polyisocyanate reactants are added, more preferably to the starting mixture or pre-reaction mixture.

[0207] If added, the chain extender is preferably added before the polyisocyanate reactants are added, more preferably to the starting mixture or pre-reaction mixture.

[0208] Preferred is a process for preparing the composition, comprising the step of incorporating a stabilizer combination, as component (ii), into a polyurethane foam or a polyether polyol, as component (i), to obtain the composition.

[0209] A further embodiment of the present invention relates to the use of a stabilizer combination, i.e. component (ii), for protecting polyurethane foams or polyether polyols, i.e. component (i), against degradation. Preferably, the protection is against oxidative, thermal or light-induced degradation. In the case of polyurethane foams as component (i), the protection is preferably against yellowing. In the case of polyurethane foams as component (i), the protection is preferably against scorching. In the case of polyether polyols as component (i), the protection is preferably against oxidative degradation, more preferably against degradation by oxygen at temperatures between 100 and 300°C.

[0210] Preferred is the use of a stabilizer combination, component (ii), to protect the polyurethane foam or polyether polyol, component (i), from degradation.

[0211] Preferred is the use of a stabilizer combination to protect polyurethane foams from scorching, namely component (ii). EXAMPLES

[0212] The invention is illustrated by the following non-limiting examples.

[0213] To investigate the performance of dioctyl hydrogen phosphite in polyether polyols and PU foams, its activity was investigated as a neat additive. Furthermore, its activity was investigated in combination with high molecular weight sterically hindered phenols (Example S-1 in WO 17125291). WO 17125291 reports a synergistic combination of sterically hindered phenols and vitamin E at a total concentration of the stabilizer composition of 0.45%, so the same dose was used in the application examples described in this invention (Table TA-1). Furthermore, compounds 1-30 in EP 0871066 A1 and stabilizer 4 in WO 2020 / 002130, etc., have been investigated for their activity in combination with benzofuranone. The latter describes the testing of benzofuranone at a total concentration of 1%, so the same loading was used in the application examples reported in this invention (Tables TA-2, TA-3).

[0214] In fact, in binary combination with the above stabilizers, dioctyl hydrogen phosphite did not show significant antioxidant activity and improvement.

[0215] Surprisingly, when dioctyl phosphite was used in a ternary combination with both a sterically hindered phenol and a benzofuranone derivative, an even improved performance was detected (Table TA-4). Such an improvement was superior to the binary combination of a sterically hindered phenol and a benzofuranone derivative already described in WO 2020 / 002130.

[0216] After confirming the scorch prevention activity of such combinations, they were also tested for outgassing of polyols and PU foams. Gas-bleachable discoloration and light-induced discoloration were also investigated. The results are reported in the application examples, as well as the results with the addition of further preferred additives as outlined herein above.

[0217] Anti-scorch systems are necessary to prevent scorch during the production of flexible PU foams and they are usually introduced into the polyol, which is one of the main raw materials used in the process. Since polyols, more specifically polyether polyols, are prone to thermal degradation, it is important that the anti-scorch system used provides good stability to the polyol against thermal degradation that may also occur during storage and transportation.

[0218] The tendency of a polyol to undergo thermal decomposition can be readily measured by DSC, in which the polyol is exposed to elevated temperatures in the presence of oxygen until autoxidation begins.

[0219] Experimental Part Percentages are always by weight unless the context suggests otherwise. Reported contents are based on the content in the aqueous solution or dispersion unless otherwise stated.

[0220] [Table 1]

[0221] [Table 2]

[0222] Example 1 - Stabilization of Polyether / Polyurethane Flexible Foam The stabilizer composition according to table TA-1 is dissolved in 116.8 g of a stabilizer-free trifunctional polyether polyol containing mainly secondary hydroxyl groups, with a molecular weight of 3500 Da and OH number = 48. 10.98 g of a solution consisting of 2.40 g of Tegostab BF 2370 (RTM Evonik Industries; surfactant based on polysiloxane), 0.18 g of Tegoamin 33 (RTM Evonik Industries; universal gelling catalyst based on triethylenediamine) and 8.4 g of deionized water are added and the reaction mixture is vigorously stirred at 2600 rpm for 10 seconds. Then 0.36 g of Kosmos 29 (RTM Evonik Industries; catalyst based on stannous octoate) dissolved in 3.24 g of polyol is added and the reaction mixture is again vigorously stirred at 1400 rpm for 18 hours. Then 99.24 g of Isocyanate TDI 80 (a mixture containing 80% toluene-2,4-diisocyanate and 20% toluene-2,6-diisocyanate isomer) is added with stirring at 2600 rpm for 5-7 seconds. The mixture is then poured into a 20 x 20 x 20 cm plastic box and an exothermic foaming reaction occurs as indicated by an increase in temperature. The foam buns are cooled and stored at room temperature for 24 hours.

[0223] All foam buns prepared exhibited the same initial white color and were used in the following examples unless otherwise noted.

[0224] Examples A-1 to A-4: Scorch prevention test Scorch resistance is determined by static heat aging, i.e. static aluminium block test. The foam buns are cut into thin cylindrical shapes (2 cm thick, 1.5 cm diameter). From each foam bun, a thin cylinder is taken as a foam sample. The foam sample is heated in an aluminium block. The temperature is kept at 190°C for 30 minutes.

[0225] Scorch resistance is evaluated by measuring the color of the foam samples after aging. The measured color is reported as the Yellowness Index (YI) measured on the foam samples according to the ASTM D 1925-70 Yellowness Test. A lower YI value indicates less discoloration and a higher YI value indicates more severe discoloration. The whiter the foam sample remains, the more stabilized it is.

[0226] As a measure of scorch resistance, ΔYI was calculated as the difference between the discoloration of each foam formulation compared to the discoloration of the foam without added antioxidant. Since higher discoloration is measured for foams without stabilizers, the following calculation of ΔYI gives a negative number: ΔYI=(discoloration of PU stabilized compound)-(discoloration of non-PU stabilized compound) The lower the calculated ΔYI value, the higher the scorch prevention performance.

[0227] Example A-1

[0228] [Table 3]

[0229] As shown in Table TA-1, the use of the sterically hindered phenol stabilizer alone shows scorch protection, while the use of the aliphatic phosphorous acid (III) compound dioctyl hydrogen phosphite alone causes even greater discoloration compared to the control. The use of a binary 1:1 stabilizer combination with the same total concentration of stabilizers as the stabilizers used alone shows weaker scorch protection performance, i.e., higher ΔYI values, than the use of the sterically hindered phenol stabilizer alone, and as the ratio is gradually changed in favor of a higher proportion of the sterically hindered phenol, improvements in scorch protection performance are observed. However, the lowest ΔYI values ​​are still achieved when the sterically hindered phenol is used alone.

[0230] Example A-2

[0231] [Table 4]

[0232] As shown in Table TA-2, the use of the benzofuranone derivative stabilizer BF-2 alone shows scorch protection, while the use of the aliphatic phosphorous (III) compound dioctyl hydrogen phosphite alone causes even greater discoloration compared to the control. Use of a binary 1:1 stabilizer combination with the same total stabilizer concentration as the stabilizer used alone shows weaker scorch protection performance, i.e., higher ΔYI values, than the use of the benzofuranone derivative stabilizer BF-2 alone, and when the ratio is changed to a lower percentage of the benzofuranone derivative, lower scorch protection performance is observed. The lowest ΔYI values ​​are achieved when the benzofuranone derivative is used alone.

[0233] Example A-3

[0234] [Table 5]

[0235] Similar to what was observed in Table TA-2, Table TA-3 for the use of another benzofuranone derivative stabilizer BF-1 also shows that for a binary 1:1 stabilizer combination (Example A-3-4) having the same total stabilizer concentration as the benzofuranone BF-1 stabilizer used alone (A-3-2), weaker scorch prevention performance, i.e., higher delta YI values, are observed for the use of a combination of dioctyl hydrogen phosphite and the second tested benzofuranone derivative BF-1, while the lowest delta YI values ​​are achieved when the benzofuranone derivative is used alone.

[0236] Example A-4

[0237] [Table 6]

[0238] Table TA-4a illustrates how a binary combination of a sterically hindered phenol and a benzofuranone derivative shows improved performance compared to the neat antioxidants used alone. Furthermore, when an aliphatic dioctyl hydrogen phosphite is added to this binary combination, the resulting ternary combination provides further performance improvement.

[0239] [Table 7]

[0240] [Table 8]

[0241] The data in Table TA-4b, Part I, show that the ternary combination according to the invention provides high scorch protection performance even with increasing aging temperatures, and in Part II, it is shown that the performance achieved can be maintained or even improved by adding further preferred additives to the ternary combination of the invention.

[0242] Example A-5 Oxidation resistance test: The oxidation resistance of the resulting stabilized polyether polyol samples is measured by differential scanning calorimetry (DSC). The samples are heated under oxygen starting at 50° C. at a heating rate of 5° C. / min until 200° C. is reached. The appearance of an exothermic peak indicates the onset of the thermo-oxidative reaction. The temperature at the onset of the exothermic peak is recorded. More stabilized samples are characterized by a higher temperature at the onset. The results are depicted in Table TA-5.

[0243] [Table 9]

[0244] [Table 10]

[0245] Table TA-5 Part I shows that the novel ternary combination according to the invention significantly increases the autoxidation temperature of polyols, and Part II shows that this effect may be even further improved by the addition of further preferred additives.

[0246] Example A-6: Emissions measurement in polyols Polyols, especially polyethers, are prone to thermo-oxidative decomposition leading to volatile by-products including aldehydes.

[0247] Anti-scorch systems that can prevent degradation should also play a role in reducing the amount of volatile by-products released. Among the volatile emissions, aldehydes are of particular importance due to their classification and contribution to odor. Especially in Asia, the industry is addressing standards and regulations aimed at reducing the amount of aldehyde-based volatiles.

[0248] In this example, the aldehydes released by polyols are measured and compared with values ​​measured for polyols that do not contain a stabilizer and for polyols that contain a stabilizing composition according to Table TA-6.

[0249] Polymer polyol samples without stabilizer (OH number = 25-32, 40-45% solids (styrene, acrylonitrile)) and samples containing the stabilizer compositions shown in Table TA-6 were analyzed by HPLC to detect released aldehydes. The polyol samples were then heated to 100°C and held at this temperature for 48 hours before measuring aldehydes. The results are depicted in Table TA-6 (in ppm).

[0250] [Table 11]

[0251] The results in Table TA-6 show that the addition of a ternary stabilizer combination according to the present invention to a polyol contributes to a significant reduction in the level of aldehydes released upon heat aging.

[0252] Example A.7: Emission measurement of PU foam Preparation of polyether / polyurethane flexible foams: The stabilizer composition according to table TA-7 is dissolved in 217.3 g of a stabilizer-free trifunctional polyether polyol containing mainly secondary hydroxyl groups, with a molecular weight of 3500 Da and OH number = 48. 11.00 g of a solution consisting of 4.40 g of Tegostab BF 2370 (RTM Evonik Industries; surfactant based on polysiloxane), 0.33 g of Tegoamin 33 (RTM Evonik Industries; universal gelling catalyst based on triethylenediamine) and 6.27 g of deionized water are added and the reaction mixture is vigorously stirred at 2600 rpm for 10 seconds. Then 0.26 g of Kosmos 29 (RTM Evonik Industries; catalyst based on stannous octoate) dissolved in 2.38 g of polyol is added and the reaction mixture is again vigorously stirred at 1400 rpm for 18 hours. Then 92.4 g of Isocyanate TDI 80 (a mixture containing 80% toluene-2,4-diisocyanate and 20% toluene-2,6-diisocyanate isomer) is added with stirring at 2600 rpm for 5-7 seconds. The mixture is then poured into a 20 x 20 x 20 cm plastic box and an exothermic foaming reaction occurs as indicated by an increase in temperature. The foam buns are cooled and stored at room temperature for 24 hours.

[0253] All the prepared foam buns had the same initial white color and were used in Example 7.

[0254] Exhaust Gas Measurement On foam samples prepared according to the above method, the exhaust emissions are measured according to the VDA 278 10 / 11 method, which is a method widely used in the automotive industry to determine the exhaust emissions from non-metallic materials used in automotive interiors. Two cumulative values ​​are determined, which estimate the emission of volatile organic compounds (VOC value) and the part of condensable substances (FOG value). In addition, single substance exhaust emissions are also determined. During the analysis, the samples are thermally extracted and the exhaust gases are separated by gas chromatography and detected by mass spectrometry. The results are expressed in ppm of volatile substances; the lower the number, the better. The maximum emission levels accepted by the industry for maximum emissions according to the VDA 278 10 / 11 method may vary, but VOC emissions of less than 100 ppm and FOG emissions of less than 250 ppm are considered good values.

[0255] The results are contained in Table TA-7.

[0256] [Table 12]

[0257] Table TA-7 shows how foams stabilized with the novel stabilizer compositions described in this invention produce emissions significantly below thresholds considered significant in the industry.

[0258] Example A-8 - Stabilization of Polyether / Polyurethane Flexible Foam Against Gas Fade Preparation of polyether / polyurethane flexible foams: The stabilizer composition according to table TA-8 is dissolved in 116.8 g of a stabilizer-free trifunctional polyether polyol containing mainly secondary hydroxyl groups, with a molecular weight of 3500 D and OH number = 48. 10.98 g of a solution consisting of 2.40 g of Tegostab BF 2370 (RTM Evonik Industries; polysiloxane-based surfactant), 0.18 g of Tegoamin 33 (RTM Evonik Industries; triethylenediamine-based universal gelling catalyst) and 8.4 g of deionized water are added and the reaction mixture is vigorously stirred for 10 seconds at 2600 rpm. Then 0.36 g of Kosmos 29 (RTM Evonik Industries; stannous octoate-based catalyst) dissolved in 3.24 g of polyol is added and the reaction mixture is again vigorously stirred for 18 seconds at 2600 rpm. Then 99.24 g of Isocyanate TDI 80 (a mixture containing 80% toluene-2,4-diisocyanate and 20% toluene-2,6-diisocyanate isomer) is added with stirring at 2600 rpm for 5-7 seconds. The mixture is then poured into a 20 x 20 x 20 cm plastic box and an exothermic foaming reaction occurs as indicated by an increase in temperature. The foam buns are cooled and stored at room temperature for 24 hours.

[0259] All the foam buns prepared had the same initial white color and were used in Examples 8 and 9.

[0260] Exposure to NOx gases Gas fade resistance is an important secondary property for foams that may discolor during storage due to interaction with nitrogen oxides present in the atmosphere. Such attitude is determined by exposing prepared foam samples in a controlled atmosphere chamber containing 4-6 ppm nitrogen oxides.

[0261] For scorch prevention systems comprising the ternary stabilizer combinations of the present invention, it is important that they do not adversely affect the gas fade resistance of the polyurethane flexible foam.

[0262] Gas fade resistance is evaluated by measuring the color of the foam samples after exposure. The measured color is reported as the Yellowness Index (YI) measured on the foam samples according to the ASTM 1926-70 Yellowness Test. A lower YI value indicates less discoloration and a higher YI value indicates more severe discoloration. The whiter the foam sample remains, the more stabilized it is.

[0263] As a measure of gas fade resistance, ΔYI was calculated as the difference between the discoloration of each foam formulation compared to the discoloration of foams without added antioxidant. Since higher discoloration is measured in foams without stabilizers, the calculation of ΔYI as (discoloration of PU stabilized formulation - discoloration of non-PU stabilized formulation) results in a negative number. The lower the calculated delta YI, the better the performance.

[0264] Table TA-8 depicts the discoloration upon exposure to nitrogen oxides for the ternary stabilizer combinations that are the subject of the present invention, as well as for these ternary stabilizer combinations with additional additives.

[0265] [Table 13]

[0266] [Table 14]

[0267] Table TA-8 Part I shows that the ternary stabilizer combination according to the present invention reduces the discoloration effect under NOx exposure, thereby increasing the gas fade resistance of the exposed foam, and Part II shows that this effect is largely maintained in the presence of further preferred additives.

[0268] Example A-9 - Weather Stabilization of Polyether / Polyurethane Flexible Foams Xenon lamp exposure Polyurethane foams widely used on the market are based on aromatic isocyanates and therefore tend to discolor when exposed to light during storage and final use. Such properties are determined under laboratory conditions by exposing produced foam samples to a light source that mimics solar radiation in a temperature and humidity controlled chamber. For this purpose, xenon lamps are widely used in accelerated so-called "weathering" due to the similarity of their light spectrum to the solar spectrum.

[0269] Light-induced discoloration is 0.36 W / m 2 After exposure to xenon lanthanum (Lam) at 20 nm radiation, black panel temperature 63°C + / - 3°C, chamber temperature 42°C + The foam is evaluated by measuring the color of the foam samples at + / -4°C, chamber relative humidity of 50% + / - 5%, and continuous light irradiation at a wavelength of 340 nm.

[0270] It is important for scorch prevention systems comprising the ternary stabilizer combinations of the present invention that they do not affect the light-induced discoloration of polyurethane flexible foams.

[0271] The measured color is reported as the Yellowness Index (YI) measured on the foam samples according to the ASTM 1926-70 Yellowness Test. A lower YI value indicates less discoloration and a higher YI value indicates more discoloration. The whiter the foam sample remains, the more stabilized it is.

[0272] Delta YI, as a measure of light-induced discoloration, was calculated as the difference in discoloration of each foam formulation compared to the discoloration of foams without added antioxidants. Since higher discoloration was measured in foams without stabilizers, the calculation of Delta YI as (discoloration of PU stabilized formulation - discoloration of PU unstabilized formulation) results in a negative number. The lower the calculated Delta YI, the better the performance.

[0273] [Table 15]

[0274] [Table 16]

[0275] Table TA-9 Part I shows that the ternary stabilizer combination according to the invention significantly reduces discoloration of exposed foam, and Part II shows that this effect is largely maintained in the presence of further preferred additives.

Claims

1. Component (i) a polyether polyol or polyurethane foam; Component (ii) Component (ii.1): a compound of formula (I.1-1), (I.1-2), (I.1-3), (I.1-4) or (I.1-5), 【Chemical 1】 at least one 3-phenylbenzofuran-2-one derivative selected from: Component (ii.2): Formula (II), 【Chemistry 2】 (In the formula, n is 1, 2, 3, 4, 5, 6, 7, 8, 9, 10 or 11. at least one sterically hindered phenol stabilizer derivative, which is a bisphenol-based stabilizer compound of the formula: Component (ii.3): at least one aliphatic phosphite or phosphonate ester of at least one aliphatic alcohol, the aliphatic alcohol moiety of which has at least one primary hydroxyl group; a ternary stabilizer combination comprising A composition comprising:

2. 2. The composition of claim 1, wherein component (i) is a polyether polyol or polyurethane foam obtained by polymerization of starting materials comprising a polyether polyol as one of the starting materials.

3. 10. The composition of claim 1, wherein component (i) is a polyurethane foam.

4. 10. The composition of claim 1, wherein the polyurethane foam is obtained from the reaction of a polyisocyanate reactant with a polyol reactant in a reaction mixture, and the amount of the stabilizer combination (ii) is from 0.01 to 10 parts by weight, based on 100 parts by weight of the polyol reactant, for the polyurethane foam, and from 0.01 to 10 parts by weight, based on 100 parts by weight of the polyether polyol, for the polyether polyol.

5. The 3-phenylbenzofuran-2-one derivative has the formula (I.1-3): 【Chemistry 3】 2. The composition of claim 1, wherein the compound is a substituted compound of the formula:

6. Component (ii.2) of said stabilizer combination (ii) is represented by the formula II.2-1, 【Chemistry 4】 2. The composition of claim 1, wherein the stabilizer compound is a bisphenol-based stabilizer compound of the formula:

7. 2. The composition of claim 1, wherein component (ii.3) of the stabilizer combination (ii) is a phosphite ester that is a diester of two fatty alcohols having at least one primary hydroxyl group on their fatty alcohol moieties, preferably the two fatty alcohols are the same.

8. 8. The composition of claim 7, wherein component (ii.3) of said stabilizer combination (ii) is di-n-octyl hydrogen phosphite.

9. 6. The composition of claim 5, wherein the weight ratio of components (ii.1), (ii.2), and (ii.3) is from 1:2:1 to 1:30:1, preferably from 1:2:1 to 1:20:1, more preferably from 1:4:1 to 1:10:

1.

10. 6. The composition of claim 5, wherein the weight ratio of components (ii.1) and (ii.2) is from 1:10 to 3:1, preferably from 1:6 to 2:1, more preferably from 1:2 to 2:

1.

11. From the group of chromanol-containing antioxidants, such as tocopherol antioxidants, for example α-tocopherol, β-tocopherol, γ-tocopherol, δ-tocopherol, and mixtures thereof (vitamin E), vitamin E acetate, etc.; and / or A group of aromatic amine antioxidants such as phenylarylamines (the amines are phenyl and C ６ ~C １０ substituted only by aryl, and ６ ~C １０ aryl is alkylated); and / or from the group of esters of 3,5-di-tert-butyl-4-hydroxyphenylacetic acid with monohydric or polyhydric alcohols, such as methanol, ethanol, octanol, octadecanol, 1,6-hexanediol, 1,9-nonanediol, ethylene glycol, 1,2-propanediol, neopentyl glycol, thiodiethylene glycol, diethylene glycol, triethylene glycol, pentaerythritol, tris(hydroxyethyl)isocyanurate, N,N'-bis(hydroxyethyl)oxamide, 3-thiaundecanol, 3-thiapentadecanol, trimethylhexanediol, trimethylolpropane, and 4-hydroxymethyl-1-phospha-2,6,7-trioxabicyclo[2.2.2]octane; The composition of any one of claims 1 to 10, further comprising at least one selected further additive (iii).

12. (iii) Formula III, 【Chemistry 5】 (In the formula, R １－ｉｉｉ and R ２－ｉｉｉ are each independently H or methyl.

12. The composition of claim 11, comprising as a further additive at least one chromanol stabilizer of the formula:

13. (iii) The composition according to claim 11, comprising as a further additive at least a mixture of phenylarylamines as an aromatic amine antioxidant obtained by the reaction of diphenylamine with diisobutylene, comprising 4-tert-butyldiphenylamine, 4-tert-octyldiphenylamine, 4,4'-di-tert-butyldiphenylamine, 2,4,4'-tris-tert-butyldiphenylamine, 4-tert-butyl-4'-tert-octyldiphenylamine, o,o', m,m', or p,p'-di-tert-octyldiphenylamine, 2,4-di-tert-butyl-4'-tert-octyldiphenylamine, 4,4'-di-tert-octyldiphenylamine, and 2,4-di-tert-octyl-4'-tert-butyldiphenylamine.

14. (iii) at least α-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid and a compound of formula (V): 【Chemistry 6】 12. The composition of claim 11, comprising as a further additive an ester of with octadecanol.

15. (a) premixing components (ii.1), (ii.2), and (iii.3) with the stabilizer combination (ii) of claim 1; (b) incorporating the stabilizer combination (ii) as component (i) into the polyurethane foam or polyether polyol of claim 1 to obtain the composition of claim 1; A method for producing the composition of any one of claims 1 to 10, comprising:

16. 10. Use of the stabilizer combination (ii) of claim 1 as component (ii) for protecting a polyurethane foam or a polyether polyol of claim 1 as component (i) from degradation.

Images